CA3118800A1 - Artificial turf infill and artificial turf - Google Patents
Artificial turf infill and artificial turf Download PDFInfo
- Publication number
- CA3118800A1 CA3118800A1 CA3118800A CA3118800A CA3118800A1 CA 3118800 A1 CA3118800 A1 CA 3118800A1 CA 3118800 A CA3118800 A CA 3118800A CA 3118800 A CA3118800 A CA 3118800A CA 3118800 A1 CA3118800 A1 CA 3118800A1
- Authority
- CA
- Canada
- Prior art keywords
- particles
- coating
- turf
- artificial turf
- infill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a turf infill (100) comprising a mixture of -cork particles, wherein the cork particles are coated with a polymer and/or resin component, and -rubber particles, wherein the rubber particles are coated with a polymer and/or resin component.
Description
Artificial turf infill and artificial turf Description The invention relates to artificial turf infill and an artificial turf system with an artificial turf and artificial turf infill.
Artificial turf or artificial grass is a surface that is made up of fibers and is used to replace grass. The structure of the artificial turf is designed such that the artificial turf has an appearance that resembles grass. Artificial turf is typically used as a surface for sports such as soccer, American football, rugby, tennis and golf, or for playing fields or exercise fields. Furthermore, artificial turf is frequently used for landscaping applications.
Artificial turf may be manufactured using techniques for manufacturing carpets. For example, artificial turf fibers, which have the appearance of grass blades, may be tufted or attached to a backing. Oftentimes, artificial turf infill is placed between the artificial turf fibers.
Artificial turf infill is a granular material that covers the bottom portion of the artificial turf fibers. The use of artificial turf infill may have a number of advantages. For example, artificial turf infill may help the artificial turf fibers stand up straight. Artificial turf infill may also absorb impact from walking or running and provide an experience similar to that of being on real turf. The artificial turf infill may also help keep the artificial turf carpet flat and in place by weighing it down.
Even though the artificial turf infills known from the art are constantly being further developed, rubber granulate or recycled (e.g., from car tires) rubber granulate is still most commonly used as artificial turf infill. The most commonly used rubbers are
Artificial turf or artificial grass is a surface that is made up of fibers and is used to replace grass. The structure of the artificial turf is designed such that the artificial turf has an appearance that resembles grass. Artificial turf is typically used as a surface for sports such as soccer, American football, rugby, tennis and golf, or for playing fields or exercise fields. Furthermore, artificial turf is frequently used for landscaping applications.
Artificial turf may be manufactured using techniques for manufacturing carpets. For example, artificial turf fibers, which have the appearance of grass blades, may be tufted or attached to a backing. Oftentimes, artificial turf infill is placed between the artificial turf fibers.
Artificial turf infill is a granular material that covers the bottom portion of the artificial turf fibers. The use of artificial turf infill may have a number of advantages. For example, artificial turf infill may help the artificial turf fibers stand up straight. Artificial turf infill may also absorb impact from walking or running and provide an experience similar to that of being on real turf. The artificial turf infill may also help keep the artificial turf carpet flat and in place by weighing it down.
Even though the artificial turf infills known from the art are constantly being further developed, rubber granulate or recycled (e.g., from car tires) rubber granulate is still most commonly used as artificial turf infill. The most commonly used rubbers are
2 styrene-butadiene rubber (SBR) and ethylene propylene diene monomer (EPDM), both of which can be generated from recycled rubber (post-consumer waste or post-industrial waste) or virgin material. Recycled rubbers are cost-effective as they are derived from existing products that have reached the end of their service life. Even though recycling of, e.g., used car tires to make artificial turf infill particles has an environmentally friendly aspect, concerns have arisen lately about the potential health effects of substances released by the granulate in synthetic turf sports fields with vulcanized (either by peroxide or sulphur vulcanization) recycled rubber infill.
Further, in the hot season, when the outside surfaces are subjected to severe heat, rubber-based artificial turf infill materials tend to heat to 20-40 C above the ambient temperature.
It is therefore the purpose of the invention to provide an improved turf infill material which is environmentally friendly and less likely to release potentially health-affecting substances.
The invention provides for an improved turf infill and an artificial turf with the improved turf infill. The problem is solved by the features as specified in the independent claims. Embodiments of the invention are given in the dependent claims. The embodiments and examples described herein can freely be combined with each other unless they are mutually exclusive.
In one aspect, the invention provides for a turf infill comprising a mixture of cork particles, wherein the cork particles are coated with a polymer and/or resin component, and rubber particles, wherein the rubber particles are coated with a polymer and/or resin component.
The particles of cork and rubber may be of any suitable shape, including granules, gravel, grains and combinations thereof, and in various dimensions thereof.
The coating may be applied to the cork particles and rubber particles using any suitable method, and such methods are well known in the art. The cork particles may be coated, e.g., in a flow reactor or batch reactor, separately from the rubber
Further, in the hot season, when the outside surfaces are subjected to severe heat, rubber-based artificial turf infill materials tend to heat to 20-40 C above the ambient temperature.
It is therefore the purpose of the invention to provide an improved turf infill material which is environmentally friendly and less likely to release potentially health-affecting substances.
The invention provides for an improved turf infill and an artificial turf with the improved turf infill. The problem is solved by the features as specified in the independent claims. Embodiments of the invention are given in the dependent claims. The embodiments and examples described herein can freely be combined with each other unless they are mutually exclusive.
In one aspect, the invention provides for a turf infill comprising a mixture of cork particles, wherein the cork particles are coated with a polymer and/or resin component, and rubber particles, wherein the rubber particles are coated with a polymer and/or resin component.
The particles of cork and rubber may be of any suitable shape, including granules, gravel, grains and combinations thereof, and in various dimensions thereof.
The coating may be applied to the cork particles and rubber particles using any suitable method, and such methods are well known in the art. The cork particles may be coated, e.g., in a flow reactor or batch reactor, separately from the rubber
3 particles, or both (rubber particles and cork particles) may be coated simultaneously, e.g., in the same flow reactor or batch reactor. Methods for coating the particles are disclosed for example in WO 2017/153261, which is hereby incorporated in its entirety by reference herein.
It is intended that the polymer and/or resin component of the coatings does not show any environmental toxicity. Possible polymer and/or resin components are selected from the group consisting of polyurethane (PU), polyvinyl butyral (PVB), acrylic resin, acrylate monomers, methacrylates, methyl acrylates and blends thereof.
The use of cork particles as part of the mixture of the inventive turf infill may be beneficial, as cork is a renewable raw material derived from the bark of the cork oak (Quercus suber) from sustainably managed sources, and the particles can also be recycled from leftover material, e.g., from bottle cork production.
Furthermore, cork is not known to have any environmental toxicity, has insulating properties with low heat absorption when exposed to sunlight and has elastic features. Hence cork particles as part of the mixture of the inventive turf infill may be beneficial, even though the ultraviolet radiation (U.V.) resistance and the mechanical stability/resistance are limited.
The coating of the cork particles may be beneficial, as the coating may weigh down the relatively light cork particles. This can reduce the tendency of cork to float away during heavy rainfall or be blown away by wind and may reduce the unmixing of particles of different weight. The coating can comprise one or more layers.
The layers can have the same or different thicknesses. The polymer and/or resin component of the layers of the coating may be the same or different. In addition, coating may have the effect that coated cork particles cling together or are honed by friction during particle movement and the abrasion and wear is thus reduced and the mechanical stability may be increased.
The coating of the known rubber particles may be beneficial, as the coating may prevent the release of possibly health-affecting substances. Hence, rubber particles
It is intended that the polymer and/or resin component of the coatings does not show any environmental toxicity. Possible polymer and/or resin components are selected from the group consisting of polyurethane (PU), polyvinyl butyral (PVB), acrylic resin, acrylate monomers, methacrylates, methyl acrylates and blends thereof.
The use of cork particles as part of the mixture of the inventive turf infill may be beneficial, as cork is a renewable raw material derived from the bark of the cork oak (Quercus suber) from sustainably managed sources, and the particles can also be recycled from leftover material, e.g., from bottle cork production.
Furthermore, cork is not known to have any environmental toxicity, has insulating properties with low heat absorption when exposed to sunlight and has elastic features. Hence cork particles as part of the mixture of the inventive turf infill may be beneficial, even though the ultraviolet radiation (U.V.) resistance and the mechanical stability/resistance are limited.
