CA2691460C - Continuous digestion of chip blends containing a western red cedar chip furnish - Google Patents

Abstract

A continuous process is provided for delignifying lignocellulosic material, including feeding a lignocellulosic blend comprising a Western Red Cedar (WRC) chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution at the feed end of a digester to produce a lignocellulosic mass. The second lignocellulosic material is provided in a proportion that increases the density of the mass to enable the mass to move through the digester while minimizing production effects associated with low density WRC chips. The mass moves through the digester to produce a pulp that may be bleached to have a kappa no greater than 5, a yield of at least 38%, a fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.

Description

Continuous Digestion of Chip Blends Containing a Western Red Cedar Chip Furnish 1. FIELD OF THE DISCLOSURE
The invention relates to delignification of lignocellulosic materials, and more particularly to a process of delignifying blends of lignocellulosic materials comprising less than 85% Thuj a plicata by oven dry weight.

2. BACKGROUND
The production of cellulosic pulp from lignocellulosic materials is well known and may involve mechanical, chemical, and thermal processes, or various combinations of such processes, to produce cellulosic materials that can be manufactured into various products, for example, paper.
Chemical pulping is an economically attractive process due to high pure cellulose fibre (pulp) yields and the resultant fibre properties which are applicable to a wide variety of end-use applications.
In a typical chemical pulping process, comminuted lignocellulosic materials are subjected to chemical reagents that remove lignin, hemicellulose, gums, carbohydrates, and fatty materials from the lignocellulosic materials to release cellulose fibers during the digestion process. The dominant chemical pulping process is currently the "kraft", or "sulphate", process. In the kraft process, sodium hydroxide and sodium sulfite comprise the principal cooking or digestive chemicals ("cooking liquor") which, when mixed with water at specified levels, are generally referred to as "alkaline pulping liquor" or "white liquor". The alkaline reagents react with lignin, hemicellulose and other resin molecules to break them into smaller fragments whose sodium salts are soluble or dispersible in the cooking liquor.
In the kraft process, a select amount of the lignocellulosic material, e.g.
wood chips, is fed to a digester vessel along with white liquor to attain a select "chemical" or "liquid-to-wood" ratio.
This material charge is then subjected to controlled heat and pressure over a select period of time.
Both batch and continuous digestion processes are known. In batch processes, the material charged may be held in a vessel (a "batch digester") under select temperature/pressure condition for a calculated period of time to attain a desired pulp characteristic, typically residual lignin content, and then "discharged" or "blown" into a holding tank so as to yield a pulp suitable for further processing, including washing, and/or bleaching, prior to paper manufacturing.
In a continuous digestion process, the material charge is controllably moved through zones of select temperature/pressure to a regulated discharge point (i.e. a valve) to continuously yield pulp having desired characteristics (i.e. a select level of delignification, reduced "resins" content, water drainability, etc.).
Bleached kraft pulp prepared from chip furnishes comprising greater than 90%
fine-fibered, low coarseness Thuja plicata (Western Red Cedar; "WRC") by oven dried weight, or high-WRC
("HRWC") pulp, is highly prized worldwide for unique high value end product applications owing to the unique combination of pulp fibre properties. One example is in medical specialty applications where highly closed sheet composites prepared with HWRC pulps guarantee a fluid barrier.
The production of WRC-containing pulps from chip furnishes exceeding 40% WRC
by oven dried weight is generally confined to batch pulping systems due to low wood density, low pulp yield, corrosivity of the residual ("black") liquors, significant issues with chip plug movement in continuous digesters, and plugging of liquor extraction screens by fine cedar fibers that detach from the chips during pulping.

3. SUMMARY
In accordance with one aspect of the disclosure, there is provided a continuous process for delignifying lignocellulosic material. The process includes feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution at the feed end of a digester to produce a lignocellulosic mass. The second lignocellulosic material is provided in a proportion that increases the density of the mass so as to enable the mass to move through the continuous digester while minimizing production effects associated with low density WRC chips. Accordingly the mass moves through the digester to produce a cellulosic pulp having a pre-bleaching kappa of no greater than 30 under conditions having an H-Factor of at least 1500. The continuous process further includes recovering the cellulosic pulp at a recovery end of the digester, such that it may be subsequently bleached to produce a bleached pulp having a post-bleaching kappa no greater than 5, a yield of at least 38%, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.

The process may further include a further step of bleaching the cellulosic pulp to produce a bleached pulp having a post-bleaching kappa no greater than 5, a yield of at least 38%, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF. The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.51cm at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.
Thuja plicata fibers may make up less than 80% of the fibers of the cellulosic pulp.
Alternatively, Thuja plicata fibers may make up less than 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70% 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
According to another aspect of the disclosure, there is provided a process for delignifying lignocellulosic material. The process includes feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass. The the Thuja plicata chip furnish will make up less than 85% of the blend by oven dry weight. The process further includes producing a cellulosic pulp under conditions having an H-Factor of at least 1500, and recovering the cellulosic pulp from the digester, wherein the cellulosic pulp has a kappa no greater than 30 with a yield of at least 38%.
The cellulosic pulp may be subsequently bleached to produced a bleached pulp having a post-bleaching kappa no greater than 5, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.
The process may further include a subsequent step of bleaching the cellulosic pulp to produce a bleached pulp having a post-bleaching kappa no greater than 5, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF. The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.51cm at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.

4 The process may be a continuous process. Thuja plicata fibers may make up less than 85%
of the fibers of the cellulosic pulp. Alternatively, Thuja plicata fibers may make up less than 80%, 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70%, 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
According to another aspect of the disclosure, there is provided a use of a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material in the preparation of a cellulosic pulp by continuous process. The use includes feeding the lignocellulosic blend into an aqueous alkaline pulping solution at a feed end of a digester to produce a lignocellulosic mass. The second lignocellulosic material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution.
Accordingly the mass moves through the digester to produce a cellulosic pulp having a fully or semi-bleached pre-bleaching kappa of no greater than 30 under conditions having an H-Factor of at least 1500. The use further includes recovering the cellulosic pulp at a recovery end of the digester, such that it may be subsequently bleached to produce a bleached pulp having a post-bleaching kappa no greater than 5, a yield of at least 38%, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.
The use may further include a further step of bleaching the cellulosic pulp to produce a bleached pulp having a post-bleaching kappa no greater than 5, a yield of at least 38%, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF. The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.5km at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.
Thuja plicata fibers may make up less than 80% of the fibers of the cellulosic pulp.
Alternatively, Thuja plicata fibers may make up less than 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70% 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
In accordance with yet another aspect of the disclosure, there is provided a use of a lignocellulosic blend, including a Thuja plicata chip furnish and a second lignocellulosic, material in the preparation of a cellulosic pulp. The use includes feeding the lignocellulosic blend into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass. The Thuja plicata chip furnish makes up less than 85% of the blend by oven dry weight. The use further includes producing a fully or semi-bleached pre-bleached cellulosic pulp under conditions having an H-Factor of at least 1500, and recovering the cellulosic pulp from the digester, wherein the pre-bleached cellulosic pulp has a pre-bleaching kappa no greater than 30 with a yield of at least 38%.
The cellulosic pulp may be subsequently bleached to produced a bleached pulp having a post-bleaching kappa no greater than 5, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.
The use may further include subsequent bleaching the pre-bleached cellulosic pulp to produce a bleached pulp having a post-bleaching kappa no greater than 5, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF. The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.5km at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.
The use may be with a continuous digester. Thuja plicata fibers may make up less than 85% of the fibers of the cellulosic pulp. Alternatively, Thuja plicata fibers may make up less than 80%, 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70%, 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
In accordance with another aspect of the disclosure, there is provided a bleached pulp produced according to a continuous process for delignifying lignocellulosic material. The process includes feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution at the feed end of a digester to produce a lignocellulosic mass. The second lignocellulosic material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution. Accordingly the mass moves through the digester to produce a fully or semi-bleached cellulosic pulp having a pre-bleaching kappa of no greater than 30 under conditions having an H-Factor of at least 1500. The continuous process further includes recovering the cellulosic pulp at a recovery end of the digester, and subsequent bleaching to produce a bleached pulp having a post-bleaching kappa no greater than

5, a yield of at least 38%, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/m, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF. The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.5Icm at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.
Thuja plicata fibers may make up less than 80% of the fibers of the bleached pulp.
Alternatively, Thuja phcata fibers may make up less than 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70% 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
In accordance with another aspect of the disclosure, there is provided a bleached pulp produced according to a process for delignifying lignocellulosic material. The process includes feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass.
The process may be a continuous process. The Thuja plicata chip furnish will make up less than 85% of the blend by oven dry weight. The process further includes producing a fully or semi-bleached cellulosic pulp under conditions having an H-Factor of at least 1500, and recovering the fully or semi-bleached cellulosic pulp from the digester, wherein the cellulosic pulp has a pre-bleaching kappa no greater than 30 with a yield of at least 38%. The cellulosic pulp is subsequently bleached to produced a bleached pulp having a post-bleaching kappa no greater than 5, a length weighted fiber length no greater than 2.2mm, a coarseness no greater than 0.16mg/rn, a freeness no greater than 610mL, a tensile strength of at least 8.0 km at 500 CSF, and a porosity no greater than 60 Gurley sec at 500 CSF.

