CA2513580C - Heat exchanger plates and methods for manufacturing heat exchanger plates - Google Patents
Heat exchanger plates and methods for manufacturing heat exchanger plates Download PDFInfo
- Publication number
- CA2513580C CA2513580C CA2513580A CA2513580A CA2513580C CA 2513580 C CA2513580 C CA 2513580C CA 2513580 A CA2513580 A CA 2513580A CA 2513580 A CA2513580 A CA 2513580A CA 2513580 C CA2513580 C CA 2513580C
- Authority
- CA
- Canada
- Prior art keywords
- channel
- forming
- bosses
- plate
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A method for forming heat exchanger plates (10) comprises formation of a fluid flow channel (28) along the edges (22) of a sheet metal strip or blank, and formation of a pair of raised end bosses. The raised end bosses (32) are elongated in the longitudinal dimension and are formed within the final width dimension of the plate so as to avoid the need for trimming of excess material along the edges of the plate. The method generates less scrap than prior art processes using progressive stamping, and also permits variation of the plate lengths.
Description
HEAT EXCHANGER PLATES AND METHODS FOR MANUFACTURING
HEAT EXCHANGER PLATES
FIELD OF THE INVENTION
The invention relates to methods for manufacturing plates for heat exchangers, particularly to methods in which generation of scrap is reduced, and to heat exchanger plates made by these methods.
BACKGROUND OF THE INVENTION
Heat exchangers are commonly made from multiple stacked plate pairs which define coolant flow passages extending between a pair of headers. As shown in Figure 1 of IJ.S. Patent No. 6,273,133 issued on August 14, 2001 to So et al., the plates of each pair are arranged in beak-to-back relation and are joined together at their peripheral edges. The plates have raised central portions which define a flow passage therebetween and in which turbuli~ers may be located. Raised bosses are provided afi the ends of the plates, and are apertured to provide inlet and outlet openings. When the heat exchanger is assembled, the bosses are aligned and in communication with one another thereby forming a pair of headers. Expanded metal fins may then be located between fihe plate pairs to allow another fluid, such as air, to flow transversely through the plate pairs. The raised end bosses also serve to create spaces between the plate pairs for insertion of the fins.
The individual plates making up such a heat exchanger are usually formed by a process known as "progressive stamping" in which the plates are progressively formed by successive stamping operations performed on a coil of sheet metal.
As explained above, the end bosses must be of a sufficient height to allow insertion of cooling fins. The bosses must also be of a specific diameter or area to allow sufficient coolant flow through the headers. Thus, the strip width required for each plate is generally determined by the width of strip material required for formation of the bosses.
HEAT EXCHANGER PLATES
FIELD OF THE INVENTION
The invention relates to methods for manufacturing plates for heat exchangers, particularly to methods in which generation of scrap is reduced, and to heat exchanger plates made by these methods.
BACKGROUND OF THE INVENTION
Heat exchangers are commonly made from multiple stacked plate pairs which define coolant flow passages extending between a pair of headers. As shown in Figure 1 of IJ.S. Patent No. 6,273,133 issued on August 14, 2001 to So et al., the plates of each pair are arranged in beak-to-back relation and are joined together at their peripheral edges. The plates have raised central portions which define a flow passage therebetween and in which turbuli~ers may be located. Raised bosses are provided afi the ends of the plates, and are apertured to provide inlet and outlet openings. When the heat exchanger is assembled, the bosses are aligned and in communication with one another thereby forming a pair of headers. Expanded metal fins may then be located between fihe plate pairs to allow another fluid, such as air, to flow transversely through the plate pairs. The raised end bosses also serve to create spaces between the plate pairs for insertion of the fins.
The individual plates making up such a heat exchanger are usually formed by a process known as "progressive stamping" in which the plates are progressively formed by successive stamping operations performed on a coil of sheet metal.
As explained above, the end bosses must be of a sufficient height to allow insertion of cooling fins. The bosses must also be of a specific diameter or area to allow sufficient coolant flow through the headers. Thus, the strip width required for each plate is generally determined by the width of strip material required for formation of the bosses.
In many cases, the width of strip material required to form the bosses is greater than a desired width of the plate pairs. This results in the need to trim excess material along the edges of the plates, particularly between the end portions in which the bosses are formed. The amount of scrap material generated by conventional progressive stamping of heat exchanger plates can be as high as 35 percent.
Thus, there is a need for improved methods of forming heat exchanger plates in which generation of scrap is reduced or eliminated, and in which plates of varying lengths may be produced without excessive tooling costs.
SUMMARI~ ~F THE INVENTI~N
In one aspect, the present invention provides a method for forming a plate for a heat exchanger, the plate having a length and a width, the length defining a longitudinal axis, the method comprising: (a) providing a flat, sheet metal strip having elongate, longitudinally extending side edges, the strip having a width substantially the same as the width of the plate; (b) forming a fluid flow channel extending along the side edges of the strip, the fluid flow channel being raised relative to the side edges; and (c) forming a pair of raised bosses in the strip, the bosses being raised relative to the side edges and the fluid flow channels, wherein a longitudinal dimension of the bosses is greater than a transverse dimension of the bosses.
In another aspect, the present invention provides a heat exchanger plate, comprising: (a) a central portion defining an elongate fluid flow channel; (b) a pair of end portions separated by the central portion; (c) a raised boss provided in each of the end portions, each raised boss having an interior and an upper surface provided with a fluid flow aperture, wherein the interiors of the bosses are in communication with the fluid flow channel; (d) a planar flange extending continuously about an entire periphery of the plate and surrounding the fluid flow channel and the raised bosses; and (e) a plurality of tabs, each of which is integrally formed with the flange and extends from the flange, each of the tabs being located in one of the end portions of the plate.
In yet another aspect, the present invention provides A heat exchanger, comprising a plurality of plate pairs formed from the heat exchanger plates according to the invention, each of the plate pairs being formed by sealing the flanges of the plates together with the interiors of the bosses of one plate communicating with the interiors of the bosses of the other plate and so that the central portions of the plates combine to form a fluid passage in communication with the interiors of the bosses, the plate pairs being stacked with the apertures of the bosses in registry, the bosses of the plate pairs forming a pair of headers.
~(~IEF ~E~~t~li~l'I~~ ~F THE ~~AIi~~~
The invenfiion will now be described, by way of example only, with reference to the accompanying drawings, in which:
Figure 1 is a top, perspective view of a preferred heat exchanger plate according to the present invention;
Figure 2 is a top plan view of the plate shown in Figure 1;
Figure 3 is a bottom plan view of one end of the plate shown in Figure 1;
Figure 4 is a top plan view of a strip or blank from which the plate of Figure 1 is formed;
Figure 5 is a top plan view of the blank of Figure 4, after formation of the flow channel;
Figure 6 is a top plan view of the blank of Figure 5, after a first boss stamping step;
Thus, there is a need for improved methods of forming heat exchanger plates in which generation of scrap is reduced or eliminated, and in which plates of varying lengths may be produced without excessive tooling costs.
SUMMARI~ ~F THE INVENTI~N
In one aspect, the present invention provides a method for forming a plate for a heat exchanger, the plate having a length and a width, the length defining a longitudinal axis, the method comprising: (a) providing a flat, sheet metal strip having elongate, longitudinally extending side edges, the strip having a width substantially the same as the width of the plate; (b) forming a fluid flow channel extending along the side edges of the strip, the fluid flow channel being raised relative to the side edges; and (c) forming a pair of raised bosses in the strip, the bosses being raised relative to the side edges and the fluid flow channels, wherein a longitudinal dimension of the bosses is greater than a transverse dimension of the bosses.
In another aspect, the present invention provides a heat exchanger plate, comprising: (a) a central portion defining an elongate fluid flow channel; (b) a pair of end portions separated by the central portion; (c) a raised boss provided in each of the end portions, each raised boss having an interior and an upper surface provided with a fluid flow aperture, wherein the interiors of the bosses are in communication with the fluid flow channel; (d) a planar flange extending continuously about an entire periphery of the plate and surrounding the fluid flow channel and the raised bosses; and (e) a plurality of tabs, each of which is integrally formed with the flange and extends from the flange, each of the tabs being located in one of the end portions of the plate.
In yet another aspect, the present invention provides A heat exchanger, comprising a plurality of plate pairs formed from the heat exchanger plates according to the invention, each of the plate pairs being formed by sealing the flanges of the plates together with the interiors of the bosses of one plate communicating with the interiors of the bosses of the other plate and so that the central portions of the plates combine to form a fluid passage in communication with the interiors of the bosses, the plate pairs being stacked with the apertures of the bosses in registry, the bosses of the plate pairs forming a pair of headers.
