CA1070985A - Electrochemically active aluminum alloy - Google Patents
Electrochemically active aluminum alloyInfo
- Publication number
- CA1070985A CA1070985A CA240,922A CA240922A CA1070985A CA 1070985 A CA1070985 A CA 1070985A CA 240922 A CA240922 A CA 240922A CA 1070985 A CA1070985 A CA 1070985A
- Authority
- CA
- Canada
- Prior art keywords
- thallium
- alloy
- parts
- aluminium
- gallium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
ABSTRACT OF THE DISCLOSURE
Electrochemically active alloys of aluminum with at least one of indium, gallium and thallium contain, for each 100 parts of aluminum at least 0.01 parts (W/W) of thallium and from 0.01 to 0.5 parts (W/W) of indium, gallium and thallium together where more than one of these elements is present, or from 0.01 to 0.5 parts (W/W) of thallium where it alone is present, and are useful for protecting corrodible materials against corrosion.
Electrochemically active alloys of aluminum with at least one of indium, gallium and thallium contain, for each 100 parts of aluminum at least 0.01 parts (W/W) of thallium and from 0.01 to 0.5 parts (W/W) of indium, gallium and thallium together where more than one of these elements is present, or from 0.01 to 0.5 parts (W/W) of thallium where it alone is present, and are useful for protecting corrodible materials against corrosion.
Description
~ ~7 ~ ~ ~ S
This invention relates to al~inium alloys.
The electrodes for batteries are usually made of zinc.
However, due to the high price of zinc it has been necessary to - try and discover a material which has the same properties as zinc, or even better, but which is cheaper.
Aluminium dipped in an electrolytic solution represents in principle a useful system for practical application as an electrode for batteries or for protection against corrosion. It has a high negative theoretical equilibrium potential and a high ampere-hour capacity since each atom exchanges 3 electrons in the process of ionisation. In practice, however, pure aluminium metal cannot be used, since, due to the formation of a protective oxide layer, the open-circuit potential spontaneously establishes itself at a far more positive value than the theoretical one.
If the potential is made more positive than the open-circuit potential in order tv dissolve aluminium anodically, passivisation of the aluminium surface very soon occurs and the process of ~` dissolving stops. Besides, contrary to expectations, hydrogen `' evolution with the corresponding self-corrosion of aluminium is enhanced at more positive potentiaLs (the so-called "negative differential effect").
We set ourselves the task of making a material based on aluminium which would remain active for anodic dissolution up to ~ high anodic current densities and under a wider span of ., ,,~ ~
` A ~ ~
.~............. . . ... . .
, ,~ . . . . .
.
. ~ .
~
.. . . . . . ..
.~- .
potentials and at the same time become more corroslon resistant and have a small negative differential effect. Such a material was obtained by alloying aluminlum with small amounts of thallium, optionally together with indium and gallium.
According to one aspect of the present invention there is provided an alloy consisting of aluminium with thallium, containing, for each 100 parts of aluminium, at least 0.01 parts (W/W~ of thallium and 0.01 to 0.5 parts (W/W) of indium, gallium and thallium together, to form a quaternary alloy, the ratios between indium, gallium and thallium being arbitrary.
According to a further aspect of the present invention there is provided a method for obtaining the above-described alloy wherein the chosen mix~ure of elements is heated in an inert atmosphere until the elements melt, the mixture is homogenized and then cooled. The above-described method may comprisa the further steps of heating the cooled alloy to 300 to 400C for 1 to 4 hours and then cooling it slowly to ambient temperature.
It has been shown experimentally that such a material satisfied the above requirements, i.e.
a~ such alloys establish a relatively negative open-circuit potential in alkali chloride solutions;
~ .
, . .
.. . . .
: ~' : , .
~7~
b) the corroslon rate of these alloys, when immersed in such solutions, is relatively low;
c) at more positive potential than the open-circuit one, the alloys dissolve anodically up to relatively very high current densities without passivisation and with low anodic over potentials (small losses of voltage);
d) the self-corrosion current (i.e. hydrogen evolution) increases only slightlyl so that, at current densities higher than 100 mA/cm2 the aluminium remains active for anodic dissolution.
It is rather surprising to find that such a material has such gualities and hence can be used successfully as a substitute for the materials used so Ear (e.g.zinc)~where good electro-chemical activity is needed, such as in the negative electrodes of primary batteries or batteries with changeable plates. It appears, also, that the said alloys can be successfully used as protectors ; against the corrosion of different structures (e.g. ships and cars).
