CA2729718A1 - Antifungal compositions - Google Patents
Antifungal compositions Download PDFInfo
- Publication number
- CA2729718A1 CA2729718A1 CA 2729718 CA2729718A CA2729718A1 CA 2729718 A1 CA2729718 A1 CA 2729718A1 CA 2729718 CA2729718 CA 2729718 CA 2729718 A CA2729718 A CA 2729718A CA 2729718 A1 CA2729718 A1 CA 2729718A1
- Authority
- CA
- Canada
- Prior art keywords
- ions
- borate
- antifungal composition
- metal ions
- ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An antifungal composition includes a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions. For example, the ion-exchange type antimicrobial agent may be a zeolite and the metal ions may be magnesium ions and manganese ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance.
Description
TITLE
ANTIFUNGAL COMPOSITIONS
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefit of United States Provisional Application No_ 61/298,672, filed January 27, 2010, the disclosure of which is incorporated herein by reference.
BACKGROUND OF THE INVENTION
ANTIFUNGAL COMPOSITIONS
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefit of United States Provisional Application No_ 61/298,672, filed January 27, 2010, the disclosure of which is incorporated herein by reference.
BACKGROUND OF THE INVENTION
[0002] This invention relates in general to antifungal compositions, and in particular to antifungal compositions that can be added to provide mold resistance to building materials and other materials.
[00031 Mold problems can arise in interior living spaces- In the past 30 years as buildings have become better insulated and more energy efficient there has been an increase in mold problems due to trapped moisture. Building materials such as wood, insulation materials and wallboard used in building construction are susceptible to mold and fungal growth in moist environments or when exposed to wetting.
Fluffed cellulose fiber, shredded paper, low density fiberboard used as insulating materials and. nonwoven webs, such as paper, used to cover gypsum wallboard, are all prime growth media for fungi. Several species of mold and fungus that grow in these environments are toxic to humans. A number of health risks such as occupational asthma, rhinoconjunctivitis, hypersensitivity pneumonitis and organic dust toxic syndrome (ODTS), aspergillosis and histoplasma have been linked to antigens generated by fungi. Diseases associated with inhalation of fungal spores can include toxic pneumonitis, hypersensitivity pneumonitis, tremors, chronic fatigue syndrome, kidney failure, and cancer.
10004] The current mold resistant wallboard technology (DensArmor Georgia Pacific) consists of a fiberglass based product that has limitations in implementation due to its cost and its density. The shell of DensArmor is composed of fiberglass.
This makes it weigh more than regular wallboard which uses paper as the shell.
An ideal mold resistant drywall would be of similar construction as standard drywall but be able to resist mold growth. Ecology Coatings, Inc. has developed a coating for drywall that needs to be cured by exposure to UV light.
[0005] It would be desirable to provide an antifungal composition that confers mold resistance to building materials such as loose fill and dense packed cellulose insulation, wallboards and to other materials.
SUMMARY OF THE INVENTION
[0006] In one embodiment, an antifungal composition comprises a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions.
The combination of the metal ions and the borate provide a synergistic effect in fungal resistance.
[00071 In another embodiment, an antifungal composition comprises an ion-exchange type antimicrobial agent with borate ions and two or more different metal ions. The combination of the borate ions and the metal ions provide a synergistic effect in fungal resistance.
[0008] A fungus resistant building material comprises a building. material susceptible to fungus growth and an antifungal composition comprising a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance.
[0009] Various aspects of this invention will become apparent to those skilled in the art from the following detailed description of the preferred embodiments.
BRIEF DESCRIPTION OF THE DRAWING
[00101 Figure I is a bar graph showing the week at which mold growth was first observed based on paper handsheet compositions in testing done with different additives-DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[00111 The present development relates to an antifungal composition that comprises a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance. The antifungal composition can be effective in providing resistance to one or more types of fungus, such as molds, yeasts, mushrooms and other eukaryotic organisms.
