CA2088675A1 - Thermocouple equipped with ceramic insulator and sheath and method of making same - Google Patents
Thermocouple equipped with ceramic insulator and sheath and method of making sameInfo
- Publication number
- CA2088675A1 CA2088675A1 CA 2088675 CA2088675A CA2088675A1 CA 2088675 A1 CA2088675 A1 CA 2088675A1 CA 2088675 CA2088675 CA 2088675 CA 2088675 A CA2088675 A CA 2088675A CA 2088675 A1 CA2088675 A1 CA 2088675A1
- Authority
- CA
- Canada
- Prior art keywords
- insulator
- sheath
- ceramic
- thermowell
- thermocouple
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A thermocouple assembly comprising a unitary, axially elongated ceramic insulator (12) formed with a pair of axially-extending passageways (13) for receiving a pair of thermoelements (11), and an axially elongated unitary ceramic sheath (14) provided with a chamber (15) having a closed end for receiving the elongated, ceramic-insulator (12). This thermocouple assembly (10) may be housed cartridge-style in an existing thermowell, or inserted into a stainless steel tube (20) which is then threaded into the wall of a chamber to be monitored, or provided with a spark plug-type externally threaded shell (23) for mounting in an exhaust manifold or the like. In this manner, a durable and readily replaceable thermocouple assembly (10) is provided.
Description
W092/02794 PCT/US9t/0~32 7 a Title: Thermocouple Equipped with Ceramic Insulator and Sheath and Method of Making Same i Backaround of the Invention:
The present invention relates to temperature sensing apparatus and more particularly to those devices adapted for use with internal combustion enqines, nuclear reactors, and other apparatus which require high temperature .
monitoring.
In the past, various ap~ratus which operate at high temperatures have been equipped with thermocouples, particularly the "~ and "K~ types, which have been inserted to monitor reaction temperatures. The materials which jacketed these temperature sensing elements were typically formed from stainless steel or other conductive metals.
Much of the reaa-out instrumentation to which the thermocouple was attached required electrically ungrounded thermoelements. Accordingly, the metal jackets were electrically isolated from the iron-constantin or chromel-alumel thermoelement wires, typically by filling the space between the eIements and jacket.with powdered magnesium oside. The major deficiency of.these previous . .
thermocoupie designs was the use of a.hygroscopic mineral ~ . .
o~ide ~o insulate the metallic thermoelement wires from the WO 92/02794 PCI`/US91/05'132 metal, protective jacket. The insulative capacity of the mineral oxide was compromised by water vapor invading the .
insulative material from the surrounding atmosphere. Even a slight amount of moisture in the powdered mineral 02ide permitted formation of at least a temporary ground between the jacket and the thermocouple wires, thereby rendering the device non-functional. Over the years, this problem was tolerated, with many operators simply discontinuing use of the thermocouple and associated pyrometer for a period of time. However, with the growth in use of unmanned machinery, the constant monitoring required for computer control and computer monitoring, and the dangers posed by escessive temperatures in combustion reactions, the need for a durable and reliable thermocouple has become paramount. :
For example, use of thermocouples in internal combustion engines, particularly in monitoring eshaust gas temperatures, has become more widespread and critical. In addition to the above-mentioned grounding problem, conventional thermocouples were frequently sized to project `
deeply into the exhaust gas stream. Naturally, the metallic jackets for such elongated thermocouples were subject to considerable wear from esposure to hot and corrosive gases.
In addition, many earlier thermocouples employed tapered pipe threads for attachment to the eshaust mani~olds. Removal and replacement typically involved a cutting torch, thus requiring engine shutdown, so that possibly combustible gases in a classified location (i.g., .. , , , . ... .. , .. , ~ ....................... -: .
., ~. ~ . . -Class 1, Group D, Division 1 or 2) or other engine room were not ignited by sparks from the torch. Likewise, in the absence of a relatively permanent thermowell from which the spent thermocouple could be e~tracted, engine shutdown was reguired so that poisonous exhaust gases would not escape through the opening in the exhaust manifold formed when the old thermocouple was removed.
Accordingly, the present inventor was faced with the problems of devising a thermocouple which was substantially impervious to moisture, capable of withstanding substantial heat and vibration, less exposed to the corrosive forces within the high temperature environment, and easily removed and replaced.
