CH644089A5 - Binder mix for mortar and its use. - Google Patents
Binder mix for mortar and its use. Download PDFInfo
- Publication number
- CH644089A5 CH644089A5 CH456179A CH456179A CH644089A5 CH 644089 A5 CH644089 A5 CH 644089A5 CH 456179 A CH456179 A CH 456179A CH 456179 A CH456179 A CH 456179A CH 644089 A5 CH644089 A5 CH 644089A5
- Authority
- CH
- Switzerland
- Prior art keywords
- chj
- binder
- mortar
- binder mixture
- repair
- Prior art date
Description
Die Erfindung betrifft ein Bindemittelgemisch für Mörtel oder Beton und seine Verwendung als Reparaturmasse, insbesondere zur Sanierung von schadhaften Stahlbetonteilen. The invention relates to a binder mixture for mortar or concrete and its use as a repair compound, in particular for the renovation of defective reinforced concrete parts.
Es ist bekannt, Bindemittel für Mörtel oder Beton Expoxidharze zuzusetzen, die zusammen mit Polyamiden als Härtungsmittel auch in Gegenwart von Wasser aushärten (vgl. z. B. H. Saechtling «Bauen mit Kunststoffen», Carl Hanser Verlag, München 1973, Seite 73). Solche Bindemittelgemische wurden auch bereits zur Herstellung von Reparaturmörtel verwendet. It is known to add binders for mortar or concrete to epoxy resins which, together with polyamides as hardening agents, also harden in the presence of water (cf., for example, H. Saechtling “Building with plastics”, Carl Hanser Verlag, Munich 1973, page 73). Such binder mixtures have also been used for the production of repair mortars.
Zum Ausbessern beschädigter Stahlbetonbauteile war es bisher notwendig, nach Entrosten der schadhaften Stahlarmierungen die Stahlteile mit einem geeigneten Korrosions-schutzprimer zu behandeln. Danach wurden die schadhaften Stellen mit einer Mörtelmasse, z. B. nach dem Spritzbetonverfahren, ausgebessert, wobei entsprechend DIN 1045 bzw. To repair damaged reinforced concrete components, it was previously necessary to treat the steel parts with a suitable corrosion protection primer after the defective steel reinforcements had been removed. Then the damaged areas were coated with a mortar, e.g. B. after the shotcrete process, repaired, according to DIN 1045 or
10 10th
DIN 18551 auf eine Mindestüberdeckung der Stahleinlagen zu achten ist. DIN 18551, a minimum coverage of the steel inserts must be observed.
Insbesondere die vor dem Auftragen der Reparaturmasse erforderliche Behandlung der Stahlteile mit einem geeigneten Korrosionsschutzprimer stellt einen zeitraubenden und kostspieligen Faktor bei der Reparatur von Stahlbetonbauten dar. Aufgabe der Erfindung war es daher, ein Bindemittelgemisch für Mörtel und Beton zu finden, welches diese Nachteile überwindet. In particular, the treatment of the steel parts with a suitable corrosion protection primer, which is required before the application of the repair compound, is a time-consuming and costly factor in the repair of reinforced concrete structures. The object of the invention was therefore to find a binder mixture for mortar and concrete which overcomes these disadvantages.
Diese Aufgabe wird durch ein Bindemittelgemisch aus einem hydraulischen Binder, wie z. B. Wasserkalk und insbesondere Zement, Epoxidharzen, einm Härter, Wasser und gegebenenfalls Reaktivverdünnern, Pigmenten und/oder weiteren üblichen Hilfsmitteln gelöst, das dadurch gekennzeichnet ist, dass es als Härtungsmittel Verbindungen der Formeln I und/oder II enthält: This task is performed by a mixture of binders from a hydraulic binder, such as. B. water lime and in particular cement, epoxy resins, a hardener, water and optionally reactive diluents, pigments and / or other conventional auxiliaries, which is characterized in that it contains compounds of the formulas I and / or II as hardening agents:
H2N-"R-NH-CH2-CH-CH2-0-R ' OH H2N- "R-NH-CH2-CH-CH2-0-R 'OH
h2N-R-NH-ch2-CH-CH2-0-R"-0-ch2-ch-ch2-NH-R-NH2 ii h2N-R-NH-ch2-CH-CH2-0-R "-0-ch2-ch-ch2-NH-R-NH2 ii
I ^ I I ^ I
oh oh worin R -CH2-CH2-NH-CH2-CH2-, oh oh where R -CH2-CH2-NH-CH2-CH2-,
-ch2-ch2-nh-ch2-ch2-nh-ch2-ch2 -, -ch2-ch2-nh-ch2-ch2-nh-ch2-ch2 -,
CHj CH2- CHj CH2-
oder or
■C^VCH, ■ C ^ VCH,
CH3—CH2—CHj—CH,— CH3 — CH2 — CHj — CH, -
oder und or and
R R
CHj CHj
644089 644089
oder or
4 4th
CHj OH CH3 CHj OH CH3
bedeuten. mean.
