CA2185701C - Method and device for manufacturing biaxially oriented tubing from thermoplastic material - Google Patents
Method and device for manufacturing biaxially oriented tubing from thermoplastic material Download PDFInfo
- Publication number
- CA2185701C CA2185701C CA002185701A CA2185701A CA2185701C CA 2185701 C CA2185701 C CA 2185701C CA 002185701 A CA002185701 A CA 002185701A CA 2185701 A CA2185701 A CA 2185701A CA 2185701 C CA2185701 C CA 2185701C
- Authority
- CA
- Canada
- Prior art keywords
- tube
- mandrel
- calibration
- external dimensions
- downstream
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Method and device for manufacturing biaxially oriented tubing from thermopla stic material. The method comprises forcing the tube over a mandrel (3) at an orientation temperature of the plastic material, wh ich mandrel comprises an expansion part (5) which produc es expansion in the circumferential direction of the tube. Downstream of the ma ndrel and axial pulling force is exerted on the tube, an d the biaxially oriented tube is cooled down. At a distance downstream of the mandrel the tube is drawn through a calibration opening (12) bounded by calibration means, the calibration opening being such that i t produces a reduction in the external dimensions of the tube. Accurate regulation of the external dimensions of the tube is provided by re gulating the distance between the mandrel (3) and the ca libration means (12), in particular depending on the external dimensions of the tube m easured downstream of the calibration means.
Description
Method and device for manufacturing biaxially oriented tubing from thermoplastic material.
The present invention relates to a method for manufacturing biaxially oriented tubing from thermoplastic material, comprising forcing the tube over a mandrel at an orientation'temperature of the plastic material, which mandrel comprises an expansion part which produces expansion in the circumferential direction of the tube, while downstream of the mandrel an axial pulling force is exerted on the tube, and the biaxially oriented tube is cooled down, and downstream of the mandrel the tube is subjected to calibration of its external dimensions. In the context of the present invention the term tube also relates to hose-type products.
The object of biaxially orienting the plastic material of a tube, also known as biaxia~ly drawing a tube, is to improve the properties of the tube through orientation of the molecules of the plastic material of the tube in two mutually perpendicular directions. In the case of a certain known method the biaxial orientation is produced by forcing the tube over a mandrel, with the result that the tube is deformed. Upstream of the mandrel the tube is brought to a suitable orientation temperature.
In practice, the temperature distribution inside the tube wall is within a suitable range for biaxial orientation of the molecules of the plastic material of the tube.
In the case of the known method the tube is forced over the mandrel through an axial pulling force being exerted on the tube downstream of the mandrel. The mandrel comprises an expansion part which produces the increase in the dimensions in the circumferential direction of the tube. The fact that the tube passes over this expansion part essentially determines the orientation of the plastic material in the circumferential direction of the tube. The axial pulling force essentially determines the orientation in the axial direction. The biaxial orientation obtained is fixed (frozen) by cooling~down the tube.
WO 95/25628 ~ PCT/NL95/00099 A method of the type mentioned in the preamble is known from, for example, Wo 93/19924. This publication describes how a tube with a cylindrical tube wall is manufactured by means of an extruder. Viewed in the direction of movement of the tube, a so~.id, undeformable mandrel with a conical expansion part i~> situated down-stream of said extruder. The tube is forced over the mandrel at an orientation temperature which is suitable for the plastic material concerned, through an axial pulling force being exerted on the tube downstream of the mandrel.
At the level of a run-off part of the mandrel, connected to the expansion part of the mandrel, the tube is cooled externally in order to fix the orientation obtained.
In order to guarantee th<~t the ultimately manu-factured biaxially oriented tube has the desired external dimensions - in this case external diamsater - with suffi-cient accuracy, this publication proposes that a vacuum calibration sleeve should be placed downstream of the mandrel, between the mandrel and the pu7_ling device, The tube is pulled through this calibration sleeve, in the course of which the tube is sucked against the inside wall of the calibration sleeve by means of a vacuum created by a vacuum source, The result of this is that the tube is stretched here in the circumferential direction until it reaches an external diameter determined by the inside wall of the calibration sleeve. In order to make stretching of the tube possible, the tube has to be heated in the case of this known method. The heating is carried out by heating the calibration sleeve.
