CA1067260A - Apparatus for forming closure liners - Google Patents

Abstract

ABSTRACT OF THE DISCLOSURE
An apparatus for moulding plastic liners or gaskets in container closures consisting of a two stage apparatus for deforming a pellet of the plastic material. The first stage comprises a heated deforming member which is adapted to heat the plastic material by direct conduction and to partially deform it. In the second stage a relatively cool final moulding die effects further deformation to impart the desired finished configuration to the gasket. The pressure member, and possibly also a workpiece support on which the upturned closure rests, is heated by means of a radiant heat source directing radiant heat onto a blackened roughened surface of the pressure member, and the workpiece support where applicable. The pressure member has a low-adhesive surface of polytetrafluoroethylene.

Description

1067;~60 The present invention relates to a method of and apparatus for moulding thermoplastic compositions. In a preferred form, the invention relates to the moulding of liners or gaskets in container closures.
Hitherto it has been known for example when forming a liner for a container closure to pre-heat the thermoplastic material and to mould the heated and thus softened material using a mould die which is not itself heated and may even be positively cooled so that in either case it presents a relatively cool moulding surface. However, the above described moulding process involves a considerable dwell time of the thermoplastic material in an oven, through which closures carrying metered quantities of the plastics material, are passed along a tortuous conveyor path. Such a system is for example~ disclosed in our United States Patent 3,963,396, Keith Shotbolt, June 15, 1976 in which the heat is imparted to the thermoplastic material by radiation within the oven. This has the disadvantage that, if for any reason the movement of the closure-carrying conveyor through the oven stops, the closures in the oven rapidly become overheated and "scorched" with the result that they are unsuitable for use.
In accordance with the present invention there is provided'an .,e apparatus for applying a moulded surface covering of a thermoplastic material to a workpiece comprising means for supporting the workpiece, means for feed-ing a thermoplastic material into contact with the workpiece, means for heat-ing the thermoplastic material, and means for deforming the heated thermo-plastic material, the improvement wherein the means for heating and deforming the thermoplastic material comprise pressure member means for partially deforming the thermoplastic material, means for imparting heat to said pressure member means for maintaining the pressure member means at an elevated temperature to ensure heating of the plastics material during said partial deformation, moulding die means for further deforming said partially deformed thermoplastic material, temperature control means for maintair ng the temper-atures ~f said moulding die means and said pressure member means at separate values with the moulding die cooler than the pressure member means, and means for driving said pressure member means and said moulding die means towards 067~60 and awa~ from said workpiece support means for deforming the thermoplastic material.
The present invention provides a method of moulding thermoplastic material comprising the steps of heating a quantity of the material by con-tact with a heated pressure member which both heats the thermoplastic material and deforms the material into a partially moulded configuration and subse-quently deforming the material into a desired finished configuration, using a moulding member shaped to impart the desired finished configuration to the thermoplastic material but maintained at a temperature less than that of the heated - la -1~672~0 and partially deformed thermoplastic material. The die is thus desirably not heated at all or is positively cooled.
In order to ensure that the thermoplastic material does not stick to the heating member that surface of the pressure member which in use con-tacts the thermoplastic material may be coated with a medium imparting low-adhesion characteristics. Preferably the coating may comprise polytetra-fluoroethylene (P.T.F.E.). More preferably, the particular P.T.F.E. coating employed may be in accordance with the *"ARMOURCO~E" system in which the surface of the pressure member is first of all given a sintered stainless steel layer, onto which the subsequently applied P.T.F.E. can more securely be keyed.
By exerting pressure on the pellet or spot while heating it, the thickness of the thermoplastic material is reduced and the area is increased.
Thus the rate of transfer of heat is increased markedly. For example, if the diameter of a pellet is doubled the heat transfer is increased by 16 times.
The invention also provides apparatus for applying a moulded sur-face covering of a thermoplastic m~terial to a workpiece comprising mePns for supporting the workpiece, means for placing a thermoplastic material into contact with the workpiece, a heated pressure member for partially deforming the thermoplastic material and imparting heat thereto, a moulding die drive-able towards and away from the workpiece for further deforming said partially deformed thermoplastic material, and temperature control means for maintain-ing the temperatures of said moulding die and said pressure member at sepa-rate values with the moulding die cooler than the pressure member.
The invention further provides a container closure having a sealing gasket moulded therein by the above method or use o~ the above apparatus.
Preferably, the pressure member is given a low-adhesion surface such as P.T.F.E.
Desirably the apparatus may include a rotary turret incorporating a plurality of workpiece supports and a plurality of separate pressure members, all associated with a common radiant heat source and arranged ona *Trademark - 2 -106 ~ Z60 circular arcuate path around the axis of rotation of the turret. The work-piece can be supported on a respective one of the workpiece supports and the associated pressure members will be driven down into contact with thermo-plastic material on the workpiece to impart heat thereto while causing initial deformation of the thermoplastic material.
Advantageously, means may be provided for heating the workpiece supports, so that the workpiecesthemselves are heated thereby.
Conveniently the means for heating the pressure member and/or the workpiece support may comprise a source of radiant heat located ad~acent the pressure member. Advantageously, the pressure member includes a blackened surface disposed directly opposite the radiant heat source which, in a pre-ferred form, may be an infra-red electrical heating element which can be caused to glow when energised.
Other alternative forms of heating the pressure member and/or the workpiece supports may be employed. For example the heat may be imparted by direct conduction from electrical cartridge heaters, or by playing a gas flame on the heating member and/or the support.
A stripper member may be located above the workpiece path to hold down the workpiece as the pressure member is withdrawn after hot pressing the plastics material. Where the workpieces are container closures the stripper member is a plate with a slot extending peripherally of the turret to receive the pressure member, in this case a plunger which may have flats formed to enter the slot while the hot pressing operation is carried out by a moulding head below the stripper plate which may or may not have similar flats, as desired.
The heating turret may include separate temperature sensors for detecting the temperatures of the workpiece supports and the temperatures of the pressure members and a separate control system may desirably be provided for controlling the temperature of the supports and the pressure members to maintain optimum heat transfer conditions.
This heating turret may be fed from an insertion device, such as a further turret of the form disclosed in our United States Patent 3,963,396, ~06~i~6~) Keith Shotbolt, June 15, 1976, and the heating turret may be arranged to deliver the workpiece with partly deformed plastics material directly to a further moulding turret.
~ he workpieces may suitably be preheated before insertion of the plastics material by means of a rotary preheating turret in which the work-pieces rest on hot supports. The hot supports may be heated by electrical cartridge heaters, gas flames or the like. Advantageously the supports may be heated by means of conduction from a hot receptor arranged to receive heat from a stationary radiant source such as an infra-red heating element.
By avoiding the conventional convective or direct radiation heating of the plastics material, it is possible to impart to the plastics material the desired softness together with an advantageous pre-shaping in a time which, when moulding liners or gaskets in container closures, can be reduced from the order of 25-40 seconds down to the order of 2.5 seconds. In the event of shut down of the machine while the heating turret is loaded, very few if any closures will be rendered unusable, because they are not sub~ected to intense heat.
Similarly the use of direct conduction for preheating the empty workpieces means that heat can be transferred quickly into the workpiece from a large capacity heat-transmitting conductor member without the need for fierce radiation directly onto the workpiece surface since this radiation tends to mar some lacquers used on container closures.
The main heating turret used in the preferred embodiment of appa-ratus according to the invention is far more compact than the previously used ovens.
In order that the present invention may more readily be understood the following description is given, merely by way of example, reference being made to the accompanying drawings in which:-Figure 1 is a schematic top plan view of apparatus for lining con-tainer closures in accordance with the present invention;
Figure 2 is a vertical sectional view through one of the positionson the heating/pressing turret;

