CA2510816C - Microorganism-removing filter medium having high isoelectric material and low melt index binder - Google Patents
Microorganism-removing filter medium having high isoelectric material and low melt index binder Download PDFInfo
- Publication number
- CA2510816C CA2510816C CA 2510816 CA2510816A CA2510816C CA 2510816 C CA2510816 C CA 2510816C CA 2510816 CA2510816 CA 2510816 CA 2510816 A CA2510816 A CA 2510816A CA 2510816 C CA2510816 C CA 2510816C
- Authority
- CA
- Canada
- Prior art keywords
- filter medium
- recited
- particles
- inorganic material
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A filter medium capable of removing microorganisms from a fluid such as water. The filter medium includes particles of activated carbon, particles of a substantially insoluble inorganic material having an isoelectric point greater than the fluid being filtered. A low melt index binder, preferably with a melt index of less than about 1 gram per 10 minutes, binds the particles of activated carbon and particles of inorganic material, such that the binder will become tacky at elevated temperatures without becoming sufficiently liquid to substantially wet the particles of activated carbon and inorganic material. An antimicrobial material can be incorporated into the filter to prevent biofilm growth. The use of a biocidal material in combination with the high isoelectric point material provides a trap-and-kill mechanism for microorganism removal
Description
MICROORGANISM-REMOVING FILTER MEDIUM HAVING HIGH
ISOELECTRIC MATERIAL AND LOW MELT INDEX BINDER
The present invention relates to filtration materials, and more particularly, this invention relates to a filter medium having enhanced microorganism-removing properties.
BACKGROUND OF THE INVENTION
The use of home water treatment systems to treat tap water continues to grow dramatically in the U.S. and abroad, in part because of heightened public awareness of the health concerns associated with the consumption of untreated tap water. Of particular concern are pathogens, which are microbes that cause disease. They include a few types of bacteria, viruses, protozoa, and other organisms. Some pathogens are often found in water, frequently as a result of fecal matter from sewage discharges, leaking septic tanks, and runoff from animal feedlots into bodies of water from which drinking water is taken. Bio-terrorism also poses a significant threat to water supplies.
Total Coliforms are a group of closely related bacteria that live in soil and water as well as the gut of animals. The extent to which total coliforms are present in the source water can indicate the general quality of that water and the likelihood that the water is fecally contaminated. Specific types of coliforms (i.e., fecal coliforms or E. coli) can present serious health risks. The Environmental Protection Agency (EPA) has set forth minimum standards for acceptance of a device proposed for use as a microbiological water purifier. Devices that claim removal of coliforms, represented by the bacteria E. coli and Klebsiella Terregina, must show a minimum 6-log reduction, 99.9999% of organisms removed, from an influent concentration of 1x107/100 ml.
Cryptosporidium is a single-celled microbe contained in a group generally known as protozoa. Cryptosporidium may cause a disease, cryptosporidiosis, when ingested. Cryptosporidiosis symptoms can range from mild stomach upset to life threatening disease in those who are immunocompromised (e.g., people with severely compromised immune systems). Oocysts are a stage in the life-cycle of some Cryptosporidium. In this stage, the Cryptosporidium can infect humans and other animals. The EPA requires removal of at least 99% of Cryptosporidium from water for qualified devices.
Giardia lamblia (commonly referred to as Giardia) are single-celled microbes contained in a group known as protozoa. When ingested, they can cause a gastrointestinal disease called giardiasis. Giardiasis is a frequent cause of diarrhea.
Symptoms may include diarrhea, fatigue, and cramps. Waterborne giardiasis may occur as a result of disinfection problems or inadequate filtration procedures. Cysts 482.116A
ISOELECTRIC MATERIAL AND LOW MELT INDEX BINDER
The present invention relates to filtration materials, and more particularly, this invention relates to a filter medium having enhanced microorganism-removing properties.
BACKGROUND OF THE INVENTION
The use of home water treatment systems to treat tap water continues to grow dramatically in the U.S. and abroad, in part because of heightened public awareness of the health concerns associated with the consumption of untreated tap water. Of particular concern are pathogens, which are microbes that cause disease. They include a few types of bacteria, viruses, protozoa, and other organisms. Some pathogens are often found in water, frequently as a result of fecal matter from sewage discharges, leaking septic tanks, and runoff from animal feedlots into bodies of water from which drinking water is taken. Bio-terrorism also poses a significant threat to water supplies.
Total Coliforms are a group of closely related bacteria that live in soil and water as well as the gut of animals. The extent to which total coliforms are present in the source water can indicate the general quality of that water and the likelihood that the water is fecally contaminated. Specific types of coliforms (i.e., fecal coliforms or E. coli) can present serious health risks. The Environmental Protection Agency (EPA) has set forth minimum standards for acceptance of a device proposed for use as a microbiological water purifier. Devices that claim removal of coliforms, represented by the bacteria E. coli and Klebsiella Terregina, must show a minimum 6-log reduction, 99.9999% of organisms removed, from an influent concentration of 1x107/100 ml.
Cryptosporidium is a single-celled microbe contained in a group generally known as protozoa. Cryptosporidium may cause a disease, cryptosporidiosis, when ingested. Cryptosporidiosis symptoms can range from mild stomach upset to life threatening disease in those who are immunocompromised (e.g., people with severely compromised immune systems). Oocysts are a stage in the life-cycle of some Cryptosporidium. In this stage, the Cryptosporidium can infect humans and other animals. The EPA requires removal of at least 99% of Cryptosporidium from water for qualified devices.
Giardia lamblia (commonly referred to as Giardia) are single-celled microbes contained in a group known as protozoa. When ingested, they can cause a gastrointestinal disease called giardiasis. Giardiasis is a frequent cause of diarrhea.
Symptoms may include diarrhea, fatigue, and cramps. Waterborne giardiasis may occur as a result of disinfection problems or inadequate filtration procedures. Cysts 482.116A
are a stage in the life-cycle of some Giardia. In this stage, the Giardia can infect humans and other animals. Devices that claim cyst removal must show a minimum log reduction, 99.9% of cysts removed, from an influent concentration of 1x10'2.
Viruses, including hepatitis A virus, rotaviruses, and Norwalk and other caliciviruses, are microbes that can cause serious illness. The EPA requires water purifiers to ensure a 4 log reduction, 99.99% of viruses removed, from an influent concentration of 1x107/L.
Two types of systems exist for the filtration of tap water. One type is pressurized, such as a faucet-mount system, and typically uses a porous carbon block as part of the filtration system. The other type is a low pressure system, such as a pitcher filter system, and typically uses activated carbon granules as part of the filtration system. However, few filtration materials are able to meet EPA
standards for more than a few liters of water with filters of a reasonable size.
We have surprisingly found that a synergistic effect occurs when inorganic materials with high isoelectric points, such as magnesium salts, and activated carbon are bound by a low melt index binder. The resulting filter medium is very effective at removing microorganisms from large quantities of water, in filters small enough for point-of-use systems.
Magnesium salts have been used to remove polar materials from non-polar liquids by filtration. For example, United States Patent No. 6,338,830 to Moskovitz and Kepner describes the use of Group IIA, Group IIIA, Goup IVA, Group VA and transition metal oxide to remove contaminants from non-aqueous liquid or gas streams.
482.116A
Viruses, including hepatitis A virus, rotaviruses, and Norwalk and other caliciviruses, are microbes that can cause serious illness. The EPA requires water purifiers to ensure a 4 log reduction, 99.99% of viruses removed, from an influent concentration of 1x107/L.
Two types of systems exist for the filtration of tap water. One type is pressurized, such as a faucet-mount system, and typically uses a porous carbon block as part of the filtration system. The other type is a low pressure system, such as a pitcher filter system, and typically uses activated carbon granules as part of the filtration system. However, few filtration materials are able to meet EPA
standards for more than a few liters of water with filters of a reasonable size.
We have surprisingly found that a synergistic effect occurs when inorganic materials with high isoelectric points, such as magnesium salts, and activated carbon are bound by a low melt index binder. The resulting filter medium is very effective at removing microorganisms from large quantities of water, in filters small enough for point-of-use systems.
Magnesium salts have been used to remove polar materials from non-polar liquids by filtration. For example, United States Patent No. 6,338,830 to Moskovitz and Kepner describes the use of Group IIA, Group IIIA, Goup IVA, Group VA and transition metal oxide to remove contaminants from non-aqueous liquid or gas streams.
482.116A
United States Patent Application No. 2002/0050474 to Munson and Roberts describes the use of magnesium silicate to remove polar impurities from used cooking oils.
Magnesium ions have also been used to promote cell survival. For example, United States Patent No. 6,096,216 to Shanbrom describes the use of magnesium salts to preserve biological fluids during filtration through iodinated resin.
United States Patent Application No. 2002/0053537 to Lucido and Shaffer describes the use of magnesium as a nutrient to feed microorganisms in a bioreacter.
International Patent Application WO 01/07090 to Hou et al. describes cationic polymers attached to substrates, including carbon blocks, for removing microorganisms.
Some prior art filters use biocidal resins and peroxides to kill microorganisms.
For example, United States Patent No. 4,361,486 to Hou and Webster describes the use of magnesium peroxide to oxidize soluble iron and inactivate microorganisms. A
drawback to such filters is that the biocidal agent as well as the dead microorganisms pass through the filter and into the drinking water.
International Patent Application WO 02/076577 to Hughes broadly describes the use of magnesium compounds in carbon block form to remove microorganisms from a fluid, and is herein incorporated by reference. The purification material disclosed in Application WO 02/076577 removes microorganisms from fluids through adsorption to the magnesium compound. However, because the magnesium containing material only represents a small percentage of the surface area exposed to the fluid, the sites to which microorganisms can become adsorbed are few.
Thus, the efficiency of the filter is limited, in that many microorganisms are not captured but merely pass through the filter. In addition, the adsorption sites quickly fill up, making 482.116A
Magnesium ions have also been used to promote cell survival. For example, United States Patent No. 6,096,216 to Shanbrom describes the use of magnesium salts to preserve biological fluids during filtration through iodinated resin.
United States Patent Application No. 2002/0053537 to Lucido and Shaffer describes the use of magnesium as a nutrient to feed microorganisms in a bioreacter.
International Patent Application WO 01/07090 to Hou et al. describes cationic polymers attached to substrates, including carbon blocks, for removing microorganisms.
Some prior art filters use biocidal resins and peroxides to kill microorganisms.