The coating of the cork particles may be beneficial, as the coating may weigh down the relatively light cork particles. This can reduce the tendency of cork to float away during heavy rainfall or be blown away by wind and may reduce the unmixing of particles of different weight. The coating can comprise one or more layers.
The layers can have the same or different thicknesses. The polymer and/or resin component of the layers of the coating may be the same or different. In addition, coating may have the effect that coated cork particles cling together or are honed by friction during particle movement and the abrasion and wear is thus reduced and the mechanical stability may be increased.
The coating of the known rubber particles may be beneficial, as the coating may prevent the release of possibly health-affecting substances. Hence, rubber particles
4 recycled even from car tires, e.g., in the shape of granules, can be used for the inventive infill material. The coating can comprise one or more layers. The layers can have the same or different thicknesses. The polymer and/or resin component of the layers of the coating may be the same or different.
The combination of cork particles and rubber particles may be beneficial in many aspects, as both cork particles and rubber particles can be recycled from previously manufactured materials, rubber particles from, e.g., car tires and cork particles from, e.g., leftover material from bottle cork production. In addition, cork is a renewable raw material. Furthermore, the heating up of the artificial turf to high temperatures (i.e., to temperatures well above the ambient temperature), caused by the heating up of rubber particles, may be reduced due to the insulating properties of cork particles. Further, the coating of the cork particles and the rubber particles, which may, e.g., have a higher coefficient of friction than rubber or cork and/or may be slightly sticky, may slow the segregation (unmixing) of particles over time due to different weights or sizes.
In one embodiment of the invention, the weight percentage ratio of the cork particles to the rubber particles is between 1 : 4 and 1 : 8, in particular between 1 :
The combination of cork particles and rubber particles may be beneficial in many aspects, as both cork particles and rubber particles can be recycled from previously manufactured materials, rubber particles from, e.g., car tires and cork particles from, e.g., leftover material from bottle cork production. In addition, cork is a renewable raw material. Furthermore, the heating up of the artificial turf to high temperatures (i.e., to temperatures well above the ambient temperature), caused by the heating up of rubber particles, may be reduced due to the insulating properties of cork particles. Further, the coating of the cork particles and the rubber particles, which may, e.g., have a higher coefficient of friction than rubber or cork and/or may be slightly sticky, may slow the segregation (unmixing) of particles over time due to different weights or sizes.
In one embodiment of the invention, the weight percentage ratio of the cork particles to the rubber particles is between 1 : 4 and 1 : 8, in particular between 1 :
5.5 and 1 : 6.5.
This proportion of weight percentage is beneficial, as the bulk density and/or poured density (freely settled bulk density) of the cork particles is much lighter than that of the rubber particles. Therefore, in order to obtain an optimal weight distribution of cork particles and rubber particles, the weight percentage ratio can be chosen to be between 1 : 4 and 1 : 8. This weight percentage ratio range is beneficial as it may provide that the size and the surface areas of both the cork and rubber particles are within the same range; thus the friction resistance between the particles, e.g. cork particles and rubber particles, is basically homogenous. In order to obtain an approximately even number of cork particles and rubber particles, the weight percentage ratio can be chosen to be between 1 : 5.5 and 1 : 6.5. Due to this optimized weight percentage ratio, it may also be possible to achieve the optical perception that the particles are homogeneous.
According to one embodiment, it is envisaged that the infill is configured such that the poured density of the coated cork particles is between any one of the 5 following: 90 g/dm3 and 180 g/dm3, 100 g/dm3 and 150 g/dm3, and 125 g/dm3 and 135 g/dm3; and the poured density of the coated rubber particles is between any one of the following: 400 g/dm3 and 650 g/dm3, 450 g/dm3 and 600 g/dm3, and 530 g/dm3 and 550 g/dm3.
In one embodiment of the invention, the polymer and/or resin component of the coating of the cork particles and/or rubber particles is polyurethane.
A polyurethane coating may be beneficial as fully reacted polyurethane polymer is considered to be chemically inert and thus environmentally friendly and may be produced as a hard, abrasion-resistant and durable coating, which may seal the rubber granule.
Alternatively, the polymer and/or resin component of the coating of the cork particles and/or rubber particles is polyvinyl butyral.
The use of PVB as a coating may be beneficial, as PVB is a resin which can be prepared from polyvinyl alcohol by reaction with butyraldehyde, and can be acquired from remnants during production of laminated glass or can be recycled from laminated glass. PVB may be used as a protective layer around the particles.
In addition, PVB has good adhesion to rubber and cork, may be sticky, and is tough and flexible.
In one embodiment of the invention, the coating of the cork particles comprises fillers, in particular barium sulphate (barite), calcium carbonate (chalk), talc, quartz silica, other silicates, other oxides (such as iron oxides), hydro oxides, hollow glass spheres, organic fillers or a combination thereof.
This proportion of weight percentage is beneficial, as the bulk density and/or poured density (freely settled bulk density) of the cork particles is much lighter than that of the rubber particles. Therefore, in order to obtain an optimal weight distribution of cork particles and rubber particles, the weight percentage ratio can be chosen to be between 1 : 4 and 1 : 8. This weight percentage ratio range is beneficial as it may provide that the size and the surface areas of both the cork and rubber particles are within the same range; thus the friction resistance between the particles, e.g. cork particles and rubber particles, is basically homogenous. In order to obtain an approximately even number of cork particles and rubber particles, the weight percentage ratio can be chosen to be between 1 : 5.5 and 1 : 6.5. Due to this optimized weight percentage ratio, it may also be possible to achieve the optical perception that the particles are homogeneous.
According to one embodiment, it is envisaged that the infill is configured such that the poured density of the coated cork particles is between any one of the 5 following: 90 g/dm3 and 180 g/dm3, 100 g/dm3 and 150 g/dm3, and 125 g/dm3 and 135 g/dm3; and the poured density of the coated rubber particles is between any one of the following: 400 g/dm3 and 650 g/dm3, 450 g/dm3 and 600 g/dm3, and 530 g/dm3 and 550 g/dm3.
In one embodiment of the invention, the polymer and/or resin component of the coating of the cork particles and/or rubber particles is polyurethane.
A polyurethane coating may be beneficial as fully reacted polyurethane polymer is considered to be chemically inert and thus environmentally friendly and may be produced as a hard, abrasion-resistant and durable coating, which may seal the rubber granule.
Alternatively, the polymer and/or resin component of the coating of the cork particles and/or rubber particles is polyvinyl butyral.
The use of PVB as a coating may be beneficial, as PVB is a resin which can be prepared from polyvinyl alcohol by reaction with butyraldehyde, and can be acquired from remnants during production of laminated glass or can be recycled from laminated glass. PVB may be used as a protective layer around the particles.
In addition, PVB has good adhesion to rubber and cork, may be sticky, and is tough and flexible.
In one embodiment of the invention, the coating of the cork particles comprises fillers, in particular barium sulphate (barite), calcium carbonate (chalk), talc, quartz silica, other silicates, other oxides (such as iron oxides), hydro oxides, hollow glass spheres, organic fillers or a combination thereof.
6 The use of fillers can be advantageous, as the fillers are able to increase the weight of the coating and may thus increase the overall poured density of the coated cork particles. Thus, as the weight of the coated particles increases, the risk of coated cork floating away during heavy rainfall or being blown away by strong wind is further reduced. It is envisaged that the coating may comprise between 0.1 wt.%
and 60 wt.% of fillers.
In one embodiment, it is envisaged that the coating of the cork particles comprises barium sulphate (barite) and/or calcium carbonate (chalk) as fillers, to increase the total weight of the artificial turf infill.
Barium sulphate and calcium carbonate are particularly advantageous, as they have a high density ¨ e.g., calcium carbonate has a density of 2.7 g/cm3 and barium sulphate has a density of between 4.0 and 4.5 g/cm3. They are also relatively cheap materials and may be used to provide a dense coating.
According to one embodiment, the coating of the cork particles and/or rubber particles comprises particles selected from the group consisting of colored pigments, copper(II) sulfate particles, silver particles, chitosan particles or mixtures thereof.