[0012] Any suitable borate fungicide can. be used in the composition. Borate fungicides are well known in the industry and include, for example, boric acid, sodium borate, borax, sodium tetraborate decahydrate, sodium tetraborate pentahydrate, disodium octaborate tetrahydrate, disodium octoborate, sodium metaborate, sodium perborate, sodium perborate tetrabydrate, sodium pentaborate decahydrate, and the like. In apart icular embodiment, the borate fungicide is sodium perborate tetrahydratc, which is available commercially as Polybor from U.S. Borax Inc., Valencia, California-[00131 The ion-exchange type antimicrobial agent can be any suitable type.
These agents typically comprise an inorganic ion-exchange carrier and one or more antimicrobial metals and/or metal ions, most preferably one or more antimicrobial metal ions. The inorganic ion-exchange carrier is preferably an ion-exchange type ceramic particle wherein antimicrobial metal ions have been exchanged (replaced) for other non-antimicrobially effective ions in the ceramic particles or a combination of the foregoing with an antimicrobial metal salt. Suitable ceramic particles include, but are not limited to zeolites, hydroxyapatite, zirconium phosphates and other ion-exchange ceramics, and come in many forms and types, including natural and synthetic forms.
[00141 The term "zeolite" is used here in its generic sense and refers to crystalline inorganic molecular sieves such as aluminophophates, silicon aluminum phosphates, microporous borosilicates, titanosilicates and tatanioaluminosilicates, as well as rnieroporous aluminosilicates and their silica analogs, having a framework structure consisting of nanopores and interconnected cavities which can be occupied by ions and/or water molecules, both of which have considerable freedom of movement permitting ion exchange and reversible dehydration. In contrast to amorphous materials these crystalline structures contain regular arrays of intracrystalline pores (zianopores) and voids of uniform dimensions. A typical naturally occurring zeolite is the mineral clinoptilolite with formula (Ca, Na, l( 2.3AI3(AI,Si)2Si13O3fi 12(H2O). As used herein, "ion exchanged zeolite" refers-to a natural or synthetic zeolite that has' been modified by an ion exchange process to increase the content of one or more metal ions in the zeolite.
[0015] The ion-exchange type antimicrobial agent is modified by exchange with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance. For example, as described in the experiments below, it was discovered that the combination of magnesium ions and manganese ions and the borate provide a synergistic effect in fungal resistance. Using the ASTM D6523 Standard Test Method for Resistance to Growth of Mold it has been demonstrated that this combination is an unexpectedly effective mold inhibitor.
However, other combinations of ions may also provide such a synergistic effect.
[00161 The experiments below describe the use of silver and zinc ions as well as magnesium and manganese. Some other metal ions known for use in ion exchange materials include, but are not limited to, copper, gold, mercury, tin, lead, iron, cobalt, nickel, arsenic, antimony, bismuth, barium, cadmium, chromium and thallium.
[0017] In an alternative embodiment, instead of using a borate fungicide along with the ion-exchange type antimicrobial agent, the antifungal composition can comprise an ion-exchange type antimicrobial agent having borate ions in addition to the metal ions. Any suitable borate ions can be used.
[0018] Other embodiments of this technology could include a binder, such as nanocellulose or other natural or synthetic binder, to aid in incorporating and retaining the antifungal composition into or onto the material to which it is applied.
(00191 The antifungal composition can have any suitable effectiveness against fungi. In certain embodiments, the antifungal composition scores a 10 in the ASTM
D3273 test for mold resistance. Also, in certain embodiments, the antifungal composition is effective to prevent mold growth onset at least about 3 weeks according to mold resistance test ASTM D6523. Such testing is described in the experiments below.
[0020] The antifungal composition can be used in many different applications where it is desirable to prevent fungal growth. The antifungal composition may be applied as a coating or may be incorporated into a material. Such applications can involve applying the antifungal composition in or on many different materials-Such materials may include, for example, wood, paper, metal, plastic, glass, or fabric/textile. In certain embodiments, the antifungal composition is incorporated into or coated onto any number of inorganic materials, especially those employed in building construction, like wood, paper, fluffed cellulose fiber, fiberboard, cements, mortar, grout, plaster, and the like, or in the manufacture of building materials, such as ceramics and cements for tiles, In certain embodiments, the antifungal composition is used as a building material additive, for example, in wallboard of any type, more particularly in the paper cover of drywall or in cellulose insulation formulations - both loose fill and dense packed products.
