BR202018011247U2

BR202018011247U2 - article in the form of a multilayer structure

Info

Publication number: BR202018011247U2
Application number: BR202018011247U
Authority: BR
Inventors: Azerraf Clarite; Michael Leibler David; Kulbak Einav; Ben Shalom Tal; Nevo Yuval
Original assignee: Melodea Ltd
Priority date: 2018-06-01
Filing date: 2018-06-01
Publication date: 2020-04-07

Abstract

artigo na forma de estrutura com múltiplas camadas o presente modelo fornece artigos ou estruturas com múltiplas camadas com alta estabilidade e versáteis, com base em nanomateriais de celulose, adaptados e processados para uma série de aplicações, como materiais superiores na indústria de embalagem de alimentos.article in the form of a multilayered structure the present model provides highly stable and versatile multilayered articles or structures, based on cellulose nanomaterials, adapted and processed for a number of applications, as superior materials in the food packaging industry.

Description

ARTIGO NA FORMA DE ESTRUTURA COM MÚLTIPLAS CAMADAS CAMPO DO MODELO [001] O presente modelo refere-se, de forma geral, a artigos com múltiplas camadas e seus usos.ARTICLE IN STRUCTURE FORM WITH MULTIPLE LAYERS CAMPO DO MODELO [001] The present model refers, in general, to articles with multiple layers and their uses.

ANTECEDENTES DO MODELO [002] Nanocristais de celulose (CNC) são uma das formas conhecidas de celulose, o principal componente de paredes celulares de árvores e plantas. CNCs podem estar presentes na forma de solução de cristal líquido em água e são conhecidos por sua automontagem em filmes ordenados em escala macro que possuem espessuras em nanoescala.BACKGROUND OF THE MODEL [002] Cellulose nanocrystals (CNC) are one of the known forms of cellulose, the main component of cell walls of trees and plants. CNCs can be present in the form of a liquid crystal solution in water and are known for their self-assembly in films ordered on a macro scale that have nanoscale thicknesses.

[003] Os cristais nanodimensionados possuem interessantes propriedades ópticas e estruturais dependentes do seu tamanho. A capacidade de alterar as variáveis de processamento fornece a capacidade de controlar a estrutura, composição, tamanho e nível de dispersão desses nanocristais.[003] The nanodimensioned crystals have interesting optical and structural properties depending on their size. The ability to change processing variables provides the ability to control the structure, composition, size and dispersion level of these nanocrystals.

ANTECEDENTES DA TÉCNICA [004] 1. WO 2017/046798; e [005] 2. WO 2013/132491.BACKGROUND OF THE TECHNIQUE [004] 1. WO 2017/046798; and [005] 2. WO 2013/132491.

DESCRIÇÃO RESUMIDA DO MODELO [006] Os inventores da tecnologia descrita no presente desenvolveram artigos ou estruturas com múltiplas camadas com alta estabilidade e versáteis, com base em nanomateriais de celulose, tais como nanocristais de celulose (CNC), que podem ser adaptados e processados para uma série de aplicações, que são materiais superiores às folhas de alumínio utilizadas, por exemplo, na indústria de embalagem de alimentos e exibem barreiras superiores a gases, solventes orgânicos, óleos e outros agentes.BRIEF DESCRIPTION OF THE MODEL [006] The inventors of the technology described in the present have developed articles or structures with multiple layers with high stability and versatility, based on cellulose nanomaterials, such as cellulose nanocrystals (CNC), which can be adapted and processed to a series of applications, which are superior materials to aluminum foils used, for example, in the food packaging industry and exhibit superior barriers to gases, organic solvents, oils and other agents.

[007] Os artigos de acordo com o presente[007] Articles in accordance with this

Petição 870180060742, de 13/07/2018, pág. 4/35Petition 870180060742, of 07/13/2018, p. 4/35

2/24 modelo são livres de nanopartículas metálicas e, portanto, são apropriados para uma ampla variedade de aplicações, incluindo como materiais de embalagem para alimentos, bebidas, bens de consumo e produtos farmacêuticos. Os artigos podem ser adaptados ou previamente estruturados de acordo com um ou mais usos ou aplicações finais. Os artigos de acordo com o presente modelo podem ser especificamente adaptados como material de embalagem de alimentos secos ou como material de embalagem de alimentos líquidos.2/24 models are free of metallic nanoparticles and are therefore suitable for a wide variety of applications, including as packaging materials for food, beverages, consumer goods and pharmaceuticals. Articles can be adapted or previously structured according to one or more end uses or applications. The articles according to the present model can be specifically adapted as packaging material for dry foods or as packaging material for liquid foods.