The method of calibration of the external dimen-sions of the biaxially oriented tube proposed in the case of this known method has proved disadvantageous. In particular, it has been found that the biaxial orientation of the plastic material of the tube produced during the passage over the mandrel is impaired in an undesirable way, both through increasing the external dimensions of the tube during calibration and through heating applied to the tube during the calibration.
The object of the present invention is to eliminate - 3.
the abovementioned disadvantage and also to provide a method which comprises accurate regulation for the external dimensions of the tube.
This object is achieved by a method for manufacturing biaxially oriented tubing from thermoplastic material, comprising forcing the tube over a mandrel at an orientation temperature of the plastic material, which mandrel comprises an expansion part which produces expansion in the circumferential direction of the tube, while downstream of the mandrel an axial pulling force is exerted on the tube, and the biaxially oriented tube is cooled down, and downstream of the mandrel the tube is subjected to calibration of the external dimensions of the tube, characterized in that at a difference downstream of the mandrel the tube is drawn through a calibration opening bounded by calibration means, the calibration opening being such that it produces a reduction in the external dimensions of the tube. The calibration means can be in the form of, for example, a solid draw plate with a calibration opening formed therein or a number of rollers which together bound the calibration opening.
In this respect it is important to recognize that the tube will shrink downstream of the mandrel through cooling, in particular produced by cooling means set up at that point. This shrinkage occurs both in the case of the method according to the present invention and in the case of the methods already known. In order to produce the effective reduction in the external dimensions of the tube envisaged according to the present invention, the reduction must therefore lead to smaller external dimensions than the external dimensions which the tube would acquire if allowance is made for the shrinkage which occurs.
Unlike the above-described known method, the calibration means produce a reduction in the external dimensions of the tube. Since a reduction in the external dimensions now occurs, it is not necessary for the tube and/or the calibration means to be heated, which is advantageous for achieving the envisaged biaxial orientation.
In the case of the method according to the invention the cross-section of the tube undergoes a progressive 14 reduction between the mandrel and the calibration opening. The way in which said reduction occurs here, in particular the speed at which it occurs, can advantageously be used for controlling the biaxial drawing WO 95/25628 ,~, PCTlNL95100099 process, as will emerge from the sub-claims and the corresponding description.
The tube also encounters a resistance at the moment when it is passing through the calibration means. This resistance can also advantageously be used for controlling the biaxial drawing process.
It is pointed out that European Patent Application EP 0157601 discloses a method of the type mentioned in the preamble in which, downstream of the expansion part of the mandrel, the tube to be oriented is drawn through a draw plate lying around a cylindrical run-off part of the mandrel. It is clear that this draw plate does not serve as a calibration means for the external dimensions of the tube after the tube has left the mandrel, as in the case of the present invention. On the contrary, EP 0157601 discloses an interaction between the draw plate and the part of the mandrel lying inside it for producing the biaxial orientation of the plastic material of the tube.
In the case of the method according to the present invention it is a great advantage if the distance between the mandrel and the calibration opening is regulated. For this purpose, it is, of course, necessary for the calibration means to be movable relative to the mandrel, which is simple to carry out.
The distance between the mandrel and the calibra-tion opening is preferably regulated depending on charac-teristics measured downstream of the calibration opening, in particular the external dimensions of the biaxially oriented tube.
The distance between the mandrel and the calibra-tion opening is advantageously increased if the measured external dimensions of the biaxially oriented tube are smaller than the desired external dimensions, and the distance between the mandrel and the calibration opening is reduced if the measured external dimensions of the biaxially oriented tube are greater than the desired external dimensions.
In an advantageous embodiment of the method according to the invention the calibration means are _ g -cooled. The tube is also preferably cooled further when it is downstream of the calibration means. The influence of the shrinkage of the tube caused by this cooling on the external dimensions of the tube can be determined (for example, experimentally) and used in determining or adjust-ing the dimensions of the calibration opening, which are necessary to obtain the desired external dimensions of the tube.