~(~IEF ~E~~t~li~l'I~~ ~F THE ~~AIi~~~
The invenfiion will now be described, by way of example only, with reference to the accompanying drawings, in which:
Figure 1 is a top, perspective view of a preferred heat exchanger plate according to the present invention;
Figure 2 is a top plan view of the plate shown in Figure 1;
Figure 3 is a bottom plan view of one end of the plate shown in Figure 1;
Figure 4 is a top plan view of a strip or blank from which the plate of Figure 1 is formed;
Figure 5 is a top plan view of the blank of Figure 4, after formation of the flow channel;
Figure 6 is a top plan view of the blank of Figure 5, after a first boss stamping step;
Figure 7 is a top plan view of the blank of Figure 6, after a second boss stamping step;
Figure 8 is a top plan view of the blank of Figure 7, after a third boss stamping step;
Figure 9 is a top plan view of the blank of Figure 8, after a fourth boss stamping step;
Figure 10 is a top plan view of the blank of Figure 9, after formation of the apertures in the bosses and optional trimming of the end flange;
Figure 11 illustrates an alternate blank according to the invention having apertured end portions;
Figure 12 is a cross section of an alternate preferred plate according to the invention, taken along line IX-IX' of Figure 9; and Figure 13 is a side view of one end of a plate pair formed from a pair of plates shown in Figure 1;
Figures 14 and 15 are flop plan views of blanks after formation of channel portions according to a preferred method according to the invention;
Figures 16 to 21 are schemafiic side views showing the formation of the channel portions in the blanks of Figures 14 and 15;
Figure 22 schematically illustrates the steps in the method of Figures 14 to 21;
Figures 23, 24 and 31 are top plan views of blanks after formation of channel portions and raised bosses by another preferred method according to the invention;
Figure 8 is a top plan view of the blank of Figure 7, after a third boss stamping step;
Figure 9 is a top plan view of the blank of Figure 8, after a fourth boss stamping step;
Figure 10 is a top plan view of the blank of Figure 9, after formation of the apertures in the bosses and optional trimming of the end flange;
Figure 11 illustrates an alternate blank according to the invention having apertured end portions;
Figure 12 is a cross section of an alternate preferred plate according to the invention, taken along line IX-IX' of Figure 9; and Figure 13 is a side view of one end of a plate pair formed from a pair of plates shown in Figure 1;
Figures 14 and 15 are flop plan views of blanks after formation of channel portions according to a preferred method according to the invention;
Figures 16 to 21 are schemafiic side views showing the formation of the channel portions in the blanks of Figures 14 and 15;
Figure 22 schematically illustrates the steps in the method of Figures 14 to 21;
Figures 23, 24 and 31 are top plan views of blanks after formation of channel portions and raised bosses by another preferred method according to the invention;
Figures 25 to 30 are schematic side views showing the formation of channel portions and raised bosses in the blanks of Figures 23, 24 and 31; and Figure 32 schematically illustrates the steps in the method of Figures 23 to 31.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
Figures 1 to 3 illustrate a preferred heat exchanger plate 10 according to the present invention. The plate 10 has an elongate central portion 12 located between a pair of end portions 14. Dotted lines 16 shown in Figures 1 to 3 indicate the approximate boundaries between the cenfiral portion 12 and the end portions 14.
The plate 10 has an upper surface 18 and an opposed lower surface 20, with elongate side edges 22 extending along the entire length of plate 10 and terminating at end edges 24. Extending along the side edges 22 of plate 10 are a pair of shoulders 2G, these shoulders 26 defining a longitudinally extending fluid flow channel 28 extending along the lower surface 20 of plate 10. The fluid flow channel 28 preferably extends along substantially the entire central portion 12 of plate 10, and may preferably extend beyond dotted lines 16 into the end portions 14 of plate 10. The shoulders 26 are spaced from the side edges 22 so as to form flat peripheral side flanges 30 between fihe side edges 22 and the shoulders 26. The side flanges 30 extend longitudinally along the side edges 22 between the end portions 14.
Located in the end portions 14 of plate 10 are a pair of raised bosses 32. The bosses 32 are raised relative to the side edges 22 and relative to the fluid flow channel 28, having a height sufficient such that when a heat exchanger is formed by stacking plate pairs formed from plates 10, each plate pair formed by joining a pair of plates 10 with their lower surfaces facing one another, sufficient space exists between the plate pairs for insertion of cooling fins.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
Figures 1 to 3 illustrate a preferred heat exchanger plate 10 according to the present invention. The plate 10 has an elongate central portion 12 located between a pair of end portions 14. Dotted lines 16 shown in Figures 1 to 3 indicate the approximate boundaries between the cenfiral portion 12 and the end portions 14.
The plate 10 has an upper surface 18 and an opposed lower surface 20, with elongate side edges 22 extending along the entire length of plate 10 and terminating at end edges 24. Extending along the side edges 22 of plate 10 are a pair of shoulders 2G, these shoulders 26 defining a longitudinally extending fluid flow channel 28 extending along the lower surface 20 of plate 10. The fluid flow channel 28 preferably extends along substantially the entire central portion 12 of plate 10, and may preferably extend beyond dotted lines 16 into the end portions 14 of plate 10. The shoulders 26 are spaced from the side edges 22 so as to form flat peripheral side flanges 30 between fihe side edges 22 and the shoulders 26. The side flanges 30 extend longitudinally along the side edges 22 between the end portions 14.
Located in the end portions 14 of plate 10 are a pair of raised bosses 32. The bosses 32 are raised relative to the side edges 22 and relative to the fluid flow channel 28, having a height sufficient such that when a heat exchanger is formed by stacking plate pairs formed from plates 10, each plate pair formed by joining a pair of plates 10 with their lower surfaces facing one another, sufficient space exists between the plate pairs for insertion of cooling fins.
The bosses 32 can be of any desired shape, including circular. Preferably, the bosses 32 each have a major diameter extending in the longitudinal direction which is greater than a minor diameter extending in the transverse direction.
Most preferably, the bosses are of an oval shape. As used herein, the term "oval" refers to any non-circular shape having a generally smoothly curving periphery, such as an ellipse, a rectangle with rounded corners, or other oblong or egg shape. In the preferred embodiment shown in the drawings, the bosses 32 are oval in plan view, having substantially straight longitudinally extending sides 34 extending between smoothly curved ends, a proximal end 36 located at or near the dotted line 16 between the central portion 12 and end portions 14, and a distal end 33 located proximate the end edge 24 of the plate 10.
As shown in Figure 2, the sides 34 of bosses 32 are spaced inwardly from the side edges 22 and the distal ends 33 of bosses 32 are spaced inwardly from the end edges 24, thereby forming peripheral end flanges 40 extending around the end porfiions 14 of plate 10. The side flanges 30 and peripheral end flanges 40 combine fio form a continu~us flange about the entire periphery of the plate 10. The continuous flange provides a surface along which a pair of plates 10 can be joined, for e~zample by brazing, in baclz-to-baclz relation (with lower surfaces 20 facing one another) to form a plate pair.
In order to provide fluid communication through the headers after assembly of the heat exchanger, the upper surface 44 of each boss 32 is provided with an aperture 42. The area of the aperture 42 is sufficiently large to provide adequate fluid flow throughout the header, while maintaining an annular sealing surface 46 on the upper surface 44. During assembly of the heat exchanger, adjacent plate pairs are joined to one another, for example by brazing, along the annular sealing flanges 46. As shown in the preferred plate 10, the aperture 42 may preferably be centred on upper surface 44 and may generally follow the shape of the raised bosses 32, although this is not essential.
As best seen in the bottom plan view of Figure 3, the side flanges 30 become broader and curve inwardly toward one another as they approach the bosses 32, such that the side flanges 30 intersect the bosses 32 at points 50 which are located proximate the intersection between the sides 34 and the proximal ends 36 of the bosses 32. Thus, each peripheral end flange 40 substantially extends only around the sides 34 and distal end 38 of a boss 32, leaving an area 49 (substantially coextensive with proximal end 36) at which the fluid flow channel 28 is in flow communication with the interior of the boss 32.
As mentioned above, the plate pairs formed from plates 10 may be provided with turbulizers such as the expanded metal turbulizers disclosed in the above-mentioned patent to So et al., which is incorporated by reference herein in its entirety. The turbulizers are preferably rectangular in shape and are received between the plates 10 of the plate pairs, preferably extending throughout substantially the entire central portions 12 of the plates 10. As well as enhancing heat transfer, turbulizers provide support for the central portions of plates 10, preventing collapse or narrowing of the fluid flow channels 28.
In a heat exchanger constructed from pairs of plates 10, the ends of the turbulizers preferably overlap the proximal curved ends 36 of the bosses 32, so that the turbulizers provide support along the entire length of the fluid flow channels 28. The inward tapering ~f the side flanges 30 functi~ns as an integral turbulizer stop so as to prevent I~angitudinal sliding of the turbulizer between the plate pairs. A preferred position of fihe end of a turbulizer (not shown) is indicated by dotted line 51 in Figure 3.
Having now described the preferred heat exchanger plate 10 according to the invention, the following is a description of preferred methods for manufacturing a heat exchanger plate 10 according to the invention.
