CA1286688C - Process for manufacture of alkene oxide - Google Patents

Abstract

Abstract:

A process for the epoxidation of alkene to form alkene oxide comprising contacting alkene and oxygen-containing gas under epoxidation conditions in the presence of at least one gaseous efficiency-enhancing member of a redox-half reaction pair, e.g., nitric oxide, a supported silver catalyst and an efficiency-and/or activity-enhancing amount of water, the cata-lyst comprising a catalytically-effective amount of silver and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair, e.g., potassium nitrate.

Description

~28668~3 J

PROCESS FOR MANUFACTURE OF ALKENE OXIDE

Technical Field:

The present invention is directed to improved processes for the preparation of alkene oxide from alkene and oxygen-containing gas employing a sup-ported silver catalyst. Particular aspects of thepresent invention relate to processes for epoxidizing alkene in the vapor phase to produce the correspond-ing alkene oxide at high efficiencies.

Background And Backqround Art:

The production of alkene oxides, or epoxides, particularly ethylene oxide, by the direct epoxida-tion of the corresponding alkene in the presence of a silver-containing catalyst has been known for many years. One of the earliest disclosures of a process for the direct epoxidation of ethylene was that of Lefort, U. S. Patent 1,998,878, issued in 1935 (re-issued in 1942 as Re. 20,370). Lefort discloses that ethylene oxide can be formed by reacting ethylene and oxygen according to the following equation:

121~68~

2CH2=CH2 + 02~ 2CH2 CH2 (I) Lefort recognized, however, that some of the ethylene, when reacted with oxygen, is completely oxidized to carbon dioxide according to the following equation:

C2H4 + 32 - -~2H20 ~2C02 (II) Reaction II, as well as other reactions in which alkene is converted to products other than alkene oxide, is undesirable since the alkene reactant is ~
consumed in the formation of undesired products.
Further, the undesired products, e.g., carbon di-oxide, may adversely affect the reaction system. In general, the overall effectiveness of an alkene oxide production system is gauged by the performance char-acteristics of the system. The most important per-formance characteristics are the efficiency, theactivity, and the useful life of the catalyst, all of which are defined and more completely described be-low.
Percent conversion is defined as the percentage of the alkene introduced to the reaction system that undergoes reaction. Of the alkene that reacts, the percentage that is converted into the corresponding alkene oxide is referred to as the selectivity or efficiency of the process. The commercial success of a reaction system depends in large measure on the efficiency of the system. At present, maximum effi-ciencies in commercial production of ethylene oxide by epoxidation are in the low 80s, e.g., 80 or 81 percent. Even a very small increase in efficiency will provide substantial cost benefits in large-scale 12~688 operation. For example, taking 100,000 metric tons as a typical yearly yield for a conventional ethylene oxide plant, an increase in efficiency of from 80 to 84 percent, all other things being equal, would re-sult in a savings of 3790 metric tons of ethylene peryear. In addition, the heat of reaction for Reaction II ~formation of carbon dioxide) is much greater than that of Reaction I (formation of ethylene oxide) so heat-removal problems are more burdensome as the efficiency decreases. Furthermore, as the efficiency decreases, there is the potential for a greater amount of impurities to be present in the reactor effluent which can complicate separation of the de-sired alkene oxide product. It would be desirable, therefore, to develop a process for the epoxidation of alkene in which the efficiency is greater than that obtained in conventional commercial processes, e.g., with ethylene, efficiences of 84 percent or greater, while maintaining other performance charac-teristics, particularly the activity, as describedbelow, in a satisfactory range.
The product of the efficiency and the conversion is equal to the yield, or the percentage of the al-kene fed that is converted into the corresponding oxide. The definitions of conversion, efficiency and yield may be represented as follows:

% Conversion = moles alkene reacted x 100 moles alkene fed % Efficiency = moles alkene oxide produced x 100 moles alkene reacted % Yield = moles alkene oxide produced x 100 moles alkene fed Generally, in a process for the epoxidation of alkene, a reaction inlet stream containing reactants and perhaps other additional materials enters the reactor or reaction zone in which catalytic material is provided and in which favorable reaction condi-tions (e.g., temperature and pressure) are maintain-ed. The reactor effluent is withdrawn or collected from the reactor. The reactor effluent contains reaction products, together with unreacted components - from the reaction inlet stream.
Since at least some alkene is generally not converted during ;ts initial pass through the reac-tor, alkene is generally present in the reactor ef-fluent. To increase the overall yield of the pro-cess, at least a portion of the alkene in the reactor effluent is returned to the reactor via a recycle stream. Means are provided for removing and recover-ing at least a portion of the alkene oxide from the reactor effluent, prior to recycling, to form the product stream. At least a portion of the remaining reactor effluent (after the product stream has been withdrawn) becomes the recycle stream. The recycle stream preferably contains substantially all of the alkene that was contained in the reactor effluent.
Reactants, i.e., oxygen-containing gas and al-kene, need to be continuously replaced and are pro-vided to the reactor by means of a makeup feed-stream. In general, the makeup feedstream and the recycle stream are combined to form the reaction inlet stream which is sent into the reactor or reac-tion zone. Alternatively, the makeup feedstream and the recycle stream can be introduced into the reactor separately.

12~366~38 The epoxidation of alkene is generally carried out in the presence of a supported silver catalyst located within the reactor or reaction zone. The silver may be supported by a conventional support material, for example, alpha-alumina. The per-formance of the catalyst may be affected by the pre-sence of solid, liquid or gaseous compounds which may, for example, be incorporated in the catalyst or provided via the makeup feedstream.
The activity of a reaction system is a measure of the rate of production of the desired product, e.g., ethylene oxide, for a particular reaction sys-tem at a particular temperature. In order to provide a meaningful comparison of the effectiveness of two or more reaction systems or of a single reaction system at different times, factors, such as feed rate, feed composition, temperature, and pressure, that affect the rate of production of the desired alkene oxide must be normalized or accounted for, preferably by using a standard or fixed set of oper-ating conditions. Since the rate of production of alkene oxide is proportional to the volume of cata-lyst in the reaction system, the activity is usually expressed in terms of pounds of alkene oxide produced per hour per cubic foot of catalyst. It should be noted that this method of measuring activity does not take into account variations in the densities of the catalysts since the controlling factor is the volume of the reaction system available, not the weight of catalyst which will fit into a given volume. Other factors that have an effect on the rate of production of the desired compound include the following:
(1) the composition of the reaction stream;

(2) the gas hourly space velocity of the reac-tion stream;

12~66~8 (3) the temperature and pressure within the reactor or reaction zone.
In order to compare the effectiveness of two or more reaction systems or of a single reaction system at different times, differences in factors 1 through 3 above should be minimized and/or factored into the evaluation of relative effectiveness.
If the activity of a reaction system is low, then, all other things being equal, the commercial value of that system will be low. The lower the activity of a reaction system, the less product pro-duced in a unit time for a given feed rate, reactor temperature, catalyst, surface area, etcetera. A low activity can render even a high efficiency process commercially impractical. In general, an activity below 4 pounds of ethylene oxide per hour per cubic foot of catalyst is unacceptable for commercial prac-tice. The activity is preferably greater than 8 pounds, and in some instances an activity greater than 11 pounds of ethylene oxide per hour per cubic foot of catalyst is desired.
Reaction systems generally deactivate over time, i.e., the activity of the catalyst begins to decrease as the process is carried out. Activity may be plot-ted as a function of time to generate a graph showingthe aging behavior of the catalyst. Experimentation for the purpose of developing an activity plot is usually conducted at a set temperature since, in general, activity can be increased by raising the reaction temperature. Alternatively, an activity plot can be a graph of the temperature required to maintain a given activity versus time. The rate at which activity decreases, i.e., the rate of deactiva-tion at a given point in time, can be represented by the slope of the activity plot, i.e., the derivative of activity with respect to time:

deactivation = d[activity~/dt.

The average rate of cleactivation over a period of time can be represented then by the change in activity divided by the time period:

average deactivation = ~activity/ ~t.
At some point, the activity decreases to an unacceptable level, for example, the temperature required to maintain the activity of the system be-comes unacceptably high or the cate of production becomes unacceptably low. At this point, the cata-lyst must either be regenerated or replaced. The useful life of a reaction system is the length of time that reactants can be passed through the reac-tion system during which acceptable activity is ob-served. The area under a plot of activity versustime is equal to the number of pounds of alkene oxide produced during the useful life of the catalyst per cubic foot of catalyst. The greater the area under such a plot, the more valuable the process is since regeneration or replacement of the catalyst involves a number of expenses, sometimes referred to as turn-around costs. More specifically, the replacement of the catalyst generally requires that the reactor be shut down for an extended period of time, e.g., two weeks or more, to discharge the catalyst, clean the reactor tubes, etcetera. This operation requires extra manpower and the use of special equipment. The costs involved, which may include replacement cata-lyst, can mount into the millions of dollars.

