CA1100434A - Process for electrolytic deposition of metals on zirconium materials - Google Patents
Process for electrolytic deposition of metals on zirconium materialsInfo
- Publication number
- CA1100434A CA1100434A CA288,487A CA288487A CA1100434A CA 1100434 A CA1100434 A CA 1100434A CA 288487 A CA288487 A CA 288487A CA 1100434 A CA1100434 A CA 1100434A
- Authority
- CA
- Canada
- Prior art keywords
- article
- zirconium
- solution
- process according
- tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
PROCESS FOR ELECTROLYTIC DEPOSITION
OF METALS ON ZIRCONIUM MATERIALS
Abstract A process for the electrolytic deposition of a metal layer on an article comprised of zirconium or a zirconium alloy is disclosed. The article is activated in an aged aqueous solution comprising from about 10 to about 20 grams per liter ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid. The solution is aged by immersion of pickled zirconium in the solution for at least about 10 minutes. The loosely adhering film formed on the article in the activating step is removed and the article is contacted with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current.
OF METALS ON ZIRCONIUM MATERIALS
Abstract A process for the electrolytic deposition of a metal layer on an article comprised of zirconium or a zirconium alloy is disclosed. The article is activated in an aged aqueous solution comprising from about 10 to about 20 grams per liter ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid. The solution is aged by immersion of pickled zirconium in the solution for at least about 10 minutes. The loosely adhering film formed on the article in the activating step is removed and the article is contacted with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current.
Description
24NF-04~32 4~
Background of the Invention This invention relates to a process for electrolytic deposition of a metal layer on zirconium or a zlrconium alloy, and more particularly to an improved process for electrolytic deposition of a metal film such as a copper film on the internal surface of a long hollow cylindrical tube of zirconium or a zirconium alloy.
Nuclear reactors are presently being designed, constructed and operated with the nuclear fuel being contained in fuel elements which can have various geometric shapes, such as plates, tubes, or rods. The fuel material is usually enclosed in a corrosion-resistant, non-reactive, heat conductive container or cladding. The elements are assembled together in a lattice at fixed distances from each other in a coolant flow channel or lS region forming a fuel assembly, and sufficient fuel assemblies are combined to form the nuclear fission chain reacting assembly or reactor core capable of a self-sustained fission reaction.
The core in turn is enclosed within a reactor vessel through which a coolant is passed.
The cladding serves several purposes and two primary purposes are: first, to prevent contact and chemical reactions between the nuclear fueI and the coolant or the moderator if a moderator is present, or both if both coolant and moderator are present; and second, to prevent the radioactive fission products, some of which are gases, from being released from the fuel into the coolant or the rnoderator, or both if both coolant and moderator are presen-t.
common cladding materials are zirconium and its alloys are well as others that are commonly used. Tl~e failure of the cladding, i.e., a 105s of the leak ti~htnèss, can contaminate the coolant or moderator and the associated systems ~ith radioactive long-lived products to a degree which interferes with plant operation~
1~ b ~
..
3~
Problems have been encountered in the operation of nuclear fuel elements which employ certain metals and alloys as the clad material due to mechanical or chemical reactions of these cladding materials under certain circumstances. Zirconium and its alloys, under normal circumstances, are excellent nuclear fuel claddings since they have low neu-tron absorption cross sections and at temperatures below about 750F (about 398C) are strong, ductile~ extremely stable and non-reactive in the presence of demineralized water or steam which are commonly used as reactor coolants and moderators.
However, fuel elemen-t performance has revealed a problem with the brittle splitting of the cladding due to the combined interactions between the nuclear fuel, the cladding and the fission products produced during nuclear Eission reactions. It has been discovered that this bri-ttle splitting is due to localized mechanical stresses resulting from the differential expansion of the fuel into contact with the cladding (i.e., stresses in the cladding are localized at cracks in the nuclear fuel). Corrosi~e fission products are released from the nuclear fuel and are present at - the intersection of the fuel cracks with the cladding surface~ Fission products are created in the nuclear fuel during the fission chain reaction occurring during operation of a nuclear reactor. The localized stress is accentuated by high friction between the fuel and the cladding.
~.
~.
L3~
A novel aqueous electrol~tic activating solution ancl a method for electroplating a metal layer on zirconium and zixconium allo~s are disclosed in United States Patent Number 4,017,36a. This Patent issued in the names of Daniel E. Wax and Robert L. Cowan on April 12, 1977 and is assigned to the same assignee as the present invention. The electrolplating method of this invention is particularly suitable for coating the inside surface of zirconium or a zirconium alloy with the protective layer of copper, nickel or iron. The first step of the process comprises acti~ating the zirconium or zirconium allo~ in an aged a~ueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride and from 0.75 to about
Background of the Invention This invention relates to a process for electrolytic deposition of a metal layer on zirconium or a zlrconium alloy, and more particularly to an improved process for electrolytic deposition of a metal film such as a copper film on the internal surface of a long hollow cylindrical tube of zirconium or a zirconium alloy.
Nuclear reactors are presently being designed, constructed and operated with the nuclear fuel being contained in fuel elements which can have various geometric shapes, such as plates, tubes, or rods. The fuel material is usually enclosed in a corrosion-resistant, non-reactive, heat conductive container or cladding. The elements are assembled together in a lattice at fixed distances from each other in a coolant flow channel or lS region forming a fuel assembly, and sufficient fuel assemblies are combined to form the nuclear fission chain reacting assembly or reactor core capable of a self-sustained fission reaction.
The core in turn is enclosed within a reactor vessel through which a coolant is passed.