[0021] The antifungal composition can be used in any amount suitable for providing fungal resistance. For example, the composition may be used in an amount of from about 1% to about 30% by weight of the material when used as an additive, or by weight of a coating when applied as a coating-[0022] Development. and Test of the Innovation [0023] The main goal of this innovation was to identify a zeolite formulation which would inhibit mold growth when incorporated into paper. The scope of work comprised two parts. Part I tested pre-screening of ion exchanged zeolite candidates for mold inhibition on paper handsheets. The best mold inhibitor candidates were chosen for a second round of tests, Part II. Combinations of two metals and metals with Polybor were utilized in making handsheets which were then tested for mold.
inhibition. Finally, a sample of "drywall paper" with the best performing zeolite was submitted to an ASTM lab in order to test its effectiveness under the ASTM
mold resistance test (ASTM D6523).
[0024] Part I.
[0025] The testing was performed in two stages. The first stage involved preparing a series of handsheets which incorporated a range of ceolite/metal compositions.
[0026], Handsheet Compositions Hand Sheet Mold Test Key:
Sheet Composition A Ag/OLIN
B Fe/CLIN
C Mg/CLIN
D Mn/CLIN
E Zn/CLIN
F Ti/CLIN (#3- normal pH, exchanged in ethanol, CLIN normal) G Ti/CLIN (#2- low pH, exchanged in water, CLIN damaged?) II Zn/50% exchange I Ag/FAU
J CLIN (unexchanged) K BLANK
L Polybor CLIN: clinoptilolite FAU: faujasite Polybor: spray-on boric acid compound [0027] Mold Test Results [0028] Inhibition of mold growth was conducted in Dr. Jody Jellison's lab at the University of Maine. Dr_ Jellison is an expert in mold microbiology and performs consulting work for private industry. The choice of mold species was recommended by her and Zeomatrix' experimental design was modified by her to best suit the' facilities available and her knowledge of best known practices. The test utilized four mold spores common to domestic environments.
[0029] The mold species used in this study are as follows:
Aspergillus niger ATCC 6275 - isolated from leather Aspergillus niger ATCC 9642 - isolated from wireless radio equipment, New South Wales, Australia Cladosporium minourae ATCC 52853 -isolated from rotting wood, Japan Penicillium funiculosum ATCC 11797 - isolated from mercury-treated fabric,.Maryland [0030] A cocktail of these organisms were prepared from individual cultures obtained from ATCC (American Type Culture Collection). Careful preparation of the cocktail required that each mold species be present at the same concentration (steps 1 through 4). This process required four weeks. Paper samples (5 each) were 4.0 cm diameter circles cut from handsheets and placed in a randomized fashion 4 at a time onto agar plates (step 5). Each plate was inoculated with mold spores by spraying with 10 mL of the spore cocktail (step 6). The plates were incubated at 25 C
in humid conditions for 4 weeks. The plates were photographed each week (step 8). The ability of the paper samples to inhibit mold growth nearby was determined by measuring zones of partial and total inhibition (step 9)"
1. Molds Grown on Potato Dextrose Agar (PDA) 2. Spores Collected Using Minimal Salts Solution 3. Spores Counted Using l-Iemocytometer 4. 105 Spores from Each Mold Added to Spore.Cocktail 5. Plates Assembled Using Minimal Salts Solution And Samples 6. 10 mL Spore Cocktail Sprayed onto Each Plate Using Minimal Salts Agar 7. Plates Incubated At 25 C In Humid Conditions for Four-Weeks 8. Plates Were Photographed Regularly 9. Zones of Total and Partial Inhibition Were Measured [0031] Results:
[0032] Zones of inhibition showed that handsbeets containing zeolites exchanged with silver, and magnesium in combination with boric acid were effective in preventing mold from growing near the paper samples. Samples containing silver, natural zeolite, zinc, and boric acid demonstrated some effectiveness at inhibiting mold growth on the paper samples.
[0033] Part II.
[0034] Part II of this research effort involved three different exchanged zeolites which exhibited mold inhibition in Part I - Ag, Mg and Zn- exchanged. The Ag-exchanged sample was used as a control and is not a good candidate for a commercial product. However, both the Mg and Zn samples were tested in the follow-on study.
