CA1270452A - Dimensionally stable thermoplastic tubular articles - Google Patents

Abstract

DIMENSIONALLY STABLE THERMOPLASTIC TUBULAR
ARTICLES

ABSTRACT OF THE DISCLOSURE

A food container comprising an open-ended cylin-drical body which is made of a crystallizable poly-ethylene terephthalate material, and end closures at each end of the body forming with the body a closed container, the body material being biaxially oriented and the container body having been head-set, while restrained against radial or axial shrinkage, at a temperature between about 180°C. and about 240°C., whereby the container is able to withstand hot-filling, pasteurisation or sterilisation temperatures of up to about 120°C. without undergoing shrinkage of its linear dimensions by more than 3%.

Description

~1~ A IC-~ ~ U~

DIMENSIONALLY STABLE T~ERMOPLASTIC TUBULAR
ARTICLES
~his application is a division of Canadian Serial Serial No. 501,674, filed February 12, 1986.
This invention rela~es to thermoplastic tubular articles made from crystallisable polymers and dimension-ally stable up to a specific elevated temperature, which articles are particularly tubular bodies of saturated linear polyester materials such as polyethylene tereph-10 thalate, intended for processable food and beverage containers.
It is known that biaxial drawing bf a thermoplastic saturated linear polyester material, such as polyethylene terephthalate, can improve its mechanical properties while inducing a degree of biaxial orientation and crystallisation, 15 without impairing the clarity of the material. The material will, however, shrink if heated above the temperature at which it was drawn. It is known that the tendency of biaxially drawn polyester film material to shrink can be decreased by annealing the material under restraint, utilising temperatures in the 20 range 150C to 230C, the process being known as heat setting.
Biaxial drawing is also effected, for example, in the stretch-blow moulding of polyethylene terephthalate bottles.
Another method of forming biaxially oriented tubular articles which may be used as bodies for processable food containers is 25 disclosed in our copending U.K.Patent Application No. 8037137, published under No. 2089276A. The forming process described therein involves longitudinal stretching and radial expansion under internal fluid pressure within a mould and is normally carried out at a temperature in the range from 75C to 120C.
30 The tubular bodies thereby produced are dimensionally stable up to the temperatures encountered in many container filling operations, but a heat-setting treatment is necessary if the containers are to be filled with hot product (e.g. at 80C

: .
.

: ' :.,; - ,.. .
. . ~
~ :.
., .

. ... ..

3L~7q~

to 100C) or are to be subjected to pasteurisation (at about 60C to 100C) or sterilisation (at about 120C). Without such a heat-setting treatment, the thermoplastic linear polyester material (e.~ polyethylene terephthalate) would shrink and distort to an unacceptable degree during the hot filling or processing, as a result of relaxation of strained portions of the material back into their preferred state in which the molecular chains are coiled rather than extended. In the heat-setting treatment described in Specification 2089276A, the tubular articles were held for a time at a temperature at least equal to, and preferably somewhat greater than, the sterilisation or pasteurisation temperature whilst restraining them from shrinking beyond their desired circumferential and longitudinal dimensions. The restraint was provided by internal fluid pressure, so as to set the strained? oriented amorphous portions of the polyester material by at least partial crystallisation and relaxation. Internal fluid pressure cannot be conveniently used when the tubes have been cut so as to be open at both ends, and it is not convenient to combine the heat-setting with the forming process of our Specification No.
2089276A because it would involve additional complication and extended process times.
European patent application published under No. 0081451 discloses a heat-setting process and apparatus for making closed-ended containers from PET. The process comprises deep-drawing a pre-heated sheet of PET into a heated female mould by means of a male plug, which is at a temperature below the glass transition temperature lTg) of the PET. The mould is kept at a temperature above Tg, typically 140C. Air pressure introduced around the plug is used to blow the plug-formed article into contact with the mould for heating it above Tg. When it has been in contact with the mould for long .
; ` ; :

~ 7~5~

enough to be heat-set, it is allowed to shrink back into contact with the plug which restrains it from further shrinkage and cools it to a temperature below the heat-set temperature. Contact between the heat-set article and the plug can be released by forcing air through an axial passage in the plug. In this process the heat-setting is essentially carried out while the article is held against the female mould by internal gas pressure, rather than when it is restrained from axial shrinkage by the plug. The heat-set operation cannot be carried out independently of the biaxial drawing, and is clearly not applicable for heat-setting open-ended tubes.
According to the present invention, there is provided a food container comprising an open-ended cylindrical body which is made of a crystallisable polyethylene tere-phthalate material. End closure means at each end of the body form with the body a closed container. The body material is biaxially oriented and the container body is heat-set, whilst restrained against radial or axial shrinkage, at a temperature between about 180C.
and about 240C., whereby the container is able to with-stand hot-filling, pasteurisation or sterilisation temperatures of up to about 120C. without undergoing shrinkage of its linear dimensions by more than 3%.
The heat-setting operation is effected independently of the forming operation and does not cause problems there-in. A residual linear shrinkage of up to 3% is usually found after heat-setting, but it can be eliminated by a further step of re-heating the article to the specific elevated temperature without internal restraint against shrinkage. Such residual shrinkage may be used to eliminate or reduce head space in a container having a body heat-set by the method of the invention.