The cladding serves several purposes and two primary purposes are: first, to prevent contact and chemical reactions between the nuclear fueI and the coolant or the moderator if a moderator is present, or both if both coolant and moderator are present; and second, to prevent the radioactive fission products, some of which are gases, from being released from the fuel into the coolant or the rnoderator, or both if both coolant and moderator are presen-t.
common cladding materials are zirconium and its alloys are well as others that are commonly used. Tl~e failure of the cladding, i.e., a 105s of the leak ti~htnèss, can contaminate the coolant or moderator and the associated systems ~ith radioactive long-lived products to a degree which interferes with plant operation~
1~ b ~
..
3~
Problems have been encountered in the operation of nuclear fuel elements which employ certain metals and alloys as the clad material due to mechanical or chemical reactions of these cladding materials under certain circumstances. Zirconium and its alloys, under normal circumstances, are excellent nuclear fuel claddings since they have low neu-tron absorption cross sections and at temperatures below about 750F (about 398C) are strong, ductile~ extremely stable and non-reactive in the presence of demineralized water or steam which are commonly used as reactor coolants and moderators.
However, fuel elemen-t performance has revealed a problem with the brittle splitting of the cladding due to the combined interactions between the nuclear fuel, the cladding and the fission products produced during nuclear Eission reactions. It has been discovered that this bri-ttle splitting is due to localized mechanical stresses resulting from the differential expansion of the fuel into contact with the cladding (i.e., stresses in the cladding are localized at cracks in the nuclear fuel). Corrosi~e fission products are released from the nuclear fuel and are present at - the intersection of the fuel cracks with the cladding surface~ Fission products are created in the nuclear fuel during the fission chain reaction occurring during operation of a nuclear reactor. The localized stress is accentuated by high friction between the fuel and the cladding.
~.
~.
L3~
A novel aqueous electrol~tic activating solution ancl a method for electroplating a metal layer on zirconium and zixconium allo~s are disclosed in United States Patent Number 4,017,36a. This Patent issued in the names of Daniel E. Wax and Robert L. Cowan on April 12, 1977 and is assigned to the same assignee as the present invention. The electrolplating method of this invention is particularly suitable for coating the inside surface of zirconium or a zirconium alloy with the protective layer of copper, nickel or iron. The first step of the process comprises acti~ating the zirconium or zirconium allo~ in an aged a~ueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride and from 0.75 to about
2 grams per liter of sulfuric acid. The solution is aged by immersion of pickled zirconium in the solution for about 10 minutes. The second step of the process comprises electroplating the zirconium material in a plating bath of the metal to be plated on the zirconium material in the presence o~ an electrode.
~n electroplating process requires the use o~ an electrode approximately the same length as the piece being plated. The nuclear fuel cladding is a tube of about 14 feet in length and about 0.50 inch in internal aiameter. This means that an
~n electroplating process requires the use o~ an electrode approximately the same length as the piece being plated. The nuclear fuel cladding is a tube of about 14 feet in length and about 0.50 inch in internal aiameter. This means that an
- 3 -A~
~ ~ 24NF-04232 electrode of about 14 feet in length with about 0.125 inch in diameter is required for an electroplating process.
zirconium materials activated in an ammonium bifluoride-sulfuric acid solution have on the sur~ace a first layer of a black color that is highly adherent to the ~irconium s~s-trate and is electrically conductive. This layer is believed to make it possible to initiate electroplating of the zirconium material.
These activa-ted zirconium materials also have a second layer on the first layer that is a loosely adhering layer of similar color to the first layer. The presence of this second layer is believed to have an adverse effect on adhesion and to give rise to the possibility of blistering of the coating.
Therefore it is desirable to develop an electrolytic process for plating zirconium materials that includes a step oE removing the loosely adhering la~er on the zirconium material resulting from the activation of the zirconium material in the ammonium bifluoride-sulfuric acid solution.
Summary_of the Invention ~ It has now been discovered that an article comprised of zirconium or a zirconium alloy can be electrolytically plated with a metal layer of a metal seIected from the group consisting of copper, nickel and chromium to achieve improved adhesion between the metal layer and the article when the article is free of any loosely adhering films formed during an activation step.
The first step of this process is activating the article in an aged a~ueous activating solution comprised of from about 10 to about 20 grams per liter of ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid. The next step of the pro~ess is removing the loosely adhering film formed on the article in the activating step. The last step of the process is contacting the article ~ith an electrolytic plating solution ~¢~, ~ 3~ 24NF-Q4232 containing the metal therein to be deposited on the article in the presence of an electrode receiving current.
The removal of the loosely adhering film formed on -the article in the activation step can be done by chemical treatment, ultrasonic treatment or by swabbing the surface with cotton or an organic material. The chemical removal of the film is accom-plished by using (a) an aqueous solution comprising from about 2 to about 10 percent fluoboric acid and the balance waterr or (b) an aqueous solution comprising from about 2 to about 10 percent hydrofluosilicic acid and the balance water. The ultrasonic removal of the film is accomplished by immersing the article in water and applying ultrasonic energy to the article.
Obiects of'the Invention . . . _ It is an object of this invention to provide a process for the electrolytic plating of an article comprised of zirconium or a zirconium alloy, especially when the article is in the form of a nuclear fueI element cladding comprising a long hollow cylindrical tube of small diameter.
Another object of this invention is to provide a step for removing the loosely adhering film on an article comprised of zirconium or a æirconium alloy after being contacted in an activating solution and prior to being subjected to electrolytic plating.
Othér objects and advantages of this invention will become apparent to the person skilled in the art from the following description of the invention and from the appended claims.
... . . . . ..