[00351 Mold Study [0036] As before, zeolite samples were exchanged by Zeomatrix and handsheets incorporating these zeolites were prepared by the Process Development Center (PDC) at UM. The handsheets were divided up into samples as shown in Table 1 and submitted to Jody Jellison for incubation with the test mold spores. The mold testing was conducted for 8 weeks and the results are in Figure 1.
Table I. Handsheet Sample Compositions Hands-beet Sam 1e Number Exchanged Ions Composition A M Zn 1:1 B MnZn 1:1 C Mn 1:1 D MgMnZn 1:1:1 E Ag Control P No exchange Zeolite Control G MMn 1:1, 3.5% Polybor H MnZn. 1:1, 4.7% Pol bor I MgMn 1:1, 3.0% Pol bor J MgMnZn I- L 1, 4.1% Polybor K Ag 3.6% Polybor L No exchange 5.0% Polybor [0037] The exchanged zeolites in the preceding table were incorporated into handsheets in the amounts indicated (1:1, 300rng_300mg). The Polybor was applied as a spray-on solution at the various levels indicated. The Polybor is simply a boric acid solution comprised of boron, oxygen, and sodium.
[0038] Mold Test [0039] The mold test was conducted as previously described (Part I). The plates were prepared in a double blind study where the biology researchers were unaware of the different compositions of samples A-L. Different samples were randomly grouped.
on the 5 plates in sets of three in order to test 5 replicates of each composition. The results of the replicates are summarized in the table in Table 11-Table II. Summary of Initial Mold Growth for Replicate Samples.
Groai F tst ;" :weexr"I :~C X X X I X X X
--- ' x I_ x NOM AtwccX4ev-ovearmc ir typolu airu,eormo- rve kaes-Yimmoldgrna 0 f 0 0 O 3 I 0 3 1 2 3 4 3 HMIMw;l6ne, 0 0 0 0 3 -I 0 -3--~ 2 4-.-_.
gowdh21Wccr61 - -- - -= --I - -- -=-- =--- - ---- -- ' s- Wei, 0- I. 0 0 0 4 1 0 3 3 4 3 4 3 Acplir~tcsrilh=m ---~ -~ --0 __j---_p - - =-0-- q- 0 4--~ 3 - ~- - 4---,-` _ -4 - --- 3' ... ...: : ... .. . .
. I I
I , I
~aapt6ca~ac wfth,iol .0 .. ~.~_ 0- i 0 4 i 0 s 13 _4 19v'pyp~ at WeeK z ~.--[0040] Summary of Innovation Test [00411 The Polybor definitely had a positive effect on the mold resistance properties. The best overall performers (all replicates over eight weeks) were the ones containing either magnesium plus manganese, or silver, plus Polybor- However, the mg:mn plus polybor samples (I and G) were more resistant to mold growth onset than the Ag -- Polybor as shown in Figure 1. This composition (Mg:Mn + polybor) was selected for the drywall test panel. There was a definite synergistic effect of the two metals (Mg and Mn) in combination with Polybor. The result is non-obvious considering that the addition of zinc (MgMnZnP) did not inhibit mold growth more than no exchange at all.
[00421 The drywall panel was submitted to Accugen Laboratory in Illinois for the ASTM
D3273 test. This test showed that the MgMn Polybor treated drywall sample scored a "10"
out of 10, or the highest score for mold resistance, [0043] The principle and mode of operation of this invention have been explained and illustrated in its preferred embodiment. However, it must be understood that this invention may be practiced otherwise than as specifically explained and illustrated without departing from its spirit or scope.
[00031 Mold problems can arise in interior living spaces- In the past 30 years as buildings have become better insulated and more energy efficient there has been an increase in mold problems due to trapped moisture. Building materials such as wood, insulation materials and wallboard used in building construction are susceptible to mold and fungal growth in moist environments or when exposed to wetting.
Fluffed cellulose fiber, shredded paper, low density fiberboard used as insulating materials and. nonwoven webs, such as paper, used to cover gypsum wallboard, are all prime growth media for fungi. Several species of mold and fungus that grow in these environments are toxic to humans. A number of health risks such as occupational asthma, rhinoconjunctivitis, hypersensitivity pneumonitis and organic dust toxic syndrome (ODTS), aspergillosis and histoplasma have been linked to antigens generated by fungi. Diseases associated with inhalation of fungal spores can include toxic pneumonitis, hypersensitivity pneumonitis, tremors, chronic fatigue syndrome, kidney failure, and cancer.
