CA2000572A1

CA2000572A1 - Pultrusion system for condensation resin injection

Info

Publication number: CA2000572A1
Application number: CA002000572A
Authority: CA
Inventors: Frank C. Beall; Johan D. Koppernaes
Original assignee: Weyerhaeuser Co
Current assignee: Weyerhaeuser Co
Priority date: 1988-10-13
Filing date: 1989-10-12
Publication date: 1990-04-13
Also published as: ZA897788B; WO1990003877A1; EP0403607A4; AU4485989A; EP0403607A1; JPH04502889A

Abstract

PULTRUSION SYSTEM FOR CONDENSATION RESIN INJECTION
ABSTRACT
A composition, apparatus and method for making resin bonded composite pultruded products using a thermosetting resin is disclosed. The resin comprises a condensation resin which has a high solids content.
A pultrusion system comprises reinforcing material supply, a pultrusion die adapted to be heated, injection device for injecting resin into the die, and pulling device for drawing product through the die.
The method comprises supplying strands of the reinforcing material to the die and grasping the strands with the pulling device, injecting a condensation-type monomer resin into the die to impregnate the reinforcing material within the die, and pulling the resin-impregnated strands through the die at a rate that permits the resin to condense to an essentially cured state by the time the composite product is withdrawn from the die. The die is a modular die such that various sections of the die may be selected as desired to change process parameters.
The die is divided lengthwise into a plurality of regions or sections, typically comprising an entry section, a resin injection section, a transition section and a profile section, which are joined together to create the desired die characteristics.
Also disclosed is an adaptation die to convert a conventional non-injection die into an injection die.
The adaption die comprises an entry section, a resin injection section and a transition section adapted for connection to the conventional die.

Description

PULTRUSION 8Y~TEM FOR CONDEN8ATION RE~IN INJEC~ION

BACKGROUND OF THE INVENTION
The present invention relates to a composition and method for making pultruded products using a thermosetting resin which is injected into a forming die. In particular, the resin is a condensation-type monomer which is injected into a modular die with variable heating zones and cross-sectional configurations.
Pultrusion is a process for continuously forming reinforced plastic materials having a uniform cross-sectional profile. The term "pultrusion" is a hybrid which combines the words "pull" and "extrusion"
to designate that the product is literally pulled through a forming die. In its most usual form, pultrusion involves feeding a plurality of reinforcing filaments, such as fiberglass roving strands, with or without additional plies of glass mat of appropriate width, through a resin bath and a pultrusion die. The pultrusion die is typically heated to polymerize the resin and the cross-sectional shape of the die's exit orifice generally determines the shape of the finished product. The typical resin in the resin bath is a thermosetting addition-type monomer. Alternatively, the reinforcing filaments are drawn directly into the die where resin is injected directly. As the product is pulled through the die and out of the exit orifice in the end of the die, the resin is either cured, or very nearly cured. The endless product so formed is then cut to appropriate length. Many variations of this general process have been developed as the technology has matured. A general background on pultrusion is found in an article by Ewald, Modern Plastics Encyclopedia, pp. 378-84, McGraw-Hill, Inc., New York (1988).

Pultruded prod~cts have unique physical properties, such as being electrically insulativP, thermally insulative and corrosion resistant, along with having high specific strength and relatively unlimi~ed length. Pultruded products are therefore used in a great variety of applications. In many instances they have replaced metallic construction materials, particularly ~hose used in highly corrosive environments. Structural beams, floor gratings, handrails, ladders and many similar products are now made using a pultrusion process.
Reported commercial pultrusion resins are comprised substantia]ly of addition-type monomers, which produce no water or other by-products during polymerization. An experimental resin of the condensation type (an acid-catalyzed phenolic) has a sufficiently low viscosity for use in a resin-bath pultrusion system. Although this resin has a rapid cure rate, it has several undesirable side effects, such as severe corrosion of the steel dies and residual acidity of the final product. In addition, acid-catalyzed phenolics must be mixed immediately before use because of their relatively short pot life.
The inherent instability of the acid-catalyzed resin may also cause variability in the product.
An alternative approach is to use neutral or basic phenolics that would not have these disadvantages. However, neutral or basic phenolics have high viscosities and require relatively high curing temperatures (approximately 150 to 200C).
This high viscosity makes the resins very difficult to use in open~bath pultrusion systems, where low viscosity is required to obtain proper wetting of the fiberglass reinforcing strands. In addition, there are processing and product advantages in using resins with the highest possible solids content. However, ~o~