Description of th'e I'nvention This inventlon comprises a process for the electrolytic deposition of a metal film on an article being comprised of zirconium or a zirconium alloy. Thé process broadly comprises a step of activating the article, a step of removing any loosely, ~4NF-04232 3~
adhering films formed on the article in the activation step and a step of contactlng the article with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current. The process can also include the optional steps of rinsing the article in water (preferably deionized wa-ter) after the activation step, the ~ilm removal step and the e:Lectrolytic plating step. The rinsing prevents carry-over on the surface of the article of the solution with which it was in contact so there is no formation of deposits or films on the article from this solution~ When the article is to be contacted with another solution, the rinsing also prevents introduction of impurities in that other solution.
~ detailed discussion of the process of this invention will now be presented as shown in the attached Figure. In the first step the article of ~irconium or a zirconium alloy is contacted with an aged aqueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride (preferably a starting amount of a~out 15 grams per liter ammonium bifluoride) and from a~out 0.75 to about 2.0 grams per liter o sulfurlc acid (prefera~Iy a starting amount of about 1.0 grams per liter).
The solution is aged by immersion of a piece of pickled zirconium for at least ahout lO minutes at ambient temperature. It has been found that solutions outside the foregoing ranges for the ammonium bifluoride component and the sulfuric acid component do not produce good adherent platings on the article.
The article is contacted wit~ the aged aqueous activating solution for about one minute at ambient temperature (approximately 20-30C)~ and the activating solution is stirred or otherwise agitated ~rior to contacting the article with the solution. The article is ready for immediate`wse in the following steps of : .
.
this process or can be stored for several days or longer before being used in the following steps of this process.
An optional step of rinsing the article in water can he practiced, preferably using deionized water, to free the article of any residual traces of the activating solution.
The next step is removing any loosely adhering film (i.e.
"smut") ~ormed on the article in the activating step. This step is performed by either contacting the article in a chemical solution ~hich removes the film from the article, using ultrasonic energy to remove the film, or swabbing the surface of the article with a cotton s~ab or an organic swab such as nylon or polyester. The organic swab can be ~rapped around a rubber plug and forced through the article when the article is a hollow tube and the wrapped plug is approximately the same size as the internal diameter of the tube~ This leaves the article with a dark adherent electrically conducting sur~ace ~ilm or layer of zirconium o~ide that can ~e plated with any of the known electrolytic metal plating solutions.
One chemical solution for contacting the article to remove the looseIy adhering film is comprised of from about 2 to about 10 percent fluo~oric acid by volume`in wa~er. Solutions belo~
about 2 percent by volume do not remove the loosely adhering film, and solutions above ahout 10 percent by volume start to attack the more adherent film underlying the loosely adhering film.
The solution is used at about 25+5C and the article is contacted in this solution for about one minute.
~nother chemical solution for contacting the article to remove the looseIy adhering film i5 comprised o~ from about 2 to about 10 pexcent hydro~luosilicic acid b~ volume in water.
Solutions beIow abou~ 2 percent ~ volume do not remove the loosely adhering ~il~, and solutions above~about 10 percent by volume - .
.
~ '4 34 24NF-04232 start to attack the more adherent film underlying the loosely adhering film. The solution is used at about 25~5C and the article is contacted in this solution for about one minu-te.
Removal of the loosely adhering film from the article can -' 5 also be accomp]ished by the use of ultrasonic rinsing in water, iOe., su~merging the article in water and applying ultrasonlc energy in the range of about 20,000 to'about 300,000 cycles per second (cps). This is continued ~or a time of about one to two minutes or more, or until visual observa-tion shows that no more film is being removed. Below about 20,000 cps, the rate of removal is too slow, and the equipment for running above 300,000 cps involves added expense. '-Swabbing the loosely adhering film from the article is done by uniformly rubbing the surface with'co-tton or paper or other absorbent material, or ~y brushing the surface with a brush con-taining natural hog bristles or nylon bristles. In one method ~' cotton swabs or organic swabs such as polyester and nylon swabs are rubbed over the surface of the article. When the article is in the~form of a tube the swab is driven through the tube by use of air pressure.
Next, after removal of the loosely adhering film, an optional step of rinsing the article in water can be practiced, preferably using deionized water, to free the article of any residual traces of the material used in removing the loosely adhering film. 'This step is desirahle when one of the chemical solutions has been used.
The article is contacted wi-th any of the kno~n electrolytic ' plating solutions containing the'metal to be deposited on the article upon contact with'the article in the presence of an ; 30 electrode'receiving current. Typically the article is submerged ~ in the'electrolytic plating solution adjacent the electrode with . . .
~ 43 ~ 24NF-04232 a gap between the article and the electrode of about 0.2 inch or more to enable uniform build up of the metal on the article.
Preferred met~ls to be deposited on the arkicle of zirconium or a zirconium alloy include copper, nickel and c'nromium, and an especially preferred metal to be deposited on the article is copper.
For electrolytically depositing copper, an aqueous bath of the following composition has been employed: 150 to 250 grams/
liter of copper sulfate ~CuS04 . 5 H20), 45 tollO grams/liter of sulfuric acid (~2 S04), and 0.002 to 0.005 grams/liter of thiourea (NH2 CS NH2) with the balance being water. The temperature of the bath is maintained between 32 and ~2C during plating, and a current density of 16 to 22 amps/decimeter2 (dm2) is applied. When the article is in the :orm of a long hollow cylindrical tube, the bath is flowed through the tube at 800 to 12Q0 ml./minute, and the anode is a solid oxygen-free high conductivity copper cylindrical tube 0.125 to 0.200 inch in diameter. This procedure produces a very good as-plated adherence with no porosity. In order -to insure that the plated article can be used at elevated temperatures without any substantial loss of adhesion, the plated zirconium is out-gassed at a temperature of about 300 to about 400F (149 to 204C~ Eor a time period of about three hours. In thi:s out-gassing the temperature is raised from ambient to the final temperature at a rate of abouk 50F to 125F per ~our.