10004] The current mold resistant wallboard technology (DensArmor Georgia Pacific) consists of a fiberglass based product that has limitations in implementation due to its cost and its density. The shell of DensArmor is composed of fiberglass.
This makes it weigh more than regular wallboard which uses paper as the shell.
An ideal mold resistant drywall would be of similar construction as standard drywall but be able to resist mold growth. Ecology Coatings, Inc. has developed a coating for drywall that needs to be cured by exposure to UV light.
[0005] It would be desirable to provide an antifungal composition that confers mold resistance to building materials such as loose fill and dense packed cellulose insulation, wallboards and to other materials.
SUMMARY OF THE INVENTION
[0006] In one embodiment, an antifungal composition comprises a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions.
The combination of the metal ions and the borate provide a synergistic effect in fungal resistance.
[00071 In another embodiment, an antifungal composition comprises an ion-exchange type antimicrobial agent with borate ions and two or more different metal ions. The combination of the borate ions and the metal ions provide a synergistic effect in fungal resistance.
[0008] A fungus resistant building material comprises a building. material susceptible to fungus growth and an antifungal composition comprising a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance.
[0009] Various aspects of this invention will become apparent to those skilled in the art from the following detailed description of the preferred embodiments.
BRIEF DESCRIPTION OF THE DRAWING
[00101 Figure I is a bar graph showing the week at which mold growth was first observed based on paper handsheet compositions in testing done with different additives-DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[00111 The present development relates to an antifungal composition that comprises a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance. The antifungal composition can be effective in providing resistance to one or more types of fungus, such as molds, yeasts, mushrooms and other eukaryotic organisms.
[0012] Any suitable borate fungicide can. be used in the composition. Borate fungicides are well known in the industry and include, for example, boric acid, sodium borate, borax, sodium tetraborate decahydrate, sodium tetraborate pentahydrate, disodium octaborate tetrahydrate, disodium octoborate, sodium metaborate, sodium perborate, sodium perborate tetrabydrate, sodium pentaborate decahydrate, and the like. In apart icular embodiment, the borate fungicide is sodium perborate tetrahydratc, which is available commercially as Polybor from U.S. Borax Inc., Valencia, California-[00131 The ion-exchange type antimicrobial agent can be any suitable type.
These agents typically comprise an inorganic ion-exchange carrier and one or more antimicrobial metals and/or metal ions, most preferably one or more antimicrobial metal ions. The inorganic ion-exchange carrier is preferably an ion-exchange type ceramic particle wherein antimicrobial metal ions have been exchanged (replaced) for other non-antimicrobially effective ions in the ceramic particles or a combination of the foregoing with an antimicrobial metal salt. Suitable ceramic particles include, but are not limited to zeolites, hydroxyapatite, zirconium phosphates and other ion-exchange ceramics, and come in many forms and types, including natural and synthetic forms.
[00141 The term "zeolite" is used here in its generic sense and refers to crystalline inorganic molecular sieves such as aluminophophates, silicon aluminum phosphates, microporous borosilicates, titanosilicates and tatanioaluminosilicates, as well as rnieroporous aluminosilicates and their silica analogs, having a framework structure consisting of nanopores and interconnected cavities which can be occupied by ions and/or water molecules, both of which have considerable freedom of movement permitting ion exchange and reversible dehydration. In contrast to amorphous materials these crystalline structures contain regular arrays of intracrystalline pores (zianopores) and voids of uniform dimensions. A typical naturally occurring zeolite is the mineral clinoptilolite with formula (Ca, Na, l( 2.3AI3(AI,Si)2Si13O3fi 12(H2O). As used herein, "ion exchanged zeolite" refers-to a natural or synthetic zeolite that has' been modified by an ion exchange process to increase the content of one or more metal ions in the zeolite.
[0015] The ion-exchange type antimicrobial agent is modified by exchange with two or more different metal ions. The combination of the metal ions and the borate provide a synergistic effect in fungal resistance. For example, as described in the experiments below, it was discovered that the combination of magnesium ions and manganese ions and the borate provide a synergistic effect in fungal resistance. Using the ASTM D6523 Standard Test Method for Resistance to Growth of Mold it has been demonstrated that this combination is an unexpectedly effective mold inhibitor.
