CA1218218A - Zone heating for fluidized bed silane pyrolysis - Google Patents

Zone heating for fluidized bed silane pyrolysis

Info

Publication number
CA1218218A
CA1218218A CA000438549A CA438549A CA1218218A CA 1218218 A CA1218218 A CA 1218218A CA 000438549 A CA000438549 A CA 000438549A CA 438549 A CA438549 A CA 438549A CA 1218218 A CA1218218 A CA 1218218A
Authority
CA
Canada
Prior art keywords
silicon
zone
silane
reaction zone
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CA000438549A
Other languages
French (fr)
Inventor
Sridhar K. Iya
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Union Carbide Corp
Original Assignee
Union Carbide Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Union Carbide Corp filed Critical Union Carbide Corp
Application granted granted Critical
Publication of CA1218218A publication Critical patent/CA1218218A/en
Expired legal-status Critical Current

Abstract

ZONE HEATING FOR FLUIDIZED BED SILANE PYROLYSIS
ABSTRACT

An improved heated fluidized bed reactor and method for the production of high purity polycrystalline silicon by silane pyrolysis wherein silicon seed particles are heated in an upper heating zone of the reactor and admixed with particles in a lower reaction zone, in which zone a silane-containing gas stream, having passed through a lower cooled gas distribution zone not conducive to silane pyrolysis, contacts the heated seed particles whereon the silane is heterogeneously reduced to silicon.

D-13,697

Description

Zone Heatin~ for Fluidized Bed Silane Pyrolysis . _ . .
OESCRI PTI)N

Technical Field This invention relates to an improved heated fluidized bed silane pyrolysis reactor and a method for the production of hi~h purity silicon wherein the silicon is efficiently deposited on fluid bed particles. The improvement of the present 1~ invention comprises heating silicon seed parti~les in the uppermost zone of the fluidized bed reactor, -- admixing the ~eated particles from the h~ating zone with particles in a reaction zone therebelow by the inherent mixing characteristics of the fluidized bed and maintaining a lower gas distribution zone of the reactor at temperatures below which silane decomposes to silicon. The heating enhances heteroqeneous silicon deposition on the silicon seed . particles while the cool gas distribution zone diminishes the deposition of silicon thereon and on the adjacent reactor surfaces in the xeaction zone and reduces the formation of silicon dust.
. Background of the Invention The development of new techniques for the utilization of non-polluting, renewable sources of D-13,697 ~
.
. - . .

: . ~

energy is of paramount interest to meet the energy demands of the future. Solar energy is among the energy sources of greatest interest because o~ its non-polluting nature and its abundant, non-diminishing availability. One approach to the utilization of solar energy involves the conversion of solar energy into electricity by means of the photovoltaic effect upon the absorption of sunlight by solar cells.
Silicon solar cells, the most commonly employed devices based on the photovoltaic ef~ect, have been utilized reliably in spacecraft applications fox many years. Crystals of ultra-high purity silicon are also important for use as semiconductors in the electronics industry.
However, the costs associated with the production of such high purity, high-perfection crystals for these applications and for industrial and commercial applications in general, are often not economically feasible.
High purity silicon is generally prepared by procedures involving the conversion of metallurgical grade silicon to silane or a halosilane, which is subsequently purified and ~hen reduced to produce polycrystalline, semiconductor grade silicon from which single crystals can be - grown. One such process to upgrade metallurgical grade silison to the ultra-high purity silicon needed for either solar cell or semi-conductor usage is disclosed in U.S. Patent 4,340,574 to Coleman.
This process includes reaction of metallurgical grade silicon with silicon tetrachloride and hydrogen to yield an intermediate trichlorosilane and silicon tetrachloride feed stream. The D-13,697 ,rP
"t :
. . .. ,, ,, ~ ~ . ., ., . . ... , , . ~ . .., . , . .. .... . . ,~, . . . . .