.
.. : .
:; .:

~ .

~2~ ;2 Where the polymer is a saturated linear polyester, the temperature to which the tube is heated on the mandrel is preferably a~ least 60 higher than the specific elevated temperature, and in particular, where polyethylene terephthalate is used, the specific elevated temperature is preferably about 120C and the tube is heated to at least 180C on the mandrel.
The degree of dimensional stability which is achieved depends on the temperature to which the tube is heated on the mandrel (the "heat-setting temperature") and the time for which the tube is maintained at this temperature, and it may be adjusted to the particular requirements for which the tubular articles are made. For example, if it is desired that the linear dimensions of the article should not alter by more than 3~ when it is heated to a specific elevated temperature of 120C, the tube may be heated at 180C for a period of 1 to 5 minutes or, preferably, at 240C for 12 to 15 seconds.
The contact between the tube and mandrel may be released by forcing fluid (e.g. air) under pressure from inside the mandrel through small holes in its surface to form an fluid cushion between the tube and mandrel. Alternatively it may be released by collapsing at least a part of the mandrel surface inwards.
The tubular article may be given a shape which departs from that of a plain cylindrical tube by providing the mandrel with a complementary shape, which is adopted by the tube as it shrinks on to the mandrel. For example, the tubular article may be formed with circumferential beads by providing the mandrel with corresponding circumferential projections. Other shapes may be produced in this manner, such as tapered, barrelled or waisted tubes, or tubes of rectangular, oval or other cross-sections.

.

,. , ~' :

- , :"

~2~ 5~

When making a tubular article which is open at both ends, the clamping is preferably effected by circumferentially clamping both ends of the tube to the mandrel. The tube may then be cut into individual lengths before it is separated from the mandrel. For example, the tube may be cut by knives which penetrate through the tube material into circumferential grooves in the mandrel as the mandrel is rotated.
When making a tubular article which is closed at one end, preferably a mandrel is used which has a correspondingly shaped closed end and clamping is effected by clamping the other, open end of the tube to the mandrel. The open end of the tube may be clamped axially against a radially extending flange on the mandrel. Preferably the closed end of the tube is additionally clamped axially against the closed end of the mandrel.
In a preferred embodiment of the invention, using a plurality of vertical hollow mandrels of high thermal conductivity, each mandrel is indexed past operating stations at which:-(a) the tube is fitted over the mandrel, whose temperature is below the glass transition temperature of the polymer, (b) clamps are applied to the tube to clamp it to the mandrel, (c) a heating element is introduced into the interior of the mandrel to heat it to a temperature at least 60C higher than the specific elevated temperature, (d) the said higher temperature is maintained for a time sufficient to ensure the required degree of dimensional stability, (e) the heating element is removed, and the tube is cooled to below the specific elevated temperature, (f) the clamps are released, , (g) the ends of the mandrel are sealed and air under pressure is introduced into it and forced out through , . -: .;

s~

small holes in its surface to release contact between the tube and the mandrel, and (h) the tube is removed from the mandrel.
Where the tube is long enough to make several open-ended articles (e.g. container bodies), it is convenient to arrange that, after cooling of the tube, the mandrel is rotated and knives are brought into contact with the tube to cut it into individual lengths.
The invention also pertains to apparatus for making a thermo-plastic tubular article of a crystallisable polymer which is heat-set so as to be dimensionally stable up to a specific elevated temperature, comprising a mandrel having a plurality of apertures in its surface, heating means for heating the mandrel internally and thereby heating the article to a temperature higher than the specific elevated temperature, clamping means for clamping an at least partially biaxially oriented tube of the crystallisable polymer to restrain axial shrinkage of the tube, and a pressurized fluid supply for supplying fluid under pressure from inside the mandrel through the plurality of apertures in its surface, to release contact hetween the mandrel and a tube shrunk thereon.
Specific embodiments of the invention will now be described in more detail by way of example and with reference to the accompanying drawings in which:-Figure 1 is a diagrammatic perspective view of apparatus including a mandrel for use in heat-setting tubular bodies for making multiple container bodies by the method of the invention, Figure 2 is a diagrammatic sectional view of a modified form of the mandrel, showing a heating element inserted therein, Figure 3 is a view similar to Figure 2 of a further form of mandrel for heat-setting single container bodies, Figure 4 is a diagrammatic cross-sectional view showing a modification of the mandrels of Figures 1, 2 or 3, Figure 5 is a perspective view of a thermally processable container with a body heat-set by the method of the invention on a mandrel as shown in any one of Figures 1 to 4, appearing with Figure 2, and Figure 6 is a diagrammatic sectlonal view of another form of mandrel for use in heat-setting tubular bodies which are .. . ..