In a variant of the method according to the present invention, downstream of the mandrel the tube is drawn through several calibration openings placed one after the other and bounded by calibration means, each calibration opening being such that it produces a further reduction in the external dimensions of the tube. This means that the reduction per passage through a calibration opening is limited, which in a number of cases is advantageous as regards the influence of said reduction on the biaxial orientation achieved in the case of the mandrel.
The invention will be explained in greater detail below with reference to Figure 1, in which in a top view the part of the exemplary embodiment of a device according to the invention for manufacturing biaxially oriented tubing which is relevant for explaining the invention is shown.
Figure 1 is based on an application in which a tube with a smooth cylindrical wall is manufactured from thermoplastic material. It will be clear that the inventive idea and solutions described here can also be used for the manufacture of tubular sections of a different cross-section, if necessary by adapting the embodiment of the solutions described herein.
Figure 1 shows a part of a tube 1 (in longi-tudinal section) made of thermoplastic material, which tube is manufactured in a continuous process by means of an extruder (not shown). Downstream of the extruder the plastic material of the tube 1 is brought by means of tem-perature-regulating means .(not shown) to a temperature suitable for biaxial orientation, for example cooling by air or water.
WO 95/25628 ~ PCT/NL95/00099 The plastic material of the tempered tube 1 is biaxially oriented (drawn) by subsequently forcing the tube 1 over a metal mandrel 3 fixed by a tension member 2 to the extruder. The mandrel 3 has a cylindrical run-on part 4, a conical expansion part 5 and a slightly tapered run-off part 6.
For forcing the tube 1 over the mandrel 3 a pulling device (not shown) is present downstream of the mandrel 3, for exerting an axial pulling force on the tube 1. A
pushing device may also be placed upstream of the mandrel 3, for exerting a pushing force on the tube 1.
In order to fix the biaxial orientation of the molecules of the plastic material of the tube 1 during the passage over the mandrel 3, the tube is subjected to external cooling downstream of the expansion part 5 of the mandrel 3. For this purpose, a diagrammatically indicated cooling device 8 is set up at this point, for example with spray nozzles for cooling water.
At a distance downstream from the mandrel 3, there is a calibration and cooling device 10 according to the invention, which will be explained below. The calibration and cooling device 10 comprises a draw plate 11, in the form of a metal disc with a central calibration opening 12.
The draw plate 11 is slidably mounted on guide bars 13 of the fixed frame of the calibration device 10, in such a way that the distance between the draw plate 11 and the mandrel 3 can be set within a suitable range. The calibration device 10 comprises a diagrammatically indicated displacement unit 14 for moving the draw plate 11.
Arms 15 with cooling medium spray nozzles 16 are fixed to the draw plate 11, for cooling the biaxially oriented tube 1 during and after its passage through the draw plate 11. The cooling medium, for example water, is supplied through a pipe 17 to the spray nozzles 16. The cooling medium is collected in a tank 18 placed around the calibration and cooling device 10.
The diameter of the calibration opening 12 of the draw plate 11 is selected in such a way that the external diameter of the tube 1 is reduced when it is passing ~, CA 02185701 1996-09-16~
through the draw plate 11. The reduction which the draw plate 11 produces in the external diameter relative to the external diameter of the tube 1 at the moment of leaving the mandrel 3 is greater than the reduction in the external diameter of the tube 1 resulting from the shrinkage through cooling of the tube in the path between the mandrel 3 and the calibration opening 12. In other words, the draw plate il exerts an effective force on the tube 1, thereby reducing the external diameter of the tube 1. By making an allowance for further shrinkage of the tube 1 after it leaves the calibration opening, the diameter of said calibration opening 12 can be selected in such a way that the ultimately manufactured tube 1 acquires the envisaged external diameter With great accuracy.