- 3 ~

intermediate feed stream i~ further processed in a redistribution reactor and distillation column section whereby the trichlorosilane is upgraded and separated into an ultra-high purity silane product and recycle silicon tetrachloride. The high purity silane is pyrolyzed to produce the ul~ra-high purity silicon product and hydrogen by-product.
It is well known in the prior art to reduce a halosilane product such as trichlorosilane to polycrystalline silicon in a reactor having carrier rods electrically heated to about 1100C on which reactant gases precipitate silicon. This process, commonly known as the Siemens process, is described in United States patent 3,979,490 to Dietze et al.
This batch-type process, which is now highly commerciali~ed, possesses high material costs and power requirements.
Another method for obtaining high purity silicon rom silane or a halosilane is by pyrolysis in a fluidized bed. Silicon seed particles are suspended in a fluidizing gas stream into which silane or a halosilane is injected through some type of gas distribution apparatusO Process conditions are desirably maintained so that the silane ~5 decomposes to silicon on the surface of the seed particles in the fluidized bed. By this process seed particles grow by silicon deposition thereon and drop out of the reaction zone falling through the fluidized gas stream into a collector such as a boot-type separator~ ~ydrogen, which may be formed as a by-product from the silane decomposition, can be removed separately overhead from the reaction zone. When chlorosilanes are decomposed the by-product gas generally comprises hydrogen chloride.

D-13,697 , The pyrolysis of silane or a halosilane may be achieved by capacitive heating of the fluidized bed reaction zone, as disclosed in United States patent 4,292,344 to McHale. Other methods of heating such as uniform induction coils, electrical resistance elements and indirect gas firing may also be utiliæed and are disclosed in United States patents 3,012,861 to Ling and 3,012,8S2 to Bertrand et al.
The decomposition of silane or a halosilane in a heated fluidized bed reactor may result in an undesirable deposit of silicon on the wall thereof or on other internal components of the fluidized bed. In some instances, as when the wall temperature in the reaction zone exceeds the temperature of the silicon seed particles, the deposition of silicon on ~he reactor apparatus may occur in preference to the desired deposition of silicon on the fluidized seed particles. Silane or halosilane decomposition in heated fluidized beas may a~so result in the homogenous decomposition of silane which produces fine silicon powder or dust.
- This light powder is undesira~le in fluidized bed operations as it requires costly additional handling for recovery and consolidation for melting, which handling increases the risk of contaminating the ultra-pure product silicon and results in some - material loss.
The need exists, therefore, for the development of an improved heated fluidized bed reactor for the production of high purity silicon for semiconductor and solar cell applications and an improved process for reducing silanes and halosilanes in a fluidized bed reactor without an D-13,697 :~,,', . ~`I..`

.

- s -accumulation of silicon on the internal surfaces therein and without the homogenous formation o~
silicon dust.
Hence, it is an object of this invention to S provide an apparatus and a process for the enhanced heterogene~us formation of high purity silicon.
It is another object of this invention to provide an improved heated fluidized bed reactor whose interior surfaces are not preferred fo.r the deposition of silicon thereon.
It is still another object of the invention to provide a process which enhances the heterogene~us decomposition of a silane or halosilane feed gas passed through a heated fluidized bed reaction zone and which efectively eliminates silicon deposition on the interior surfaces of the reactor.
A further object of this invention is to provide an improved process for the fluidi~ed ~ed decomposition of silane and halosilanes with a minimal formation of silicon dust.
Still another object of the invention is to provide an energy efficient process for the formation of high purity silicon~
The foregoin~ and additional objects of ~his invention will become more fully apparent from the following description and accompanying drawings.
Disiclosure of the Invention The invention relates to an improved fl~id bed silane pyrolysis reactor comprising: ;
a) a vessel closed to the ambient surroundings and having a lower inlet port for the entrance of a silane and/or halosilane-containing D-13,697 . s :
... . .

~~

gas stream and for the removal of silicon particles from said vessel~ and an upper outlet for the removal of said gas stream and the gaseous by-products of the silane and/or halosilane decomposition;
lb) an upper heating zone in the reactor vessel having heating means therein which maintain said heating ~one at temperatures between about 650C and about ~00C and having silicon seed particles therein in fluid suspension at about the above-said temperatures;
c3 a reaction %one below said upper heating zone in said reactor vessel, said reaction zone effectively heated by silicon seed particles descending from said heating zone, which heatins establi~hes and maintains a vertical temperature gradient within the fluidized bed wherein the temperature at the top of said reaction zone is from about 650C to about 800C an3 the temperature at the base of said reaction zone is from abou~ 450C
to about 650~C and wherein sai~ silicon seed particles at about every height throughout said reaction zone are generally hotter than the laterally disposed portion of the reaction zone wall so th~t silane and~or halosilane in the gas stream preferentially decompose to silicon on the seed particles in ~he heterogenous mode;
d) a feed gas distribution zone below said reaction ~one having cooling means for maintainin~ the wall and internal surfaces of said distribution zone at a temperature of from about 200C to about 400~C, at which temperature the reaction rate of silane and/or halosilane decomposition is effectively eliminated; and D-13,697 . .