The bleached pulp may have a post-bleaching kappa greater than zero, a length weighted fiber length no less than 1.8 mm, a freeness no less than 550 mL, a tensile strength no more than 9.5km at 500 CSF, and a porosity no less than 20 Gurley sec at 500 CSF.
Thuja plicata fibers may make up less than 85% of the fibers of the cellulosic pulp.
Alternatively, Thuja plicata fibers may make up less than 80%, 70%, 60%, or 50% of the fibers of the cellulosic pulp. Thuja plicata chips may make up less than 80% of the chip furnish by oven dry weight. Alternatively, Thuja plicata chips may make up less than 70%, 60%, or 50% of the chip furnish by oven dry weight. The second source of lignocellulosic material may be a Callitropsis nootkatensis.
Various embodiments of the claimed invention relate to a continuous process for delignifying lignocellulosic material, comprising: feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution at a feed end of a digester, wherein the Thuja plicata chip furnish is about 50% or more of the blend by oven dry weight, to produce a lignocellulosic mass, wherein the second lignocellulosic material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution so as to move the mass through the digester to produce a cellulosic pulp under conditions having an H-Factor of at least 1500; recovering the cellulosic pulp at a recovery end of the digester; and bleaching the cellulosic pulp to produce a bleached pulp having: a) a post-bleaching kappa no greater than 5; b) an average length weighted fiber length no greater than 2.2 mm; c) a coarseness of no more than 0.16 mg/m; d) a freeness no greater than 610 mL; e) a tensile strength of at least 8.0 km at 500 Csf; and 0 a porosity no greater than 60 Gurley sec. at 500 Csf.
Various embodiments of the claimed invention relate to a process for delignifying lignocellulosic material, comprising: feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass, wherein the Thuja plicata chip furnish is between 50%
and 85% of the blend by oven dry weight, to produce a cellulosic pulp under conditions having an H-Factor of at least 1500; and recovering the cellulosic pulp from the digester, wherein the cellulosic pulp has: a) a kappa no greater than 30; b) a yield of at least 38%.
Various embodiments of the claimed invention relate to the use of a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material, wherein the Thuja 7a plicata chip furnish is about 50% or more of the blend by oven dry weight, in the preparation of a cellulosic pulp by a continuous process, the process comprising: feeding the lignocellulosic blend into an aqueous alkaline pulping solution at a feed end of a digester, to produce a lignocellulosic mass, wherein the second lignocellulosic material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution so as to move the mass through the digester to produce the cellulosic pulp under conditions having an H-Factor of at least 1500;
recovering the cellulosic pulp at a recovery end of the digester; and bleaching the cellulosic pulp to produce a bleached pulp having: a) a post-bleaching kappa no greater than 5;
b) a yield of at least 38%; c) an average length weighted fiber length no greater than 2.2 mm; d) a coarseness no more than 0.16 mg/m; e) a freeness no greater than 610 mL; 0 a tensile strength of at least 8.0 km at 500 Csf; and g) a porosity no greater than 60 Gurley sec. at 500 Csf.
Various embodiments of the claimed invention relate to the use of a lignocellulosic blend comprising a Thula plicata chip furnish and a second lignocellulosic material, wherein the Thula plicata chip furnish is about 50% or more of the blend by oven dry weight in the preparation of a cellulosic pulp, the use comprising: feeding the lignocellulosic blend into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass, wherein the Alija pilau(' chip furnish comprises less than 85% of the blend by oven dry weight, to produce the cellulosic pulp under conditions having an H-Factor of at least 1500 and recovering the cellulosic pulp from the digester, wherein the cellulosic pulp has: a) a kappa no greater than 30; and b) a yield of at least 38%.
Various embodiments of the claimed invention relate to a bleached pulp prepared according to the process as described herein, wherein between 50% and 85% of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.
Various embodiments of the claimed invention relate to a cellulosic pulp prepared according to the process as described herein, wherein the cellulosic pulp has a kappa no greater than 5, and wherein between 50% and 85% of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.
4. BRIEF DESCRIPTION OF THE DRAWINGS
Figure 1 shows a cross-sectional schematic diagram of a lignocellulosic fiber 7b Figure 2 is a histogram showing chip size distribution of chips from WRC, Yellow Cypress, and Sitka Spruce.
Figure 3 is a histogram showing the basic density of WRC, Yellow Cypress, and Sitka Spruce chips.
Figure 4 is a histogram showing the bulk density of WRC, Yellow Cypress, and Sitka Spruce.
Figure 5 is a histogram showing the kappa values of the pulps resulting from small cooks of WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 6 shows the kappa values as a function of H-factor for 'WRC, Yellow Cypress, and Sitka Spruce.
Figure 7 shows the unscreened yield as a function of kappa for WRC, Yellow Cypress, and WRC/Yellow Cypress blends.
Figure 8 shows the unscreened yield as a function of kappa for WRC, Sitka Spruce, and WRC/Sitka Spruce blends.
Figure 9 shows the breaking length as a function of PFI for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.

Figure 10 shows the tear index as a function of PFI for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 11 shows burst index as a function of PFI for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 12 is a histogram showing the Wet Zero Span of WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 13 is a histogram showing the L&W Fibre Tester fiber coarseness of WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 14 is a histogram showing the L&W Fibre Tester % fines for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 15 is a histogram showing the L&W Fibre Tester kink index for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 16 is a histogram showing the L&W Fibre Tester shape index for WRC, Yellow Cypress, Sitka Spruce, WRC/Yellow Cypress blends, and WRC/Sitka Spruce blends.
Figure 17 shows the L&W Fibre Tester fiber length distribution of WRC, Yellow Cypress, and the 50/50 WRC/Yellow Cypress pulps.
Figure 18 shows the L&W Fibre Tester shape factor distribution for WRC, Yellow Cypress, and the 50/50 WRC/Yellow Cypress pulps.
Figure 19 shows the corrected Canadian Standard Freeness as a fiinction of PFI
beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.
Figure 20 shows the density as a function of PFI beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.

Figure 21 shows brightness as a function of PFI beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.
Figure 22 shows the tensile breaking length as a function of PFI beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.
Figure 23 shows the tear index as a function of PFI beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.
Figure 24 shows the burst index as a function of PFI beating for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress pulps.
Figure 25 is a histogram showing the Wet Zero Span for WRC, Yellow Cypress, 50/50 and 50/50 WRC/Yellow Cypress pulps.
Figure 26 shows the L&W Fibre Tester fiber length distribution of WRC, Yellow Cypress, 50/50 WRC/Yellow Cypress pulps.
Figure 27 shows the L&W Fibre Tester shape factor distribution of WRC, Yellow Cypress, 50/50 WRC/Yellow Cypress.
Figure 28 shows the L&W Fibre Tester fiber lengths distribution of HS-480 pulp.
Figure 29 shows the L&W Fibre Tester fiber width distribution of HS-480 pulp.
Figure 30 is a series of histograms showing the L&W Fibre Tester fiber property distributions of HS-480 pulp.
Figure 31 shows the Canadian Standard Freeness of HS-480 pulp as a function of PFI.
Figure 32 shows the tensile breaking lengths of HS-480 pulp as a function of PFI.
Figure 33 is a histogram showing the Wet Zero Span of HS-480 pulp.