67~60 Figure 3 is a horizontal section on the line III-III of Figure 2, and Figure 4 is a view similar to Figure 2 but showing an alternative form of heating/pressing turret;
Figure 5 is a plan view of the stripping plate shown in Figure 4, Figure 6a and 6b are a side elevational, partly sectional and an end elevational view, respectively, of the plunger bottom pad shown in Figure 4.
Referring now to Figure 1, the closures to be lined are advanced along a schematically illustrated chute conveyor generally designated 1, to a feed star wheel 2 from which the stream of empty closures is fed to a pre-heating turret 3 to be preheated by direct conduction of heat from a closure support. The closures passing around the turret 3 are heated to a temperature sufficient to cause subsequently inserted pellets of thermoplastic material to adhere securely to the inner face of the closure for subsequent operations.
From the preheater turret 3 the closures pass around a first trans-fer star wheel 4 and are fed to a pellet insertion turret 5, preferably of the form disclosed in our United States Patent 3,963,396, Keith Shotbolt, June 15, 1976.
The star wheel 4 has a plurality of pockets which advance the closures while the disc-like end walls of the closures ride on a smooth guide rail which has a small contact area with the closures so as to mini-mize heat loss from the already preheated closures and to avoid scratching the decorative lacquer which will already have been applied to the outer surface of the closure.
Individual pellets of thermoplastic material are introduced to respective ones of the preheated closuresby turret 5 before the closures are transferred by means of a similar secondary transfer star wheel 6 onto a turret 7 to be heated and initially deformed, as will be described in more detail below. From the heating turret 7 the closures, which now have a soft flattened plastics disc therein, are transferred, via a third similar type of transfer star wheel 8, to a moulding turret 9 where mould dies 1(~67~60 considerably cooler than both the thermoplastic material and the heated deforming members of turret 7 impart the final desired shape to the thermo-plastic material, before the closures then advance to an inspection station along the same or a different conveyor as shown at 10.
Figure 2 shows one station 11 on the heater turret 7 comprising a vertically movable pressure member or heating plunger 12 having an upper part 12a of an asbestos impregnated phenolic resin known by the Trade Name *Ferobestos. At the top end of the upper part 12a is the cam follower roller 25 mounted in a bifurcated carrier 26 which is spring urged upwardly by a helical compression spring 27 into contact with a circumferential cam 16. A
heat-absorption member 13 on the plunger 12 has an arcuate surface 14 arranged on a circular arc about the centre of a thermostatically controlled heating element 15 which itself extends around the circumference of the main turret.
i The circumferential cam 16 at the top of the machine provides the means for causing periodic raising and lowering of each plunger 12 relative to a container closure resting on a support member 17, so that a removable bottom pad 18 of the plunger enters the closure to compress the pellet of a thermoplastic material, in this case a composition consisting of polyethylene and butyl rubber as disclosed in British Patents Nos. 1112023, 1112024 and 1112025. Amongst many other suitable materials is polyvinyl chloride. Also suitable are the mixtures of polyethylene and styrene butadiene as disclosed in British Patents Nos. 1196125 and 1196127.
This action imparts heat to the pellet allowing it to soften and at the same time to spread due to the downward compression of the plunger. By the end of the heating and compression operation the entire body of the plastics material is soft and ready for a subsequent moulding operation using a relatively cold mould at the moulding turret 9.
The arcuate surface 14 of the heat receiving member 13 is both blackened and roughened so as to improve its heat-absorption characteristics with respect to radiant heat, and a reflector 19, extending around the cir-cumference of the turret, throws back radiant heat against the surface 14.