:~2~
_ 7 _ e) a collection zolle beneath said feed gas distribution zone wherein ~illcon-coated silicon seed particles may be removed.
The invention also rela~es to an improved process for the production of high purity polycrystalline silicon in a vertical fluidized bed reactor comprising the steps of:
a~ heating fluidized silicon seed particles in an upper heating zone of said reactor to a temperature of rom about 650~C to about 800C;
b) maintaining a reaction zone immediately beneath sai~ heatiny zone, said reaction zone effec~ively heated by silicon seed particles descending from said heating zone which heating establishes and maintains a vertical temp2rature gradient within the fluidized bed wherein the bed temperature at the top of said reaction zone is from about 650C to about 800C and the bed temperature at the base of said reaction zone is from about 450C to about 650C and wherein said silicon seed particles at about every heigh~ throuyhout said reaction zone are generally ho~ter than the laterally disposed portion of the reaction zone wall;
c~ coolinq a gas distribution zone vertically below said reac~ion zone such that the temperature in said gas distribution zone is from about 200~C to about 400C;
d~ introducing a silane and/or halosilane-containing gas stream into saîd gas distribution zone and passing said gas stream into said reaction zone;
e) decomposing said silane and/or halosilane onto said silicon seed particles, which particles being the hottest component of said reaction ~one thereby enhancing the heterogeneou~
D-13~697 formation of silicon on said ~ilicon seed particles and minimizlng the deposition o~ silicon on the internal surfaces of sa;d reactor and the undesirable homogeneous formation of silicon powder within sai~ reactori f3 removing the unreacted portion of said yas stream and the gaseous b~-products of said silane and/or halosilane decomposition; and g) collecting the silicon-coated silicon seed particles whereby silicon is obtained continuously or semicontinuously as low-cost, high purity polycrystalline silicon.
In accordance with the present invenkion an improved fluid bed reactor utilizes variable zone heatin~ to accomplish e~ficient thermal decompos~tion of silane and halosilanes onto silicon fluid becl particles and provides a process fo~ the thermal decompositiGn of silane and halo.silanes to silicon in the heterogeneous mode with a marked ~ 20 preference for deposition onto the silicon seed particles in the fluidized bed and not on the interior surfaces of the reactor. Further~ the present invention utilizes heating efficiently 50 as to reduce the power requirements needed to produce - 23 silico~.
As used herein, heterogeneous decomposition refers to the reduction of silane or a halosilane to - silicon which occurs in ~wo or more phases as when t~ decomposition occurs at a boundary between the gas and solid phase. This heterogeneous decomposition results in deposition of silicon on either suspended silicon particles in the fluidized bed or on the internal ~urfaces of the fluidized bed reactor. Homogeneous decomposition occurs in a D-13 7 69~

single phase such as the gas phase and produces light~ high surEace area xilicon powder or dust. At a g~ven temperature, the decomposition o 6ilane and halosilanes will be either heterogeneou~ or homogeneous depending on the silane or halosilane concentration, At 1000K ehe decomposition reaction is heteroyeneous if the silane and/or halosilane ooncentration is maintained below about 10 2 mole fraction~ By mole fraction is meant the number of m~les o~ silane and~or halosilane in a unit volum~
of the inlet gas stream divided by the total number of moles per unit volume o~ the inlet ~as stream.
The rela~ionship between the heterogeneous and homogeneous decomposi~ion of silanes is reported in the literature as in ~Influence of As~3r PH3 and B2R~ on ~.h~ Grow~h Rate and Resi5tivity o Polycrystall;nes ~ilicon Fil~ Deposlted from a SiH4-H~ Plixture~, Eversteyn and Put, Journal of Electrochemical Society, Solid State Science and Technology, January 1973, V~lume 120, No. 1, pages 106-110. Generally, a low silane/halosilane feed concentration ~s desirable to maintain the decomposition of silane and halosilane to silicon in a heterogeneous ~ode. ~owever~ a very low ~eed concentration of silane and~or halosilane may not provide a hiyh production rate of silicon.
- For the pyrolysis of silane and halosilane~
in the fluidized ~ed reactor the decomposition reaction preferably proceeds in the heterogeneous mode. In this manner silicon formed by reducing silane and/or halosilane is deposited on silicon particles suspended ln the fluidized ~edO Sili~on deposition on the walls or internal surfaces of the reactor may be siqnif icantly avoided by selectively maintaining the reactor surfaces at a temperature D-13,697 `~

