CA2633808A1 - Manufacture method of single phase aragonite precipitated calcium carbonate by controlling calcium ion - Google Patents
Manufacture method of single phase aragonite precipitated calcium carbonate by controlling calcium ion Download PDFInfo
- Publication number
- CA2633808A1 CA2633808A1 CA002633808A CA2633808A CA2633808A1 CA 2633808 A1 CA2633808 A1 CA 2633808A1 CA 002633808 A CA002633808 A CA 002633808A CA 2633808 A CA2633808 A CA 2633808A CA 2633808 A1 CA2633808 A1 CA 2633808A1
- Authority
- CA
- Canada
- Prior art keywords
- aqueous solution
- suspension
- phase aragonite
- controlling
- manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is related to the methods of manufacture of single-phase aragonite by controlling calcium ions, particularly, to the methods of manufacture of single-phase aragonite in the solution process by controlling the rate of elution of calcium ions in the suspension of calcium hydroxide by adding the highly concentrated aqueous solution of sodium hydroxide to the suspension of calcium hydroxide and adding the aqueous solution of sodium carbonate to the above mixed aqueous solution at a constant rate. The method of manufacture of single-phase aragonite according to the present invention is characterized by containing no calcite practically since this method is comprised of the steps of manufacturing a suspension in which calcium hydroxide is dispersed in distilled water; controlling calcium ions in the suspension of calcium hydroxide by adding the aqueous solution of sodium hydroxide to the suspension; and supplying the aqueous solution of sodium carbonate at a constant rate while stirring the suspension of calcium hydroxide.
Claims (6)
1. A method of manufacture of single-phase aragonite by controlling calcium ions comprising the steps of:
manufacturing 0.2 to 3 mol/L suspension of calcium hydroxide in which calcium hydroxide is dispersed in distilled water;
manufacturing a mixed solution by adding 3 to 10 mol/L aqueous solution of sodium hydroxide to said suspension of calcium hydroxide; and manufacturing single-phase aragonite by inserting the aqueous solution of sodium carbonate to said mixed solution at a constant rate while stirring said mixed solution.
manufacturing 0.2 to 3 mol/L suspension of calcium hydroxide in which calcium hydroxide is dispersed in distilled water;
manufacturing a mixed solution by adding 3 to 10 mol/L aqueous solution of sodium hydroxide to said suspension of calcium hydroxide; and manufacturing single-phase aragonite by inserting the aqueous solution of sodium carbonate to said mixed solution at a constant rate while stirring said mixed solution.
2. The method of manufacture of single-phase aragonite by controlling calcium ions in Claim 1, characterized by that the concentration of said aqueous solution of sodium carbonate is 0.1 to 1 mol/L, and the rate of insert of said aqueous solution of sodium carbonate is 1 to 5 ml/minute.
3. The method of manufacture of single-phase aragonite by controlling calcium ions in Claim 2, characterized by that the reaction temperature in said step of manufacturing single-phase aragonite is 60 to 80 °C
4. The method of manufacture of single-phase aragonite by controlling calcium ions in Claim 3, characterized by that the concentration of said aqueous solution of sodium hydroxide is to 8 mol/L.
5. Single-phase aragonite characterized by having no calcite contained practically as said single-phase aragonite is manufactured according to a method of manufacture comprising the steps of:
manufacturing 0.2 to 3 mol/L suspension of calcium hydroxide in which calcium hydroxide is dispersed in distilled water;
manufacturing a mixed solution by adding 5 to 8 mol/L aqueous solution of sodium hydroxide to said suspension of calcium hydroxide; and manufacturing single-phase aragonite by inserting 0.1 to 0.5 mol/L aqueous solution of sodium carbonate to said mixed solution at a rate of 1 to 5 mL/minute while stirring said mixed solution at 75 to 80 °C
manufacturing 0.2 to 3 mol/L suspension of calcium hydroxide in which calcium hydroxide is dispersed in distilled water;
manufacturing a mixed solution by adding 5 to 8 mol/L aqueous solution of sodium hydroxide to said suspension of calcium hydroxide; and manufacturing single-phase aragonite by inserting 0.1 to 0.5 mol/L aqueous solution of sodium carbonate to said mixed solution at a rate of 1 to 5 mL/minute while stirring said mixed solution at 75 to 80 °C
6. The single-phase aragonite in Claim 5, characterized by that said single-phase aragonite shows no calcite peaks in the x-ray diffraction pattern.