Summarv and Ob;ects of the Invention:
The thermocouple which is the subject of the present invention basically comprises at least one thermoelement, a unitary ceramic insulator formed with at least one thermoelement-receiving passageway, and a unitary ceramic sheath formed with an insulator-receiving chamber.
In addition, the present thermocouple may be equipped with a metal shell formed with a sheath-receiving bore and provided with cooperative fastening-means for securing the thermocouple in an operative position. Preferably, the above-mentioned cooperative fastening means includes~
standard spark plug threads, but may also use NPT threads.
It is also preferable for the above-mentioned metal shell or - . - .~ .
~Q~&7`~ - 4 -jacket to be constructed in such a manner that a sensor end of the thermoelement e~tends into the sampling area less deeply than what has been the norm in the past.
A primary object of the present invention is to provide a thermocouple which is practically impervious to moisture in the atmosphere surrounding the apparatus into ~hich it is inserted. Another object of the present thermocouple is to be more durable and less intrusive in the ;
sample area which it monitors than was obtained heretofore.
Yet another object of the present invention is to provide a thermocouple which is readily adapted for insertion in an existing thermowell, as well as being adapted to receive an outer threaded sleeve or relatively complete cover. A ~ `;
further object of the presént thermocouple is to be readily removable from the sample area it is intended to monitor.
.. :, Brief Description of the Drawinqs:
Fig. 1 is a front elevational view of a thermocouple according to the present invention equipped with a threaded metallic outer shell;
Fig. 2 is a vertical sectional view taken along line 2-2 of Fig. 1 and particularly illustrating the manner in which the present thermocouple is constructed;
Fig. 3 is a front elevational view of a ther,mocouple according to the present invention~equipped with an elongated metal tube or thermowell; and ... . ~ -. . . . . . . .
, .. ., . ~, . . ~, , , . ................ ,: .
. . . . . ,.: . . . 7 ~ 3 ,~
Fiq. 4 is a vertical sectional view taken along line 4-4 of Fig. 3 and particularly illustrating the manner in which the present thermocouple is mounted in the tube or thermowell.
Detailed Descri~tion of the Preferred Embodiment:
As best indicated in Fiqs. 2 and 4, the present thermocouple, generally designated 10, basically comprises at least one and preferably two thermoelements 11, a unitary ceramic insulator 12 formed with at least one and preferably two relatively spaced apart thermoelement-receiving passageways 13, and a unitary ceramic sheath 14 formed with an insulator-receiving chamber 15. Prefera~ly, the thermoelsments are either iron-constantin or chromel-alumel wires, although other thermocouple alloys may be employed.
The thermoelement insulator 12 is preferably an elongated, cylindrical articlé fabricated from high purity calcined alumina oxide powder which is milled and blended with some plasticizers and flexing agents to provide an homogeneous material of ninety-six percent alumina oxide- ;-content. Other material compositions fall within the scope of the present invention which is not to be restricted to this one preferred embodiment. Typically, this alumina oxide material is e~truded to form the insulator 12, and is then sintered at elevated temperatures to form it to its final dimensions. One of the bare thermoelement wires 11 is inserted into and through each of the passageways, and a con~entional thermocouple junction 16 is provided at a 092/02794 PCT/US91/0~32 ~ 6 -sensor end of the ceramic insulator 12 adjacent to the closed end of the insulator-receiving chamber 15 of the -ceramic sheath 14.
Preferably, the oeramic sheath 14 is manufactured by those methods commonly used to fabricate spark plug insulators from high purity alumina oxide formulas. In this instance, the calcined alumina oxide powder is milled and blended with plasticizers and fluxing agents to form an homogeneous material of ninety-six percent alumina oxide ;
content. This material is then extruded or isostatically pressed into blanks. The resulting blank is then shaped to its unfired profile and dimensioned by lathe cutting or form grinding. Alternatively, the unformed alumina oxide material may be injection molded into the desired shape.
Once the ceramic sheath 14 is shaped, it is sintered under `
controlled firing conditions at elevated temperatures where it is reduced in size to the final dimensions, within standard commercial tolerances.