One preferred method of the invention begins by providing a sheet metal strip 52, preferably comprised of a brazeable material, which is preferably selected from the group comprising aluminum, an aluminum alloy, and aluminum or aluminum alloy clad with an aluminum brazing alloy. The strip 52 as defined herein is of indefinite length, having longitudinally extending side edges 54, an upper surface and an opposed lower surface (not shown). The width of strip _$_ 52, measured in the transverse direction, is substantially the same as the width of the plate 10 described above.
A plurality of strips 52 may be formed by longitudinally slitting a coil of sheet metal (having a width greater than the width of strip 52) at one or more points across its width, with the longitudinal direction of the strip 52 being parallel to the direction of slitting. Alternatively, strips 52 may be formed by dividing a coil into sheets which are then slit longitudinally or transversely into strips 52.
During the method of the invention, the strip 52 is severed in the transverse direction at one or more points to form a plurality of blanks 53, each of which has a length, measured in the longitudinal direction, which is substantially the same as the length of plate 10.
Another preferred method of the invention begins by providing a sheet metal blank 53 having a width the same as that of strip 52 and having a length which is substantially the same as that of plate 10. The blanks 53 may preferably be formed as described above by transversely severing strips 52 of indefinite length. Where the length of the blank 10 is the same as the width of the sheet metal coil, the blanles 53 may be formed by cutting transversely across the width of the coil. lnlhere the length of the blank 53 is somewhat greater Than the width of the coil, the blanks 53 may be formed by slitting the coil diagonally, that is with the side edges 54 of the strip 52 being angled relative to the transverse direction of the coil.
Except as otherwise indicated, the method now described below begins with a blank 53 having a length and a width which are substantially the same as the length and width of the plate 10. However, to indicate that the method may begin with the provision of either a strip 52 or a blank 53, Figure 4 illustrates (in dotted lines) portions of strip 52 extending beyond the end edges 56 of blank 53. In addition, Figures 4 and 5 show the central portions 12, end portions 14 and the dotted lines 16 separating the central and end portions 12 and 14.
_g_ The next step in the method comprises the formation of the fluid flow channel 28, preferably by formation of shoulders 26 along the side edges 54 of the blank 53. Preferably, as shown in Figure 5, the shoulders 26 terminate so as not to substantially extend into the end portions 14. As shown in Figure 5, it may be preferred to terminate the shoulders 26 at or near the line 16 dividing the central portion 12 from the end portions 14. The termination of shoulders 26 is preferred so that the shoulders do not interfere with formation of a flat end flange 40 in the end portion of plate 10.
It will be appreciated that the formation of shoulders 26 provides each plate with a single, longitudinally extending flow channel 28, with side flanges 30 extending along either side of the flow channel 28. The plates 10 may, however, be of more complex configuration and may be formed with more than one fl~w channel, although all configurations would be formed with flanges adjacent the side edges 54, and a raised central portion forming the flow channel(s).
As mentioned above, the width of strip 52 or blank 53 is substantially the same as fibs width of plate 10. As used herein with reference i~ the veidth of plate 10, the term "substantially the same" is intended to mean that the width of strip or blank 53, measured transversely across the central portion 12 thereof, after formation of flow channel 28, is the same as the width of fibs plate 10, measured transversely across the central portion 12 thereof, such that n~ edge trimming of the plate 10 is required. It will be appreciated that the width of the strip 52.or blank 53, prior to formation of the flow channel 28, will be slightly greater than the width of plate 10 since the material required for formation of the shoulders 26 will be drawn from the width of the strip 52 or blank 53.
It will be appreciated that, where the method begins by provision of a strip 52 of indefinite length, the shoulders 26 may be roll-formed prior to severing the strip 52 into individual blanks 53. Of course, the shoulders 26 may also be formed by stamping the strips 52 or blank 53 with an appropriate die.
The next step in the method comprises formation of the raised bosses 32 in each of the end portions 14 of strip 52 or blank 53. The bosses 32 are formed by a plurality of successive stamping or drawing operations, with the degree of boss formation in each successive stamping operation being illustrated in Figures 6 to 9. As can be seen from the drawings, some of the material from which the bosses 32 are formed is drawn from the surrounding material of the strip 52 or blanks 53. This results in material of the end portions 14 becoming drawn inwardly toward the bosses 32. This is apparent from Figures 6 to 9 which show the side edges 54 of the.strip 52 or blank 53 converging inwardly toward one another along the sides 34 of the bosses 32.
In the most preferred embodiments according to the invention, it is preferred that the strips 52 are severed into blanks 53 prior to formation of bosses 32, and thafi the bosses 32 are formed by successive stamping operations by pairs of dies. The dies are preferably mounted in an apparatus in such a manner that the distance between the dies can be adjusted, thereby permitting the formation of plafies having various lengths, which is not possible in progressive stamping dies.
It will be appreciated that the length, width and height of the bosses 32 are selected such that fihe heat exchanger formed by pairs of plates 10 will have a desired flow through its headers, such that a desired spacing will be maintained between the plate pairs to allow insertion of cooling fins, and such that the bosses 32 may be formed within the width dimension of the strip 52 or blank 53, thereby avoiding the need to trim excess material from the edges of the plate 10.
After formation of the bosses 32, the next step in the method comprises the formation of apertures 42 in bosses 32, for example using a cutting die.
As shown in Figure 9, there may be some excess material located between the distal end 38 of the bosses 32 and the end edges 24 of the plate 10. Although not essential, some of this material may be removed by trimming, for example to provide smoothly rounded edges 62 as shown in Figure 10, while maintaining an end flange 40 of sufficient dimensions to allow leak-free formation of the plate pairs, for example by brazing.
As mentioned above, the length of the blank 53 is substantially the same as the length of plate 10. As used herein with reference to the length of plate 10, the term "substantially the same" is intended to mean that the total length of blank 53, measured longitudinally between end edges 56, after formation of bosses 32, is the same as the total length of plafie 10, before end trimming as described in relation to Figure 10. It will be appreciated that the length of the blank 53, prior to formation of the bosses 32, will be slightly greater than the length of plate 10, before end trimming, since the formation of bosses 32 will somewhat reduce the length of the blank 53.
As can be seen from Figures G to 9, the end flanges 40 of plate 10 reach their narrowest points adjacent the edges 34 of bosses 32, due to the fact that much of the material from which the bosses 32 are formed is drawn inwardly from the surrounding portions of the strip 52 or blank 53. Excessive narrowing of the flange 40 in these regions results in narrowing of the surfaces along which the plate pairs are formed, possibly affecting the reliability of joint formation in this area, and limiting the width dimensions of the bosses 32. To avoid excessive narrowing of flange 40 in this region, the strips 52 or blanks 53 may preferably be provided with apertures 64 in the end portions 14. These apertures 64 are centrally located in the areas of end portions 14 which will be cut out to form the flow apertures 42 of bosses 32. During formation of bosses 32, some of the material required for formation of the bosses 32 will be drawn outwardly from apertures 64 in the direction of the arrows in Figure 11, thereby reducing the amount of material which is drawn from the area surrounding the bosses 32.
In the preferred embodiment of the invention, in which the bosses 32 and apertures 42 are oval in shape, the apertures 64 are preferably also elongated in the longitudinal direction. In the particularly preferred embodiment shown in Figure 11, the apertures 64 may be dumbbell-shaped, comprising a pair of circular apertures 66 joined by a longitudinal slit 68.
Rather than trimming the end flange 40 as shown in Figure 10, the flanges 40 may be bent along lines 70 shown in Figure 9 to form tabs 72. The lines 70 are parallel to the longitudinal axis and are substantially tangential with the curve defined by the inwardly curved portion of flange 40, which is located proximate the sides 34 of bosses 32. As shown in Figure 12, the tabs 72 preferably extend at right angles to the remainder of flange 40, and are preferably both bent upwardly. Thus, when the plates 10 are combined to form plate pairs, the ends of the plate pair have an H-shaped cross section, having tabs 72 extending both upwardly and downwardly from flanges 40. The configuration of the tabs 72 in a plate pair 74 is also illustrated in Figure 12, with a second plate 10 being illustrated in dashed lines.
then the plate pairs 74 are stacked to form a heal exchanger, the tabs 72 will extend into the space between the plafies 10. In some preferred embodiments, the tabs 72 of adjacent plate pairs 74 are of sufficient height to abut one another, and may become connected to one another during brazing of the heat exchanger, thus providing an additional brazed connection between the plates 10. In other preferred embodiments, the tabs are of lesser height, such that the tabs 72 of adjacent plate pairs do not contact one another. Where the tabs 72 of adjacent plate pairs do not engage one another, they serve to provide a plurality of surfaces to which a heat exchanger mounting bracket may be secured. ~f course, a mounting bracket can also be secured to the tabs 72 in the embodiment where the tabs of adjacent plate pairs 74 abut one another.
Figure 13 is a side view showing one end of a preferred plate pair 74 which is formed by joining a pair of plates 10 in back-to-back relation, such that the flanges 30 and 40 of the plates 10 engage one another and are joined in a leak-free manner, such as by brazing.
