CA2620504A1 - Printed thermoformable laminate with increased security against forgery - Google Patents
Printed thermoformable laminate with increased security against forgery Download PDFInfo
- Publication number
- CA2620504A1 CA2620504A1 CA002620504A CA2620504A CA2620504A1 CA 2620504 A1 CA2620504 A1 CA 2620504A1 CA 002620504 A CA002620504 A CA 002620504A CA 2620504 A CA2620504 A CA 2620504A CA 2620504 A1 CA2620504 A1 CA 2620504A1
- Authority
- CA
- Canada
- Prior art keywords
- film
- laminate
- pvc
- thermoformable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The invention relates to a printed thermoformable laminate comprised of at least two plastic films. The printing is placed between plastic films inside the laminate in order to increase protection against forgery. Preferred laminates have the following structure: film A / print / laminating agent /
film C; film A / print / laminating agent / film B / laminating agent / film C, and; film A / print / laminating agent / film B / laminating agent / print / film C.
film C; film A / print / laminating agent / film B / laminating agent / film C, and; film A / print / laminating agent / film B / laminating agent / print / film C.
Description
Printed thermoformabMe laminate with increased security against forgery The invention relates to a printed thermoformable laminate made of at least two plastics material films.
Thermoformable plastics material laminates may be printed for customer information before or after forming. The printing of the laminates before the thermoforming into containers or beakers takes place prirriarily on the container wall with current printirig methods. If the plastics material laminate is printed before the thermoforming the printing may detach to a greater or lesser extent from the laminate surface during forming or during the logistics because of the reduced adhesion of the printing dyes to the background, as a function of the degree of forming.
In the two cases of conventional printing, the print is located on the outside of the laminate surface formirig the packaging and is therefore easily accessible for forgeries, in that the print can be removed from the packaging and can easily be replaced by printing on new information.
When using pre-printed laminates, there is also the possibility that these may be produced by forgers, as plastics material films and laminates made of plastics materials are available to an almost unlimited extent commercially.
The invention is based on the object of providing a thermoformable laminate of the type mentioned at the outset with a printing such that, in comparison to the printed thermoformable laminates according to the prior art, a substantially higher degree of security against forgery is produced.
The fact that the printing is arranged between adjacent plastics material films to increase the security against forgery leads to the achievement of the object according to the invention.
The followirig structures are preferred for the laminates according to the invention:
film A/ print / laminating means / film C
film A/ print i laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating rrieans / print / film C.
The films A, B and C; are thermoformable plastics material films based on chlorinated hydrocarboris, such as polyvinyl chloride and polyvinylidene chloride, chlorofluorocarbons, for example ACLARO, polyolefins, polyethyleneterephthalates, polyacrylonitriles, for example BAREX , cycloolefin copolymers, cycloolefiri polymers, polysulphones or biologically degradable plastics materials, or combinations of these plastics materials in the laminate.
PVDC may be a film or a coating.
The total thickness of the laminates is 150 to 500 pm and also 90 to 150 pm in PVC/PE laminates.
The lamination takes place with laminatirig adhesives based on water, with solvent-based or solvent-free laminating adhesives and/or by extrusion lamination as monoextrusion or coextrusion. In the case of COC or COP laminates with PE
or PP, a lacquer lamination or else the production of a partial laminate by coextrusion is recommended.
The interlaminar bond of the individual layers should be at least 2 N/15 mm.
When using dyed films for the printing, the colour of the printed image may be changed by a corresponding choice of colour. For example, blue printing of a film which is dyed yellow leads to a printed image which appears green. The security against forgery of printed laminates cari be further iricreased with colour combinations of this type.
The preferred film combinations for the laminates according to the invention are compiled in Table 1. The abbreviations of the plastics materials on which the films are based mean~
Thermoformable plastics material laminates may be printed for customer information before or after forming. The printing of the laminates before the thermoforming into containers or beakers takes place prirriarily on the container wall with current printirig methods. If the plastics material laminate is printed before the thermoforming the printing may detach to a greater or lesser extent from the laminate surface during forming or during the logistics because of the reduced adhesion of the printing dyes to the background, as a function of the degree of forming.
In the two cases of conventional printing, the print is located on the outside of the laminate surface formirig the packaging and is therefore easily accessible for forgeries, in that the print can be removed from the packaging and can easily be replaced by printing on new information.
When using pre-printed laminates, there is also the possibility that these may be produced by forgers, as plastics material films and laminates made of plastics materials are available to an almost unlimited extent commercially.
The invention is based on the object of providing a thermoformable laminate of the type mentioned at the outset with a printing such that, in comparison to the printed thermoformable laminates according to the prior art, a substantially higher degree of security against forgery is produced.
The fact that the printing is arranged between adjacent plastics material films to increase the security against forgery leads to the achievement of the object according to the invention.
The followirig structures are preferred for the laminates according to the invention:
film A/ print / laminating means / film C
film A/ print i laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating rrieans / print / film C.
The films A, B and C; are thermoformable plastics material films based on chlorinated hydrocarboris, such as polyvinyl chloride and polyvinylidene chloride, chlorofluorocarbons, for example ACLARO, polyolefins, polyethyleneterephthalates, polyacrylonitriles, for example BAREX , cycloolefin copolymers, cycloolefiri polymers, polysulphones or biologically degradable plastics materials, or combinations of these plastics materials in the laminate.