Figure 34 shows the density of HS-480 pulp as a function of PFI beating.
Figure 35 shows the sheet porosity of HS-480 pulp as a function of PFI
beating.
5 Figure 36 shows the smoothness of HS-480 pulp as a function of PFI
beating.
Figure37 shows the scattering coefficient of HS-480 pulp as a function of PFI
beating.
Figure 38 shows the stiffness of HS-480 pulp as a function of PFI beating.
Figure 39 shows the stretch of HS-480 and pulp as a function of PFI beating.
5. DETAILED DESCRIPTION
In various embodiments, the invention provides processes for producing a HWRC-like pulp from lignocellulosic materials comprising less than 85% WRC by oven dry (OD) weight under conditions having an H-factor of at least 1500.
Definitions and General Information As used herein, "lignocellulosic material" refers to any material comprising mainly cellulose, hemicellulose, and lignin. "Cellulose" is an unbranched polysaccharide consisting of a linear chain of several hundred to over ten thousand 13(1-4) linked D-glucose units, and is the main structural component of plant and algal cell walls. Cellulose comprises about 33% of plant matter, and about 35-60% of natural lignocellulosic materials.
"Hemicellulose" is non-cellulosic polysaccharides associated with cellulose in plant tissues.
Hemicellulose comprises about 20-35% w/w of natural lignocellulosic materials, consisting predominantly of D-pentose (five-carbon) sugar units, mostly xylose, although more minor proportions of hexose (six-carbon) sugar units, are generally also present.
"Lignin" is a complex cross-linked polymer based on variously substituted p-hydroxyphenylpropane units, and generally constitutes about 25-33% w/w of natural lignocellulosic materials. It is covalently linked to cellulose and hemicellulose, and consequently confers mechanical strength to the cell wall, and the plant as a whole, by crosslinking different plant polysaccharides, The cellulosic fibers can be separated from the lignocellulosic raw material, e.g.
wood, by chemical or mechanical defiberizing processes referred to as "pulping". Pulping processes are generally known in the art.
As used herein, "cellulosic pulp" or "pulp" is a dry fibrous material prepared by .. chemical or mechanical pulping of lignocellulosic materials. Cellulosic pulp which is formed into sheets to be shipped and sold as cellulosic pulp, and not further processed into paper at the same location, is referred to as "market pulp".
As used herein, "chemical pulp" refers to cellulosic pulp produced by combining lignocellulosic materials and chemicals in large pressure vessels known as "digesters" where heat, pressure, and the chemicals break down bonds that link lignin to the cellulose binding without seriously degrading the cellulose fibers. As used herein, "chemical cooking" or "cooking" is the process of exposing the lignocellulosic material to chemicals under heat and pressure to break down the lignin.
The "kraft process", also known as "kraft pulping" or the "sulfate process", is the dominant chemical pulping method in the world. As used herein, the "'craft process" refers to a process of cooking lignocellulosic material with a mixture of sodium hydroxide and sodium sulfide, thereby converting the lignocellulosic material into a cellulosic pulp comprised of almost pure cellulose fibers.
As used herein, a "batch chemical pulping process" or "batch cooking process"
or "batch process" is a process in which discrete quantities of lignocellulosic material are individually processed. Industrial batch processes, including "conventional"
batch processes and "displacement" batch processes, are well known in the art and are described in Papermaking Science and Technology Series, Book 6A "Chemical Pulping", Eds.
Johan Gullichsen and Hannu Paulapuro, Fapet 0y,1999. In a batch process, a "batch digester" is .. filled with lignocellulosic material before being charged with the cooking liquor. Chips may be transported from storage to the digester by belt conveyors. A known amount of dry wood will be charged into the digester to obtain a uniform degree of delignification from cook to cook. Chip mass may be measured, for example, by strain gauges in the digester legs.
Accurate measurement of chip moisture is necessary to determine the appropriate alkali charge, which is based on the amount of dry wood in the digester. Proper chip packing and distribution is also important for uniform cooking and can be attained, for example, by steam packing. The digester is then sealed and, with steam and/or hot black liquor, the temperature of the digester is brought up to a cooking temperature at which the digester is maintained for a period of time referred to as "the cook". At the conclusion of the cook, a "blow" valve in the digester is opened, and the contents of the digester are then discharged into a "blow tank".
As used herein, a "continuous chemical pulping process" or "continuous cooking process" or "continuous process" is a method of chemical cooking in which raw lignocellulosic materials and cooking liquors are continuously fed at controlled rates into a pressurized digester at a "feed end" while at the same time pulp and black liquor (i.e. the combined cooking liquids that contain the lignin fragments, carbohydrates from the breakdown of hemicellulose, sodium carbonate, sodium sulfate and other inorganic salts) are removed at a "recovery end". Continuous processes, including modified kraft cooking (MCC), isothermal cooking (ITC), LoLevelTM feed system, and Lo-SolidsTM, are well known in the art and are described, for example, in Papermaking Science and Technology Series, Book 6A "Chemical Pulping", Eds. Johan Gullichsen and Hannu Paulapuro, Fapet 0y,1999. Digesters for a continuous process include the type supplied by Kamyr, Inc. of Glens Falls, N.Y. or Kamyr AB of Karlstad, Sweden.
In continuous processes, the lignocellulosic materials move down through successive cooking zones within the digester and are continuously discharged at the bottom as pulp.
Lignocellulosic materials may be fed into the digester via conveyor belts to a chip bin which may employ atmospheric pre-steaming to heat the lignocellulosic materials for the purpose of removing entrained air, thereby preparing the lignocellulosic materials to subsequently absorb the cooking liquors uniformly and allowing the chips to sink in the digester. The steamed chips may be discharged from the bottom of the bin at a controlled rate by a rotary feeder, with a variable speed drive called a "chipmeter", into a horizontal steaming vessel that conveys and discharges the chips into a vertical chute. In a continuous process, the lignocellulosic materials are fed at a rate which allows the pulping reaction to be complete by the time the materials exit the digester.
A vertical chute may be used to feeds chips into the inlet of a high pressure feeder where the chips initially contact the cooking liquor. Chips are flushed with liquor to the top of the digester vessel where they form a chip column that moves vertically down. Gravity draws the chip column downward according to the difference in density between the column and the unbound liquor. While chips and bound liquor move down, unbound liquor can move in any direction or velocity relative to the chip column. The top of the digester is generally an impregnation zone, where the chips are retained for 45-60 minutes, with a series of digester screens below that allow selective extraction of unbound liquor.
Immediately below the impregnation zone is a heating zone where the column undergoes indirect heating using external liquor heat circulation to bring the chip column to full cooking temperature.
Beneath the heating circulations is a concurrent cooking zone, where chips may be maintained, for example, for 1.5-2.5h. Below this is the extraction zone where unbound liquor is removed from the system. An upward flow of unbound liquor is generated beneath the extraction zone to create a counter current washing zone, where chips may be further retained for 1-4 h. Finally, a blow and cooling zone is located at the bottom of the digester where cooled chips may be discharged from the bottom of the digester using an outlet scraping device.
Delignification may typically require several hours at temperatures ranging from 130 to 180 C. Under these conditions, the lignin and hemicellulose may degrade to give fragments that dissolve in the alkaline cooking liquid. The remaining pulp (about 40-48%
by weight based on the dry wood chips), once collected in a blow tank in a batch process or at the recovery end of the digester in a continuous process, is known as "brown stock".
Certain cellulosic fibers will give paper, and related products, specific desirable properties. Accordingly, some fibers give the paper increased strength, while other fiber types may improve other properties, e.g. brightness, smoothness, opacity, or porosity. There are numerous fiber combinations, and also combinations of properties which are desired in paper.
Preferred lignocellulo sic materials in the context of the invention are derived from wood, more specifically heart/core wood and/or outer wood derived from trunks or stems of coniferous trees. However, it will be understood by one skilled in the art that any source of lignocellulo sic material could potentially be of value, including: wood from the branches or roots of trees or shrubs; non-wooden plant material in the form of stem, stalk, foliage, bark, root, shell, pod, nut, husk, fiber, vine, straw, hay, grass, bamboo or reed, singularly; algal material; or recycled paper.
Useful sources of wood may include numerous species of coniferous and broad-leaved trees/shrubs. Preferred sources of wood in the context of the invention are derived from conifers, specifically WRC (Thuja plicata) and Yellow Cypress (Callitropsis nootkatensis also known as Chamaecyparis nootkatensis). It will be understood by a person skilled in the art that several other sources of conifer could be of value, including Sitka Spruce.
One skilled in the art will appreciate that the original physical characteristics of lignocellulosic materials will make it desirable to comminute the material in order to obtain pieces of sufficiently small size and/or sufficiently high surface area to mass ratio to enable pulping of the material to be performed satisfactorily. In the case of wood, material of suitable dimensions will often be available as a waste product in the form of wood chips, wood flakes, sawdust, twigs and the like from sawmills, forestry and other commercial sources. Preferred dimensions will be in the form of wood chips.
As used herein, "accepts" refers to the lignocellulosic material, such as wood chips, chosen for pulping.
As used herein, basic wood chip density is obtained by dividing the oven dried (OD) weight of the wood chips by the green (swollen) volume.
A pulp mill may adjust various parameters, including lignocellulosic material, chemical, and process parameters, in an attempt to achieve maximum throughput of a select pulp grade at the lowest possible cost per unit of pulp. Accordingly, pulp mills seek to balance operating/output parameters, typically expressed as Kappa number (degree of delignification), percentage of pulp-yielding material rejects, cooking or digestion parameters (temperature, pressure, time, etc.), white liquor requirements, H-factor, etc.
Improvements in any one or more of these and other variables can lead to either greater through-put in a pulp mill or a lower cost per unit of pulp.
As used herein, kappa is the degree of delignification of a cellulosic pulp.
The standard method of determining kappa of pulp is described in TAPPI T236. In general, kappa number reflects a balance between pulp strength, pulp yield, and downstream processing costs including bleaching.
As used herein, "H-factor" is the integrated value of reaction rate at a given temperature over time. H-factor is calculated as:
H-factor = _(16113/(T+273))dt 3/(T+273)) where temperature (T) is in C and time (t) is in hours. When combined with cooking chemical concentration, H-factor is used to predict and control the degree of delignification (kappa) that occurs as the chip travels through the digester.
As used herein, "yield" refers to the ratio of cellulosic pulp output (i.e.
recovered pulp) to raw material input, expressed as a percentage. "Unscreened yield"
refers to yield including cellulosic shives, that is, under-cooked lignocellulosic material of dimensions which will not pass through mill pulp screening systems.
As used herein, "breaking length" values refer to the tensile force required to break or rupture a test specimen, reported in terms of the length of the sample strip that will break under its own weight (expressed in km). Finer and longer fibers are reported to exhibit higher sheet breaking length due to increased inter-fiber bonding.
Accordingly, differences in breaking length may be attributed to the cumulative effects of fiber length, bonding, and strength in pulp. Breaking length is measured using Tappi standard T494.
5 As used herein "tear index" refers to the mean force (expressed in mN) required to continue the tearing of paper from an initial cut per basis weight (expressed in g/m2) of a single one square meter sheet. Differences in tear index are due to the cumulative effects of fiber length, bonding, and strength in pulp. Tear index is measured using Tappi standard T414.
10 As used herein, "burst strength" refers to the resistance of paper to rupture as measured by the hydrostatic pressure required to burst it when a uniformly distributed and increasing pressure is applied to one of its sides. As used herein, "burst index" refers to the ratio of the burst strength (expressed in kilopascal) and the basis weight (expressed in g/m2).
Burst strength is measured using Tappi standard T403.
15 As used herein, the "tensile strength" is the maximum strength of randomly oriented pulp fibers when formed in a sheet. Tensile strength provides an indication of the maximum possible strength of pulp when beaten under ideal conditions. Several methods of measuring tensile strength are known in the art. "Zero span breaking strength", for example, is described in TAPPI T231. "Wet zero span tensile strength" of pulp is measured using TAPPI T273.
As used herein, "wet zero-span" testing measures the tensile strength of single fibers by testing hand sheets with a span as close to zero as possible. Using wet zero-span reduces the effect of bonds, and the resulting data can be used to describe deformation of fibers within each pulp.
Fiber length is one of the most important parameters of pulp. Pulp strength is directly proportional to fiber length and dictates its final use. Several methods of measuring fiber length of pulp are known in the art. The "fiber length of pulp by projection"
is described in TAPPI T232. The "fiber length of pulp by classification" is described in TAPPI T233.
"Fiber length of pulp and paper by automated optical analyzer using polarized light" is described in TAPPI T271. As used herein, the "length-weighted fiber length" is described in Tappi T271.
As used herein, "coarseness" is the weight per unit length of a cellulosic fiber. Fiber coarseness is described in TAPPI T234. Another method now commonly used relies on the measurement of the total length of a known mass of pulp fibers with an optical fiber length analyzer. Coarseness is obtained by dividing the pulp mass by the total measured length of the fibers.
As used herein, "fines" refers to the portion of fibers which are shorter than a specified length, typically less than 0.2 mm.
As used herein, "kink index" refers to the sum of the number of sharp bends within a range of kink angles divided by the total fiber length of all the fibers.
As used herein, "shape index" refers to the ratio of actual fiber length to the distance between the two fiber ends minus 1. Shape index indicates the continuous curvature of the fibers greater than 0.5 mm in length within the selected range limits.
As used herein, "rejects" refers to the material removed and discarded during the cleaning and screening of brown stock pulp. "% rejects" is the ratio of rejects to retained cellulosic pulp, expressed as a percentage.
As used herein, "viscosity" of a pulp provides an estimation of the average degree of polymerization of the cellulose fiber. Accordingly, viscosity indicates the relative .. degradation of cellulose fiber during the pulping and bleaching process.
The standard procedure of measuring pulp viscosity is described in TAPPI T230.
Standardized reference pulp can be processed by beating in a "PFI Mill" in accordance with ISO 5264/2 and TAPPI T-248. In a PFI Mill, a measured amount of pulp at specified concentration is beaten between a roll with bars and a smooth-walled beater .. housing, both rotating in the same direction but at different peripheral speeds. Beating action is achieved through the differential rotational action and the application of a specified load between the beater roll and the housing for a specified number of revolutions.
PFI Mill beating is a widely accepted method of simulating commercial refining practices. Physical testing of handsheets formed from this pulp helps predict the ultimate performance of pulp .. when converted to paper.
As used herein, "freeness" refers to the drainage time of a cellulosic pulp and is discussed in reference to market pulp and/or unrefined pulp. Freeness can provide an indication of: fiber length of pulp, as long fiber pulps have more freeness compared to short fiber pulps; fiber damage during pulping, bleaching or drying, as short fibers or fines .. produced during the pulping operation reduces pulp freeness; and refining energy required to achieve certain slowness during stock preparation. The standard procedure of measuring pulp freeness is described in TAPPI T221, T227, ISO 5267-1 and ISO 5267-2.
Canadian Standard Freeness, for example, is described by TAPPI T227 and reported as CSF.
"Pulp density" is calculated as the ratio between grammage and the thickness of the material and is expressed in g/cm3.
As used herein, "brightness" refers to the reflectance or brilliance of the pulp when measured under a specially calibrated blue light and is measured using Tappi standard T452.
As used herein, "porosity" refers to the permeability of a pulp to air.
Porosity is, among other things, an important factor in ink penetration and is measured using Tappi standard T460.
As used herein, "stiffness" refers to the slope of the tangent of the tensile strength-strain curve at the point of zero strain. The tensile stiffness (in N/m of width) is equal to the elastic modulus multiplied by the paper thickness. When the tensile stiffness is divided by .. the grammage, it is called the tensile stiffness index (Nm/kg), which numerically equals the specific elastic modulus (in Nrn/kg).
As used herein, "stretch" refers to the maximum tensile strain developed in the sample strip before rupture. The stretch or percentage elongation is expressed as a percentage and is measured using Tappi standard T404.
As used herein, "smoothness" refers to the surface uniformity of paper. Sheets that are flat and even provide better ink dot formation and sharper images and is measured using Tappi standard T538.
As used herein, "scattering coefficient" refers to the tendency of a sheet to scatter light and is measured using Tappi standard 1220.
As used herein, "collapse index" refers to the fractional loss of lumen volume that results from fiber processing. The collapse index depends on the treatment and fiber morphology, including fiber dimensions and the fiber wall material. The behavior of fibers as they collapse affects how fibers conform to one another in the sheet.
As used herein, a high HWRC pulp is a cellulosic pulp comprising at least 85%
cellulosic fibers from WRC and having the following physical characteristics:
a. a post-bleaching kappa between 0 and 5 b. a length-weighted fiber length between 1.8 and 2.2 mm;
c. a coarseness between of 0.06 and 0.16 mg/m;
d. a brownstock freeness of between 550 mL and 610 mL;
e. a tensile strength between 8.0 km and 9.5 km at 500 Csf; and tl a porosity between 20 Gurley secand 60 Gurley sec. at 500 Csf.
Accordingly, a "HWRC-like" pulp, as used herein, is a cellulosic pulp comprising less than 85% cellulolosic fibers from WRC but otherwise having the same physical characteristics, namely:

a. a post-bleaching kappa between 0 and 5 b. a length-weighted fiber length between 1.8 and 2.2 mm;
c. a coarseness between of 0.06 and 0.16 mg/m;
d. a brownstock freeness of between 550 mL and 610 mL;
e. a tensile strength between 8.0 km and 9.5 km at 500 Csf; and f. a porosity between 20 Gurley second 60 Gurley sec. at 500 Csf.
The species composition of a cellulosic pulp may be determined, for example, by conventional microscopy using PAPTAC procedures B2 or B7, or Tappi standard T401. A
HWRC-like pulp may comprise less than 80%, 70%, or 60% cellulosic fibers from WRC, and may comprise as little as 50% cellulosic fibers from WRC.
A HWRC-like pulp will comprise cellulosic fibers from a second source of lignocellulosic material. The cellulosic fibers from a second source of lignocellulosic material may comprise more than 20%, 30%, 40% of the cellulosic fibers of a HWRC-like pulp, and may comprise as much as 50% of the cellulosic fibers of a HWRC-like pulp.
A pulp comprising a mixture of cellulosic fibers from WRC and a second source of lignocellulosic material will be produced by the delignification of a blend of WRC materials and the second lignocellulosic material. HWRC-like pulps may be produced from the delignification of a blend comprising less than 80%, 70%, 60% lignocellulosic material from WRC by OD weight, and as little as 50% lignocellulosic material from WRC by OD
weight.
Correspondingly, the blend may comprise more than 20%, 30%, 40%
lignocellulosic material from the second source by OD weight, and may comprise as much as 50%
lignocellulosic material from the second source by OD weight.
Processes of producing a HWRC-like pulp comprising less than 80% WRC
In one aspect of the disclosed invention, a process is provided for delignifying a lignocellulosic material comprising a blend of WRC chip furnishes and a second lignocellulosic material to produce a HWRC-like pulp comprising less than 85%
WRC
fibres.
In one embodiment involving a batch process for delignifying lignocellulosic material comprising a blend of WRC chip furnishes and the second lignocellulosic material to produce a HWRC-like pulp comprising less than 80% WRC fibres, the lignocellulosic blend may be fed into a batch digester and held in an aqueous alkaline pulping solution under select temperature/pressure conditions for a calculated period of time, typically an H-factor of at least 1500, and preferably 1750, to attain desired pulp characteristics. The aqueous alkaline pulping solution may preferably include a mixture of sodium hydroxide and sodium sulfide. The cooked pulp may then be recovered into a different vessel to yield an amount of pulp suitable for further processing, such as chemical and/or heat recovery, washing, further digestive-type processing, or bleaching, prior to paper manufacturing.
Desired pulp characteristics may include, for example, a kappa in the range of 15-30.
Additional desired pulp characteristics may include fiber length, fiber coarseness, fiber strength, freeness, and porosity. Preferably, the pulp will have the characteristics of a HWRC-like pulp.
In another embodiment involving a continuous digestion process for delignifying lignocellulosic material comprising a blend of WRC chip furnishes and a second lignocellulosic material to produce a HWRC-like pulp, the blend is fed into an aqueous alkaline pulping solution at the feed end of a digester and controllably moved through zones of select temperature/pressure, typically an H-factor of at least 1500, and preferably 1750, to a regulated recovering end (i.e. a valve) to continuously yield pulp having desired characteristics. The aqueous alkaline pulping solution may preferably include a mixture of sodium hydroxide and sodium sulfide. The cooked pulp may then be recovered, i.e.
"blown", into a different zone to yield an amount of pulp suitable for further processing, such as chemical and/or heat recovery, washing, further digestive-type processing, bleaching, prior to paper manufacturing. Desired pulp characteristics may include, for example, a kappa in the range of 15-30. Bleaching may include oxygen delignification.
Bleached pulp may then be refined in a PFI mill at 0, 3000, 6000, and 9000 revolutions, and the like. Desired pulp characteristics may include, for example, a kappa in the range of 0-5.
Additional desired pulp characteristics may include fiber length, fiber coarseness, fiber strength, freeness, and porosity. Preferably, the pulp may have the characteristics of a HWRC-like pulp. Additional desired pulp characteristics may include fiber length, fiber coarseness, fiber strength, freeness, and porosity. Preferably, the pulp may have the characteristics of a HWRC-like pulp.
In a preferred embodiment the second source of lignocellulosic material may be a Yellow Cypress chip furnish. However it will be understood by one skilled in the art that several sources of lignocellulosic material could be of value. One of skill in the art will appreciate that any source of lignocellulosic material may be used provided that its fiber properties are generally compatible with the production of a HWRC-like pulp, and the differences in the pulping rate between WRC chips and the second lignocellulosic material do not cause bleaching issues or negatively impact the fiber coarseness of the resulting pulp.