Although the method according to the invention has been described as including formation of the flow channel prior to formation of the bosses, it is to be appreciated that this sequence of steps is preferred, but not essential. In other preferred embodiments, the bosses may be formed prior to formation of the flow channel. However, it may be preferred to form the flow channel first since the channel form improves the rigidity of the blank, thereby reducing its tendency to bend or twist, and possibly resulting in improved accuracy of the boss stamping operation.
In some preferred methods of the invention, the channel 28 of plate 10 is formed by stamping the strip 52 or blank 53 with a single channel-forming die which is of fixed length and which is stationary relative to the longitudinal axis of strip 52 or blank 53. The bosses 32 are then formed by a plurality of dies which may preferably be movable relative to the longitudinal axis. This type of arrangement may permit a limified amount of variation in the length of plate (as further described below with reference to Figures 23 to 32). However, where it is necessary to accommodate large variations in the length of plate 10, replacement of the channel-forming die by another die of different length would be required. The relative positions of the boss-forming dies w~auld then be adjusted for compatibility wifih the new channel length.
In order to minimize tooling costs, the present invention provides methods which allow the channel length to be easily varied without replacemenfi of the channel-forming die. A preferred embodiment of such a method is described below with reference to Figures 14 to 22, which illustrates a method in which the channel 28 is formed by one or more stamping operations involving the use of a channel-forming die 80 which is movable along the longitudinal axis of the .
strip 52 or blank 53, thereby permitting variation of the channel length for production of plates 10 having lengths within a predetermined range.
Each stamping operation using an axially movable channel-forming die 80 produces a channel segment having a length which is equal to or less than the total length of the channel 28. For example, where the desired plate length is at the lower limit of the predetermined range, the channel 28 is preferably formed by one stamping operation using an axially movable channel-forming die 80, wherein the length of the channel segment produced by the axially movable channel-forming die 80 is equal to the total length of the channel 28.
On the other hand, where the desired plate length is above the lower limit of the predetermined range, the channel 28 will be formed by two or more stamping operations, at least one of which involves the use of a movable channel-forming die 80. In this case, the length of the channel segment produced by the axially movable channel-forming die 80 will be less than the total length of the channel 28. It will be appreciated that the two or more stamping operations could be performed by a single axially movable channel-forming die 80, by two or more axially-movable channel forming dies 80, or by an axially movable channel-forming die 80 in combination with a stationary channel-forming die.
In the particular method illustrated by Figures 14 to 22, the desired length of channel 28 is greafier than the lower limit of the predetermined range, such that multiple stamping operations are required to form channel 28. In this preferred embodiment, at least one of the stamping operations is performed by an axially movable channel-forming die 80. This preferred method is now described in detail below.
The method illustrated in Figures 14 to 21 begins with a blank 53 which has a width and length substantially the same as that of plate 10 as described above.
As in Figure 4, the blank 53 has an elongate central portion 12 located between a pair of end portions 14, with the approximate boundaries between central portion 12 and end portions 14 being indicated by dotted lines 16. The blank 53 is fed to an apparatus 78 comprising one or more axially movable channel-forming dies 80, each of which comprises an upper die portion 82 and a lower die portion 84.
As shown in Figures 16 and 17, the upper and lower die portions 82 and 84 are closed on the blank 53 to form a first channel portion 28a having a proximal end portion 86a and a distal end portion 88a, shown in Figure 14. The distal end portion 88a terminates at or near the boundary 16 between the central portion 12 and one of the end portions 14 of the blank 53.
Following formation of the first channel portion 28a, the die portions 82 and are opened as in Figure 18. As shown in Figures 16 to 21, the opposite ends 90, 92 of upper die portion 82 are rounded or tapered. This provides the proximal and distal end portions 86a, 88a of first channel portion 28a with gradual terminations 98a, 1 OOa which may either be rounded or tapered, thereby avoiding damage to the blank 53. In the drawings, the terminations 98a and 100a are shown as being rounded and are exaggerated so as to be clearly visible.
The next step in the method comprises formation of a second channel portion 28b which, as shown in Figure 15, comprises a proximal end portion 86b and a distal end portion 88b, with the distal end portion 88b terminafiing at or near the boundary 16 between the central portion 12 and one of the end portions 14 of the blank 53. It can be seen from Figure 15 that the proximal end portion 86a of the first channel portion 28a and the proximal end portion 86b of the second channel portion 28b overlap one another by an amount A, and that the distal end portions 88a and 88b are spaced from one another along the longitudinal axis by an amount which is preferably equal to the desired length of channel 28.
The second stamping operation may preferably be performed by the same die 80 which performed the first stamping operation illustrated in Figures 16 to 18.
In this case, the blank 53 preferably remains stationary during the formation of channel 28, while the single channel-forming die 80 is displaced axially between the first and second stamping operations.
In the alternative, as shown in Figures 19 to 22, the first and second stamping operations may be performed by different channel-forming dies 80. Although the dies 80 may be axially aligned relative to one another, they are shown in Figure 22 as being located at different stamping stations which are transversely spaced from one another such that the blank 53 must be moved transversely between the first and second stamping operations.
Although dies 80 are described above as being axially movable, it will be appreciated that one of the dies 80 used to form the first channel portion 28a and the second channel portion 28b could be stationary with respect to the longitudinal axis of blank 53.
The upper die portion 82 of channel-forming die 80 used in the second stamping operation shown in Figure 19 also has rounded or tapered ends 90, 92 so as to provide the second channel portion 28b with a gradual termination 100b at the distal end portion 88b. Due to the overlap of the proximal end portions 86a and 86b, no gradual termination 98b will be seen at the proximal end portion 86b of the second channel portion 28b. l~or is the terminal end portion 98a of the first channel portion 28a visible after the second stamping operation. Rather, the proximal end portions 86a and 86b will blend smoothly together to form a channel 28 of substantially uniform cross section.
fps mentioned above, at least one of the channel-forming dies 80 is movable along the longitudinal axis so as to vary the area of overlap A. In order to ensure that the. channel 28 is of constant cross section, it is necessary that the proximal end portions 86a and 86b overlap to an extent sufficient that the gradual terminations 98a and 98b are not present in the channel 28. In most preferred embodiments of the invention, at least about 1 inch ofi overlap will be required to ensure that the channel 28 is of constant cross-section.
Following the channel stamping operations shown in Figures 14 to 21, the formation of plate 10 is completed by formation of the raised bosses 32 as .
described above with reference to Figures 6 to 10. As.shown in Figure 22, the bosses may be formed simultaneously by axially-aligned boss-forming dies 81, both of which are preferably movable relative to the longitudinal axis. It will, however, be appreciated that the boss-forming dies 81 may be transversely spaced from one another and that the formation of each of the bosses 32 will typically require multiple stamping operations performed by multiple pairs of boss-forming dies 81.
Another preferred variation of the method according to the invention is illustrated in Figures 23 to 32. In this variation of the method, a blank 53 is provided as in the previous embodiments having a width and length substantially the same as that of plate 10, and having an elongate central portion 12 located between a pair of end portions 14, with the approximate boundaries between central portion 12 and end portions 14 being indicated by dotted lines 16. The blank 53 is fed to an apparatus 102 comprising a channel-forming die 104 having an upper die portion 106 and a lower die portion 108.
In this embodiment, a first channel portion 110 is formed having end portions 112 and 114. The first channel portion 110 has a length which is somewhat less than the length of the channel 28, such that at least one of its end portions is spaced from the approximate boundary 16 between the central portion 12 and fihe end portions 14 of the blank 53. In the preferred embodiment shown in the drawings, both end portions 112, 114 of the channel portion 110 are spaced from lines 16.
The channel-forming die 104 may either be movable al~ng the longitudinal axis or may be stationary. In the preferred embodiment shown in Figures 25 to 27, the channel-forming die 104 is stationary. If desired, the stationary channel die 104 may be replaced by dies) 80 as described above such that the first channel portion 110 is formed in two separate stamping operations.
As in the previously described embodiment, the upper~die portion106 of channel-forming die 104 preferably has opposite ends 116, 118 which are rounded or tapered. As shown in Figure 23, the curvature of the upper die portion 106 provides the end portions112, 114 of the first channel portion 110 with gradual terminations 120, 122, thereby avoiding damage to the blank 53.
As in the embodiment described above, the curvature of ends 116, 118 is exaggerated in the drawings.
The next step in the method, illustrated in Figures 24, 28 and 29, comprises formation of a second channel portion 124 and a first one of the raised bosses 32, the channel portion 124 and the first boss 32 being formed together by stamping the blank 53 with a combined die 126 having an upper die portion 128 and a lower die portion 130. The upper and lower die portions 128, 130 have boss-forming portions 132, 134 for forming the boss, and also have channel-forming portions 136,, 138 for forming the second channel portion 124. The .
terminal end 140 of the channel-forming portion136 of the upper die portion128 is preferably smoothly rounded or tapered to blend the first and second channel portions 110, 124.
