CA1222779A - Sulfur-modified polytetramethylene ether glycols, a method for preparing them, and polyurethanes prepared therefrom - Google Patents
Sulfur-modified polytetramethylene ether glycols, a method for preparing them, and polyurethanes prepared therefromInfo
- Publication number
- CA1222779A CA1222779A CA000414170A CA414170A CA1222779A CA 1222779 A CA1222779 A CA 1222779A CA 000414170 A CA000414170 A CA 000414170A CA 414170 A CA414170 A CA 414170A CA 1222779 A CA1222779 A CA 1222779A
- Authority
- CA
- Canada
- Prior art keywords
- ether glycol
- polytetramethylene ether
- mixture
- modified
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
TITLE
Sulfur-Modified Polytetramethylene Ether Glycols, A Method for Preparing Them, and Polyurethanes Prepared Therefrom ABSTRACT OF THE DISCLOSURE
Polytetramethylene ether glycol is modified so that it contains 1-25%, by weight of .beta.,.beta.'-dihydroxyalkyl sulfide moieties.
These modified polytetramethylene ether gly-cols have enhanced resistance to degradation by heat and oxygen. The invention also relates to a method of making the modified PTMEG's, to their use as stabilizers against the degradation of the polyether chain, and to polyurethanes made with them.
Sulfur-Modified Polytetramethylene Ether Glycols, A Method for Preparing Them, and Polyurethanes Prepared Therefrom ABSTRACT OF THE DISCLOSURE
Polytetramethylene ether glycol is modified so that it contains 1-25%, by weight of .beta.,.beta.'-dihydroxyalkyl sulfide moieties.
These modified polytetramethylene ether gly-cols have enhanced resistance to degradation by heat and oxygen. The invention also relates to a method of making the modified PTMEG's, to their use as stabilizers against the degradation of the polyether chain, and to polyurethanes made with them.
Description
2~7t79 TITLE
Sulfur~Modified Polytetramethylene Ether Glycols, A Method for Preparing Them, and Polyurethanes Prepared Therefrom S DESCRIPTION
Technical Field This invention relates to polytetramethylene ether glycol (PTMEG), which has been modified so that it contains sulfur-containing moieties in its polymer chain. It is more particularly directed to such a PTMEG modified to contain dehydrated ~,~'-dihydroxyalkyl sulfide (HAS) moieties in its chain.
The invention also relates to a method of making the modified PTMEG's, to their use as stabili-zers against the degradation the polyether chain, andto polyurethanes made with them.
Background and Summary of the Invention Polyurethanes have been known and used for many years, and the basic general chemistry for their ~ 20 preparation, the reaction of a polyol, a polyisocyanate and a chain extender, is fully documented.
A polyol frequently used for this purpose is PTMEG, which is well known to be degraded by exposure to oxygen, light and heat. It has been the general practice to guard against this degradation by blending with the PTMEG an external stabilizer such as a phenolic, an amine or a sulfur compound.
It has now been found, according to the in-vention, that the stabilization can be more effectively and efficiently achieved if the PTMEG is modified so that it contains in its chain 1-25%, by weight, pref-erably 3-15%, even more preferably 4-10%, of moieties represented by the structure R R
~ where R is hydrogen, an alkyl radi-cal of 1-3 carbon atoms or phenyl, and the oxygen atom is linked to a hydrogen atom or a carbon atom;
the modified PTMEG having an oxygen/sulfur atom ratio of 3/1 or greater~
It has been found, according to the inven-tion, that the scabilization against degradation can also be achieved if unmodified PTMEG to be used is physically blended with about 0.4-20%, by weight, of the modified PTMEG.
In addition, the method for preparing the modified PTMEG of the invention can be used to in-crease the molecular weight of PTMEG by coupling polymer chain segments with HAS moieties.
It has also been found that PTMEG modified - according to the invention shows significantly better resistance to acid-catalyzed depolymerization and to oxidative degradation at high temperatures than unmodi-fied PTMEG.
Detailed Description of the Invention The modified PTMEG of the invention is made by catalytically reacting a PTMEG with an HAS.
The PTMEG used can be any of those commer-cially available, or can be prepared by any of the well-known methods of catalytically polymerizing tetra-hydrofuran. Preferably, the PTMEG has a number average molecular weight of 500-6000, more preferably 650-3000.