For example, United States Patent No. 4,361,486 to Hou and Webster describes the use of magnesium peroxide to oxidize soluble iron and inactivate microorganisms. A
drawback to such filters is that the biocidal agent as well as the dead microorganisms pass through the filter and into the drinking water.
International Patent Application WO 02/076577 to Hughes broadly describes the use of magnesium compounds in carbon block form to remove microorganisms from a fluid, and is herein incorporated by reference. The purification material disclosed in Application WO 02/076577 removes microorganisms from fluids through adsorption to the magnesium compound. However, because the magnesium containing material only represents a small percentage of the surface area exposed to the fluid, the sites to which microorganisms can become adsorbed are few.
Thus, the efficiency of the filter is limited, in that many microorganisms are not captured but merely pass through the filter. In addition, the adsorption sites quickly fill up, making 482.116A
adsorption difficult if not impossible and/or resulting in clogging of the filter pores ultimately resulting in a short filter life. For example, Application WO
only discloses the ability to remove microorganisms from 500 ml of water.
Moreover, the filter disclosed in Application WO 02/076577 is very large, with an outer diameter of 2.5 inches, an inner diameter of 1.25 inches, and length of 9.8 inches, making it unsuitable for many point-of-use purposes and in portable devices.
United States Patent Nos. 4,753,728 and 5,017,318 to Vanderbilt et al.
describe a filter constructed of powdered activated carbon bound by an ultra high molecular weight polyethylene binder, but which is only capable of capturing insignificant quantities of microorganisms.
United States Patent Application No. US 2003/0038084 to Mitchell et al.
describes a filter composed of carbon particles heated in an oven in an atmosphere of ammonia that purportedly removes microorganisms through a combination of capturing fimbriae and surface polymers of the microorganisms in pores on the surface of the particular carbon particle, by adsorption and size exclusion.
What is needed is a more efficient filter medium capable of removing microorganisms to EPA standards from substantially larger quantities of water per unit filter medium than was heretofore possible.
482.116A
only discloses the ability to remove microorganisms from 500 ml of water.
Moreover, the filter disclosed in Application WO 02/076577 is very large, with an outer diameter of 2.5 inches, an inner diameter of 1.25 inches, and length of 9.8 inches, making it unsuitable for many point-of-use purposes and in portable devices.
United States Patent Nos. 4,753,728 and 5,017,318 to Vanderbilt et al.
describe a filter constructed of powdered activated carbon bound by an ultra high molecular weight polyethylene binder, but which is only capable of capturing insignificant quantities of microorganisms.
United States Patent Application No. US 2003/0038084 to Mitchell et al.
describes a filter composed of carbon particles heated in an oven in an atmosphere of ammonia that purportedly removes microorganisms through a combination of capturing fimbriae and surface polymers of the microorganisms in pores on the surface of the particular carbon particle, by adsorption and size exclusion.
What is needed is a more efficient filter medium capable of removing microorganisms to EPA standards from substantially larger quantities of water per unit filter medium than was heretofore possible.
482.116A
SUMMARY OF THE INVENTION
The present invention solves the problems described above by providing a filter medium capable of removing a large percentage of microorganisms from a fluid such as water. The filter medium includes particles of activated carbon (e.g., granular activated carbon (GAC), powdered activated carbon, etc.). The filter medium also has particles of a substantially insoluble inorganic material having an isoelectric point greater than the pH of the fluid being filtered, typically above about 7.0 pH, preferably greater than 9.0 pH, and even more preferably greater than 10.0 pH.
A
binder binds the particles of activated carbon and particles of inorganic material. The binder has a melt index of less than about 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load, such that the binder will become tacky at elevated temperatures without becoming sufficiently liquid to substantially wet the particles of activated carbon and inorganic material.
When water at a pH less than the isoelectric point of the inorganic material is passed through the filter, the high-isoelectric-point inorganic material imparts a positive charge on the filter surface, thereby attracting and adsorbing negatively charged microorganisms to the filter surface by electrostatic forces.
In one embodiment, the inorganic material is present in an amount ranging from about 25 weight percent to about 45 weight percent of the total weight of the filter medium. In another embodiment, the inorganic material is present in an amount ranging from about 40 weight percent to about 50 weight percent of the total weight of the filter medium. A preferred inorganic material is a magnesium compound such as magnesium hydroxide or magnesium oxide.
482.116A
The present invention solves the problems described above by providing a filter medium capable of removing a large percentage of microorganisms from a fluid such as water. The filter medium includes particles of activated carbon (e.g., granular activated carbon (GAC), powdered activated carbon, etc.). The filter medium also has particles of a substantially insoluble inorganic material having an isoelectric point greater than the pH of the fluid being filtered, typically above about 7.0 pH, preferably greater than 9.0 pH, and even more preferably greater than 10.0 pH.
A
binder binds the particles of activated carbon and particles of inorganic material. The binder has a melt index of less than about 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load, such that the binder will become tacky at elevated temperatures without becoming sufficiently liquid to substantially wet the particles of activated carbon and inorganic material.
When water at a pH less than the isoelectric point of the inorganic material is passed through the filter, the high-isoelectric-point inorganic material imparts a positive charge on the filter surface, thereby attracting and adsorbing negatively charged microorganisms to the filter surface by electrostatic forces.
In one embodiment, the inorganic material is present in an amount ranging from about 25 weight percent to about 45 weight percent of the total weight of the filter medium. In another embodiment, the inorganic material is present in an amount ranging from about 40 weight percent to about 50 weight percent of the total weight of the filter medium. A preferred inorganic material is a magnesium compound such as magnesium hydroxide or magnesium oxide.
482.116A
The binder can be an ultra high molecular weight polymer having a molecular weight greater than about 4 million. For example, the binder can be ultra high molecular weight polyethylene. In one embodiment, the melt index of the binder is less than about 0.1 grams per 10 minutes as determined by ASTM D 1238 at 190 degrees C. and 15 kilograms load. In one embodiment, the binder is present in an amount ranging from about 20 weight percent to about 35 weight percent of the total weight of the filter medium.
Another embodiment implements inorganic particles of differing particle size distributions to optimize structural integrity of the filter medium as well as contaminant removal. Particularly, the material with the larger particle size distribution results in a filter with greater structural integrity whereas the material with the smaller particle size distribution provides greater contaminant removal.
Note that additional adsorptive and/or binding materials may be added other than the activated carbon, inorganic material, and binder to alter the properties of the filter.
To further improve the antimicrobial effectiveness of the filter, and to extend the life of the filter, an antimicrobial material can be incorporated into the filter to prevent biofilm growth. The use of a biocidal material in combination with the high isoelectric point material provides a trap-and-kill mechanism for microorganism removal. Illustrative antimicrobial materials are silver-containing materials.
One type of silver-containing material implements soluble silver material to kill microbes by entering the water surrounding the filter medium via ion exchange. Another type of silver-containing material kills microorganisms on contact but does not elute or leach into solution. Particularly useful are materials comprising a polymeric matrix 482.116A
Another embodiment implements inorganic particles of differing particle size distributions to optimize structural integrity of the filter medium as well as contaminant removal. Particularly, the material with the larger particle size distribution results in a filter with greater structural integrity whereas the material with the smaller particle size distribution provides greater contaminant removal.
Note that additional adsorptive and/or binding materials may be added other than the activated carbon, inorganic material, and binder to alter the properties of the filter.
To further improve the antimicrobial effectiveness of the filter, and to extend the life of the filter, an antimicrobial material can be incorporated into the filter to prevent biofilm growth. The use of a biocidal material in combination with the high isoelectric point material provides a trap-and-kill mechanism for microorganism removal. Illustrative antimicrobial materials are silver-containing materials.
One type of silver-containing material implements soluble silver material to kill microbes by entering the water surrounding the filter medium via ion exchange. Another type of silver-containing material kills microorganisms on contact but does not elute or leach into solution. Particularly useful are materials comprising a polymeric matrix 482.116A
impregnated with a water-insoluble antimicrobial compound such as a silver halide (e.g., silver iodide).
In one embodiment, 75 grams of the filter medium performs a greater than 1 x plaque forming units/milliliter reduction of viruses in 100 gallons of water passing through the filter medium.
The mean pore size of pores formed by the particles and binder is can be between 0.01 micron and 10 microns, and preferably between 0.1 micron and 1 microns.
The filter medium can be shaped into any desired form, such as in the form of a block or sheet. For example, the filter medium can be cylindrically shaped with an outer diameter of less than about 4 inches and a maximum length between ends of the filter medium of less than about 3 inches.
The filter medium can be formed by mixing particles of activated carbon, particles of inorganic material, and the binder. The mixture is heated such that the binder becomes tacky without becoming sufficiently liquid to substantially wet the particles of activated carbon and inorganic material.
The filter medium is adaptable for use in a filtration device having a housing. The filtration device may be of the type adapted to be mounted to a water source, a pitcher, a bottle, water dispenser, etc. A pump can be coupled to the housing for controlling the flow of the fluid through the filter medium.
The embodiments described herein have particular applicability for countering a bioterrorism act, by enabling removal of potentially life-threatening microbials introduced into a water supply by a terrorist.
Accordingly, in one aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material;
In one embodiment, 75 grams of the filter medium performs a greater than 1 x plaque forming units/milliliter reduction of viruses in 100 gallons of water passing through the filter medium.
The mean pore size of pores formed by the particles and binder is can be between 0.01 micron and 10 microns, and preferably between 0.1 micron and 1 microns.
The filter medium can be shaped into any desired form, such as in the form of a block or sheet. For example, the filter medium can be cylindrically shaped with an outer diameter of less than about 4 inches and a maximum length between ends of the filter medium of less than about 3 inches.
The filter medium can be formed by mixing particles of activated carbon, particles of inorganic material, and the binder. The mixture is heated such that the binder becomes tacky without becoming sufficiently liquid to substantially wet the particles of activated carbon and inorganic material.
The filter medium is adaptable for use in a filtration device having a housing. The filtration device may be of the type adapted to be mounted to a water source, a pitcher, a bottle, water dispenser, etc. A pump can be coupled to the housing for controlling the flow of the fluid through the filter medium.
The embodiments described herein have particular applicability for countering a bioterrorism act, by enabling removal of potentially life-threatening microbials introduced into a water supply by a terrorist.