As shown in Figure 24, the end portion 112 of the first channel portion 110 and the second channel portion 124 overlap one another by an amount B which is variable depending on the desired length of the plate 10. Preferably, the combined die 126 is movable along the longitudinal axis to vary the amount of overlap B and thereby vary the length of the plate 10. In order to ensure that the channel 28 is of a substantially uniform cross secfiion, the amount of overlap is sufficient to ensure that rounded terminations of the first and second channel portions 110, 12~~ are not present in the channel. Preferably, as mentioned above, the amount of overlap B is at least about 1 inch.
As shown in Figures 6 to 10, it will be appreciated that more than one operation is typically required to form the bosses 32. In the preferred embodiment using combined die 126, at least one of the boss forming operations will be performed by a combined die 126, with one or more of the boss-forming operations optionally being performed by dies) which have only a boss-forming portion.
The partially finished plate 10 shown in Figure 24 is then subjected to a third stamping operation, shown in Figure 30, in which a third channel portion 144 and a second boss 32' are formed together by stamping the partially finished plate 10 with a combined die 126' which is preferably an identical mirror image of combined die 126. Combined die 126' has an upper die portion 128' with a boss-forming portion 132' and a channel-forming portion 136', and has a lower die portion 130' with a boss-forming portion 134' and a channel-forming portion 138'. As shown in Figure 31, the end portion 114 of the first channel portion 110 overlaps the third channel portion 144 by an amount C which is variable depending on the desired length of the plate 10, and is preferably at least about 1 inch. Preferably, the combined die 126' is movable along the longitudinal axis to vary the amount of overlap C and thereby vary the length of the plate 10.
Figure 32 illustrates the sequence of steps which may be followed in the method described above with reference to Figures 23 to 31. In the embodiment illustrated in Figure 32, the blank 53 is fed transversely to a channel-forming die 104 and then to axially-aligned combined dies 126 and 126'. It will, however, be appreciated that the boss-forming dies are not necessarily axially aligned with one another.
Although the invention has been described in relation to certain preferred embodiments, it is not limited thereto. Rather, the invention includes all embodiments which may fall within the sc~pe of the following claims.
Most preferably, the bosses are of an oval shape. As used herein, the term "oval" refers to any non-circular shape having a generally smoothly curving periphery, such as an ellipse, a rectangle with rounded corners, or other oblong or egg shape. In the preferred embodiment shown in the drawings, the bosses 32 are oval in plan view, having substantially straight longitudinally extending sides 34 extending between smoothly curved ends, a proximal end 36 located at or near the dotted line 16 between the central portion 12 and end portions 14, and a distal end 33 located proximate the end edge 24 of the plate 10.
As shown in Figure 2, the sides 34 of bosses 32 are spaced inwardly from the side edges 22 and the distal ends 33 of bosses 32 are spaced inwardly from the end edges 24, thereby forming peripheral end flanges 40 extending around the end porfiions 14 of plate 10. The side flanges 30 and peripheral end flanges 40 combine fio form a continu~us flange about the entire periphery of the plate 10. The continuous flange provides a surface along which a pair of plates 10 can be joined, for e~zample by brazing, in baclz-to-baclz relation (with lower surfaces 20 facing one another) to form a plate pair.
In order to provide fluid communication through the headers after assembly of the heat exchanger, the upper surface 44 of each boss 32 is provided with an aperture 42. The area of the aperture 42 is sufficiently large to provide adequate fluid flow throughout the header, while maintaining an annular sealing surface 46 on the upper surface 44. During assembly of the heat exchanger, adjacent plate pairs are joined to one another, for example by brazing, along the annular sealing flanges 46. As shown in the preferred plate 10, the aperture 42 may preferably be centred on upper surface 44 and may generally follow the shape of the raised bosses 32, although this is not essential.
As best seen in the bottom plan view of Figure 3, the side flanges 30 become broader and curve inwardly toward one another as they approach the bosses 32, such that the side flanges 30 intersect the bosses 32 at points 50 which are located proximate the intersection between the sides 34 and the proximal ends 36 of the bosses 32. Thus, each peripheral end flange 40 substantially extends only around the sides 34 and distal end 38 of a boss 32, leaving an area 49 (substantially coextensive with proximal end 36) at which the fluid flow channel 28 is in flow communication with the interior of the boss 32.
As mentioned above, the plate pairs formed from plates 10 may be provided with turbulizers such as the expanded metal turbulizers disclosed in the above-mentioned patent to So et al., which is incorporated by reference herein in its entirety. The turbulizers are preferably rectangular in shape and are received between the plates 10 of the plate pairs, preferably extending throughout substantially the entire central portions 12 of the plates 10. As well as enhancing heat transfer, turbulizers provide support for the central portions of plates 10, preventing collapse or narrowing of the fluid flow channels 28.
In a heat exchanger constructed from pairs of plates 10, the ends of the turbulizers preferably overlap the proximal curved ends 36 of the bosses 32, so that the turbulizers provide support along the entire length of the fluid flow channels 28. The inward tapering ~f the side flanges 30 functi~ns as an integral turbulizer stop so as to prevent I~angitudinal sliding of the turbulizer between the plate pairs. A preferred position of fihe end of a turbulizer (not shown) is indicated by dotted line 51 in Figure 3.
Having now described the preferred heat exchanger plate 10 according to the invention, the following is a description of preferred methods for manufacturing a heat exchanger plate 10 according to the invention.
One preferred method of the invention begins by providing a sheet metal strip 52, preferably comprised of a brazeable material, which is preferably selected from the group comprising aluminum, an aluminum alloy, and aluminum or aluminum alloy clad with an aluminum brazing alloy. The strip 52 as defined herein is of indefinite length, having longitudinally extending side edges 54, an upper surface and an opposed lower surface (not shown). The width of strip _$_ 52, measured in the transverse direction, is substantially the same as the width of the plate 10 described above.
A plurality of strips 52 may be formed by longitudinally slitting a coil of sheet metal (having a width greater than the width of strip 52) at one or more points across its width, with the longitudinal direction of the strip 52 being parallel to the direction of slitting. Alternatively, strips 52 may be formed by dividing a coil into sheets which are then slit longitudinally or transversely into strips 52.
During the method of the invention, the strip 52 is severed in the transverse direction at one or more points to form a plurality of blanks 53, each of which has a length, measured in the longitudinal direction, which is substantially the same as the length of plate 10.
Another preferred method of the invention begins by providing a sheet metal blank 53 having a width the same as that of strip 52 and having a length which is substantially the same as that of plate 10. The blanks 53 may preferably be formed as described above by transversely severing strips 52 of indefinite length. Where the length of the blank 10 is the same as the width of the sheet metal coil, the blanles 53 may be formed by cutting transversely across the width of the coil. lnlhere the length of the blank 53 is somewhat greater Than the width of the coil, the blanks 53 may be formed by slitting the coil diagonally, that is with the side edges 54 of the strip 52 being angled relative to the transverse direction of the coil.
Except as otherwise indicated, the method now described below begins with a blank 53 having a length and a width which are substantially the same as the length and width of the plate 10. However, to indicate that the method may begin with the provision of either a strip 52 or a blank 53, Figure 4 illustrates (in dotted lines) portions of strip 52 extending beyond the end edges 56 of blank 53. In addition, Figures 4 and 5 show the central portions 12, end portions 14 and the dotted lines 16 separating the central and end portions 12 and 14.
_g_ The next step in the method comprises the formation of the fluid flow channel 28, preferably by formation of shoulders 26 along the side edges 54 of the blank 53. Preferably, as shown in Figure 5, the shoulders 26 terminate so as not to substantially extend into the end portions 14. As shown in Figure 5, it may be preferred to terminate the shoulders 26 at or near the line 16 dividing the central portion 12 from the end portions 14. The termination of shoulders 26 is preferred so that the shoulders do not interfere with formation of a flat end flange 40 in the end portion of plate 10.
It will be appreciated that the formation of shoulders 26 provides each plate with a single, longitudinally extending flow channel 28, with side flanges 30 extending along either side of the flow channel 28. The plates 10 may, however, be of more complex configuration and may be formed with more than one fl~w channel, although all configurations would be formed with flanges adjacent the side edges 54, and a raised central portion forming the flow channel(s).
As mentioned above, the width of strip 52 or blank 53 is substantially the same as fibs width of plate 10. As used herein with reference i~ the veidth of plate 10, the term "substantially the same" is intended to mean that the width of strip or blank 53, measured transversely across the central portion 12 thereof, after formation of flow channel 28, is the same as the width of fibs plate 10, measured transversely across the central portion 12 thereof, such that n~ edge trimming of the plate 10 is required. It will be appreciated that the width of the strip 52.or blank 53, prior to formation of the flow channel 28, will be slightly greater than the width of plate 10 since the material required for formation of the shoulders 26 will be drawn from the width of the strip 52 or blank 53.
It will be appreciated that, where the method begins by provision of a strip 52 of indefinite length, the shoulders 26 may be roll-formed prior to severing the strip 52 into individual blanks 53. Of course, the shoulders 26 may also be formed by stamping the strips 52 or blank 53 with an appropriate die.