the viscosity of the phenolic resins increases directly with increased solids content, thus making high solids content resins hard to utilize in open bath systems.
Two general types of dies can be used in pultrusion -- a conventional profile die ("profile") and a resin injection die ("injection"). The profile die is used in combination with open resin bath systems, whereas the injection die has resin injected directly into the die. In general, both of these die types are custom made of steel, which is often chrome plated, and are ver~ costl~ to manufacture. Different die configurations are required depending on the type of resin used, curing rate, final product structural configuration, cross-sectional profile, etc.
A paper entitled "The Development of In-Situ Pultrusion for Polymeric Composites" presented by H.H.
Hsu et al. at the 33rd International SAMPE Symposium, March 7-10, 1988 discusses the use of a laboratory resin injection system for addition polymerization (i.e., epoxy). The resin injection die described is similar to that manufactured by Nordic Supply AS, Aalesund, Norway, which has been available commercially for approximately 20 years. The process described is similar to that for mixing and injecting acid-catalyzed phenolics, which has been practiced at Nordic Supply since around March, 1987.
Mixing/injection equipment for such resin injection has been manufactured by several companies.
In Hsu et al., an epoxy resin with filler is mixed with a hardener and an accelerator in the die head. A preheating stage is used to reduce the viscosity of the resin sufficiently for mixing and injection while keeping the temperature below that of initial reaction. The temperature increase is also 3~97~

needed to reduce the viscosity sufficiently for penetration of the fiberglass.
The process of Hsu et al. is also disclosed in Brazilian patent No. ~70~536 to Tong, which shows a continuous process wherein epoxy r~sin and hardener are continuously mixed and then passed without contact with air into a die where it contacts reinforcing fibers fed through the die. The fibers are impregnated with the resin-hardener mixture and shaped by the dieA ~owever, the patent does not discuss the use of an injection system for use with condensation-type resins.
It is an object of the present invention to overcome the problems associated with acid-cured phenolics.
It is also an object of the present invention to provide a neutral or basic phenolic resin which can be easily accommodated in in~ection dies.
It is a further object to provide an injection system which can be utilized with neutral or basic phenolic resins.
It is also an object of the present invention tG provide a die for processing a condensation-type resin.
It is also an object of the present invention to adapt conventional pultrusion dies to permit resin injection pultrusion with any addition or condensation resin.
It is a further object to provide a modular ~ie in which the operating parameters of the die, such as cross-sectional profile, length, temperature and injection site, can be easily changed for varying tne process parameters and producing differing products, Q~

thus reducing machine downtime, die cost and experimentation risk.
A further object of the present invention is to permit on-line experimentation and optimization of die length, taper, volume and other die parameters in die development to match to processing and product needs (speed, shrinkage, density, product diameter, etc.).
It is a further object of the present invention to allow different construction materials to be used for the various sections. This can result in cost savings, in addition to time savings during fabrication of the sections, and flexibility in means of heating.
These and many other objects of the present invention will become readily apparent to those skilled in the art upon reading the following detailed description.