Accordingly, in one aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material;
wherein the insoluable inorganic material is admixed together with the particles of activated carbon; and wherein a first portion of the particles of inorganic material have a first mean particle size distribution and a second portion of the particles of inorganic material have a second mean particle size distribution, the first mean particle size distribution being larger than the second mean particle size distribution, and wherein the filter medium is formed in a block or sheet and wherein the binder has a melt index of less than 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load.
In another aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of magnesium hydroxide present at 40% to 50% by weight; and a binder for binding the particles of activated carbon and inorganic material, wherein magnesium hydroxide is admixed together with the particles of activated carbon and wherein, the binder has a melt index of less than 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load, and wherein the filter medium is formed in a block or sheet.
In yet a further aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material; an antimicrobial material, and wherein the filter medium is formed from a block or sheet and wherein the binder has a melt index of less than I gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load.
BRIEF DESCRIPTION OF THE DRAWINGS
For a fuller understanding of the nature and advantages of the present invention, as well as the preferred mode of use, reference should be made to the following detailed description read in conjunction with the accompanying drawings.
- 9a-Figure 1 is a chart showing the microorganism-removing capabilities of filter media having varying the concentration of magnesium hydroxide.
Figure 2 illustrates a block of the filter medium in cylindrical form.
Figure 3 illustrates the filter medium in the form of a sheet.
Figure 4 is a chart showing the removal of PRD-1 and MS-2 (representing rotavirus and poliovirus, respectively) and Klebsiella Terregina (representing bacteria) for 120+
gallons.
Figure 5 is a table showing the results of seven experiments testing the removal of bacteriophage MS-2 by cylindrically shaped filter media with varying concentrations of carbon, binder and magnesium hydroxide.
BEST MODES FOR CARRYING OUT THE INVENTION
The following description includes the best embodiments presently contemplated for carrying out the present invention. This description is made for the purpose of illustrating the general principles of the present invention and is not meant to limit the inventive concepts claimed herein.
The present invention provides a filter medium capable of removing microorganisms (bacteria, viruses, cysts, etc.) from large quantities of water, and in compliance with the EPA standards mentioned above. The inventors have surprisingly found that a synergistic effect occurs when inorganic materials with high isoelectric points and activated carbon are bound by a low melt index binder.
While not wishing to be bound by any particular theory, it is believed that the high-isoelectric-point inorganic material tends to adhere to the surface of the binder and possibly the carbon as well, and acts as an adsorption-enhancing material that imparts a positive charge on the surface of the pores of the filter medium when in the presence of a fluid having a pH lower than the isoelectric point of the inorganic material. Most microorganisms of concern have a negative surface charge. For example, most types of bacteria have a membrane layer of phospholipids that give the bacteria a negative charge. When negatively charged viruses and bacteria pass through the pores of the filter medium, they are attracted to the positively charged surface of the filter medium and become adsorbed to the surface by electrostatic interactions. Because most, if not all, of the surfaces of the pores themselves become charged, the filter medium has more charged sites with which to adsorb microorganisms, as well as an overall increase in electrostatic forces. Thus, the filter 482.116A
In another aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of magnesium hydroxide present at 40% to 50% by weight; and a binder for binding the particles of activated carbon and inorganic material, wherein magnesium hydroxide is admixed together with the particles of activated carbon and wherein, the binder has a melt index of less than 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load, and wherein the filter medium is formed in a block or sheet.
In yet a further aspect, the present invention resides in a filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material; an antimicrobial material, and wherein the filter medium is formed from a block or sheet and wherein the binder has a melt index of less than I gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load.
BRIEF DESCRIPTION OF THE DRAWINGS
For a fuller understanding of the nature and advantages of the present invention, as well as the preferred mode of use, reference should be made to the following detailed description read in conjunction with the accompanying drawings.
- 9a-Figure 1 is a chart showing the microorganism-removing capabilities of filter media having varying the concentration of magnesium hydroxide.
Figure 2 illustrates a block of the filter medium in cylindrical form.
Figure 3 illustrates the filter medium in the form of a sheet.
Figure 4 is a chart showing the removal of PRD-1 and MS-2 (representing rotavirus and poliovirus, respectively) and Klebsiella Terregina (representing bacteria) for 120+
gallons.
Figure 5 is a table showing the results of seven experiments testing the removal of bacteriophage MS-2 by cylindrically shaped filter media with varying concentrations of carbon, binder and magnesium hydroxide.
BEST MODES FOR CARRYING OUT THE INVENTION
The following description includes the best embodiments presently contemplated for carrying out the present invention. This description is made for the purpose of illustrating the general principles of the present invention and is not meant to limit the inventive concepts claimed herein.
The present invention provides a filter medium capable of removing microorganisms (bacteria, viruses, cysts, etc.) from large quantities of water, and in compliance with the EPA standards mentioned above. The inventors have surprisingly found that a synergistic effect occurs when inorganic materials with high isoelectric points and activated carbon are bound by a low melt index binder.
While not wishing to be bound by any particular theory, it is believed that the high-isoelectric-point inorganic material tends to adhere to the surface of the binder and possibly the carbon as well, and acts as an adsorption-enhancing material that imparts a positive charge on the surface of the pores of the filter medium when in the presence of a fluid having a pH lower than the isoelectric point of the inorganic material. Most microorganisms of concern have a negative surface charge. For example, most types of bacteria have a membrane layer of phospholipids that give the bacteria a negative charge. When negatively charged viruses and bacteria pass through the pores of the filter medium, they are attracted to the positively charged surface of the filter medium and become adsorbed to the surface by electrostatic interactions. Because most, if not all, of the surfaces of the pores themselves become charged, the filter medium has more charged sites with which to adsorb microorganisms, as well as an overall increase in electrostatic forces. Thus, the filter 482.116A
medium is able to remove substantially more microorganisms per unit weight of filter medium and/or per unit volume of filter medium than was heretofore possible.
As mentioned above, the adsorption-enhancing inorganic material has a high isoelectric point. A high isoelectric point is preferred, because if a fluid having the same or higher pH as the inorganic material is introduced to the filter medium, the microorganisms adsorbed to the filter medium will become detached and exit the filter. Thus, the "high isoelectric point" of the inorganic material is above a threshold pH suitable for the desired use. In other words, the isoelectric point of the inorganic material should be higher than the pH of the fluid being filtered.
Additionally, the greater the isoelectric point of the inorganic material, the greater the surface charge of the filter at neutral pH. One skilled in the art will understand that the pH
of the fluid to be filtered can be readily determined. For example, if the fluid is water with a pH
varying from 6.9 to 7.1, the isoelectric point of the inorganic material should be higher than 7.1. For commercial filters, a higher isoelectric point may be required.
For example, one test protocol of the EPA requires washing the filter with water having a pH of 9Ø The filter media disclosed in the EXAMPLES section below do not lose microorganisms under these conditions.
The term "particles" as used herein can refer to particles of any shape, as well as short pieces of strands or fibers, hollow or porous particles, etc. The term "fluid"
includes aqueous fluids such as water, or gases and mixtures of gases.
One method of making the filter medium is by mixing and heating particles of activated carbon, particles of inorganic material, and particles of binder in a mold of the desired shape, then compressing the mixture to encourage binding and to adjust the pore size. An illustrative range of compression is between about 1 percent to 482.116A
As mentioned above, the adsorption-enhancing inorganic material has a high isoelectric point. A high isoelectric point is preferred, because if a fluid having the same or higher pH as the inorganic material is introduced to the filter medium, the microorganisms adsorbed to the filter medium will become detached and exit the filter. Thus, the "high isoelectric point" of the inorganic material is above a threshold pH suitable for the desired use. In other words, the isoelectric point of the inorganic material should be higher than the pH of the fluid being filtered.
Additionally, the greater the isoelectric point of the inorganic material, the greater the surface charge of the filter at neutral pH. One skilled in the art will understand that the pH
of the fluid to be filtered can be readily determined. For example, if the fluid is water with a pH
varying from 6.9 to 7.1, the isoelectric point of the inorganic material should be higher than 7.1. For commercial filters, a higher isoelectric point may be required.
For example, one test protocol of the EPA requires washing the filter with water having a pH of 9Ø The filter media disclosed in the EXAMPLES section below do not lose microorganisms under these conditions.
The term "particles" as used herein can refer to particles of any shape, as well as short pieces of strands or fibers, hollow or porous particles, etc. The term "fluid"
includes aqueous fluids such as water, or gases and mixtures of gases.
One method of making the filter medium is by mixing and heating particles of activated carbon, particles of inorganic material, and particles of binder in a mold of the desired shape, then compressing the mixture to encourage binding and to adjust the pore size. An illustrative range of compression is between about 1 percent to 482.116A
about 30 percent reduction of the volume of the filter medium. This method is described in more particularity in the EXAMPLES section below, but is presented briefly here to provide a context for the following description.
The pore size of the filter medium is important, as it is desirable to place the microorganism in close proximity to the adsorbent surface of the filter medium. In general, the smaller the pore size, the more readily the microorganisms become adsorbed to the surface of the filter medium. This is because as pore size decreases, the microorganisms come into closer proximity to the adsorptive surface as they pass with the fluid through the pores of the filter medium. The pore size can be made small enough to physically filter out more oocysts (e.g., cryptosporidium) and cysts (e.g., Giardia muris and Giardia lamblia) than required by the EPA standards discussed above. An exemplary range of mean pore sizes is 0.01 to 10 microns.
In one embodiment, the mean pore size of the filter medium is within the range 0.1 to I
microns.
The term "low melt index binder" preferably refers to binders that have very low to virtually no melt index (melt flow rate), meaning that when heated the binders will become tacky at elevated temperatures without becoming sufficiently liquid to significantly wet the surfaces of the carbon particles and the particles of inorganic material, i.e., will not flow. The use of a low melt index binder in the present invention maximizes the effectiveness of the inorganic material. Because the binder becomes tacky rather than fluid, the activated carbon and inorganic material adhere to the surface of the binder rather than becoming encased in the binder during formation of the filter medium into its final shape. This maximizes the exposed surface area of the activated carbon and inorganic material, and thus their effectiveness.
482.116A
The pore size of the filter medium is important, as it is desirable to place the microorganism in close proximity to the adsorbent surface of the filter medium. In general, the smaller the pore size, the more readily the microorganisms become adsorbed to the surface of the filter medium. This is because as pore size decreases, the microorganisms come into closer proximity to the adsorptive surface as they pass with the fluid through the pores of the filter medium. The pore size can be made small enough to physically filter out more oocysts (e.g., cryptosporidium) and cysts (e.g., Giardia muris and Giardia lamblia) than required by the EPA standards discussed above. An exemplary range of mean pore sizes is 0.01 to 10 microns.