12~ti6S8 As used herein, an activity-reducing compound refers to a compound which, when present in an acti-vity-reducing amount, causes a reduction in activity, some or all of which activity may subsequently be regained by returning to a situation in which the concentration of the compound is below the minimum activity-reducing amount. The minimum activity-reducing amount varies depending on the particular system, the feedstream and the activity-reducing compound.
Conversely, deactivation, as used herein, refers to a permanent loss of activity, i.e., a decrease in activity which cannot be recovered. As noted above, activity can be increased by raising the temperature, lS but the need to operate at a higher temperature to maintain a particular activity is representative of deactivation. Catalysts tend to deactivate more rapidly when reaction is carried out at higher tem-peratures.
As previously noted, since the work of Lefort (U. S. Patent 1,998,878), research efforts have been directed toward improving the performance character-istics of reaction systems, i.e., improving the acti-vity, efficiency and useful life. Research has been conducted in areas such as feedstream additives, removal of materials in the recycle stream and methods of catalyst preparation, including the depos-ition or impregnation of a particular type or form of silver. Additionally, research efforts have been di-rected toward the composition and formation of thesupport, as well as toward additives deposited on or impregnated in the support.
One of the difficulties in carrying out research is the necessity of considering the interrelationship of the various variables. The improvement or en-128~688 hancement of one performance characteristic must not be at the expense of, or have too great an adverse effect on, one of the other performance characteris-tics. For example, if a reaction system is designed which has a very short useful life, the system may be commercially impractical even though the efficiency and initial activity of the catalyst are outstand-ing. Accordingly, a system that provides an increase in the efficiency of the overall catalytic reaction system, while only minimally affecting the activity and useful life of the catalyst, would be particular-ly beneficial.
Diluents have generally been included in the gaseous mixture to reduce the likelihood of explo-sion. Diluents are generally supplied via the makeupfeedstream. Such diluent materials have generally been believed to be inert, i.e., their function is primarily to act as a heat sink and to dilute the gaseous mixture. Nitrogen has been found to be a suitable diluent material. It is well known to use air to supply both oxygen and nitrogen to the reac-tion zone. Another material that has been used as a diluent is carbon dioxide. EPO Patent 3642 discloses that a diluent, for example, helium, nitrogen, argon, carbon dioxide, and/or a lower paraffin, for example, ethane and/or methane, may be present in proportions of 10-80 percent and preferably 40-70 percent by volume in total. Similarly, U. K. Patent Application GB 2 014 133A mentions carbon dioxide as a possible diluent. Other patents, e.g., U. S. Patents 3,043,854, 4,007,135, and 4,206,128, Japanese Patent 53-39404, and U. K. Patents 676,358 and 1,571,123, also mention that carbon dioxide is suitable for use as an additive.

12866~38 Lefort, in U. S. Patent 1,998,878 (Re. 20,370), states that carbon dioxide may be introduced into the reactor to limit the rate of complete oxidation of ethylene to carbon dioxide. Similar disclosure is found in V. S. Patent 2,270,780. U. S. Patent 2,615,900 discloses a process for producing ethylene oxide in which carbon dioxide gas may be added to the feed gases to act as a "depressant" or "anti-cata-lytic material". U. S. Patent 4,007,135 discloses a process in which, according to the patent, carbon dioxide may be used to raise the selectivity of the reaction. According to Chem. Abstracts, Vol. 80, Issue 11, Section 22, Abstract 059195, the presence of carbon dioxide tends to retard the deactivation of the silver catalyst.
As mentioned above, any alkene contained in the reactor effluent stream is preferably returned to the reaction zone via a recycle stream. It is sometimes preferred to remove some of the gas contained in the reactor effluent stream via a purge stream prior to introducing the recycle stream into the reaction zone. The purge stream may comprise a straight purge, i.e., the purge stream can merely draw off a percentage of the recycle stream. Since a straight purge stream generally has a composition substantial-ly similar to that of the stream from which it is removed, some alkene will generally be purged when a straight purge is employed. For this reason, means are sometimes provided to ensure that purge streams have relatively high concentrations of materials other than alkene, such as nitrogen and carbon diox-ide.
U. S. Patent 2,241,019 discloses a process in which the purge gas is carried through and in contact with an adsorptive agent which is adapted to adsorb ~2~66~8 selectively the ethylene content of the purge gas, while the nitrogen and much of the carbon dioxide present in the purge gas pass through the adsorption agent and are discharged to the atmosphere.
U. S. Patent 2,376,987 discloses a process for the two-stage preparation of butadiene in which, in the first stage, ethylene is oxidized in a converter to form ethylene oxide. The converter contains an oxidizing catalyst which is preferably finely divided silver on a carrier such as alumina. According to the patent, if concentrated oxygen is used as the oxygen source, the ethylene in the stream containing the oxidation products from the converter may be con-centrated and recycled to the process by scrubbing to remove carbon dioxide, etcetera.
U. S. Patent 2,653,952 discloses a process for the manufacture of ethylene oxide in which the pro-ducts from the reactor, consisting essentially of ethylene oxide, ethylene, oxygen, nitrogen, helium and carbon dioxide, are delivered to an ethylene oxide absorber. The gases are then passed in contact with a solvent for carbon dioxide. Ordinarily, ethanolamine is used as a solvent in this process.
The gas discharged from the carbon dioxide absorber contains ethylene and is recycled to be again passed in contact with the catalyst in the reactor. This patent recognizes that nitrogen tends to build up to high concentrations when the oxygen is supplied by air. The process of this patent therefore employs relatively nitrogen-free oxygen in the feedstream and dilutes the gaseous mixture with helium.
U. S. Patent 2,799,687 discloses a preferred embodiment for the oxidation of olefins in which the reactor effluent may be passed into an ethylene oxide absorber after which about 70-90 percent of the ef-12l3t~

fluent from the ethylene oxide absorber is reeyeled and the remainder plus adclitional oxygen is diverted to a second reactor. According to the patent, by the diversion of a portion of the effluent from the first reactor to the second reac:tor, the buildup of carbon dioxide above certain limits, such as above about 5-7 percent, can be prevented. Similarly, U. S. Patent 4,206,128, Netherlands Patent Application 6,414,284, and V. K. Patent 1 191 983 all disclose processes in which some carbon dioxide is removed from the recycle stream.
According to U. K. Patent 1,055,147, one must remove carbon dioxide from the ethylene oxide produc-tion system to keep the carbon dioxide concentration in an acceptable range since, according to the pat-ent, carbon dioxide acts as an inhibitor and suppres-ses the reaction of ethylene to form both ethylene oxide and carbon dioxide.
U. S. Patent 1,998,878, U. S. Patent 3,904,656, "The Manufaeture Of Ethylene Oxide And Its Deriva-tives", The Industrial Chemist, February, 1963, Kirk Othmer, "Ethylene Oxiden, Volume 8, pages 534,545, "Ethylene Oxide By Direct Oxidation Of Ethylene", Petroleum Processing, November, 1955, all inelude, as a process step, the removal of carbon dioxide from the alkene oxide for the purification of the alkene oxide produet.
Sinee the early work on the direet eatalytic oxidation of ethylene to ethylene oxide, it has been suggested that the addition of eertain eompounds to the gaseous feedstream or direet incorporation of metals or eompounds in the eatalyst eould enhanee or promote the production of ethylene oxide. Sueh metals or eompounds have been known variously as "anti-eatalystsn, "promoters" and "inhibitors".

1281~688 ~hese substances, which are not considered catalysts, are believed to contribute to the overall utility of the process by inhibiting the formation of carbon dioxide or by promoting the production of ethylene oxide.
Various Compounds have been found to provide some beneficial effects when contained within the gaseous mixture supplied to the reactor. It is well known that chlorine-containing compounds, when sup-plied to an ethylene oxide production process, helpto improve the overall effectiveness of the pro-cess. For example, Law and Chitwood, in U. S. Patent 2,194,602, disclose that higher yields of olefin oxide are obtained by retarding the complete oxida-tion of the olefin through the addition of very smallamounts of deactivating materials (also referred to by Law and Chitwood as repressants or anti-catalytic materials) such as ethylene dichloride, chlorine, sulfur chloride, sulfur trioxide, nitrogen dioxide, or other halogen-containing or acid-forming mater-ials. V. S. Patents 2,270,780, 2,279,469, 2,279,470, 2,799,687, 3,144,416, 4,007,135, 4,206,128, 4,368,144, EPO Patent 11 356, U. R. Patents 676,358, 1,055,147 and 1,571,123 also discuss the addition of halide compounds, such as ethyl chloride, ethylene dichloride, potassium chloride, vinyl chloride and alkyl chloride.
U. S. Patent 2,194,602 discloses a method for the activation of silver catalysts in which the acti-vation is accomplished by bringing the catalyst incontact with an aqueous solution of barium, strontium or lithium hydroxide after the catalyst has first been treated with a "repressant" such as ethylene di-chloride, nitrogen dioxide, or other halogen-contain-ing or acid-forming material.