The thermoelement-bearing ceramic insulator 12 is then coated with a high temperature alumina ceramic cement and inserted into the ceramic sheath 14. This assembly is then cured under controlled temperature conditions to set the adhesive~ Note that fillers, such as powdery fillers -(e.g., sand, magnesium oxide) are not necessary in the assembly of the present invention. If the foregoing -as~embly is intended for use in an e~isting thermowell, then-no more needs to be done to the assembly 10-other than to apply ANSI standard colored insulation to the thermoelement '.
,,,, . . ,, ,- " , -,,.. . . .. , .,.. ~, .,,,, - -, , ~ ; . .; .,. , -.. . .
. - . : . .
- : . - : . .
W O 92/02794 PC~r/US91/05432 wires ll so that the connection to the instrumentation (not shown) will result in accurate temperature levels being monitored. Once the sensor assembly 10 is inserted into the thermowell, an externally threaded gland 18 (Fig. 4) may be screwed onto the cooperative internal threads of the thermowell in surrounding and overlying relation to an upper shoulder portion l9 of the ceramic sheath 14.
As indicated in Figs. 3 and 4, the present ceramic thermocouple 10 may be fitted cartridge-style into a stainless steel tube 20. This tube 20 may be somewhat permanent to the manifold or other housing into which it is installed and thus may constitute the above-referenced thermowell. The subject tube or thermowell 20 is formed with a sheath-receiving chamber ~1, the sensor end o which is closed. Preferably, the tube 20 is designed to project into the manifold or other chamber no more than one-quarter of the distance between opposing walls thereof.
Advantageously, the outer tube or thermowell 20 is equipped with esternal threads for cooperative engagement with a threaded coupling (not shown) on the mani~old wall. In addition, a hesagonal or octagonal head or shoulder 23 is formed on the stainless steel tube for extracting and fastening the tube to the manifold or chamber wall.
Alternatively, as indicated in Figs. l and 2, the present ceramic thermocouple 10 may be fitted înto a steel shell 23 which is hermetically sealed to the ceramic sheath 14 in a manner well known in the art of sealing a spark plug insulator to its surrounding metal shell. Preferably, the , :
q ~n~
shell is formed with standard SAE spark plug threads 24, a gasket 25 and a hesagonal or octagonal head 26. Preferably, the shell 23 is mounted on the ceramic thermocouple lO so that the sensor end 16 of the thermocouple projects at least one inch into the chamber which is to be monitored. In the case of exhaust gas temperature monitoring, the sensor end I ;-16 preferably extends less than one-half of the distance between opposing walls of the manifold in which it is mounted.
As an alternative to SAE threads 24, the shell may be provided with IS0 or DIN standard spark plug threads, as well as with NPT threads. In this manner, the subject ;
thermocouple may be replaced as easily as a spark plug and/or retrofitted into an existing threaded socket. Since the majority of prior art eshaust gas thermocouples have used one-ourth, three-eights, one-half or three-fourths inch NPT threads, it would be advantageous to employ 18 millimeter by 1.5 millimeter SAE or IS0 spark plug threads.
Preferably, a range of thread lengths would be provided, typically 12.7 millimeters, 18.5 millimeters and 2S.4 millimeters. The 18.5 millimeter length would be virtually identical to the thread length of a one-half inch NPT pipe ' ,~
thread. - 1 In addition, using TIG-welding procedures--typically !.
used in the manufacture of specialized industrial spark -plugs, the manuiacturer or o~erator may attach additional ~, ' ' ' ' ;` ' ' :' ' .
` W092/02794 PCT/VS9l/05432 , 9 ~ 6~
threads to the shell 23, thereby allowing for attachment of various hazardous location protective heads (not shown) for suppressing sparks and/or corrosion.
Thus, the present invention provides a thermocouple which is readily adapted for use in a variety of applications, either in combination with a metal tube or thermowell projecting into the area whose temperature is to be monitored or in association with a threaded metal shell :
similar in construction to those employed with spark plugs. -The present ceramic thermocouple 10 is preferably of cartridge design for ready replacement and for relatively permanent attachment to a spark plug-type threaded metal shell 23. ~y constructing the present thermocouple 10 from a unitary alumina oside insulator 12 which houses the thermoelements and a surrounding unitary alumina oxide sheath 14, the present invention is able to withstand the forces at work in the chamber being monitored and in the surrounding environment which tends to cause conventional thermocouples to ground out.