The heat picked up by the surface 14 is then conducted through the heat *Trademark - 6 -1(~67260 absorption me~ber 13 to the plunger 12 so as to maintain the bottom surface 18 at a temperature of approximately 200C to impart the necessary heat to the plastics material.
The closure-supporting member 17 is provided with a similar heat-absorbing member 20 mounted close to a second separately thermostatically controlled heating element 21 and a second reflector 22 so that the under-side of the closure is also heated to assist in transferring heat to the pellet.
The entire turret is driven for rotation in synchronism with the remainder of the apparatus.
As shown in the top plan view of Figure 3, the various heat absorb-ing members for the closure support members and the plungers are angularly spaced from one another to avoid any problems of circumferential expansion in the range of temperature encountered between room temperature and the operating temperature of around 200C.
Compressing the pellet as it is heated ensures that there is improved contact area between the plastics material and the heated surface of the plunger and the surface 18 is coated with the "*Armourcote" technique using sintered stainless steel as a keying surface for P.T.F.E. The portion of the plunger 12 carrying the P.T.F.E. may be detachable, so that it can be replaced should the P.T.F.E. become worn The heating system of the preheater turret 3 is similar to that of the main heating/pressing turret 7 in that the closure supports are heated from below by radiation from a thermostatically controlled heating element with a reflector to throw back the radiant heat towards a blackened heat-receiving surface of the closure support.
A stripping plate (not shown) is provided ~ust above the work-piece path around the turret 7 at the position where the plungers are with-drawn from the closures, this stripping plate having an arcuate slot through which the plunger extends slidably. As the plungers are withdrawn upwardly the rims of the closure skirts will strike the underside of the stripper plate to hold the closures down to effect separation of the plungers from *Trademark _ 7 _ ~067Z60 the heated plastics material.
Figure 4 shows a vertical section~l view similar to that of Figure