Es hat sich nun überraschenderweise gezeigt, dass das er-findungsgemässe Bindemittelgemisch eine Reparaturmasse darstellt, mit der die aufgezeigten Nachteile vermieden werden können, d.h., es ist möglich, den Reparaturmörtel direkt, also ohne vorherige Behandlung der Stahlarmierungen mit einem Korrosionsschutzprimer, auf diese aufzubringen. Ausserdem wird ausreichender Korrosionsschutz auch schon bei Überdeckungen erreicht, die die vorschriftsmässig geforderten Mindestüberdeckungen deutlich unterschreiten können, was sowohl technisch als auch wirtschaftlich von Vorteil ist. Surprisingly, it has now been shown that the binder mixture according to the invention is a repair compound with which the disadvantages shown can be avoided, i.e. it is possible to apply the repair mortar directly to this, i.e. without prior treatment of the steel reinforcements with a corrosion protection primer. In addition, sufficient corrosion protection is achieved even with overlaps that can significantly fall below the minimum overlaps required by the regulations, which is both technically and economically advantageous.
Gegenstand der Erfindung ist deshalb auch die Verwendung des erfindungsgemässen Bindemittelgemisches als Reparaturmasse, insbesondere zur Sanierung von schadhaften Stahlbetonteilen, welches dadurch gekennzeichnet ist, dass auf die entrosteten Flächen von Stahlarmierungen das erfin-dungsgemässe Bindemittelgemisch aufgetragen wird, vorzugsweise ohne vorherige Behandlung der Stahlarmierungen mit einem Korrosionsschutzprimer. The invention therefore also relates to the use of the binder mixture according to the invention as a repair compound, in particular for the restoration of damaged reinforced concrete parts, which is characterized in that the binder mixture according to the invention is applied to the rust-free surfaces of steel reinforcements, preferably without prior treatment of the steel reinforcements with a corrosion protection primer .
Die Aminaddukte werden durch Umsetzung der entsprechenden Aminkomponente mit der entsprechenden Epoxid-komponente im Verhältnis 1 Mol Amin zu 0,1 bis 2,0 Epoxidäquivalenten, vorzugsweise 1 Mol Amin zu 0,2 bis 1,5 Epoxidäquivalenten, erhalten. The amine adducts are obtained by reacting the corresponding amine component with the corresponding epoxy component in a ratio of 1 mol of amine to 0.1 to 2.0 epoxy equivalents, preferably 1 mol of amine to 0.2 to 1.5 epoxy equivalents.