The next step in the method comprises formation of the raised bosses 32 in each of the end portions 14 of strip 52 or blank 53. The bosses 32 are formed by a plurality of successive stamping or drawing operations, with the degree of boss formation in each successive stamping operation being illustrated in Figures 6 to 9. As can be seen from the drawings, some of the material from which the bosses 32 are formed is drawn from the surrounding material of the strip 52 or blanks 53. This results in material of the end portions 14 becoming drawn inwardly toward the bosses 32. This is apparent from Figures 6 to 9 which show the side edges 54 of the.strip 52 or blank 53 converging inwardly toward one another along the sides 34 of the bosses 32.
In the most preferred embodiments according to the invention, it is preferred that the strips 52 are severed into blanks 53 prior to formation of bosses 32, and thafi the bosses 32 are formed by successive stamping operations by pairs of dies. The dies are preferably mounted in an apparatus in such a manner that the distance between the dies can be adjusted, thereby permitting the formation of plafies having various lengths, which is not possible in progressive stamping dies.
It will be appreciated that the length, width and height of the bosses 32 are selected such that fihe heat exchanger formed by pairs of plates 10 will have a desired flow through its headers, such that a desired spacing will be maintained between the plate pairs to allow insertion of cooling fins, and such that the bosses 32 may be formed within the width dimension of the strip 52 or blank 53, thereby avoiding the need to trim excess material from the edges of the plate 10.
After formation of the bosses 32, the next step in the method comprises the formation of apertures 42 in bosses 32, for example using a cutting die.
As shown in Figure 9, there may be some excess material located between the distal end 38 of the bosses 32 and the end edges 24 of the plate 10. Although not essential, some of this material may be removed by trimming, for example to provide smoothly rounded edges 62 as shown in Figure 10, while maintaining an end flange 40 of sufficient dimensions to allow leak-free formation of the plate pairs, for example by brazing.
As mentioned above, the length of the blank 53 is substantially the same as the length of plate 10. As used herein with reference to the length of plate 10, the term "substantially the same" is intended to mean that the total length of blank 53, measured longitudinally between end edges 56, after formation of bosses 32, is the same as the total length of plafie 10, before end trimming as described in relation to Figure 10. It will be appreciated that the length of the blank 53, prior to formation of the bosses 32, will be slightly greater than the length of plate 10, before end trimming, since the formation of bosses 32 will somewhat reduce the length of the blank 53.
As can be seen from Figures G to 9, the end flanges 40 of plate 10 reach their narrowest points adjacent the edges 34 of bosses 32, due to the fact that much of the material from which the bosses 32 are formed is drawn inwardly from the surrounding portions of the strip 52 or blank 53. Excessive narrowing of the flange 40 in these regions results in narrowing of the surfaces along which the plate pairs are formed, possibly affecting the reliability of joint formation in this area, and limiting the width dimensions of the bosses 32. To avoid excessive narrowing of flange 40 in this region, the strips 52 or blanks 53 may preferably be provided with apertures 64 in the end portions 14. These apertures 64 are centrally located in the areas of end portions 14 which will be cut out to form the flow apertures 42 of bosses 32. During formation of bosses 32, some of the material required for formation of the bosses 32 will be drawn outwardly from apertures 64 in the direction of the arrows in Figure 11, thereby reducing the amount of material which is drawn from the area surrounding the bosses 32.
In the preferred embodiment of the invention, in which the bosses 32 and apertures 42 are oval in shape, the apertures 64 are preferably also elongated in the longitudinal direction. In the particularly preferred embodiment shown in Figure 11, the apertures 64 may be dumbbell-shaped, comprising a pair of circular apertures 66 joined by a longitudinal slit 68.
Rather than trimming the end flange 40 as shown in Figure 10, the flanges 40 may be bent along lines 70 shown in Figure 9 to form tabs 72. The lines 70 are parallel to the longitudinal axis and are substantially tangential with the curve defined by the inwardly curved portion of flange 40, which is located proximate the sides 34 of bosses 32. As shown in Figure 12, the tabs 72 preferably extend at right angles to the remainder of flange 40, and are preferably both bent upwardly. Thus, when the plates 10 are combined to form plate pairs, the ends of the plate pair have an H-shaped cross section, having tabs 72 extending both upwardly and downwardly from flanges 40. The configuration of the tabs 72 in a plate pair 74 is also illustrated in Figure 12, with a second plate 10 being illustrated in dashed lines.
then the plate pairs 74 are stacked to form a heal exchanger, the tabs 72 will extend into the space between the plafies 10. In some preferred embodiments, the tabs 72 of adjacent plate pairs 74 are of sufficient height to abut one another, and may become connected to one another during brazing of the heat exchanger, thus providing an additional brazed connection between the plates 10. In other preferred embodiments, the tabs are of lesser height, such that the tabs 72 of adjacent plate pairs do not contact one another. Where the tabs 72 of adjacent plate pairs do not engage one another, they serve to provide a plurality of surfaces to which a heat exchanger mounting bracket may be secured. ~f course, a mounting bracket can also be secured to the tabs 72 in the embodiment where the tabs of adjacent plate pairs 74 abut one another.
Figure 13 is a side view showing one end of a preferred plate pair 74 which is formed by joining a pair of plates 10 in back-to-back relation, such that the flanges 30 and 40 of the plates 10 engage one another and are joined in a leak-free manner, such as by brazing.
Although the method according to the invention has been described as including formation of the flow channel prior to formation of the bosses, it is to be appreciated that this sequence of steps is preferred, but not essential. In other preferred embodiments, the bosses may be formed prior to formation of the flow channel. However, it may be preferred to form the flow channel first since the channel form improves the rigidity of the blank, thereby reducing its tendency to bend or twist, and possibly resulting in improved accuracy of the boss stamping operation.
In some preferred methods of the invention, the channel 28 of plate 10 is formed by stamping the strip 52 or blank 53 with a single channel-forming die which is of fixed length and which is stationary relative to the longitudinal axis of strip 52 or blank 53. The bosses 32 are then formed by a plurality of dies which may preferably be movable relative to the longitudinal axis. This type of arrangement may permit a limified amount of variation in the length of plate (as further described below with reference to Figures 23 to 32). However, where it is necessary to accommodate large variations in the length of plate 10, replacement of the channel-forming die by another die of different length would be required. The relative positions of the boss-forming dies w~auld then be adjusted for compatibility wifih the new channel length.
In order to minimize tooling costs, the present invention provides methods which allow the channel length to be easily varied without replacemenfi of the channel-forming die. A preferred embodiment of such a method is described below with reference to Figures 14 to 22, which illustrates a method in which the channel 28 is formed by one or more stamping operations involving the use of a channel-forming die 80 which is movable along the longitudinal axis of the .
strip 52 or blank 53, thereby permitting variation of the channel length for production of plates 10 having lengths within a predetermined range.
Each stamping operation using an axially movable channel-forming die 80 produces a channel segment having a length which is equal to or less than the total length of the channel 28. For example, where the desired plate length is at the lower limit of the predetermined range, the channel 28 is preferably formed by one stamping operation using an axially movable channel-forming die 80, wherein the length of the channel segment produced by the axially movable channel-forming die 80 is equal to the total length of the channel 28.
On the other hand, where the desired plate length is above the lower limit of the predetermined range, the channel 28 will be formed by two or more stamping operations, at least one of which involves the use of a movable channel-forming die 80. In this case, the length of the channel segment produced by the axially movable channel-forming die 80 will be less than the total length of the channel 28. It will be appreciated that the two or more stamping operations could be performed by a single axially movable channel-forming die 80, by two or more axially-movable channel forming dies 80, or by an axially movable channel-forming die 80 in combination with a stationary channel-forming die.
In the particular method illustrated by Figures 14 to 22, the desired length of channel 28 is greafier than the lower limit of the predetermined range, such that multiple stamping operations are required to form channel 28. In this preferred embodiment, at least one of the stamping operations is performed by an axially movable channel-forming die 80. This preferred method is now described in detail below.
The method illustrated in Figures 14 to 21 begins with a blank 53 which has a width and length substantially the same as that of plate 10 as described above.
As in Figure 4, the blank 53 has an elongate central portion 12 located between a pair of end portions 14, with the approximate boundaries between central portion 12 and end portions 14 being indicated by dotted lines 16. The blank 53 is fed to an apparatus 78 comprising one or more axially movable channel-forming dies 80, each of which comprises an upper die portion 82 and a lower die portion 84.
As shown in Figures 16 and 17, the upper and lower die portions 82 and 84 are closed on the blank 53 to form a first channel portion 28a having a proximal end portion 86a and a distal end portion 88a, shown in Figure 14. The distal end portion 88a terminates at or near the boundary 16 between the central portion 12 and one of the end portions 14 of the blank 53.
Following formation of the first channel portion 28a, the die portions 82 and are opened as in Figure 18. As shown in Figures 16 to 21, the opposite ends 90, 92 of upper die portion 82 are rounded or tapered. This provides the proximal and distal end portions 86a, 88a of first channel portion 28a with gradual terminations 98a, 1 OOa which may either be rounded or tapered, thereby avoiding damage to the blank 53. In the drawings, the terminations 98a and 100a are shown as being rounded and are exaggerated so as to be clearly visible.