2, but depicts a modified form of the heating plunger construction for use on the main heating/pressing turret 7.
Since many of the components Or the turret of Figure 4 are iden-tical to those of Figure 2, the same reference numerals have, in many cases been employed. Where the reference numerals in Figure 4 have been primed, they denote modified elements which may be analogous to the corresponding elements of Figure 2.
The plunger 12' in this embodiment of the turret co-operates with a slotted stripping plate 28 which extends horizontally above the path of the closure support members 20 at the part of the heating/pressing turret where the plunger 12' is to rise away from the partially moulded plastics composition in the container closure 30.
The stripping plate 28 acts in the same manner as the non-illustrated stripper plate of Figure 2 to hold down the closure 30 since the rim 31 of the skirt of the closure will rise to strike the underside of the stripping plate 28 as the plunger is withdrawn and further withdrawal of the plunger 12' will raise the bottom pad 18' away from the heated and partially formed plastics composition in the bottom of the closure since the adhesion of the plastics composition to the bottom of the closure is stronger than its adhesion to the bottom pad 18', by virtue of the coating of polytetrafluoroethylene on the underside of the pad 18'.
In order to allow this co-operation between the stripper plate 28 and the plunger 12', the plunger and the bottom pad both have flats 29 formed in their lateral surfaces and these flats leave the plunger 12', 18' with a transverse dimension which is considerably less than the diameter parallel to the flats. These flats allow the plunger to be withdrawn upwardly into the slot of the stripper plate so as to release the closure for radially outward removal from the press/heating turret 7 at the third transfer star wheel 8 for advancing to the moulding turret 9.
After this stripping action has been completed, the plunger 12' 1~167Z60 will continue its travel around the turret 7 and will rise out of the end of the slot 43 in the stripper plate 28 after the closure 30 has been separated from the heating pad 18'.
This flatted circular form of pad 18' is particularly advantageous where, as illustrated in Figure 4, the closures 30 are of the deep drawn type without a beaded rim to the skirt, since the transverse dimension of the stripper plate slot will be as small as possible so that the delicate closure rim bears against the stripper plate over as great as possible a part of its periphery thereby distributing the end loading on the skirt rim more evenly.
As illustrated in Figures 6a and 6b, the mounting system for the bottom pad 18' involves a stud 32 of unthreaded form on the pad, but having at some point along its length a peripheral groove 33 whose lower wall is defined by a radially extending planar face and whose upper wall is of up-wardly divergent conical form when in situ. A grub screw 34 extends radially inwardly of the plunger 12', as shown in Figure 4, and a similar screw ex-tends inwardly from a diametrically opposite position so that these two screws both abut the upwardly divergent conical wall of the groove to pull the stem 32 upwardly as the two grub screws 34 are tightened. In this way, a secure clamping action can be exerted on the bottom plate 18' independently of the particular orientation of the pad 18' about the vertical axis.
Although not shown in detail in Figure 2, the bottom pad 18 is circular and has a threaded stem which is screwed into a threaded socket in the bottom end of the plunger 12 Such an arrangement requires a widening at the downstream end of the stripper plate slot to accommodate the circular plunger. The initial separating action of the plunger and closure occurs at a narrower upstream portion of the slot where flats in the plunger body allow the plunger body to pass along the slot even though the bottom pad 18 is wider than this part of the slot and is still disposed in the closure below the narrow slot portion. The arrangement in Figure 4 is preferably where flatted bottom pads 18' are to be used.
The side elevational, partly sectional, view of Figure 6a illus-trates the profile of one form of pad where the end face is slightly con-_ g _ ca~ely dished.
Temperature control for the heating elements 15 and 21 is effectedby means of a thermocouple 35 which picks up radiant heat from the heat-collecting member 13 for the plunger 12', and a further thermocouple 36 for sensing the temperature of the closure support bosses 17. The thermocouple 35 is effective to control the power supply to heating element 15 for main-taining accurate temperature stability of the plunger 12' and the thermo-couple 36 is effective to control the power supply to the lower heating element 21 for ensuring temperature stability of the closure support 17.
The temperature monitoring station is disposed at a part of the turret periphery past which all the closure support members 17 and heating members 12' move while the plungers 12' are down in their heating and deform-ing positions, and is effective to vary the power supply to the heaters in response to the mean temperature, around the turret, of these respective setæ of elements.
A further difference between the turret of Figure 2 and that of Figure 4 is that the peripheral edge cam is replaced by the plate cam 16' of Figure 4 having a cam slot formed in one edge to receive the cam follower roller 25' which in Figure 4 is mounted on the side of the plunger body at the top end of the plunger. This dispenses with the need for a spring return action since the slot can now both drive the plunger downwardly and lift the plunger up again thanks to the side mounted cam follower roller configura-tion.
Furthermore, whereas in Figure 2 the upper plunger portion 12a was formed of the asbestos-impregnated phenolic resin material known by the trade name *Ferobestos, chosen for its temperature stability characteristics~ it has been found convenient to adopt a different arrangement in the embodiment of Figure 4. Here the plunger 12 has a stainless steel main body portion 37 with an integral threaded upper shaft portion 38 at the upper end of this portion 37. The threaded shaft extends as a clearance fit through the car-rier 39 on which the cam follower roller 25' is secured in a side-mounted configuration.