lZ1~68~3 U. S Patents 2,279,469 and 2,279,470 disclose processes of making olefin oxides in which very small amounts, i.e., less than 0.1 percent of the total volume, of "anti-catalysts" are incorporated with the reactants. Halogens and compounds containing halo-gens, e.g., ethylene dichloride, and compounds con-taining nitrogen, e.g., nitric oxide, can be used as the anti-catalysts. According to the patents, it is possible to employ mixtures of the individual anti-catalyst substances.
U. S. Patent 3,144,416 discloses a method ofmanufacturing silver catalysts to be used for the oxidation of olefins. According to the patent, in order to increase the selectivity of the catalyst, a small quantity of halogen compound or nitrogen com-pound may be added to the reaction gas or catalyst.
EPO Patent 3642 and U. K. Patent Application GB
2 014 133A disclose processes of producing an olefin oxide by contacting an olefin with oxygen in the presence of a silver-containing catalyst and a chlorine-containing reaction modifier, for example, dichloroethane, methyl chloride, or vinyl chloride.
According to these references, the catalyst per-formance is improved, for example, the selectivity is increased, by contacting the catalyst with a nitrate-or nitrite-forming substance, for example, a gas containing dinitrogen tetroxide, nitrogen dioxide and/or a nitrogen-containing compound, together with an oxidizing agent, such as nitric oxide and oxy-gen. The catalyst preferably comprises 3 to 50 per-cent, more preferably 3 to 30 percent, by weight silver. According to the references, it is preferred that the catalyst should contain cations, for exam-ple, alkali and/or alkaline earth metal cations, as the corresponding nitrate or nitrite, particularly if 121~88 the catalyst is treated with the nitrate- or nitrite-forming substance intermittently. According to the patents, suitable concentrations of the cations may be, for example, 5 x 10-5 to 2, preferably 5 x 10-4 to 2, more preferably 5 x 10-4 to 0.5, gram equiva-lents per kilogram of catalyst. Suitably, Mo, K, Sr, Ca and/or Ba are present in amounts of 2 to 20,000, preferably 2 to 10,000, more preferably 10 to 3,000, microgram equivalents per gram of silver. Tn the processes of these two references, a diluent, for example, carbon dioxide, may be present and uncon-verted olefin may be recycled, suitably after removal of carbon dioxide.
Rumanian Patent No. 53012, published December 2, 1971, discloses a process in which the catalyst is brought in direct contact with a gas mixture composed of 5-15 percent oxygen, 8-20 percent carbon dioxide, 60-80 percent nitrogen, completed by 1-5 percent nitrogen oxides.
V. K. Patent 524,007 discloses a method for activating catalysts which may be accomplished by contacting the catalyst with an aqueous solution of a hydroxide of lithium, after the catalyst has first been treated with an "anti-catalyst", such as ethy-lene dichloride or nitrogen dioxide. According to the patent, the treatment may most advantageously be conducted simultaneously with the oxidation reaction of the olefins, inasmuch as the presence of very small amounts of anti-catalyst (less than 0.1 per-cent) increases the efficiency by limiting the forma-tion of carbon dioxide.
There has been some disclosure directed to the effect of water contained in the gaseous mixture which is fed to the reactor. Water can be introduced through the feedstream, or, since it is a by-product 1286i688 of one of the side reactions in the oxidation of alkenes, it can be accumulated through recycling.
U. S. Patent 1,998,~78 states that the efficien-cy of the reaction is increased by introducing a suitable quantity of water. According to the patent, if water is introduced in a suitable quantity, the reaction giving CO2 is checked, owing, as is pro~-able, to the partial pressure of water.
U. S. Patent 2,367,169 states that in some cases, for instance, when pure ethylene gas is being treated, it is advantageous to introduce into the gas stream traversing the reaction zone small amounts of steam.
U. S. Patent 2,376,987 discloses a process for the preparation of butadiene in which ethylene is subjected to an oxidation reaction in converter.
Water or steam may be supplied to the converter to assist in controlling the temperature by absorbing the heat evolved in the reaction. According to the patent, water in the reaction also tends to increase the production of ethylene oxide and reduce the for-mation of other oxidation products in the reaction.
U. S~ Patent 2,615,900 discloses a process for producing ethylene oxide in which steam may be in-cluded in the feed gases to act as a depressant oranti-catalytic material.
U. S. Patent 3,959,316 discloses a procedure for propylene oxide synthesis in which the reaction is carried out in the presence of water vapor which can be between 2 and 25 percent with respect to the total of the feed gas and is preferably between 2 and 15 percent.
U. S. Patent 4,094,889 discloses a process for restoring the selectivity of unstable alkali metal promoted silver-containing catalysts for the oxida-tion of olefins to olefin oxides by wetting the cata-lyst with water and drying it. The catalyst may be wet with water by contacting it with li~uid water by wetting it with wet steam or by absorbing water into the catalyst from steam in the vapor phase.
U. S. Patent 4,125,480 discloses a process for improving the performance of silver catalysts which comprises washing the used catalyst with water and depositing from about 0.00004 to about 0.008 gram equivalent weights per kilogram of total catalyst of ions of one or more of the alkali metals, sodium, potassium, rubidium or cesium. The ions are deposited by impregnating the washed catalyst with a solution of one or more compounds of these alkali metals in a suitable solvent, particularly an organic solvent. Examples of suitable compounds are the hydroxides, nitrates, chlorides, iodides, bromides, bicarbonates, and carbonates. According to the pat-ent, the process may be carried out within the reac-tor, for example, water may be passed through thereactor containing the used silver catalyst.
Japanese Patent Publication No. 40051/1976 dis-closes a process for producing an olefin oxide in which steam is employed in the starting gas in cer-tain of the examples given in the patent. In Exam-ples 1-5, steam comprises 7 percent of the starting gas and in the Comparative Example it comprises 8 percent of the starting gas.
In the reference, "A Study of the Oxidation of Ethylene to Ethylene Oxide on a Silver Catalyst", K.
E. Murray, studies indicate that the presence of water vapor increases the yield of the reaction but considerably decreases conversion.

12~36688 Chem. Abstracts, Volume 80, Issue 11, Section 22, Abstract 059195, teaches that ~2 has a retarding effect on the catalyst deactivation in the oxidation of ethylene over a silver catalyst.
U. S. Patents 2,270,780, 3,119,837, 4,061,659, 4,248,740, 4,368,144, 4,471,071, and Japanese Patent 53-39404 all discuss the use of water or steam as an inert material or diluent.
Scientific literature is replete with examples of the use of alkali metals and alkaline earth metals and their cations to promote the efficiency of silver catalysts used in epoxidation reactions. Numerous examples may be found in literature regarding prefer-ence for the inclusion or exclusion of one or several metals or cations in silver catalysts. Although many reports have indicated that no particular effective-ness is observed with one alkali metal or alkaline earth metal cation vis-a-vis another, several have suggested clear preferences for particular metal cations.
Potassium is well known as a catalyst promoter for the epoxidation of alkenes. One of the first patents to recognize potassium as a suitable promoter was U. S. Patent 2,177,361. According to this pat-ent, the catalyst may be promoted by the presence ofvery small proportions of alkali or alkaline earth metals.
U. R. Patent Application 2,122,913A discloses a catalyst and a process for oxidation of ethylene in which an amount of alkali metal is deposited on the catalyst which removes substantially all activity from the silver catalyst and then activity and selec-tivity are recovered by heating the catalyst in a nitrogen atmosphere.

128~68~3 When potassium is employed in the catalyst, it is generally introduced in conjunction with an an-ion. The choice of the anion has not always been regarded as significant. For example, U. S. Patents 3,962,136, 4,010,115, 4,012,425, and 4,356,312 state that no unusual effectiveness is observed with the use of any particular anion in the alkali metal salts ~sed to prepare the catalysts and suggests that ni-trates, nitrites, chlorides, iodides, bromates, et-cetera, may be used. Potassium nitrate was employed in the silver salt solution of Example 1 in each patent. According to the patents, from about 4.0 x 10 5 to about 8.0 x 10 3 gram equivalent weights of ionic higher alkali metal, e.g., rubidium, cesium or potassium or mixtures thereof, per kilogram of cata-lyst is deposited on the catalyst support simultan-eously with the deposit of silver. The amount of higher alkali metal preferably ranges from about 2.0 x 10-4 to about 6.5 x 10-3 gram equivalent weights per kilogram of finished catalyst. According to the patents, the amount of the higher alkali metal (or metals) present on the catalyst surface is critical and is a function of the surface area of catalyst.
According to the patents, the alkali metal is present in final form on the support in the form of its ox-ide. U. S. Patents 3,962,136, 4,010,115 and 4,012,425 note that the highest level of selectivity obtainable when potassium is employed typically is lower than that obtainable when rubidium or cesium is employed while U. S. Patent 4,356,312 notes that particularly good results are obtained with potas-sium.
U. S. Patent 4,066,575 notes that alkali metal nitrate is suitable for supplying an alkali metal promoter, but it notes that the anion associated with 12~ ;8~