[008] Em primeiro aspecto, o presente modelo fornece artigos na forma de estrutura com múltiplas camadas (que pode ou não apresentar-se na forma de folha substancialmente bidimensional), que compreende três ou mais camadas de materiais, em que pelo menos uma das mencionadas três ou mais camadas compreende um nanomaterial de celulose selecionado a partir de nanocristais (CNC), celulose nanofibrilar (NFC), celulose microfibrilada (MFC), combinação de CNC e NFC, combinação de CNC e MFC, mistura de CNC com pelo menos um aditivo, tal como um polímero, ou uma mistura de NFC com pelo menos um aditivo, tal como um polímero que é hidrossolúvel ou dispersível em água (tais como polímeros ricos em hidroxila ou carboxila).[008] In the first aspect, the present model provides articles in the form of a multilayered structure (which may or may not be in the form of a substantially two-dimensional sheet), comprising three or more layers of materials, in which at least one of the mentioned three or more layers comprises a cellulose nanomaterial selected from nanocrystals (CNC), nanofibrillar cellulose (NFC), microfibrillated cellulose (MFC), combination of CNC and NFC, combination of CNC and MFC, mixture of CNC with at least one additive, such as a polymer, or a mixture of NFC with at least one additive, such as a polymer that is water-soluble or dispersible in water (such as polymers rich in hydroxyl or carboxyl).

[009] [009] Em algumas In some realizações, achievements, o artigo the article com with múltiplas multiple camadas layers compreende um substrato, comprises a substrate, nanomaterial nanomaterial de in celulose, cellulose, tal such como like camada com layer with base em CNC, CNC based, e uma camada and a layer de in cobertura roof , de , in tal such forma que way that a camada de the layer of nanomaterial nanomaterial de in celulose cellulose forme for me uma an interface entre o substrato e a camada interface between substrate and layer de in

cobertura.roof.

[010] Em algumas realizações, o artigo com múltiplas camadas compreende um substrato, uma camada com[010] In some embodiments, the multilayered article comprises a substrate, a layer with

Petição 870180060742, de 13/07/2018, pág. 5/35Petition 870180060742, of 07/13/2018, p. 5/35

3/24 base em CNC e uma camada de cobertura, de tal forma que a camada com base em CNC forme uma interface entre o substrato e a camada de cobertura.3/24 CNC base and a covering layer, such that the CNC based layer forms an interface between the substrate and the covering layer.

[011] Em algumas realizações, o substrato e a camada de cobertura são os mesmos. Em algumas realizações, o substrato e a camada de cobertura são diferentes.[011] In some embodiments, the substrate and the covering layer are the same. In some embodiments, the substrate and the covering layer are different.

[012] Em algumas realizações, o artigo possui uma estrutura em camadas da forma ABC, em que cada uma dentre[012] In some embodiments, the article has a layered structure of the ABC form, in which each of

A, B e C é uma camada de material, conforme ilustrado na Fig.A, B and C is a layer of material, as shown in Fig.

1, em que: A é um substrato que compreende ou consiste de um material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, tal como papelão, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso ou material de membrana; e outros; B é um nanomaterial de celulose, conforme selecionado no presente, tal como material com base em CNC que compreende CNC ou consiste de CNC; C é uma camada de cobertura que compreende ou consiste de material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, tal como papelão, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso ou material de membrana, ou material metálico, tal como folha ou chapa metálica.1, where: A is a substrate that comprises or consists of a material selected from polymeric material, paper or paper-based material, material based on polymer-coated paper, such as cardboard, nanocellulose film, film nanocellulose and polymer, woven material, porous material or membrane material; and others; B is a cellulose nanomaterial, as selected at present, such as a CNC-based material that comprises CNC or consists of CNC; C is a cover layer comprising or consisting of material selected from polymeric material, paper or paper-based material, material based on polymer-coated paper, such as cardboard, nanocellulose film, nanocellulose film and polymer, woven material, porous material or membrane material, or metallic material, such as sheet or sheet metal.

