CA2252036A1 - Chromate-free conversion layer and process for producing the same - Google Patents
Chromate-free conversion layer and process for producing the sameInfo
- Publication number
- CA2252036A1 CA2252036A1 CA002252036A CA2252036A CA2252036A1 CA 2252036 A1 CA2252036 A1 CA 2252036A1 CA 002252036 A CA002252036 A CA 002252036A CA 2252036 A CA2252036 A CA 2252036A CA 2252036 A1 CA2252036 A1 CA 2252036A1
- Authority
- CA
- Canada
- Prior art keywords
- conversion layer
- chromate
- producing
- same
- free conversion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A chromate-free, chromic and substantially coherent conversion layer based on zinc or zinc alloys offers a protection against corrosion from about 100 to 1000 h, as proven by the salt spray test of DIN 50021 SS or ASTM B 117-73 to first corrosion as described by DIN
50961, chapter 10, even when it does not contain other components such as silicate, Cer, aluminium and borate. This conversion layer is clear, transparent, substantially colourless and iridescent, is about 100 nm to 1000 nm thick, hard, adheres well and is stable against wiping.
50961, chapter 10, even when it does not contain other components such as silicate, Cer, aluminium and borate. This conversion layer is clear, transparent, substantially colourless and iridescent, is about 100 nm to 1000 nm thick, hard, adheres well and is stable against wiping.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE19615664.5 | 1996-04-19 | ||
DE19615664A DE19615664A1 (en) | 1996-04-19 | 1996-04-19 | Chromium (VI) free chromate layer and process for its production |
PCT/DE1997/000800 WO1997040208A1 (en) | 1996-04-19 | 1997-04-18 | Chromate-free conversion layer and process for producing the same |
Publications (2)
Publication Number | Publication Date |
---|---|
CA2252036A1 true CA2252036A1 (en) | 1997-10-30 |
CA2252036C CA2252036C (en) | 2006-12-05 |
Family
ID=37560875
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CA002252036A Expired - Lifetime CA2252036C (en) | 1996-04-19 | 1997-04-18 | Chromate-free conversion layer and process for producing the same |
Country Status (1)
Country | Link |
---|---|
CA (1) | CA2252036C (en) |
-
1997
- 1997-04-18 CA CA002252036A patent/CA2252036C/en not_active Expired - Lifetime
Also Published As
Publication number | Publication date |
---|---|
CA2252036C (en) | 2006-12-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU3087397A (en) | Chromate-free conversion layer and process for producing the same | |
CA2304240A1 (en) | Improved methods and compositions for preventing corrosion of metal substrates | |
DE69417909D1 (en) | HYDROPHILE COATINGS FOR ALUMINUM | |
CA2396514A1 (en) | Surface-treated tin-plated steel sheet and surface treatment solution | |
CA2205468A1 (en) | Water-reducible coating composition for providing corrosion protection | |
CA2270879A1 (en) | Method of preventing corrosion of metal sheet using vinyl silanes | |
CA2208078A1 (en) | Formulations and methods for reducing skin irritation | |
IE841650L (en) | Water resistant aluminium particles and coating | |
KR970704915A (en) | Corrosive agent for aluminum alloy | |
ZA951876B (en) | Corrosion resistant treatment for metal surfaces | |
CA2172614A1 (en) | Nonabrasive, Corrosion Resistant, Hydrophilic Coatings for Aluminum Surfaces, Methods of Application, and Articles Coated Therewith | |
CA2234819A1 (en) | Zinc phosphate conversion coating compositions and process | |
CA2311494A1 (en) | Modification of surfaces in order to increase surface tension | |
TW332820B (en) | Organometallic compound | |
CA2074545A1 (en) | Method for removing coatings from metal substrates prone to corrosion or deterioration | |
ES2082903T3 (en) | CHROME METHOD FOR STEEL PLATES WITH ZINC-BASED COATING. | |
EP0846744A4 (en) | Adhesion accelerator compositions and adhesive rubber composition | |
CA2252559A1 (en) | Chromate passivating and storage stable concentrate solutions therefor | |
GB2223239A (en) | Phosphating process | |
CA2093612A1 (en) | Phosphating solution for metal substrates | |
CA2252036A1 (en) | Chromate-free conversion layer and process for producing the same | |
CA2028688A1 (en) | Composition and method for producing chromate conversion coatings | |
CA2387967A1 (en) | Galvanized steel for use in vehicle body | |
CA2164008A1 (en) | Rapidly dissolving and storage stable titanium phosphate containing activating composition | |
CA2150165A1 (en) | Boron Nitride-Silicate Sealant |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
EEER | Examination request | ||
MKEX | Expiry |
Effective date: 20170418 |