below which the decomposition of silane or halosilane to ~ilicon takes place and/or by ~aintaining the reactor surfaces at a temperature below that of adjacent and nearby sillcon particles in ~he fluidized bed so that the deposition of silicon is directed towards the higher-temperature seed particles It is known that silane and halosilane decomposition to silicon is dependent on the reaction temperature. As reported in ~A Stagnant Layer ~iodel for the Epitaxial Growth of Silicon from Silane in a Horizontal Reactorn, F. C. Eversteyn, Journal of Electrochemical Society, Solid State Science and ~echnology, July 1970, vol. 117 noO 7 page 925, the decomposition reaction to form silicon increases significantly with increasing temperature. The decomposition r~te of silane and/or halosilane increases at a ten-fold rate from about 575C to about 675C and increases again at a ten-fold rate from about 675C to about 775C.
Thus, h~gh reaction temperatures are desirable to achieve a high decomposition rate of silane and halosilane to silicon.
~he fluiaized bed reactor in accordance with this inYention is a vertical, generally cylindrical vessel wherein high purity silicon is deposited on silicon seed particles suspended in the - fluidized bed~ The ratio of bed height to bed diameter may be from about 2:1 to about 20:1~
preferably about 1~:1. The silicon seed particles are fluidized b~ a gas stream made up of the silane and/or halosilane feed and a recycle by-product gas stream or an inert gas stream or a combination thereof, such that the silane/halosilane D-13,697 ~, ............... ..

concentration is between about 10% and about 100%, preferably about 50~ based on the volume of the gas stream~
From about 70 to about 90 percent of the total heat input of the fluidized bed reactor is provided in the uppermost section of the vessel, th~
heating zone, which may occupy about the uppermost twenty-five percent of the total volume of the reactor. Heat may be supplied to this zone and to the silicon seed particles raised through the fluid bed to this zone by wall and/or immersion heaters, such as resistance heaters, which heat the fluidized bed particles to from about ~SO~C to about 800C, preferab~y about 700C.
The reaction zone immediately beneath the heating zone oGcupies the remaining portion of the fluidized bed. This portion of the fluidized bed is primarily heated by interacting with hot silicon particles from the upper heating zone of the reactor. Guard heaters disposed around the circumference of the reaction zone supply only that heat necessary to compensate for heat losses. The reactor wall temperature at the base of the fluidi~ed bed is from about 300C to about 600~C, preferably about 450C. The temperature of the fluidized bed at its base is from about 450C to about 650C. The temperature of the fluidized bed at its top, which is in intimate contact with the heating zone, is from about 650C to about 800C.
Typically the fluidized bed temperature in the reaction zone is maintained at a gradient of from about 550C at the base of the fluidized bed to about 700C at the top of the reaction zone~ At every height in the reaction zone the temperature of D-13,697 .. . . ... . . .. . ... . . .. . .

the fluidized bed is greater than the reactor wall temperature so that the ~eed silane and halosilane is preferentially decomposed to silicon on the surface of the fluidized bed particles.
Beneath the reaction zone, the reactor employs a gas distrihutor for the introduction of the feed and other possible fluidi~ing gas streams, and where seed particles to be fluidized may optionally be introduced and~or generated. The ratio of gas velocity to minimum f~uidi2ation velocity just above the distributor is from about
2:1 to about 6:1, preferably about 4:1. In this gas distribution zone, the reactor walls are cooled to a range of from about 200~C to about 400C, by cooling water, nitrogen or the like, at which temperatures the decomposition of silane and halosilane t~
silicon is not favored so that little silicon is formed in this zone. Because of the concentration of silane and/or halosilane in the feed stream, silicon formation in this zone may be homogeneous, producing silicon powder that may obstruct openings in this portion of the reactor if the silicon production rate therein were significant.
The reactor further employs a collector ~5 ~eans such as a boot separator or the like at its base to segregate product particles of predetermined size from the seed particles, which may also be introduced in this section, and to accumulate product silicon particles. This product withdrawal zone is relatively cool, having a temperature below about 200C.
The silicon seed particles used in the above-described reactor and process have typical initial diameters of about 40 to about 400 microns D-13,697 depending on the size of the re~ctor. The size oE
the particles comprising the fluidized bed is not critical to the invention and may be maintained within the limits commonly employed in various fluidized bed applications known in the art.
In accordance with the process of this invention~ as the silane and/or halosilane decompose to silicon, the seed particles grow in size to abou~
400 microns and larger whereupon these product particles descend from the fluidized bed.
Additional seed particles are introduced into the reactor to maintain the pr~cess. Fluidization conditions in the boot separator are established so as to allow only larger silicon particles to settle within the chamber of the boot vessel while transporting the seed size p~rticles into the fluidized bed reaction zone. These large product particles canlthen ~e either continuously or per;odically removed as product ma~erial. Such large particles are of suficient size to be easily handled without any undue contamination of the ultra-high purity material.
~ hus the present invention provides a fluidized bed silane pyrolysis reactor wherein silicon bea particle5 are heated in the uppermost porti~n of the reactor, a heating zone, and which par~icles then transfer heat ~o the reaction zone - wherein the bed particles maintain a higher temperature than the walls of the reactor in the reaction zone, so that the thermal heterogeneous decomposition of silane to silicon preferentially occurs on silicon bed particles, the wall temperature of the reactor not being as preferred for the decomposition reac~ion. The present D-13, 697 .