In one embodiment, the mean pore size of the filter medium is within the range 0.1 to I
microns.
The term "low melt index binder" preferably refers to binders that have very low to virtually no melt index (melt flow rate), meaning that when heated the binders will become tacky at elevated temperatures without becoming sufficiently liquid to significantly wet the surfaces of the carbon particles and the particles of inorganic material, i.e., will not flow. The use of a low melt index binder in the present invention maximizes the effectiveness of the inorganic material. Because the binder becomes tacky rather than fluid, the activated carbon and inorganic material adhere to the surface of the binder rather than becoming encased in the binder during formation of the filter medium into its final shape. This maximizes the exposed surface area of the activated carbon and inorganic material, and thus their effectiveness.
482.116A
The melt flow rate or melt index is determined by ASTM D1238 or DIN
53735 at 190 degrees C. and 15 kilograms. The amount of material that flows through the die should be less than about I gram/I 0 minutes, in one embodiment is less than 0.5 grams/10 minutes and in another embodiment is less than 0.1 gram/10 minutes. The most preferred binder is an ultra high molecular weight, high density polyethylene. The high molecular weight gives rise to the restricted flow properties of the melted material which is so important to this aspect of the invention.
The following table shows a comparison of selected properties of the ultra high molecular weight, high density polyethylene with other types of polyethylene binders.
Table 1 - Binders for carbon blocks Melt Temp. C Melt index* Extrudable LDPEa 102-110 5-70 yes HDPE b 134 10.5 no VHMWPEc 135 1.8 no UHMWPEd 135 <0.1 no The melt index of a material is measured at 190 C with a 15 Kg weight and the units are in grams/10 minutes.
a) Low Density Polyethylene a) High Density Polyethylene c) Very High Molecular Weight Polyethylene (VHMW PE) d) Ultra High Molecular Weight Polyethylene (UHMW PE) One ultra high molecular weight, high density polyethylene has a density of 0.930 grams per cubic centimeter and a melt index of less than 0.1 grams per ten minutes as determined by ASTM D1238 at 190/15. It has a vicat softening point of approximately 80 degrees centigrade and a crystalline melting point of about degrees C. (The Vicat softening point, measured by ASTM D 1525 (ISO 306) procedures, is the temperature at which a flattened needle of 1 mm2 cross section, and under a specified constant load, penetrates a specimen of the plastic to a depth of I
mm. It is useful as a rough comparative guide to a resin's resistance to elevated 482.116A
53735 at 190 degrees C. and 15 kilograms. The amount of material that flows through the die should be less than about I gram/I 0 minutes, in one embodiment is less than 0.5 grams/10 minutes and in another embodiment is less than 0.1 gram/10 minutes. The most preferred binder is an ultra high molecular weight, high density polyethylene. The high molecular weight gives rise to the restricted flow properties of the melted material which is so important to this aspect of the invention.
The following table shows a comparison of selected properties of the ultra high molecular weight, high density polyethylene with other types of polyethylene binders.
Table 1 - Binders for carbon blocks Melt Temp. C Melt index* Extrudable LDPEa 102-110 5-70 yes HDPE b 134 10.5 no VHMWPEc 135 1.8 no UHMWPEd 135 <0.1 no The melt index of a material is measured at 190 C with a 15 Kg weight and the units are in grams/10 minutes.
a) Low Density Polyethylene a) High Density Polyethylene c) Very High Molecular Weight Polyethylene (VHMW PE) d) Ultra High Molecular Weight Polyethylene (UHMW PE) One ultra high molecular weight, high density polyethylene has a density of 0.930 grams per cubic centimeter and a melt index of less than 0.1 grams per ten minutes as determined by ASTM D1238 at 190/15. It has a vicat softening point of approximately 80 degrees centigrade and a crystalline melting point of about degrees C. (The Vicat softening point, measured by ASTM D 1525 (ISO 306) procedures, is the temperature at which a flattened needle of 1 mm2 cross section, and under a specified constant load, penetrates a specimen of the plastic to a depth of I
mm. It is useful as a rough comparative guide to a resin's resistance to elevated 482.116A
temperatures.) Another ultra high molecular weight, high density polyethylene has a density of 0.935 grams per cubic centimeter and a melt index of less than 0.1 grams per ten minutes as determined by DIN 53735 at 190/15. It has a vicat softening point of approximately 74 degrees centigrade and a crystalline melting range of 135 to 138 degrees C. Such polyethylenes have a molecular weight higher than 4 million, and typically from about 4 to about 6 million.
The temperature at which the binder used becomes sufficiently tacky to adhere to the carbon particles may vary depending on the specific polymer used. With the high molecular weight, high density polyethylene, the binder and carbon particles can be processed at a temperature of from about 175 degrees C. to about 205 degrees C.
for about 2 hours.
The percentage of binder used to bind the activated carbon and inorganic material can be in the range of about 10 to about 40 weight percent, in another embodiment in the range of about 20 to about 35 weight percent, and in yet another embodiment about 25 to about 30 percent by weight based on the total weight of the filter medium. These ranges provide enough binder to hold the particles of carbon and inorganic material together, while not blocking the surface pores of the carbon particles.
The binder can be utilized in particulate or powder form so that it can be uniformly mixed and dispersed with the carbon particles. The use of polymer binders allows one to bind the particles of carbon and inorganic material together without excessively wetting the particles when melted and thereby effectively occluding much of the surface area of the particles.
An illustrative mean particle size of the binder is in the range from about 80 microns to about 140 microns. Note, however, that the mean particle size of the 482.116A
The temperature at which the binder used becomes sufficiently tacky to adhere to the carbon particles may vary depending on the specific polymer used. With the high molecular weight, high density polyethylene, the binder and carbon particles can be processed at a temperature of from about 175 degrees C. to about 205 degrees C.
for about 2 hours.
The percentage of binder used to bind the activated carbon and inorganic material can be in the range of about 10 to about 40 weight percent, in another embodiment in the range of about 20 to about 35 weight percent, and in yet another embodiment about 25 to about 30 percent by weight based on the total weight of the filter medium. These ranges provide enough binder to hold the particles of carbon and inorganic material together, while not blocking the surface pores of the carbon particles.
The binder can be utilized in particulate or powder form so that it can be uniformly mixed and dispersed with the carbon particles. The use of polymer binders allows one to bind the particles of carbon and inorganic material together without excessively wetting the particles when melted and thereby effectively occluding much of the surface area of the particles.
An illustrative mean particle size of the binder is in the range from about 80 microns to about 140 microns. Note, however, that the mean particle size of the 482.116A
binder used is not critical and can be made larger or smaller based on the desired properties of the filter medium. For example, smaller particle size can be used to make the pore size smaller with a resultant increase in contaminants captured and reduction in flow rate.
The mean particle size of the carbon used is not critical and can be made larger or smaller based on the desired properties of the filter medium. For example, smaller particle size carbon can be used to make the pore size smaller with a resultant increase in contaminants captured and reduction in flow rate.
The percentage of carbon in the filter medium can be in the range of about 30 to about 50 weight percent, in another embodimment in the range of about 37.5 to about 45 weight percent, and in another embodiment from about 40 to about 45 percent by weight based on the total weight of the filter medium.
As mentioned above, we have surprisingly found that a synergistic effect occurs when substantially insoluble inorganic materials with high isoelectric points and activated carbon are bound by a low melt index binder. This effect is clearly illustrated in Table 2 below comparing filters prepared with the same amount of magnesium hydroxide and binders of different melt indexes.
Table 2 - Removal of bacteriophage MS-2 by faucet mount filters with binders with different melt indexes (MIs) Unit ID 74-A 74-C 77-C 78-F 168-C2 171-Al Binder EVA EVA VHMW PE VHMW PE UHMW PE UHMW PE
MI 5-70 5-70 1.8 1.8 <0.1 <0.1 0 2.525 1.039 4.396 >4.697 >6.099 >6.099 30(25%) 1.358 0.245 2.412 2.869 >6.035 >6.035 60 50% 0.933 0.243 2.132 1.832 >6.054 >6.054 Da y2 0 stagnation NA NA NA NA >6.088 >6.088 90(75%) 0.939 0.228 0.609 2.983 >5.906 >5.906 120 100% 0.431 0.208 0.169 0.81 >5.937 >5.937 482.116A
The mean particle size of the carbon used is not critical and can be made larger or smaller based on the desired properties of the filter medium. For example, smaller particle size carbon can be used to make the pore size smaller with a resultant increase in contaminants captured and reduction in flow rate.
The percentage of carbon in the filter medium can be in the range of about 30 to about 50 weight percent, in another embodimment in the range of about 37.5 to about 45 weight percent, and in another embodiment from about 40 to about 45 percent by weight based on the total weight of the filter medium.
As mentioned above, we have surprisingly found that a synergistic effect occurs when substantially insoluble inorganic materials with high isoelectric points and activated carbon are bound by a low melt index binder. This effect is clearly illustrated in Table 2 below comparing filters prepared with the same amount of magnesium hydroxide and binders of different melt indexes.
Table 2 - Removal of bacteriophage MS-2 by faucet mount filters with binders with different melt indexes (MIs) Unit ID 74-A 74-C 77-C 78-F 168-C2 171-Al Binder EVA EVA VHMW PE VHMW PE UHMW PE UHMW PE
MI 5-70 5-70 1.8 1.8 <0.1 <0.1 0 2.525 1.039 4.396 >4.697 >6.099 >6.099 30(25%) 1.358 0.245 2.412 2.869 >6.035 >6.035 60 50% 0.933 0.243 2.132 1.832 >6.054 >6.054 Da y2 0 stagnation NA NA NA NA >6.088 >6.088 90(75%) 0.939 0.228 0.609 2.983 >5.906 >5.906 120 100% 0.431 0.208 0.169 0.81 >5.937 >5.937 482.116A
Illustrative inorganic materials have an isoelectric point above 7 pH, preferably above 9 pH, and ideally above 10 pH. The percentage of inorganic material in the filter medium can be in the range of about 10 to about 50 weight percent, in another embodiment in the range of about 25 to about 45 weight percent, and in yet another embodiment from about 28 to about 40 percent by weight based on the total weight of the filter medium.
The following table lists several insoluble inorganic materials that can be implemented in the filter medium of the present invention. Note that the inorganic materials can be added to the filter medium individually or in combination with each other.