This material is many times cheaper than the material used so far.
The following Examples illustrate the present invention.
An aluminium - thallium alloy was prepared so that for each 100 parts (by weight) of aluminium, 0.05 parts of thallium wer~ added. The mixture was heated in an inert atmosphere until both metals melted after whi~h it was homogenized and cooled.
~; The solid material obtained can be used as an electrode. Such : I
~4-", ~ .
. . . .
: , - :
. ~.. . . . .
i .
' :,' ' ' ' ` ' ' ~ ' ; ~
, ~ .
:
37~g~
an electrode. Such an electrocle was tested in a solution of NaCl. The measured open-circuit potential was -1.400 V when measured in relation to a saturated calomel electrode (SCE).
The measured corrosion rate at this at this potential was found to be negligible.
The anodic polarization curve for this alloy was detenmined and it was found that anodic current densities up to 100 mA/cm2 are obtained with low overpotentials (smaller lOOmV) and that the passivisation current density is larger than 0.5 A/cm2.
The alloy in Example 1 was used for the corrosion protection of a piece of steel dipped in a sodium chloride solution. It was found that with a current of only 0.38 mA
; ~etween the protector made of this alloy and the steelj the piece of steel o~tained the negative potential of -0.6 V, sufficient for good corrosion protection, while with zinc as the protector for the same piece of steel, a ourrent of 0.55mA was . ...................................... .
`~ necessary to achieve the same protection. In the latter case more material would be required for the same protective action.
Aluminium alloys with indium, gallium and thallium were prepared so that 100 parts of aluminium were mixed with 0.01 to 0.5 - weight parts of the said metals and were used to make cans of the Leclanche dry cell as prepared by the normal industrial .; ~
,~.
: . :, . .
, ~ . .: .
,~ , . . . .
.: :, . ~ . .
~ 35 method. The properties o~ such cells were compared with the same type of conventional commercial cells with the can made of zinc. The results obtained were somewhat better when the can was made of the aluminium alloys.
The alloy prepared as described in Example 1 after homogeni~ation and cooling was heated again to 300 to 400C
and kept at this temperature for 1 to 4 hours, and then slowly cooled. The alloy treated in this way showed even better properties; somewhat more negative open circuit potential and considerably small negative differential effect.
:
' ~ --6 :. ~
This invention relates to al~inium alloys.
The electrodes for batteries are usually made of zinc.
However, due to the high price of zinc it has been necessary to - try and discover a material which has the same properties as zinc, or even better, but which is cheaper.
Aluminium dipped in an electrolytic solution represents in principle a useful system for practical application as an electrode for batteries or for protection against corrosion. It has a high negative theoretical equilibrium potential and a high ampere-hour capacity since each atom exchanges 3 electrons in the process of ionisation. In practice, however, pure aluminium metal cannot be used, since, due to the formation of a protective oxide layer, the open-circuit potential spontaneously establishes itself at a far more positive value than the theoretical one.
If the potential is made more positive than the open-circuit potential in order tv dissolve aluminium anodically, passivisation of the aluminium surface very soon occurs and the process of ~` dissolving stops. Besides, contrary to expectations, hydrogen `' evolution with the corresponding self-corrosion of aluminium is enhanced at more positive potentiaLs (the so-called "negative differential effect").
We set ourselves the task of making a material based on aluminium which would remain active for anodic dissolution up to ~ high anodic current densities and under a wider span of ., ,,~ ~
` A ~ ~
.~............. . . ... . .
, ,~ . . . . .
.
. ~ .
~
.. . . . . . ..
.~- .
potentials and at the same time become more corroslon resistant and have a small negative differential effect. Such a material was obtained by alloying aluminlum with small amounts of thallium, optionally together with indium and gallium.
According to one aspect of the present invention there is provided an alloy consisting of aluminium with thallium, containing, for each 100 parts of aluminium, at least 0.01 parts (W/W~ of thallium and 0.01 to 0.5 parts (W/W) of indium, gallium and thallium together, to form a quaternary alloy, the ratios between indium, gallium and thallium being arbitrary.