the promoter metal is not critical. U. S. Pat~nt 4,207,210 discloses a process for preparing an ethy-lene oxide catalyst in which higher alkali metals, such as potassium, rubidium and cesium, are deposited on a catalyst support prior to the deposition of silver. According to the patent, the amount of high-er alkali is a critical function of the surface area of the support. This patent also notes that no un-usual effectiveness is observed with the use of any particular anion in preparing the catalysts and lists nitrates as one type of salt that may be used. Car-bon dioxide and steam are listed as diluent mater-ials.
The use of potassium nitrate, however, to impart a promoting effect on the catalyst has been widely described. For example, U. S. Patent 4,007,135 lists a number of materials, including potassium, which can be used as promoters. According to the patent, in general, 1 to 5,000, preferably 1 to 1,000, more preferably 40 to 500, and particularly 20 to 200, atoms of potassium are present per 1,000 atoms of silver. Suitably an aqueous solution of a compound, such as a chloride, sulfate, nitrate, nitrite, et-cetera, of the promoter is used for impregnation.
U. S. Patent 4,094,889 discloses a process for re-storing the selectivity of silver catalysts in which alkali metal may be introduced as a nitrate and in which the preferred content of potassium is in the range of 2 x 10-2 to 3 x 10-5 grams/square meter of surface area of support. U. S. Patent 4,125,480 discloses a process for reactivating used silver catalyst comprising (a) washing the used catalyst, and (b) depositing from 0.00004 to 0.008, preferably from 0.0001 to 0.002 gram equivalent weights per kilogram of catalyst of ions of one or more of the ~2~688 alkali metals, such as sodium, potassium, rubidium, or cesium. The ions of, e.g., potassium are de-posited on the catalyst by impregnating it with a solution of one or more compounds, such as potassium nitrate. U. S. Patents 4,226,782, 4,235,757, 4,324,699, 4,342,667, 4,368,144, 4,455,392, Japanese Patent 56/89843, and U. ~. Patent 1,571,123 suggest the use of potassium nitrate in various amounts.
Potassium nitrate may also be formed in situ when a carrier material is treated with certain amines in the presence of potassium ions, for example, when silver is introduced to a carrier material in a sil-ver-impregnating solution containing an amine and potassium ions, followed by roasting.
There has been some disclosure directed to cata-lysts for use in an ethylene oxide production system in which silver is present in relatively large pro-portions, e.g., 35 percent or more. For example, U. S. Patents 3,565,828 and 3,654,318 disclose cata-lysts for the synthesis of ethylene oxide from oxygen and ethylene. According to the patents, the cata-lysts contain from 60 percent to 70 percent by weight of silver.
U. S. Patent 2,593,099 discloses a magnesium oxide-barium oxide silver catalyst support. Accord-ing to the patent, the conventional amount of silver is deposited on the support, namely, 2 to 50 percent, with the best results being obtained between 4 and 20 percent.
U. S. Patent 2,713,5~6 discloses a process for the oxidation of ethylene to ethylene oxide in which, according to the patent, the conventional amount of silver is deposited on the support, namely, 5 to 50 percent, with the best results being obtained between 4 and 20 percent.

12~j688 U. S. Patent 3,793,231 discloses a process for the preparation of silver catalysts for the produc-tion of ethylene oxide in which the silver content of the catalysts generally range between 15 to 30 per-cent by weight, preferably 19 to 27 percent byweight. ~
A large body of art directed to various aspects of alkene oxide production has been developed over the years since Lefort (U. S. Patent 1,998,878).
Much of it is contradictory and incapable of recon-ciliation. None of the art is believed to disclose or suggest a high efficiency process for the produc-tion of alkene oxide by contacting alkene and oxygen-containing gas in the presence of at least one gas-eous efficiency-enhancing member of a redox-half reaction pair, a supported silver catalyst and an efficiency- and/or activity-enhancing amount of water.

Disclosure of_the Invention:

In a process for the manufacture of alkene ox-ide, by contacting alkene and oxygen-containing gas under epoxidation conditions in the presence of a gaseous efficiency-enhancing member of a redox-half reaction pair and a supported silver catalyst which includes an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair, the efficiency and/or activity can be enhanced by the addition of small amounts of water, e.g., for ethylene oxide manufacture, less than about one and one-half percent by volume, to the reaction inlet stream during the operation of the process.

12~688 The present invention provides a high efficiency process for the epoxidation of alkene to form alkene oxide comprising contacting alkene, particularly ethylene and oxygen-containing gas, under epoxidation conditions and in the presence of at least one gas-eous efficiency-enhancing member of a redox-half reaction pair, preferably nitric oxide and/or nitro-gen dioxide, a supported silver catalyst and an effi-ciency- and/or activity-enhancing amount of water.
The catalyst comprises a catalytically-effective amount of silver and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair, preferably potassium nitrate, on a support. The water may be added con-tinuously or intermittently. The process of thisinvention may be used whether or not carbon dioxide is present in the reaction inlet stream. However, the amount of enhancement in efficiency has been found to be greater in the case where carbon dioxide is present in the reaction inlet stream. Also, when carbon dioxide is present, the water should, in gen-eral, be introduced prior to introduction of carbon dioxide since it has been observed that the desirable effect of the water is reduced when carbon dioxide has been introduced prior to the water.

~rief DescriPtion Of The Drawinqs:

Figure 1 is a flow chart of a process in ac-cordance with the invention.

~2~688 Detai~ed DescriPtion Of The Invention:

The present invention is directed to high effi-ciency processes for the epoxidation of alkene to form alkene oxide by contacting alkene and oxygen-containing gas in a reaction zone under epoxidation conditions in the presence of a gaseous efficiency-enhancing member of a redox-half reaction pair, a supported silver catalyst and water. The silver catalyst generally comprises a catalytically-effective amount of silver and an efficiency-enhancing amount of at least one salt of a member of a redox-half reaction pair on a porous support. A
performance-enhancing gaseous halide is preferably present in the reaction zone. According to the in-vention, an efficiency- and/or activity-enhancing amount of water, preferably comprising from about 0.25 to about 1.5, more preferably 0.25 to 1.0, per-cent by volume when the alkene is ethylene, is con-tained in the reaction inlet stream.
The following description of the preferred sys-tem for epoxidation of alkene in accordance with the present invention may be better understood by refer-ence to the flow chart in Figure 1.
In steady-state operation of the preferred sys-tem, a reaction inlet stream containing reactants, together with other gaseous materials as discussed below, is fed to a reactor at a controlled gas hourly space velocity (G~SV). The reactor may take a vari-ety of forms, but is preferably a collection of ver-tical tubes containing a supported silver catalyst.
The reaction inlet stream enters the reactor, passes through the catalyst, and exits the reactor as the reactor effluent. The desired product, e.g., ethy-lene oxide, is separated from the other components in 12~

the reactor effluent, preferably by a scrubbjng oper-ation. The remainder of the reactor effluent becomes the recycle stream. It is sometimes preferred to remove a portion of the material in the recycle stream in order to, for example, prevent buildup of certain materials in the system. The removal of material from the recycle stream may be selective, i.e., certain compounds may be removed from the re-cycle stream in greater proportions than other com-pounds. The remainder of the recycle stream is usu-ally combined with a makeup feedstream to form the reaction inlet stream. The reaction system will be discussed in greater detail below.
Although the present invention can be used with any size and type of alkene oxide reactor, including both fixed bed and fluidized bed reactors, it is contemplated that the present invention will find most widespread application in standard fixed bed, multi-tubular reactors. These generally include wall-cooled as well as adiabatic reactors. Tube lengths typically range from about 5 to about 60 feet (1.52 to 18.3 meters), frequently from about 15 to about 40 feet (1.52 to 12.2 meters). The tubes gen-erally have internal diameters from about 0.5 to about 2 inches (1.27 to 5.08 centimeters), typically - from about 0.8 to about 1.5 inches (2.03 to 3.81 centimeters).
The catalyst generally comprises a support hav-ing catalyst material or a mixture of catalyst mater-ial and an efficiency-enhancing material impregnated or coated on the support. The support can be gener-ally described as a porous, inorganic substrate which is not unduly deleterious to the performance of the system and is preferably substantially inert toward the other materials in the system, i.e., the catalyst ~21~88 material, any other components present in the cata-lyst, e.g., efficiency-enhancing salt, and components in the reaction inlet stream. In addition, the sup-port should be able to withstand the temperatures employed within the reactor, as well as, of course, the temperatures employed in manufacturing the cata-lyst, e.g., if the catalyst material is reduced to its free metallic state by roasting. Suitable sup-ports for use in accordance with the present inven-tion include silica, magnesia, silicon carbide, zir-conia, and alumina, preferably alpha-alumina. The support preferably has a surface area of at least about 0.7 m2/g, preferably in the range of from about 0.7 to about 16 m2/g, more preferably about 0.7 to about 7 m2/g. The surface area is measured by the B. E. T. nitrogen method described by Brunauer, Emmet and Teller in J. Am. Chem. Soc. 60, 309-316 (1938).
The support may be composed of a particulate matrix. In a preferred support, at least about 50 percent of the total number of support particles having a particle size greater than about 0.1 micro-meter have at least one substantially flat major surface. The support particles are preferably formed into aggregates or "pills~ of such a size and shape that they are readily usable in commercially operated tubular reactors. These aggregates or pills general-ly range in size from about 2 millimeters to about 15 millimeters, preferably about 3 millimeters to about 12 millimeters. The size is chosen to be consistent with the type of reactor employed. In general, in fixed bed reactor applications, particle sizes rang-ing from about 3 millimeters to about 10 millimeters have been found to be most suitable in the typical tubular reactors used in commerce.