, . ~

invention has been found to effectively utilize heating so as to reduce the overall power requirements to produce silicon~
Brief ~escription of the Drawings The present invention will become more apparent from the following description thereof when considered together with the accompanying drawings which are set forth as being merely illustrative of the invention and are not intended in any manner to be limitative thereof and wherein:
Figure 1 is a schematic representation of the process for silane pyrolysis to form silicon;
Fig~re 2 is a partial cross-section of the reaction vessel showing the heating, reaction and distribution zones;
Figure 3 is a partial cross-section of the gas distribution zone; and Figure 4 is a partial cross-section of the reaction vessel showing the distribution of seed particles therein.
Common components in each of the Figures are identified with the same reference number7 As used herein, reference to silane includes silane and the halosilanes.
Detailed Description of the Drawings . A~ shown in the schematic representation of .- Figure 1, the hi~h purity silane to be pyrolyzed enters through conduit 1 to heat exchanger 2, which may be used to preheat the silane or simply to insure a constan~ feed temperature o~ about 25C.
Valves 3, 21 and 22 control the flow of the feed silane, recycle by-product gases, and secondary D-13,697 ....

. .
3 ' diluent, if one is de~ired, respectively. These feed streams are homogenized in mixer 4 before being introduced in the gas distributor ~ of the reaction vessel 8.
Th~ general function of the gas distributor 7 is to allow introduction of the gaseous streams in a way that efficiently fluidizes the particles in the bed. The decomposition of silane occurs in the fluidized bed reaction vessel 8. The expanded head 9 reduces the velocity of the by-product gases exiting the top of the reactorO
Product, high-purity silicon particles are separated from smaller-diameter seed particles in the boot separator 18, a small diameter cylindrical vessel located below the reaction vessel 8 and distributor 7. Seed particles on which decomposition will occur may be ;ntroduced in boot separator 18 through valve 5 from seed particle hopper 6. Some of the silane gas, by-product gases and/or inert gas is circulated through boot separator 18 and into fluidized bed 8. The gas flow is regulated so that smaller particles are carried from the boot separator and maintained within the bed until they reach a larger size, at which time they settle from ~he fluidized bed into the b~ot separator 18 and can be removed as product material through control valves 19 and stored in product hopper 20~
The by-product gas stream 10 taken from the 30 top of the bed is cooled in heat exchanger 11 and any entrained dust is removed in filter 120 A
by-proauct gas stream 14, which may comprise hydrogen ~uel in the case of silane pyrolysis, may ~hen be bled from the loop by valve 13 for other use ~-13,697 . . .. . . .. .. . . . . . . . . . . . . . . . ..