Number average molecular weight is determined by first determining the hydroxyl number of the sample by titrating it with acetic anhydride according to ~;~Z~77~
ASTM-D-1638 and then converting this number to number average molecular weight according to the formula g hydroxyl number where n is the hydroxyl functionality of the sample The HAS used is represented by the structure R R
where R is hydrogen, an alkyl radi-cal of 1-3 carbon atoms, or phenyl.
The HAS preferred for use is ~ dihydroxy-ethyl sulfide.
Any such HAS not available in the marketplace can be made by the well-known reaction of hydrogen sul-fide and an alkylene oxide.
The preparative reaction is conducted in a mixture of PTMEG and HAS. The relative amounts of HAS and P~MEG used are dictated by the weight of HAS
moieties desired in the product. These amounts can be easily calculated using the principles of stoichiometry.
In general, one uses 0.5-6 moles of HAS for each mole of PTMEG, preferably 1-2 moles.
The catalyst used can be any heterogeneous or homogeneous acid catalyst stronger than H3PO~. The catalyst is preferably an alkyl- or aryl sulfonic acid, even more preferably one of the strongly acidic catio-nic ion-exchange resins bearing -SO3H groups, insolu-ble in the reaction medium. '1Insoluble" means that the amount of resin which dissolves in the medium under reaction conditions will give the modified PTMEG prod-uct an acid number of no greater than 0.05 mg of KOH
:~22~79 per gram. The nature of the "backbone" of the resin is unimportant. The most common of the commercially available resins o~ this type have backbones which are of the polystyrene type, but resins having other back-bones can be used.
Preferred among the polystyrene type resins, and prefexred for this use according to the invention, is one sold by the Rohm & Haas Company of Philadelphia, PA as Amberlyst* XN-1010. This macroreticular resin has a cation exchange capacity of 3.1 milliequivalents per gram, a surface area of 450 square meters per gram, a porosit~ of 41%l and a mean pore diameter of 0.005 micron.
The catalyst is used at a concentration of 0.1-10%, by weight of the PTMEG, preferably 2-5%.
The preparation is begun by placing the re-actants and catalyst in a vessel and bringing the re-sulting mixture to a temperature of 130-170C, prefer-ably about 150~C, and holding it at that temperature, with stirring, until the HAS has been consu~ed, as shown by periodic sampling and analysis by gas chromatography.
The water formed by the reaction can be re-moved from the reaction mass by vacuum distillation or by sweeping the reaction zone with an inert gas e-g-nitrogen. Preferably, the water is removed as a water/hydrocarbon azeotrope, even more preferably as a water/toluene azeotrope. The hydrocarbon can then be separated from the azeotrope by condensation in a suitable trap and can be recycled to the reaction mass.
When this procedure is used, the temperature of the reaction mass can easily be held within the desired range by adjusting the concentration of toluene.
When the PTMEG-HAS reaction i5 finished, heating is stopped, the catalyst is filtered off (if a * denotes trade mark 7~
heterogeneous catalyst is used) and the remaining mate-rial is stripped of residual volatiles. The resulting product is a viscous liquid having a number average molecular weigh-t of 500-10,000, preferably 800-500~, and an oxygen/sulfur atom ratio of 3/1 or greater, preferably 5-60/1. Molecular weight can be varied by simply allo~ing the reaction to proceed until the desired molecular weight is reached.
The blends of unmodified PTMEG and PTMEG
modified according to the invention can be made by simply mixing them in amounts which will give a mixture containing 0.4-20%, by weight, of the modified PTMEG.
A polyurethane can be prepared from a modi-~ied PTMEG of the invention, or from a modified-unmodi-fied blend, by reacting it with an organic polyisocyan-ate and an aliphatic polyol or polyamine chain extender, as is well known in the art.