[013] [013] Em algumas In some realizações, a achievements, camada B layer B não not compreende, nem understand nor consiste de NFC. consists of NFC. [014] [014] Uma ou ambas One or both as camadas A layers A e C podem and C can ser, to be, alternativa ou alternative or adicionalmente, additionally, revestidas coated ou feitas or made de in

material de verniz. Como é conhecido na técnica, vernizes sãovarnish material. As is known in the art, varnishes are

Petição 870180060742, de 13/07/2018, pág. 6/35Petition 870180060742, of 07/13/2018, p. 6/35

4/24 materiais hidrofóbicos que, por si próprios, podem agir como camada resistente à água, barreira de vapor d'água ou fornecem proteção mecânica a qualquer camada à qual estejam associados, tais como a camada B ou qualquer das camadas A e C conforme definido no presente. As camadas de verniz, seja diretamente sobre a camada B ou sobre qualquer uma ou ambas as camadas A ou C, podem também ser fornecidas de forma a fornecer a capacidade de impressão sobre elas. A composição ou material de verniz pode ser obtida conforme disponível comercialmente ou pode ser adaptada para o propósito específico. O material de verniz é tipicamente uma composição que contém um ou mais polímeros, tais como poliuretano, acrílico, epóxi ou poliéster; resinas tais como resina fenólica, resina de alquídeo ou resina de poliuretano; e óleos tais como óleo de linhaça, óleo de nozes, óleo de tungue e óleo de soja.4/24 hydrophobic materials which, by themselves, can act as a water resistant layer, water vapor barrier or provide mechanical protection to any layer with which they are associated, such as layer B or any of layers A and C as per defined in the present. Varnish layers, either directly over layer B or over either or both layers A or C, can also be supplied in order to provide the ability to print on them. The composition or varnish material can be obtained as commercially available or can be adapted for the specific purpose. The varnish material is typically a composition that contains one or more polymers, such as polyurethane, acrylic, epoxy or polyester; resins such as phenolic resin, alkyl resin or polyurethane resin; and oils such as linseed oil, nut oil, tung oil and soy oil.

[015] Em algumas realizações, para propósitos e aplicações específicas, a folha externa (substrato A ou camada de cobertura C exibida na Fig. 1) pode ser um filme ou folha metálica, ou um composto de metal. A camada B não é um filme ou folha metálica, nem compreende material(is) metálico(s).[015] In some embodiments, for specific purposes and applications, the outer sheet (substrate A or cover layer C shown in Fig. 1) can be a film or foil, or a metal compound. Layer B is not a film or foil, nor does it comprise metallic material (s).

[016] Em algumas realizações, nem o substrato[016] In some embodiments, neither the substrate

A, nem a camada de cobertura C, é um filme de nanocelulose, nem compreende esse material.A, nor the covering layer C, is a nanocellulose film, nor does it comprise this material.

[017] Dever-se-á observar que os termos substrato e “camada de cobertura” não deverão ser considerados propondo direcionalidade a artigos de acordo com o presente modelo. Em outras palavras, o termo substrato não necessita ser a camada inferior ou a camada a partir da[017] It should be noted that the terms substrate and “covering layer” should not be considered when proposing directionality to articles in accordance with this model. In other words, the term substrate does not have to be the bottom layer or the layer from

Petição 870180060742, de 13/07/2018, pág. 7/35Petition 870180060742, of 07/13/2018, p. 7/35

5/24 qual se inicia a fabricação do artigo. De forma similar, a expressão “camada de cobertura” não deverá ser contemplada como a camada superior, nem a camada que envolve ou cobre as camadas restantes ou características da estrutura com múltiplas camadas.5/24 which starts the manufacture of the article. Similarly, the term “cover layer” should not be considered as the top layer, nor the layer that surrounds or covers the remaining layers or features of the structure with multiple layers.

[018] Conforme indicado no presente, a camada B compreende ou consiste de um nanomaterial de celulose, tal como CNC e NFC. Em algumas realizações, a camada B é livre de NFC.[018] As indicated herein, layer B comprises or consists of a cellulose nanomaterial, such as CNC and NFC. In some embodiments, layer B is free of NFC.

