CA2258996A1 - Moldable refractory composition and process for preparing the same - Google Patents
Moldable refractory composition and process for preparing the same Download PDFInfo
- Publication number
- CA2258996A1 CA2258996A1 CA002258996A CA2258996A CA2258996A1 CA 2258996 A1 CA2258996 A1 CA 2258996A1 CA 002258996 A CA002258996 A CA 002258996A CA 2258996 A CA2258996 A CA 2258996A CA 2258996 A1 CA2258996 A1 CA 2258996A1
- Authority
- CA
- Canada
- Prior art keywords
- weight
- phosphoric acid
- refractory composition
- wollastonite
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This moldable refractory composition is intended to be used in the production of cast refractory pieces resistant to molten metals, especially molten aluminum. It comprises 8 to 25% by weight of an aqueous phosphoric acid solution having a concentration of phosphoric acid ranging from 40 to 85% by weight, with up to 50% of the primary acidic function of the acid phosphoric acid neutralized by reaction with vermiculite. It also comprises from 75 to 92% by weight of a mixture containing wollastonite and an aqueous suspension containing from 20 to 40% by weight of colloidal silica. The weight ratio of the aqueous suspension to the wollastonite within the mixture ranges from 0.5 to 1.2. The composition according to the invention is particularly interesting in that it can be unmolded within a very short period of time that is less than 2 hours and can be as small as 10 minutes.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CA002258996A CA2258996C (en) | 1999-02-02 | 1999-02-02 | Moldable refractory composition and process for preparing the same |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CA002258996A CA2258996C (en) | 1999-02-02 | 1999-02-02 | Moldable refractory composition and process for preparing the same |
Publications (2)
Publication Number | Publication Date |
---|---|
CA2258996A1 true CA2258996A1 (en) | 2000-08-02 |
CA2258996C CA2258996C (en) | 2003-10-21 |
Family
ID=29256122
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CA002258996A Expired - Fee Related CA2258996C (en) | 1999-02-02 | 1999-02-02 | Moldable refractory composition and process for preparing the same |
Country Status (1)
Country | Link |
---|---|
CA (1) | CA2258996C (en) |
-
1999
- 1999-02-02 CA CA002258996A patent/CA2258996C/en not_active Expired - Fee Related
Also Published As
Publication number | Publication date |
---|---|
CA2258996C (en) | 2003-10-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2003003860A3 (en) | Stabilized compositions and processes of their preparation | |
CA2294362A1 (en) | Stainless steel powder | |
EP1686131A3 (en) | Process for preparation of penam derivatives | |
HK1043780A1 (en) | Zeolites and methods of making thereof | |
EP1099498A4 (en) | Cast steel piece and steel product excellent in forming characteristics and method for treatment of molted steel therefor and method for production thereof | |
CA2282570A1 (en) | Low water diamine/dicarboxylic acid salt preparation | |
BG106939A (en) | Method for the preparation of citalopram | |
AU1560701A (en) | Refining of metallurgical grade silicon | |
CA2258996A1 (en) | Moldable refractory composition and process for preparing the same | |
EP0400454A3 (en) | Stabilized phosphite compositions | |
WO2004094315A3 (en) | Method of producing copper hydroxosulphates and copper fungicidal compositions containing same | |
DE3269334D1 (en) | Method of manufacturing molds by using binders based on alkali metal silicate solutions | |
CA2412049A1 (en) | Process for the preparation of 5-aminosalicyclic acid | |
NZ235465A (en) | Process for preparing purine derivatives; intermediates | |
AU6296480A (en) | Process for the preparation of aluminium alloys | |
EP0476699B1 (en) | Magnesium alloy for casting and having a narrower solidification range | |
CA2389447A1 (en) | Glassware forming mold and method of manufacture | |
ZA200005110B (en) | Process for preparing intermediates. | |
WO2003032752A1 (en) | Inorganic-particle-containing additive composition, process for producing the same, and food composition containing the additive composition | |
ES8607967A1 (en) | Thiazolylacetic acid derivatives and their preparation. | |
MY121362A (en) | Benzoylguanidine derivatives with advantageous properties processes for preparing them and their use in the production of pharmaceutical compositions | |
CA2410036A1 (en) | Composition based on renewable raw materials | |
HUP0004005A2 (en) | Method for producing (+)-trans-chrysanthenum-monocarboxylic acid | |
SU1337366A1 (en) | Refractory compound for coatings | |
SU1217551A1 (en) | Method of producing silicate binder ,particularly, for making moulds and cores |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
EEER | Examination request | ||
MKLA | Lapsed |
Effective date: 20140204 |