The present invention relates to temperature sensing apparatus and more particularly to those devices adapted for use with internal combustion enqines, nuclear reactors, and other apparatus which require high temperature .
monitoring.
In the past, various ap~ratus which operate at high temperatures have been equipped with thermocouples, particularly the "~ and "K~ types, which have been inserted to monitor reaction temperatures. The materials which jacketed these temperature sensing elements were typically formed from stainless steel or other conductive metals.
Much of the reaa-out instrumentation to which the thermocouple was attached required electrically ungrounded thermoelements. Accordingly, the metal jackets were electrically isolated from the iron-constantin or chromel-alumel thermoelement wires, typically by filling the space between the eIements and jacket.with powdered magnesium oside. The major deficiency of.these previous . .
thermocoupie designs was the use of a.hygroscopic mineral ~ . .
o~ide ~o insulate the metallic thermoelement wires from the WO 92/02794 PCI`/US91/05'132 metal, protective jacket. The insulative capacity of the mineral oxide was compromised by water vapor invading the .
insulative material from the surrounding atmosphere. Even a slight amount of moisture in the powdered mineral 02ide permitted formation of at least a temporary ground between the jacket and the thermocouple wires, thereby rendering the device non-functional. Over the years, this problem was tolerated, with many operators simply discontinuing use of the thermocouple and associated pyrometer for a period of time. However, with the growth in use of unmanned machinery, the constant monitoring required for computer control and computer monitoring, and the dangers posed by escessive temperatures in combustion reactions, the need for a durable and reliable thermocouple has become paramount. :
For example, use of thermocouples in internal combustion engines, particularly in monitoring eshaust gas temperatures, has become more widespread and critical. In addition to the above-mentioned grounding problem, conventional thermocouples were frequently sized to project `
deeply into the exhaust gas stream. Naturally, the metallic jackets for such elongated thermocouples were subject to considerable wear from esposure to hot and corrosive gases.
In addition, many earlier thermocouples employed tapered pipe threads for attachment to the eshaust mani~olds. Removal and replacement typically involved a cutting torch, thus requiring engine shutdown, so that possibly combustible gases in a classified location (i.g., .. , , , . ... .. , .. , ~ ....................... -: .
., ~. ~ . . -Class 1, Group D, Division 1 or 2) or other engine room were not ignited by sparks from the torch. Likewise, in the absence of a relatively permanent thermowell from which the spent thermocouple could be e~tracted, engine shutdown was reguired so that poisonous exhaust gases would not escape through the opening in the exhaust manifold formed when the old thermocouple was removed.
Accordingly, the present inventor was faced with the problems of devising a thermocouple which was substantially impervious to moisture, capable of withstanding substantial heat and vibration, less exposed to the corrosive forces within the high temperature environment, and easily removed and replaced.
Summarv and Ob;ects of the Invention:
The thermocouple which is the subject of the present invention basically comprises at least one thermoelement, a unitary ceramic insulator formed with at least one thermoelement-receiving passageway, and a unitary ceramic sheath formed with an insulator-receiving chamber.
In addition, the present thermocouple may be equipped with a metal shell formed with a sheath-receiving bore and provided with cooperative fastening-means for securing the thermocouple in an operative position. Preferably, the above-mentioned cooperative fastening means includes~
standard spark plug threads, but may also use NPT threads.
It is also preferable for the above-mentioned metal shell or - . - .~ .
~Q~&7`~ - 4 -jacket to be constructed in such a manner that a sensor end of the thermoelement e~tends into the sampling area less deeply than what has been the norm in the past.
A primary object of the present invention is to provide a thermocouple which is practically impervious to moisture in the atmosphere surrounding the apparatus into ~hich it is inserted. Another object of the present thermocouple is to be more durable and less intrusive in the ;
sample area which it monitors than was obtained heretofore.
Yet another object of the present invention is to provide a thermocouple which is readily adapted for insertion in an existing thermowell, as well as being adapted to receive an outer threaded sleeve or relatively complete cover. A ~ `;
further object of the presént thermocouple is to be readily removable from the sample area it is intended to monitor.
