CH634667A5 - Film for electrostatic reprography - Google Patents
Film for electrostatic reprography Download PDFInfo
- Publication number
- CH634667A5 CH634667A5 CH1186577A CH1186577A CH634667A5 CH 634667 A5 CH634667 A5 CH 634667A5 CH 1186577 A CH1186577 A CH 1186577A CH 1186577 A CH1186577 A CH 1186577A CH 634667 A5 CH634667 A5 CH 634667A5
- Authority
- CH
- Switzerland
- Prior art keywords
- coating
- film
- film according
- carrier material
- thickness
- Prior art date
Description
Die Erfindung betrifft eine Folie für die elektrostatische Bei einer besonders vorteilhaften Ausbildung der erfin- The invention relates to a film for electrostatic In a particularly advantageous embodiment of the invented
Reprographie, insbesondere für die Herstellung von Transpa- dungsgemässen Folie fliesst die Hälfte einer auf die Folie aufge-rentkopien auf Normalkopiergeräten. « brachten Ladung in weniger als 100 Sekunden ab. Reprography, especially for the production of transparent film, flows half of one copy on the film on normal copying machines. «Took charge in less than 100 seconds.
Die bekannten Geräte arbeiten mit Papier, das Vorzugs- Die Erfindung wird durch die nachstehenden Beispiele weise beschichtet ist, das jedoch nur geringe oder schlechte erläutert: The known devices work with paper, which is preferred. The invention is coated by the following examples, but this explains only little or bad:
Lichtdurchlässigkeit hat. Solche Papierträger haben ausserdem den Nachteil, dass sie leicht reissen und nur für die Herstellung Beispiel 1 Has translucency. Such paper carriers also have the disadvantage that they tear easily and only for the production of example 1
einer begrenzten Anzahl von Kopien geeignet sind. 50 Zur Zubereitung einer Beschichtungslösung für die erfin- a limited number of copies are suitable. 50 To prepare a coating solution for the invented
Diese Nachteile werden durch die neue Folie gemäss der dungsgemässe Folie wurde mit folgenden Geräten gearbeitet: Erfindung überwunden. Gefässe: Rührbehälter aus V4A-Stahl oder Polyäthylen, These disadvantages are overcome by the new film according to the film according to the invention, the following devices were used: the invention was overcome. Vessels: stirred tanks made of V4A steel or polyethylene,
Gegenstand der Erfindung ist die im Patentanspruch 1 defi- zylindrisch mit Deckel, vorzugsweise mit Bodenauslaufbahn, nierte Folie für elektrostatische Reprographie, insbesondere Mischwaage : Mechanische Waage mit Mischdrehskala und für die Herstellung von Transparentkopien. 55 Tariervorrichtung. Waagefehler: 0,2 kg, Bereich: 0-300 kg. The subject of the invention is the defi-cylindrical film with a cover, preferably with a bottom run-out, and a coated film for electrostatic reprography, in particular a mixed scale: a mechanical scale with a mixed rotary scale and for the production of transparent copies. 55 buoyancy compensator. Scale error: 0.2 kg, range: 0-300 kg.
Die Hauptverwendungsmöglichkeit solcher Folien liegt in Dampfheizung: Heizschlange aus V4A, passend zu Rührbe- The main use of such foils is in steam heating: heating coil made of V4A, suitable for stirring
der Herstellung von Transparentkopien für die Tageslichtpro- hälter. Heizmedium = Dampf bei etwa 4 bar. Zuleitung zu Heiz-jektion. Es können aber damit auch Zeichenkopien hergestellt schlänge = dampffeste Gummischläuche. the production of transparent copies for the daylight containers. Heating medium = steam at about 4 bar. Supply line for heating injection. However, it can also be used to make copies of characters: snake = steam-proof rubber hoses.