The colored pigments may be inorganic, such as iron oxide pigments, chromium oxide pigments and/or cobalt oxide pigments, or organic pigments. Further, the colored pigments may be infrared-reflective pigments, which are beneficial due to their ability to reflect infrared light. This may reduce the heating of the artificial turf infill. Further, as the infrared-reflective colored pigments may be contained solely in the applied coating, the costs for the comparably expensive and precious pigments, being merely on the surface of the cork particles and/or rubber particles, is reduced.
Copper(II) sulfate particles and/or chrome particles and/or iron oxide particles may be further beneficial due to their color, relatively low manufacturing costs and/or antibacterial properties. Other antibacterial components that may be used are silver and/or chitosan particles, both of which have natural antibacterial properties.
and 60 wt.% of fillers.
In one embodiment, it is envisaged that the coating of the cork particles comprises barium sulphate (barite) and/or calcium carbonate (chalk) as fillers, to increase the total weight of the artificial turf infill.
Barium sulphate and calcium carbonate are particularly advantageous, as they have a high density ¨ e.g., calcium carbonate has a density of 2.7 g/cm3 and barium sulphate has a density of between 4.0 and 4.5 g/cm3. They are also relatively cheap materials and may be used to provide a dense coating.
According to one embodiment, the coating of the cork particles and/or rubber particles comprises particles selected from the group consisting of colored pigments, copper(II) sulfate particles, silver particles, chitosan particles or mixtures thereof.
The colored pigments may be inorganic, such as iron oxide pigments, chromium oxide pigments and/or cobalt oxide pigments, or organic pigments. Further, the colored pigments may be infrared-reflective pigments, which are beneficial due to their ability to reflect infrared light. This may reduce the heating of the artificial turf infill. Further, as the infrared-reflective colored pigments may be contained solely in the applied coating, the costs for the comparably expensive and precious pigments, being merely on the surface of the cork particles and/or rubber particles, is reduced.
Copper(II) sulfate particles and/or chrome particles and/or iron oxide particles may be further beneficial due to their color, relatively low manufacturing costs and/or antibacterial properties. Other antibacterial components that may be used are silver and/or chitosan particles, both of which have natural antibacterial properties.
7 According to one embodiment of the invention, the overall layer thickness of the coating of the cork particles and/or rubber particles is between 0.1 pm and 1 mm, or between 0.5 pm and 750 pm, or between 10 pm and 150 pm. The coating of the cork particles and/or rubber particles may each comprise one or more (sub-)layers.
The (sub-)layers may have the same or different thicknesses; however, the sum of the individual layer thicknesses is between 0.1 pm and 1 mm. In one embodiment, the overall layer thickness of the coating of the cork particles and/or rubber particles is between 10 pm and 150 pm.
It is contemplated that the particles can be coated with one layer or with multiple layers. To increase the likelihood that the particles are fully encapsulated and thus no possibly health-affecting substances may be released, it may be beneficial to coat the particles two or more times. Alternatively or in addition the use of multiple layers comprising colored particles may have the advantageous effect of providing a more intense and saturated coloring of the coated infill particles.
According to one embodiment, the size of the coated cork particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm; and the size of the coated rubber particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm.
This configuration allows for a well-adjusted particle size distribution for artificial turf.
Furthermore, the (natural) particle size distribution within each range allows the particles to be packed more densely.
It is feasible that the turf infill further comprises microporous zeolite mineral particles. The microporous zeolite mineral particles have pores that form openings on their outer surface. Hence, the use of the microporous zeolite mineral as an infill material is advantageous, as the particles are able to regulate the presence of water and may thus provide for a cooling effect of the surface of the artificial turf. Hence, increased playing comfort can be achieved when the outside temperatures are high.
The (sub-)layers may have the same or different thicknesses; however, the sum of the individual layer thicknesses is between 0.1 pm and 1 mm. In one embodiment, the overall layer thickness of the coating of the cork particles and/or rubber particles is between 10 pm and 150 pm.
It is contemplated that the particles can be coated with one layer or with multiple layers. To increase the likelihood that the particles are fully encapsulated and thus no possibly health-affecting substances may be released, it may be beneficial to coat the particles two or more times. Alternatively or in addition the use of multiple layers comprising colored particles may have the advantageous effect of providing a more intense and saturated coloring of the coated infill particles.
According to one embodiment, the size of the coated cork particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm; and the size of the coated rubber particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm.
This configuration allows for a well-adjusted particle size distribution for artificial turf.
Furthermore, the (natural) particle size distribution within each range allows the particles to be packed more densely.
It is feasible that the turf infill further comprises microporous zeolite mineral particles. The microporous zeolite mineral particles have pores that form openings on their outer surface. Hence, the use of the microporous zeolite mineral as an infill material is advantageous, as the particles are able to regulate the presence of water and may thus provide for a cooling effect of the surface of the artificial turf. Hence, increased playing comfort can be achieved when the outside temperatures are high.
8 The microporous zeolite mineral particle may be selected from the group consisting of chabazite, erionite, mordenite, clinoptilolite, faujasite, phillipsite, zeolite A, zeolite L, zeolite Y, zeolite X and ZSM-5. The zeolite used may thus be natural or obtained by synthesis.
Since artificial turf infill may be used to modify an artificial turf carpet to have more earth-like properties, a microporous zeolite, with a Mohs hardness above 3 and/or a strong absorbent power and/or a color that approximately resembles one of the well-known surface colors (e.g., red, brown, green), may preferably be used. The most preferred microporous zeolite mineral may be of the chabazite and/or clinoptilolite and/or mordenite type.
It is envisaged that the particle size of the microporous zeolite mineral particles is between any one of the following: 0.5 mm and 3.5 mm, and 1.0 mm and 2.5 mm;
and the weight percentage ratio of the microporous zeolite mineral particles to the cork particles and the rubber particles is between 2: 7 and 4: 7, in particular between 2.5: 7 and 3.5: 7.
For the microporous zeolite mineral particles, it may be envisaged that the outer surface of at least some microporous zeolite mineral particles is partly covered with a polyurethane coating. Hereby it may be feasible that 20% to 99% of the outer surface of a microporous zeolite mineral particle is partly covered with a polyurethane coating.
For this embodiment, it may be provided that the partial covering is applied on each side of each microporous zeolite mineral particle, but that there are gaps (holes) in the covering enclosing the particles. The partial coating may be advantageous, since water can be absorbed and/or released by the microporous zeolite mineral particles through their pores which are not covered by the polyurethane coating. The polyurethane coating may be advantageous, as the polymerization reaction may be controlled, as the polyurethane educts are smaller than many fully polymerized polymers, such as polymers in a molten plastic mass. Thus, the surface and the micropores of the microporous zeolite mineral particles may be wetted with the
Since artificial turf infill may be used to modify an artificial turf carpet to have more earth-like properties, a microporous zeolite, with a Mohs hardness above 3 and/or a strong absorbent power and/or a color that approximately resembles one of the well-known surface colors (e.g., red, brown, green), may preferably be used. The most preferred microporous zeolite mineral may be of the chabazite and/or clinoptilolite and/or mordenite type.
It is envisaged that the particle size of the microporous zeolite mineral particles is between any one of the following: 0.5 mm and 3.5 mm, and 1.0 mm and 2.5 mm;
and the weight percentage ratio of the microporous zeolite mineral particles to the cork particles and the rubber particles is between 2: 7 and 4: 7, in particular between 2.5: 7 and 3.5: 7.
For the microporous zeolite mineral particles, it may be envisaged that the outer surface of at least some microporous zeolite mineral particles is partly covered with a polyurethane coating. Hereby it may be feasible that 20% to 99% of the outer surface of a microporous zeolite mineral particle is partly covered with a polyurethane coating.
For this embodiment, it may be provided that the partial covering is applied on each side of each microporous zeolite mineral particle, but that there are gaps (holes) in the covering enclosing the particles. The partial coating may be advantageous, since water can be absorbed and/or released by the microporous zeolite mineral particles through their pores which are not covered by the polyurethane coating. The polyurethane coating may be advantageous, as the polymerization reaction may be controlled, as the polyurethane educts are smaller than many fully polymerized polymers, such as polymers in a molten plastic mass. Thus, the surface and the micropores of the microporous zeolite mineral particles may be wetted with the
9 educts, e.g., with a liquid polyurethane reaction mixture, and when the desired degree of wetting or the desired penetration depth into the pores is achieved, the polymerization can be initialized. Further, the reacted polyurethane polymer is chemically inert.
