CA1293101C - Use of magnetic field in continuous casting - Google Patents
Use of magnetic field in continuous castingInfo
- Publication number
- CA1293101C CA1293101C CA000547277A CA547277A CA1293101C CA 1293101 C CA1293101 C CA 1293101C CA 000547277 A CA000547277 A CA 000547277A CA 547277 A CA547277 A CA 547277A CA 1293101 C CA1293101 C CA 1293101C
- Authority
- CA
- Canada
- Prior art keywords
- magnetic field
- metal
- mold
- magnetic
- continuous casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Abstract of the Disclosure The continuous casting of heavy metals in a magnetic field is improved by using a magnetic field in the form of essentially uniform flux lines closely parallel to the casting surface. The instability experienced with the liquid meniscus is minimized and higher intensity fields, permitting casting of heavier metals, can be achieved.
Description
3~
~SE OF MAGNETIC_FIELD LN CDNIINI~US CASTING
The present invention relates to the continuous casting of heavy metals.
Ths use of magnetic fields in the casting of h~avy metals, such as aluminum is well known. In one known process, called "electromagnetic casting", an alternating magnetic field forces the aluminum away Prom the walls of the casting pit, so that no contact is provided between the metal and the mold during cooling, which produces aluminum ingots with smoother, cleaner surfaces.
This techni~ue also has been applied to continuous casting wherein the conventional chill mold is replaced by a magnetic field which exerts a radial force on the molten metal. When the metal solidifies, it forms a column, which is lowered continuously at the same time as molten metal is supplied to the mold.
Problems arise, however, in the commercial application of such casting techniques. In particular, a rolling action often is experienced at the meniscus of the melt as a result of unbalanced magnetic forces acting on this area, which leads to surface imper~ections in the cooled metal. In add:Ltion, metals heavier than aluminum, such as copper and iron, are di~icult or impossible to process by such techniques, because of the much higher magnetic fields involved.
The present invention is directed to improvements in the continuous casting of heavy metals in the presence of a magnetic field which avoid the problems of the prior art discussed above and which enable a broader range of metals to be cast, including copper and iron.
In the present invention, a magnetic field in the form of essentially uniform flux lines closely parallel to the casting surface is employed. A magnetic field of this type minimizes the unbalanced forces which cause the menisclls to roll in the prior art. In addition, this type of magnetic ~ield permits the higher magnetic `j intensities required by heavier metals to ~e achieved.
o~
The essentially unifo~n flux lines of the magnetic field are achieved using a magnetic coil which has a reactance which is linear thrsughout its height. This result may be achieved by partially enclosing the magnetic coil within an inner core.
Another drawback of the prior art lies in the fact that, with the existing magnetic coil structure, the bottom of the liquid meniscus needs to be maintained at approximately the centre of the magnetic coil. The improved magnetic coil arrangement o~ the. present invention enables a considerably-greater portion of the coil to be employed.
Accordingly, in one aspect of the present invention, there is provicled a method of continuous casting o~ a heavy metal wherein the heavy metal in the molten state is subjected to a magnetic field and is cooled to a æolid state, the improvement which comprises providing the magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting sur~ace and having a physical height correspondiny to ~he physical height of the metal in its molten state.
Further, in a~other aspect of the invention, there is provided a continuous casting mold having an electromagnet for applying a magnetic field to a molten heavy metal, the improvement wherein the magnetic field is provided by a magnetic coil which has a reactance which is linear throughout its height and which has a physical height corresponding substantially to the intended height of molten metal in the mold and thereby produces a magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting of molten metal cast in the mold.
The invention is dascribed further, by way of illustration with reference to the accompanying drawings, in which:
Figure 1 is a sectional view of part of an existing continuous casting mold;
Figure 2 is a sectional view of part of a ~' 31~1 continuous casting mold provided in accordance with one embodiment of the invention; and Figure 3 is a partial sect:ional view of an electromagnetic coil use~ul in the continuous casting device of Figure 2.
Re~erring to Figure 1, there is illustrated a continuous casting mold 10 wherein a strand of aluminum 12 is formed from a ca~t molten aluminum. A magnetic coil 14 surrounding the strand 12 exerts a magnetic field on the strand 12 and maintains the strand 12 away from the mold wall.