[019] Nanocristais de celulose (CNC) ou celulose nanocristalina (NCC) são fibras produzidas com celulose, em que os CNCs são tipicamente cristais isolados com alta pureza. Eles constituem uma classe genérica de materiais que possuem resistência mecânica equivalente às forças de ligação de átomos adjacentes. A estrutura altamente ordenada resultante produz não apenas resistências incomumente altas, mas também alterações significativas de propriedades térmicas, elétricas, ópticas, magnéticas, ferromagnéticas, dielétricas, condutoras e até supercondutoras. As propriedades de resistência à tensão de CNC estão muito acima dos reforços de teor de alto volume atuais e permitem o processamento das resistências compostas mais altas que podem ser atingidas.[019] Cellulose nanocrystals (CNC) or nanocrystalline cellulose (NCC) are fibers produced with cellulose, where CNCs are typically isolated crystals with high purity. They constitute a generic class of materials that have mechanical strength equivalent to the binding forces of adjacent atoms. The resulting highly ordered structure produces not only unusually high resistances, but also significant changes in thermal, electrical, optical, magnetic, ferromagnetic, dielectric, conductive and even superconducting properties. The CNC's tensile strength properties are far above today's high volume reinforcements and allow the processing of the highest composite resistances that can be achieved.

[020] Como é conhecido na técnica, nanofibrilas de celulose (CNF ou NFC) são materiais celulósicos compostos de pelo menos uma fibrila primária, que contém regiões amorfas e cristalinas, com razões de aspecto normalmente de mais de 50. O seu comprimento é de 0,1-5 pm e seu diâmetro é de 5-60 nm. De forma similar, microfibrilas de celulose (CMF ou MFC) são materiais celulósicos que contêm regiões amorfas[020] As is known in the art, cellulose nanofibrils (CNF or NFC) are cellulosic materials composed of at least one primary fibril, containing amorphous and crystalline regions, with aspect ratios normally over 50. Their length is 0.1-5 pm and its diameter is 5-60 nm. Similarly, cellulose microfibrils (CMF or MFC) are cellulosic materials that contain amorphous regions

Petição 870180060742, de 13/07/2018, pág. 8/35Petition 870180060742, of 07/13/2018, p. 8/35

6/24 e cristalinas, com razões de aspecto normalmente de mais de 50. O seu comprimento é de alguns micrômetros e o seu diâmetro é de mais de 100 nm. CMF pode conter alguma fração de CNF.6/24 and crystalline, with aspect ratios usually over 50. Its length is a few micrometers and its diameter is over 100 nm. CMF may contain some fraction of CNF.

[021] Em algumas realizações, o nanomaterial de celulose é caracterizado por possuir pelo menos 50% de cristalinidade. Em algumas realizações, o nanomaterial de celulose é monocristalino. Em algumas realizações, o nanomaterial de celulose é material monocristalino com alta pureza.[021] In some embodiments, cellulose nanomaterial is characterized by having at least 50% crystallinity. In some embodiments, cellulose nanomaterial is monocrystalline. In some embodiments, cellulose nanomaterial is monocrystalline material with high purity.

[022] Em algumas realizações, os nanocristais do nanomaterial possuem comprimento de pelo menos cerca de 50 nm. Em outras realizações, eles possuem comprimento de pelo menos cerca de 100 nm ou possuem comprimento de, no máximo, 1000 nm. Em outras realizações, os nanocristais possuem comprimento de cerca de 100 nm a 1000 nm, comprimento de 100 nm a 900 nm, comprimento de 100 nm a 600 nm ou comprimento de[022] In some embodiments, nanomaterial nanocrystals are at least about 50 nm long. In other embodiments, they are at least about 100 nm long or at most 1000 nm long. In other embodiments, nanocrystals have a length of about 100 nm to 1000 nm, a length of 100 nm to 900 nm, a length of 100 nm to 600 nm or a length of

100 nm a 500 nm.100 nm to 500 nm.

[023] Em algumas realizações, os nanocristais possuem comprimento de cerca de 10 nm a 100 nm, 100 nm a 1000 nm, 100 nm a 900 nm, 100 nm a 800 nm, 100 nm a 600 nm, 100 nm[023] In some embodiments, nanocrystals are about 10 nm to 100 nm in length, 100 nm to 1000 nm, 100 nm to 900 nm, 100 nm to 800 nm, 100 nm to 600 nm, 100 nm

a The 500 500 nm, nm, 100 nm a 100 nm at 400 400 nm, nm, 100 100 nm a 300 nm at 300 nm ou cerca de nm or about 100 nm 100 nm a The 200 200 nm. nm. [024] [024] Os The nanocristais podem ser nanocrystals can be selecionados selected para for que what possuam own razão reason de in aspecto aspect média average (razão (reason entre in between

comprimento e diâmetro) de 10 ou mais. Em algumas realizações, a razão em aspecto média é de 10 a 100, 20 alength and diameter) of 10 or more. In some embodiments, the average aspect ratio is 10 to 100, 20 to