The present invention provides a solution to effectively controlling the external diameter of the biaxial oriented tube 1. To this end, a diagrammatically shown measuring device 20 is placed downstream of the calibration device 10. This measuring device 20 measures the external dimensions, in this case the external diameter, of the tube 1. The measuring device 20 transmits a signal representing the external dimensions to a control unit 21, which compares this signal with a signal representing the desired external dimensions of the tube 1.
A control signal based on the difference between these two signals is supplied by the control unit 21 to the displacement unit 14 of the calibration device 10. This produces the movement of the draw plate 11 relative to the mandrel 3. If it is found by the control unit 21 that the external diameter of the tube is smaller than the desired external diameter, the control unit 21 transmits such a signal to the displacement unit 14 that the distance between the mandrel 3 and the draw plate 11 increases.
However, if the external diameter of the tube 1 is greater than the desired external diameter, the draw plate 11 is moved towards the mandrel 3.
The basic principle of this method can be explained by the speed at which the cross-section of the tube is reduced. This speed depends on the distance between mandrel g _ 3 and draw plate 11. If the speed of reduction of the cross-section is relatively great, the ultimate diameter reduction is found to be greater than that at a lower speed (a great distance between the mandrel and the draw plate).
The resistance formed by the draw plate 11 to the tube 1 passing through it can also be used advantageously for the biaxial orientation to be achieved. Although this orientation occurs essentially when the tube 1 is passing over the mandrel 3, it is found that the axial tension in the tube 1 in the path after it has passed through the draw plate 11 has an influence on the ultimately manufactured tube 1. In particular, the cooling of the tube can be regu-lated suitably by means of the cooling device 8 so that the biaxially oriented tube 1 is cooled in the path between the mandrel 3 and the draw plate 11. This then leads to an increase in the resistance formed by the draw plate 11 to the tube 1 passing through it. This change in the resis-tance, combined with the pulling force exerted on the tube 1, leads to a change in the axial tension in the tube 1.
This method of changing the axial tension in the tube 1 can advantageously be used for obtaining the envisaged biaxial orientation.
The present invention relates to a method for manufacturing biaxially oriented tubing from thermoplastic material, comprising forcing the tube over a mandrel at an orientation'temperature of the plastic material, which mandrel comprises an expansion part which produces expansion in the circumferential direction of the tube, while downstream of the mandrel an axial pulling force is exerted on the tube, and the biaxially oriented tube is cooled down, and downstream of the mandrel the tube is subjected to calibration of its external dimensions. In the context of the present invention the term tube also relates to hose-type products.
The object of biaxially orienting the plastic material of a tube, also known as biaxia~ly drawing a tube, is to improve the properties of the tube through orientation of the molecules of the plastic material of the tube in two mutually perpendicular directions. In the case of a certain known method the biaxial orientation is produced by forcing the tube over a mandrel, with the result that the tube is deformed. Upstream of the mandrel the tube is brought to a suitable orientation temperature.
In practice, the temperature distribution inside the tube wall is within a suitable range for biaxial orientation of the molecules of the plastic material of the tube.
In the case of the known method the tube is forced over the mandrel through an axial pulling force being exerted on the tube downstream of the mandrel. The mandrel comprises an expansion part which produces the increase in the dimensions in the circumferential direction of the tube. The fact that the tube passes over this expansion part essentially determines the orientation of the plastic material in the circumferential direction of the tube. The axial pulling force essentially determines the orientation in the axial direction. The biaxial orientation obtained is fixed (frozen) by cooling~down the tube.
WO 95/25628 ~ PCT/NL95/00099 A method of the type mentioned in the preamble is known from, for example, Wo 93/19924. This publication describes how a tube with a cylindrical tube wall is manufactured by means of an extruder. Viewed in the direction of movement of the tube, a so~.id, undeformable mandrel with a conical expansion part i~> situated down-stream of said extruder. The tube is forced over the mandrel at an orientation temperature which is suitable for the plastic material concerned, through an axial pulling force being exerted on the tube downstream of the mandrel.
At the level of a run-off part of the mandrel, connected to the expansion part of the mandrel, the tube is cooled externally in order to fix the orientation obtained.