In addition, since the microporous zeolite mineral particles may be partly coated with the polyurethane coating, natural abrasion and wear of the microporous zeolite mineral during use may be reduced, since the polyurethane coating may provide for a harder and thus protective surface compared with that of uncoated microporous zeolite mineral particles. It may also be advantageous that the Mohs hardness of polyurethane coating can be chosen to be higher or much higher than the Mohs hardness of the microporous zeolite mineral particles. It may be thus beneficial that the Mohs hardness of the polyurethane coating is at least one Mohs unit higher than the Mohs hardness of the selected microporous zeolite mineral particles.
The gaps in the coating of the inventive infill material may result during the manufacture of the infill material, since during the mixing, e.g., in a flow reactor or a batch reactor or a tumbler, the microporous zeolite mineral particles and a liquid polyurethane reaction mixture are mixed and while they are being mixed a solidification reaction is initiated. During the mixing and while the solidification takes place, the microporous zeolite mineral particles may physically touch and interact with each other, thereby causing collision defects such as gaps in the coating and leaving the surface of the microporous zeolite particles partly uncovered.
Thus, water may still be absorbed and released by the microporous zeolite mineral particles in those areas in which the pores of the microporous zeolite minerals are not covered by the polyurethane coating.
It is further envisaged for this embodiment that the polyurethane coating may extend over some of the pores, forming respective covers of the pore openings, wherein the polyurethane coating may coat a portion of the inner surface of the covered pores in the region of the cover. Alternatively, the polyurethane coating may extend for a distance into some of the pores, forming reinforcements, with the reinforcements forming openings that provide a passage for sorbing water into the pores or desorbing water from the pores.
For alternative partial coatings of the microporous zeolite mineral, the coating may 5 penetrate a slight distance, for example between 0.2 pm and 500 pm, preferably between 1 pm and 150 pm and most preferred between 10 pm and 100 pm, into the surface pores and thus may interfere with the pores in a form-locking manner;
this may increase the hold of the coating on the microporous zeolite mineral particles and at the same time the overall stability and hardness of the microporous zeolite
In addition, since the microporous zeolite mineral particles may be partly coated with the polyurethane coating, natural abrasion and wear of the microporous zeolite mineral during use may be reduced, since the polyurethane coating may provide for a harder and thus protective surface compared with that of uncoated microporous zeolite mineral particles. It may also be advantageous that the Mohs hardness of polyurethane coating can be chosen to be higher or much higher than the Mohs hardness of the microporous zeolite mineral particles. It may be thus beneficial that the Mohs hardness of the polyurethane coating is at least one Mohs unit higher than the Mohs hardness of the selected microporous zeolite mineral particles.
The gaps in the coating of the inventive infill material may result during the manufacture of the infill material, since during the mixing, e.g., in a flow reactor or a batch reactor or a tumbler, the microporous zeolite mineral particles and a liquid polyurethane reaction mixture are mixed and while they are being mixed a solidification reaction is initiated. During the mixing and while the solidification takes place, the microporous zeolite mineral particles may physically touch and interact with each other, thereby causing collision defects such as gaps in the coating and leaving the surface of the microporous zeolite particles partly uncovered.
Thus, water may still be absorbed and released by the microporous zeolite mineral particles in those areas in which the pores of the microporous zeolite minerals are not covered by the polyurethane coating.
It is further envisaged for this embodiment that the polyurethane coating may extend over some of the pores, forming respective covers of the pore openings, wherein the polyurethane coating may coat a portion of the inner surface of the covered pores in the region of the cover. Alternatively, the polyurethane coating may extend for a distance into some of the pores, forming reinforcements, with the reinforcements forming openings that provide a passage for sorbing water into the pores or desorbing water from the pores.
For alternative partial coatings of the microporous zeolite mineral, the coating may 5 penetrate a slight distance, for example between 0.2 pm and 500 pm, preferably between 1 pm and 150 pm and most preferred between 10 pm and 100 pm, into the surface pores and thus may interfere with the pores in a form-locking manner;
this may increase the hold of the coating on the microporous zeolite mineral particles and at the same time the overall stability and hardness of the microporous zeolite
10 mineral particles may be increased.
Further, since the infill material is preferably produced by mixing the microporous zeolite mineral particles with a liquid polyurethane reaction mixture and initializing the solidification reaction during the mixing, the microporous zeolite mineral particles may have substantially the same amount of their outer surface covered by the coating relative to the total outer surface. Substantially the same amount means that the outer surface of each of the partly coated microporous zeolite mineral particles may be coated between 20% and 99%, preferably between 50% and 98% and most preferred between 70% and 99% with the polyurethane coating. Further, since the outer surface of each of the partly coated microporous zeolite mineral particles may, with the exception of the gaps, be essentially fully coated, fine dusts may be bound.
The polyurethane coating of the microporous zeolite mineral particles may be based on a liquid polyurethane reaction mixture, which may be a dispersion or solution, comprising ¨ at least one isocyanic prepolymer with a totally blocked isocyanic functionality;
¨ a hydroxyl component, wherein the hydroxyl component is selected from the group of polyether polyol or polyester polyol; and ¨ at least one catalyst selected from the group consisting of linear or cyclic tertiary amines such as triethylenediamine or 1,4-Diazabicyclo[2.2.2]octane; cyclic amines such as 1,8-
Further, since the infill material is preferably produced by mixing the microporous zeolite mineral particles with a liquid polyurethane reaction mixture and initializing the solidification reaction during the mixing, the microporous zeolite mineral particles may have substantially the same amount of their outer surface covered by the coating relative to the total outer surface. Substantially the same amount means that the outer surface of each of the partly coated microporous zeolite mineral particles may be coated between 20% and 99%, preferably between 50% and 98% and most preferred between 70% and 99% with the polyurethane coating. Further, since the outer surface of each of the partly coated microporous zeolite mineral particles may, with the exception of the gaps, be essentially fully coated, fine dusts may be bound.
The polyurethane coating of the microporous zeolite mineral particles may be based on a liquid polyurethane reaction mixture, which may be a dispersion or solution, comprising ¨ at least one isocyanic prepolymer with a totally blocked isocyanic functionality;
¨ a hydroxyl component, wherein the hydroxyl component is selected from the group of polyether polyol or polyester polyol; and ¨ at least one catalyst selected from the group consisting of linear or cyclic tertiary amines such as triethylenediamine or 1,4-Diazabicyclo[2.2.2]octane; cyclic amines such as 1,8-
11 Diazabicyclo(5.4.0)undec-7-ene (DBU); and inorganic compounds such as sodium hydroxide (NaOH), chromium(III) oxide and zinc oxide (Zn0).
The use of an above-described liquid polyurethane reaction mixture may be advantageous, because it is a reaction mixture that can be solidified or cured (e.g., by cross-linking) under heat and/or by adding water. Therefore, the zeolite mineral particles and the liquid polyurethane reaction mixture may be mixed and solidified simultaneously in a batch reactor, a continuous reactor or a tumbler, resulting in the partial polyurethane coating or the coating with gaps. Further, the resulting polyurethane coating may be a waterborne polyurethane coating.
Alternatively, the polyurethane coating of the microporous zeolite mineral particles may be based on a liquid polyurethane reaction mixture comprising i. an NCO-terminal polymer, one or more components selected from a pre-polymer, a polymeric isocyanate, an oligomeric isocyanate or a monomer, such as a. aromatic diisocyanate of the group of toluene diisocyanate and/or methylene-2,2-diisocyanate; or b. aliphatic diisocyanate of the group hexamethylene diisocyanate, isophorone diisocyanate and/or 1,4-cyclohexyl diisocyanate; and ii. a hydroxyl component, wherein the hydroxyl component is selected from the group of polyether polyol or polyester polyol.