The polyisocyanates used in preparing the polyurethanes can be any of the aliphatic or aromatic polyisocyanates ordinarily used to pxepare polyure-thanes. "Polyisocyanate" means any compound bearing two or more -NCO radicals. Illustrative are 2,4-toluene diisocyanate 2,6-toluene diisocyanate hexamethylene-1,6-diisocyanate tetramethylene-1,4-diisocyanate cyclohexane-1,4-diisocyanate naphthalene-1,5-diisocyanate diphenylmethane-4,4'-diisocyanate xylylene diisocyanate hexahydro xylylene diisocyanate dicyclohexylmethane-4,4'-diisocyanate 1,4-benzene diisocyanate
Sulfur~Modified Polytetramethylene Ether Glycols, A Method for Preparing Them, and Polyurethanes Prepared Therefrom S DESCRIPTION
Technical Field This invention relates to polytetramethylene ether glycol (PTMEG), which has been modified so that it contains sulfur-containing moieties in its polymer chain. It is more particularly directed to such a PTMEG modified to contain dehydrated ~,~'-dihydroxyalkyl sulfide (HAS) moieties in its chain.
The invention also relates to a method of making the modified PTMEG's, to their use as stabili-zers against the degradation the polyether chain, andto polyurethanes made with them.
Background and Summary of the Invention Polyurethanes have been known and used for many years, and the basic general chemistry for their ~ 20 preparation, the reaction of a polyol, a polyisocyanate and a chain extender, is fully documented.
A polyol frequently used for this purpose is PTMEG, which is well known to be degraded by exposure to oxygen, light and heat. It has been the general practice to guard against this degradation by blending with the PTMEG an external stabilizer such as a phenolic, an amine or a sulfur compound.
It has now been found, according to the in-vention, that the stabilization can be more effectively and efficiently achieved if the PTMEG is modified so that it contains in its chain 1-25%, by weight, pref-erably 3-15%, even more preferably 4-10%, of moieties represented by the structure R R
~ where R is hydrogen, an alkyl radi-cal of 1-3 carbon atoms or phenyl, and the oxygen atom is linked to a hydrogen atom or a carbon atom;
the modified PTMEG having an oxygen/sulfur atom ratio of 3/1 or greater~
It has been found, according to the inven-tion, that the scabilization against degradation can also be achieved if unmodified PTMEG to be used is physically blended with about 0.4-20%, by weight, of the modified PTMEG.
In addition, the method for preparing the modified PTMEG of the invention can be used to in-crease the molecular weight of PTMEG by coupling polymer chain segments with HAS moieties.
It has also been found that PTMEG modified - according to the invention shows significantly better resistance to acid-catalyzed depolymerization and to oxidative degradation at high temperatures than unmodi-fied PTMEG.
Detailed Description of the Invention The modified PTMEG of the invention is made by catalytically reacting a PTMEG with an HAS.
The PTMEG used can be any of those commer-cially available, or can be prepared by any of the well-known methods of catalytically polymerizing tetra-hydrofuran. Preferably, the PTMEG has a number average molecular weight of 500-6000, more preferably 650-3000.
Number average molecular weight is determined by first determining the hydroxyl number of the sample by titrating it with acetic anhydride according to ~;~Z~77~
ASTM-D-1638 and then converting this number to number average molecular weight according to the formula g hydroxyl number where n is the hydroxyl functionality of the sample The HAS used is represented by the structure R R
where R is hydrogen, an alkyl radi-cal of 1-3 carbon atoms, or phenyl.
The HAS preferred for use is ~ dihydroxy-ethyl sulfide.
Any such HAS not available in the marketplace can be made by the well-known reaction of hydrogen sul-fide and an alkylene oxide.
The preparative reaction is conducted in a mixture of PTMEG and HAS. The relative amounts of HAS and P~MEG used are dictated by the weight of HAS
moieties desired in the product. These amounts can be easily calculated using the principles of stoichiometry.
In general, one uses 0.5-6 moles of HAS for each mole of PTMEG, preferably 1-2 moles.
The catalyst used can be any heterogeneous or homogeneous acid catalyst stronger than H3PO~. The catalyst is preferably an alkyl- or aryl sulfonic acid, even more preferably one of the strongly acidic catio-nic ion-exchange resins bearing -SO3H groups, insolu-ble in the reaction medium. '1Insoluble" means that the amount of resin which dissolves in the medium under reaction conditions will give the modified PTMEG prod-uct an acid number of no greater than 0.05 mg of KOH
:~22~79 per gram. The nature of the "backbone" of the resin is unimportant. The most common of the commercially available resins o~ this type have backbones which are of the polystyrene type, but resins having other back-bones can be used.