During the plating of copper on the article, a considerable : quantity of hydxogen gas is evolved. The electrolytic copper plating solution is flowed slowly over the article, and this results in the hydrogen tending to adhere to the wall of the tube.
It is necessary to remove this hydrogen gas so that it does not develop back-pressure during plating (i.e.~ pressure on the .
~ _ g _ .,. ,. ~
,.~;~", surface of the article being plated that stops the plating~.
- The plating process is further facilitated when the surface of the article to be plated is positioned in a vertical position so -that evolved hydrogen is swept upward away from -the surface being plated.
For electrolytically plating nickel on zirconium, an aqueous bath of the following composition is emp:Loyed: 320 to 340 grams/
liter of nickel sulfate ~Ni SO4 6 H2O)l 40 to 50 grams/liter nickel chloride (Ni C12 6 H2O), 36 to 40 grams/liter of boric acid (H3 BO3) wi~h the balance being water. The pH is maintained between 1.5 to 4.5 by adding more acid. The temperature of the ; bath is maintained between 45 and 65C during plating and a current densi-ty of 2.5 to 10 amps/dm2 is applied. When the article is in the form of a long hollow c~lindrical tube, the bath is flowed through the tube at S00-1200 ml./minute, and the anode is a solid rolled carbon-nickel cylindrical tube 0.125 to 0.200 inch in diameterO This procedure produces a very good as~
plated adherence with no porosity. In order to insure that the plated article can be used at eIevated -temperatures without any ; 20 substantial loss of adhe~sion, the same out-gassing procedure employed above fox copper plated article is used.
For electrolytically plating chromium on zirconium, a bath of the following composition is employed: 200 to 300 grams/liter of chromic oxide (CrO3)~ and 2 to 3 grams/liter of sulfuric acid (M2 SO4) with the balance being water The temperature of the bath is maintained between 30 and 50C during plating, and a current density of 10 to 20 amps/dm2 is applied. When the article is in the form of a long hbllow cylindrical tube, the bath is flowed through the tube at 800 to 1200 ml./minute, and the anode is a solid lead coated iron cylindrical t~e 0.125 to 0.200 inch in diame-ter. This procedure produces a very good as-plated ,:
~ 34 24NF-04~32 adherence with no porosity. In order to insure that the plated article can be used at elevated temperatures without any substantial loss of adhesion, the same out-gassing procedure employed above for copper plated article is used.
The articles treated by the process of this invention can be zirconium materials taken directly from milling operations or can - be articles su~jected to prior mechanical cleaning (e.g., grit blasting) or chemically cleaned articles (e.g., cleaned by acid and/or alkaline etching)~
Utilizing the foregoing method and the aqueous activating solution, it is possible to obtain a continuous deposit of the metal to be plated on the article of zirconium or a zirconium alloy with a minimu~ thickness of about 1~5 microns or greater.
For best results it is pre~erred to have a thickness of from about 3 to about 15 microns plated on the article, and it is possible to achieve even thicker coatings with the process of this invention. Articles plated by thé foregoing process protect the zirconium against most of the usual agents encountered at high temperatures including oxygen, air, water, steam and fission ~0 products produced in nuclear fueI eIements during nuclear Eission.
After the plating it is possible to subject the metal coatings on the article to various treatments including diffusion annaaling treatments or plating of a second metal.
The process of this invention produces plated articles having increased adhesion between the plated metal layer and the article.
The plated articles of this invention will pass an adhesion test ~merican Society of Testing Materials Standard B571-72) requiring the test specimen to be ~ent 180~ in repeated cycles until the specimen breaks. ~ollowing the fracture of the article, no 3Q separation of the plated metal layer is detected for the axticles plated according to the practice of this invention.
`
^~ ~
~ 3~ 2~NF-04232 The follo~ing non-limiting examples illustrate the results obtained in the practice of this invention for achieving coatings upon zirconium articles.
A hollow Zircaloy-2 cladding tube 4 meters in length, 10.7 mm. in inside diame-ter and 12.4 mm. in outside diameter was plated according to the following procedure. The tube had previously been etched in an acid solution of 50% by weight hydrofluoric acid and 50% by weight nitric acid, contacted with lQ an aqueous 50% by weight sodium hydroxide solution and then rinsed in water.
The tube was cleaned in lol~l trichlorethane, rinsed in deionized water and allowed to dry. The inside surface of the final 7.6+1.3 mm. at each end o the tube was coated with a vinyl lacquer.
Next an aged aqueous activating solution was pumped through the tube at the rate of 1000+200 ml./minute. The sQlution was comprised of 15 grams/liter of ammonium bifluoride, 0.5 ml./liter sulfuric acid and the balance was deionized water. The solution is aged by immersion of pickled zirconium in the solution for about 10 minutes. This pumping was continued for one minute.
The temperature of the solution was 21~2C throughout the time the solution was pumped through the tube.
The tube was rinsed by circulating room temperature deionized water through the tube for one minute at a flow rate of about 1000+200 ml./minute.
The loosely adhering film (smut) on the inside surface of -the tube was removed by immersing the tube in a water bath and apply-ing about 40,000+5000 cycles per second of ultrasonic energy to the tube for one minute while deionized water is circulated through the tube. The water leaving the tube was dar]c and as - lZ -~ 434 24NF~04232 time passes becomes lighter ln color until after one minute the water was substantially clean.