However, other combinations of ions may also provide such a synergistic effect.
[00161 The experiments below describe the use of silver and zinc ions as well as magnesium and manganese. Some other metal ions known for use in ion exchange materials include, but are not limited to, copper, gold, mercury, tin, lead, iron, cobalt, nickel, arsenic, antimony, bismuth, barium, cadmium, chromium and thallium.
[0017] In an alternative embodiment, instead of using a borate fungicide along with the ion-exchange type antimicrobial agent, the antifungal composition can comprise an ion-exchange type antimicrobial agent having borate ions in addition to the metal ions. Any suitable borate ions can be used.
[0018] Other embodiments of this technology could include a binder, such as nanocellulose or other natural or synthetic binder, to aid in incorporating and retaining the antifungal composition into or onto the material to which it is applied.
(00191 The antifungal composition can have any suitable effectiveness against fungi. In certain embodiments, the antifungal composition scores a 10 in the ASTM
D3273 test for mold resistance. Also, in certain embodiments, the antifungal composition is effective to prevent mold growth onset at least about 3 weeks according to mold resistance test ASTM D6523. Such testing is described in the experiments below.
[0020] The antifungal composition can be used in many different applications where it is desirable to prevent fungal growth. The antifungal composition may be applied as a coating or may be incorporated into a material. Such applications can involve applying the antifungal composition in or on many different materials-Such materials may include, for example, wood, paper, metal, plastic, glass, or fabric/textile. In certain embodiments, the antifungal composition is incorporated into or coated onto any number of inorganic materials, especially those employed in building construction, like wood, paper, fluffed cellulose fiber, fiberboard, cements, mortar, grout, plaster, and the like, or in the manufacture of building materials, such as ceramics and cements for tiles, In certain embodiments, the antifungal composition is used as a building material additive, for example, in wallboard of any type, more particularly in the paper cover of drywall or in cellulose insulation formulations - both loose fill and dense packed products.
[0021] The antifungal composition can be used in any amount suitable for providing fungal resistance. For example, the composition may be used in an amount of from about 1% to about 30% by weight of the material when used as an additive, or by weight of a coating when applied as a coating-[0022] Development. and Test of the Innovation [0023] The main goal of this innovation was to identify a zeolite formulation which would inhibit mold growth when incorporated into paper. The scope of work comprised two parts. Part I tested pre-screening of ion exchanged zeolite candidates for mold inhibition on paper handsheets. The best mold inhibitor candidates were chosen for a second round of tests, Part II. Combinations of two metals and metals with Polybor were utilized in making handsheets which were then tested for mold.
inhibition. Finally, a sample of "drywall paper" with the best performing zeolite was submitted to an ASTM lab in order to test its effectiveness under the ASTM
mold resistance test (ASTM D6523).
[0024] Part I.
[0025] The testing was performed in two stages. The first stage involved preparing a series of handsheets which incorporated a range of ceolite/metal compositions.
[0026], Handsheet Compositions Hand Sheet Mold Test Key:
Sheet Composition A Ag/OLIN
B Fe/CLIN
C Mg/CLIN
D Mn/CLIN
E Zn/CLIN
F Ti/CLIN (#3- normal pH, exchanged in ethanol, CLIN normal) G Ti/CLIN (#2- low pH, exchanged in water, CLIN damaged?) II Zn/50% exchange I Ag/FAU
J CLIN (unexchanged) K BLANK
L Polybor CLIN: clinoptilolite FAU: faujasite Polybor: spray-on boric acid compound [0027] Mold Test Results [0028] Inhibition of mold growth was conducted in Dr. Jody Jellison's lab at the University of Maine. Dr_ Jellison is an expert in mold microbiology and performs consulting work for private industry. The choice of mold species was recommended by her and Zeomatrix' experimental design was modified by her to best suit the' facilities available and her knowledge of best known practices. The test utilized four mold spores common to domestic environments.