~ 16 -in the silane production process or elsewhere. The remaining recycle by-product gas is compressed in compressor 15 sufficiently to be returned to the bed operating pressure of from about 5 to about 10 psig after equipment pressure drops and is reheated in heat exchanger 16. ~he recycle hydrogen stream can be directed through valve 17 to the bottom of boot separator 18 for fluidization o particles therein and/or can be directed through valve 21 for use as a diluent for the silane feed stream, as previously described.
The fluidized bed reactor 8 is shown in cross-section in Figure 2~ The internal surfaces of the reaction vessel is preferably a non-contaminating surface such as incoloy all~y.
Wall heaters 32 encircling reaction vessel 8 may be used separately or in conjunction with immersion heaters 30 suspended from the top of reaction vessel 8 to apply heat to bed particles in the heating zone. References to wall temperatures ;n this description are intended to include the surface temperature of i~mersion heaters 30. Further, it is within the scope of this invention to heat the bed in the heating zone exclusively with immersion heaters 30 ~r any other heating means that w~uld accomplish ~he same end. Expanded head 9 is shown positioned slightly to the side of vessel 8 to -- permit easy access to bed internals and to minimize the required length o immersion heaters 30.
During operation, the majority of heat inpu~, about 70 to 90 percent of the to~al heat input, preferably 80 percent, is provided in the heating zone ~9 which is shown occupying about the top 2-1/2 bed diameters of the reaction vessel 8.

D-13,S97 .. . . . . ... . .. . . . . .. . . ... . . ... .. ..... ..

-The ratio of bed height to bed diameter is generally from ~:1 to 20:1 but i9 preferably about 10:1. The heaters 32 encircling the vessel 8 may be ceramic or the like, but the immersion heaters 30 should preferably have a non-contaminating surface, for example quartz or the alloy incoloy. These resistance-type heaters are operated so that the bed temperature in this zone 29 is from about 650C to 800C. Within the heating zone ~9, the heat may be applied uniformly or in a gradient with the same effect. Since the heating ~one is relatively short when compared to bed diameter~ the inherent mixing of the fluidized bed tends to equilibrate the-temperature in this heating zone.
The remainder of the heat input is applied in the reaction zone 28 by wall heaters 32 so that the wall temperature at the bottom of the vessel 8 is from about 300C to about 600C, and the bed temperature at its base i5 between 450~C and 650C, preferably about 550C. These heaters essentially provide heat only to compensate for heat losses.
The majority of the hea~ in the reaction ~one 28 comes from fluidized bed particles from the heating zone 29. The mixing which occurs in the fluidized bed is responsible for heating the particles in the reaction zone 28. The temperature gradient in the reaction zone is a re~ult o the heating zone 29 above and the relatively cool gas distribution zone 27 ~low.
Annular cooling means 33 surrounds the gas distributor 7. Fluidizing cone 34 of the distributor 7 allows introduction of the feed stream gases. The entire assembly of reaction vessel 8, distributor 7 and boot separator 18 is encased by insulation 31.
D-13,697 - lB -Figure 3 shows the gas distributor 7 in detail. The uniformly perforated fluidizing cone 34 is encircled by cooling coils 39. Supplemental cooliny may be provided by annular cooling means 33 at the base of ~he fluidized bed R. The fluidizing feed gases are introduced thIough inlet 38 and directed properly toward cone 34 by annular dividing means 36, which seals off the region defined by cone 34 and distributor casing 37. The gas distribution zone is shown encased by insulation 31.
The distributor 7 is cooled to about 30~C
by cooling water, nitrogen, or any well known means~ The perforated metal cone 34 of the distributor 7 provides the means for feed stream introduction whereby the bed particles are fluidized uniformly~ The ratio of feed stream superficial gas velocity to minimum fluidization velocity just above the distributor is generally between 2:0 and 6Ø
This ratio increases with temperature, S9 the preferred ratio may be about 7:1 or 8:1 at the top of the bed. The composition oE the feed stream may be between about 10 and about 100 percent silane by volume, but is typically about 50 percent by volume.
Figure 4 shows a typical distribution of ~5 silicon seed particles ;n a vertical cross-section of a fluidized bed reactor in accordance with this inventionO The silicon seed particles, some of which are designated by the number 23, are shown i~troduced into separator 18 through inlet 22.
These par~icles have initial diameters ~f from about 40 to about 400 microns. The seed particles are entrained in a gas stream which enters through inlet 24 containing inert gases and/or recirculant by-product gases which causes the particles to ascend into the fluidized bed.
D-13,697 i`' ~2~