Preferred among the polystyrene type resins, and prefexred for this use according to the invention, is one sold by the Rohm & Haas Company of Philadelphia, PA as Amberlyst* XN-1010. This macroreticular resin has a cation exchange capacity of 3.1 milliequivalents per gram, a surface area of 450 square meters per gram, a porosit~ of 41%l and a mean pore diameter of 0.005 micron.
The catalyst is used at a concentration of 0.1-10%, by weight of the PTMEG, preferably 2-5%.
The preparation is begun by placing the re-actants and catalyst in a vessel and bringing the re-sulting mixture to a temperature of 130-170C, prefer-ably about 150~C, and holding it at that temperature, with stirring, until the HAS has been consu~ed, as shown by periodic sampling and analysis by gas chromatography.
The water formed by the reaction can be re-moved from the reaction mass by vacuum distillation or by sweeping the reaction zone with an inert gas e-g-nitrogen. Preferably, the water is removed as a water/hydrocarbon azeotrope, even more preferably as a water/toluene azeotrope. The hydrocarbon can then be separated from the azeotrope by condensation in a suitable trap and can be recycled to the reaction mass.
When this procedure is used, the temperature of the reaction mass can easily be held within the desired range by adjusting the concentration of toluene.
When the PTMEG-HAS reaction i5 finished, heating is stopped, the catalyst is filtered off (if a * denotes trade mark 7~
heterogeneous catalyst is used) and the remaining mate-rial is stripped of residual volatiles. The resulting product is a viscous liquid having a number average molecular weigh-t of 500-10,000, preferably 800-500~, and an oxygen/sulfur atom ratio of 3/1 or greater, preferably 5-60/1. Molecular weight can be varied by simply allo~ing the reaction to proceed until the desired molecular weight is reached.
The blends of unmodified PTMEG and PTMEG
modified according to the invention can be made by simply mixing them in amounts which will give a mixture containing 0.4-20%, by weight, of the modified PTMEG.
A polyurethane can be prepared from a modi-~ied PTMEG of the invention, or from a modified-unmodi-fied blend, by reacting it with an organic polyisocyan-ate and an aliphatic polyol or polyamine chain extender, as is well known in the art.
The polyisocyanates used in preparing the polyurethanes can be any of the aliphatic or aromatic polyisocyanates ordinarily used to pxepare polyure-thanes. "Polyisocyanate" means any compound bearing two or more -NCO radicals. Illustrative are 2,4-toluene diisocyanate 2,6-toluene diisocyanate hexamethylene-1,6-diisocyanate tetramethylene-1,4-diisocyanate cyclohexane-1,4-diisocyanate naphthalene-1,5-diisocyanate diphenylmethane-4,4'-diisocyanate xylylene diisocyanate hexahydro xylylene diisocyanate dicyclohexylmethane-4,4'-diisocyanate 1,4-benzene diisocyanate
3,3'-dimethoxy-4,4'-diphenyl diisocyanate ~Z~77~
m-phenylene diisocyanate isophorone diisocyanate polymethylene polyphenyl isocyanate
m-phenylene diisocyanate isophorone diisocyanate polymethylene polyphenyl isocyanate
4,4'-biphenylene diisocyanate 4-isocyanatocyclohexyl-4'-isocyanatophenyl methane p-isocyanatomethyl phenyl isocyanate.
Mixtures of isocyanates can also be used.
The isocyanates preferred for use because of the desirable properties they confer on the polyure-thane products are diphenylmethane-4,4'-diisocyanate and the toluene diisocyanates.
The chain extenders used in preparing the polyurethanes can be any of the aliphatic polyols, or any oE the aliphatic or aromatic polyamines ordinarily used to prepare polyurethanes.
Illustrative of the aliphatic polyols which can be used as chain extenders are 1,4-butanediol ethylene glycol ., 1,6-hexanediol glycerine trimethylolpropane pentaerythritol 1,4-cyclohexane dimethanol phenyl diethanolamine Diols like hydroquinone bis(~-hydroxyethyl)ether, tetra-chlorohydroquinone-1,4-bis(~-hydroxyethyl)ether and tetrachlorohydroquinone-1,4-bis(~-hydroxyethyl)sulfide, even though they contain aromatic rings, are considered to be aliphatic polyols Eor purposes of the invention.