[0029] The mold species used in this study are as follows:
Aspergillus niger ATCC 6275 - isolated from leather Aspergillus niger ATCC 9642 - isolated from wireless radio equipment, New South Wales, Australia Cladosporium minourae ATCC 52853 -isolated from rotting wood, Japan Penicillium funiculosum ATCC 11797 - isolated from mercury-treated fabric,.Maryland [0030] A cocktail of these organisms were prepared from individual cultures obtained from ATCC (American Type Culture Collection). Careful preparation of the cocktail required that each mold species be present at the same concentration (steps 1 through 4). This process required four weeks. Paper samples (5 each) were 4.0 cm diameter circles cut from handsheets and placed in a randomized fashion 4 at a time onto agar plates (step 5). Each plate was inoculated with mold spores by spraying with 10 mL of the spore cocktail (step 6). The plates were incubated at 25 C
in humid conditions for 4 weeks. The plates were photographed each week (step 8). The ability of the paper samples to inhibit mold growth nearby was determined by measuring zones of partial and total inhibition (step 9)"
1. Molds Grown on Potato Dextrose Agar (PDA) 2. Spores Collected Using Minimal Salts Solution 3. Spores Counted Using l-Iemocytometer 4. 105 Spores from Each Mold Added to Spore.Cocktail 5. Plates Assembled Using Minimal Salts Solution And Samples 6. 10 mL Spore Cocktail Sprayed onto Each Plate Using Minimal Salts Agar 7. Plates Incubated At 25 C In Humid Conditions for Four-Weeks 8. Plates Were Photographed Regularly 9. Zones of Total and Partial Inhibition Were Measured [0031] Results:
[0032] Zones of inhibition showed that handsbeets containing zeolites exchanged with silver, and magnesium in combination with boric acid were effective in preventing mold from growing near the paper samples. Samples containing silver, natural zeolite, zinc, and boric acid demonstrated some effectiveness at inhibiting mold growth on the paper samples.
[0033] Part II.
[0034] Part II of this research effort involved three different exchanged zeolites which exhibited mold inhibition in Part I - Ag, Mg and Zn- exchanged. The Ag-exchanged sample was used as a control and is not a good candidate for a commercial product. However, both the Mg and Zn samples were tested in the follow-on study.
[00351 Mold Study [0036] As before, zeolite samples were exchanged by Zeomatrix and handsheets incorporating these zeolites were prepared by the Process Development Center (PDC) at UM. The handsheets were divided up into samples as shown in Table 1 and submitted to Jody Jellison for incubation with the test mold spores. The mold testing was conducted for 8 weeks and the results are in Figure 1.
Table I. Handsheet Sample Compositions Hands-beet Sam 1e Number Exchanged Ions Composition A M Zn 1:1 B MnZn 1:1 C Mn 1:1 D MgMnZn 1:1:1 E Ag Control P No exchange Zeolite Control G MMn 1:1, 3.5% Polybor H MnZn. 1:1, 4.7% Pol bor I MgMn 1:1, 3.0% Pol bor J MgMnZn I- L 1, 4.1% Polybor K Ag 3.6% Polybor L No exchange 5.0% Polybor [0037] The exchanged zeolites in the preceding table were incorporated into handsheets in the amounts indicated (1:1, 300rng_300mg). The Polybor was applied as a spray-on solution at the various levels indicated. The Polybor is simply a boric acid solution comprised of boron, oxygen, and sodium.
[0038] Mold Test [0039] The mold test was conducted as previously described (Part I). The plates were prepared in a double blind study where the biology researchers were unaware of the different compositions of samples A-L. Different samples were randomly grouped.
on the 5 plates in sets of three in order to test 5 replicates of each composition. The results of the replicates are summarized in the table in Table 11-Table II. Summary of Initial Mold Growth for Replicate Samples.
Groai F tst ;" :weexr"I :~C X X X I X X X
--- ' x I_ x NOM AtwccX4ev-ovearmc ir typolu airu,eormo- rve kaes-Yimmoldgrna 0 f 0 0 O 3 I 0 3 1 2 3 4 3 HMIMw;l6ne, 0 0 0 0 3 -I 0 -3--~ 2 4-.-_.
gowdh21Wccr61 - -- - -= --I - -- -=-- =--- - ---- -- ' s- Wei, 0- I. 0 0 0 4 1 0 3 3 4 3 4 3 Acplir~tcsrilh=m ---~ -~ --0 __j---_p - - =-0-- q- 0 4--~ 3 - ~- - 4---,-` _ -4 - --- 3' ... ...: : ... .. . .