~2~688 The shapes of the carrier aggregates useful for purposes of the present invention can vary widely.
Common shapes include spheres and cylinders, especi-ally hollow cylinders.
The preferred support particles in accordance with the present invention have at least one substan-tially flat major surface and may be characterized as having a lamellate or platelet-type morphology. Some of the particles have two, or sometimes more, flat surfaces. The major dimension of a substantial por-tion of the particles having platelet-type morphology is less than about 50 microns, preferably less than about 20 microns. When alpha-alumina is employed as the support material, the platelet-type particles frequently have a morphology which approximates the shape of hexagonal plates.
The carrier materials of the present invention may generally be described as porous or microporous and they generally have median pore diameters of from about 0.01 to about 100 microns, preferably about 0.5 to about 50 microns, and most preferably about 1 to about 5 microns. Generally, they have pore volumes of about 0.6 to about 1.4 cc/g, preferably about 0.8 to about 1.2 cc/g. Pore volumes may be measured by any conventional technique, such as conventional mercury porosity or water absorption techniques.
Generally improved results have been demon-strated when the support material is composition-pure and also phase-pure. By "composition-pure" is meant a material which is substantially a single substance, such as alumina, with only trace impurities being present. The term "phase-pure" refers to the homo-geneity of the support with respect to its phase. In the present invention, alumina, having a high or exclusive alpha-phase purity (i.e., alpha-alumina) is 12~ 88 preferred. Most preferred is a material composed of at least 98 percent, by weight, alpha-alumina.
Under some conditions even small amounts of leachable sodium can adversely affect the service life of the catalyst. Notably improved results have been observed when the support contains less than about 50 parts per million ~ppm) by weight, prefer-ably less than 40 ppm, based on the welght of the total catalyst. ~he term leachable sodium, as used herein, refers to sodium which can be removed from the support by immersing the support in a 10 percent by volume nitric acid solution at 90 degres C for one hour. Suitable alpha-aluminas having concentrations of sodium below 50 ppm may be obtained commercially from suppliers such as the Norton Company. Alterna-tively, suitable alpha-alumina support materials may be prepared so as to obtain leachable sodium concen-trations below 50 ppm by the method described by Weber et al in U. S.Patent 4,3~9,134.
A particularly preferred support is a high-puri-ty alpha-alumina support, having platelet morphology, of the type disclosed in Canadian Patent Appl.
No. 515,864-8, filed August 13, 1986, by Thomas M. Notermann, entitled "Improved Catalytic System Por Epoxidation of Alkenesn, attorney's docket number 15013 The present invention includes in the catalyst at least one efficiency-enhancing salt of a member of a redox-half reaction pair. The term ~redox-half reaction~ ~s defined herein to mean half-reactions such as those found in equations presented in tables of standard reduction or oxidation potentials, also known as standard or single electrode potentials.
These equations are found in, for instance, ~Handbook `~ 15016 ~2l~tj6f~8 of Chemistryn, N. A. Lange, Editor, McGraw-Hill Book CGmpany~ Inc., pages 1213-1218 (1961) or "CRC Rand-book of Chemistry and Physics", 65th Edition, CRC
Press, Inc., Boca ~aton, F]orida, pages D lS5-162 (1984). The term "redox-half reaction pair" refers to the pairs of atoms, molecules or ions, or mixtures thereof, which undergo oxidation or reduction in such half-reaction equations. A member of a redcx-half reaction pair is, therefore, one of the atoms, mole-cules or ions that appear in a particular redox-half reaction equation. The term redox-half reaction pair is used herein to include those members of the class of substances which provide the desired performance enhancement rather than a mechanism of the chemistry occurring. Preferably, such compounds, when asso-ciated with the catalyst as salts of members of a redox-half reaction pair, are salts in which the an-ions are oxyanions, preferably an oxyanion of a poly-valent atom, i.e., the atom of the anion to which oxygen is bonded is capable of existing, when bonded to a dissimilar atom, in different valence states.
The preferred efficiency-enhancing salts are potas-sium nitrate and potassium nitrite.
The catalysts of the present invention are pre-ferably prepared by depositing catalyst material and at least one efficiency-enhancing salt, sequentially or simultaneously, on and/or within a solid porous support. The preferred catalyst material in accord-ance with the present invention comprises silver, preferably of a particle size less than about 0.5 micron. Any known method of introducing the catalyst material and efficiency-enhancing salt into the cata-lyst support may be employed, but it is preferred that the support is either impregnated or coated.
The more preferred of these is impregnation wherein, 12~688 in general, a solution of a soluble salt Gr complex of silver and/or one or more efficiency-enhancing salt is dissolved in a suitable solvent or "complex-ing/solubilizing" agent. This solution may be used to impregnate a porous catalyst support or carrier by immersing the carrier in the silver- and/or efficien-cy-enbancing salt-containing impregnation solution.
Sequential impregnation means that silver is first deposited within the carrier in one or more impregnation steps, and then salt is deposited in a separate impregnation step.
One aspect of the present invention involves the beneficial effects observed when the catalyst con-tains high concentrations of silver. In order to provide such a catalyst by impregnation, it has been found that it is preferable to deposit the silver via several impregnation steps. Thus, if a high silver-content catalyst, e.g., a catalyst containing 30 or more percent silver, is desired and a sequential impregnation procedure is to be used, a four-step process may be employed. Such a process would in-volve three silver-only impregnation steps followed by one salt-only impregnation step.
In general, a silver-only impregnation step is carried out by first immersing the support in a sil-ver-containing impregnation solution, preferably by placing the support particles in a vessel, evacuating the vessel and then adding the impregnation solu-tion. The excess solution may then be allowed to drain off or the solvent may be removed by evapora-tion under reduced pressure at a suitable tempera-ture. Typically, a silver-containing solution is prepared by dissolving silver oxide in a suitable solvent or complexing/solubilizing agent as, for example, a mixture of water, ethylenediamine, oxalic 12l~ 38 acid, silver oxide, and monoethanolamine.
After impregnation, the silver-impregnated car-rier particles are treated to convert silver salt to silver metal to effect deposition of silver on the surface of the support. This may be done by treating the impregnated particles with a reducing agent, such as oxalic acid, alkanolamine or by roasting at an elevated temperature on the order of about 100 to about 900 degrees C, preferably about 200 to about 650 degrees C, to decompose the silver compound and reduce the silver to its free metallic state. The duration of roasting is generally for a period of from about 1 to about 10 minutes, with longer times for lower temperatures, depending on the temperature used. As used herein, the term "surfacen, as applied to the support, not only inclu2es the external sur-faces of the carrier but also the internal surfaces, that is, the surfaces defining the pores or internal portion of the support particles.
The efficiency-enhancing salt may be introduced into the catalyst in any suitable manner. In gener-al, the preferred amount of efficiency-enhancing salt can be deposited in one impregnation step. After immersion of the silver loaded support in the effi-ciency-enhancing salt impregnation solution, the excess solution is generally drained and the silver-and efficiency-enhancing salt-containing support is dried, for example by heating to from 80 to 200 de-grees C. When more than one salt of a member of a redox-half reaction pair is employed, the salts may be deposited together or sequentially.
Concurrent or coincidental impregnation means that generally the final (perhaps the only) impregna-tion step involves immersion of the support in an impregnation solution which contains silver as well ~28668~3 as one or more efficiency-enhancing salts. Such an impregnation step may or may not be preceded by one or more silver-only impregnation steps. Thus, to make a high silver-content catalyst by coincidental impregnation, several silver-only impregnation steps might be carried out, followed by a silver- and effi-ciency-enhancing salt-impregnation step. A low sil-ver-content catalyst, e.g., from about 2 to about 20 weight percent silver, may be made by a single sil-ver- and efficiency-enhancing salt-impregnation step. For the purposes of this invention, these two sequences are both referred to as concurrent or coin-cidental impregnation.
The three types of impregnation solutions, name-ly, silver-containing, efficiency-enhancing salt-containing, and silver- and efficiency-enhancing salt-containing, are discussed in more detail below.
There are a large number of suitable solvents or complexing/solubilizing agents which may be used to form the silver-containing impregnating solution. A
suitable solvent or complexing/solubilizing agent, besides adequately dissolving the silver or convert-ing it to a soluble form, should be capable of being readily removed in subsequent steps, either by a washing, volatilizing or oxidizing procedure, or the like. It is also generally preferred that the sol-vents or complexing/solubilizing agents be readily miscible with water since aqueous solutions may fre-quently be employed.
Among the materials found suitable as solvents or complexing/solubilizing agents for the preparation of the silver-containing solutions are alcohols, including glycols, such as ethylene glycol, ammonia, amines and aqueous mixtures of amines, such as ethy-lenediamine and monoethanolamine, and carboxylic 128~6~8 acids, such as oxalic acid and lactic acid.
The particular silver salt or compound used to form the silver-containing impregnating solution in a solvent or a complexing/solubilizing agent is not particularly critical and any known silver salt or compound generally known to the art which is soluble in and does not react with the solvent or complex-ing/solubilizing agent may be employed. ~hus, the silver may be introduced into the solvent or complex-ing/solubilizing agent as an oxide, a salt, such as anitrate or carboxylate, for example, an acetate, propionate, butyrate, oxalate, lactate, citrate, phthalate, generally the silver salts of higher fatty acids, and the like.
Materials which may be employed in the efficien-cy-enhancing salt-containing impregnation solution to act as a solvent for the efficiency-enhancing salt include generally any solvent capable of dissolving the salt, which solvent will neither react with the silver nor leach silver from the support. ~queous solutions are generally preferred but organic li-quids, such as alcohols, may also be employed.
In order to perform coincidental impregnation, the efficiency-enhancing salt and the silver catalyst material must both be soluble in the solvent or com-plexing/solubilizing liquid used.
Suitable results have been obtained with both the sequential and coincidental procedures. Some results have indicated that greater amounts of silver with more uniform distribution of silver throughout the pill can be obtained by three or more silver-impregnation cycles. High silver-containing cata-lysts prepared by a coincidental impregnation techni-que generally provide better initial performance than those prepared by a sequential technique.