.. :, Brief Description of the Drawinqs:
Fig. 1 is a front elevational view of a thermocouple according to the present invention equipped with a threaded metallic outer shell;
Fig. 2 is a vertical sectional view taken along line 2-2 of Fig. 1 and particularly illustrating the manner in which the present thermocouple is constructed;
Fig. 3 is a front elevational view of a ther,mocouple according to the present invention~equipped with an elongated metal tube or thermowell; and ... . ~ -. . . . . . . .
, .. ., . ~, . . ~, , , . ................ ,: .
. . . . . ,.: . . . 7 ~ 3 ,~
Fiq. 4 is a vertical sectional view taken along line 4-4 of Fig. 3 and particularly illustrating the manner in which the present thermocouple is mounted in the tube or thermowell.
Detailed Descri~tion of the Preferred Embodiment:
As best indicated in Fiqs. 2 and 4, the present thermocouple, generally designated 10, basically comprises at least one and preferably two thermoelements 11, a unitary ceramic insulator 12 formed with at least one and preferably two relatively spaced apart thermoelement-receiving passageways 13, and a unitary ceramic sheath 14 formed with an insulator-receiving chamber 15. Prefera~ly, the thermoelsments are either iron-constantin or chromel-alumel wires, although other thermocouple alloys may be employed.
The thermoelement insulator 12 is preferably an elongated, cylindrical articlé fabricated from high purity calcined alumina oxide powder which is milled and blended with some plasticizers and flexing agents to provide an homogeneous material of ninety-six percent alumina oxide- ;-content. Other material compositions fall within the scope of the present invention which is not to be restricted to this one preferred embodiment. Typically, this alumina oxide material is e~truded to form the insulator 12, and is then sintered at elevated temperatures to form it to its final dimensions. One of the bare thermoelement wires 11 is inserted into and through each of the passageways, and a con~entional thermocouple junction 16 is provided at a 092/02794 PCT/US91/0~32 ~ 6 -sensor end of the ceramic insulator 12 adjacent to the closed end of the insulator-receiving chamber 15 of the -ceramic sheath 14.
Preferably, the oeramic sheath 14 is manufactured by those methods commonly used to fabricate spark plug insulators from high purity alumina oxide formulas. In this instance, the calcined alumina oxide powder is milled and blended with plasticizers and fluxing agents to form an homogeneous material of ninety-six percent alumina oxide ;
content. This material is then extruded or isostatically pressed into blanks. The resulting blank is then shaped to its unfired profile and dimensioned by lathe cutting or form grinding. Alternatively, the unformed alumina oxide material may be injection molded into the desired shape.
Once the ceramic sheath 14 is shaped, it is sintered under `
controlled firing conditions at elevated temperatures where it is reduced in size to the final dimensions, within standard commercial tolerances.
The thermoelement-bearing ceramic insulator 12 is then coated with a high temperature alumina ceramic cement and inserted into the ceramic sheath 14. This assembly is then cured under controlled temperature conditions to set the adhesive~ Note that fillers, such as powdery fillers -(e.g., sand, magnesium oxide) are not necessary in the assembly of the present invention. If the foregoing -as~embly is intended for use in an e~isting thermowell, then-no more needs to be done to the assembly 10-other than to apply ANSI standard colored insulation to the thermoelement '.
,,,, . . ,, ,- " , -,,.. . . .. , .,.. ~, .,,,, - -, , ~ ; . .; .,. , -.. . .
. - . : . .
- : . - : . .
W O 92/02794 PC~r/US91/05432 wires ll so that the connection to the instrumentation (not shown) will result in accurate temperature levels being monitored. Once the sensor assembly 10 is inserted into the thermowell, an externally threaded gland 18 (Fig. 4) may be screwed onto the cooperative internal threads of the thermowell in surrounding and overlying relation to an upper shoulder portion l9 of the ceramic sheath 14.
As indicated in Figs. 3 and 4, the present ceramic thermocouple 10 may be fitted cartridge-style into a stainless steel tube 20. This tube 20 may be somewhat permanent to the manifold or other housing into which it is installed and thus may constitute the above-referenced thermowell. The subject tube or thermowell 20 is formed with a sheath-receiving chamber ~1, the sensor end o which is closed. Preferably, the tube 20 is designed to project into the manifold or other chamber no more than one-quarter of the distance between opposing walls thereof.