und Zeichnungen, Diagramme, Tabellen und dgl. in einem Rührwerk: Wandhub-Rührwerk mit Mischpropeller mit and drawings, diagrams, tables and the like in one agitator: wall-lift agitator with mixing propeller
Arbeitsgang kopiert und verkleinert werden. Weitere Anwen- 60 Leitring, Drehzahlen stufenlos regelbar von 200 bis 1200 U/min. dungsmöglichkeiten bestehen in der Xerographie, der Teleko- Messzylinder: Inhalt 100-500 ml, Graduierung 1-5 ml. pie, der Mikroverfilmung und Duplizierung, in der Infrarot- und Elektrische Tischware: Bereich = 2000 g, Teilung = 0,1 g. Ultraviolett-Spektroskopie, in der Aufzeichnung chromati- Dispergator : «V-Turrax» von Janke + Kunkel. Operation can be copied and reduced. Other applications - 60 guide ring, speeds infinitely variable from 200 to 1200 rpm. Possible uses are in xerography, the telekom measuring cylinder: content 100-500 ml, graduation 1-5 ml. pie, microfilming and duplication, in the infrared and electrical tableware: range = 2000 g, division = 0.1 g. Ultraviolet spectroscopy, in the chromatographic dispersion: "V-Turrax" from Janke + Kunkel.
scher Trennverfahren. In allen Fällen wird der Vorteil erreicht, In den Rührbehälter wurden mit Hilfe der Mischwaage 56,4 dass einfach und wirtschaftlich bis zu lOOOmal Transparentko- 65 Gew.% 1,'2-Dichloräthan, 5,0 Gew.% Cyclohexanon und 26,0 pien erhalten werden können. Diese Transparentkopien sind im Gew.% Tetrahydrofuran als Lösungsmittel vorgelegt. Die Gegensatz zu Papierträgern reissfest und stabil und bieten die Lösungsmittel wurden dann mit der Dampfheizung auf 40 bis Möglichkeit zur weiteren Durchlichtkopie. Sie lassen sich auch 50 °C aufgeheizt und 12,5 Gew.-% gesättigtes Polyesterharz, separation process. In all cases, the advantage is achieved. Mixing scales 56.4 are used to easily and economically add up to 100 times transparent co- 65 wt.% 1, 2-dichloroethane, 5.0 wt.% Cyclohexanone and 26.0 pien can be obtained. These transparent copies are presented in% by weight of tetrahydrofuran as a solvent. In contrast to paper carriers, they are tear-resistant and stable and offer the solvents with steam heating at 40 to the possibility of further transmitted-light copies. They can also be heated to 50 ° C and 12.5% by weight saturated polyester resin,
634 667 634 667
M DG r|5000, unter kräftigem Rühren in die warmen Lösungsmittel gegeben und gelöst. Danach wurden 0,05 Gew.% Steara-midopropyldimethylammoniumnitrat als Mittel zum Antistatischmachen mit dem Messzylinder abgemessen und zugegeben. Als Körnungsmittel wurden 0,08 Gew.-% Siliciumdioxid, mittlere Körnung: 6-8,5 (im, SÌO2:94 Gew.-% auf der Tischwaage abgewogen und zum Schluss zugegeben. Die fertige Lösung wurde nach etwa 15 Minuten bei mittlerer Drehzahl von etwa 500 Umdrehungen/Minute gerührt und dann in bekannter Weise auf eine Polyesterfolie beidseitig aufgetragen. Es wurde eine Polyesterfolie der Firma DuPont de Nemours mit folgenden Massen verwendet: Breite 125 cm, Dicke 0,1 mm, Länge per Rolle 1100 laufende Meter. M DG r | 5000, added to the warm solvents with vigorous stirring and dissolved. Then 0.05% by weight of stearamidopropyldimethylammonium nitrate was measured and added as an antistatic agent using the measuring cylinder. 0.08% by weight of silicon dioxide, average grain size: 6-8.5 (in, SÌO2: 94% by weight) were weighed out on the bench scale and added at the end. The finished solution was after about 15 minutes at medium speed of about 500 revolutions / minute and then applied in known manner to a polyester film on both sides, using a polyester film from DuPont de Nemours with the following dimensions: width 125 cm, thickness 0.1 mm, length per roll 1100 running meters.
Die erhaltenen Lösungen sind im allgemeinen niedrig viskos und zeigen ein newtonisches Fliessverhalten. The solutions obtained are generally of low viscosity and show Newtonian flow behavior.
Bekannte Verfahren sind Angiessen Antauchen und Anspülen; bei schnellaufenden Beschichtungsmaschinen wird vorzugsweise vordosiert und der Überschuss über hochglanzpolierte Rakelwalzen abgetragen. Die Maschinengeschwindigkeit lag bei 30 m/Minute bei Tempraturen von 80 bis 130 °C und einer Luftbeaufschlagung von 5 m3/Sekunde/m2. Known methods are pouring, dipping and rinsing; in the case of high-speed coating machines, it is preferably pre-metered and the excess is removed via highly polished doctor blades. The machine speed was 30 m / minute at temperatures from 80 to 130 ° C and an air exposure of 5 m3 / second / m2.