100, 100, 30 30 a The 100, 100, 40 40 a The 100, 100, 50 50 a 100, 60 a to 100, 60 to 100, 100, 70 70 a 100, to 100, 80 a 80 to 100, 100, 90 90 a The 100, 100, 61 61 a The 100, 100, 62 62 a 100, 63 a to 100, 63 to 100, 100, 64 64 a 100, to 100, 65 a 65 to 100, 100, 66 66 a The 100, 100, 67 67 a The 100, 100, 68 68 a 100 ou 69 a to 100 or 69 to 100. 100.

Petição 870180060742, de 13/07/2018, pág. 9/35Petition 870180060742, of 07/13/2018, p. 9/35

7/24 [025] Em algumas realizações, a razão de aspecto média é de 67 a 100.7/24 [025] In some embodiments, the average aspect ratio is 67 to 100.

[026] Em algumas realizações, o nanomaterial de celulose é CNC. Em algumas realizações, o nanomaterial de celulose não é NFC.[026] In some projects, cellulose nanomaterial is CNC. In some embodiments, cellulose nanomaterial is not NFC.

[027] Dependendo do processo utilizado para a produção de CNC ou NFC, o material pode apresentar-se em uma série de purezas. Em alguns casos, o nanomaterial de celulose pode compreender sais e/ou carboidratos, tais como hemicelulose, xiloglucano, derivados de celulose e outros. Desta forma, o CNC ou NFC utilizado de acordo com o presente modelo pode compreender 0,01 a 0,5% de impurezas, tais como carboidratos e sais.[027] Depending on the process used for the production of CNC or NFC, the material can be presented in a series of purities. In some cases, the cellulose nanomaterial may comprise salts and / or carbohydrates, such as hemicellulose, xyloglucan, cellulose derivatives and others. In this way, the CNC or NFC used according to the present model can comprise 0.01 to 0.5% of impurities, such as carbohydrates and salts.

[028] A camada B confere à estrutura com múltiplas camadas uma ou mais propriedades que podem ser aprimoradas, reduzidas ou modificadas de outra forma por meio da seleção de uma camada de cobertura ou substrato apropriado. Em algumas realizações, a composição de material da camada B é selecionada para exibir propriedades de barreira contra gás, propriedades de barreira contra óleo e propriedades de barreira contra vapor d'água. As propriedades de barreira contra gás incluem a prevenção, suspensão ou minimização da permeação ou transporte de gases ao longo da estrutura com múltiplas camadas, em que o gás é selecionado a partir de oxigênio, dióxido de carbono, aroma, SOx, NOx, metano, gases fluoretados e outros. As propriedades de barreira contra óleo incluem a prevenção, suspensão ou minimização da permeação ou transporte de óleos tais como óleo vegetal, óleo mineral e graxa.[028] Layer B gives the multilayer structure one or more properties that can be enhanced, reduced or otherwise modified by selecting an appropriate covering layer or substrate. In some embodiments, the layer B material composition is selected to exhibit gas barrier properties, oil barrier properties and water vapor barrier properties. The gas barrier properties include preventing, suspending or minimizing the permeation or transport of gases along the multilayer structure, where the gas is selected from oxygen, carbon dioxide, aroma, SOx, NOx, methane, fluoridated gases and others. Oil barrier properties include preventing, suspending or minimizing the permeation or transportation of oils such as vegetable oil, mineral oil and grease.

[029] A camada B pode também ser selecionada[029] Layer B can also be selected

Petição 870180060742, de 13/07/2018, pág. 10/35Petition 870180060742, of 07/13/2018, p. 10/35

8/24 para que possua composição ou espessura que forneça suporte mecânico à estrutura com múltiplas camadas. Ela pode ser uma camada transparente, opaca ou não transparente e, em alguns casos, pode ser adaptada para bloquear certos comprimentos de onda.8/24 so that it has composition or thickness that provides mechanical support to the structure with multiple layers. It can be a transparent, opaque or non-transparent layer and, in some cases, can be adapted to block certain wavelengths.