Table 3 - Insoluble inorganic materials Compound Isoelectric point Magnesium hydroxide, Mg(OH)2 10.5 Magnesium oxide, MgO 12.5 Titanium dioxide, Ti02 6.6-8.9 Zirconium dioxide, Zr02 6.7-7.4 Aluminum oxide, A1203 6.8-9.2 Barium oxide, BaO 13.3 Calcium oxide, CaO 12.9 Cesium oxide, Ce203 9.8 Iron (II) oxide, FeO 11.8 Iron (III) oxide, Fe203 9.3 Zirconium oxide, Zr02 11.3 Hydroxyapatite, Ca5(HPO4)30H <6.9 Chromium oxide, Cr203 9.2 Cobalt oxide, Co304 8-9 Chrysotile asbestos, M 3Si2O5(OH)4 >7 The preferred inorganic materials are magnesium compounds with an isoelectric point above 9 pH, and more preferably above 10 pH, such as magnesium hydroxide and magnesium oxide. The most preferred material is magnesium 482.116A
The following table lists several insoluble inorganic materials that can be implemented in the filter medium of the present invention. Note that the inorganic materials can be added to the filter medium individually or in combination with each other.
Table 3 - Insoluble inorganic materials Compound Isoelectric point Magnesium hydroxide, Mg(OH)2 10.5 Magnesium oxide, MgO 12.5 Titanium dioxide, Ti02 6.6-8.9 Zirconium dioxide, Zr02 6.7-7.4 Aluminum oxide, A1203 6.8-9.2 Barium oxide, BaO 13.3 Calcium oxide, CaO 12.9 Cesium oxide, Ce203 9.8 Iron (II) oxide, FeO 11.8 Iron (III) oxide, Fe203 9.3 Zirconium oxide, Zr02 11.3 Hydroxyapatite, Ca5(HPO4)30H <6.9 Chromium oxide, Cr203 9.2 Cobalt oxide, Co304 8-9 Chrysotile asbestos, M 3Si2O5(OH)4 >7 The preferred inorganic materials are magnesium compounds with an isoelectric point above 9 pH, and more preferably above 10 pH, such as magnesium hydroxide and magnesium oxide. The most preferred material is magnesium 482.116A
hydroxide, as it is non-toxic to humans and exhibits superior adsorptive properties. A
preferred mean particle size for magnesium hydroxide is in the range of about 5 to about 14 microns, but again, larger or smaller particle sizes can be used.
When selecting a particle size for the inorganic material, several things should be considered. Smaller particles provide a greater surface to volume ratio, and consequently exhibit increased effectiveness at microbe removal. However, the use of smaller particle sizes results in an increased pressure drop, and consequential lower flow-through rate. On the other hand, larger particle sizes allow greater structural integrity.
It has surprisingly been found that by mixing inorganic particles of differing particle size distributions, the structural integrity of the filter medium as well as contaminant removal can be optimized. Particularly, the material with the larger particle size distribution results in a filter with greater structural integrity whereas the material with the smaller particle size distribution provides greater contaminant removal.
In generally, about 85% or more of the inorganic particles should have a mean particle size distribution that is at least twice as large as the mean particle size distribution of the remaining (15% or less) inorganic particles. In one embodiment implementing magnesium hydroxide, a first portion of the magnesium hydroxide particles have a particle size distribution of greater than about 10 m while about 5%
(+/- 2.5%) by weight of the magnesium hydroxide particles have a particle size distribution of less than about 10 m. In one example, some of the magnesium hydroxide particles have a size distribution of about 12 - 15 m, while about 5% (+/-482.116A
preferred mean particle size for magnesium hydroxide is in the range of about 5 to about 14 microns, but again, larger or smaller particle sizes can be used.
When selecting a particle size for the inorganic material, several things should be considered. Smaller particles provide a greater surface to volume ratio, and consequently exhibit increased effectiveness at microbe removal. However, the use of smaller particle sizes results in an increased pressure drop, and consequential lower flow-through rate. On the other hand, larger particle sizes allow greater structural integrity.
It has surprisingly been found that by mixing inorganic particles of differing particle size distributions, the structural integrity of the filter medium as well as contaminant removal can be optimized. Particularly, the material with the larger particle size distribution results in a filter with greater structural integrity whereas the material with the smaller particle size distribution provides greater contaminant removal.
In generally, about 85% or more of the inorganic particles should have a mean particle size distribution that is at least twice as large as the mean particle size distribution of the remaining (15% or less) inorganic particles. In one embodiment implementing magnesium hydroxide, a first portion of the magnesium hydroxide particles have a particle size distribution of greater than about 10 m while about 5%
(+/- 2.5%) by weight of the magnesium hydroxide particles have a particle size distribution of less than about 10 m. In one example, some of the magnesium hydroxide particles have a size distribution of about 12 - 15 m, while about 5% (+/-482.116A
2.5%) by weight of the magnesium hydroxide particles have a particle size distribution of about 4-5 m.
The following table illustrates how varying the concentration of magnesium hydroxide in the filter medium affects the microorganism-removing capacity of the filter medium. This experiment used carbon blocks tested with faucet mount system at 60 PSI. As shown, even small amounts of magnesium hydroxide remove microorganisms. Increasing the amount of magnesium hydroxide in the filter medium improves its microorganism-removing properties. Note also that the log reduction flattens out at about a 30 weight percent concentration of magnesium hydroxide in this particular configuration.
Table 4 - Removal of bacteriophage MS-2 by faucet mount filters with different concentrations of magnesium hydroxide 60 gal C 3.3% magnesium hydroxide 1.7 log reduction B 15% magnesium hydroxide 2.4 D 30% magnesium hydroxide 3.8 F 40% magnesium hydroxide 3.8 Control - no magnesium 0.7 hydroxide Experiments have found that amounts of inorganic material at the upper end of the range (e.g., 40-50 weight percent inorganic material) provide the longest filter life, with respect to microbe removal. Data from long-term studies show that increasing the magnesium hydroxide content to 50% by weight extends the life of the filter to beyond 4 months with greater than 4 log reduction of viruses and without a significant reduction in virus removal properties.
482.116A
The following table illustrates how varying the concentration of magnesium hydroxide in the filter medium affects the microorganism-removing capacity of the filter medium. This experiment used carbon blocks tested with faucet mount system at 60 PSI. As shown, even small amounts of magnesium hydroxide remove microorganisms. Increasing the amount of magnesium hydroxide in the filter medium improves its microorganism-removing properties. Note also that the log reduction flattens out at about a 30 weight percent concentration of magnesium hydroxide in this particular configuration.
Table 4 - Removal of bacteriophage MS-2 by faucet mount filters with different concentrations of magnesium hydroxide 60 gal C 3.3% magnesium hydroxide 1.7 log reduction B 15% magnesium hydroxide 2.4 D 30% magnesium hydroxide 3.8 F 40% magnesium hydroxide 3.8 Control - no magnesium 0.7 hydroxide Experiments have found that amounts of inorganic material at the upper end of the range (e.g., 40-50 weight percent inorganic material) provide the longest filter life, with respect to microbe removal. Data from long-term studies show that increasing the magnesium hydroxide content to 50% by weight extends the life of the filter to beyond 4 months with greater than 4 log reduction of viruses and without a significant reduction in virus removal properties.
482.116A
Figure 1 is a chart 100 showing how varying the concentration of magnesium hydroxide in the filter medium affects the microorganism-removing capacity of the filter. This experiment used carbon blocks tested with faucet mount system at 60 PSI.
The influent liquid was water containing a 4.3 log (lx 1043 PFU/ml) concentration of MS-2, where PFU = Plaque Forming Units. PFUs represent an estimate of the concentration of a bacteriophage solution, determined by mixing the bacteriophage with a solution of susceptible bacteria, plating, incubating, and counting the number of plaques present on the bacterial lawn, with each plaque representing a viable bacteriophage. For example, if a phage stock solution has 1010 PFU/ml, it means that every ml of this stock has 1010 phage particles which can form plaques.
As shown in Figure 1, at 20 weight percent magnesium hydroxide and above, a 6 log reduction of MS-2 is still achieved after 120 gallons of contaminated water introduced to the filter. For filters with no magnesium hydroxide and 10 weight percent magnesium hydroxide, the effectiveness of the filter medium is inversely proportional to the volume of water filtered.
Table 4 (below) shows a relative comparison of the microorganism-removing capabilities of materials having different isoelectric points. As shown, the materials with higher isoelectric points removed significantly more MS-2 than materials with lower isoelectric points. The experiment was conducted by swirling the given amounts of the compounds in water spiked with approximately 9.0 x 105 PFU/ml of bacteriophage MS-2 for 5 minutes then filtered through a 0.45 micron syringe filter, previously treated with 5 ml of 1.5% beef extract solution (pH 7.2, 0.05 M
glycine).
482.116A
The influent liquid was water containing a 4.3 log (lx 1043 PFU/ml) concentration of MS-2, where PFU = Plaque Forming Units. PFUs represent an estimate of the concentration of a bacteriophage solution, determined by mixing the bacteriophage with a solution of susceptible bacteria, plating, incubating, and counting the number of plaques present on the bacterial lawn, with each plaque representing a viable bacteriophage. For example, if a phage stock solution has 1010 PFU/ml, it means that every ml of this stock has 1010 phage particles which can form plaques.
As shown in Figure 1, at 20 weight percent magnesium hydroxide and above, a 6 log reduction of MS-2 is still achieved after 120 gallons of contaminated water introduced to the filter. For filters with no magnesium hydroxide and 10 weight percent magnesium hydroxide, the effectiveness of the filter medium is inversely proportional to the volume of water filtered.
Table 4 (below) shows a relative comparison of the microorganism-removing capabilities of materials having different isoelectric points. As shown, the materials with higher isoelectric points removed significantly more MS-2 than materials with lower isoelectric points. The experiment was conducted by swirling the given amounts of the compounds in water spiked with approximately 9.0 x 105 PFU/ml of bacteriophage MS-2 for 5 minutes then filtered through a 0.45 micron syringe filter, previously treated with 5 ml of 1.5% beef extract solution (pH 7.2, 0.05 M
glycine).