SUMMARY OF THE INVENTION
The present invention comprises a method for making a resin bonded composite pultruded product and the resin which is used. The method uses a pultrusion system comprising a supply of reinforcing materials, a heated pultrusion die, injection means for injecting the resin into the die and a pulling mechanism for drawing product out of the die~ The method comprises supplying strands of the reinforcing material to the die and grasping the strands with the pulling mechanism. A monomeric resin is injected into the die to impregnate the reinfcrcing materials within the die. The resin-impregnated strands are drawn through the heated die with the pulling means at a rate that permits the resin to condense to an essentially cured state by the time the composite product is withdrawn from the die. If desired, the resin is heated before ~a~ s-~

injection into the die to reduce its viscosity to facilitate injection and impregnation into the reinforcing material.
The resin of the present invention is a condensation-type resin. ~he phenolic resin disclosed is a typical condensation monomer that has been formulated to eliminate the acid-catalyzed phenolic problems. Ths resin is constituted to have a high solids content and is essentially neutral. Curing is effected by a direct condensation reaction at elevated temperature without using an acid catalyst.
The die of the present invention is a modular die such that various sections of the die may be selected as desired to change process parameters for the formation of the finished product. The die is divided lengthwise into a plurality of discrete sections, typically comprising an entry section, a resin injection section, a transition section and a profile section. Each of the sections may have different heating capabilities and different configurations, such as cross-sectional profile, length, sloped areas, etc. and are joined together to create the desired die characteristics.

FIG. 1 is a schematic diagram showing a pultrusion system for use with the present invention.
FIG. 2 is a graph showing the relationship of viscosity to temperature for several types of resins.
FIG. 3 is a cross-sectional view of a modular injection die in accordance with the present nventlon.
FIG. 4 is a cross-sectional view of another modular injection die in accordance with the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

GENERAL PUI,TRUSION SYSTEM
The present invention is utilized with a general pultrusion system, such as shown in FIG. 1.
The pultrusion system includes a source of reinforcing materials 1, such as fiberglass reinforcing strands 2.
The strands 2 are fed through a former 3 in which the individual strands 2 are ~athered to form a bundle 4 which is fed into a pultrusion die 10. A
thermosetting resin from a resin source 5 is injected into the die by injection means 6, such as a pump or other suitable injection system. The bundle 4 of reinforcing strands are impregnated with the resin in the die 10, which may be provided with an external source of heat 3 if desired. The resin is either cured or partially cured within the die 10 to form a finished composite product 11 of resin and reinforcing materials.
A pulling system, such as a pair of pullers 12, is provided to pull the finished product 11 out of the die 10. The resin-impregnated bundle 4 is drawn through the heated die 10 by the pulling means 12 at a rate that permits the resin to condense and harden to an essentially cured state by the time the composite product 11 is withdrawn from the die 10. Dies of various sizes, internal cross-sectional areas, length, etc. may be used depending upon the type of resin used, the finished product re~uirements, and other parameters.
A post-cure heater 13 may be provided, if desired, to heat the finished product 11 and complete the resin cure. A cutter 14 cuts the finished product into pieces of the desired length.

?~31~ri'~

RESIN
The resin used in accordance with the present invention is a condensation-type monomer resin. The resin is a neutral or basic resin to overcome many of the problems associated with acid-catalyzed resins.
A condensation resin undergoes condensation or step-reaction polymerization in which two polyfunctional molecules react to produce one larger polyfunctional molecule, often with the elimination (condensation) of small molecules such as water. In contrast, an addition resin undergoes addition or chain-reaction polymerization which involves chain reactions, typified by vinyl monomers in which a free radical reacts to open the double bond of a monomer and add to it, with an electron remaining unpaired.
Addition reactions typically produce a long chain in a relatively short time.
The condensation resin used in accordance with the present invention, can be activated by heat, either alone or in combination with an alkaline catalyst. In general, the presence or lack of a catalyst has an effect on the temperature required to cure the final product. The alkaline catalyst can be any one of a number of basic materials such as calcium carbonate or caustic soda.
In general, it is desirous to use a resin with a high solids content so that fewer byproducts are produced by condensation polymerization.