Silicon seed particles having relatively ~mall diameters rise through the reaction zone 28 where they intermix with and are heated by other silicon particles. The temperature of the fluidized bed in the reaction ~one ranges from about 450C to about C50DC at its base to from about 650C to about 800C at its top. Above the reaction zone is the heating zone ~9 wherein a temperature between about 650~C and 800C is maintained by the use of heating 1~ means such as wall heaters 32 and immersion heaters 30. Small diameter silicon seed particles rise into the heating zone and attain a temperature substantially equal to the temperature in the heating zone. The particles return to the react~on zone ~8 by the inherent mixing action of the fluidizea bed. ~eat is transferred between particles so as to maintain the temperature and the temperature gradient of the reaction zone.
A feed stream containing silane is in~roduced through inlet 380 The feed gas ~tream passes through the perforations in fluidi2ing cone 34 an~ enters into the reaction zone 28 of the fluidizea bed.
Silane is reduced in the reaction zone and deposits silicon preferentially on the hot silicon particles. A high silane concentration in the ~eed gas stream entesing at the base of the 1uidized bed ~ - is exposed to a sufficiently low reaction temperature so as to favor heterogeneous decomposition over homogeneous decomposition. As the feed gas stream advances upward through the reaction zone the silane concentration decreases as the bed temperature lncreases which promote higher reaction ra~es that continue to favor heterogeneous D-13,697 .

L~ 8 -- o --decompositionO At the top of the reaction zone, substantially all of the silane in the feed gas stream has decomposed. As product silicon is depos.ited on the seed particles, the particles grow in size. When the diameter of a product silicon particle is from about 400 to about 1500 microns o~
larger; depending on the size of the reactor, the particle descends from the reaction zone 28, past the gas distribution zone 27 and the separator 18, and into a collectox 20.
The following example further illustrates the p~esent invention:
EXAMPLE
The reactor and process of this invention as depicted in the preceding Figures were used to thermally decompose silane to silicon.
The reactor had a bed height of 72 inches and a bed diameter of 6 inches for a bed height-to-diameter ratio of 12:10 Approximately ~
Xw of power in the form of heat were supplied to the top 15 inches of the bed, the heating zone, and approximately 2 Kw were supplied over the remainder of the bed, the reaction zone. Bed operating ~5 pressure was about S psig. The distxibutor temperature was 319C and the ratio of superfici21 -eed strea~ velocity to minimum fluidization velocity was 4:1 at the bottom of the bea. The feed - stream of 21.6 volume percent silane was introduced a~ a temperature o~ about 25C and a pressure of about 30 psig and provided a 1 Kg silicon per hour throughput.
In the zoned heating concept of the present invention, the highest temperature occurs in the D-13 t 697 ... . . . .

heating zone, where the silanle has essentially all reactedD Since the silane concentration is extremely low, it is not likely to plate on the walls or to form powder, The reaction zone contains fluidized bed particles that have been heated by back mixing of the particles from the heating zone.
These particles are hotter than the walls in this zone, so silicon deposition on particle surfaces is favored over deposition on the reactor walls. The low distributor temperature inhibits decomposition of silicon on its walls because the reaction rate of silane to silicon and hy-product hydrogen is very low at this temperature. By maintaining the temperatures in ~hese zones, the silane pyrolysis occurs continuously with no significant plating of silicon on the reactor surfaces nor any significant homogeneous silicon powder accumulation in the reactor to obstruct the opera~ion of the reactor.
The temperature profiles of these three zones are shown in Figure SO The temperature along the center of the fluidized bed is shown as a solid line. The temperature of the fluidized bed adjacent to the reactor wall is shown as a dashed line~ The temperature of the reactor wall is depicted as a 2~ dotted line. As can be seen from the Figure, the temperature of the fluidized bed particles at a given height is higher than the wall temperature at that height over most of the height of the fluidized bed. This temperature differential is most pronounced in the lower portion of the fluidized bed where most of the silane pyrolysis occur~, The 10 XW power input which yielded about 1 Xg silicon per hour in accordance with the present invention is approximately thirty times as energy D-13,697 , , .. . . . . . . . . ..

~.2~

efficient as the Siemen's process as disclosed in U~SD patent 3~979,490 and may represent a savings over other fluidized bed processes.
It is to be understood that modifications 5 and changes to the preferred embodiment of the invention herein described and shown can be made without departing from the spirit and scope of the invention.