482.116A
Table 5 - Isoelectric point and MS-2 removal Mineral (grams tested) Isoelectric point (pH) Removal (Log reduction) Mg(OH)2 (2.0) 10.5 4.9 Magnesium silicate (5.0) -3 2.7 M (2.0 12.5 3.68 MgCO3 (Magnetite) 5.5 N/A*
A1203 (2.0) 9.4 2.71 AlO(OH) (Boehemite) (5.0) 9.7 4.67 A12Si2O5 OH 4 (Kaolinite) 1.5-3.5 N/A
a-Fe203 (hematite) 7.5 N/A
FeO(OH) (2.0) N/A 2.49 Cr2O3 9.2 N/A
Sn02 4.5 N/A
(CaF)Ca4(PO4)3 (Apatite) (5.5) 4-6 3.08 TiO2 (2.1 6.6-8.9 0.96 TiO(OH) (2.0) N/A 1.93 ZrO2 11.3 N/A
Sepiolite (2.0) N/A 2.22 Saponite (2.0) N/A 0.125 * Indicates data not gathered.
The following table shows the results of a batch study comparing the effectiveness of magnesium hydroxide to that of magnesium silicate. The experiment was conducted using 20 ml of water that was contaminated with MS-2 bacteriophage.
1, 3, or 5 grams of the material was added (as indicated below) to the contaminated water. The mixture was then mixed and the magnesium compound and filtered off to determine how much virus the material removed. As shown, magnesium hydroxide works significantly better than magnesium silicate, primarily because magnesium hydroxide has a higher isoelectric point and superior adsorptive properties.
Table 6 - Removal of bacteriophage MS-2 by powdered magnesium silicate and magnesium hydroxide MS-2 log 10 removal I magnesium silicate 2.0 5 magnesium silicate 2.7 1 magnesium hydroxide 2.9 3 magnesium hydroxide 3.8 5 g magnesium hydroxide 4.4 482.116A
A1203 (2.0) 9.4 2.71 AlO(OH) (Boehemite) (5.0) 9.7 4.67 A12Si2O5 OH 4 (Kaolinite) 1.5-3.5 N/A
a-Fe203 (hematite) 7.5 N/A
FeO(OH) (2.0) N/A 2.49 Cr2O3 9.2 N/A
Sn02 4.5 N/A
(CaF)Ca4(PO4)3 (Apatite) (5.5) 4-6 3.08 TiO2 (2.1 6.6-8.9 0.96 TiO(OH) (2.0) N/A 1.93 ZrO2 11.3 N/A
Sepiolite (2.0) N/A 2.22 Saponite (2.0) N/A 0.125 * Indicates data not gathered.
The following table shows the results of a batch study comparing the effectiveness of magnesium hydroxide to that of magnesium silicate. The experiment was conducted using 20 ml of water that was contaminated with MS-2 bacteriophage.
1, 3, or 5 grams of the material was added (as indicated below) to the contaminated water. The mixture was then mixed and the magnesium compound and filtered off to determine how much virus the material removed. As shown, magnesium hydroxide works significantly better than magnesium silicate, primarily because magnesium hydroxide has a higher isoelectric point and superior adsorptive properties.
Table 6 - Removal of bacteriophage MS-2 by powdered magnesium silicate and magnesium hydroxide MS-2 log 10 removal I magnesium silicate 2.0 5 magnesium silicate 2.7 1 magnesium hydroxide 2.9 3 magnesium hydroxide 3.8 5 g magnesium hydroxide 4.4 482.116A
As mentioned above, magnesium oxide can also be used. Magnesium oxide hydrates in the presence of water, forming a magnesium hydroxide surface layer.
However, starting with magnesium hydroxide as the adsorptive material results in better performance, in part because of the length of time for magnesium oxide to completely hydrate, and also because magnesium oxide is slightly soluble in water and so can wash out of the filter.
Additional materials having high isoelectric points include titanium dioxide, iron oxides, aluminum oxides, barium oxides, calcium phosphate and alumina-coated silica. Other magnesium-containing minerals include: antigorite, clinochrysotile, lizardite, orthochrysotile and parachrysotile, clinochore, hectabrite, vermiculite, ripidolite, saponite, and sepiolite.
The filter medium can be created in virtually any desired shape. Figure 2 illustrates a block 200 of the filter medium in cylindrical form, and which is particularly adapted to faucet mount systems such as the system found in U.S.
Patent No. 6,123,837 to Wadsworth et al. and to pitcher systems such as the system found in U.S. Patent No. Des. 398,184 to Silverberg et al., each of which are herein incorporated by reference. A standard-sized cylindrical filter block for point-of-use systems is about 4 inches in length or less between the ends 202, 204 of the block 200, and has an outer diameter (OD) of less than about 4 inches and an inner diameter (ID) of less than about one inch. One embodiment is less than about 3 inches in length and has an outer diameter of less than about 2.5 inches and an inner diameter of less than about 0.5 inch.
Figure 3 illustrates the filter medium in the form of a sheet 300. The sheet can then be placed in a housing and a fluid such as water passed therethrough.
482.116A
However, starting with magnesium hydroxide as the adsorptive material results in better performance, in part because of the length of time for magnesium oxide to completely hydrate, and also because magnesium oxide is slightly soluble in water and so can wash out of the filter.
Additional materials having high isoelectric points include titanium dioxide, iron oxides, aluminum oxides, barium oxides, calcium phosphate and alumina-coated silica. Other magnesium-containing minerals include: antigorite, clinochrysotile, lizardite, orthochrysotile and parachrysotile, clinochore, hectabrite, vermiculite, ripidolite, saponite, and sepiolite.
The filter medium can be created in virtually any desired shape. Figure 2 illustrates a block 200 of the filter medium in cylindrical form, and which is particularly adapted to faucet mount systems such as the system found in U.S.
Patent No. 6,123,837 to Wadsworth et al. and to pitcher systems such as the system found in U.S. Patent No. Des. 398,184 to Silverberg et al., each of which are herein incorporated by reference. A standard-sized cylindrical filter block for point-of-use systems is about 4 inches in length or less between the ends 202, 204 of the block 200, and has an outer diameter (OD) of less than about 4 inches and an inner diameter (ID) of less than about one inch. One embodiment is less than about 3 inches in length and has an outer diameter of less than about 2.5 inches and an inner diameter of less than about 0.5 inch.
Figure 3 illustrates the filter medium in the form of a sheet 300. The sheet can then be placed in a housing and a fluid such as water passed therethrough.
482.116A
The filter medium can be used in a wide variety of applications. As mentioned above, one use to which it is particularly adaptable is for pressurized and gravity-flow applications such as faucet-mount filters and pitcher filters, as well as in water dispensers (e.g., standalone water coolers), such as the type having a bottle receiving portion for receiving a bottle of water, a filtration portion for filtering water received from the bottle, and a filtered water outlet (e.g., spigot). Other applications are use in granular filters, high volume "under-the-sink" or commercial-type filters, and refrigerator filters. Yet another application is use in air filtration systems.
The filter medium can also be made for/used in portable applications, such as for use in filters for camping, bottles with filters, emergency kits, etc. The filter medium is also useful in med-evac systems, allowing filtration of water in the field to rehydrate soldiers. In portable uses, the filter medium can be formed in a block smaller than the cylindrical block disclosed above for 5, 15, 30 gallons, etc.
The filter medium would also be particularly effective at purifying water contaminated by an act of bio-terrorism. For example, the faucet-mount system could allow users to continue to use a contaminated public water supply until fresh water were made available. Similarly, portable versions (pitchers, bottles, bags, etc. with the filter medium attached) can be stored in homes and businesses, stored in emergency kits, carried in automobiles, etc. Further, such portable versions can be made available and/or distributed to people rather quickly in response to a bio-terrorism attack.
A hand-pump, foot-pump, battery-pump, solar-powered pump, etc. may be coupled to any of the embodiments described herein to pressurize the influent water and/or reduce pressure in the effluent stream to draw water through the filter medium.
EXAMPLES
482.116A
The filter medium can also be made for/used in portable applications, such as for use in filters for camping, bottles with filters, emergency kits, etc. The filter medium is also useful in med-evac systems, allowing filtration of water in the field to rehydrate soldiers. In portable uses, the filter medium can be formed in a block smaller than the cylindrical block disclosed above for 5, 15, 30 gallons, etc.
The filter medium would also be particularly effective at purifying water contaminated by an act of bio-terrorism. For example, the faucet-mount system could allow users to continue to use a contaminated public water supply until fresh water were made available. Similarly, portable versions (pitchers, bottles, bags, etc. with the filter medium attached) can be stored in homes and businesses, stored in emergency kits, carried in automobiles, etc. Further, such portable versions can be made available and/or distributed to people rather quickly in response to a bio-terrorism attack.
A hand-pump, foot-pump, battery-pump, solar-powered pump, etc. may be coupled to any of the embodiments described herein to pressurize the influent water and/or reduce pressure in the effluent stream to draw water through the filter medium.
EXAMPLES
482.116A
Example I
Following is an example of a preferred procedure for forming a porous block of filter medium. Granular activated carbon with a mean particle size (outer diameter) of about 100 microns is mixed with particles of an ultra high molecular weight polyethylene binder (and/or other binder) having a mean particle size in the range of about 120 to 140 microns, a melt index of less than 1, and a melting temperature of about 135 C. Particles of magnesium hydroxide (and/or other inorganic material) are blended into the mixture of carbon and binder. The preferred particle size of the magnesium hydroxide is in the range of about 5 to about 14 microns. See Table 6 and Figure 5 for illustrative compositions of the mixture. The mixture of magnesium hydroxide, carbon, and binder are thoroughly mixed in a blender or other suitable mixing device for a period of time sufficient to create a substantially uniform dispersion of materials in the mixture. The blended mixture is heated and compressed in a stainless steel mold having the desired shape. The material in the mold is heated to about 473 degrees F (245 C.) for about 40 minutes. The heating makes the binder sticky so that it binds the magnesium hydroxide and carbon particles into a porous block. The magnesium hydroxide may also adhere to the carbon.
Formation of the filter medium by extrusion is also possible, though is not desirable for the preferred embodiments as the preferred materials require higher heating temperatures, which require a longer extruder heating zone resulting in a very high backpressure on the extruded block. As a result, these extruded blocks have high pressure drops and low flow-through rates.