The use of an above-described liquid polyurethane reaction mixture may be .. advantageous, because it is a reaction mixture that may be solidified or cured (e.g., by cross-linking) by adding a catalyst, e.g., a secondary amine catalyst; a tertiary amine catalyst, such as triethylenediamine or, e.g., 1,4-Diazabicyclo[2.2.2]octane;
cyclic amines such as 1,8-Diazabicyclo(5.4.0)undec-7-ene (DBU) or a metal organic catalyst; and water. Therefore, the zeolite mineral particles and the liquid polyurethane reaction mixture may be mixed and solidified simultaneously in a controlled manner in a batch or continuous reactor, resulting in the partial polyurethane coating or the coating with holes.
The use of an above-described liquid polyurethane reaction mixture may be advantageous, because it is a reaction mixture that can be solidified or cured (e.g., by cross-linking) under heat and/or by adding water. Therefore, the zeolite mineral particles and the liquid polyurethane reaction mixture may be mixed and solidified simultaneously in a batch reactor, a continuous reactor or a tumbler, resulting in the partial polyurethane coating or the coating with gaps. Further, the resulting polyurethane coating may be a waterborne polyurethane coating.
Alternatively, the polyurethane coating of the microporous zeolite mineral particles may be based on a liquid polyurethane reaction mixture comprising i. an NCO-terminal polymer, one or more components selected from a pre-polymer, a polymeric isocyanate, an oligomeric isocyanate or a monomer, such as a. aromatic diisocyanate of the group of toluene diisocyanate and/or methylene-2,2-diisocyanate; or b. aliphatic diisocyanate of the group hexamethylene diisocyanate, isophorone diisocyanate and/or 1,4-cyclohexyl diisocyanate; and ii. a hydroxyl component, wherein the hydroxyl component is selected from the group of polyether polyol or polyester polyol.
The use of an above-described liquid polyurethane reaction mixture may be .. advantageous, because it is a reaction mixture that may be solidified or cured (e.g., by cross-linking) by adding a catalyst, e.g., a secondary amine catalyst; a tertiary amine catalyst, such as triethylenediamine or, e.g., 1,4-Diazabicyclo[2.2.2]octane;
cyclic amines such as 1,8-Diazabicyclo(5.4.0)undec-7-ene (DBU) or a metal organic catalyst; and water. Therefore, the zeolite mineral particles and the liquid polyurethane reaction mixture may be mixed and solidified simultaneously in a controlled manner in a batch or continuous reactor, resulting in the partial polyurethane coating or the coating with holes.
12 In one embodiment of the invention, the polyurethane coating of the microporous zeolite mineral particles is a reaction product of a liquid polyurethane reaction mixture comprising ¨ 0.1 ¨ 80 wt.% of an NCO-terminal prepolymer, ¨ 0.001 ¨ 0.5 wt.% of 1,8-diazabicyclo(5.4.0)undec-7-ene (DBU) and ¨ 0.001 ¨ 20.0 wt.% water, and optionally at least one further component selected from the group consisting of = 0.001 ¨ 30.0 wt.% colored pigments, = 0.001 ¨3.0 wt.% copper(II) sulfate, = 0.05 ¨ 60 wt.% flame retardants, = 0.01 ¨ 1.0 wt.% U.V. absorbers, = 0.01 ¨ 60 wt.% filler and = 0.01 ¨ 1.0 wt.% rheology additive, wherein the amounts by weight add up to 100 wt.% and the amounts by weight are based on the total weight of the polyurethane coating.
The NCO-terminal prepolymer of this embodiment may be an NCO-terminal isocyanic prepolymer, which is a (oligomeric) urethane having at least one free isocyanate group, and which may be obtained by reacting polyisocyanates with polyols. The NCO-terminal prepolymer of this embodiment may have an NCO-content of 5.5% to 11.5%, preferably an NCO-content of 6.5% to 10.5% or most preferred an NCO-content of 8.0% to 9.0%. Further, the NCO-terminal prepolymer of this embodiment may have a curing time in air of 35 hours to 45 hours. A
suitable prepolymer is known under the trade name P2440 (Polytex Sportbelage Produktions GmbH). The prepolymer may be mixed with the microporous zeolite particles in a batch or continuous reactor, and the solidification reaction may be initialized (during the mixing) by adding water and/or a catalyst. The prepolymer may be advantageously used for a moisture-curing 1K system, in which the reaction (formation of urea groups) may be started with water and/or a catalyst, here 1,8-diazabicyclo(5.4.0)undec-7-ene (DBU). DBU may be particularly useful as a catalyst for a 1K system, as it may be soluble in water. In addition, the curing rate of the polyurethane formation may be controlled by the addition of the DBU-water mixture,
The NCO-terminal prepolymer of this embodiment may be an NCO-terminal isocyanic prepolymer, which is a (oligomeric) urethane having at least one free isocyanate group, and which may be obtained by reacting polyisocyanates with polyols. The NCO-terminal prepolymer of this embodiment may have an NCO-content of 5.5% to 11.5%, preferably an NCO-content of 6.5% to 10.5% or most preferred an NCO-content of 8.0% to 9.0%. Further, the NCO-terminal prepolymer of this embodiment may have a curing time in air of 35 hours to 45 hours. A
suitable prepolymer is known under the trade name P2440 (Polytex Sportbelage Produktions GmbH). The prepolymer may be mixed with the microporous zeolite particles in a batch or continuous reactor, and the solidification reaction may be initialized (during the mixing) by adding water and/or a catalyst. The prepolymer may be advantageously used for a moisture-curing 1K system, in which the reaction (formation of urea groups) may be started with water and/or a catalyst, here 1,8-diazabicyclo(5.4.0)undec-7-ene (DBU). DBU may be particularly useful as a catalyst for a 1K system, as it may be soluble in water. In addition, the curing rate of the polyurethane formation may be controlled by the addition of the DBU-water mixture,
13 time and temperature so that, for example, the polyurethane coating may only penetrate the pores to a certain depth or the curing takes place very quickly.
Correspondingly, curing may also be achieved such that the individual coated zeolite particles do not stick to each other.
The polyurethane coating of the microporous zeolite mineral particles may further comprise a rheology additive that is adapted to induce a thixotropic flow behavior in one of the above-described liquid polyurethane reaction mixtures.
Adding a rheology additive with thixotropic capabilities may be advantageous in order to achieve a controllable viscosity-increasing thixotropic flow behavior (i.e., liquid or fluid) of the polyurethane coating while applying it (e.g., by mixing the liquid polyurethane reaction mixture with the microporous zeolite mineral particles, to the surface of the microporous zeolite mineral particles) in order to control or reduce the depth of penetration of the liquid polyurethane reaction mixture into the pores contained in the surfaces of the microporous zeolite mineral particles.
Suitable rheology additives may be, e.g., fumed silica (e.g., synthetic, hydrophobic, amorphous silica), also known as pyrogenic silica, made from flame pyrolysis of silicon tetrachloride or from quartz sand vaporized in a 3000 C electric arc, hydrophobic fumed silica, bentonite, acrylates, or a combination of the aforementioned additives.
It may be further beneficial to charge at least some of the microporous zeolite mineral particles with a salt solution.
Charging the microporous zeolite mineral particles with salt ions may allow for an increased water adsorption and/or water desorption effect.
This incorporation of salt into the microporous zeolite mineral particles allows a synergy to operate between the following properties: the adsorption, absorption and release of water of the microporous zeolite mineral particles, and the ability to lower the freezing temperature of the water. Actually, in the presence of humidity, the
Correspondingly, curing may also be achieved such that the individual coated zeolite particles do not stick to each other.
The polyurethane coating of the microporous zeolite mineral particles may further comprise a rheology additive that is adapted to induce a thixotropic flow behavior in one of the above-described liquid polyurethane reaction mixtures.
Adding a rheology additive with thixotropic capabilities may be advantageous in order to achieve a controllable viscosity-increasing thixotropic flow behavior (i.e., liquid or fluid) of the polyurethane coating while applying it (e.g., by mixing the liquid polyurethane reaction mixture with the microporous zeolite mineral particles, to the surface of the microporous zeolite mineral particles) in order to control or reduce the depth of penetration of the liquid polyurethane reaction mixture into the pores contained in the surfaces of the microporous zeolite mineral particles.
Suitable rheology additives may be, e.g., fumed silica (e.g., synthetic, hydrophobic, amorphous silica), also known as pyrogenic silica, made from flame pyrolysis of silicon tetrachloride or from quartz sand vaporized in a 3000 C electric arc, hydrophobic fumed silica, bentonite, acrylates, or a combination of the aforementioned additives.