12~;~8 If the catalyst material is to be coated on the catalyst support rather than impregnated in the sup-port, the catalyst material, e.g., silver, is pre-formed or precipitated into a slurry, preferably an aqueous slurry, such that the silver particles are deposited on the support and adhere to the support surface when the carrier or support is heated to removed the liquids present.
The concentration of silver in the finished catalyst may vary from about 2 percent to 60 percent or higher, by weight, based on the total weight of the catalyst, more preferably from about 8 percent to about 50 percent, by weight. When a high silver content catalyst is employed, a silver concentration range of from about 30 to about 60 percent, by weight, is preferred. When a lower silver content catalyst is used, a preferred range is from about 2 to about 20 weight percent. The silver is preferably distributed relatively evenly over the support sur-faces. The optimum silver concentration for a par-ticular catalyst must take into consideration per-formance characteristics, such as catalyst activity, system efficiency and rate of catalyst aging, as well as the increased cost associated with greater concen-trations of silver in the catalyst material. Theapproximate concentration of silver in the finished catalyst can be controlled by appropriate selection of the number of silver-impregnation steps and of the concentration of silver in the impregnation solution or solutions.
The amount of the efficiency-enhancing salt of a member of a redox-half reaction pair present in the catalyst directly affects the activity and efficiency of the epoxidation reaction. The most preferable amount of the salt of a member of a redox-half reac-~2~

tion pair varies depending upon the alkene belng epoxidized, the compound used as the gaseous effi-ciency-enhancing member of a redox-half reaction pair, the concentration of components in the reaction 5 inlet stream, particularly the gaseous efficiency-enhancing compound and carbon dioxide, the amount of silver contained in the catalyst, the surface area, morphology and type of support, and the process con-ditions, e.g., gas hourly space velocity, tempera-ture, and pressure. The preferred efficiency-enhancing salt is potassium nitrate.
It has been noted that when conventional analyses have been conducted with catalysts prepared by co-impregnation with silver and efficiency-enh~ncing salt, not all the anion associated with thecation has been accounted for. For example, cata-lysts prepared by co-impregnation with a potassium nitrate solution have been analyzed by conventional techniques and about 3 moles of the nitrate anion have been observed or every 4 moles of the potassium cation. This is believed to be due to limitations in the conventional analytical techniques and does not necessarily mean that the unaccounted for anions a~e not nitrate. For this reason, the amount of the efflciency-enhancing salt in the catalyst is given, in some instances, in terms of the weight percentage of the cation of the effLciency-enhancing salt (based on the weight of the entire catalyst), with the un-derstanding that the anion associated with the cation is also present in the catalyst in an amount roughly proportional (on a molar basis) to the cation.
lt is generally preferable that the efficiency-enhancing salt be provided in such an amount that the finished catalyst contaLns from about 0.01 to about 5.0 percent, by weight, of the cation of the salt, based on the total weight of the catalyst, more pref-erably from about 0.02 to about 3.0 weight percent, most preferably from about 0.03 to about 2.0 weight percent. The approximate concentration of efficien-cy-enhancing salt in the finished catalyst can be controlled by appropriate selection of the concentra-tion of efficiency-enhancing salt in the salt-impreg-nation solution.
When more than one salt of a member of a redox-half reaction pair is employed, the salts may bedeposited together or sequentially. It is preferred, however, to introduce the salts to the support in a single solution, rather than to use sequential treat-ments using more than one solution and a drying step between impregnation steps, since the latter tech-nique may result in leaching the first introduced salt by the solution containing the second salt.
Concurrent or coincidental impregnation may be ac-complished by forming an impregnating solution which contains the dissolved efficiency-enhancing salt of a member of a redox-half reaction pair as well as sil-ver catalyst material. Silver-first impregnation can be accomplished by impregnating the support with the silver-containing solution, drying the silver-con-taining support, reducing the silver, and impreg-nating the support with the efficiency-enhancing salt solution.
Reaction conditions maintained in the reactor during operation of the process are those typically used in carrying out epoxidation reactions. Tempera-tures within the reaction zone of the reactor gener-ally range from about 180 to about 300 degrees C and pressures generally range from about 1 to about 30 atmospheres, typically from about 10 to about 25 atmospheres. The gas hourly space velocity (GHSV) lZB~688 may vary, but it will generally range from about 1,000 to about 16,000 hr~l.
The product, for example, ethylene oxide, is recovered from the reactor effluent, e.g., by an absorption process. One such method comprises sup-plying the reactor effluent stream to the bottom of an absorption column while adding a solvent, for example, water, to the top of the absorption col-umn. The solvent preferably absorbs the ethylene oxide and carries it out of the bottom of the ab-sorption column, while the remainder of the reaction effluent passes out of the top of the absorption column to form the recycle stream. The desired pro-duct is thereafter recovered, for example, by passing the solvent and absorbed product through a stripper.
As noted above, it may be preferable to remove a portion of the recycle stream prior to returning the recycle stream to the reaction zone. It is generally preferable to selectively remove certain compounds.
An absorption column or other types of separation means can be used to provide a selective purge.
The recycle stream generally contains the dilu-ents and inhibitor~ fed to the system, unreacted alkene and oxygen, together with by-products of the reaction, such as carbon dioxide and water, and any minor amount of alkene oxide which is not recovered as product. After removal of the purge stream, the recycle stream is returned to the reaction zone, preeerably being mixed with the makeup feedstream prior to or as it enters the reaction zone.
The makeup feedstream replaces reactants, i.e., alkene and oxygen-containing gas, as well as other materials not contained in the recycle stream in sufficient amounts. Alkene, as used herein, refers 128~ 8 to cyclic and acyclic alkenes which are in a gaseous state or have significant vapor pressures under epox-idation conditions. Typically these eompounds are characterized as having on the order of 12 carbon atoms or less and which are gaseous under epoxidation conditions. In addition to ethylene and propylene, examples of alkenes which may be used in the present invention include such compounds as butene, dodecene, cyclohexene, 4-vinylcyclohexene, styrene, and norbor-nene.
The oxygen-containing gas employed in the reac-tion may be defined as including pure molecular oxy-gen, atomic oxygen, any transient radieal species derived from atomie or molecular oxygen eapable of existence under epoxidation conditions, mixtures of another gaseous substance with at least one of the foregoing, and substances capable of forming one of the foregoing under epoxidation conditions. Such oxygen-containing gas is typically oxygen introduced to the reactor either as air, eommereially pure oxy-gen or any other gaseous substanee whieh forms oxygen under epoxidation eonditions.
The makeup feedstream may also contain one or more additives, for example, a performance-enhancing gaseous halide, preferably an organie halide, includ-ing saturated and unsaturated halides, such as 1,2-dichloroethane, ethyl chloride, vinyl chloride, methyl ehloride, and methylene ehloride, as well as aromatic halides. The performance-enhancing gaseous halide preferably eomprises 1,2-diehloroe~hane and/or ethyl ehloride. ~n addition, a hydroearbon, sueh as ethane, ean be included in the makeup feedstream.
The makeup feedstream may also contain a diluent or ballast, such as nitrogen, as is the case when air is used as the oxygen-eontaining gas.

12~

The makeup feedstream generally also includes at least one gaseous efficiency-enhancing member of a redox-half reaction pair. The phrase "gase~us effi-ciency-enhancing compound", as used herein, is an alternative expression for the expression "at least one gaseous efficiency-enhancing member of a redox-half reaction pair. n Both phrases are therefore meant to include single gaseous efficiency-enhancing members of redox-half reaction pairs as well as mix-tures thereof. The term "redox-half reaction pair"
has essentially the same meaning as defined in con-nection with efficiency-enhancing salts, above. The preferred gaseous efficiency-enhancing materials are, preferably, compounds containing oxygen and an ele-ment capable of existing in more than two valencestates. Examples of preferred gaseous efficiency-enhancing members of redox-half reaction pairs in-1 de NO, NO2, N2O4, N2O3, any substance capable offorming gaseous NO and/or NO2 under epoxidation con-ditions, or mixtures thereof. In addition, mixturesof one of the compounds listed above, particularly NO, with one or more of PH3, CO, SO3, and SO2 are suitable. Nitric oxide is particularly preferred.
In some cases it is preferable to employ two members of a particular half-reaction pair, one in the efficiency-enhancing salt and the other in the gaseous efficiency-enhancing compound employed in the feedstream, as, for example, with a preferred combin-ation of RNO3 and NO. Other combinations, such as KNO3/N2O3, KNO3/NO2, and KNO2/N2O4 may also be em-ployed in the same system. In some instances, the salt and the gaseous members may be found in half-reactions which represent the first and last reac-tions in a series of half-reaction equations of an overall reaction.