According to a further aspect of the present invention there is provided a method for obtaining the above-described alloy wherein the chosen mix~ure of elements is heated in an inert atmosphere until the elements melt, the mixture is homogenized and then cooled. The above-described method may comprisa the further steps of heating the cooled alloy to 300 to 400C for 1 to 4 hours and then cooling it slowly to ambient temperature.
It has been shown experimentally that such a material satisfied the above requirements, i.e.
a~ such alloys establish a relatively negative open-circuit potential in alkali chloride solutions;
~ .
, . .
.. . . .
: ~' : , .
~7~
b) the corroslon rate of these alloys, when immersed in such solutions, is relatively low;
c) at more positive potential than the open-circuit one, the alloys dissolve anodically up to relatively very high current densities without passivisation and with low anodic over potentials (small losses of voltage);
d) the self-corrosion current (i.e. hydrogen evolution) increases only slightlyl so that, at current densities higher than 100 mA/cm2 the aluminium remains active for anodic dissolution.
It is rather surprising to find that such a material has such gualities and hence can be used successfully as a substitute for the materials used so Ear (e.g.zinc)~where good electro-chemical activity is needed, such as in the negative electrodes of primary batteries or batteries with changeable plates. It appears, also, that the said alloys can be successfully used as protectors ; against the corrosion of different structures (e.g. ships and cars).
This material is many times cheaper than the material used so far.
The following Examples illustrate the present invention.
An aluminium - thallium alloy was prepared so that for each 100 parts (by weight) of aluminium, 0.05 parts of thallium wer~ added. The mixture was heated in an inert atmosphere until both metals melted after whi~h it was homogenized and cooled.
~; The solid material obtained can be used as an electrode. Such : I
~4-", ~ .
. . . .
: , - :
. ~.. . . . .
i .
' :,' ' ' ' ` ' ' ~ ' ; ~
, ~ .
:
37~g~
an electrode. Such an electrocle was tested in a solution of NaCl. The measured open-circuit potential was -1.400 V when measured in relation to a saturated calomel electrode (SCE).
The measured corrosion rate at this at this potential was found to be negligible.
The anodic polarization curve for this alloy was detenmined and it was found that anodic current densities up to 100 mA/cm2 are obtained with low overpotentials (smaller lOOmV) and that the passivisation current density is larger than 0.5 A/cm2.
The alloy in Example 1 was used for the corrosion protection of a piece of steel dipped in a sodium chloride solution. It was found that with a current of only 0.38 mA
; ~etween the protector made of this alloy and the steelj the piece of steel o~tained the negative potential of -0.6 V, sufficient for good corrosion protection, while with zinc as the protector for the same piece of steel, a ourrent of 0.55mA was . ...................................... .
`~ necessary to achieve the same protection. In the latter case more material would be required for the same protective action.
Aluminium alloys with indium, gallium and thallium were prepared so that 100 parts of aluminium were mixed with 0.01 to 0.5 - weight parts of the said metals and were used to make cans of the Leclanche dry cell as prepared by the normal industrial .; ~
,~.
: . :, . .
, ~ . .: .
,~ , . . . .
.: :, . ~ . .
~ 35 method. The properties o~ such cells were compared with the same type of conventional commercial cells with the can made of zinc. The results obtained were somewhat better when the can was made of the aluminium alloys.
The alloy prepared as described in Example 1 after homogeni~ation and cooling was heated again to 300 to 400C
and kept at this temperature for 1 to 4 hours, and then slowly cooled. The alloy treated in this way showed even better properties; somewhat more negative open circuit potential and considerably small negative differential effect.
:
' ~ --6 :. ~
Claims (5)
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. An alloy consisting of aluminium with thallium, containing, for each 100 parts of aluminium, at least 0.01 parts (W/W) of thallium and 0.01 to 0.5 parts (W/W) of indium, gallium and thallium together, to form a quaternary alloy, the ratios between indium, gallium and thallium being arbitrary.
2. An electrode comprising an alloy as claimed in claim 1
3. A material protected against corrosion by being electrically connected to an electrode as claimed in claim 2.
4. A method of obtaining an alloy as claimed in claim 1, wherein the chosen mixture of elements is heated in an inert atmosphere until the elements melt, the mixture is homogenized and then cooled.
5. A method as claimed in claim 4 comprising the further steps of heating the cooled alloy to 300 to 400°C for 1 to 4 hours and then cooling it slowly to ambient temperature.