Example 2 Following is an example of a preferred procedure for forming a porous cylindrically-shaped block of filter medium. Particles of magnesium hydroxide, 482.116A
Following is an example of a preferred procedure for forming a porous block of filter medium. Granular activated carbon with a mean particle size (outer diameter) of about 100 microns is mixed with particles of an ultra high molecular weight polyethylene binder (and/or other binder) having a mean particle size in the range of about 120 to 140 microns, a melt index of less than 1, and a melting temperature of about 135 C. Particles of magnesium hydroxide (and/or other inorganic material) are blended into the mixture of carbon and binder. The preferred particle size of the magnesium hydroxide is in the range of about 5 to about 14 microns. See Table 6 and Figure 5 for illustrative compositions of the mixture. The mixture of magnesium hydroxide, carbon, and binder are thoroughly mixed in a blender or other suitable mixing device for a period of time sufficient to create a substantially uniform dispersion of materials in the mixture. The blended mixture is heated and compressed in a stainless steel mold having the desired shape. The material in the mold is heated to about 473 degrees F (245 C.) for about 40 minutes. The heating makes the binder sticky so that it binds the magnesium hydroxide and carbon particles into a porous block. The magnesium hydroxide may also adhere to the carbon.
Formation of the filter medium by extrusion is also possible, though is not desirable for the preferred embodiments as the preferred materials require higher heating temperatures, which require a longer extruder heating zone resulting in a very high backpressure on the extruded block. As a result, these extruded blocks have high pressure drops and low flow-through rates.
Example 2 Following is an example of a preferred procedure for forming a porous cylindrically-shaped block of filter medium. Particles of magnesium hydroxide, 482.116A
activated carbon, and binder are blended into a mixture. The blended mixture is heated and compressed in a stainless steel mold having the desired shape. The material in the mold is heated to about 473 degrees F (245 C.) for about 40 minutes.
The ends of the block can be capped using any suitable adhesive, such as polymeric glue. The block can then be placed in a housing that directs influent water to an outer periphery of the block so that the water passes through the block into the center chamber of the block and is then expelled through one of the end caps as filtered water. Note that the flow through the filter may also be reversed.
Figure 4 is a chart 400 showing the reduction of microorganisms using a filter medium such as the one described in Example 2 with about 30 weight percent magnesium hydroxide, about 25 weight percent ultra high molecular weight polyethylene binder, and about 45 weight percent activated carbon and about a pressure drop of 5.2 atm across the filter medium. As shown, a greater than 4 log reduction of PRD-1 and MS-2 (representing rotavirus and poliovirus, respectively) is achievable for 120+ gallons of water. A greater than 7 log reduction of Klebsiella Terregina (representing bacteria) is also achievable for 120+ gallons.
Examples 3-5 The following table illustrates the results of experiments testing the removal of bacteriophage MS-2 by cylindrical filters with different concentrations of carbon, binder and magnesium hydroxide. The influent liquid for the 30 and 90 gallon runs was water containing a 4.3 log (1x1043 PFU/ml) concentration of MS-2, where PFU =
Plaque Forming Units. The influent liquid for the 120 gallon runs was water containing a 4.5 log (1x1045 PFU/ml) concentration of MS-2. The filter blocks themselves were about 75 g carbon blocks of the composition shown with dimensions 482.116A
The ends of the block can be capped using any suitable adhesive, such as polymeric glue. The block can then be placed in a housing that directs influent water to an outer periphery of the block so that the water passes through the block into the center chamber of the block and is then expelled through one of the end caps as filtered water. Note that the flow through the filter may also be reversed.
Figure 4 is a chart 400 showing the reduction of microorganisms using a filter medium such as the one described in Example 2 with about 30 weight percent magnesium hydroxide, about 25 weight percent ultra high molecular weight polyethylene binder, and about 45 weight percent activated carbon and about a pressure drop of 5.2 atm across the filter medium. As shown, a greater than 4 log reduction of PRD-1 and MS-2 (representing rotavirus and poliovirus, respectively) is achievable for 120+ gallons of water. A greater than 7 log reduction of Klebsiella Terregina (representing bacteria) is also achievable for 120+ gallons.
Examples 3-5 The following table illustrates the results of experiments testing the removal of bacteriophage MS-2 by cylindrical filters with different concentrations of carbon, binder and magnesium hydroxide. The influent liquid for the 30 and 90 gallon runs was water containing a 4.3 log (1x1043 PFU/ml) concentration of MS-2, where PFU =
Plaque Forming Units. The influent liquid for the 120 gallon runs was water containing a 4.5 log (1x1045 PFU/ml) concentration of MS-2. The filter blocks themselves were about 75 g carbon blocks of the composition shown with dimensions 482.116A
of about 2.94 inches in length, about 1.84 inch outer diameter and about 0.5 inch inner diameter tested on a faucet mount system at 60 PSI.
Table 7 - Removal of bacteriophage MS-2 by cylindrical filters with different concentrations of magnesium hydroxide MS-2 log 10 removal 30 gal 90 gal 120 gal A 37.5% magnesium > 4.3 > 4.3 > 4.5 hydroxide 37.5% Activated Carbon 25% Binder B 30% magnesium hydroxide > 4.3 > 4.3 > 4.5 45% Activated Carbon 25% Binder C 28% magnesium hydroxide > 4.3 > 4.3 > 4.5 42% Activated Carbon 30% Binder Control - no magnesium 1.4 0.2 0.1 hydroxide Examples 6-12 Figure 5 is a table 500 showing the results of seven experiments testing the removal of bacteriophage MS-2 by cylindrical filters with varying concentrations of carbon, binder and magnesium hydroxide. The influent liquid was water containing a 4.755 log (1x104755 PFU/ml) concentration of MS-2, where PFU = Plaque Forming Units. The filter blocks themselves were about 75 g carbon blocks of the composition and compression shown with dimensions of about 2.94 inches in length, about 1.84 inch outer diameter and about 0.5 inch inner diameter tested on a faucet mount system.
One particular parameter of interest is the concentration of inorganic cation (of high isoelectric point) times the pressure drop. As shown in Figure 5, the performance of the filters depends on the amount of Mg and the flow rate (or pressure drop) of the filter. The pressure drop shown in Figure 5 is measured in pounds per 482.116A
Table 7 - Removal of bacteriophage MS-2 by cylindrical filters with different concentrations of magnesium hydroxide MS-2 log 10 removal 30 gal 90 gal 120 gal A 37.5% magnesium > 4.3 > 4.3 > 4.5 hydroxide 37.5% Activated Carbon 25% Binder B 30% magnesium hydroxide > 4.3 > 4.3 > 4.5 45% Activated Carbon 25% Binder C 28% magnesium hydroxide > 4.3 > 4.3 > 4.5 42% Activated Carbon 30% Binder Control - no magnesium 1.4 0.2 0.1 hydroxide Examples 6-12 Figure 5 is a table 500 showing the results of seven experiments testing the removal of bacteriophage MS-2 by cylindrical filters with varying concentrations of carbon, binder and magnesium hydroxide. The influent liquid was water containing a 4.755 log (1x104755 PFU/ml) concentration of MS-2, where PFU = Plaque Forming Units. The filter blocks themselves were about 75 g carbon blocks of the composition and compression shown with dimensions of about 2.94 inches in length, about 1.84 inch outer diameter and about 0.5 inch inner diameter tested on a faucet mount system.
One particular parameter of interest is the concentration of inorganic cation (of high isoelectric point) times the pressure drop. As shown in Figure 5, the performance of the filters depends on the amount of Mg and the flow rate (or pressure drop) of the filter. The pressure drop shown in Figure 5 is measured in pounds per 482.116A
square inch (psi). The inorganic cation is calculated as the percentage of Mg(OH)2 in the filter times the ratio of Mg to Mg(OH)2. A sample calculation for Filter A
follows:
[0.375 g Mg(OH)2 / g filter] x [0.417 g Mg / g Mg(OH)2] x [4.15 lb/in2]
= 0.649 [g Mg = lb] / [g filter = in2] Equation I
The pressure drop measurements can be taken by measuring the resistance of air flow through the filter at a given pressure, and more particularly, by measuring the differential pressure of air flow through the filter with the tared pressure being the pressure of the air flow without a filter.
As described herein, the filter medium meets EPA standards for viruses (4 log reduction (99.99%) required for viruses). In fact, the filter medium can achieve near 100% microorganism removal at over 120 gallons. In comparative experimentation, the filter disclosed in International Patent Application WO 02/076577 to Hughes was only effective up to about 1.33 gallons; at 30 gallons, very poor results were obtained.
Thus, the virus-removing properties of the filter medium disclosed herein can process nearly 100 times the volume, and thus may have almost 100 times the life, as other systems.
Using inorganic materials with high isoelectric points such as magnesium hydroxide is instrumental in the removal of the microorganisms from water, but does not effectively kill the trapped organisms. In other words, the microbes remain viable on the surface of the filter medium. If the filter is used infrequently, or for an extended time period, the trapped microorganisms may form a biofilm over the active 482.116A
follows:
[0.375 g Mg(OH)2 / g filter] x [0.417 g Mg / g Mg(OH)2] x [4.15 lb/in2]
= 0.649 [g Mg = lb] / [g filter = in2] Equation I
The pressure drop measurements can be taken by measuring the resistance of air flow through the filter at a given pressure, and more particularly, by measuring the differential pressure of air flow through the filter with the tared pressure being the pressure of the air flow without a filter.
As described herein, the filter medium meets EPA standards for viruses (4 log reduction (99.99%) required for viruses). In fact, the filter medium can achieve near 100% microorganism removal at over 120 gallons. In comparative experimentation, the filter disclosed in International Patent Application WO 02/076577 to Hughes was only effective up to about 1.33 gallons; at 30 gallons, very poor results were obtained.
Thus, the virus-removing properties of the filter medium disclosed herein can process nearly 100 times the volume, and thus may have almost 100 times the life, as other systems.
Using inorganic materials with high isoelectric points such as magnesium hydroxide is instrumental in the removal of the microorganisms from water, but does not effectively kill the trapped organisms. In other words, the microbes remain viable on the surface of the filter medium. If the filter is used infrequently, or for an extended time period, the trapped microorganisms may form a biofilm over the active 482.116A
filter surfaces, reducing the performance of the filter over time by covering up the active sites. To further improve the antimicrobial effectiveness of the filter, and to extend the life of the filter, an antimicrobial material can be incorporated into the filter to prevent biofilm growth. The use of a biocidal material in combination with the high isoelectric point material provides a trap-and-kill mechanism for microorganism removal.
Illustrative antimicrobial materials are silver-containing materials. One type of silver-containing material implements soluble silver material to kill microbes by entering the water surrounding the filter medium via ion exchange.