The ultrasonic energy was turned off and the tube was then further rinsed by circulating deionized water (at room temperature) through the tube for one minute at a flow rate of about 1000+
200 mlO/minute~
Next a solid cylindrical copper anode 0.125 inch in diameter was inserted into the tube and the tube was plated ~y pumping an electrolytic copper plating solution through the tube at the rate of 1000+200 ml./minute for twenty-five minutes under a current density of 20 amps/dm2. The solution was comprised of 200 grams/liter copper sulfate, 100 grams/liter sulfuric acid and 0,005 grams/liter thiourea with the balance water. The temperature of the' plating solution was maintained between 34 and 36C while being pumped through the tube. The tube was next purged with inert gas (nitrogen) for one minute at a flow rate of 3 cubic feet/minute.
The tube was then rinsed by circulating room temperature deionized water through the tube for five minutes at a flow ra-te of 1000+200 ml./minute.
The tube was air dried and the lacquer was removed from each'end with l.l.1 trichlorethane.
Examination of the tube showed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside surface of the Zircaloy tube,' excep-t for the ends masked with the lacquer . . . . .
'EXAMnLE 2 The'procedure of Example 1 is repeated on another Zircaloy~2 tube'of identical dimension~. Thé process is the' same except for a change in the step of removing the loosely adherin~ film on the tube after the activation step.
~ 434 24NF-04232 For this example, 6 cotton swabs ~ere pneumatically forced through the tube at the rate of about 100 meters/second. The first 5 swabs were observed to be disclosed, with each succeed-iny swab showing less discoloration and the sixth swab bein~
substantially free of any discoloration.
Examination of the tube after the~electrolytic plating step showed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside surface of the Zircaloy tube, except for the ends masked wlth the lacquer.
EXAMPLE ~3 The procedure of Example 2 is repeated replacing the cotton swabs with 6 organic swabs prepared by wrapping cylindrical rubber plugs with'a single layer of polyester to give a plug diameter of about 10 mm.
The first 5 swabs were'observed to be discolored with each succeeding swab'showing less discoloration, and the'sixth swab being substantially free of any discoloration.
Examination of the tube after the eIectroless plating step shbwed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside'surface of the Zircaloy tube, except for the ends masked with -the lacquer.
The procedure of Example 1 is repeated on another Zircaloy-2 tube of identical dimensions. Thé process is identical except for a change in the steps of removing the loosely adhering film on the tube after the activation step.
For this example'an aqueous solution comprised of a~out 10 ,-percent fluoboric acid by volume is pumped through the tube at the rate o~ 1000~20a ml./minute.' This was ~ontinued for about one minute and very effectiveIy removed the loosely adhering film from the tube~
` 24NF 04232 3~
Examination of the tube after the electrolytic plating step showed a copper layer of 10 microns in thickness was substantially uniformly plated in the inside surface of the Zircaloy tube, except for the ends masked with the lacquer.
The procedure of Example 1 is repeated on another Zircaloy-2 tube of identical dimensions. The process is identical except for a change in the step of removing the looseIy adhering film on the tube after the activation s-tep.
For this example an aqueous solution comprised of about 10 percent hydrofluosilicic acid by volume is pumped through the tube at the rate of 1000 200 ml./minute. This was continued for about one minute and very effectiveIy removed the loosely adhering film from the tube.
Examination of the tube after the electrolytic plating step showed a copper layer of lO microns in thickness ~as substantially uniformly plated on the inside surface of the Zircaloy tube, except for the ends masked with the lacquer.
As will be`apparent to those skilled in the art, various modifications and changes may be made in the invention described herein. It is accordingly the inte.ntion that the invention be construed in the broadest manner within the spirit and scope as set forth`in the accompanying claims.
,
~ ~ 24NF-04232 electrode of about 14 feet in length with about 0.125 inch in diameter is required for an electroplating process.
zirconium materials activated in an ammonium bifluoride-sulfuric acid solution have on the sur~ace a first layer of a black color that is highly adherent to the ~irconium s~s-trate and is electrically conductive. This layer is believed to make it possible to initiate electroplating of the zirconium material.
These activa-ted zirconium materials also have a second layer on the first layer that is a loosely adhering layer of similar color to the first layer. The presence of this second layer is believed to have an adverse effect on adhesion and to give rise to the possibility of blistering of the coating.
Therefore it is desirable to develop an electrolytic process for plating zirconium materials that includes a step oE removing the loosely adhering la~er on the zirconium material resulting from the activation of the zirconium material in the ammonium bifluoride-sulfuric acid solution.
Summary_of the Invention ~ It has now been discovered that an article comprised of zirconium or a zirconium alloy can be electrolytically plated with a metal layer of a metal seIected from the group consisting of copper, nickel and chromium to achieve improved adhesion between the metal layer and the article when the article is free of any loosely adhering films formed during an activation step.
The first step of this process is activating the article in an aged a~ueous activating solution comprised of from about 10 to about 20 grams per liter of ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid. The next step of the pro~ess is removing the loosely adhering film formed on the article in the activating step. The last step of the process is contacting the article ~ith an electrolytic plating solution ~¢~, ~ 3~ 24NF-Q4232 containing the metal therein to be deposited on the article in the presence of an electrode receiving current.
The removal of the loosely adhering film formed on -the article in the activation step can be done by chemical treatment, ultrasonic treatment or by swabbing the surface with cotton or an organic material. The chemical removal of the film is accom-plished by using (a) an aqueous solution comprising from about 2 to about 10 percent fluoboric acid and the balance waterr or (b) an aqueous solution comprising from about 2 to about 10 percent hydrofluosilicic acid and the balance water. The ultrasonic removal of the film is accomplished by immersing the article in water and applying ultrasonic energy to the article.
Obiects of'the Invention . . . _ It is an object of this invention to provide a process for the electrolytic plating of an article comprised of zirconium or a zirconium alloy, especially when the article is in the form of a nuclear fueI element cladding comprising a long hollow cylindrical tube of small diameter.