Das erhaltene Produkt besass folgende Eigenschaften: Aussehen: klar und körnig The product obtained had the following properties: Appearance: clear and granular
Oberflächenwiderstand: zwischen 107-5x 10u Ohm Lichtdurchlässigkeit: 90% Surface resistance: between 107-5x 10u Ohm light transmission: 90%
Trübung: 5 ± 2% Turbidity: 5 ± 2%
«multiple feeding» 10 Folien übereinander müssen einzeln eingezogen werden* Planlage der Kopie: Keine kurzen Wellen am Rand des Formates und keine lokalen Deformationen * Das «multiple feeding» wird mit verschiedenen Normalpapierkopiergeräten getestet. "Multiple feeding" 10 foils on top of each other must be drawn in individually * flatness of the copy: no short waves at the edge of the format and no local deformations * the "multiple feeding" is tested with various plain paper copiers.
Eine solche Folie ist insbesondere für Trockenkopiergeräte geeignet. Such a film is particularly suitable for dry copiers.
Tonerhaftung: fingernagelfest Toner adhesion: fingernail resistant
Schichtdicke: 0,2-6 |im Layer thickness: 0.2-6 | im
Rauhigkeit: 0,2-6 (im Roughness: 0.2-6 (in
Beschriftung: wässrige und lösemittelhaltige Inscription: water-based and solvent-based
Filzschreiber waren geeignet Schichthaftung: nach Gitterschnitt einwandfreie Haftung bei Prüfung mit verschiedenen Klebebändern Felt-tip pens were suitable for layer adhesion: perfect adhesion after testing with various adhesive tapes
Beispiel 2 Example 2
Es wurde wie im Beispiel 1 gearbeitet, jedoch vor dem Aufbringen auf die Trägerfolie noch mit einem Dispergator etwa 90 Minuten lang dispergiert. Für die Ansetzung der Lösung wurden folgende Reagenzien verwendet: (Konzentrationsangaben in den Beispielen sind gewichtsmäs-sig) The procedure was as in Example 1, but was dispersed with a disperser for about 90 minutes before being applied to the carrier film. The following reagents were used to prepare the solution: (Concentration figures in the examples are by weight)
Lösungsmittel 80,15% Methyläthylketon Solvent 80.15% methyl ethyl ketone
8,16% Diosan 8.16% diosan
Harz 12,33% Polymethylmethacrylat Resin 12.33% polymethyl methacrylate
Dispergierhilfsmittel 0,12% Siliconöl, 100 mm2/s Körnungsmittel 1,24% disperse Kieselsäure Dispersing agent 0.12% silicone oil, 100 mm2 / s granulating agent 1.24% disperse silica
Oberfläche etwa 200 m2/g Surface about 200 m2 / g
Es wurde eine transparente, hitzestabilisierte Polyesterfolie verwendet. Diese Folie gewährt nach dem Aufbringen der leicht mattierten Beschichtung eine einwandfreie Annahme von Flüssigkeitstoner. Die Rückseite entsprach der farblosen Beschichtung von Beispiel 1. A transparent, heat-stabilized polyester film was used. After the slightly matt coating has been applied, this film guarantees perfect acceptance of liquid toner. The back corresponded to the colorless coating of Example 1.
Beispiel 3 Example 3
Es wurde wie in Beispiel 1 gearbeitet und auf eine Trägerfolie wie in Beispiel 1 eine Beschichtung aus den nachfolgend aufgeführten Bestandteilen aufgebracht: The procedure was as in Example 1 and a coating of the components listed below was applied to a carrier film as in Example 1:
s Lösungsmittel 45,65% Methyläthylketon s solvent 45.65% methyl ethyl ketone
45,65% Dioxan 3,05% Cyclohexanon Harz 5,50% Polymethaerylat 45.65% dioxane 3.05% cyclohexanone resin 5.50% polymethaerylate
Mittel zum 0,12% handelsübliches quaternäres Average to 0.12% commercial quaternary
10 Antistatischmachen Ammoniumsalz Körnungsmittel 0,03% Polyäthylen, mikrofein 10 Antistatic make ammonium salt grain size 0.03% polyethylene, microfine
Die erhaltene Folie besass die Eigenschaften der Folie des Beispiels 1. The film obtained had the properties of the film of Example 1.