Als Epoxidharze können die üblichen Epoxidharze, z.B. auf der Basis Bisphenol A und/oder Bisphenol F mit einem EÄ von 175 bis 210, vorzugsweise 175 bis 190, verwendet werden. Die Menge der Kombination Epoxidharz + Härter beträgt vorzugsweise 1-40 Gew.-%, insbesondere 20-40 Gew.-%, bezogen auf die Bindemittelmischung. Bei Verwendung von Reaktivverdünnern werden Epoxidharze und Reaktivverdünner vorzugsweise im Verhältnis 75-95 zu 25-5 verwendet, wobei als Reaktivverdünner insbesondere solche auf Basis eines Di- oder Triglycidyläthers eingesetzt werden, wie sie in der deutschen Patentanmeldung P 2 726 269 der Rütgerswerke AG beschrieben werden. Die Härtungsmittel und die Epoxidharze werden im üblichen Mengenverhältnis zueinander eingesetzt (vgl. Jahn, Epoxidharze, Leipzig 1968, Seite 49). Als Zemente können die üblichen Zementsorten, wie z. B. Portlandzement, Eisen-Portlandzement, Hochofenzement usw., eingesetzt werden. Übliche Hilfsmittel sind z.B. Verlaufmittel, Entlüftungsmittel, Entschäumer und Pigmentstabilisatoren. The usual epoxy resins, e.g. based on bisphenol A and / or bisphenol F with an EA of 175 to 210, preferably 175 to 190, can be used. The amount of the combination of epoxy resin + hardener is preferably 1-40% by weight, in particular 20-40% by weight, based on the binder mixture. If reactive diluents are used, epoxy resins and reactive diluents are preferably used in a ratio of 75-95 to 25-5, with those based on a di- or triglycidyl ether, in particular those used as described in German Patent Application P 2 726 269 by Rütgerswerke AG, being used as reactive diluents . The curing agents and the epoxy resins are used in the usual quantitative ratio to one another (cf. Jahn, Epoxidharze, Leipzig 1968, page 49). The usual types of cement, such as. B. Portland cement, iron Portland cement, blast furnace cement, etc. can be used. Common tools are e.g. Leveling agents, deaerating agents, defoamers and pigment stabilizers.
Vor dem Auftragen der Reparaturmasse nach dem erfindungsgemässen Verfahren können die Betonflächen auch mit einer sogenannten Haftbrücke versehen werden, wie dies bei den üblichen Verfahren zur Sanierung von schadhaften Betonteilen üblich und auch erforderlich ist; bei den mit den erfindungsgemässen Härtern hergestellten Reparaturmassen ist dies in der Regel aber nicht erforderlich. Before applying the repair compound according to the method according to the invention, the concrete surfaces can also be provided with a so-called adhesive bridge, as is customary and also necessary in the customary methods for the restoration of damaged concrete parts; in the case of the repair compositions produced with the hardeners according to the invention, however, this is generally not necessary.
Vorstehend und nachstehend bedeuten Prozentangaben Gewichtsprozente. GT steht für Gewichtsteile, EÄ für Epoxidäquivalentgewicht. Above and below, percentages mean percentages by weight. GT stands for parts by weight, EÄ for epoxy equivalent weight.
Beispiele Examples
15 Epoxidharz-Zusammensetzung 1 : 15 epoxy resin composition 1:
85 GT Diglycidyläther des Bisphenol A EÄ = 175-190 15 GT Triglydicyläther des Trimethylolpropen 85 pbw diglycidyl ether of bisphenol A EÄ = 175-190 15 pbw triglydicyl ether of trimethylol propene
EÄ = 150-170 EÄ = 150-170
20 Epoxidharz-Zusammensetzung 2: 20 epoxy resin composition 2:
85 GT Diglycidyläther des Bisphenol F EÄ = 170-190 15 GT Diglydidyläther des Neopentylglycil 85 pbw diglycidyl ether of bisphenol F EÄ = 170-190 15 pbw diglydidyl ether of neopentylglycil
EÄ = 130-145 EÄ = 130-145
25 Härtungsmittel A 25 hardening agent A
Rütepox VE 2883 der Bakelite GmbH, Letmathe (vgl. Firmenschrift vom Jan. 1977), ein Addukt aus einem cyclo-aliphatischen Amin und einer Epoxidverbindung mit einem EA von 175-190 (Digylcidyläther des Bisphenol A). Das 30 Aminaddukt wird mit Benzylalkohol auf Verarbeitungsvis-. kosität verdünnt. Rütepox VE 2883 from Bakelite GmbH, Letmathe (see company publication of January 1977), an adduct of a cyclo-aliphatic amine and an epoxy compound with an EA of 175-190 (digylcidyl ether of bisphenol A). The 30 amine adduct is processed with benzyl alcohol. diluted.