Aliphatic diols of 2-10 carbon atoms are pre-Eerred. Especially preEerred is 1,4-butanediol.
Mixtures of diols can also be used.
:~L2Z~779 Illustrati~e of the polyamines which can be used as chain extenders are p,p'-methylene dianiline and complexes thereo~ wi~h alkali metal chlorides, bromides, iodides, nitrites and nitrates.
4,4'-methylene bis~2-chloroaniline) dichlorobenzidine piperazine 2-methylpiperazine oxydianiline hydrazine - ethylenediamine hexamethylenediamine xylylenediamine bis(p-aminocyclohexyl)methane dimethyl ester of 4,4'-methylenedianthranilic acid p-phenylenediamine m-phenylenediamine 4,4'-methylene bis(2-methoxyaniline) 4,4'-methylene bis(N-methylaniline) 2,4-toluenediamine 2,~-toluenediamine benzidine 3,4'-dimethylbenzidine 3,3'-dimethoxybenzidine l dianisidine ; 1,3-propanediol bis(p-aminobenzoate) isophorone diamine 1,2-bis(2'-aminophenylthio)ethane.
The amines preferred for use are 4,4'-methylene bis(2-chloroaniline), 1,3-propanediol 7~79 bis(p-aminobenzoate) and p,p'-methylenedianiline and complexes thereof with alkali metal chlorides, bromides, iodides, nitrites and nitrates. Mixtures of amines can also be used.
The polyurethanes can be prepared in two steps, the ~irst of which is conducted under nitrogen at ambient pressure to prevent oxidation of the re-actants and pro~uct, and to prevent exposure of the reaction mass to atmospheric moisture. In the first step, the modified PTMEG starting material is dried by heating it at a temperature of 80-100C under vacuum, and is then held at 60-125C, preferably about 70-90C, while a stoichiometric excess, preferably twofold to tenfold, of organic polyisocyanate is added, with stirring. The actual amount of isocyanate used depends on the molecular weight of the modified PTMEG used, as is well known in the art. The reaction mass is held for about 1-4 hours at 60-125C, with stirring, and the free isocyanate content of the mass is then determined by titrating it with di-n-butylamine, as described in Analytic Chemistry of the Polyurethanes, Volume XVI, Part III, D. J. David and H. B. Staley, Wiley-Interscience, 1969, pages 357-359.
In the second step, an amount of polyamine or polyol chain extender calculated to gi~e an isocyanate/hydroxyl or amine mole ratio of about 0.9-1.1 to 1 in the reaction mass, preferably 1-1.05/1, is degassed at about 30-120C and 1330-5330 Pa (10-50 mm Hg) pressure and quickly added to the reaction mass.
- 30 A conventional curing catalyst can be added at this point if desired. Illustrative of catalysts which can be used are dibutyltin dilaurate and stannous octoate. The catalyst can be added to the reaction mass to give a concentration of about 0.001-0.1%, by weight, preferably about 0.01%.
r;~7~3 The reaction mass is held with stirring at 60 130C until it is homogeneous, which normally takes 1-5 minutes. The mass is then poured into molds, pref-erably preheated to 100-120C, and then cured at about 100-120C at a pressure of 1700-2500 kPa for from 5 minutes to several hours. The casting is then cooled, removed from the mold, aged for about one week at ambient temperature, and is then ready for use.
The polyurethanes can also be made by reac-tion-injection and liquid-injection molding techniques, whereby the starting materials are simultaneously in-jected and mixed in a mold, preferably together with a conventional polyurethane catalyst,and then subjected to pressures ranging from ambient to several million pascals and temperatures ranging from ambient to lS0C.
Use of a foaming agent e.g. a fluorocarbon or water is optional.
BEST MODE
In the following example, all parts are by weight.
The following were added to a reaction vessel fitted with a reflux condenser and a Dean Stark trap:
PTMEG (Mn 1000) 100 parts ~ dihydroxyethyl sulfide 12.2 parts Toluene 50 parts Amberlyst XN-101~ 4 parts The resulting mixture was heated to and held at reflux temperature for four hours, with stirring, while water 30 was continuously removed from the reaction zone as the water/toluene azeotrope.