RESIN INJECTION DIE
A modular die 20 in accordance with the present invention are shown in FIG. 3. The die generally has four discrete regions or sections: entry section 22, resin injection section 24, transition section 26 and profile section 28. The sections are ~ )Q'3~

aligned s~ch that a continuous axial bore 30 extends through the die 20.
In opPration, reinforcing strands (not shown) are threaded through the bore 30 and a suitable pulling means (not shown) is provided for pulling the strands and finished product through and out of the die 20. The sections are connected together by a suitable means (not shown) adapted to permit rapid replacement of any section with a minimum of machine downtime. Such suitable means may include external bolts, cla~ps, frames, etc.
The length, bore size and shape, and other dimensions of each of the regions or sections may be varied depending upon the process parameters required, the finished product's characteristics, the type of resin being used, etc. The dimensions and shape of the die may be somewhat different depending upon whether the resin is an addition resin (such as polyester, vinyl ester, epoxy, or methyl methacrylate) or a condensation resin (such as phenol formaldehyde, polyurethane, or polyamide). Much of this difference can be attributed to the polymerization process itself and generation of byproducts from the condensation resins. For example, at any given time during polymerization, addition resins have two distinct chemical species, monomer and polymer, as a consequence of the rapid growth of a polymer chain after initiation of polymerization. Polymerization of condensation resins, also known as "step-wise polymerization," shows a gradual growth in degree of polymerization. Because of this, the monomer disappears early in the process through the formation of dimers, trimers, etc. and most of the water produced by condensation is released at that time.
The characteristics of the die which are affected by the reaction differences between addition and a~

condensation resins will be explained as the various sections are discussed.
Entry section 22 has an intPrnal bore 30A with an inlet opening 32. The inlet opening 32 is typically sized slightly smaller than the rest of the bore 30A to compress the reinforcing strands tightly together, thereby sealing the opening 32 and preventing leakage of resin from the die 20. If desired, the entry section 30A is also cooled to minimize backflow of the resin out of the die 20. The entry se~tion 32 helps to maintain the orientation of the reinforcing strands as they enter the die 20. The size of the inlet opening 32 may be modified to allow changes in the amount, size, and type of reinforcing strands being fed through the die 20 or the degree of compression of the strands. The size of the inlet opening 32 also depends upon the resin pressure in the die 20.
The resin is injected into the bore 3OB of the resin injection section 24 through a suitable injection port 34. Most addition resins are premixed with suitable catalysts before being pumped into the resin injection section 24. The resin is typically injected under pressure to assure proper penetration of the reinforcing strands. During injection, the applied pressure during pumping of the resin is maintained at a level sufficient to assure full penetration of the fiberglass strands and depends somewhat on the machine speed ~nd resin curing rate.
Typical injection pressures are in the range of about 30 to 100 psi.
If desired, the resin may also be heated, to a temperature below the point of polymerization, to decrease its viscosity and assist in injection and wetting. The relationship between resin viscosity and temperature is shown in FIG. 2 for various 7'~

thermosetting resins, including a low solids phenolic resin, a high solids phenolic resin and a polyester resin. The resin viscosity at the time of wetting should be less than about 200 cp for adequate penetration and wetting of the reinforcing strands.
If desired, an external resin preheating process step may be added. Generally, the resin may be heated to a temperature above ambient for injection, up to a temperature of around 60C.
However, external preheating is often a highly unreliable process because of resin precuring within the heated lines and necessity to frequently purge and clean the system. Resin pressurization has a critical role in resin penetration (also affected by resin viscosity), volatilization of gases from the resin, and backflow of resin through the entry section 12.
To lower the resin viscosity, the resin injection section 24 is typically heated to heat the resin being injected to achieve proper reinforcing strand penetration. The die is typically heated to a temperature of at least about 180C. A greater degree of heating may be required to reduce the viscosity caused by the high solids content which are typical of neutral or basic condensation resins. Other sections of the die, such as the transition section 26 and the profile section 28 may also be heated to assist resin gelling and curing.
Heating of the die may be accomplished in a number of ways depending upon the type of material from which the die is constructed. In some sections, particularly the profile section 28, it may be desirable to fabricate the section from a material which would permit transmission of ~lectromagnetic waves through the die for curing the resin. Such materials include ceramics, glass, and plastics. In a typical configuration, the resin injection section 24 is made of metal, permitting the outer surface of the section to be heated by direct contact with conventional heating elements and the heat conducted through the metal to the resin.
The size and shape of the resin injection section 24 depends on the amount and type of reinforcing fibers and resin being used. The cross-sectional diameter of bore 30B of the resin injection section 24 generally increases in the direction of product travel to permit some "springback" or separation of the reinforcing strands for improved penetration and wetting by the resin.
The transition section 26 has a hollow bore 30C which connects the bore 30B of the in~ection section 24 to bore 30D of the profile section 28. The cross-sectional area of the bore 30C is generally tapered down in the direction of product travel, causing excess resin to be squeezed out of the reinforcing strands. Polymerization may be initiated in this section, but for most addition resins, the resin solution remains primarily monomer.
The transition section 26 of the die 2~ has distinctly different function when condensation polymers are being used. Whereas the transition section 26 for addition resins is adapted primarily to squeeze out monomer, the section 26 acts as a compression section for condensation resins to squeeze out resin, reduce final shrinkage, and control directional movement of reaction gases. The taper of the transition section 26 can be matched to the shrinkage characteristics of the condensation resins.
The resin injection section 24 and the transition section 26 are most likely to be adjusted for this optimization. If desired, for some processes, these two sections can be combined as a single modular section.