12~688 The gaseous efficiency-enhancing member of a redox-half reaction pair is preferably present in an amount that favorably affects the efficiency and/or the activity. The precise amount is determined, in part, by the particular efficiency-enhancing salt employed and the concentration thereof, as well as the other factors noted above which influence the amount of efficiency-enhancing salt. Suitable ranges of concentration for the gaseous efficiency-enhancing compound are generally dependent upon the particular alkene which is being epoxidized, larger amounts of the gaseous efficiency-enhancing compound generally being preferable with higher alkenes. For example, in an ethylene epoxidation system, a suitable range of concentration for the gaseous efficiency-enhancing member of a redox-half reaction pair is typically about 0.1 to about 100 ppm by volume of the reaction inlet stream. Preferably, the gaseous efficiency-enhancing compound is present in the reaction inlet stream in an amount within the range of from 0.1 to 80 ppm, by volume, when about 3 percent, by volume, carbon dioxide is present in the reaction inlet stream. When nitric oxide is employed as the gaseous efficiency-enhancing compound in an ethylene epoxida-tion system, it is preferably present in an amount offrom about 0.1 to about 60 ppm by volume. When about 3 percent, by volume, carbon dioxide is present in the reaction inlet stream, nitric oxide, if used as the gaseous efficiency-enhancing compound, is prefer-ably present in an amount of from about 1 to about 40ppm. On the other hand, in a propylene or higher alkene epoxidation system a suitable concentration of the gaseous efficiency-enhancing compound is typical-ly higher, e.g., from about 5 to about 2,000 ppm by volume of the reaction inlet stream when using nitro-1~8~688 gen ballast.
Similarly, the concentration of the performance-enhancing gaseous halide, if one is used, is depen-dent, inter alia, upon the particular alkene which is being oxidized. A suitable range of concentration for gaseous halide in an ethylene epoxidation system is typically from about 0.1 to about 60 ppm by volume of the reaction inlet stream. A suitable concentra-tion for gaseous halide in the reaction inlet stream in a propylene epoxidation system is typically from about 5 to about 2,000 ppm by volume when using ni-trogen ballast. The preferred concentration of per-formance-enhancing gaseous halide, if one is used, varies depending on the particular compounds used as the efficiency-enhancing salt and the gaseous effi-ciency-enhancing compound and the concentrations thereof, as well as the other factors noted above which influence the preferred amount of efficiency-enhancing salt.
The ranges for the concentration of alkene, oxygen, hydrocarbon, carbon dioxide and nitrogen or other ballast gas such as methane, in the reaction inlet stream, are dependent upon the alkene being epoxidized. The tables below show typical ranges for the materials (other than the efficiency-enhancing compound and the gaseous halide) in the reaction inlet stream for the epoxidation of ethylene (Table A) and propylene (Table B).

12~688 Table A

Component Concentration 5 E.hylene at least about 2, often about 5 to about 50, volume percent 10 Oxygen about 2 to about 8 volume percent Hydrocarbon about 0 to about 5 volume percent Carbon Dioxide about 0 to about 7 volume percent Nitrogen or other remainder 20 ballast gas, e.g., methane Table B

Component Concentration 5 Propylene about 2 to about 50 volume percent Oxygen about 2 to about 10 volume percent Hydrocarbon about 0 to about 5 volume percent Carbon Dioxide about 0 to about 15 volume percent Nitrogen or other remainder ballast gas, e.g., methane The ranges set out in Table B for the concentra-tion of materials in the reaction inlet stream may be useful for epoxidation of higher alkenes, e.g., al-kenes having from 4 to 12 carbon atoms.
In the manufacture of ethylene oxide, the water is preferably present in the reaction inlet strea~ in an amount of from about 0.25 to about 1.5, more pref-erably 0.25 to 1Ø volume percent. For the manufac-ture of propylene oxide, the water is preferably present in an amount of from about 0.25 to about 10 volume percent.
As previously noted, water can be added to the reaction inlet stream continuously or intermittent-ly. Continuously is preferred. Also, water is pref-35 erably introduced contemporaneously or prior to the 12lY668~3 introduction of carbon dioxide since the beneficial effect of water is greater when it is $ntroauced before carbon dioxide is present in significant amounts in the reaction zone.
The ~nvention will be better understood by ref-erence to the following examples which are offered by way of illustration and not by way of limitation.

Exam?le 1.
A supported silver catalyst as described below under the heading Method Of Preparation Of Catalyst was tested by placing 80 ml of the catalyst in an autoclave reactor using the feedstream set out in Table I under the conditions set out in Table II.
The autoclave was a backmixed, bottom-agitated Mag-nedrive* autoclave as described in Figure 2 of the paper by J. M. Berty entitled ~Reactor For Vapor Phase-Catalytic Studies~ in Chemical Enqineerin~
Progress, Volume 70, Number 5, pages 78-84, 1974.

TABLE I

Makeup Feedstream Composition ComPonentAmount (BY Volume) ethylene 30 percent oxygen 8 percent chloroethane 5 ppm nitr~c oxide 5 ppm nitrogen balance.

* - Trade~ark ~5016 12~688 i TAsLE I~

GHSV 8,000 hr 1 Temperature 240 degrees C
5 Pressure 275 psLg.

The efficiency and activity of the catalyst prior to the addition of water using the feedstream as described in Table 1 were 89 percent and 12.7 pounds of ethylene oxide per cubic foot of catalyst per hour (calculated based on the 80 milliliters of catalyst present in the autoclave), respectively.
Water comprising one-half volume percent (based on the feedstream composition) was then fed into the autoclave with a Varian TM 8500 liquid chromatography pump. The activity and efficiency were 89.9 percent and 13.9 pounds per cubic foot per hour, respective-ly. Carbon dioxide comprising 1 volume percent of the makeup feedstream was then introduced into the autoclave, together with the one-half volume percent water previously referred to. The efficiency and the activity of the catalyst were then determined to be 89.0 percent and 6.9 pounds per cubic foot per hour, respectively. Thereafter, the water feed to the autoclave was terminated while maintaining the flow of 1 percent by volume carbon dioxide. The efficien-cy and activity of the system were then found to be 85.9 percent and 5.7 pounds per cubic foot per hour, respectively.

128f~688 .

Method Of PreParation Of Catalyst-.

A silver-containing impregnation solution was prepared by dissolving 142.5 grams of ethylenediamine with 200.0 grams of distilLed water and stirring for a period of 10 minutes. ~o the st~rred solutian were slowly added 142.5 grams of oxalic acid dihydrate.
The resulting solution was stirred for 10 minutes.
To this solution were added, in portions, 249.6 grams of silver oxide. The resulting silver-containing 601ution was thereafter stirred for an additional hour and 49.9 grams of monoethanolamine were then added to the stirred silver-containing solution.
Stirrlng was continued for an additional 10 min-utes. This solution was then diluted to a totalvolume of 750 ml by addition of distilled water.
Righ-purity alpha-alumina support pellets (268.2 grams), having platelet morphology of the type disclosed in Canadian Patent Appl. Ser. No. 515,864-8, filed August 13, 1986, having a surface area o~ 1.06 meters squarea per gram and a porosity of 0.74 cc.
per gram were placed in a tube which was then evacu-ated, following which the support pellets were im-pregnated by immersing them in the silver-containing impregnation solution, formed as described above, for 1 hour. Excess impregnation solution was then drained and the resulting pellets were then belt-roasted at 500 degrees C in a 66.5 SCFH air flow for 2.5 minutes. The catalyst pellets were then immersed in a solution comprising 4.3 grams potassium nitrate dissolved in 300 ml distilled water. After standing in the solution for 15 minutes, the pellets were removed and dried at 120 degrees C in an oven for 2 hours. The finished catalyst contained 17.0 percent 35 ~ilver ~nd 0.31 percent potassium.

; 15016 2~6813 ( Example 2 - Coincidental or Coimpregnation Method Of Preparation Of A Potassium Nitrate-Containing Supported Hiqh Sil~er Concentration Catalvst-A first silver-containing impregnation solution was prepared by dissolving 1,292.8 grams ethylene-diamine with 1,281.6 grams of distilled water and stirring for a period of 10 minutes. To the stirred solution were slowly added 1~294.8 grams of oxalic acid dihydrate. The resulting solution was stirred for 10 minutes. To this solution were added, in portions, 2,268.4 grams of Ag20. The resulting sil-ver-containing solution was thereafter stirred for an additi~nal hour and 453.6 grams of monoethanolamine were then added to the stirred silver-containing solution. Stirring was continued for an additional 10 minutes. This solution was then diluted to a total volume of 5,000 ml by addition of distilled water.
High-purity alpha-alumina support pellets (1,925.4 grams) having platelet morphology of the type disclosed in Ca~adian Pa~ent Application Ser. No.
515,864-8, filed 8/13/~6, hav~ng a sur~ace area of about 1.2 m~g and a porosity of about 0.8 cc/g were placed in a tube which was then evacuated, following which a first impregnation was conducted by immersing the support particles in the first silver-containing impregnation solution formed as described above, for one hour. Excess impregnation solution was then drained and ehe cesulting pellets were then belt-roasted at 500 degrees C in a 66 SCF~ air flow for 2.5 minutes. The resulting material contained 24.9 35 percent ~ilver by weight.

n l ~

~B6688 A co-impregnation solution was prepared by plac-ing 1,260.5 grams of ethylenediamine into a 5,000 ml beaker and mixing therewith 1,249.6 grams of dis-tilled water to form a solution. To the stirred 5 solution were slowly added 1,262.4 grams of oxalic acid dihydrate and, with continuous stirring, 2,211.7 grams of silver oxide were slowly added. When dis-solution was complete, 442.3 grams of monoethanol-amine were added directly to the solution. To the 10 silver-containing solution were added 26.4 grams of potassium nitrate dissolved in 50 milliliters of dis-tilled water. To the resulting solution was added sufficient water to dilute the solution to 4,875 ml. The silver-impregnated catalyst pellets (2,495.6 15 grams) were impregnated in a manner similar to the first impregnation described above. The resulting catalyst contained 39.8 weight percent silver and 0.098 weight percent potassium.