In order to guarantee th<~t the ultimately manu-factured biaxially oriented tube has the desired external dimensions - in this case external diamsater - with suffi-cient accuracy, this publication proposes that a vacuum calibration sleeve should be placed downstream of the mandrel, between the mandrel and the pu7_ling device, The tube is pulled through this calibration sleeve, in the course of which the tube is sucked against the inside wall of the calibration sleeve by means of a vacuum created by a vacuum source, The result of this is that the tube is stretched here in the circumferential direction until it reaches an external diameter determined by the inside wall of the calibration sleeve. In order to make stretching of the tube possible, the tube has to be heated in the case of this known method. The heating is carried out by heating the calibration sleeve.
The method of calibration of the external dimen-sions of the biaxially oriented tube proposed in the case of this known method has proved disadvantageous. In particular, it has been found that the biaxial orientation of the plastic material of the tube produced during the passage over the mandrel is impaired in an undesirable way, both through increasing the external dimensions of the tube during calibration and through heating applied to the tube during the calibration.
The object of the present invention is to eliminate - 3.
the abovementioned disadvantage and also to provide a method which comprises accurate regulation for the external dimensions of the tube.
This object is achieved by a method for manufacturing biaxially oriented tubing from thermoplastic material, comprising forcing the tube over a mandrel at an orientation temperature of the plastic material, which mandrel comprises an expansion part which produces expansion in the circumferential direction of the tube, while downstream of the mandrel an axial pulling force is exerted on the tube, and the biaxially oriented tube is cooled down, and downstream of the mandrel the tube is subjected to calibration of the external dimensions of the tube, characterized in that at a difference downstream of the mandrel the tube is drawn through a calibration opening bounded by calibration means, the calibration opening being such that it produces a reduction in the external dimensions of the tube. The calibration means can be in the form of, for example, a solid draw plate with a calibration opening formed therein or a number of rollers which together bound the calibration opening.
In this respect it is important to recognize that the tube will shrink downstream of the mandrel through cooling, in particular produced by cooling means set up at that point. This shrinkage occurs both in the case of the method according to the present invention and in the case of the methods already known. In order to produce the effective reduction in the external dimensions of the tube envisaged according to the present invention, the reduction must therefore lead to smaller external dimensions than the external dimensions which the tube would acquire if allowance is made for the shrinkage which occurs.
Unlike the above-described known method, the calibration means produce a reduction in the external dimensions of the tube. Since a reduction in the external dimensions now occurs, it is not necessary for the tube and/or the calibration means to be heated, which is advantageous for achieving the envisaged biaxial orientation.
In the case of the method according to the invention the cross-section of the tube undergoes a progressive 14 reduction between the mandrel and the calibration opening. The way in which said reduction occurs here, in particular the speed at which it occurs, can advantageously be used for controlling the biaxial drawing WO 95/25628 ,~, PCTlNL95100099 process, as will emerge from the sub-claims and the corresponding description.
The tube also encounters a resistance at the moment when it is passing through the calibration means. This resistance can also advantageously be used for controlling the biaxial drawing process.
It is pointed out that European Patent Application EP 0157601 discloses a method of the type mentioned in the preamble in which, downstream of the expansion part of the mandrel, the tube to be oriented is drawn through a draw plate lying around a cylindrical run-off part of the mandrel. It is clear that this draw plate does not serve as a calibration means for the external dimensions of the tube after the tube has left the mandrel, as in the case of the present invention. On the contrary, EP 0157601 discloses an interaction between the draw plate and the part of the mandrel lying inside it for producing the biaxial orientation of the plastic material of the tube.
In the case of the method according to the present invention it is a great advantage if the distance between the mandrel and the calibration opening is regulated. For this purpose, it is, of course, necessary for the calibration means to be movable relative to the mandrel, which is simple to carry out.
The distance between the mandrel and the calibra-tion opening is preferably regulated depending on charac-teristics measured downstream of the calibration opening, in particular the external dimensions of the biaxially oriented tube.