~?t?~

Most of the polymeriæation and cure of the addition-type monomers occurs in the profile section 28 which has a hollow bore 30D and an exit orificQ 36.
The polymerization reaction is itself exothermic which helps accelarate polymerization due to several types of free-radical initiators that decompose at the higher temperature levels produced during the polymerization process. If desired, the profile section 28 may also be heated to accelerate polymerization and cure of the final product.
Typically, this section is heated to a temperature which is above the temperature of the injection section 24.
The cross-sectional area and length of the bore 30D may be selected so that the peak temperature of the reaction exotherm occurs at an intermediate position along the length of the bore to assure a suitable degree of curing when the product exits through exit orifice 36. The bore 30D may be uniform in cross section or tapered in the direction of product travel, depending on the degree of shrinkage of the resin as it cures. In addition, the exit orifice may be shaped to form product of any desired shape, such as square, rectangular, round, etc.
FIG. 4 shows another modular die 40 in accordance with the present invention. The die 40 comprises an inlet/resin injection transition section 42 and a separate profile section 44. The operation of the die 40 is similar to the operation of die 20.
The inletlresin injection transition section 42 basically comprises an "adaptation" die which may be connected to a conventional non-injection die (in essence, profile section 44) by suitable means, such as clamps, bolts, etc., to convert the conventional die to a resin injection die.

't'~

Tn another embodim~nt of the present invention, the sections are further segmented, such as by dividing a section about the longitudinal axis of its bore 20. This segmentation allows individual sections to be replaced to change the die configuration without restringing the reinforcing strands through the entire pultrusion apparatus.

RESIN TESTS
10 Tests 1 and 2 were run using a "polyester design" injection die for 0.975 cm rods on a standard pultrusion machine. Fiberglass roving was used to obtain about 70% glass by mass.
Base case resin:
Phenolic resole Solids: ~0 to 85% (by mass~
Viscosity at 25C: 10,000-20,000 cp pH at 25C: 6.0 to 7.0 Test 1. The Base Case resin was run at two resin preheat temperatures (40, 65C) and die temperatures of 180 and 200C with strand speed of from 4 to 2~ cm/min. The product was analyzed for degree of cure and shrinkage. The degree of cure was considered acceptable at 80%, which occurred at 18 cm/min at 180C and 24 cm/min at 200C. Shrinkage varied between 2.9 to 5.1% in area.
Test 2. The Base Case resin was mechanically injected into the die at room temperature without preheating. Injection pressure ranged from 30 to 100 psi, with other variables the same as in Test 1~
Material was pultruded satisfactorily with complete penetration of the resin into the fiberglass strands at all pressures.
Test 3. Three series of tests were made using phenolic resin and one series of tests was made using t~