Another object of this invention is to provide a step for removing the loosely adhering film on an article comprised of zirconium or a æirconium alloy after being contacted in an activating solution and prior to being subjected to electrolytic plating.
Othér objects and advantages of this invention will become apparent to the person skilled in the art from the following description of the invention and from the appended claims.
... . . . . ..
Description of th'e I'nvention This inventlon comprises a process for the electrolytic deposition of a metal film on an article being comprised of zirconium or a zirconium alloy. Thé process broadly comprises a step of activating the article, a step of removing any loosely, ~4NF-04232 3~
adhering films formed on the article in the activation step and a step of contactlng the article with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current. The process can also include the optional steps of rinsing the article in water (preferably deionized wa-ter) after the activation step, the ~ilm removal step and the e:Lectrolytic plating step. The rinsing prevents carry-over on the surface of the article of the solution with which it was in contact so there is no formation of deposits or films on the article from this solution~ When the article is to be contacted with another solution, the rinsing also prevents introduction of impurities in that other solution.
~ detailed discussion of the process of this invention will now be presented as shown in the attached Figure. In the first step the article of ~irconium or a zirconium alloy is contacted with an aged aqueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride (preferably a starting amount of a~out 15 grams per liter ammonium bifluoride) and from a~out 0.75 to about 2.0 grams per liter o sulfurlc acid (prefera~Iy a starting amount of about 1.0 grams per liter).
The solution is aged by immersion of a piece of pickled zirconium for at least ahout lO minutes at ambient temperature. It has been found that solutions outside the foregoing ranges for the ammonium bifluoride component and the sulfuric acid component do not produce good adherent platings on the article.
The article is contacted wit~ the aged aqueous activating solution for about one minute at ambient temperature (approximately 20-30C)~ and the activating solution is stirred or otherwise agitated ~rior to contacting the article with the solution. The article is ready for immediate`wse in the following steps of : .
.
this process or can be stored for several days or longer before being used in the following steps of this process.
An optional step of rinsing the article in water can he practiced, preferably using deionized water, to free the article of any residual traces of the activating solution.
The next step is removing any loosely adhering film (i.e.
"smut") ~ormed on the article in the activating step. This step is performed by either contacting the article in a chemical solution ~hich removes the film from the article, using ultrasonic energy to remove the film, or swabbing the surface of the article with a cotton s~ab or an organic swab such as nylon or polyester. The organic swab can be ~rapped around a rubber plug and forced through the article when the article is a hollow tube and the wrapped plug is approximately the same size as the internal diameter of the tube~ This leaves the article with a dark adherent electrically conducting sur~ace ~ilm or layer of zirconium o~ide that can ~e plated with any of the known electrolytic metal plating solutions.
One chemical solution for contacting the article to remove the looseIy adhering film is comprised of from about 2 to about 10 percent fluo~oric acid by volume`in wa~er. Solutions belo~
about 2 percent by volume do not remove the loosely adhering film, and solutions above ahout 10 percent by volume start to attack the more adherent film underlying the loosely adhering film.
The solution is used at about 25+5C and the article is contacted in this solution for about one minute.
~nother chemical solution for contacting the article to remove the looseIy adhering film i5 comprised o~ from about 2 to about 10 pexcent hydro~luosilicic acid b~ volume in water.
Solutions beIow abou~ 2 percent ~ volume do not remove the loosely adhering ~il~, and solutions above~about 10 percent by volume - .
.
~ '4 34 24NF-04232 start to attack the more adherent film underlying the loosely adhering film. The solution is used at about 25~5C and the article is contacted in this solution for about one minu-te.
Removal of the loosely adhering film from the article can -' 5 also be accomp]ished by the use of ultrasonic rinsing in water, iOe., su~merging the article in water and applying ultrasonlc energy in the range of about 20,000 to'about 300,000 cycles per second (cps). This is continued ~or a time of about one to two minutes or more, or until visual observa-tion shows that no more film is being removed. Below about 20,000 cps, the rate of removal is too slow, and the equipment for running above 300,000 cps involves added expense. '-Swabbing the loosely adhering film from the article is done by uniformly rubbing the surface with'co-tton or paper or other absorbent material, or ~y brushing the surface with a brush con-taining natural hog bristles or nylon bristles. In one method ~' cotton swabs or organic swabs such as polyester and nylon swabs are rubbed over the surface of the article. When the article is in the~form of a tube the swab is driven through the tube by use of air pressure.
Next, after removal of the loosely adhering film, an optional step of rinsing the article in water can be practiced, preferably using deionized water, to free the article of any residual traces of the material used in removing the loosely adhering film. 'This step is desirahle when one of the chemical solutions has been used.
The article is contacted wi-th any of the kno~n electrolytic ' plating solutions containing the'metal to be deposited on the article upon contact with'the article in the presence of an ; 30 electrode'receiving current. Typically the article is submerged ~ in the'electrolytic plating solution adjacent the electrode with . . .
~ 43 ~ 24NF-04232 a gap between the article and the electrode of about 0.2 inch or more to enable uniform build up of the metal on the article.
Preferred met~ls to be deposited on the arkicle of zirconium or a zirconium alloy include copper, nickel and c'nromium, and an especially preferred metal to be deposited on the article is copper.