It may be further beneficial to charge at least some of the microporous zeolite mineral particles with a salt solution.
Charging the microporous zeolite mineral particles with salt ions may allow for an increased water adsorption and/or water desorption effect.
This incorporation of salt into the microporous zeolite mineral particles allows a synergy to operate between the following properties: the adsorption, absorption and release of water of the microporous zeolite mineral particles, and the ability to lower the freezing temperature of the water. Actually, in the presence of humidity, the
14 microporous mineral particle may be in a position to adsorb and/or absorb this humidity in order to prevent, on the one hand, the surface formation of a layer of slippery frost, in the case of a negative temperature, and on the other hand, the agglomeration of the turf infills.
In the context of using the microporous mineral particles on outside artificial turf surfaces that are subjected to severe heat, the coated rubber and coated cork particles in combination with the microporous mineral particles, which are loaded with salt and water, may allow further increased release of the water and the maintenance of relative humidity at the surface of said turf. Thus, on a turf surface subjected to severe heat, when it is refreshed by watering, the microporous mineral loaded with salt adsorbs and/or absorbs the water and then continuously releases those water molecules by desorption. This continuous release of the water by the microporous mineral prevents rapid evaporation of the water after the surface is watered and allows a lower than ambient temperature to be maintained at the level of the field surface. Said microporous mineral loaded with salt thus further reduces the amount of watering usually necessary to refresh a turf surface.
In a further aspect, the invention relates to turf infill, as described above, for an artificial turf comprising an artificial turf carpet, wherein the artificial turf carpet comprises multiple artificial turf fiber tufts, and wherein the turf infill is configured for scattering between the multiple artificial turf fiber tufts of the artificial turf.
In a further aspect, the invention relates to an artificial turf system comprising an artificial turf, wherein the artificial turf comprises an artificial turf carpet, wherein the artificial turf carpet comprises multiple artificial turf fiber tufts, and a turf infill, as described above. The turf infill may be scattered, distributed or brushed between the multiple artificial turf fiber tufts of the artificial turf.
It is understood that one or more of the aforementioned embodiments of the invention may be combined as long as the combined embodiments are not mutually exclusive.
Below, the following embodiments of the invention are explained in greater detail, by way of example only, making reference to the drawings, in which Fig. 1 illustrates an example of artificial turf with an artificial turf carpet and 5 turf infill scattered between the artificial turf fiber tufts;
Fig. 2 shows a detail from Fig. 1, where the alignment of cork particles and rubber particles is enlarged;
Fig. 3 illustrates the coated cork particles and rubber particles in sectional views;
10 Fig. 4 illustrates the coated cork particles and rubber particles in sectional views, wherein the coating of the cork particles contains fillers and the coating of the rubber granules comprises two layers;
Fig. 5 shows a turf infill comprising coated cork particles, coated rubber particles and microporous zeolite particles;
In the context of using the microporous mineral particles on outside artificial turf surfaces that are subjected to severe heat, the coated rubber and coated cork particles in combination with the microporous mineral particles, which are loaded with salt and water, may allow further increased release of the water and the maintenance of relative humidity at the surface of said turf. Thus, on a turf surface subjected to severe heat, when it is refreshed by watering, the microporous mineral loaded with salt adsorbs and/or absorbs the water and then continuously releases those water molecules by desorption. This continuous release of the water by the microporous mineral prevents rapid evaporation of the water after the surface is watered and allows a lower than ambient temperature to be maintained at the level of the field surface. Said microporous mineral loaded with salt thus further reduces the amount of watering usually necessary to refresh a turf surface.
In a further aspect, the invention relates to turf infill, as described above, for an artificial turf comprising an artificial turf carpet, wherein the artificial turf carpet comprises multiple artificial turf fiber tufts, and wherein the turf infill is configured for scattering between the multiple artificial turf fiber tufts of the artificial turf.
In a further aspect, the invention relates to an artificial turf system comprising an artificial turf, wherein the artificial turf comprises an artificial turf carpet, wherein the artificial turf carpet comprises multiple artificial turf fiber tufts, and a turf infill, as described above. The turf infill may be scattered, distributed or brushed between the multiple artificial turf fiber tufts of the artificial turf.
It is understood that one or more of the aforementioned embodiments of the invention may be combined as long as the combined embodiments are not mutually exclusive.
Below, the following embodiments of the invention are explained in greater detail, by way of example only, making reference to the drawings, in which Fig. 1 illustrates an example of artificial turf with an artificial turf carpet and 5 turf infill scattered between the artificial turf fiber tufts;
Fig. 2 shows a detail from Fig. 1, where the alignment of cork particles and rubber particles is enlarged;
Fig. 3 illustrates the coated cork particles and rubber particles in sectional views;
10 Fig. 4 illustrates the coated cork particles and rubber particles in sectional views, wherein the coating of the cork particles contains fillers and the coating of the rubber granules comprises two layers;
Fig. 5 shows a turf infill comprising coated cork particles, coated rubber particles and microporous zeolite particles;
15 Fig. 6 illustrates a sectional view of a microporous zeolite mineral particle, which is partially coated with a polyurethane coating;
Fig. 7 illustrates a section of the sectional view of Fig. 6; and Fig. 8 illustrates a partially coated microporous zeolite mineral particle.
Like-numbered elements in these figures either are equivalent elements or perform the same function. Elements that have been discussed previously will not necessarily be discussed in later figures if the function is equivalent.
In Fig. 1, an artificial turf 600 with artificial turf carpet 500 is shown.
The artificial turf carpet 500 contains a backing 502. The artificial turf carpet 500 is a tufted artificial turf carpet, which is formed by artificial turf fiber tufts 504 that are tufted into the backing 502. The artificial turf fiber tufts 504 are tufted in rows. There is row spacing 506 between adjacent rows of tufts. The artificial turf fiber tufts 504 also extend a distance above the backing 502. The distance that the fibers 504 extend above the backing 502 is the pile height 508. In Fig. 1, it can be further seen that the artificial turf carpet 500 has been installed by placing or attaching it to the ground 510 or to a floor. As can be further seen, the turf infill 100 has been spread out on the surface
Fig. 7 illustrates a section of the sectional view of Fig. 6; and Fig. 8 illustrates a partially coated microporous zeolite mineral particle.
Like-numbered elements in these figures either are equivalent elements or perform the same function. Elements that have been discussed previously will not necessarily be discussed in later figures if the function is equivalent.
In Fig. 1, an artificial turf 600 with artificial turf carpet 500 is shown.
The artificial turf carpet 500 contains a backing 502. The artificial turf carpet 500 is a tufted artificial turf carpet, which is formed by artificial turf fiber tufts 504 that are tufted into the backing 502. The artificial turf fiber tufts 504 are tufted in rows. There is row spacing 506 between adjacent rows of tufts. The artificial turf fiber tufts 504 also extend a distance above the backing 502. The distance that the fibers 504 extend above the backing 502 is the pile height 508. In Fig. 1, it can be further seen that the artificial turf carpet 500 has been installed by placing or attaching it to the ground 510 or to a floor. As can be further seen, the turf infill 100 has been spread out on the surface
16 and distributed between the artificial turf fiber tufts 504. The turf infill 100 comprises coated cork particles (here granules) and coated rubber particles (here granules).
In Fig. 2 a detail from Fig. 1 is shown to visualize the turf infill comprising cork particles 200, wherein the cork particles 200 are coated with a polymer and/or resin component, and rubber particles 300, wherein the rubber particles 300 are coated with a polymer and/or resin component. The cork particles 200 and the rubber particles 300 both have a coating, which may, e.g., have a higher coefficient of friction than rubber or cork by itself or may be slightly sticky. The coating may slow the segregation (unmixing) over time due to different weights or sizes of the different granules. In order to obtain an optimal weight distribution of the coated cork particles 200 and the coated rubber particles 300, the weight percentage ratio may be chosen to be between 1 : 4 and 1 : 8.
In Fig. 3 the coated cork particles 200 and the coated rubber particles 300 of the turf infill are depicted. The coating 202 of the cork particles 200 is manufactured from a polymer and/or resin component, which may be polyurethane or polyvinyl butyral.