The distance between the mandrel and the calibra-tion opening is advantageously increased if the measured external dimensions of the biaxially oriented tube are smaller than the desired external dimensions, and the distance between the mandrel and the calibration opening is reduced if the measured external dimensions of the biaxially oriented tube are greater than the desired external dimensions.
In an advantageous embodiment of the method according to the invention the calibration means are _ g -cooled. The tube is also preferably cooled further when it is downstream of the calibration means. The influence of the shrinkage of the tube caused by this cooling on the external dimensions of the tube can be determined (for example, experimentally) and used in determining or adjust-ing the dimensions of the calibration opening, which are necessary to obtain the desired external dimensions of the tube.
In a variant of the method according to the present invention, downstream of the mandrel the tube is drawn through several calibration openings placed one after the other and bounded by calibration means, each calibration opening being such that it produces a further reduction in the external dimensions of the tube. This means that the reduction per passage through a calibration opening is limited, which in a number of cases is advantageous as regards the influence of said reduction on the biaxial orientation achieved in the case of the mandrel.
The invention will be explained in greater detail below with reference to Figure 1, in which in a top view the part of the exemplary embodiment of a device according to the invention for manufacturing biaxially oriented tubing which is relevant for explaining the invention is shown.
Figure 1 is based on an application in which a tube with a smooth cylindrical wall is manufactured from thermoplastic material. It will be clear that the inventive idea and solutions described here can also be used for the manufacture of tubular sections of a different cross-section, if necessary by adapting the embodiment of the solutions described herein.
Figure 1 shows a part of a tube 1 (in longi-tudinal section) made of thermoplastic material, which tube is manufactured in a continuous process by means of an extruder (not shown). Downstream of the extruder the plastic material of the tube 1 is brought by means of tem-perature-regulating means .(not shown) to a temperature suitable for biaxial orientation, for example cooling by air or water.
WO 95/25628 ~ PCT/NL95/00099 The plastic material of the tempered tube 1 is biaxially oriented (drawn) by subsequently forcing the tube 1 over a metal mandrel 3 fixed by a tension member 2 to the extruder. The mandrel 3 has a cylindrical run-on part 4, a conical expansion part 5 and a slightly tapered run-off part 6.
For forcing the tube 1 over the mandrel 3 a pulling device (not shown) is present downstream of the mandrel 3, for exerting an axial pulling force on the tube 1. A
pushing device may also be placed upstream of the mandrel 3, for exerting a pushing force on the tube 1.
In order to fix the biaxial orientation of the molecules of the plastic material of the tube 1 during the passage over the mandrel 3, the tube is subjected to external cooling downstream of the expansion part 5 of the mandrel 3. For this purpose, a diagrammatically indicated cooling device 8 is set up at this point, for example with spray nozzles for cooling water.
At a distance downstream from the mandrel 3, there is a calibration and cooling device 10 according to the invention, which will be explained below. The calibration and cooling device 10 comprises a draw plate 11, in the form of a metal disc with a central calibration opening 12.
The draw plate 11 is slidably mounted on guide bars 13 of the fixed frame of the calibration device 10, in such a way that the distance between the draw plate 11 and the mandrel 3 can be set within a suitable range. The calibration device 10 comprises a diagrammatically indicated displacement unit 14 for moving the draw plate 11.
Arms 15 with cooling medium spray nozzles 16 are fixed to the draw plate 11, for cooling the biaxially oriented tube 1 during and after its passage through the draw plate 11. The cooling medium, for example water, is supplied through a pipe 17 to the spray nozzles 16. The cooling medium is collected in a tank 18 placed around the calibration and cooling device 10.
The diameter of the calibration opening 12 of the draw plate 11 is selected in such a way that the external diameter of the tube 1 is reduced when it is passing ~, CA 02185701 1996-09-16~
through the draw plate 11. The reduction which the draw plate 11 produces in the external diameter relative to the external diameter of the tube 1 at the moment of leaving the mandrel 3 is greater than the reduction in the external diameter of the tube 1 resulting from the shrinkage through cooling of the tube in the path between the mandrel 3 and the calibration opening 12. In other words, the draw plate il exerts an effective force on the tube 1, thereby reducing the external diameter of the tube 1. By making an allowance for further shrinkage of the tube 1 after it leaves the calibration opening, the diameter of said calibration opening 12 can be selected in such a way that the ultimately manufactured tube 1 acquires the envisaged external diameter With great accuracy.