The next step in the method comprises formation of a second channel portion 28b which, as shown in Figure 15, comprises a proximal end portion 86b and a distal end portion 88b, with the distal end portion 88b terminafiing at or near the boundary 16 between the central portion 12 and one of the end portions 14 of the blank 53. It can be seen from Figure 15 that the proximal end portion 86a of the first channel portion 28a and the proximal end portion 86b of the second channel portion 28b overlap one another by an amount A, and that the distal end portions 88a and 88b are spaced from one another along the longitudinal axis by an amount which is preferably equal to the desired length of channel 28.
The second stamping operation may preferably be performed by the same die 80 which performed the first stamping operation illustrated in Figures 16 to 18.
In this case, the blank 53 preferably remains stationary during the formation of channel 28, while the single channel-forming die 80 is displaced axially between the first and second stamping operations.
In the alternative, as shown in Figures 19 to 22, the first and second stamping operations may be performed by different channel-forming dies 80. Although the dies 80 may be axially aligned relative to one another, they are shown in Figure 22 as being located at different stamping stations which are transversely spaced from one another such that the blank 53 must be moved transversely between the first and second stamping operations.
Although dies 80 are described above as being axially movable, it will be appreciated that one of the dies 80 used to form the first channel portion 28a and the second channel portion 28b could be stationary with respect to the longitudinal axis of blank 53.
The upper die portion 82 of channel-forming die 80 used in the second stamping operation shown in Figure 19 also has rounded or tapered ends 90, 92 so as to provide the second channel portion 28b with a gradual termination 100b at the distal end portion 88b. Due to the overlap of the proximal end portions 86a and 86b, no gradual termination 98b will be seen at the proximal end portion 86b of the second channel portion 28b. l~or is the terminal end portion 98a of the first channel portion 28a visible after the second stamping operation. Rather, the proximal end portions 86a and 86b will blend smoothly together to form a channel 28 of substantially uniform cross section.
fps mentioned above, at least one of the channel-forming dies 80 is movable along the longitudinal axis so as to vary the area of overlap A. In order to ensure that the. channel 28 is of constant cross section, it is necessary that the proximal end portions 86a and 86b overlap to an extent sufficient that the gradual terminations 98a and 98b are not present in the channel 28. In most preferred embodiments of the invention, at least about 1 inch ofi overlap will be required to ensure that the channel 28 is of constant cross-section.
Following the channel stamping operations shown in Figures 14 to 21, the formation of plate 10 is completed by formation of the raised bosses 32 as .
described above with reference to Figures 6 to 10. As.shown in Figure 22, the bosses may be formed simultaneously by axially-aligned boss-forming dies 81, both of which are preferably movable relative to the longitudinal axis. It will, however, be appreciated that the boss-forming dies 81 may be transversely spaced from one another and that the formation of each of the bosses 32 will typically require multiple stamping operations performed by multiple pairs of boss-forming dies 81.
Another preferred variation of the method according to the invention is illustrated in Figures 23 to 32. In this variation of the method, a blank 53 is provided as in the previous embodiments having a width and length substantially the same as that of plate 10, and having an elongate central portion 12 located between a pair of end portions 14, with the approximate boundaries between central portion 12 and end portions 14 being indicated by dotted lines 16. The blank 53 is fed to an apparatus 102 comprising a channel-forming die 104 having an upper die portion 106 and a lower die portion 108.
In this embodiment, a first channel portion 110 is formed having end portions 112 and 114. The first channel portion 110 has a length which is somewhat less than the length of the channel 28, such that at least one of its end portions is spaced from the approximate boundary 16 between the central portion 12 and fihe end portions 14 of the blank 53. In the preferred embodiment shown in the drawings, both end portions 112, 114 of the channel portion 110 are spaced from lines 16.
The channel-forming die 104 may either be movable al~ng the longitudinal axis or may be stationary. In the preferred embodiment shown in Figures 25 to 27, the channel-forming die 104 is stationary. If desired, the stationary channel die 104 may be replaced by dies) 80 as described above such that the first channel portion 110 is formed in two separate stamping operations.
As in the previously described embodiment, the upper~die portion106 of channel-forming die 104 preferably has opposite ends 116, 118 which are rounded or tapered. As shown in Figure 23, the curvature of the upper die portion 106 provides the end portions112, 114 of the first channel portion 110 with gradual terminations 120, 122, thereby avoiding damage to the blank 53.
As in the embodiment described above, the curvature of ends 116, 118 is exaggerated in the drawings.
The next step in the method, illustrated in Figures 24, 28 and 29, comprises formation of a second channel portion 124 and a first one of the raised bosses 32, the channel portion 124 and the first boss 32 being formed together by stamping the blank 53 with a combined die 126 having an upper die portion 128 and a lower die portion 130. The upper and lower die portions 128, 130 have boss-forming portions 132, 134 for forming the boss, and also have channel-forming portions 136,, 138 for forming the second channel portion 124. The .
terminal end 140 of the channel-forming portion136 of the upper die portion128 is preferably smoothly rounded or tapered to blend the first and second channel portions 110, 124.
As shown in Figure 24, the end portion 112 of the first channel portion 110 and the second channel portion 124 overlap one another by an amount B which is variable depending on the desired length of the plate 10. Preferably, the combined die 126 is movable along the longitudinal axis to vary the amount of overlap B and thereby vary the length of the plate 10. In order to ensure that the channel 28 is of a substantially uniform cross secfiion, the amount of overlap is sufficient to ensure that rounded terminations of the first and second channel portions 110, 12~~ are not present in the channel. Preferably, as mentioned above, the amount of overlap B is at least about 1 inch.
As shown in Figures 6 to 10, it will be appreciated that more than one operation is typically required to form the bosses 32. In the preferred embodiment using combined die 126, at least one of the boss forming operations will be performed by a combined die 126, with one or more of the boss-forming operations optionally being performed by dies) which have only a boss-forming portion.
The partially finished plate 10 shown in Figure 24 is then subjected to a third stamping operation, shown in Figure 30, in which a third channel portion 144 and a second boss 32' are formed together by stamping the partially finished plate 10 with a combined die 126' which is preferably an identical mirror image of combined die 126. Combined die 126' has an upper die portion 128' with a boss-forming portion 132' and a channel-forming portion 136', and has a lower die portion 130' with a boss-forming portion 134' and a channel-forming portion 138'. As shown in Figure 31, the end portion 114 of the first channel portion 110 overlaps the third channel portion 144 by an amount C which is variable depending on the desired length of the plate 10, and is preferably at least about 1 inch. Preferably, the combined die 126' is movable along the longitudinal axis to vary the amount of overlap C and thereby vary the length of the plate 10.
Figure 32 illustrates the sequence of steps which may be followed in the method described above with reference to Figures 23 to 31. In the embodiment illustrated in Figure 32, the blank 53 is fed transversely to a channel-forming die 104 and then to axially-aligned combined dies 126 and 126'. It will, however, be appreciated that the boss-forming dies are not necessarily axially aligned with one another.
Although the invention has been described in relation to certain preferred embodiments, it is not limited thereto. Rather, the invention includes all embodiments which may fall within the sc~pe of the following claims.
Claims (41)
1. A method for forming a plate for a heat exchanger, comprising:
(a) providing a flat sheet metal blank having a pair of elongate, longitudinally extending side edges and having end edges extending between the side edges, the side edges being parallel to each other such that the blank is of constant width, the blank having a central portion located between a pair of longitudinally-spaced end portions;
(b) forming a pair of raised shoulders in the central portion of the blank, the shoulders being spaced from one another and spaced from the side edges, wherein a raised fluid flow channel is defined between the shoulders and wherein a width of the central portion after formation of the shoulders defines a maximum width of the plate;
and (c) forming a pair of raised bosses in the blank, each of the bosses being formed in one of the end portions of the blank and being raised relative to the side edges and the fluid flow channel;
wherein each of the bosses has a pair of longitudinally-extending sides and has a longitudinal dimension which is greater than its transverse dimension;
wherein, during formation of the bosses, material from the end portions of the blank is drawn inwardly toward the bosses, thereby causing the side edges to converge inwardly toward one another along the sides of the bosses, such that a transverse distance between the side edges reaches a minimum along the sides of the bosses;
wherein said minimum transverse distance between the side edges defines a minimum width of the plate; and wherein the shoulders and the bosses are sufficiently spaced from the side edges of the plate such that a continuous flange is formed along an entire periphery of the plate.