%Trademark - 10 -1()6726() The heat-receiving member 13 is clamped to the bottom end of the stainless steel body portion 37 by means of a cap screw 44 which bears against a heat-insulating bush 45 of the thermal insulating material known by the trade name Sindanyo. This bush 45 is received in a bore 46 of the heat-receiving member 13, and a further heat insulating bush 47 is placed between the stainless steel main body portion 37 of the plunger and the upper side of the heat-receiving member 13. Total thermal insulation of the plunger body 37 from the heat-receiving member is completed by an air gap 48 between the screw 44 and the heat-receiving member.
Above and below the carrier 39 are nuts 40 and 41 which can be ad~usted in their position up and down the threaded shaft 38 so as to set precisely the vertical distance between the upper face of the cam groove in cam 16' and the lower extremity of the bottom plunger pad 18' at the lobe of the cam. This is clearly an important dimension in the machine since even the smallest inaccuracy in the spacing between the top face of the closure support 17 and the flat underneath face of the pad 18' will provide a con-siderable variation in the degree of pressing to which the plastics material 49 is sub~ected during the heating operation. The extent of this squashing action is particularly important in view of the fact that the heat exchange contact area between the bottom pad 18' and the plastics material 49 varies as the square of the radius of the squashed plastics mass. The carrier 39 may be formed of any suitable material. For example it may be formed of *Ferobestos or may be in~ection moulded from a plastics material.
Thus, once the turret has been assembled it is rotated step by step between successive ad~ustment stages in which, as each plunger 12' is brought into line with the lobe of the cam 16', the clearance between the flat bottom face of the pad 18' and the flat upper face of the closure sup-port 17 is checked and if necessary ad~usted by moving the shaft 38 upwardly or downwardly relative to the carrier 39 by virtue of the ad~usting nuts 40 and 41.
Apart from the cam operated fully automatic turrets illustrated in Figures 2 and 4, it has also proved aavantageous to construct a laboratory *Trademark - 11 -test rig in which a pellet of plastics material is placed manually in an up-turned closure using a hand-held insertion tool operated in a similar manner to the inserter disclosed in our United States Patent 3,963,396, Keith Shotbolt, June 15, 1976, and for this pellet of plastics material to be moved into register with a press/heating plunger similar to the plunger 12 of Fig-ure 2, or the plunger 12' of Figure 4, and then for the closure with its partially pressed plastics composition to be moved to a moulding station where a relatively cold final moulding tool is brought down manually with the assistance of lever action to compress the plastics material into its final moulded configuration. Suitable means for pre-heating the closure before insertion of the plastics material will, of course be employed even if not incorporated in the actual laboratory rig.
In this way it is possible for the various parameters of the moulding process, for example the composition of the plastics material, the pre-heating temperature, the configuration or temperature of the press/
heating mould, the configuration of the moulding face of the cold mould tool and many other variables to be changed relatively easily so as to ascertain the optimum conditions for any particular type of closure. In this way the development work can be carried out on a single station machine and the lessons from this development work can subsequently be incorporated in a multi-station machine similar to the turrets illustrated in Figure 2 and Figure 4.
The advantages of the direct conduction form of heating for the plastics composition as proposed by the present invention include the fact that the heat is now applied directly to the top face of the plastics com-position by conduction, and the rate of supply of heat increases during the pressing operation because of the progressive increase in the contact area between the squashed plastics composition and the bottom pad 18, or 18' of the plunger 12 or 12'.
This improvement of deforming while heating the plastics composi-tion assists in ensuring a more easily mouldable state for the plastics material which, on arrival at the final cold moulding station, has approx-~n67260 imately the desired finished diameter. The cold mould now only has to carry out the final shaping operation so a much thinner centre panel can be pro-vided in the finished gasket.
Furthermore, with the press/heating step of the present invention there is no incidence of a "shadow" of the top surface of the initial pellet in the finished gasket. This phenomenon was apparently due to the fact that the cold mould initially contacts the top face of the soft but undeformed pellet to "freeze" it so that during a subsequent moulding operation the material which was initially at the top of the pellet is never adequately deformed. With the present invention the cross-section of the pellet grows during heating and thus when the cold moulding tool impinees on the pre-pressed pellet or disc 49 the whole of the top surface of the disc starts at a uniform temperature and finishes up at a uniform temperature immediately after moulding.
Furthermore9 whereas in the past the final cold moulding tool configuration was contoured to give the finished gasket a central portion contoured in the form of a plurality of concentric circular ribs and grooves in order to disguise the unpleasant appearance of the "shadow", the fact that this shadow no longer appears makes it possible for the gasket thickness to be considerably reduced in that these ribs and grooves may be eliminated if desired. This in turn provides greater economy of plastics material, an important saving having regard to the spiralling cost of plastics materials generally. However grooves or ribs may be included to give the centre panel of the gasket a more pleasing shape if desired.
~ he above described process is particularly suitable for use with bottle caps, such as crown caps or other caps and is especially suitable for deep drawn caps or the very deep drawn caps known by the trade name *Stel Caps.
In order that the heated workpiece support member 17 should present the smoothest possible surface to the delicate lacquer on the closures, the member 17 preferably has a highly polished chromium plated upper surface.