D-13,697 ~ "

Claims (13)

1) An improved fluidized bed silane pyrolysis reactor comprising:
a) a vessel closed to the ambient surroundings and having a lower inlet for the entrance of at least one of a silane and halosilane-containing gas stream and for the removal of silicon particles from said vessel, and an upper outlet for the removal of said gas stream and the gaseous by-products of the at least one of silane and halosilane decomposition;

(b) an upper heating zone in the reactor vessel having heating means therein which maintain said heating zone at temperatures between about 650°C and about 800°C and having silicon seed particles therein in fluid suspension at about the above-said temperatures;
c) a reaction zone below said upper heating zone, in said reactor vessel, said reaction zone effectively heated by silicon seed particles descending from said heating zone, which heating establishes and maintains a vertical temperature gradient within the fluidized bed wherein the temperature at the top of said reaction zone is from about 650°C to about 800°C and the temperature at the base of said reaction zone is from about 450°C
to about 650°C and wherein said silicon seed particles at about every height throughout said reaction zone are generally hotter than the laterally disposed portion of the reaction zone wall so that silane and/or halosilane in the gas stream preferentially decompose to silicon on said seed particles in the heterogenous mode;
D-13,697 d) a feed gas distribution zone below said reaction zone having cooling means for maintaining the wall and internal surfaces of said distribution zone at a temperature of from about 200°C to about 400°C, at which temperature the reaction rate of silane and/or halosilane decomposition to silicon is effectively eliminated;
and e) a collection zone beneath said feed gas distribution zone wherein silicon-coated silicon seed particles may be removed.
2) The improved fluidized bed silane pyrolysis reactor in accordance with claim 1 wherein guard heaters are disposed in the walls of the reaction zone so as to compensate for heat losses through said walls.
3) The improved fluidized bed silane pyrolysis reactor in accordance with claim 1 wherein the ratio of bed height to bed diameter is from about 2:1 to about 20:1.
4) The improved fluidized bed silane pyrolysis reactor in accordance with claim 1 wherein the ratio of bed height to bed diameter is about 10:1.
5) The improved fluidized bed silane pyrolysis reactor in accordance with claim 1 wherein said collection zone comprises a boot separator.
6) An improved process for the production of high purity polycrystalline silicon in a vertical fluidized bed reactor comprising the steps of:

D-13,697 a) heating fluidized silicon seed particles in an upper heating zone of said reactor to a temperature of from about 650°C to about 800°C;
b) maintaining a reaction zone immediately beneath said heating zone, said reaction zone effectively heated by silicon seed particles descending from said heating zone which heating establishes and maintains a vertical temperature gradient within the fluidized bed wherein the bed temperature at the top of said reaction zone is from about 650°C to about 800°C and the bed temperature at the base of said reaction zon? is from about 450°C to about 650°C and wherein said silicon seed particles at every height throughout said reaction zone are generally hotter than the laterally disposed portion of the reaction zone wall;
c) cooling a gas distribution zone vertically below said reaction zone such that the temperature in said gas distribution zone is from about 200°C to about 400°C;
d) introducing at least one of a silane and halosilane-containing gas stream into said gas distribution zone and passing said gas stream into said reaction zone;
e) decomposing said at least one of silane and halosilane onto said silicon seed particles, which particles being the hottest component of said reaction zone thereby enhancing the heterogeneous formation of silicon on said silicon seed particles and minimizing the deposition of silicon on the internal surfaces of said reactor and the undesirable homogeneous formation of silicon powder within said reactor;

D-13,697 f) removing the unreacted portion of said gas stream and the gaseous by-products of said at least one of silane and halosilane decomposition; and g) collecting the silicon-coated silicon seed particles whereby silicon is obtained continuously or semicontinuously as low-cost, high purity polycrystalline silicon.
7) The process in accordance with claim 6 wherein said heating zone is heated to about 700°C.
8) The process in accordance with claim 6 wherein the fluidized bed in said reaction zone has a temperature of about 700°C at its top and about 550°C at its base.
9) The process in accordance with claim 6 wherein the bed temperature at the base of said reaction zone is about 550°C and the temperature of the reactor wall at the base of said reaction zone is 450°C.
10) The process in accordance with claim 6 wherein the ratio of gas velocity to minimum fluidization velocity immediately above said gas distribution zone is from about 2:1 to about 6:1.
11) The process in accordance with claim 6 wherein the ratio of gas velocity to minimum fluidization velocity immediately above said gas distribution zone is about 4:1.
12) The process in accordance with claim 6 wherein the concentration of said at least one of silane and halosilane in said gas stream is between about 10%
and about 100%.

D-13,697
13) The process in accordance with claim 6 wherein the concentration of said at least one of silane and halosilane in said gas stream is about 50%.

D-13,697
CA000438549A 1982-11-05 1983-10-06 Zone heating for fluidized bed silane pyrolysis Expired CA1218218A (en)