Analysedaten: Analysis data:
Aminäquivalent: 83,5 Viskosität bei 25 °C: ca. 3500 mPa • s. Amine equivalent: 83.5 Viscosity at 25 ° C: approx. 3500 mPa • s.
35 Topfzeit: 100 g-Ansatz: 30-35 min 35 Pot life: 100 g batch: 30-35 min
Härtungsmittel B Rütapox VE 2873 der Bakelite GmbH, Letmathe (vgl. Firmenschrift vom Nov. 1976), ein Addukt aus einem ali-40 phatischen Amin und Phenylglycidyläther. Das Aminaddukt wird mit Benzylalkohol auf Verarbeitungsviskosität verdünnt. Hardening agent B Rütapox VE 2873 from Bakelite GmbH, Letmathe (cf. company publication from Nov. 1976), an adduct of an ali-40 phatic amine and phenylglycidyl ether. The amine adduct is diluted to the processing viscosity with benzyl alcohol.
Analysedaten: Analysis data:
Aminäquivalent: 92,5 45 Viskosität bei 25 °C: ca. 3500 mPa • s Topfzeit: 100 g-Ansatz: 20-25 min Amine equivalent: 92.5 45 Viscosity at 25 ° C: approx. 3500 mPa • s Pot life: 100 g batch: 20-25 min
Beispiel 1 example 1
Bindemittelgemisch Binder mixture
Gewichtsteile Parts by weight
Portlandzement Portland cement
100 100
Epodidharzzusammensetzung 1 Epodid resin composition 1
28 28
Härtungsmittel A Hardening agent A
12 12
Wasser water
40 40
Zuschlagstoff: Sand 0-4 mm Aggregate: sand 0-4 mm
300 300
Beispiel 2 Example 2
Bindemittelgemisch Binder mixture
Gewichtsteile Parts by weight
Hochofenzement Blast furnace cement
100 100
Epoxidharzzusammensetzung 2 Epoxy resin composition 2
21 21st
Härtungsmittel B Hardening agent B
9 9
Wasser water
35 35
Zuschlagstoff: Sand 0-4 mm Aggregate: sand 0-4 mm
400 400
5 5
644 089 644 089
Beispiel 3 Example 3
Bindemittelgemisch Gewichtsteile Binder mixture parts by weight
Schnellzement 100 Fast cement 100
Epoxidharzzusammensetzung 1 56 Epoxy resin composition 1 56
Härtungsmittel B 24 Hardener B 24
Wasser 35 Water 35
Zuschlagstoff: Sand 0-4 mm 400 Aggregate: sand 0-4 mm 400
Ein aus den Bindemittelgemischen und den Zuschlagstoffen nach den Beispielen 1 bis 3 hergestellter Reparaturmörtel wird direkt, also ohne vorherige Korrosionsschutzbehandlung, in einer Dicke von 5-20 mm auf die Stahlarmierung eines Stahlbetonteils aufgebracht. Eine Überprüfung der Stahlarmierungen nach 12 Monaten zeigte keinerlei Veränderung. A repair mortar produced from the binder mixtures and the additives according to Examples 1 to 3 is applied directly to the steel reinforcement of a reinforced concrete part in a thickness of 5-20 mm without prior corrosion protection treatment. A review of the steel reinforcement after 12 months showed no change.
5 5
Arbeitet man wie oben angegeben mit einem Bindemittelgemisch der Zusammensetzung der Beispiele 1 bis 3, in welchem aber der erfindungsgemäss eingesetzte Härter durch einen bekannten, für ein Bindemittelgemisch aus Ze-lo ment und Epoxidharzen üblichen Polyaminoamidhärter (Handelsbezeichnung Casamid der Fa. Akzo) ersetzt wurde, so zeigen sich nach 12 Monaten bereits deutliche Spuren einer Unterrostung. If one works as indicated above with a binder mixture of the composition of Examples 1 to 3, in which, however, the hardener used according to the invention has been replaced by a known polyaminoamide hardener (trade name Casamid from Akzo), which is customary for a binder mixture of cement and epoxy resins, this shows clear signs of under-rusting after just 12 months.
Claims (3)