a polyester resin~ The results of the tests are summarized in TABLE 1.
A11 of the runs of this test were made using an experimental segmented condensa~ion resin die having three sections: entry, injection~transition, and profile. The upper half of the die was segmented;
lower half was a single part to facilitate experimentation. The product profile was rectangular in cross-section with dimensions of 9 by 32 mm. The total length of the die was 1 m. The phenolic resin was the base case resin used above. Polyester resin was commercially-available (Advanced Coatings, Boston, MA) and unfilled. The fiberglass used was the same as in previous runs and consisted of 72 strands, which was the equivalent of 50% volumetric loading of fiberglass. The die was heated using eight contact strip heaters, two pairs at each of the top and bottom of the die, downstream from the resin injection port.
Speed was monitored by a tachometer attached to one strand of fiberglass before the inlet. Pressure was maintained by a constant pressure pump.
TABLE 1. Runs and conditions for Test 3.
Run Resin Additive Temp Speed Pressure Product (~C) (cm/min) (psi) Quality 3A-1 Phenolic None 180 30 30 Good 30 3A-2 Phenolic None 180 40 30 Poor 3A-3 Phenolic None 180 40 40 Good 3A-4 Phenolic None 180 50 50 Poor 3A-5 Phenolic None 200 50 50 Poor/Good 3A-6 Phenolic None 200 50 60 Good 3B-1 Phenolic 1% Silane 180 40 Good 3B-2 Phenolic 1~ Silane 180 40 Good 3B 3 Phenolic 1% Silane 180 40 Good 3B-4 Phenolic 1% Silane 180 45 Good 3B-5 Phenolic 1% Silane 180 50 Poor 10 3C-1 Phenolic 1~ Caustic 180 30 Good 3C-2 Phenolic 1% Caustic 180 40 Good 3C-3 Phenolic 1% Caustic 180 50 15 50 Good 3C-4 Phenolic 1% Caustic 180 60 Good 3C-5 Phenolic 1% Caustic 180 70 Poor 20 3C-5 Phenolic 1% Caustic 200 60 Good 3C-7 Phenolic 1% Caustic 200 70 Good 3C-8 Phenolic 1% Caustic 200 80 25 60 Poor 3D-1 Polyester None 150 20 20 Poor/~ood 3D-2 Polyester None 150 20 30 30 Poor/Good 3D-3 Polyester None 150 40 30 Poor 3D-4 Polyester None 150 40 60 Poor 35 3D-5 Polyester None 150 30 60 Poor/Good For run series 3A, the phenolic was run at speeds beginning at 30 cm/min and at a pressure of 30 psi. When speed was increased to 40 cm/min, the resulting product delaminated. When pressure was increased to 40 psi, the delamination ceased. At 50 cm/min, increases in pressure to 60 psi did not prevent delamination, indicating that penetration of the resin was not the limiting parameter. At 50 cm/min and 50 psi, and with the temperature raised from 180C to 200C, the product improved although ~ s 7 X

there was slight delamination. Further increase in pressure to 60 psi produced an acceptable product.
This series of runs demonstrated the importance of resin pressure level and control on penetration of the resin and subsequent product quality, and the effect of temperature on accelerating the curing of the resin.
In series 3B, 1% silane by weight was added to the neat phenolic resin. In the first three runs of this series, speed and temperature were maintained at constant levels while resin pressure was sequentially reduced from 40 to 25 psi. All three runs produced acceptable product. At a constant pressure of 25 psi, speed was increased to 45 and then 50 cm/min, at which point unacceptable product resulted. This series indicated that silane promoted fiberglass penetration by the resin at substantially lower pressures than in series 3A.
For series 3C, 1% caustic soda by weight was added to the neat phenolic resin to shift the pH from approximately 6 (neutral) to about 10. Both speed and pressure were increased in uniform steps to 60 cm/min and G0 psi, all giving acceptable product. However, when the speed was increased to 70 cm/min, the product delaminated. The temperature was increased to 200C
and speed reduced to 60 cm/min at a pressure of 60 psi, which yielded acceptable product. At these temperature and pressure conditions, speed was increased to 80 cm/min before delamination. This series demonstrated that an increase in pH can be used to accelerate resin curing to obtain acceptable product, provided resin pressure is adequate for fiberglass penetration.
The final series, 3D, was run using a standard commercial polyester resin, which was unfilled, to provide a comparison with the phenolic process. Die ~31?~'4'~