15 Beispiel 4 15 Example 4
Es wurde wie in Beispiel 1 gearbeitet und auf eine Trägerfolie gemäss Beispiel 2 eine Beschichtung aus den nachfolgend aufgeführten Bestandteilen aufgebracht: The procedure was as in Example 1 and a coating of the components listed below was applied to a carrier film according to Example 2:
Lösungsmittel 85,50% Methyläthylketon Solvent 85.50% methyl ethyl ketone
20 4,50% Butylacetat 20 4.50% butyl acetate
4,50% Cylchexanon Harzmischung 3,75% Polymethaerylat 4.50% Cylchexanon resin blend 3.75% polymethaerylate
1,65% Vinylchlorid/Vinylacetat Mischpolymerisat MG 8500-9500 25 Körnungsmittel 0,03% Polyäthylen, mikrofein 1.65% vinyl chloride / vinyl acetate interpolymer MG 8500-9500 25 grit 0.03% polyethylene, microfine
Die erhaltene Folie besass alle Eigenschaften wie das Produkt von Beispiel 1, jedoch betrug der Oberflächenwiderstand etwa IO12 Ohm. Diese Folie ist besonders für Trockentoner-Duplikatoren geeignet. The film obtained had all the properties as the product of Example 1, but the surface resistance was about IO12 ohms. This film is particularly suitable for dry toner duplicators.
30 30th
Beispiel 5 Example 5
Es wurde wie in Beispiel 1 gearbeitet, die Lösungsmittel wurden jedoch nicht erhitzt. Auf eine Folie wie in Beispiel 1 wurde eine Beschichtung aus 35 Lösungsmittel 37,75% Methyläthylketon The procedure was as in Example 1, but the solvents were not heated. A coating of 35 solvents 37.75% methyl ethyl ketone was applied to a film as in Example 1
37,75% Dioxan Harze 15,90% Polyesterharz 37.75% dioxane resins 15.90% polyester resin
7,90% Polymethaerylat Mittel zum 0,50% Phosphorsäureester 7.90% polymethaerylate agent for 0.50% phosphoric acid ester
40 Antistatischmachen Körnungsmittel 0,10% Polyäthylen, mikrofein 40 Antistatic make grain size 0.10% polyethylene, microfine
Dispergierhilfsmittel 0,10% Siliconöl, 100 mm2/s aufgebracht und ein Produkt erhalten, das in seinen Eigenschaften dem Produkt aus Beispiel 1 entsprach. Dispersion aid 0.10% silicone oil, 100 mm2 / s applied and obtained a product that corresponded in its properties to the product from Example 1.
45 45
Beispiel 6 Example 6
Es wurde wie in Beispiel 5 gearbeitet und dabei der Farbstoff im Lösungsmittel 1 vorgelöst. The procedure was as in Example 5 and the dye was predissolved in solvent 1.
Auf die Folie wurde eine Beschichtung aus 50 Lösungsmittel 1 7,40% Methanol A coating of 50 solvents 1 7.40% methanol was applied to the film
2,24% Cyclohexanon blauer organischer 0,93% Kupfer-Farbstoff phtalocynaninsulfamid 2.24% cyclohexanone blue organic 0.93% copper dye phtalocynanine sulfamide
Lösungsmittel 2 24,50% Methyläthylkoton Solvent 2 24.50% methyl ethyl koton
55 53,20% Dioxan 55 53.20% dioxane
Harz 1,70% Polyesterharz Resin 1.70% polyester resin
Körnungsmittel 0,03% Siliciumdioxyd, Körnung 6-13 Grit 0.03% silica, grit 6-13
|j.m aufgebracht und ein Produkt erhalten, das in seinen Eigenschaf-60 ten weitgehend dem Produkt aus Beispiel 1 entsprach. | j.m applied and obtained a product which largely corresponded to the product from Example 1 in its properties.
Durch Austausch des Farbstoffes sind die Farbtöne gelb, grün und rot möglich. By changing the dye, the shades of yellow, green and red are possible.
Claims (8)