The coating 302 of the rubber particles 300 is also manufactured from a polymer and/or resin component, which may be polyurethane or polyvinyl butyral.
Fig. 4 depicts the coated cork particles 200 and the coated rubber particles 300 of the turf infill. As shown, the coating 202 of the cork particles 200 may comprise fillers, here barium sulphate particles 204 and calcium carbonate particles 205. It shall be understood that it is also feasible that either only barium sulphate particles 204 or only calcium carbonate particles 205 may be used as fillers. The use of both described fillers can be advantageous, as these fillers may be able to increase the weight of the coating 202 and may thus increase the overall poured density of the coated cork particles 200. As further shown, the coating 302 of the rubber particles 300 may be comprised of two layers, an inner layer 302a and an outer layer 302b.
The double-layer coating may prevent possibly health-affecting substances from being released by the rubber particles 300.
In Fig. 2 a detail from Fig. 1 is shown to visualize the turf infill comprising cork particles 200, wherein the cork particles 200 are coated with a polymer and/or resin component, and rubber particles 300, wherein the rubber particles 300 are coated with a polymer and/or resin component. The cork particles 200 and the rubber particles 300 both have a coating, which may, e.g., have a higher coefficient of friction than rubber or cork by itself or may be slightly sticky. The coating may slow the segregation (unmixing) over time due to different weights or sizes of the different granules. In order to obtain an optimal weight distribution of the coated cork particles 200 and the coated rubber particles 300, the weight percentage ratio may be chosen to be between 1 : 4 and 1 : 8.
In Fig. 3 the coated cork particles 200 and the coated rubber particles 300 of the turf infill are depicted. The coating 202 of the cork particles 200 is manufactured from a polymer and/or resin component, which may be polyurethane or polyvinyl butyral.
The coating 302 of the rubber particles 300 is also manufactured from a polymer and/or resin component, which may be polyurethane or polyvinyl butyral.
Fig. 4 depicts the coated cork particles 200 and the coated rubber particles 300 of the turf infill. As shown, the coating 202 of the cork particles 200 may comprise fillers, here barium sulphate particles 204 and calcium carbonate particles 205. It shall be understood that it is also feasible that either only barium sulphate particles 204 or only calcium carbonate particles 205 may be used as fillers. The use of both described fillers can be advantageous, as these fillers may be able to increase the weight of the coating 202 and may thus increase the overall poured density of the coated cork particles 200. As further shown, the coating 302 of the rubber particles 300 may be comprised of two layers, an inner layer 302a and an outer layer 302b.
The double-layer coating may prevent possibly health-affecting substances from being released by the rubber particles 300.
17 Fig. 5 depicts a turf infill 100 comprising microporous zeolite mineral particles 400;
cork particles 200, wherein the cork particles 200 are coated with a polymer and/or resin component; and rubber particles 300, wherein the rubber particles 300 are coated with a polymer and/or resin component. The microporous zeolite mineral particles 400 may be uncoated or partially coated, as depicted in Figures 6 to 8.
Fig. 6 shows a microporous zeolite mineral particle after it has been partially coated with a polyurethane coating 420 and may be used as part of an infill material.
As can be seen, at least some parts of the surface of the coated microporous zeolite mineral particle 400 may not be covered by the polyurethane coating 420. In Fig. 6, a dotted circle is also indicated, the schematic content of which is enlarged in Fig. 7.
As shown in the enlarged sectional view in Fig. 7, the microporous zeolite mineral particle 400, which contains pores 411, has been partially coated with a polyurethane coating 420. The polyurethane coating 420 may be formed by providing microporous zeolite mineral particles 400 and a liquid polyurethane reaction mixture in a batch reactor, tumbler or continuous reactor.
Simultaneous mixing and initialization of the solidification reaction may lead to the desired partial coating of the polyurethane coating 420 on the surface of the microporous zeolite mineral particle 400. The partial coating may result from microporous zeolite mineral particles 400 colliding while being mixed with the initialized liquid polyurethane reaction mixture. Since the initialization of the solidification reaction may take place simultaneously, uncovered spaces (e.g., gaps or holes), created by collisions, may remain on the surface of the microporous zeolite mineral particles 400.
Further, as shown in Fig. 7, the polyurethane coating 420 may coat a portion of the inner surface of the microporous zeolite mineral particle 400 in the region of the cover.
The coating 420 may penetrate with a slight distance, for example between 0.2 pm and 500 pm, preferably between 1 pm and 150 pm and most preferred between 10 pm and 100 pm, into the surface pores 411 and thus may interfere with the pores 411 in a form-locking manner; this will increase the hold of the coating on the microporous zeolite mineral particle 400 and at the same time the overall stability and hardness of the microporous zeolite mineral particle 400 may be increased.
Further, since the partially coated microporous zeolite mineral particle 400 is
cork particles 200, wherein the cork particles 200 are coated with a polymer and/or resin component; and rubber particles 300, wherein the rubber particles 300 are coated with a polymer and/or resin component. The microporous zeolite mineral particles 400 may be uncoated or partially coated, as depicted in Figures 6 to 8.
Fig. 6 shows a microporous zeolite mineral particle after it has been partially coated with a polyurethane coating 420 and may be used as part of an infill material.
As can be seen, at least some parts of the surface of the coated microporous zeolite mineral particle 400 may not be covered by the polyurethane coating 420. In Fig. 6, a dotted circle is also indicated, the schematic content of which is enlarged in Fig. 7.
As shown in the enlarged sectional view in Fig. 7, the microporous zeolite mineral particle 400, which contains pores 411, has been partially coated with a polyurethane coating 420. The polyurethane coating 420 may be formed by providing microporous zeolite mineral particles 400 and a liquid polyurethane reaction mixture in a batch reactor, tumbler or continuous reactor.
Simultaneous mixing and initialization of the solidification reaction may lead to the desired partial coating of the polyurethane coating 420 on the surface of the microporous zeolite mineral particle 400. The partial coating may result from microporous zeolite mineral particles 400 colliding while being mixed with the initialized liquid polyurethane reaction mixture. Since the initialization of the solidification reaction may take place simultaneously, uncovered spaces (e.g., gaps or holes), created by collisions, may remain on the surface of the microporous zeolite mineral particles 400.
Further, as shown in Fig. 7, the polyurethane coating 420 may coat a portion of the inner surface of the microporous zeolite mineral particle 400 in the region of the cover.
The coating 420 may penetrate with a slight distance, for example between 0.2 pm and 500 pm, preferably between 1 pm and 150 pm and most preferred between 10 pm and 100 pm, into the surface pores 411 and thus may interfere with the pores 411 in a form-locking manner; this will increase the hold of the coating on the microporous zeolite mineral particle 400 and at the same time the overall stability and hardness of the microporous zeolite mineral particle 400 may be increased.
Further, since the partially coated microporous zeolite mineral particle 400 is
18 preferably produced by mixing the microporous zeolite mineral particles with a liquid polyurethane reaction mixture and initializing the solidification reaction during the mixing, the microporous zeolite mineral particles may have substantially the same amount of their outer surface covered by the coating relative to the total outer surface. Substantially the same amount means that the outer surface of each microporous zeolite mineral particle is covered between 20% and 99%, preferably between 50% and 98% or most preferred between 70% and 99%, with the polyurethane coating 420. Since the outer surface of each microporous zeolite mineral particle 400 may, with the exception of the gaps, be essentially fully coated, fine dusts may be bound. The polyurethane coating 420 may comprise a rheology additive. The rheology additive may be added in order to achieve thixotropic flow behavior of the liquid polyurethane reaction mixture during mixing of the liquid polyurethane reaction mixture with the microporous zeolite mineral particle 400.