PVDC may be a film or a coating.
The total thickness of the laminates is 150 to 500 pm and also 90 to 150 pm in PVC/PE laminates.
The lamination takes place with laminatirig adhesives based on water, with solvent-based or solvent-free laminating adhesives and/or by extrusion lamination as monoextrusion or coextrusion. In the case of COC or COP laminates with PE
or PP, a lacquer lamination or else the production of a partial laminate by coextrusion is recommended.
The interlaminar bond of the individual layers should be at least 2 N/15 mm.
When using dyed films for the printing, the colour of the printed image may be changed by a corresponding choice of colour. For example, blue printing of a film which is dyed yellow leads to a printed image which appears green. The security against forgery of printed laminates cari be further iricreased with colour combinations of this type.
The preferred film combinations for the laminates according to the invention are compiled in Table 1. The abbreviations of the plastics materials on which the films are based mean~
PVC polyvinyl chloride PVDC polyvinylidene chloride PAN polyacrylonitrile PE polyethylene of various densities, including the metallocenes PP polypropylenes, including the rnetallocenes COC cycloolefir copolymer COP cycloolefir polymer PSU polysulphone PCTFE polychlorotrifluoroethylene EVOH ethylene vinyl alcohol PGA polyglycolic acid Containers thermoformed from the laminate, in particular blister base parts, or beakers, preferably for packaging pharmaceutical and medical products are a preferred application area of the thermoformable laminate according to the invention.
Table 1: Preferred laminate structures Film A Film B Film C
Laminate number 1 _ PVC PVC
- - - ~ ~
- -~ PE - {
PVC PVDC
COC or COP
k6 7 } PVC PVC PVC PVC
PVC PCTFE PVC
- -- - --- - -- - - ---~- -- - ----- -_ _ _ PVC PAN PVC
-- ~--- -- -- -PVC EVOH or PGA PVC
11 PVC PE PVC ~
- - - - -13 PVC COC or COP PVC
14 PVC COC or COP pp ---_ _ - - _ I -----PVC COC or COP PVDC
- , . . - - - 16 PVC COC or COP PCTFE
17 PVC COC or COP PAN
-- - -- -P _ - f PCTFE
21 pP { PVDC
22 PP COC or COP
~
23 pp PCTFE
PP
24 PP 1 EVOH or PGA i, PP
PP COC or COP PP
-- - --- ---PAN PP
! 26 PP
.27 r pp COC or COP PVDC
-----28 --PP COC or COP - -PCTFE
--29 PET !PET
-----I'ET PCTFE , - -- -- ------ --IDSU PVC
--- - - _ ~_ - --- -~ - - -- - - -34 I'SU pp 35 PSU COC or COP PP
- _ ---- ----- -- - J
36 I'SU PVC PCTFE
38. PSU ! PET PCTFE
Laminate number 1 _ PVC PVC
- - - ~ ~
- -~ PE - {
PVC PVDC
COC or COP
k6 7 } PVC PVC PVC PVC
PVC PCTFE PVC
- -- - --- - -- - - ---~- -- - ----- -_ _ _ PVC PAN PVC
-- ~--- -- -- -PVC EVOH or PGA PVC
11 PVC PE PVC ~
- - - - -13 PVC COC or COP PVC
14 PVC COC or COP pp ---_ _ - - _ I -----PVC COC or COP PVDC
- , . . - - - 16 PVC COC or COP PCTFE
17 PVC COC or COP PAN
-- - -- -P _ - f PCTFE
21 pP { PVDC
22 PP COC or COP
~
23 pp PCTFE
PP
24 PP 1 EVOH or PGA i, PP
PP COC or COP PP
-- - --- ---PAN PP
! 26 PP
.27 r pp COC or COP PVDC
-----28 --PP COC or COP - -PCTFE
--29 PET !PET
-----I'ET PCTFE , - -- -- ------ --IDSU PVC
--- - - _ ~_ - --- -~ - - -- - - -34 I'SU pp 35 PSU COC or COP PP
- _ ---- ----- -- - J
36 I'SU PVC PCTFE
38. PSU ! PET PCTFE
Claims (5)
1. Thermoformable laminate made of at least two plastics material films with printing, characterised in that the printing is arranged inside the laminate between the plastics material films to increase the security against forgery.
2. Thermoformable laminate according to claim 1, characterised in that the laminate is constructed as follows:
film A / print / laminating means / film C
film A/ print / laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating means / print /
film C.
film A / print / laminating means / film C
film A/ print / laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating means / print /
film C.
3. Thermoformable laminate according to claim 2, characterised in that the films A, B and/or C are thermoformable plastics material films or combinations of these plastics material films based on chlorinated hydrocarbons, chlorofluorocarbons, polyolefins, polyethyleneterephthalates, polyacrylonitriles, cycloolefin copolymers, cycloolefin polymers, polysulphones or biologically degradable plastics materials.
4. Thermoformed container, in particular blister base part, or beaker made of a thermoformable laminate according to any one of the preceding claims.
5. Use of thermoformed containers and beakers according to claim 4 for the packaging of pharmaceutical and medical products.