CA2001632A1 - Prevention of copper dissolution during cyanidation of gold ores - Google Patents

Abstract

ABSTRACT OF THE DISCLOSURE

PREVENTION OF COPPER DISSOLUTION DURING CYANIDATION
OF GOLD ORES
A process for treating copper containing precious metal ores prior to cyanidation and recovery of the precious metal eg gold. The process involves addition to the ore before or after milling of a water soluble or water dispersible surface active agent in the form of a fatty alkyl amine preferably an ethoxylated fatty alkyl amine. The agent reduces the high cyanide consumption, which is caused by copper dissolution, by passivating the mineral surface.

Description

Z8~.~632 : ~
Case 7071(2) PREVENTION OF COPPER DISSOLUTION DURING CYANIDATION
OF GOLD ORES
: . ' This invention relates to a method for treating ;~
copper-containing precious metal ores, particularly gold ores from which the precious metal i9 to be recovered by cyanidation, to reduce the deleterious effect of the copper on the overall precious metal winning process.
Precious metals, particularly gold, can be recovered from milled ores containing them by treatment with an alkaline cyanide solution, the precious metal going into the solution as a cyanide salt. In the case of gold the reaction can be represented as~
4Au ~ 8NaCN + 2 + 2~2 --> 4NaAu(CN)2 + 4NaOH
The precious metal can then be recovered from the solution by precipitation onto zinc dust or by adsorption onto activated carbon.
The ore may, however, contain other metals, e.g. iron, copper, ~-nickel, and zinc, which are also liable to form cyanide salts. Such 15 competition can complicate and increase the cost of the precious ;~
metal winning process in a number of ways. It can reduce the amount of precious metal recovered, increase the consumption of cyanide, and reduce the purity of the recovered precious metal. The barren cyanide solution (i.e. the solution remaining after the precious metal has been recovered) is normally recycled to maximise cyanide ~` utilisation and it may be necessary to bleed off a portion of this recycle stream to prevent a build-up of copper in the system. This bleed stream then has to be treated to remove the copper before it can be re-used or, if it is to be disposed of, it has to be treated to meet the stringent limits for effluent disposal.

':' ~.

C ~ .: . : . : , . :

Existing methods for dealing with the problem of copper all involve pretreatment of the ore to remove copper before cyanidation. This can be done either by floating off the copper mineral (for example, chalcopyrite) or by acid or alkaline leach~ng. This, of course, adds to the overall cost of the process.
The present invention is based on the finding that the deleterious effect of copper containing minerals can be reduced by a form of passivation pre-treatment during or prior to cyanidation. ;
The copper is not removed but passes through the cyanidation 10 process with a reduced tendency to form cyanide complexes. ~ ~
According to the present invention there is provided a process -for the treatment of precious metal containing ores, which contain cyanide consuming copper minerals, during or prior to cyanidation and recovery of the precious metal, the process comprising adding to the ore during or after milling a water-soluble or water-dispersible fatty alkyl amine. -The fatty alkyl amine should be one of or a blend of primary, i~
second or tertiary amines although quaternary amines may be used in ;~
blends with one or more primary, secondary or tertiary amines.
Preferred surface active agents are ethoxylated fatty alkyl amines. Examples include compounds of the types:-~(cH2cH2o)xH ~- ;
(i) R - N
(CH2CH20)yH
~ (CH2CH20)XH
or (ii) R - N -- CH2CH2CH2N \ ` ~ ~
(CH2CH20)2H (CH2CH20)yH ,,~:,,. ~."-.,.`, where x and y are integers and preferably x + y - 2 ~ -The quantity of surface active agent required will depend on the amount of cyanide con~uming copper minerals in the ore and the optimum quantity to reduce copper dissolution during cyanidation at ;-~
a reasonable cost can readily be determined by experiment. The quantities can, however, be relatively modest in relation to the amount of ore processed, e.g. from 0.01 - 1 kg of surface active agent/tonne of ore.

~' ' :~ ' ~0C~1632 .