*Trademark - 13 -

Claims (8)

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:

1. In an apparatus for applying a moulded surface covering of a thermo-plastic material to a workpiece comprising means for supporting the workpiece, means for feeding a thermoplastic material into contact with the workpiece, means for heating the thermoplastic material, and means for deforming the heated thermoplastic material, the improvement wherein the means for heating and deforming the thermoplastic material comprise pressure member means for partially deforming the thermoplastic material, means for imparting heat to said pressure member means for maintaining the pressure member means at an elevated temperature to ensure heating of the plastics material during said partial deformation, moulding die means for further deforming said partially deformed thermoplastic material, temperature control means for maintaining the temperatures of said moulding die means and said pressure member means at separate values with the moulding die cooler than the pressure member means, and means for driving said pressure member means and said moulding die means towards and away from said workpiece support means for deforming the thermo-plastic material.

2. The improvement of claim 1, wherein said pressure member means includes a surface facing said workpiece, and means imparting low-adhesion characteristics to said facing surface.

3. The improvement of claim 1, wherein said pressure member means comprises a plurality of separate pressure members, said workpiece support means comprises a rotary turret and a plurality of individual workpiece support members carried by and mounted around said turret, means are provided for mounting said pressure members on said turret for vertical sliding move-ment relative to said workpiece support members, and wherein said heating imparting means comprise radiant heat emitting means distributed around said turret for directing radiant heat onto said pressure members.

4. The improvement of claim 3 and including further radiant heat emitting means arranged around said turret for directing radiant heat towards said workpiece support members.

5. The improvement of claim 3 wherein each pressure member includes means defining a blackened, roughened surface for receiving radiant heat emitted from the radiant heat emitting means.

6. The improvement of claim 3, 4 or 5, wherein a stripper member is located around said turret at a level above that of the workpiece support members and said driving means for the pressure members is adapted to cause the pressure members to penetrate said stripper member in their vertical sliding movement to be withdrawn from said stripper member during upward movement away from said workpiece support members.

7. The improvement of claim 4 or 5 and including first temperature sensing means for detecting the temperatures of said pressure members, and further temperature sensing means for detecting the temperatures of said workpiece support members, and wherein temperature control means is connected to said first and second temperature sensing means and to the first mentioned and further radiant heat emitting means for controlling the temperature of said workpiece support members and the temperatures of said pressure members at desired different values above the temperature of said moulding die means.

8. The improvement of claim 1, 2 or 3 and further including rotary turret means for pre-heating workpieces, and rotary turret means including a support member, means for heating said support member, and means for advanc-ing closures around said turret while resting on said support member and receiving conductive heat from the support member.