Advantageously, the outer tube or thermowell 20 is equipped with esternal threads for cooperative engagement with a threaded coupling (not shown) on the mani~old wall. In addition, a hesagonal or octagonal head or shoulder 23 is formed on the stainless steel tube for extracting and fastening the tube to the manifold or chamber wall.
Alternatively, as indicated in Figs. l and 2, the present ceramic thermocouple 10 may be fitted înto a steel shell 23 which is hermetically sealed to the ceramic sheath 14 in a manner well known in the art of sealing a spark plug insulator to its surrounding metal shell. Preferably, the , :
q ~n~
shell is formed with standard SAE spark plug threads 24, a gasket 25 and a hesagonal or octagonal head 26. Preferably, the shell 23 is mounted on the ceramic thermocouple lO so that the sensor end 16 of the thermocouple projects at least one inch into the chamber which is to be monitored. In the case of exhaust gas temperature monitoring, the sensor end I ;-16 preferably extends less than one-half of the distance between opposing walls of the manifold in which it is mounted.
As an alternative to SAE threads 24, the shell may be provided with IS0 or DIN standard spark plug threads, as well as with NPT threads. In this manner, the subject ;
thermocouple may be replaced as easily as a spark plug and/or retrofitted into an existing threaded socket. Since the majority of prior art eshaust gas thermocouples have used one-ourth, three-eights, one-half or three-fourths inch NPT threads, it would be advantageous to employ 18 millimeter by 1.5 millimeter SAE or IS0 spark plug threads.
Preferably, a range of thread lengths would be provided, typically 12.7 millimeters, 18.5 millimeters and 2S.4 millimeters. The 18.5 millimeter length would be virtually identical to the thread length of a one-half inch NPT pipe ' ,~
thread. - 1 In addition, using TIG-welding procedures--typically !.
used in the manufacture of specialized industrial spark -plugs, the manuiacturer or o~erator may attach additional ~, ' ' ' ' ;` ' ' :' ' .
` W092/02794 PCT/VS9l/05432 , 9 ~ 6~
threads to the shell 23, thereby allowing for attachment of various hazardous location protective heads (not shown) for suppressing sparks and/or corrosion.
Thus, the present invention provides a thermocouple which is readily adapted for use in a variety of applications, either in combination with a metal tube or thermowell projecting into the area whose temperature is to be monitored or in association with a threaded metal shell :
similar in construction to those employed with spark plugs. -The present ceramic thermocouple 10 is preferably of cartridge design for ready replacement and for relatively permanent attachment to a spark plug-type threaded metal shell 23. ~y constructing the present thermocouple 10 from a unitary alumina oside insulator 12 which houses the thermoelements and a surrounding unitary alumina oxide sheath 14, the present invention is able to withstand the forces at work in the chamber being monitored and in the surrounding environment which tends to cause conventional thermocouples to ground out.
Claims (11)
1. A thermocouple assembly to be used within an apparatus to be monitored, comprising:
a unitary ceramic insulator formed with at least one thermoelement-receiving passageway;
at least one thermoelement at least partially disposed within said passageway; and a unitary ceramic sheath formed with an insulator-receiving chamber, within said chamber said unitary ceramic insulator is tightly secured such that said sheath and said insulator are void of any powdery fillers along the entire length of said sheath.
a unitary ceramic insulator formed with at least one thermoelement-receiving passageway;
at least one thermoelement at least partially disposed within said passageway; and a unitary ceramic sheath formed with an insulator-receiving chamber, within said chamber said unitary ceramic insulator is tightly secured such that said sheath and said insulator are void of any powdery fillers along the entire length of said sheath.
2. The thermocouple according to Claim 1, wherein the ceramic insulator is axially elongated and is provided with a sensor end at which a terminal portion of the thermoelement is disposed.
3. The thermocouple according to Claim 2, wherein the insulator-receiving chamber of the ceramic sheath is axially elongated and is formed with a closed end adjacent to which the sensor end of the insulator is disposed and with an open end out of which the insulator and thermoelement project.
4. The thermocouple according to Claim 3, wherein a metal thermowell is formed with a closed end which projects into the apparatus to be monitored, said ceramic sheath being adapted to be mounted in the thermowell with the closed end of the insulator-receiving chamber disposed adjacent to the closed end of the thermowell.