(a) providing a flat sheet metal blank having a pair of elongate, longitudinally extending side edges and having end edges extending between the side edges, the side edges being parallel to each other such that the blank is of constant width, the blank having a central portion located between a pair of longitudinally-spaced end portions;
(b) forming a pair of raised shoulders in the central portion of the blank, the shoulders being spaced from one another and spaced from the side edges, wherein a raised fluid flow channel is defined between the shoulders and wherein a width of the central portion after formation of the shoulders defines a maximum width of the plate;
and (c) forming a pair of raised bosses in the blank, each of the bosses being formed in one of the end portions of the blank and being raised relative to the side edges and the fluid flow channel;
wherein each of the bosses has a pair of longitudinally-extending sides and has a longitudinal dimension which is greater than its transverse dimension;
wherein, during formation of the bosses, material from the end portions of the blank is drawn inwardly toward the bosses, thereby causing the side edges to converge inwardly toward one another along the sides of the bosses, such that a transverse distance between the side edges reaches a minimum along the sides of the bosses;
wherein said minimum transverse distance between the side edges defines a minimum width of the plate; and wherein the shoulders and the bosses are sufficiently spaced from the side edges of the plate such that a continuous flange is formed along an entire periphery of the plate.
2. The method according to claim 1, wherein the blank has a length substantially the same as a length of the plate.
3. The method of claim 1, wherein each of the shoulders extends longitudinally along one of the side edges, such that the fluid flow channel extends longitudinally along the blank.
4. The method of claim 1, wherein the shoulders terminate so as not to substantially extend into the end portions.
5. The method of claim 1, wherein the fluid flow channel is formed by stamping.
6. The method of claim 1, wherein the fluid flow channel is formed by rolling.
7. The method of claim 1, wherein the bosses are formed by one or more stamping or drawing operations.
8. The method of claim 1, further comprising the step of:
(d) forming a first aperture in an upper surface of each of the bosses.
(d) forming a first aperture in an upper surface of each of the bosses.
9. The method of claim 8, wherein the first aperture in the upper surface of each of the bosses is formed by cutting out a central portion of the upper surface, the central portion having a second aperture.
10. The method of claim 9, wherein both the first and second apertures are elongated along the longitudinal dimensions of the bosses.
11. The method of claim 10, wherein the second aperture comprises a pair of spaced, circular holes joined by a longitudinally extending slit.
12. The method of claim 1, wherein said blank has a pair of said end edges, the end edges extending transversely between the side edges.
13. The method of claim 1, wherein the bosses are oval shaped and wherein the longitudinally-extending sides of the bosses are substantially straight.
14. The method of claim 1, wherein the plate is formed in the absence of edge trimming along the shoulders of the plate.
15. The method of claim 1, further comprising the step of severing the blank from a strip or sheet of sheet metal.
16. The method of claim 15, wherein the blanks are formed by severing the strip transversely at one or more points.
17. The method of claim 16, wherein the strip is severed prior to formation of the shoulders.
18. The method of claim 16, wherein the strip is severed after formation of the shoulders and prior to formation of the bosses.
19. The method of claim 1, further comprising the step of trimming the plate along longitudinally extending lines, each of the lines extending tangentially along one of the side edges at a point where the side edge converges inwardly toward one of the bosses, each of the lines terminating at one of the end edges.
20. The method of claim 19, wherein said step of trimming the plate produces a rounded transition between the side edges and the end edges of the plate.
21. The method of claim 1, wherein the sheet metal blank is formed from a brazeable material.
22. The method of claim 21, wherein the brazeable material is selected from the group comprising aluminum, an aluminum alloy, and aluminum or an aluminum alloy coated with a brazing alloy.
23. The method of claim 1, wherein each of the bosses is formed inwardly of a peripheral edge of one of the end portions, such that a peripheral sidewall of the boss is spaced from the peripheral edge of one of the end portions, thereby forming a peripheral flange along the peripheral edge of the end portion.
24. The method of claim 23, wherein each of the peripheral flanges extending along the sidewalls of the bosses are bent along a line which is parallel to the longitudinal axis, thereby forming tabs which extend substantially at right angles to a remaining portion of the peripheral flange.
25. The method of claim 24, wherein both tabs are bent in the same direction.
26. The method of claim 24, wherein the tabs are bent in opposite directions.
27. The method of claim 1, wherein the step of forming the fluid flow channel comprises:
stamping a first channel portion having a proximal end portion and a distal end portion; and stamping a second channel portion having a proximal end portion and a distal end portion;
wherein the proximal end portions overlap one another by a predetermined amount and the distal end portions are spaced from one another along the longitudinal axis.
stamping a first channel portion having a proximal end portion and a distal end portion; and stamping a second channel portion having a proximal end portion and a distal end portion;
wherein the proximal end portions overlap one another by a predetermined amount and the distal end portions are spaced from one another along the longitudinal axis.
28. The method of claim 27, wherein the first channel portion is formed by a first channel-forming die and the second channel portion is formed by a second channel-forming die, at least one of the first and second channel-forming dies being movable along the longitudinal axis.
29. The method of claim 28, wherein both the first and second channel-forming dies are movable along the longitudinal axis.
30. The method of claim 28, further comprising the step of moving one or both of the channel-forming dies along the longitudinal axis to increase or decrease an amount of overlap between the distal end portions of the first and second channel portions.
31. The method of claim 27, wherein the predetermined amount of overlap is sufficient to blend the proximal end portions of the first and second channel portions together, such that the fluid flow channel has a substantially uniform cross section between the distal end portions.
32. The method of claim 27, wherein the predetermined amount of overlap is at least about 1 inch measured along the longitudinal axis.
33. The method of claim 27, wherein the first channel portion is formed by a channel-forming die; and wherein the second channel portion and one of the raised bosses are formed together by one or more stamping operations, at least one of the stamping operations comprising stamping the strip with a combined die having a boss-forming portion and a channel-forming portion.
34. The method of claim 33, wherein the channel-forming die for forming the first channel portion is fixed in position relative to the longitudinal axis.
35. The method of claim 33, wherein the combined die is movable along the longitudinal axis so as to vary the predetermined amount of overlap.
36. An apparatus for forming a heat exchanger plate from a flat, sheet metal blank, the heat exchanger plate having a central portion defining an elongate fluid flow channel extending along a longitudinal axis, a pair of end portions separated by the central portion, and raised bosses provided in each of the end portions, each of the raised bosses being provided with a fluid flow aperture and having an interior in communication with the fluid flow aperture and the fluid flow channel, the apparatus comprising a plurality of dies for forming the fluid flow channel and the raised bosses, the dies including:
(a) a first channel-forming die for forming a first portion of the fluid flow channel in said blank; and (b) a second channel-forming die for forming a second portion of the fluid flow channel in said blank, wherein the first and second channel-forming dies are axially positioned relative to one another such that an area of overlap is formed where the first portion of the fluid flow channel overlaps the second portion of the fluid flow channel;
and (c) a plurality of dies for forming the raised bosses;
wherein at least one of the first and second channel-forming dies is movable along the longitudinal axis so as to vary the area of overlap.
(a) a first channel-forming die for forming a first portion of the fluid flow channel in said blank; and (b) a second channel-forming die for forming a second portion of the fluid flow channel in said blank, wherein the first and second channel-forming dies are axially positioned relative to one another such that an area of overlap is formed where the first portion of the fluid flow channel overlaps the second portion of the fluid flow channel;
and (c) a plurality of dies for forming the raised bosses;
wherein at least one of the first and second channel-forming dies is movable along the longitudinal axis so as to vary the area of overlap.
37. The apparatus of claim 36, wherein the dies for forming the bosses are fixed in position relative to the longitudinal axis.
38. The apparatus of claim 36, wherein the second channel-forming die comprises a combined die having a boss-forming portion for forming one of the raised bosses and a channel-forming portion for forming the second channel portion, wherein the boss-forming portion comprises one of said dies for forming the raised bosses.
39. The apparatus of claim 38, wherein the first channel-forming die is fixed in position relative to the longitudinal axis and the second channel-forming die is movable along the longitudinal axis.
40. The apparatus of claim 38, wherein the combined die is movable along the longitudinal axis so as to vary the predetermined amount of overlap.
41. The apparatus of claim 38, further comprising:
a third channel-forming die for forming a third portion of the fluid flow channel which overlaps the first portion of the channel and is distal to the second portion of the channel, wherein the first and third channel-forming dies are axially positioned relative to one another such that an area of overlap is formed where the first portion of the fluid flow channel overlaps the third portion of the fluid flow channel;
wherein the first channel-forming die is fixed in position relative to the longitudinal axis and both the second and third channel-forming dies are movable along the longitudinal axis so as to vary the areas of overlap; and wherein the third channel-forming die comprises a combined die having a boss-forming portion for forming one of the raised bosses and a channel-forming portion for forming the third channel portion.
a third channel-forming die for forming a third portion of the fluid flow channel which overlaps the first portion of the channel and is distal to the second portion of the channel, wherein the first and third channel-forming dies are axially positioned relative to one another such that an area of overlap is formed where the first portion of the fluid flow channel overlaps the third portion of the fluid flow channel;
wherein the first channel-forming die is fixed in position relative to the longitudinal axis and both the second and third channel-forming dies are movable along the longitudinal axis so as to vary the areas of overlap; and wherein the third channel-forming die comprises a combined die having a boss-forming portion for forming one of the raised bosses and a channel-forming portion for forming the third channel portion.