temperature was set to 150C, which was previously established as the upper limit for satisfactory product of profiles having similar thicknesses. At 2C
cm/min and 20 and ~0 psi, the product was considered mar~inal because of hairline delamination. When speed was increased to 40 cm/min and pressure increased to 60 psi, substantial delamination occurred. By maintaining pressure at S0 psi and reducing speed to 30 cm/min, a marginally acceptable product was produced. This series demonstrated that polyester resin curing is limited to no greater than 30 cm/min in order to obtain acceptable product for the particular profile being pultruded.
Although preferred embodiments of the present invention have been shown, it is obvious than many modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that the present invention may be practiced otherwise than as specifically described.

Claims

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

1. A method for making a resin bonded composite pultruded product, comprising:
providing a pultrusion system which further comprises reinforcing material supply means, a pultrusion die, injection means for injecting resin into the die, and pulling means for drawing product through the die;
supplying strands of a reinforcing material to the die and grasping the strands with the pulling means;
injecting a condensation type monomer resin into the die so as to impregnate the reinforcing material within the die; and drawing the resin-impregnated strands through the die with the pulling means at a rate that permits the resin to condense to an essentially cured state by the time the composite product is withdrawn through the die.

2. The method of claim 1 wherein the resin comprises a neutral phenolic resin.

3. The method of claim 1 wherein the resin comprises a basic phenolic resin.

4. The method of claim 1 wherein the resin comprises a phenolic resin.

5. The method of claim 4 wherein the resin has a solids content of at least about 70%.

6. The method of claim 5 wherein the resin has a solids content of at least about 80%.

7. The method of claim 1 and further comprising:
preheating the resin to reduce its viscosity to a sufficient level to permit injection and impregnation of the reinforcing material.

8. The method of claim 1 wherein the resin has a viscosity of less than about 200 cps at the time of injection.

9. The method of claim 1 wherein the resin is heated to a temperature of about 60°C prior to injection.

10. The method of claim 1 wherein the die is heated to a temperature of at least about 180°C.

11. The method of claim 1 wherein the resin is injected into the die under pressure.

12. A modular die for making a resin-bonded pultruded product, comprising:
a hollow inlet region adapted for receiving a plurality of strands of a reinforcing material therethrough;
a hollow resin injection region adapted for receiving a resin and impregnating the strands with the resin;
a hollow transitional region adapted for compressing the resin-impregnated strands; and a hollow profile region adapted and sized to facilitate curing of the resin and shaping of the product, wherein the sections are aligned to create a longitudinal bore through the die.

13. The die of claim 12 wherein the inlet region comprises an inlet opening for compressing the strands.

14. The die of claim 12 wherein the resin injection region comprises a resin injection port.

15. The die of claim 12 and further comprising connecting means for aligning and connecting the regions together.

16. The die of claim 12 wherein the die is adapted for replacement of any region.

17. The die of claim 12 wherein the resin comprises a neutral phenolic resin.

18. The die of claim 12 wherein the resin comprises a basic phenolic resin.

19. The die of claim 12 wherein the resin comprises a condensation resin.

20. The die of claim 12 and further comprising:
heating means for heating at least one region of the die.

21. The die of claim 20 wherein the heating means is an electric heater.

22. The die of claim 20 wherein the heating means is electromagnetic waves directed through the die.

23. The die of claim 12 wherein the resin is heated before it is injected into the die.

24. An adaptation die for converting a hollow conventional, non-injection die into an injection die, comprising:
a hollow inlet region adapted for receiving a plurality of strands of reinforcing material therethrough;
a hollow resin injection region adapted for receiving a resin and impregnating the strands with the resin;
a hollow transitional region adapted for compressing the resin-impregnated strands and adapted for connection to one end wherein the regions of the conventional die are aligned with the convention die to create a longitudinal bore through the injection die.