The surface active agent should be water-soluble or dispersible so as not to complicate the cyanidation process which uses an aqueous solution. .' Precious metal containing ores are normally milled prior to cyanidation to encourage precious metal extraction. Typical particle sizes for the milled ore may be from 1 to 500 micronA. The surface-active agent may be added to the ore before or during this milling process or it may be added to the milled ore with suitable agitation to ensure good contact between the copper mineral and the surface active agent. The surface active agent is added as an aqueous solution or dispersion. With addition of agent during or after milling an excess of solution may be used and the excess subsequently removed by filtration, but it has been found that this complication is not essential and that satisfactory results can be obtained simply by grinding or mixing the ore with the required amount of solution to give the required quantity of agent per tonne of ore. If it is required to grind the ore with cyanidation agent then the presenee of the surface aetive agent will not affeet the gold extraetion. -The milled ore eontaining the surfaee aetive agent ean be proeessed by eyanidation in eonventional manner. No ma~or ehanges in the eyanidation technique are necessary as a result of the presenee of the agent. In addition to the benefits of redueed eopper extraetion and lower eyanide eonsumption, there is an -~
inerease in the solids settling rate indicating that the surfaee aetive agent improves partiele aggregation and also the possibility of inereased gold extraetion.
The treatment proeess is not limited to the use of a milling stage but also eould be used during a heap leaehing proeess.
The invention is illustrated by the following Examples.
Table 1 shows a range of surface active agents used to treat -precious metal containing ores which also contain cyanide consuming ~-~ eopper minerals. The Ethomeen reagents are a group of ethoxylated --alkyl amines of strueture 2~163Z

~(CH2CH20)XH
R-N : :
(CH2CH20)yX ., where x ~ y - 2,5 and 15 for reagents designated 12,15 and 25 respectively ie in order of increasing ethoxylation and were supplied by Akzo Chemie. Ethoduomeen and Armeen 0 were also supplied by Akzo Chemie and the Duoteric reagent was supplied by ABM ;~
Chemicals. All the reagents were tested as a 0.1~ aqueous solution/dispersion with the exceptions of Armeen 0 ant Duoteric.
Armeen 0 was prepared as an isopropanol (10%)-water dispersion.
Duoteric H12 is supplied as an aqueous isopropanol solution and was ~ -diluted with water to the required concentration. ~ -The ores used in the tests were sulphidic gold containing ores from the Hope Brook mine in Canada. The copper content of the lS samples ranged from 0.42 wt % (B /M) to 0.05 wt % (HB78). The sample used in Table 2 was B /M of copper content 0.42 wt ~ as chalcopyrite. Table 3 shows assays of the ma~or elements in the ore samples.
All the ore samples were wet ground in a 5L rod mill at 60% wt solids to give a particle size of 80% less than 75 microns. The samples were milled with and without added surface active agent as ~ -shown in Table 2.
With each sample the mill was discharged into a glass bottle with enough water to reduce the pulp density to 30-35% wt solids.
25 The pH was ad~usted to 11 to 11.5 by the addition of calcium hydroxide, sodium cyanide (equivalent to 1.8 kg/t ore) atded and the ` ~
bottle agitated on rollers for 72 h. The pulp was then filtered and -~ -washed, the filtrate and washings being analysed for gold and copper by atomic absorption spectroscopy. Residual free cyanide in the solution was analysed using an ion selective electrode. The residue from the test was dried and analysed for gold by fire assay, the percentage gold extraction being based on the solution and residue ;
assays.
It will be seen that all of the surface active agents increased --~
- 35 gold extraction, reduced copper extraction and reduced sodium ' "'~

- Z0~1632 cyanide consumption. The reduction in sodium cyanide consumption was Breater than that attributable to the reduction in copper extraction. While not wishing to be bound by any theory, this appeared to be partly due to reduced thiocyanate formation, possibly resulting from coverage of the copper sulphide surfaces with the agent. ;
The improvement in gold extraction may also be, at least in part, due to the surface active agent passivating a possible gold cyanide (Au(CN)2-) adsorbing component of the ore. `~
It appears that the copper passivation i9 improved with lower degrees of amine ethoxylation and longer alkyl chain lengths.
However, amines having longer chain lengths tend to be more viscous and hence less easy to pump and handle.
Also non ethoxylated amines such as Duoteric H12 and Armeen 0 are effective in copper passivation and at higher concentrations are of similar effectiveness to ethoxylated amines.

.:'`
, . .