Production of a HWRC-like pulp by a continuous process In another embodiment, a continuous process is provided for the production of a HWRC-like pulp. A continuous process for delignifying lignocellulosic material comprising 5 a WRC chip furnish and a second lignocellulosic material may include feeding the lignocellulosic blend into an aqueous alkaline pulping solution at the feed end of a continuous digester to produce a lignocellulosic mass. The second lignocellulosic material may be provided in a proportion that increases the density of the lignocellulosic mass to a density sufficient to allow the lignocellulosic mass to sink in the pulping solution.
10 Accordingly, the mass may be controllably moved through zones of select temperature/pressure in the pulping solution, typically with an H-factor of at least 1500, to a regulated recovery end (i.e. a valve) to continuously yield pulp having desired characteristics. The aqueous alkaline pulping solution may preferably include a mixture of sodium hydroxide and sodium sulfide. The cooked pulp may comprise less than 80% WRC
15 fibres. The cooked pulp may then be recovered into a different zone to yield an amount of pulp suitable for further processing, such as chemical and/or heat recovery, washing, further digestive-type processing, bleaching, prior to paper manufacturing. Bleaching may include oxygen delignification. Bleached pulp may then be refined in a PFI mill at 0, 3000, 6000, and 9000 revolutions, and the like. Desired pulp characteristics may include, for example, a 20 kappa in the range of 0-5. Additional desired pulp characteristics may include fiber length, fiber coarseness, fiber strength, freeness, and porosity. Preferably, the pulp may have the characteristics of a HWRC-like pulp.
In a preferred embodiment the second source of lignocellulosic material may be a Yellow Cypress chip furnish. However it will be understood by one skilled in the art that several sources of lignocellulosic material could be of value. One of skill in the art will appreciate that any source of lignocellulosic material may be used provided that its fiber properties are generally compatible with the production of a HWRC-like pulp, and the differences in the pulping rate between WRC chips and the second lignocellulosic material do not cause bleaching issues or negatively impact the fiber coarseness of the resulting pulp.
Cellulosic Pulps In another embodiment, the invention provides cellulosic pulps prepared according to the aforementioned processes. The pulps may comprise less than 80% WRC fibres.

Uses of blends of lignocellulosic materials In other embodiment, the invention provides a use for blends of lignocellulosic materials from WRC and a second source of lignocellulosic material for the aforementioned processes for the production of a HWRC-like pulp.
METHODS
Chip Sources For batch process cooks, WRC chip samples were obtained from Mill and Timber Sawmills in Surrey, British Columbia. Yellow Cypress and Sitka Spruce chip samples were obtained from S&R Sawmills in North Surrey, British Columbia. For continuous process cooks, WRC and Yellow Cypress chip samples were obtained from Delta Cedar Products in Delta, British Columbia.
Chip Drying Chips were dried to a constant moisture content for four days.
Chip Analysis Dry chips were analyzed for size distribution using a chip classifier. The accepts, which are those chips passing a 16 mm round hole screen but retained on a 7 mm round hole screen, were used for the pulping.
Bulk Density was determined by dividing the oven-dried weight of the chips by the volume it occupies (i.e. 10 L).
Batch cooking A 28-liter Weverk laboratory digester was used for each cook. Varying percent mixtures of Yellow Cypress, WRC, and Sitka Spruce chip furnishes were pulped along with pure samples of each species. The effective alkali and sulphidity of the kraft pulping liquor were 17.5% and 23.88%, respectively, and the liquor to wood ratio was 4.5:1.
Bleaching. A five stage bleaching process was followed as in Table 1. Based on Kappa values for each pulp after the oxygen delignification stage, the chlorine dioxide concentration for the D100 stage was determined. All stages that required oxygen were done in a Parr Reactor Model: No. 4551.

Table 1: Bleaching Conditions for WRC, Yellow Cypress, and 50/50 WRC/Yellow Cypress Mix BLEACHING STAGE WRC Yellow Cypress 50/50 Mix 02 Delignification NaOH 4.800/0 4.80% 4.80%
Oxygen 4.80% 4.800/0 4.80%
IVIgSO4 0.17% 0.17% 0.17%
Consistency 1%] 8.5% 8.5% 8.5%
Temperature 1 C] 87 / 92 87 / 92 87 / 92 Time [minutes] 20 /20 20 /20 20 /20 pressure (kPaG) 625 / 400 625 / 400 625 / 400 POW kappa 15.4 16.9 15.3 D100 WRC Yellow Cypress 50/50 Mix C102 as Kappa Factor 0.245 0.245 0.245 C102 in % charge as Cl2 3.77% 4.15% 3.74%
Consistency [%] 3.5% 3.5% 3.5%
PH after C102 2.8 2.8 2.8 End Process pH 2.7 2.7 2.7 Temperature 1 C] 53 53 53 Time [minutes] 25 25 25 Residual C102 (')/0 of Initial) 0 0 0 Eop WRC Yellow Cypress 50/50 Mix PH after 7 min 11.2 11.2 11.2 End Process pH 10.2 102 10.2 H202 0.25% 0.25% 0.25%
NaOH 1.68% 1.68% 1.68%
MgS0.4 0.00% 0.00% 0.00%
02 % appl 0.5 0.5 0.5 Consistency [%] 11 11 11 Temperature 1 C] 90 90 90 Time [minutes] 35 35 35 DI WRC Yellow Cypress 50/50 Mix C102 % applied 0.96% 0.96% 0.96%
NaOH in feed 0.033% 0.033% 0.033%
Consistency [%] 0.11 0.11 0.11 Temperature 1 C] 72 72 72 time (min) 142 142 142 NaOH in neutralization 1.130% 1.130% 1.130%
time (min) 3 3 3 D2 WRC Yellow Cypress 50/50 Mix C102 % applied 0.23% 0.23% 0.23%
NaOH in feed 0.004% 0.004% 0.004%
Consistency 1%1 11 11 11 Temperature 1 C] 72 72 72 time (min) 472 472 472 Continuous Cooks A 50/50 Mix of WRC/Yellow Cypress was processed in an Ahlstrom Kamyr Modified Continuous Cook (MCC) digester and a two stage medium consistency oxygen delignification system at Howe Sound Pulp and Paper ("HSPP"). The resulting pulp is herein referred to as "HS480". Tables 2, 3, 4, and 5 indicate the digester, 02delignification, and bleaching conditions under which HS480 was produced.
PFI Refining and Physical Property Testing Of Bleached Pulp Bleached pulp was refined in a PFI Mill at 0, 3000, 6000, and 9000 revolutions. Ten handsheets were made for each sample.
Physical Property Testing Of Bleached Pulp Five handsheets per refined PFI revolution point were tested for their physical and optical properties as per standard TAPPI methods. Unrefined fiber properties were analyzed using a L&W Fiber Tester (Lorentzen & Wettre, Sweden).

Table 2. Mill conditions HSPP during trial HS480 production.
Production rate for period 1030.0 Bleached ADt/d 27-Jan-2009 17:00 Start of trial 29-Jan-2009 13:00 End of trial Furnish: 50.7% Cypress 49.3% Cedar Digester Total white liquor 16.14 %EA on BD wood Average H-Factor 1589 HE
Average blow kappa 26.9 kappa 02 delignification 02 delig oxygen 25.19 kg/ADt 02 delig caustic+OWL 28.55 kg/ADt Magnesium sulphate 1.93 kg/ADt Average POW kappa 16.2 kappa Bleaching Do stage C102 18.22 kg/ADt Eop stage NaOH 21.78 kg/ADt Average Pop kappa 2.94 kappa DI stage C102 11.00 kg/ADt D1 stage upflow NaOH 0.32 kg/ADt D1 stage dilution zone NaOH 13.11 kg/ADt D2 stage C102 2.68 kg/ADt D2 stage NaOH 0.09 kg/ADt Final brightness off pulp machine 88.9 % ISO
Confocal Microscopy 5 Fibers were dyed with Acridin Orange dye, deposited on cover slips, dried, and mounted on glass slides. A Bio-Rad MRC-600 microscope attached to a Nikon Optiphot microscope equipped with a 60X objective lens was used to generate pulp fiber cross-sectional images. The prepared sample slides were scanned in such a way as to ensure random sampling of fibers. Each encountered fiber was oriented perpendicular to the laser 10 scanning direction. Cross-sectional images were then constructed from a series of horizontal line scans acquired from stepping the sample stage vertically in the z-direction through the thickness of the fiber in 0.2 pm increments. Image analysis was applied to the confocal images to define outer and inner boundaries from which the fiber transverse dimension data identified in Figure 1 is derived.