An effective amount of the silver-containing material is mixed with the other materials and formed into the filter media as described above. In general, the silver-containing material is added at about 1-10% by weight based on the total weight of all materials. Experimentation has shown that the addition of about 1.5-5.0% by weight of silver-impregnated zirconium phosphate significantly extends the life of the filter.
An illustrative mean particle size of the silver-containing material is between about 1 m-200 m or larger, and in another embodiment is between about 75 m-I00 m. Note that the particle size is not as critical here, as the overall mass of silver-containing material present is the important parameter.
Another type of silver-containing material kills microorganisms on contact but does not elute or leach into solution. Particularly useful are materials comprising a polymeric matrix impregnated with a water-insoluble antimicrobial compound such as a silver halide (e.g., silver iodide or silver chloride). Illustrative polymeric materials are positively charged polymers containing quaternary ammonium compounds. The silver is transferred directly to a microorganism contacting the material, causing a toxic accumulation that results in cell death. These materials provide sustained 482.116A
Illustrative antimicrobial materials are silver-containing materials. One type of silver-containing material implements soluble silver material to kill microbes by entering the water surrounding the filter medium via ion exchange.
An effective amount of the silver-containing material is mixed with the other materials and formed into the filter media as described above. In general, the silver-containing material is added at about 1-10% by weight based on the total weight of all materials. Experimentation has shown that the addition of about 1.5-5.0% by weight of silver-impregnated zirconium phosphate significantly extends the life of the filter.
An illustrative mean particle size of the silver-containing material is between about 1 m-200 m or larger, and in another embodiment is between about 75 m-I00 m. Note that the particle size is not as critical here, as the overall mass of silver-containing material present is the important parameter.
Another type of silver-containing material kills microorganisms on contact but does not elute or leach into solution. Particularly useful are materials comprising a polymeric matrix impregnated with a water-insoluble antimicrobial compound such as a silver halide (e.g., silver iodide or silver chloride). Illustrative polymeric materials are positively charged polymers containing quaternary ammonium compounds. The silver is transferred directly to a microorganism contacting the material, causing a toxic accumulation that results in cell death. These materials provide sustained 482.116A
antimicrobial action in spite of frequent washing. One such material is SURFACINE, available from Lonza Inc., 17-17 Route 208, Fair Lawn, NJ 07410.
An effective amount of particles coated with the non-eluting silver-containing material is mixed with the other materials and formed into the filter medium as described above. Note that the substrate carrying the non-eluting silver-containing material can be the activated carbon particles. In general, the non-eluting silver-containing material is added at about 0.1-10% by weight based on the total weight of all materials in the filter medium.
While various embodiments have been described above, it should be understood that they have been presented by way of example only, and not limitation.
Thus, the breadth and scope of a preferred embodiment should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.
482.116A
An effective amount of particles coated with the non-eluting silver-containing material is mixed with the other materials and formed into the filter medium as described above. Note that the substrate carrying the non-eluting silver-containing material can be the activated carbon particles. In general, the non-eluting silver-containing material is added at about 0.1-10% by weight based on the total weight of all materials in the filter medium.
While various embodiments have been described above, it should be understood that they have been presented by way of example only, and not limitation.
Thus, the breadth and scope of a preferred embodiment should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.
482.116A
Claims (50)
1. Filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material; wherein the insoluable inorganic material is admixed together with the particles of activated carbon; and wherein a first portion of the particles of inorganic material have a first mean particle size distribution and a second portion of the particles of inorganic material have a second mean particle size distribution, the first mean particle size distribution being larger than the second mean particle size distribution, and wherein the filter medium is formed in a block or sheet and wherein the binder has a melt index of less than 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load.
2. A filter medium as recited in claim 1, wherein the inorganic material is a magnesium containing material.
3. A filter medium as recited in claim 2, wherein the inorganic material is magnesium hydroxide.
4. A filter medium as recited in claim 1, wherein the inorganic material has an isoelectric point greater than a pH of 9.
5. A filter medium as recited in claim 1, wherein the inorganic material has an isoelectric point greater than a pH of 10.
6. A filter medium as recited in claim 1, wherein the inorganic material is present in an amount between 25 weight percent to 45 weight percent of the total weight of the filter medium.
7. A filter medium as recited in claim 1, wherein the binder is an ultra high molecular weight polymer having a molecular weight greater than 4 million.
8. A filter medium as recited in claim 1, wherein the binder is ultra high molecular weight polyethylene having a molecular weight of from 4 million to 6 million.
9. A filter medium as recited in claim 1, wherein the binder is present in an amount between 20 weight percent to 35 weight percent of the total weight of the filter medium.
10. A filter medium as recited in claim 1, wherein 75 grams of the filter medium performs a greater than 1 × 10 4 plaque forming units/milliliter reduction of viruses after 100 gallons of water passes through the filter medium.
11. A filter medium as recited in claim 1, wherein the filter medium is cylindrically shaped with an outer diameter of less than 4 inches and a maximum length between ends of the filter medium of less than 3 inches.
12. A filter medium as recited in claim 11, wherein the filter medium performs a greater than 1 × 10 4 plaque forming units/milliliter reduction of viruses after 100 gallons of water passes through the filter medium.
13. A filter medium as recited in claim 1, wherein a mean pore size of pores formed by the particles and binder is between 0.01 micron and 10 microns.
14. A filter medium as recited in claim 1, wherein a mean pore size of pores formed by the particles and binder is between 0.1 micron and 1 microns.
15. A filter medium as recited in claim 1, wherein the first mean particle size distribution is at least twice as large as the second mean particle size distribution.
16. A filter medium as recited in claim 1, wherein the first mean particle size distribution is greater than 10 µm, and the second mean particle size distribution is less than 10 µm.
17. A filter medium as recited in claim 1, wherein the first portions of the particles of inorganic material are present at 85% or more by weight based on a total weight of the inorganic material.
18. A filter medium as recited in claim 1, further comprising at least one additional adsorptive material other than the activated carbon and inorganic material.
19. A filter medium as recited in claim 1, wherein the fluid is water.
20. A filter medium as recited in claim 1, wherein a percentage concentration of an inorganic cation provided by the inorganic material times pressure drop through the filter medium in pounds per square inch is at least 0.5 [g Mg.lb]/[g filter.in2].
21. A method for removing microorganisms from a fluid, comprising causing the fluid to flow through the filter medium of claim 1.
22. A device for removing microorganisms from a fluid, comprising a water dispenser implementing the filter medium of claim 1.
23. A device for removing microorganisms from air, comprising the filter medium of claim 1.
24. Filter medium for use in removing microorganisms, comprising: particles of activated carbon; particles of a insoluble inorganic material having an isoelectric point greater than a pH of a fluid being filtered; a binder for binding the particles of activated carbon and particles of inorganic material; an antimicrobial material, and wherein the filter medium is formed from a block or sheet and wherein the binder has a melt index of less than 1 gram per 10 minutes as determined by ASTM D1238 at 190 degrees C. and 15 kilograms load.
25. A filter medium as recited in claim 24, wherein the inorganic material is a magnesium containing material.
26. A filter medium as recited in claim 25, wherein the inorganic material is magnesium hydroxide.
27. A filter medium as recited in claim 24, wherein the inorganic material has an isoelectric point greater than a pH of 9.
28. A filter medium as recited in claim 24, wherein the inorganic material has an isoelectric point greater than a pH of 10.
29. A filter medium as recited in claim 24, wherein the inorganic material is present in an amount between 25 weight percent to 45 weight percent of the total weight of the filter medium.
30. A filter medium as recited in claim 24, wherein the binder is an ultra high molecular weight polymer having a molecular weight greater than 4 million.
31. A filter medium as recited in claim 24, wherein the binder is ultra high molecular weight polyethylene having a molecular weight of from 4 million to 6 million.
32. A filter medium as recited in claim 24, wherein the binder is present in an amount between 20 weight percent to 35 weight percent of the total weight of the filter medium.
33. A filter medium as recited in claim 24, wherein 75 grams of the filter medium performs a greater than 1 × 10 4 plaque forming units/milliliter reduction of viruses after 100 gallons of water passes through the filter medium.
34. A filter medium as recited in claim 24, wherein the filter medium is cylindrically shaped with an outer diameter of less than 4 inches and a maximum length between ends of the filter medium of less than 3 inches.
35. A filter medium as recited in claim 34, wherein the filter medium performs a greater than 1 × 10 4 plaque forming units/milliliter reduction of viruses after 100 gallons of water passes through the filter medium.
36. A filter medium as recited in claim 24, wherein a mean pore size of pores formed by the particles and binder is between 0.01 micron and 10 microns.
37. A filter medium as recited in claim 24, wherein a mean pore size of pores formed by the particles and binder is between 0.1 micron and 1 microns.
38. A filter medium as recited in claim 24, wherein a first portion of the particles of inorganic material have a first mean particle size distribution and a second portion of the particles of inorganic material have a second mean particle size distribution, the first mean particle size distribution being larger than the second mean particle size distribution.
39. A filter medium as recited in claim 38, wherein the first mean particle size distribution is at least twice as large as the second mean particle size distribution.
40. A filter medium as recited in claim 38, wherein the first mean particle size distribution is greater than 10 µm, and the second mean particle size distribution is less than about 10 µm.
41. A filter medium as recited in claim 38, wherein the first portions of the particles of inorganic material are present at 85% or more by weight based on a total weight of the inorganic material.
42. A filter medium as recited in claim 24, wherein the antimicrobial material is a silver-containing material.
43. A filter medium as recited in claim 42, wherein the antimicrobial material is a water-soluble silver-containing material.
44. A filter medium as recited in claim 43, wherein the antimicrobial material is selected from a group consisting of silver-impregnated zeolite and silver-impregnated zirconium phosphate.
45. A filter medium as recited in claim 42, wherein the antimicrobial material is a water-insoluble silver-containing material.
46. A filter medium as recited in claim 24, wherein the antimicrobial material is a polymeric matrix impregnated with a water-insoluble antimicrobial compound.
47. A filter medium as recited in claim 24, further comprising at least one additional adsorptive material other than the activated carbon and inorganic material.
48. A filter medium as recited in claim 24, wherein the fluid is water.
49. A filter medium as recited in claim 24, wherein a percentage concentration of an inorganic cation provided by the inorganic material times pressure drop through the filter medium in pounds per square inch is at least 0.5[g Mg.lb]/[g filter.in2].
50. A method for removing microorganisms from a fluid, comprising causing the fluid to flow through the filter medium of claim 24.