The reaction mixture was then filtered to remove the Amberlyst and the volatiles removed at a pressure of about 667 Pa (5 mm of Hg) and a temperature ~2779 of about 150C to give 98 parts of a viscous liquid product containing 5.9% of -O-CH2-CH2-S-CH2-CH2-moieties, with a number average molecular weight of 2080 and an oxygen/sulfur atom ratio of 24/1. This polymer slowly crystallized at about 20C.
Mixtures of isocyanates can also be used.
The isocyanates preferred for use because of the desirable properties they confer on the polyure-thane products are diphenylmethane-4,4'-diisocyanate and the toluene diisocyanates.
The chain extenders used in preparing the polyurethanes can be any of the aliphatic polyols, or any oE the aliphatic or aromatic polyamines ordinarily used to prepare polyurethanes.
Illustrative of the aliphatic polyols which can be used as chain extenders are 1,4-butanediol ethylene glycol ., 1,6-hexanediol glycerine trimethylolpropane pentaerythritol 1,4-cyclohexane dimethanol phenyl diethanolamine Diols like hydroquinone bis(~-hydroxyethyl)ether, tetra-chlorohydroquinone-1,4-bis(~-hydroxyethyl)ether and tetrachlorohydroquinone-1,4-bis(~-hydroxyethyl)sulfide, even though they contain aromatic rings, are considered to be aliphatic polyols Eor purposes of the invention.
Aliphatic diols of 2-10 carbon atoms are pre-Eerred. Especially preEerred is 1,4-butanediol.
Mixtures of diols can also be used.
:~L2Z~779 Illustrati~e of the polyamines which can be used as chain extenders are p,p'-methylene dianiline and complexes thereo~ wi~h alkali metal chlorides, bromides, iodides, nitrites and nitrates.
4,4'-methylene bis~2-chloroaniline) dichlorobenzidine piperazine 2-methylpiperazine oxydianiline hydrazine - ethylenediamine hexamethylenediamine xylylenediamine bis(p-aminocyclohexyl)methane dimethyl ester of 4,4'-methylenedianthranilic acid p-phenylenediamine m-phenylenediamine 4,4'-methylene bis(2-methoxyaniline) 4,4'-methylene bis(N-methylaniline) 2,4-toluenediamine 2,~-toluenediamine benzidine 3,4'-dimethylbenzidine 3,3'-dimethoxybenzidine l dianisidine ; 1,3-propanediol bis(p-aminobenzoate) isophorone diamine 1,2-bis(2'-aminophenylthio)ethane.
The amines preferred for use are 4,4'-methylene bis(2-chloroaniline), 1,3-propanediol 7~79 bis(p-aminobenzoate) and p,p'-methylenedianiline and complexes thereof with alkali metal chlorides, bromides, iodides, nitrites and nitrates. Mixtures of amines can also be used.
The polyurethanes can be prepared in two steps, the ~irst of which is conducted under nitrogen at ambient pressure to prevent oxidation of the re-actants and pro~uct, and to prevent exposure of the reaction mass to atmospheric moisture. In the first step, the modified PTMEG starting material is dried by heating it at a temperature of 80-100C under vacuum, and is then held at 60-125C, preferably about 70-90C, while a stoichiometric excess, preferably twofold to tenfold, of organic polyisocyanate is added, with stirring. The actual amount of isocyanate used depends on the molecular weight of the modified PTMEG used, as is well known in the art. The reaction mass is held for about 1-4 hours at 60-125C, with stirring, and the free isocyanate content of the mass is then determined by titrating it with di-n-butylamine, as described in Analytic Chemistry of the Polyurethanes, Volume XVI, Part III, D. J. David and H. B. Staley, Wiley-Interscience, 1969, pages 357-359.
In the second step, an amount of polyamine or polyol chain extender calculated to gi~e an isocyanate/hydroxyl or amine mole ratio of about 0.9-1.1 to 1 in the reaction mass, preferably 1-1.05/1, is degassed at about 30-120C and 1330-5330 Pa (10-50 mm Hg) pressure and quickly added to the reaction mass.