Table 3. Digester operating standards for downflow cooking at HSPP during trial I-1S480 production.
I VARIABLE IMIN<TARGET<MAX1 ______ 1 ___________________ ML 'Total ML charge %EAW 115.0< <17.01 1WL to HPF L/s I 5 IWL to feed system %EAW 111.0< <13.01 IWL to bottom circ. %EAW I 0.5< < 1.01 IWL to MC circ. %EAW I 3.5< < 4.01 IWL to wash circ. %EAW off IWL strength test g/L EA 75<
IWL clarity test ppm I <400 IBC residual test g/L EA I >12 'Upper extr. res. g/L EA 6< <8 ILower extr. res. g/L EA I 7 9 IWash extr. res. g/L EA I 4< <7 TemplChip bin top Deg C I 85 IBC temp SP Deg C I 154< <157 IMC temp SP Deg C I 158< <164 IBlow line Leg C I 85 IB1. lig. cooler Deg C I 85 FlowISV relief t/hr/RPM I 0.45 IChip Chute Pump Outlet I 17-18 threads 1Bottom circulation L/s I 180< <220 !Trim circ. L/s I off 1MC zone dilution factor I -4.0 to -3.0 1Dilution zone upflow L/s I +15 1CB to pipe L/s/ADt/d I 0.015 INC circulation L/s/ADt/d I 0.060 'Jump flow L/s/ADt/d I 0 'Main extraction L/s/RPM I 6< <9. 5 'Wash extraction L/s/ADt/d 0.05< <0.06 IB1. lig. filter rej. L/s I 5< < 8 IDiffuser dil. factor DF I 2< <3.5 PresISteaming vessel kPaG I 135 IH.P. feeder speed ratio I keep low 1No 1 flash tank kPaG I 165 1No 2 flash tank kPaG I 48 or 40 ______ 1 ___________________ 'Blow line kappa 34.0 EA = effective alkali %EAW = % effective alkali on wood. .
t/hr = tones per hour L/s/ADt/d = litres per second/air dried tonne/day %BD = % bone dry Table 4. 02 delignification operating standards at HSPP during trial HS480 production.
VARIABLE IMIN<TARGET<MAX1 --------------------- I
IFeed consistency % BDI 8.5 'First reactor Temp. Deg CI 87 'Reactor #1 pres. kPaGI 600 'Reactor 42 pres. kPaG1200<
-------------------- I
'Post 02 diffuser wash 1/51 'Mix tank dilution 1/s1250< <3001 IPOW vat dilution %I 80< <1001 1260t conductivity target uSI5000< <80001 'Temp to 260 t storage deg CI 60<
'Talc addition rate kg/ADtI 3.0 ITalc primary dilution 1/m1 15.0 !Talc flowrate 1/51 1.0 -------------------- I
IPOW Kappa, all grades I 16.0 IMgSO4: all grades: % appll 0.17 -------------------- I
'OWL recirc flow 1/316.0>
IPhase separator pres. kPaGI 600 IPhase separator temp. deg CI 140 ITemp. from coolers deg CI 90 -------------------- I
Fiber composition analysis Fiber composition of pulps was determined according to PAPTAC standards B.2 and B.7 standards. Briefly, a subsample of the pulp provided was dispersed and a slurry of approximately 0.05% consistency was made. Aliqouts of this slurry were deposited on glass slides and gently heated to dryness. Slides were stained with Graff C stain, coverslipped, and examined with a Nikon compound microscope. Fibers were identified primarily on the basis of morphology of the cross-field pitting areas of earlywood fibres. Weight factors were taken from The Practical Identification of Wood Pulp Fibers, Parham and Gray, Tappi Press, 1990.

Table 5. Bleach operating standards at HSPP during trial HS480 production.
VARIABLE IMIN<target<MAX1 DcIB. S. consistency % BD I 3.5 'Vat pH test pH I 2.6 IDc tower inlet pH pH I 2.6< <2.9 I
IKappa factor KF 0.18< <0.26I
IVat residual test g/L I 0< <0.02I
'Bottom showers % split Dca=75 Dcb=60I
1Top showers DF I 0.6 1.0 EopISteam mixer temp deg C I 92.0 'Peroxide application % 0.25 'Oxygen application 0.5 1MgSO4 application I 0.0 'Tower level 75 'Tower exit pH pH I 10.2 'Bottom showers % splitl 75 'Top shower bar DF I 0.6< <1.0 _____ 1 ___________________ Dn 1Upflow temp deg C 71.0< <75.01 1Dpflow res sample g/L 0.20< <0.401 1Upflow pH sample pH I 4.2 1Vat pH I 8.5 1Tower level 75 'Bottom showers % splitl 75 'Top shower bar OF I 0.6< <1.0 1Repulper sheet brt % ISO 85.0< <87.01 D2 IUpflow temp deg C 71.0< <75.01 Ippflow res sample g/L 0.10< <0.401 IUpflow pH sample pHI 4.2 'Tower level I 75 1 All showers OF I 0.6< <1.0 1 IRepulper sheet brt % ISO 90.0< <90.51 _____ 1 _____________________________ 1 !Bleach HW Temp deg C I 70 1 'Blue Scrubber Liquor pH I 10.0 1 ________________________________________ 1 1Machine brightness %ISO 189.0<
'Machine dirt specks/kg I <15.01 IMachine shives number I < 5.01 'Machine viscosity CP 114.0< 1 EXAMPLES:
Example 1. Small Batch Cooks Chip Classification WRC chips had the highest 16mm accepts and the lowest rejects compared to the Yellow Cypress chips and Sitka Spruce chips (Figure 2). Sitka Spruce had the highest 7mm accept chips. Yellow Cypress has the highest basic and bulk densities (Figures 3 and 4).

Figure 4 shows that WRC has the lowest bulk density, occupying ¨26.5% less volume in a 10 L container when compared to Yellow Cypress.
Kraft Pulping of Sitka Spruce, WRC and Yellow Cypress Blends Varying percent mixtures of Yellow Cypress, WRC, and Sitka Spruce chips were pulped along with pure samples of each species in a 28 L Weverk laboratory batch digester.
Each cook required four 750g OD chips per basket. A total of 12 blends were pulped, and the resulting data is outlined in Table 6. The initial cooked blends of WRC/Yellow Cypress and WRC/Sitka spruce underwent fiber analysis, PFI refining, and testing for physical properties.
Table 6 shows the cooking data for the blends. The 100% Yellow Cypress sample resulted in the highest yield. All blends with higher Yellow Cypress contents resulted in higher yields when compared to the Sitka Spruce blends.
Yellow Cypress chips required additional cooking time than WRC chips and Sitka Spruce chips (Figure 5), and the shape of the curves indicated that additional optimization in terms of chemical charge and cooking temperature might be required in order to ensure acceptable production rates and bleaching efficiency of Yellow Cypress.
Samples containing higher percentages of Yellow Cypress chips were generally harder to cook and required additional cooking time to achieve comparable kappa than samples containing higher percentages of WRC or Sitka Spruce (Table 6, Figure 6). These preliminary results suggested that Yellow Cypress would not cook well together with WRC to produce a HWRC-like pulp.
Nevertheless, blends with higher Yellow Cypress or 100% Yellow Cypress resulted in ¨4% higher unscreened yield values than WRC at any given kappa number (Figure 7).
The unscreened yield of Sitka spruce is similar to that of WRC at the kappa number 25-30 range (Figure 8). This observation, in addition to the low basic and bulk density of Sitka Spruce, suggests that Sitka Spruce would be an inferior candidate to Yellow Cypress for mixing with WRC.
Figures 9 to 16 depict the fiber properties of the various WRC, Yello Cypress, ans Sitka Spruce blends. The control and blends containing Sitka Spruce, for example, exhibited inferior breaking length by >1.5km compared to WRC and Yellow Cypress-containing pulps (Figure 9). Yellow Cypress-containing pulps maintained superior fiber strength despite requiring additional cooking.