. I I
I , I
~aapt6ca~ac wfth,iol .0 .. ~.~_ 0- i 0 4 i 0 s 13 _4 19v'pyp~ at WeeK z ~.--[0040] Summary of Innovation Test [00411 The Polybor definitely had a positive effect on the mold resistance properties. The best overall performers (all replicates over eight weeks) were the ones containing either magnesium plus manganese, or silver, plus Polybor- However, the mg:mn plus polybor samples (I and G) were more resistant to mold growth onset than the Ag -- Polybor as shown in Figure 1. This composition (Mg:Mn + polybor) was selected for the drywall test panel. There was a definite synergistic effect of the two metals (Mg and Mn) in combination with Polybor. The result is non-obvious considering that the addition of zinc (MgMnZnP) did not inhibit mold growth more than no exchange at all.
[00421 The drywall panel was submitted to Accugen Laboratory in Illinois for the ASTM
D3273 test. This test showed that the MgMn Polybor treated drywall sample scored a "10"
out of 10, or the highest score for mold resistance, [0043] The principle and mode of operation of this invention have been explained and illustrated in its preferred embodiment. However, it must be understood that this invention may be practiced otherwise than as specifically explained and illustrated without departing from its spirit or scope.
Claims (21)
1. An antifungal composition comprising a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions, the combination of the metal ions and the borate providing a synergistic effect in fungal resistance-
2. The antifungal composition of claim 1 which scores a 10 in the ASTM
D3273 test for mold resistance.
D3273 test for mold resistance.
3. The antifungal composition of claim 1 which is effective to prevent mold growth onset at least about 3 weeks according to mold resistance test ASTM
D6523.
D6523.
4. The antifungal composition of claim 1 wherein the metal ions comprise a combination of magnesium ions and manganese ions.
5. The antifungal composition of claim 1 wherein the ion-exchange type antimicrobial agent comprises a zeolite.
6. The antifungal composition of claim 1 wherein the borate fungicide comprises a borate hydrate.
7. The antifungal composition of claim 6 wherein the borate fungicide comprises disodium octaborate tetrahydrate.
8. The antifungal composition of claim 1 wherein the ion-exchange type antimicrobial agent comprises a zeolite and the metal ions comprise a combination of magnesium ions and manganese ions.
9. The antifungal composition of claim 8 wherein the borate fungicide comprises disodium octaborate tetrahydrate.
10. The antifungal composition of claim 1 wherein the ion-exchange type antimicrobial agent consists of a zeolite, the metal ions consist of a combination of magnesium ions and manganese ions, and the borate fungicide consists of disodium octaborate tetrahydrate.
11. An antifungal composition comprising an ion-exchange type antimicrobial agent with borate ions and two or more different metal ions, the combination of the borate ions and the metal ions providing a synergistic effect in fungal resistance.
12. The antifungal composition of claim 11 wherein the metal ions comprise a combination of magnesium ions and manganese ions.
13. The antifungal composition of claim 11 wherein the ion-exchange type antimicrobial agent comprises a zeolite.
14. The antifungal composition of claim 11 wherein the borate comprises a borate hydrate.
15. The antifungal composition of claim 1 wherein the ion-exchange type antimicrobial agent comprises a zeolite and the metal ions consist of a combination of magnesium ions and manganese ions.
16. A fungus resistant building material comprising a building material susceptible to fungus growth and an antifungal composition comprising a borate fungicide and an ion-exchange type antimicrobial agent with two or more different metal ions, the combination of the metal ions and the borate providing a synergistic effect in fungal resistance.
17. The building material of claim 16 wherein the metal ions comprise a combination of magnesium ions and manganese ions.
18. The building material of claim 16 wherein the ion-exchange type antimicrobial agent comprises a zeolite.
19. The building material of claim 16 wherein the borate fungicide comprises disodium octaborate tetrahydrate.
20. The building material of claim 16 which comprises a wallboard.
21. The building material of claim 16 which comprises cellulose fiber insulation.