The present invention provides a solution to effectively controlling the external diameter of the biaxial oriented tube 1. To this end, a diagrammatically shown measuring device 20 is placed downstream of the calibration device 10. This measuring device 20 measures the external dimensions, in this case the external diameter, of the tube 1. The measuring device 20 transmits a signal representing the external dimensions to a control unit 21, which compares this signal with a signal representing the desired external dimensions of the tube 1.
A control signal based on the difference between these two signals is supplied by the control unit 21 to the displacement unit 14 of the calibration device 10. This produces the movement of the draw plate 11 relative to the mandrel 3. If it is found by the control unit 21 that the external diameter of the tube is smaller than the desired external diameter, the control unit 21 transmits such a signal to the displacement unit 14 that the distance between the mandrel 3 and the draw plate 11 increases.
However, if the external diameter of the tube 1 is greater than the desired external diameter, the draw plate 11 is moved towards the mandrel 3.
The basic principle of this method can be explained by the speed at which the cross-section of the tube is reduced. This speed depends on the distance between mandrel g _ 3 and draw plate 11. If the speed of reduction of the cross-section is relatively great, the ultimate diameter reduction is found to be greater than that at a lower speed (a great distance between the mandrel and the draw plate).
The resistance formed by the draw plate 11 to the tube 1 passing through it can also be used advantageously for the biaxial orientation to be achieved. Although this orientation occurs essentially when the tube 1 is passing over the mandrel 3, it is found that the axial tension in the tube 1 in the path after it has passed through the draw plate 11 has an influence on the ultimately manufactured tube 1. In particular, the cooling of the tube can be regu-lated suitably by means of the cooling device 8 so that the biaxially oriented tube 1 is cooled in the path between the mandrel 3 and the draw plate 11. This then leads to an increase in the resistance formed by the draw plate 11 to the tube 1 passing through it. This change in the resis-tance, combined with the pulling force exerted on the tube 1, leads to a change in the axial tension in the tube 1.
This method of changing the axial tension in the tube 1 can advantageously be used for obtaining the envisaged biaxial orientation.
Claims (7)
1. Method for manufacturing biaxially oriented tubing from thermoplastic material, comprising forcing the tube over a mandrel at an orientation temperature of the plastic material, which mandrel comprises an expansion part which produces expansion in the circumferential direction of the tube, while downstream of the mandrel an axial pulling force is exerted on the tube, and the biaxially oriented tube is cooled down, and downstream of the mandrel the tube is subjected to calibration of the external dimensions of the tube, characterized in that, at a distance downstream of the mandrel, the tube is drawn through a calibration opening bounded by calibration means, the calibration opening being such that it produces a reduction in the external dimensions of the tube.
2. Method according to claim 1, wherein the distance between the mandrel and the calibration opening is regulated.
3. Method according to claim 2, wherein the distance between the mandrel and the calibration opening is regulated depending on external dimensions of the biaxially oriented tube measured downstream of the calibration opening.
4. Method according to any one of the preceding claims 1-3, wherein the calibration means are cooled.
5. Method according to claim 4, wherein the distance between the mandrel and the calibration opening is increased if the measured external dimensions of the tube are smaller than the desired external dimensions, and in that the distance between the mandrel and the calibration opening is reduced if the measured external dimensions of the tube are greater than the desired external dimensions.
6. Method according to any one of the preceding claims 1-5, wherein downstream of the mandrel the tube is drawn through several calibration openings placed one after the other and bounded by calibration means, each calibration opening being such that it produces a further reduction in the external dimensions of the tube.
7. Method according to any one of the preceding claims 1-6, wherein the tube is cooled upstream of the calibration means.