::

_ 6 ~a ~ ~ ~ a ~
~ ~ 3 ~ 3 ~
~ ~ o o o o o o o ~ o ¢ o . ~ ~
~ ~ .~ ..
.~
,~ d a ~ . '' - -- . . . . . . .
~0 L~
~ : ~:
. ~ ~ ~ ~ ~ ~ ~~ ~ ~ ~ .
~, ~ 0 co `o , . ,".
~`o ooo --- ~
s ~ ~ --p p -I ~- ~ z z, ¢1 ~ 0 ~ -c~o ~ ~ ~

c c ~30 e 0 3 3 3 ~ e :
x ~ , e a~ o o o ~ ~ o L~ L~ ; ' : :' Ox ~ x o o ~,a ~ ~, ~ TJ c ~ e ~ ~ ~
~ ~ ~ ~ ~ -z ~ ~ e _I ~ ~
oX` Ox O 0~ 0 ~ Ox O Z O ~ ea ~o ~ ~ ~ z -I a ~ ~ ~ O ~ p~ Z ~ ~ ~ o ,~
_ ~ ~
c~ o : ~.
_ _ ~ _ _ c~ _ ~:
~ O ~ C.
ze a a a a a ca a a ~o3 ,~, a~
~ e ~ 8 e e ~ a u E~ ~

:-:: :. :-; ~: :.::
. ~:::::, :: . ~, : ~:

~ _ ._ _ ~z e ~ ~ O O ~ ~ :
Z ~ ~ _ O _ O O _ _ O
.__ ._ ~ ' e ~ ~ :
O O O O O O O
_ .

~ I ~ U~ n I = O

o o o o o o I ~

a~ o u- o u~ CD
S~ ~ ~ _ ~ _ ~ ~ e ' ~ :
O ..~ U~ 0 ~
* ~ 3 ~
_ ~ _ _ _ A , C

C _ ~D ~ ~ E ~ ~ ~ ~ ' ~ a~ ~ -- ~ _ O I`
Y o 4 o ~ o o O O o e O O ~ Z ~ ~ ~ e O' e ~ Z t, e : : :
~ Z ~
o ~ C~ .~ . .. -~ o o I ,, ~'' ~. '' :: :
;~:00~632 ¦ TABLE 3 ': ' MAJOR ELEMENTS IN HOPE BROOK ORE SAMPLES
S ' -, ~ '.', % wt ¦ El-=-Gt or GroG7 ~ GB/M ¦ GB66 ¦ BB7B ¦ GB ROM ¦

Au3 tg/t~ 2.09 2.54 0.96 8.25 Cu 0.42 0.11 0.05 0.16 Fe 6.2 5.2 4.4 4.7 2 1.2 3.9 3.0 5.0 Si 34.7 32.2 32.2 37.3 `~
Al 2.1 1.9 2.4 0.5 __ ;~
Chalcopyrite4 1.20 0.31 0.14 0.46 Pyrite 2.1 7.3 5.6 9.3 :
Non-sulphide iron 4.9 1.7 1.75 0.2 ',~" ~ '' Notes: - ND - not determined ;~
1 - determined by AAS unless otherwise stated 2 - determined by combustion ;~

3 - determined by Fire Assay -~. 4 - sssuming all copper present as chalcopyrite .~ -`
and remaining sulphur present as pyrite - :

Claims (9)

1. A process for the treatment of precious metal containing ores, which contain cyanide consuming copper minerals, during or prior to cyanidation and recovery of the precious metal, the process comprising the contacting of the ore with a water soluble or water dispersible fatty alkyl amine.

2. A process according to claim 1 in which the fatty alkyl amine is a primary, secondary or tertiary fatty alkyl amine.

3. A process according to claim 1 in which the fatty alkyl amine is a blend of two or more of a primary, secondary, tertiary or quaternary amine.

4. A process according to claim 1 in which the amine is an ethoxylated fatty alkyl amine.

5. A process according to claim 1 in which the fatty alkyl amine is a coco-, tallow- or oleyl-amine.

6. A process according to claim 1 in which the precious metal containing ore is a gold containing ore.

7. A process according to claim 1 in which the ore is milled after contacting it with the fatty alkyl amine.

8. A process according to claim 1 in which the ore is milled before contacting it with the fatty alkyl amine.

9. A process according to claim 1 in which the cyanide consuming copper minerals is chalcopyrite.