-~, ,. ,, :
... ...
,: , ;

closed at one end.
The embodiments of the invention illustrated in Figures 1 to 4 are particularly concerned with the production of tubular bodies of biaxially oriented polyethylene terephthalate (PET) for thermally processable food containers as illustrated in Figure 5, which have end closures seamed to the ends of the body. The tubular bodies, open at both ends, are made from tubes of at least partly biaxially oriented PET produced by the process disclosed in our prior British Patent Application No.
8037137 (Publication No. 2089276A). As explained above, it is necessary to carry out a heat-setting treatment on the oriented PET tube to ensure that the containers will be able to withstand hot-filling, pasteurisation or sterilisation processes at temperatures of from 60C to 120C, without unacceptable shrinkage. In practice, it is a requirement that the container bodies have sufficient dimensional stability to match the end closures in a~precise manner for the production of gas-tight seams and to avoid stressing the seams excessively through subsequent shrinkage.
Figure 1 illustrates apparatus including a mandrel on which the heat-setting process can be carried out in accordance with the invention. The cylindrical mandrel body 10 is hollow and its ends are closed by end plugs 11 and 1`2 carried by rotatable shafts 111 and 121 which can be shifted axially to enable the mandrel to be removed. Plug 12 and shaft 121 have an inlet passage 14 and control valve 141 for compressed air. The mandrel body 10 is provided with a plurality of small holes 16 in its surface. At each end, it is provided with a circumferential clamp member, e.g. in the form of a snap-action clip or clamping band 20. Circumferential grooves 22, approximately 1 mm. in width, are formed in the surface of the mandrel body 10 at intervals corresponding to the length of the container bodies to be produced. A shaft 15 carrying rotary knives 17 is mounted parallel to the mandrel 10 on pivotal brackets 19 so as to be capable of being shifted towards the mandrel so thst the kni~e~ an ~:-er i~to the groov 5 22.

. . . . ..

: . :

5~

Figure 2 illustrates an alternative fonm of mandrel body 101 in the vertical position. The foot of the body 101 has a flange 24 to support a tube 26 of at least partially biaxially oriented PET resin. The outer diameter of the mandrel body 101 is clearly shown to be only very slightly less than that of the PET resin tube 261 so that the latter can be fitted thereover without excessive friction but also without substantial play.
In this embodiment, the mandrel body 101 is made of a material of high thermal conductivity but is sufficiently thin in section to have a small thermal capacity. The interior of the mandrel body 101 is slightly tapered towards the top so as to make contact with a correspondingly shaped heating element 28 when the latter is inserted from below, as shown in Figure 2, to fill the interior of the mandrel.
Figure 3 illustrates a mandrel body 102 which is similar to that of Figure 2 but of lesser height, for production of single container bodies. In this case, a circumferential groove 18 is provided at the upper end of the mandrel body 102 to co-operate with clamping members 201 in the form of laterally movable

2 0 half-rings.
In use of the mandrels of Figures 1 to 3, when a PET tube 26 has been fitted over the mandrel body 10, 101 or 102, and the ends of the tube 26 have been clamped by means of clamp members 20, the temperature of the mandrel and tube is raised, e.g. by introduction of the heating member 28 of Figures 2 and 3, from an initial temperature below the glass transition temperature of the resin to a temperature which is at least 60C above the specific elevated temperature, up to which the can bodies are to be dimensionally stable. The temperature to which the mandrel is heated may range from 125C to 240C, for heat-setting the PET tube up to specific elevated temperatures ranging from 65C
to 180C, but it is preferably from 18QC to 240C, at which the r,ate of annealing of the PET resin is sufficiently high to obtain rapid ,heat-setting. Using a temperature of 240C, it is only necessary to ensure that the whole of the PET resin attains this temperature ~or about 12 to 15 seconds. Temperatures above 240C should preferably not be used because the material can become cloudy and embrittled. The PET tube 26 shrinks radially s into contact with the mandre1 10, 101, or 102 but is restrained from any substantial radial or axial shrinkage by the mandrel and the clamps 20, 201. The supply of heat is then stopped, e.g. by withdrawing the heating member 28, and the tube and mandrel are then allowed to cool to a temperature below the said specific elevated temperature (i.e. the temperature to which the tube has been heat-set).
In the cases of Figures 1 and 2, the mandrel bodies 10, 101 are now rotated and the knives 17 (Figure 1) are brought into contact with the rotating PET tube 26 so as to penetrate through lS the tube material into the circumferential grooves 22 and thereby cut the tube into individual can body lengths. In the case of Figure 3 this step is unnecessary, but the groove 18 and clamp members 201 form a circumferential groove in the top of the body to facilitate subsequent seaming of an end closure to it.
Finally the clamp members 20, 201 are released, the ends of the mandrel body 10, 101, 102 are sealed, e.g. by the end plugs 11, 12 of Figure 1, and compressed air is admitted into the mandrel body, e.g. through the valve 141 and inlet 14, being then forced out of the holes 16 so as to release contact between the tube and mandrel by an air cushion effect. The can body or body sections are then removed from the mandrel.
Instead of using compressed air to release the contact between the tube and mandrel, a part of the mandrel surface may be collapsed inwards as shown in Figure 4. The mandrel body 103 is here provided with one or more sections 32 extending the whole length of the mandrel and movable radially from the position shown in chain-dotted lines to that shown in full lines to collapse a part of the mandrel surface, so reducing the , . .
;, , , :
.
, ': .;:

~2~5~

--1 o effective circumference and releasing contact with a PET tube which has been heat-shrunk thereon. An alternative type of collapsible mandrel which could be used is a hydraulically or pneumatically inflated tube, e.g. of silicon rubber.
As shown in Figure 5, can ends 30, 31, e.g. of metal, can conveniently be seamed to the ends of the heat-set tubular can body 26 to form a processable container.
In production, a plurality of mandrel bodies 101 or 102 are arranged vertically on an indexing platform so as to be indexed past stations at which the various operations are carried out, as follows:-ta) a PET tube (26) is fitted over a mandrel body 101 or 102 while the temperature of the mandrel is below the glass transition temperature of the resin, (b) the circumferential clamps 20, 201 are applied to each end of the PET tube 26, (c) the heating element 28 is introduced from below into the interior of the mandrel body so as to make contact with it and to heat it rapidly by conduction to a temperature of 180C to 240C, (d) this temperature is maintained for long enough to ensure the required heat-setting, (e) the heating element 28 is removed and the PET tube 26 is allowed to cool to below 140C, (f) where a multiple-length mandrel body 101 is used, the mandrel body is rotated and knives are brought into contact with the tube 26 to cut it into individual lengths, (g~ the ends of the mandrel body 101 or 102 are sealed and compressed air is introduced to release contact between the tube 26 and mandrel body, , and (h) the can body sections are removed from the mandrel body.

;, . ~

5;~

"

The method of the inven~ion can also be employed for heat-setting thermoplastic tubular articles which are closed at one end. Figure 6 illustrates the heat-setting of a PET container 34 which is formed with a recessed bottom 36. The container 34 is shown inverted on a tubular mandrel 104 which has a closed end 38 whose shape corresponds with that of the container bottom 36. The clamping means in this case comprise a clamp ring 202 which is movable axially of the mandrel to clamp a flange 40 on the end of the container 34 against a base plate 42, and a pressure member 203 with an end shaped to correspond with the shape of the container bottom 36, which is movable axially to clamp the container bottom against the closed end 38 of the mandrel body.
The mandrel body 34 is formed with air holes 16 as in the embodiments of Figures 1, 2 and 3 for removal of the heat-set container. Heating may be effected by a heating element 28 as before.
Alternative means of heating the PET tube may be used in any of the embodiments described above, such as inductive heating of a metal mandrel, using an induction coil within the mandrel. ~ielectric radio-frequency heating of the PET tube may be employed, using inner and outer electrodes, the mandrel then forming a heat sink to receive heat from the PET tube as it cools down. Radiant heat, e.g. in the infra-red region, may be ~5 used, or the mandrel and tube may be introduced into a fluidised bed maintained at the desired temperature.
Other alternatives are heating of the interior of the mandrel by flame, and interior or exterior heating by hot air or by live steam.
The mandrel need not be cylindrical but could for example be oval or rectangular in section, so as to use the heat-setting shrinkage for accurate dimensioning of shaped tubes.

., . , , , , . ;

, .
, . .;
.. ..
, ; ,. . ..
. ,: ,.

Claims

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

1. A food container comprising an open-ended cylind-rical body which is made of a crystallisable polyethylene terephthalate material, and end closure means at each end of said body forming with said body a closed container, said body material being biaxially oriented and the container body having been heat-set, whilst restrained against radial or axial shrinkage, the improvement residing in that the container body has been heat-set at a temperature between about 180°C and about 240°C, whereby said container is able to withstand hot-filling, pasteurisation or sterilisation temperatures of up to about 120°C without undergoing shrinkage of its linear dimensions by more than 3%.