Example 3 - Sequential Preparation Of A Potassium Nitrate-Containing Supported ~iqh Silver Concentration CatalYst:

A silver-containing impregnation solution was prepared by dissolving 787.0 grams ethylenediamine with 780.0 grams of distilled water and stirring for a per$od of 10 minutes. To the stirred solution were slowly added 788.3 grams of oxalic acid dihydrate.
The resulting s~lution was stirred for 10 minutes.
To this solution were added, in portions, 1,380.8 grams of Ag2O. The resulting silver-containing solu-tion was thereafter stirred for an additional hour, following which 276.3 grams of monoethanolamine were added to the stirred silver-containing solution.
Stirring was continued for an additional 10 min-12~ 8 I

utes. This solution was then diluted to a total volume of 3,125 ml by addition of distilled water.
High-purity alpha-alumina support pellets (1,172.5 grams), having platelet morphology, of the type disclosed in Canadian Patent Application Ser. No.
515,86~-8, filed 8/13/86, having a surface area of about 1.2 m~/g and a porosity of about 0.~ cc/g were placed in a tube which was then evacuated, following which the support pellets were impregnated by im-mersing them in a portion of the impregnating solu-tion formed as described above for one hour. The excess impregnation solution was drained and the resulting pellets were then belt-roasted at 500 de-grees C in a 66 SCFH air flow for 2.5 minutes. The resulting material contained 24.3 percent silver, by weight.
A second silver-containing impregnation solution was prepared in a manner similar to the preparation of the silver-containing impregnation solution de-scribed above, employing 472.2 grams ethylenediamine, 468.0 grams distilled water, 472.9 grams oxalic acid dihydrate, 828.5 grams silver nitrate, 165.8 grams monoethanolamine, and diluted to a total volume of 18.75 milliliters by addition of distilled water.
2S ~igh-purity alpha-alumina support pellets (703.5 grams), similar to those employed above, were then impregnated with the solution described immediately above in a manner similar to the first impregnation described above. The resulting material contained 24.6 precent silver.
~ he two batches of impregnated alpha-alumina formed as described above were then combined.
A ~econd impregnation cycle was perfor~ed by impregnating the silver-containing catalyst material 35 of the combined batches with a fresh ilver impregna-lZ~688 tion solution. This solution was prepared in a man-ner similar to the impregnation solutions used in the first impregnation cycle, employing 1,196.2 grams ethylenediamine, 1,185.6 grams distilled water, 1,198.1 oxalic acid dihydrate, 2,098.7 grams silver oxide, 419.9 grams monoethanolamine, and diluted to 4,750 milliliters by addition of distilled water.
The silver-containing catalyst material formed in the first impregnation cycle was impregnated with the fresh silver impregnation solution in a manner simi-lar to the manner in which the first impregnation cycle was conducted. The silver-containing catalyst resulting from the second impregnation cycle con-tained 38.5 weight percent silver.
Potassium nitrate was incorporated into the catalyst material by immersing 3,040.6 grams of the silver-impregnated pellets in a solution containing 24.8 grams KNO3 in 4000 ml of distilled water. After draining, the material was dried at 120 degrees C for 2 hours to yield a catalyst containing 38.5 percent silver and 0.010 percent potassium, by weight.
The catalysts described above in Examples 2 and 3 may be used in carrying out the process o~ this invention.

Claims (17)

1. An improved process for the epoxidation of alkene selected from the group consisting of cyclic and acylic alkenes containing up to about 12 carbon atoms to form the corresponding alkene oxide wherein said alkene is contacted with oxygen-containing gas in a reaction zone in the presence of (i) a performance-enhancing gaseous organic halide compound, (ii) at least one gaseous efficiency-enhancing member of a redox-half reaction pair selected from compounds containing oxygen in combined form with a polyvalent element, (iii) a supported silver catalyst, comprising a catalytically effective amount of silver and an efficiency-enhancing amount of at least one efficiency-enhancing salt selected from the group consisting of salts of oxyanions of polyvalent elements on a support, said oxyanion of said efficiency-enhancing salt and said gaseous efficiency-enhancing member (ii) containing a common polyvalent element and either belonging to the same redox-half reaction pair or belonging to different half reaction pairs in a series of chemically-related half reaction equations, and (iv) carbon dioxide, wherein the improvement comprises introducing water into said reaction zone in an amount which is sufficient to improve the efficiency and/or activity of the process.

2. An improved process for the epoxidation of ethylene to form ethylene oxide wherein said ethylene is contacted with oxygen-containing gas in a reaction zone in the presence of (i) a performance-enhancing gaseous organic halide compound, (ii) at least one gaseous efficiency-enhancing member of a redox-half reaction pair selected from compounds containing oxygen in combined form with a polyvalent element, (iii) a supported silver catalyst, comprising a catalytically effective amount of silver and an efficiency-enhancing amount of at least one efficiency-enhancing salt selected from the group consisting of salts of oxyanions of polyvalent elements on a support, said oxyanion of said efficiency-enhancing salt and said gaseous efficiency-enhancing member (ii) containing d common polyvalent element and either belonging to thesame redox-half reaction pair or belonging to different half reaction pairs in a series of chemically-related half reaction equations, and (iv) carbon dioxide, wherein the improvement comprises introducing water into said reaction zone in an amount which is sufficient to improve the efficiency and/or activity of the process.

3. An improved process for the epoxidation of propylene to form propylene oxide wherein said propylene is contacted with oxygen-containing gas in a reaction zone in the presence of (i) a performance-enhancing gaseous organic halide compound, (ii) at least one gaseous efficiency-enhancing member of a redox-half reaction pair selected from compounds containing oxygen in combined form with a polyvalent element, (iii) a supported silver catalyst, comprising a catalytically effective amount of silver and an efficiency-enhancing amount of at least one efficiency-enhancing salt selected from the group consisting of salts of oxyanions of polyvalent elements on a support, said oxyanion of said efficiency-enhancing salt and said gaseous efficiency-enhancing member (ii) containing a common polyvalent element and either belonging to the same redox-half reaction pair or belonging to different half reaction pairs in a series of chemically-related half reaction equations, and (iv) carbon dioxide, wherein the improvement comprises introducing water into said reaction zone in an amount which is sufficient to improve the efficiency and/or activity of the process.

4. The process of claims 1, 2 or 3, wherein said at least one gaseous efficiency-enhanting member of a redox-half reaction pair is selected from the group consisting of nitrogen monoxide, nitrogen dioxide, N2O3, N2O4, a gas capable of generating nitrogen monoxide or nitrogen dioxide under epoxidation conditions, or mixtures thereof.

5. The process of claims 1, 2 or 3, wherein said efficiency-enhancing salt of a member of a redox-half reaction pair is potassium nitrate.

6. The process of claim 4, wherein said efficiency-enhancing salt of a member of a redox-half reaction pair is potassium nitrate.

7 . The process of claim 2 , wherein carbon dioxide is present in said reaction inlet stream in an amount up to about 7 percent by volume.

8. The process of claim 6. wherein said gaseous halide is selected from the group consisting of ethyl chloride, 1,2-dichloroethane or mixtures thereof.

9. The process of claims 1, 2 or 3, wherein said gaseous efficiency-enhancing member of a redox-half reaction pair and said efficiency-enhancing salt of a member of a redox-half reaction pair are members of the same redox-half reaction pair.

10. The process of claims 1, 2 or 3, wherein said gaseous efficiency-enhancing member of a redox-half reaction pair is selected from the group consisting of mixtures of phosphine, carbon monoxide, sulfur dioxide and sulfur trioxide with a nitrogen oxide selected from the group consisting of NO, NO2, N2O4 and N2O3.

11. The process of claim 6, wherein said catalyst comprises from about 2 to about 50 weight percent silver.

12. The process of claim 6, wherein said catalyst is provided in a fluidized bed.

13. The process of claim 6, wherein said catalyst is provided in a fixed bed.

14. The process of claim 6, wherein said water is introduced continuously into the reaction inlet stream of said reaction zone.

15. The process of claim 6, wherein said water is introduced intermittently into the reaction inlet stream of said reaction zone.

16. The process of claim 2, wherein said water is introduced into the reaction inlet stream of said reaction zone in an amount such that it comprises from about 0.25 to about 1.5 volume percent of said reaction inlet stream.

17. The process of claim 2, wherein said water is introduced into the reaction inlet stream of said reaction zone in an amount such that it comprises from about 0.25 to about 1.0 volume percent of said reaction inlet stream.