5. The thermocouple according to Claim 3, which includes a metal tube having a closed end and cooperative fastening means for securing said tube to a wall portion of the chamber to be monitored.
6. The thermocouple according to Claim 5, wherein the sheath is adapted to be inserted in the tube with the closed end of the insulator-receiving chamber disposed adjacent to the closed end of the tube.
7. A thermocouple assembly adapted to monitor a sample area within a manifold or other apparatus comprising:
a unitary ceramic insulator formed with at least one thermoelement-receiving passageway;
at least one thermoelement at least partially disposed within said passageway;
a unitary ceramic sheath formed with an insulator-receiving chamber, wherein said unitary ceramic insulator is tightly-secured within said chamber; and a metal thermowell-relatively permanently installed in said apparatus, said thermowell formed with a sheath-receiving bore wherein said unitary ceramic sheath may be inserted into said bore and said unitary ceramic sheath of a cartridge style in that said sheath may be removed from said thermowell and replaced with another sheath while said thermowell remains installed within said apparatus.
a unitary ceramic insulator formed with at least one thermoelement-receiving passageway;
at least one thermoelement at least partially disposed within said passageway;
a unitary ceramic sheath formed with an insulator-receiving chamber, wherein said unitary ceramic insulator is tightly-secured within said chamber; and a metal thermowell-relatively permanently installed in said apparatus, said thermowell formed with a sheath-receiving bore wherein said unitary ceramic sheath may be inserted into said bore and said unitary ceramic sheath of a cartridge style in that said sheath may be removed from said thermowell and replaced with another sheath while said thermowell remains installed within said apparatus.
8. The thermocouple according to Claim 7, wherein the insulator-receiving chamber of the ceramic sheath is formed with a closed end and wherein the metal shell is mounted on the ceramic sheath in such a manner that the closed end of said sheath projects into the sample area to be monitored less than one-half of the distance between opposing walls of said sample area.
9. A method of making a thermocouple, said method comprising:
forming a unitary ceramic insulator with at least one passageway extending axially therethrough;
mounting a thermoelement in the insulator passageway;
forming a unitary ceramic sheath with an insulator-receiving chamber; and securing the ceramic insulator within the insulator-receiving chamber of the ceramic sheath in such a way that said thermocouple is practically impervious to moisture and is void of any powdery fillers throughout the entire length of said ceramic sheath.
forming a unitary ceramic insulator with at least one passageway extending axially therethrough;
mounting a thermoelement in the insulator passageway;
forming a unitary ceramic sheath with an insulator-receiving chamber; and securing the ceramic insulator within the insulator-receiving chamber of the ceramic sheath in such a way that said thermocouple is practically impervious to moisture and is void of any powdery fillers throughout the entire length of said ceramic sheath.
10. The method according to Claim 9, which further includes forming a thermoelement junction at one end of the ceramic insulator, forming the insulator-receiving chamber of the ceramic sheath with a closed end, and securing the ceramic insulator within the ceramic sheath with the thermoelement junction end of said insulator disposed adjacent to the closed end of the insulator-receiving chamber.
11. A method of making a thermocouple assembly which is adapted to monitor a sample area within an apparatus, said method comprising:
forming an insulator with at least one passageway extending axially therethrough;
placing a thermoelement in said insulator passageway;
forming a sheath with an insulator-receiving chamber;
securing said insulator within said insulator-receiving chamber of said sheath; and forming a metal thermowell with a sheath-receiving bore, said thermowell adapted to be relatively permanently installed within said apparatus to be monitored, said assembly of a cartridge style such that said sheath containing said insulator and said thermoelement is readily removable and replaceable within said thermowell while said thermowell remains installed within said apparatus.
forming an insulator with at least one passageway extending axially therethrough;
placing a thermoelement in said insulator passageway;
forming a sheath with an insulator-receiving chamber;
securing said insulator within said insulator-receiving chamber of said sheath; and forming a metal thermowell with a sheath-receiving bore, said thermowell adapted to be relatively permanently installed within said apparatus to be monitored, said assembly of a cartridge style such that said sheath containing said insulator and said thermoelement is readily removable and replaceable within said thermowell while said thermowell remains installed within said apparatus.