The liquid mekal cools to ~orm a solid metal which then is conveyed continuously downwardly and out o~ the mold. The liquid metal 16 initially cast i5 enclosed by the magnetic field and is on top of khe soli.dified metal 18. The liquid metal 16 forms a meniscus 20. As can be seen, the magnetic field 22 to which the molten metal is subjected is uneven and this leads to instability in the meniscus 20.
Referring now to Figure 2, a continuous casting machine 10' is provided in accordance with one embodiment of the invention. In this instance, the liquid metal 16' is surrounded by an electromagnetic coil 14' of particular construction, more particularly seen in Figure 3. The coil 14' produces a magnetic ~ield 22' in the form o~ essentially uniform flux lines closely parallel to the castiny surface 20'. The uniformity of the strength of the magnetic field through the height of the liquid metal 16' ensures stability of the meniscus 20'.
As may be seen by comparison between Figures 1 and 2, the usable height of the coil 1~' extends for the height of the liquid metal 16' while in the case of coil 14, the centre line of the coil corresponds to the interface between the liquid metal 16 and the solid metal 18~
The ability to shape the magnetic lines in accordance with this invention enables differences in hydrostatic pressure in the liquid metal 16~ to be .~ , lr~
accommodated and permitting the correct shape to be maintained during solidification and solidified metal skin formation. In addition, magnetic fields of higher intensity may be achieved, thereby permitting heavier metals to be processed.
As seen in Figure 3, the electromagnetic coil 14' is an annular structure of inside diameter sufficient to permit the coil to surround the metal strand 12'.
laminated coil 24 is accommodated within an iron powder core 26.
Although generally the procedure of the present invention is used to form metal strands of circular cross section, by appropriate alteration of the configuration of the coil, any other cross-sectional shape of metal strand, such as square or rectangular, may be produced.
In summary of this disclosure, the present invention provides improvements in the casting of heavy metal in a magnetic field, which produce a more stable meniscus and hence improved product appearance and which enables heavier metals to be cast. Modifications are possi~le within the scope of this invention.
~SE OF MAGNETIC_FIELD LN CDNIINI~US CASTING
The present invention relates to the continuous casting of heavy metals.
Ths use of magnetic fields in the casting of h~avy metals, such as aluminum is well known. In one known process, called "electromagnetic casting", an alternating magnetic field forces the aluminum away Prom the walls of the casting pit, so that no contact is provided between the metal and the mold during cooling, which produces aluminum ingots with smoother, cleaner surfaces.
This techni~ue also has been applied to continuous casting wherein the conventional chill mold is replaced by a magnetic field which exerts a radial force on the molten metal. When the metal solidifies, it forms a column, which is lowered continuously at the same time as molten metal is supplied to the mold.
Problems arise, however, in the commercial application of such casting techniques. In particular, a rolling action often is experienced at the meniscus of the melt as a result of unbalanced magnetic forces acting on this area, which leads to surface imper~ections in the cooled metal. In add:Ltion, metals heavier than aluminum, such as copper and iron, are di~icult or impossible to process by such techniques, because of the much higher magnetic fields involved.
The present invention is directed to improvements in the continuous casting of heavy metals in the presence of a magnetic field which avoid the problems of the prior art discussed above and which enable a broader range of metals to be cast, including copper and iron.
In the present invention, a magnetic field in the form of essentially uniform flux lines closely parallel to the casting surface is employed. A magnetic field of this type minimizes the unbalanced forces which cause the menisclls to roll in the prior art. In addition, this type of magnetic ~ield permits the higher magnetic `j intensities required by heavier metals to ~e achieved.
o~
The essentially unifo~n flux lines of the magnetic field are achieved using a magnetic coil which has a reactance which is linear thrsughout its height. This result may be achieved by partially enclosing the magnetic coil within an inner core.
Another drawback of the prior art lies in the fact that, with the existing magnetic coil structure, the bottom of the liquid meniscus needs to be maintained at approximately the centre of the magnetic coil. The improved magnetic coil arrangement o~ the. present invention enables a considerably-greater portion of the coil to be employed.