Fig. 8 depicts a partly coated microporous zeolite mineral particle 400. The microporous zeolite mineral particle 400 has pores 411 that form openings on the outer surface of the microporous zeolite mineral particles 400. As shown, the outer surface of the microporous zeolite mineral particle 400 may be partly coated with a polyurethane coating, wherein the coating extends over most of the pores 411, thereby forming covers over the openings. The polyurethane coating 420 may have been formed by providing a plurality of microporous zeolite minerals particles and a liquid polyurethane reaction mixture in a batch reactor, tumbler or continuous reactor. The microporous zeolite mineral particles 400 may be mixed with a liquid polyurethane reaction mixture (here comprising 0.1 ¨80 wt.% of an NCO-terminal prepolymer and optionally at least one further component selected from the group consisting of 0.001 wt.% to 30.0 wt.% colored pigments, 0.001 wt.% to 3.0 wt.%
copper(II) sulfate, 0.05 wt.% to 60 wt.% flame retardants, 0.01 wt.% to 1.0 wt.% U.V.
absorbers, 0.01 wt.% to 60 wt.% filler and 0.01 wt.% to 1.0 wt.% rheology additive) and the solidification reaction initialized during the mixing by adding a catalyst and water (here comprising 0.001 wt.% to 0.5 wt.% of 1,8-diazabicyclo(5.4.0)undec-ene (DBU) and 0.001 wt.% to 20.0 wt.% water). Simultaneous mixing and initialization of the solidification reaction may lead to the desired partial coating of the polyurethane coating 420 on the surface of the microporous zeolite mineral
Fig. 8 depicts a partly coated microporous zeolite mineral particle 400. The microporous zeolite mineral particle 400 has pores 411 that form openings on the outer surface of the microporous zeolite mineral particles 400. As shown, the outer surface of the microporous zeolite mineral particle 400 may be partly coated with a polyurethane coating, wherein the coating extends over most of the pores 411, thereby forming covers over the openings. The polyurethane coating 420 may have been formed by providing a plurality of microporous zeolite minerals particles and a liquid polyurethane reaction mixture in a batch reactor, tumbler or continuous reactor. The microporous zeolite mineral particles 400 may be mixed with a liquid polyurethane reaction mixture (here comprising 0.1 ¨80 wt.% of an NCO-terminal prepolymer and optionally at least one further component selected from the group consisting of 0.001 wt.% to 30.0 wt.% colored pigments, 0.001 wt.% to 3.0 wt.%
copper(II) sulfate, 0.05 wt.% to 60 wt.% flame retardants, 0.01 wt.% to 1.0 wt.% U.V.
absorbers, 0.01 wt.% to 60 wt.% filler and 0.01 wt.% to 1.0 wt.% rheology additive) and the solidification reaction initialized during the mixing by adding a catalyst and water (here comprising 0.001 wt.% to 0.5 wt.% of 1,8-diazabicyclo(5.4.0)undec-ene (DBU) and 0.001 wt.% to 20.0 wt.% water). Simultaneous mixing and initialization of the solidification reaction may lead to the desired partial coating of the polyurethane coating 420 on the surface of the microporous zeolite mineral
19 particle 400. The partial coating may result from collisions of microporous zeolite mineral particles 400 while being mixed with the initialized liquid polyurethane reaction mixture. Since the initialization of the solidification reaction may take place simultaneously, uncovered spaces (e.g., gaps or holes), created by collisions or by the formation of reinforcements, may remain on the surface of the microporous zeolite mineral particles 400. As indicated in Fig. 8, it may be feasible to cover 75%
to 99% of the outer surface of the microporous zeolite mineral particle 400 with a polyurethane coating 420.
List of Reference Numerals 100 turf infill 200 cork particles 202 coating of the cork particles 10 203 fillers comprised in the coating of the cork particles 204 barium sulphate particles 205 calcium carbonate particles 300 rubber particles 302 coating of the rubber particles 15 400 microporous zeolite mineral particles 411 microporous zeolite mineral particle pores 420 polyurethane coating of microporous zeolite mineral particles 430 cover
to 99% of the outer surface of the microporous zeolite mineral particle 400 with a polyurethane coating 420.
List of Reference Numerals 100 turf infill 200 cork particles 202 coating of the cork particles 10 203 fillers comprised in the coating of the cork particles 204 barium sulphate particles 205 calcium carbonate particles 300 rubber particles 302 coating of the rubber particles 15 400 microporous zeolite mineral particles 411 microporous zeolite mineral particle pores 420 polyurethane coating of microporous zeolite mineral particles 430 cover
20 500 artificial turf carpet 502 backing 504 artificial turf fiber tufts 506 row spacing between adjacent rows of tufts 508 pile height 510 ground or floor 600 artificial turf
Claims (14)
1. Turf infill (100) comprising a mixture of - cork particles (200), wherein the cork particles (200) are coated with a polymer and/or resin component, and - rubber particles (300), wherein the rubber particles (300) are coated with a polymer and/or resin component.
2. Turf infill (100) according to claim 1, wherein the weight percentage ratio of the cork particles (200) to the rubber particles (300) is between 1 : 4 and 1 : 8, in particular between 1 : 5.5 and 1 : 6.5.
3. Turf infill (100) according to claim 1 or claim 2, wherein the infill is configured such that the - poured density of the coated cork particles is between any one of the following: 90 g/dm3 and 180 g/dm3, 100 g/dm3 and 150 g/dm3, and 125 g/dm3 and 135 g/dm3; and the - poured density of the coated rubber particles is between any one of the following: 400 g/dm3 and 650 g/dm3, 450 g/dm3 and 600 g/dm3, and 530 g/dm3 and 550 g/dm3.
4. Turf infill (100) according to one of claims 1 to 3, wherein the polymer and/or resin component of the coating (202; 302) of the cork particles (200) and/or rubber particles (300) is polyurethane (PU).
5. Turf infill (100) according to one of claims 1 to 3, wherein the polymer and/or resin component of the coating (202; 302) of the cork particles (200) and/or rubber particles (300) is polyvinyl butyral (PVB).
6. Turf infill (100) according to one of claims 1 to 5, wherein the coating (202) of the cork particles (200) comprises fillers (203), in particular barium sulphate (204), calcium carbonate (205), talc, quartz silica, silicates, oxides, hydro oxides, hollow glass spheres, organic fillers or a combination thereof.
7. Turf infill (100) according to one of claims 1 to 6, wherein the coating (202) of the cork particles (200) and/or the coating (302) of the rubber particles (300) comprises particles selected from the group consisting of colored pigments, copper(II) sulfate particles, chrome particles, silver particles, chitosan particles or mixtures thereof.
8. Turf infill (100) according to any one of the preceding claims, wherein the layer thickness of the coating (202; 302) of the cork particles (200) and/or rubber particles (300) is between 0.5 pm and 0.75 mm.
9. Turf infill (100) according to any one of the preceding claims, wherein a size of the coated cork particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm; and wherein a size of the coated rubber particles is between any one of the following: 0.03 mm and 3.5 mm, and 0.3 mm and 2.5 mm.
10. Turf infill (100) according to one of claims 1 to 9, further comprising microporous zeolite mineral particles (400) having pores (411) that form openings on the outer surface of the microporous zeolite mineral particles (400), with a particle size between any one of the following: 0.5 mm and 3.5 mm, and 1.0 mm and 2.5 mm; wherein the weight percentage ratio of the microporous zeolite mineral particles (400) to the cork particles (200) and the rubber particles (300) is between 2 : 7 and 4 : 7, in particular between 2.5 :
and 3.5 : 7.
and 3.5 : 7.
11. Turf infill (100) according claim 10, wherein the outer surface of at least some of the microporous zeolite mineral particles (400) is partly coated with a polyurethane coating (420), wherein the coating extends over some of the pores (411), forming respective covers (430) of the openings, wherein the polyurethane coating (420) coats a portion of the inner surface of the covered pores (411) in the region of the cover (430) and wherein the microporous zeolite mineral particles (400) have the same amount of their outer surface coated by the coating (420) relative to the total outer surface.
12. Turf infill (100) according to claim 10 or claim 11, wherein at least some of the microporous zeolite mineral particles (400) are charged with a salt solution.
13. Turf infill (100) according to any of the preceding claims for use with an artificial turf (600) comprising an artificial turf carpet (500), wherein the artificial turf carpet comprises multiple artificial turf fiber tufts (504), and wherein the turf infill (100) is configured for scattering between the multiple artificial turf fiber tufts (504) of the artificial turf (600).
14. An artificial turf system, wherein the artificial turf system comprises - an artificial turf (600) with an artificial turf carpet (500), wherein the artificial turf carpet comprises multiple artificial turf fiber tufts (504);
and - a turf infill (100) according to one of claims 1 to 12.
and - a turf infill (100) according to one of claims 1 to 12.