For electrolytically depositing copper, an aqueous bath of the following composition has been employed: 150 to 250 grams/
liter of copper sulfate ~CuS04 . 5 H20), 45 tollO grams/liter of sulfuric acid (~2 S04), and 0.002 to 0.005 grams/liter of thiourea (NH2 CS NH2) with the balance being water. The temperature of the bath is maintained between 32 and ~2C during plating, and a current density of 16 to 22 amps/decimeter2 (dm2) is applied. When the article is in the :orm of a long hollow cylindrical tube, the bath is flowed through the tube at 800 to 12Q0 ml./minute, and the anode is a solid oxygen-free high conductivity copper cylindrical tube 0.125 to 0.200 inch in diameter. This procedure produces a very good as-plated adherence with no porosity. In order -to insure that the plated article can be used at elevated temperatures without any substantial loss of adhesion, the plated zirconium is out-gassed at a temperature of about 300 to about 400F (149 to 204C~ Eor a time period of about three hours. In thi:s out-gassing the temperature is raised from ambient to the final temperature at a rate of abouk 50F to 125F per ~our.
During the plating of copper on the article, a considerable : quantity of hydxogen gas is evolved. The electrolytic copper plating solution is flowed slowly over the article, and this results in the hydrogen tending to adhere to the wall of the tube.
It is necessary to remove this hydrogen gas so that it does not develop back-pressure during plating (i.e.~ pressure on the .
~ _ g _ .,. ,. ~
,.~;~", surface of the article being plated that stops the plating~.
- The plating process is further facilitated when the surface of the article to be plated is positioned in a vertical position so -that evolved hydrogen is swept upward away from -the surface being plated.
For electrolytically plating nickel on zirconium, an aqueous bath of the following composition is emp:Loyed: 320 to 340 grams/
liter of nickel sulfate ~Ni SO4 6 H2O)l 40 to 50 grams/liter nickel chloride (Ni C12 6 H2O), 36 to 40 grams/liter of boric acid (H3 BO3) wi~h the balance being water. The pH is maintained between 1.5 to 4.5 by adding more acid. The temperature of the ; bath is maintained between 45 and 65C during plating and a current densi-ty of 2.5 to 10 amps/dm2 is applied. When the article is in the form of a long hollow c~lindrical tube, the bath is flowed through the tube at S00-1200 ml./minute, and the anode is a solid rolled carbon-nickel cylindrical tube 0.125 to 0.200 inch in diameterO This procedure produces a very good as~
plated adherence with no porosity. In order to insure that the plated article can be used at eIevated -temperatures without any ; 20 substantial loss of adhe~sion, the same out-gassing procedure employed above fox copper plated article is used.
For electrolytically plating chromium on zirconium, a bath of the following composition is employed: 200 to 300 grams/liter of chromic oxide (CrO3)~ and 2 to 3 grams/liter of sulfuric acid (M2 SO4) with the balance being water The temperature of the bath is maintained between 30 and 50C during plating, and a current density of 10 to 20 amps/dm2 is applied. When the article is in the form of a long hbllow cylindrical tube, the bath is flowed through the tube at 800 to 1200 ml./minute, and the anode is a solid lead coated iron cylindrical t~e 0.125 to 0.200 inch in diame-ter. This procedure produces a very good as-plated ,:
~ 34 24NF-04~32 adherence with no porosity. In order to insure that the plated article can be used at elevated temperatures without any substantial loss of adhesion, the same out-gassing procedure employed above for copper plated article is used.
The articles treated by the process of this invention can be zirconium materials taken directly from milling operations or can - be articles su~jected to prior mechanical cleaning (e.g., grit blasting) or chemically cleaned articles (e.g., cleaned by acid and/or alkaline etching)~
Utilizing the foregoing method and the aqueous activating solution, it is possible to obtain a continuous deposit of the metal to be plated on the article of zirconium or a zirconium alloy with a minimu~ thickness of about 1~5 microns or greater.
For best results it is pre~erred to have a thickness of from about 3 to about 15 microns plated on the article, and it is possible to achieve even thicker coatings with the process of this invention. Articles plated by thé foregoing process protect the zirconium against most of the usual agents encountered at high temperatures including oxygen, air, water, steam and fission ~0 products produced in nuclear fueI eIements during nuclear Eission.
After the plating it is possible to subject the metal coatings on the article to various treatments including diffusion annaaling treatments or plating of a second metal.
The process of this invention produces plated articles having increased adhesion between the plated metal layer and the article.
The plated articles of this invention will pass an adhesion test ~merican Society of Testing Materials Standard B571-72) requiring the test specimen to be ~ent 180~ in repeated cycles until the specimen breaks. ~ollowing the fracture of the article, no 3Q separation of the plated metal layer is detected for the axticles plated according to the practice of this invention.
`
^~ ~
~ 3~ 2~NF-04232 The follo~ing non-limiting examples illustrate the results obtained in the practice of this invention for achieving coatings upon zirconium articles.
A hollow Zircaloy-2 cladding tube 4 meters in length, 10.7 mm. in inside diame-ter and 12.4 mm. in outside diameter was plated according to the following procedure. The tube had previously been etched in an acid solution of 50% by weight hydrofluoric acid and 50% by weight nitric acid, contacted with lQ an aqueous 50% by weight sodium hydroxide solution and then rinsed in water.
The tube was cleaned in lol~l trichlorethane, rinsed in deionized water and allowed to dry. The inside surface of the final 7.6+1.3 mm. at each end o the tube was coated with a vinyl lacquer.
Next an aged aqueous activating solution was pumped through the tube at the rate of 1000+200 ml./minute. The sQlution was comprised of 15 grams/liter of ammonium bifluoride, 0.5 ml./liter sulfuric acid and the balance was deionized water. The solution is aged by immersion of pickled zirconium in the solution for about 10 minutes. This pumping was continued for one minute.
The temperature of the solution was 21~2C throughout the time the solution was pumped through the tube.
The tube was rinsed by circulating room temperature deionized water through the tube for one minute at a flow rate of about 1000+200 ml./minute.
The loosely adhering film (smut) on the inside surface of -the tube was removed by immersing the tube in a water bath and apply-ing about 40,000+5000 cycles per second of ultrasonic energy to the tube for one minute while deionized water is circulated through the tube. The water leaving the tube was dar]c and as - lZ -~ 434 24NF~04232 time passes becomes lighter ln color until after one minute the water was substantially clean.