- 30 A conventional curing catalyst can be added at this point if desired. Illustrative of catalysts which can be used are dibutyltin dilaurate and stannous octoate. The catalyst can be added to the reaction mass to give a concentration of about 0.001-0.1%, by weight, preferably about 0.01%.
r;~7~3 The reaction mass is held with stirring at 60 130C until it is homogeneous, which normally takes 1-5 minutes. The mass is then poured into molds, pref-erably preheated to 100-120C, and then cured at about 100-120C at a pressure of 1700-2500 kPa for from 5 minutes to several hours. The casting is then cooled, removed from the mold, aged for about one week at ambient temperature, and is then ready for use.
The polyurethanes can also be made by reac-tion-injection and liquid-injection molding techniques, whereby the starting materials are simultaneously in-jected and mixed in a mold, preferably together with a conventional polyurethane catalyst,and then subjected to pressures ranging from ambient to several million pascals and temperatures ranging from ambient to lS0C.
Use of a foaming agent e.g. a fluorocarbon or water is optional.
BEST MODE
In the following example, all parts are by weight.
The following were added to a reaction vessel fitted with a reflux condenser and a Dean Stark trap:
PTMEG (Mn 1000) 100 parts ~ dihydroxyethyl sulfide 12.2 parts Toluene 50 parts Amberlyst XN-101~ 4 parts The resulting mixture was heated to and held at reflux temperature for four hours, with stirring, while water 30 was continuously removed from the reaction zone as the water/toluene azeotrope.
The reaction mixture was then filtered to remove the Amberlyst and the volatiles removed at a pressure of about 667 Pa (5 mm of Hg) and a temperature ~2779 of about 150C to give 98 parts of a viscous liquid product containing 5.9% of -O-CH2-CH2-S-CH2-CH2-moieties, with a number average molecular weight of 2080 and an oxygen/sulfur atom ratio of 24/1. This polymer slowly crystallized at about 20C.
Claims (12)
1. Polytetramethylene ether glycol modified so that it contains in its chain 1-25%, by weight, of moieties represented by the structure where R is hydrogen, an alkyl radi-cal of 1-3 carbon atoms or phenyl, and the oxygen atom is linked to a hydrogen atom or a carbon atom.
the polytetramethylene ether glycol having an oxygen/
sulfur atom ratio of 3/1 or greater.
the polytetramethylene ether glycol having an oxygen/
sulfur atom ratio of 3/1 or greater.
2. The polytetramethylene ether glycol of claim 1 in which the moieties are represented by the structure -OCH2CH2-S-CH-CH2-.
3. The polytetramethylene ether glycol of claim 2 which has a number average molecular weight of 500-10,000.
4. A mixture of unmodified polytetramethyl-ene ether glycol and 0.4-20%, by weight of the mixture, of the polytetramethylene ether glycol of claim 1.
5. A mixture of unmodified polytetramethyl-ene ether glycol and 0.4-20%, by weight of the mixture, of the polytetramethylene ether glycol of claim 2.
6. A mixture of unmodified polytetramethyl-ene ether glycol and 0.4-20%, by weight of the mixture, of the polytetramethylene ether glycol of claim 3.
7. A method for preparing a thio-modified polytetramethylene ether glycol, the method comprising bringing together, under conditions suitable for reaction, (a) polytetramethylene ether glycol;
(b) a .beta.,.beta.'-dihydroxyalkyl sulfide represented by the structure where R is hydrogen; an alkyl radical of 1-3 carbon atoms, or phenyl;
and (c) an acid catalyst.
(b) a .beta.,.beta.'-dihydroxyalkyl sulfide represented by the structure where R is hydrogen; an alkyl radical of 1-3 carbon atoms, or phenyl;
and (c) an acid catalyst.
8. The method of claim 7 in which the catalyst is Amberlyst (trade mark) XN-1010 resin.
9. The method of claim 7 in which water is removed from the reaction mass by azeotropic distillation.
10. The method of claim 9 in which the azeotrope is water/toluene.
11. A polyurethane which is the reaction product of (a) the polytetramethylene ether glycol of claim 1-3;
(b) an organic polyisocyanate;
and (c) a chain extender.
(b) an organic polyisocyanate;
and (c) a chain extender.
12. A polyurethane which is the reaction product of (a) the mixture of claims 4-6;
(b) an organic polyisocyanate;
and (c) a chain extender.
(b) an organic polyisocyanate;
and (c) a chain extender.