Table 6. Summary of Resulting Data from Small Cooks OD wt H- % Yield A Weight of % Yield Chip Blends Cooked of Kappa Factor Unscreened Rejects Screened Pulp Screened Pulp Pulp Red Cedar 1750 308.1 41.10% 0.70% 305.87 40.80%
23.1 Sitka Spruce 1750 313.6 41.80% 1.20% 309.79 41.30%

Yellow Cypress 1825 358.8 47.80% 1.10% 354.88 47.30%
27.4 20/80 Sitka Spruce/Red Cedar 1750 297.5 39.70% 1.00%
294.6 39.30% 24.7 40/60 Sitka Spruce/Red Cedar 1750 306.3 40.80% 0.50%
304.68 40.60% 24.4 60/40Sitka Spruce/Red Cedar 1750 298.5 39.80% 0.90% 295.89 39.50%
23.6 80/20 Sitka Spruce/Red Cedar 1750 325 43.30% 0.80%
322.38 43.00% 23.8 20/80 Yellow/Red Cedar 1750 322.9 43.10% 1.30% 318.77 42.50%
21.9 40/60Yellow/Red Cedar 1750 327 43.60% 1.50% 322.15 43.00%
-- 23.4 50/50Yellow/Red Cedar 1825 331.7 44.20% 1.10% 328.02 43.70%
26.3 60/40Yellow/Red Cedar 1825 320.6 42.70% 1.40% 316.27 42.20% 27.8 80/20Yellow/Red Cedar 1825 333.9 44.50% 1.50% 328.88 43.90%
27.6 5 Example 2. Large Batch Cooks for Bleaching Part 1. Cooking A 28 L Weverk laboratory digester was used for three large cooks consisting of a 10 50/50 Mix of WRC and Yellow Cypress (the "50/50 Mix"), 100% WRC, and 100% Yellow Cypress. Each cook required 3000 g OD weight of chip furnishes. 90 minutes was given to reach the maximum temperature of 170 C.
Table 7: Cooking Results from Large Cooks Sample H- OD wt % Yield % Weight of % Yield Kappa Factor of Pulp Unscreened Rejects Screened Screened Pulp Pulp WRC 1750 1210.6 40.4% 1.6% 1191.51 39.7% 27.1 Yellow 1825 1375.8 45.9% 2.3% 1343.66 44.8% 30.0 Cypress 1778 1242.7 41.4% 2.5% 1211.74 40.4% 28.1 Mix Table 7 shows the cooking data for the three large cooks, which were cooked at different H-Factors since Yellow Cypress is harder to pulp and thus requires more time for pulping. WRC reached the targeted 27.0 kappa, while Yellow Cypress was 3 kappa points __ higher. Thus, WRC experiences a higher extent of delignification when compared to Yellow Cypress. The 50/50 Mix had a kappa closer of 28.1.
WRC showed the lowest yield. Yellow Cypress had the highest percent screened yield, with 5.5 and 5.1 percent higher unscreened and screened yield than WRC.
The 50/50 Mix provided a very similar yield to WRC.
The percent rejects for Yellow Cypress were 0.7% percent higher than WRC. The 50/50 Mix had the highest percent rejects.
Part 2. Bleaching Process and Refining Table 8 shows that Yellow Cypress experienced the highest kappa reduction after the 02 delignification stage ("02 delignification") while WRC experienced the least kappa reduction. The 50/50 Mix had a kappa reduced by 1.1 more than WRC.
Table 8: Kappa Post Cook and 02 Delignification Comparison Post 02 Resulting Kappa Sample Post Cook Kappa Delignification Reduction WRC 27.1 15.4 11.7 Yellow Cypress 30.0 16.9 13.1 50/50 Mix 28.1 15.3 12.8 Table 9 tabulates the residual chemicals for the D100, DI, and D2 stage. There were no significant differences between WRC, Yellow Cypress, and the 50/50 Mix in the pH and C102 residuals found in each stage.

Table 9: D100, D1, and D2 pH and Residual Results Bleaching Stage .. Red Cedar Yellow Cypress Red/Yellow % Residual C102 0.1 0.0 0.1 D100 Stage Final pH 2.56 2.57 2.59 % Residual C102 0.4 0.4 0.4 D1 Stage Final pH 12.13 12.17 12.17 % Residual C102 1.0 0.8 0.8 D2 Stage Final pH 9.25 9.52 9.28 Part 3. Physical Testing Figures 9 to 27 depict the pulp properties of the WRC, Yellow Cypress, and Mix.
Fiber length and shape Table 10 shows the fiber property data for the unrefined pulps. All analysis was done on Okw energy refined pulp. The results show similar fiber length and coarseness for the laboratory pulps, although the 50/50 Mix had the highest fiber length and the lowest coarseness.
The fiber length distribution shows that WRC had the longest fibers, with lengths between 3.5 to 5.5 mm, while Yellow Cypress had the most fibers within the 1.5 and 3.5 mm range (Figure 17).
The shape factor distribution shows Yellow Cypress had the most fibers with a shape factor of 90 % (Figure 18).
Table 10: Average Bleached Pulp Fiber Properties Sample LW Coarseness % Fines Kink Index Shape Fiber (mgim) Length (mm) WRC 2.233 0.110 28.1 1.769 82.047 Yellow Cypress 2.151 0.104 25.2 1.876 82.891 50/50 2.243 0.104 23.7 1.859 82.408 WRC/Yellow Cypress HS 400 2.172 0.111 30.5 1.414 85.380 HS 440 2.2675 0.124 50.6 1.607 84.338 Pulp Quality The pulp quality results obtained from the PFI Mill processed pulps are indicated in Figures 19 to 27 The 50/50 Mix generally had higher CSF than WRC for each revolution point tested (Figure 19). The fines content as reported in Table 10 correlate with the CSF
values reported in Figure 19.
The WRC, Yellow Cypress, and the 50/50 Mix had higher similar densities (Figure 20).
The final brightness of WRC, Yellow Cypress, and the 50/50 Mix were lower than the targeted ISO 86 brightness (Figure 21). Yellow Cypress showed the highest brightness while WRC had the lowest resulting brightness out of the three test samples.
WRC, Yellow Cypress, and the 50/50 Mix samples had similar tensile breaking length values for any given level of PFI refining (Figure 22).
Yellow Cypress and the 50/50 Mix had higher tear indices than WRC at lower PFI
revolutions (Figure 23). As the samples near 3000 and 6000 revolutions, the disparity between the samples decreased.
WRC and Yellow Cypress showed almost identical burst strengths (Figure 24).
The 50/50 Mix had the highest burst strength.
WRC had the lowest wet zero-span of all samples (Figure 25). The wet zero-span of the 50/50 Mix was only slightly less than the Yellow Cypress. WRC has the longest fibers with lengths between 3.5 to 5.5 mm, while Yellow Cypress has the most fibers within the 1.5 and 3.5 mm range (Figure 26).
The WRC, Yellow Cypress, and the 50/50 Mix pulps had very similar shape factor distributions (Figure 27).
EXAMPLE 3. Continuous Cook A 50/50 mix of WRC and Yellow Cypress chip furnishes was processed in an Ahlstrom Kamyr Extended Modified Continuous Cook (EMCC) digester running in downflow mode and two stage medium consistency oxygen delignification system at Howe Sound Pulp and Paper. The resulting pulp is herein referred to as "HS480".
The manufacturing conditions are reported in Tables 3, 4, and 5.
Fiber measurements of HS480, as aided by confocal microscopy, are reported in Table 11. The fiber properties of HS480 pulp are reported in Tables 12 and 13.
The fiber length distribution of HS-480 pulp is depicted in Figure 28. The fiber width distribution is depicted in Figure 29.
Figures 30 reports the fiber property distributions of HS480 pulp as determined by confocal microscopy.
Table 11: Average fiber properties for HS 480.
Mean Min Max ' SD
Sample_SD
A (pm2) 88.4581 25.5057 226.1656 32.8115 2.2377 P (p-1m) 66.3396 22.6062 121.3298 19.6315 1.3389 T (pm) 1.4228 0.497 4.7586 0.645 0.044 LA (pm) 6.8082 0 131.827 16.8845 1.1515 Dmax (pm) 32.8316 12.1576 60.091 9.6519 0.6583 Dmin (pm) 5.5474 1.0707 16.5979 2.4694 0.1684 FT (pm) 3.1211 0.9494 10.7767 1.6754 0.1143 AR (pm) 0.1938 0.0319 0.7548 0.1288 0.0088 Cl 0.9341 0 1 0.1841 0.0126 C2 0.8593 0 1 0.2739 0.0187 RA 174.5381 29.0889 551.3673 77.1214 5.2596 TA 95.2663 25.5057 357.9926 42.8802 2.9244 LA% 4.748 0 50.3326 9.5126 0.6488 LP (pm) 60.3709 14.7973 119.1196 20.7038 1.412 CL (pm) 53.5359 0 119.1196 25.6076 1.7464 UCL (pm) 6.835 0 66.744 12.6969 0.8659 OFP (pm) 72.9764 27.5142 124.9682 18.5732 1.2667 FC 0.2546 0.0666 0.846 0.1456 0.0099 23.4471 6.6621 80.0828 11.6069 0.7916 A Fiber wall cross-sectional area Fiber centre-line perimeter Fiber wall thickness 5 LA Lumen area Dmax Fiber width, longest Feret diameter Dmin Fiber thickness, shortest Feret diameter FT Fiber thickness=(A+LA)/Dmax AR Aspect ratio, Dmin/Dmax 10 Cl Collapse index, 1-LA/LAo C2 1-collapsed lumen perimeter/original lumen perimeter LP Lumen perimeter CL Collapsed lumen perimeter UCL Uncollapsed lumen perimeter 15 OFP Outer fiber perimeter FC Form circle z-parameter Table 12: Average fiber properties of I-IS 480.