The ultrasonic energy was turned off and the tube was then further rinsed by circulating deionized water (at room temperature) through the tube for one minute at a flow rate of about 1000+
200 mlO/minute~
Next a solid cylindrical copper anode 0.125 inch in diameter was inserted into the tube and the tube was plated ~y pumping an electrolytic copper plating solution through the tube at the rate of 1000+200 ml./minute for twenty-five minutes under a current density of 20 amps/dm2. The solution was comprised of 200 grams/liter copper sulfate, 100 grams/liter sulfuric acid and 0,005 grams/liter thiourea with the balance water. The temperature of the' plating solution was maintained between 34 and 36C while being pumped through the tube. The tube was next purged with inert gas (nitrogen) for one minute at a flow rate of 3 cubic feet/minute.
The tube was then rinsed by circulating room temperature deionized water through the tube for five minutes at a flow ra-te of 1000+200 ml./minute.
The tube was air dried and the lacquer was removed from each'end with l.l.1 trichlorethane.
Examination of the tube showed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside surface of the Zircaloy tube,' excep-t for the ends masked with the lacquer . . . . .
'EXAMnLE 2 The'procedure of Example 1 is repeated on another Zircaloy~2 tube'of identical dimension~. Thé process is the' same except for a change in the step of removing the loosely adherin~ film on the tube after the activation step.
~ 434 24NF-04232 For this example, 6 cotton swabs ~ere pneumatically forced through the tube at the rate of about 100 meters/second. The first 5 swabs were observed to be disclosed, with each succeed-iny swab showing less discoloration and the sixth swab bein~
substantially free of any discoloration.
Examination of the tube after the~electrolytic plating step showed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside surface of the Zircaloy tube, except for the ends masked wlth the lacquer.
EXAMPLE ~3 The procedure of Example 2 is repeated replacing the cotton swabs with 6 organic swabs prepared by wrapping cylindrical rubber plugs with'a single layer of polyester to give a plug diameter of about 10 mm.
The first 5 swabs were'observed to be discolored with each succeeding swab'showing less discoloration, and the'sixth swab being substantially free of any discoloration.
Examination of the tube after the eIectroless plating step shbwed a copper layer of 10 microns in thickness was substantially uniformly plated on the inside'surface of the Zircaloy tube, except for the ends masked with -the lacquer.
The procedure of Example 1 is repeated on another Zircaloy-2 tube of identical dimensions. Thé process is identical except for a change in the steps of removing the loosely adhering film on the tube after the activation step.
For this example'an aqueous solution comprised of a~out 10 ,-percent fluoboric acid by volume is pumped through the tube at the rate o~ 1000~20a ml./minute.' This was ~ontinued for about one minute and very effectiveIy removed the loosely adhering film from the tube~
` 24NF 04232 3~
Examination of the tube after the electrolytic plating step showed a copper layer of 10 microns in thickness was substantially uniformly plated in the inside surface of the Zircaloy tube, except for the ends masked with the lacquer.
The procedure of Example 1 is repeated on another Zircaloy-2 tube of identical dimensions. The process is identical except for a change in the step of removing the looseIy adhering film on the tube after the activation s-tep.
For this example an aqueous solution comprised of about 10 percent hydrofluosilicic acid by volume is pumped through the tube at the rate of 1000 200 ml./minute. This was continued for about one minute and very effectiveIy removed the loosely adhering film from the tube.
Examination of the tube after the electrolytic plating step showed a copper layer of lO microns in thickness ~as substantially uniformly plated on the inside surface of the Zircaloy tube, except for the ends masked with the lacquer.
As will be`apparent to those skilled in the art, various modifications and changes may be made in the invention described herein. It is accordingly the inte.ntion that the invention be construed in the broadest manner within the spirit and scope as set forth`in the accompanying claims.
,
Claims (9)
1. A process for the electrolytic deposition of a metal film on an article comprised of zirconium or a zirconium alloy comprising the steps of:
(a) activating the article in an aqueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid, the solution having been aged by immersion of pickled zirconium in said solution for about 10 minutes, (b) removing any loosely adhering film formed on the article in the activating step, and (c) contacting the article with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current.
(a) activating the article in an aqueous activating solution comprising from about 10 to about 20 grams per liter of ammonium bifluoride and from about 0.75 to about 2 grams per liter of sulfuric acid, the solution having been aged by immersion of pickled zirconium in said solution for about 10 minutes, (b) removing any loosely adhering film formed on the article in the activating step, and (c) contacting the article with an electrolytic plating solution containing the metal to be deposited on the article in the presence of an electrode receiving current.
2. A process according to claim 1 in which the article is rinsed in water after each step.
3. A process according to claim 2 in which the water is deionized.
4. A process according to claim 1 in which the step of removing the loosely adhering film comprises immersing the article in water and applying ultrasonic energy on the immersed article.
5. A process according to claim 1 in which the steps of removing the loosely adhering film comprises contacting the article with an aqueous solution comprising from about 2 to about 10 percent fluoboric acid by volume.
6. A process according to claim 1 in which the step of removing the loosely adhering film comprises contacting the article with an aqueous solution comprising from about 2 to about 10 percent hydrofluosilicic acid by volume.
7. A process according to claim 1 in which the step of removing the loosely adhering film comprises contacting the article with a swab.
8. A process according to claim 7 in which the swab is comprised of an organic material selected from the group comprising polyester, nylon and cotton, individually or in combination, wrapped on a rubber plug.
9. A process according to claim 1 in which the article is in the form of a long hollow cylindrical tube of Zircaloy.