Accordingly, in one aspect of the present invention, there is provicled a method of continuous casting o~ a heavy metal wherein the heavy metal in the molten state is subjected to a magnetic field and is cooled to a æolid state, the improvement which comprises providing the magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting sur~ace and having a physical height correspondiny to ~he physical height of the metal in its molten state.
Further, in a~other aspect of the invention, there is provided a continuous casting mold having an electromagnet for applying a magnetic field to a molten heavy metal, the improvement wherein the magnetic field is provided by a magnetic coil which has a reactance which is linear throughout its height and which has a physical height corresponding substantially to the intended height of molten metal in the mold and thereby produces a magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting of molten metal cast in the mold.
The invention is dascribed further, by way of illustration with reference to the accompanying drawings, in which:
Figure 1 is a sectional view of part of an existing continuous casting mold;
Figure 2 is a sectional view of part of a ~' 31~1 continuous casting mold provided in accordance with one embodiment of the invention; and Figure 3 is a partial sect:ional view of an electromagnetic coil use~ul in the continuous casting device of Figure 2.
Re~erring to Figure 1, there is illustrated a continuous casting mold 10 wherein a strand of aluminum 12 is formed from a ca~t molten aluminum. A magnetic coil 14 surrounding the strand 12 exerts a magnetic field on the strand 12 and maintains the strand 12 away from the mold wall.
The liquid mekal cools to ~orm a solid metal which then is conveyed continuously downwardly and out o~ the mold. The liquid metal 16 initially cast i5 enclosed by the magnetic field and is on top of khe soli.dified metal 18. The liquid metal 16 forms a meniscus 20. As can be seen, the magnetic field 22 to which the molten metal is subjected is uneven and this leads to instability in the meniscus 20.
Referring now to Figure 2, a continuous casting machine 10' is provided in accordance with one embodiment of the invention. In this instance, the liquid metal 16' is surrounded by an electromagnetic coil 14' of particular construction, more particularly seen in Figure 3. The coil 14' produces a magnetic ~ield 22' in the form o~ essentially uniform flux lines closely parallel to the castiny surface 20'. The uniformity of the strength of the magnetic field through the height of the liquid metal 16' ensures stability of the meniscus 20'.
As may be seen by comparison between Figures 1 and 2, the usable height of the coil 1~' extends for the height of the liquid metal 16' while in the case of coil 14, the centre line of the coil corresponds to the interface between the liquid metal 16 and the solid metal 18~
The ability to shape the magnetic lines in accordance with this invention enables differences in hydrostatic pressure in the liquid metal 16~ to be .~ , lr~
accommodated and permitting the correct shape to be maintained during solidification and solidified metal skin formation. In addition, magnetic fields of higher intensity may be achieved, thereby permitting heavier metals to be processed.
As seen in Figure 3, the electromagnetic coil 14' is an annular structure of inside diameter sufficient to permit the coil to surround the metal strand 12'.
laminated coil 24 is accommodated within an iron powder core 26.
Although generally the procedure of the present invention is used to form metal strands of circular cross section, by appropriate alteration of the configuration of the coil, any other cross-sectional shape of metal strand, such as square or rectangular, may be produced.
In summary of this disclosure, the present invention provides improvements in the casting of heavy metal in a magnetic field, which produce a more stable meniscus and hence improved product appearance and which enables heavier metals to be cast. Modifications are possi~le within the scope of this invention.
Claims (5)
1. In a method of continuous casting of a heavy metal wherein said heavy metal in the molten state is subjected to a magnetic field and is cooled to a solid state, the improvement which comprises providing said magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting surface and having a physical height corresponding to the physical height of the metal in its molten state.
2. The method of claim .1 wherein said magnetic field is provided by magnetic coil which has a reactance which is linear throughout its height.
3. The method of claim 2 wherein said magnetic coil is partially enclosed within an iron core.
4. In a continuous casting mold having an electromagnet for applying a magnetic field to a molten heavy metal, the improvement wherein said magnetic field is provided by a magnetic coil which has a reactance which is linear throughout its height and which has a physical height corresponding substantially to the intended height of molten metal in said mold and thereby produces a magnetic field in the form of essentially uniform flux lines closely parallel to an upper casting surface of molten metal cast in said mold.
5. The mold of claim 4 wherein said magnetic coil is enclosed within an iron core except in the portion intended to face the molten metal.