Fiber wall cross sectional area 88 +/- 2 (Imo Fiber perimeter (p,m) 66 +/- 1 Fiber wall thickness (ftm) 1.42 +/- 0.04 Lumen perimeter (pm) 8.5 +/- 0.4 Aspect ratio (Dmin/Dmax) 0.19 +/- 0.01 Collapse Index (1-LA/LA0) 0.93 +/- 0.01 Fines (%) 0.110 Table 13: Average fiber properties of HS 480.
LW Fiber Coarsness Canadian Tensile Porosity Length (mm) (mg/m) Standard breaking (Gurley sec at Freeness length at 500 500 Csf Csf 2.002 0.110 598 8.40 26.4 The freeness and tensile breaking length of HS480 are depicted in Figures 31 and 32.
The Wet Zero Span measurements of H5480 are depicted in Figure 33. The density of 11S480 is depicted in Figure 34. Sheet porosity is depicted in Figure 35. The smoothness of 11S480 is depicted in Figure 36. Light scattering of HS 480 is depicted in Figure 37. The stiffness of HS480 is depicted in Figure 38. Finally, HS480 stretch values are depicted Figure 39.

Claims (49)

What is claimed is:

1. A continuous process for delignifying lignocellulosic material, comprising:
feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution at a feed end of a digester, wherein the Thuja plicata chip furnish is about 50% or more of the blend by oven dry weight, to produce a lignocellulosic mass, wherein the second lignocellulosic material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution so as to move the mass through the digester to produce a cellulosic pulp under conditions having an H-Factor of at least 1500;
recovering the cellulosic pulp at a recovery end of the digester; and bleaching the cellulosic pulp to produce a bleached pulp having:
a. a post-bleaching kappa no greater than 5;
b. an average length weighted fiber length no greater than 2.2 mm;
c. a coarseness of no more than 0.16 mg/m;
d. a freeness no greater than 610 mL;
e. a tensile strength of at least 8.0 km at 500 Csf; and f. a porosity no greater than 60 Gurley sec. at 500 Csf.

2. The continuous process according to claim 1, wherein the post-bleaching kappa is greater than zero.

3. The continuous process according to either one of claims 1 or 2, wherein the average length weighted fiber length is no less than 1.8 mm.

4. The continuous process according to any one of claims 1 to 3, wherein the freeness is no less than 550 mL.

5. The continuous process according to any one of claims 1 to 4, wherein the tensile strength is no more than 9.5 km at 500 Csf.

6. The continuous process according to any one of claims 1 to 5, wherein the porosity is no less than 20 Gurley sec.at 500 Csf.

7. The continuous process of any one of claims 1 to 6, wherein less than 80% of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

8. The continuous process of any one of claims 1 to 7, wherein the Thuja plicata chip furnish comprises less than 80% of the blend by oven dry weight.

9. The continuous process according to any one of claims 1 to 8, wherein the second source of lignocellulosic material is a Callitropsis nootkatensis chip furnish.

10. A process for delignifying lignocellulosic material, comprising:
feeding a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass, wherein the Thuja plicata chip furnish is between 50%
and 85% of the blend by oven dry weight, to produce a cellulosic pulp under conditions having an H-Factor of at least 1500; and recovering the cellulosic pulp from the digester, wherein the cellulosic pulp has:
a. a kappa no greater than 30;
b. a yield of at least 38%.

11. The process according to claim 10, wherein the process is a continuous process.

12. The process according to claim 11, comprising a further step of bleaching the cellulosic pulp to produce a bleached pulp having:
a. a post-bleaching kappa no greater than 5;
b. an average length weighted fiber length no greater than 2.2 mm;

c. a coarseness of no more than 0.16 mg/m;
d. a freeness no greater than 610 mL;
e. a tensile strength of at least 8.0 km at 500 Csf; and f. a porosity no greater than 60 Gurley sec. at 500 Csf.

13. The process according to claim 11 or 12, wherein the post-bleaching kappa is greater than zero.

14. The process according to claim 12 or 13, wherein the length weighted fiber length is no less than 1.8 mm.

15. The process according to any one of claims 12 to 14, wherein the freeness is no less than 550 mL.

16. The process according to any one of claims 12 to 15, wherein the tensile strength is no more than 9.5 km at 500 Csf.

17. The process according to any one of claims 12 to 16, wherein the porosity is no less than 20 Gurley sec.at 500 Csf.

18. The process according to any one of claims 10 to 17, wherein the Thuja plicata chip furnish comprises less than 80% of the blend by oven dry weight.

19. The process according to any one of claims 10 to 18, wherein less than 85%
of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

20. The process according to any one of claims 10 to 18, wherein less than 80%
of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

21. The process according to any one of claims 10 to 20, wherein the second source of lignocellulosic material is a Callitropsis nootkatensis chip furnish.

22. Use of a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material, wherein the Thuja plicata chip furnish is about 50%
or more of the blend by oven dry weight, in the preparation of a cellulosic pulp by a continuous process, the process comprising:
feeding the lignocellulosic blend into an aqueous alkaline pulping solution at a feed end of a digester, to produce a lignocellulosic mass, wherein the second lignocellulosie material is provided in a proportion that increases the density of the mass so that the mass sinks in the pulping solution so as to move the mass through the digester to produce the cellulosic pulp under conditions having an H-Factor of at least 1500;
recovering the cellulosic pulp at a recovery end of the digester; and bleaching the cellulosic pulp to produce a bleached pulp having:
a. a post-bleaching kappa no greater than 5;
b. a yield of at least 38%;
c. an average length weighted fiber length no greater than 2.2 mm;
d. a coarseness no more than 0.16 mg/m;
e. a freeness no greater than 610 mL:
f. a tensile strength of at least 8.0 km at 500 Csf; and g. a porosity no greater than 60 Gurley sec. at 500 Csf.

23. The use according to claim 22, wherein the post-bleaching kappa is greater than zero.

24. The use according to either one of claims 22 or 23, wherein the length weighted fiber length is no less than 1.8 mm.

25. The use according to any one of claims 22 to 24, wherein the freeness is no less than 550 mL.

26. The use according to any one of claims 22 to 25, wherein the tensile strength is no more than 9.5 km at 500 Csf.

27. The use according to any one of claims 22 to 26 wherein the porosity is no less than 20 Gurley sec.at 500 Csf.

28. The use according to of any one of claims 22 to 27, wherein less than 80%
of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

29. The use according to any one of claims 22 to 28, wherein the Thuja plicata chip furnish comprises less than 80% of the blend by oven dry weight.

30. The use according to any one of claims 22 to 29, wherein the second source of lignocellulosic material is a Callitropsis nootkatensis chip furnish.

31. Use of a lignocellulosic blend comprising a Thuja plicata chip furnish and a second lignocellulosic material, wherein the Thuja plicata chip furnish is about 50%
or more of the blend by oven dry weight, in the preparation of a cellulosic pulp, the use comprising:
feeding the lignocellulosic blend into an aqueous alkaline pulping solution in a digester to produce a lignocellulosic mass, wherein the Thuja plicata chip furnish comprises less than 85% of the blend by oven dry weight, to produce the cellulosic pulp under conditions having an H-Factor of at least 1500 and recovering the cellulosic pulp from the digester, wherein the cellulosic pulp has:
a. a kappa no greater than 30; and b. a yield of at least 38%.

32. The use according to claim 31, wherein the digester is a continuous digester.

33. The use according to claim 32, wherein the process comprises a further step of bleaching the cellulosic pulp to have:
a. a post-bleaching kappa no greater than 5;
b, an average length weighted fiber length no greater than 2.2 mm;

c. a coarseness of no more than 0.16 mg/m;
d. a freeness no greater than 610 mL;
e. a tensile strength of at least 8.0 km at 500 Csf; and f. a porosity no greater than 60 Gurley sec. at 500 Csf.

34. The use according to claim 33, wherein the post-bleaching kappa is greater than zero.

35. The use according to either one of claims 33 or 34, wherein the length weighted fiber length is no less than 1.8 mm.

36. The use according to any one of claims 33 to 35, wherein the freeness is no less than 550 mL.

37. The use according to any one of claims 33 to 36, wherein the tensile strength is no more than 9.5 km at 500 Csf.

38, The use according to any one of claims 33 to 37, wherein the porosity is no less than 20 Gurley sec.at 500 Csf.

39. The use according to any one of claims 33 to 38, wherein less than 85% of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

40. The use according to any one of claims 31 to 39, wherein the Thuja plicata chip furnish comprises less than 80% of the blend by oven dry weight.

41. The use according to any one of claims 31 to 39 40, wherein less than 80%
of the fibers comprising the cellulosic pulp are Thuja plicata fibers.

42. The use according to any one of claims 31 to 41, wherein the second source of lignocellulosic material is a Callitropsis nootkatensis chip furnish.

43. A bleached pulp prepared according to the process of any one of claims 1 to 6, wherein between 50% and 85% of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.

44. The cellulosic pulp of claim 43, wherein between 50% and 80% of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.

45. The cellulosic pulp of either of claims 43 or 44, comprising Callitropsis nootkatensis fibers.

46. A cellulosic pulp prepared according to the process of any one of claims 10 to 18, wherein the cellulosic pulp has a kappa no greater than 5, and wherein between 50% and 85%
of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.

47. The cellulosic pulp of claim 46, comprising Callitropsis nootkatensis fibers.

48. The cellulosic pulp of claim 46 or 47, wherein between 50% and 80% of the fibers of the cellulosic pulp by oven dry weight are Thuja plicata fibers.

49. The cellulosic pulp of any one of claims 46 to 48, comprising Callitropsis nootkatensis fibers.