[030] Em algumas realizações, a camada B compreende uma mistura de CNC com pelo menos um outro material de nanocelulose, tal como NFC, ou com pelo menos um aditivo. Em algumas realizações, a camada B compreende ou consiste de NFC. Quando a camada compreender NFC, ela pode compreender adicionalmente pelo menos um aditivo, tal como polímero, ou pode ser apresentada na forma de combinação com CNC.[030] In some embodiments, layer B comprises a mixture of CNC with at least one other nanocellulose material, such as NFC, or with at least one additive. In some embodiments, layer B comprises or consists of NFC. When the layer comprises NFC, it can additionally comprise at least one additive, such as polymer, or can be presented in the form of a combination with CNC.

[031] [031] Em In algumas some realizações, a achievements, camada layer B B consiste de CNC consists of CNC ou uma or a combinação combination de CNC e NFC. CNC and NFC. [032] [032] Em In algumas some realizações, a achievements, camada layer B B

compreende CNC e/ou NFC em combinação (na forma de mistura) com pelo menos um polímero selecionado a partir de PVOH, PVAc, EVOH, PVP, amido, chitosan, ácido poliacrílico, polietilenoimina, carboidratos, EVA e poliuretanos.comprises CNC and / or NFC in combination (in the form of mixture) with at least one polymer selected from PVOH, PVAc, EVOH, PVP, starch, chitosan, polyacrylic acid, polyethyleneimine, carbohydrates, EVA and polyurethanes.

[033] Em algumas realizações, o aditivo ou qualquer outro material utilizado em combinação com CNC e/ou NFC não é polipropileno biorientado (BOPP).[033] In some embodiments, the additive or any other material used in combination with CNC and / or NFC is not bioriented polypropylene (BOPP).

[034] Em algumas realizações, a camada B é uma camada de CNC que pode consistir de CNC ou pode compreender uma combinação (mistura, não camadas separadas) de CNC e pelo menos um aditivo, tal como polímero, selecionado para fornecer à camada ou material de CNC uma ou mais propriedades selecionadas a partir de barreira contra gases, barreira contra óleo, barreira contra vapor d'água, melhores[034] In some embodiments, layer B is a CNC layer that may consist of CNC or may comprise a combination (mixture, not separate layers) of CNC and at least one additive, such as polymer, selected to provide the layer or CNC material one or more properties selected from gas barrier, oil barrier, water vapor barrier, best

Petição 870180060742, de 13/07/2018, pág. 11/35Petition 870180060742, of 07/13/2018, p. 11/35

9/24 propriedades mecânicas, propriedades térmicas, propriedades adesivas e outras.9/24 mechanical properties, thermal properties, adhesive properties and others.

[035][035]

A camada de nanomaterial de celulose, tal como CNC, pode ser composta do nanomaterial, tal como CNC, e pelo menos um aditivo, tal como material polimérico, em que a quantidade do aditivo, tal como material polimérico, varia de 0,1 a 99% em peso da camada de nanomaterial (com relação à quantidade em peso total dos materiais que compõem a camada). Em algumas realizações, a quantidade do material polimérico é de 0,1 a 90%, 0,1 a 85%, 0,1 a 80%, 0,1 a 75%, 0,1 a 70%, 0,1 a 65%, 0,1 a 60%, 0,1 a 55%, 0,1 a 50%, 0,1 a 45%, 0,1 a 40%, 0,1 a 35%, 0,1 a 30%, 0,1 a 25%, 0,1 a 20%, 0,1 a 15%, 0,1 a 10%, 0,1 a 9%, 0,1 a 8%, 0,1 a 7%, 0,1 a 6%, 0,1 a 5%, 0,1 a 4%, 0,1 a 3%, 0,1 a 2%, 0,1 a 1%, 1 a 90%, 5 a 90%, 10 a 90%, 15 a 90%, 20 a 90%, 25 a 90%, 30 a 90%, 35 a 90%, 40 a 90%, 45 a 90%, 50 a 90%, 55 a 90%, 60 a 90%, 65 a 90%, 70 a 90%, 75 a 90%, 80 a 90%, 85 a 90%, 1 a 85%, 5 a 80%, 10 a 80%, 15 a 75%, 20 a 70%, 25 a 65%, 30 a 60%, 35 a 55% ou 40 a 50%.The cellulose nanomaterial layer, such as CNC, can be composed of nanomaterial, such as CNC, and at least one additive, such as polymeric material, in which the amount of the additive, such as polymeric material, ranges from 0.1 to 99% by weight of the nanomaterial layer (in relation to the total weight of the materials that make up the layer). In some embodiments, the amount of polymeric material is 0.1 to 90%, 0.1 to 85%, 0.1 to 80%, 0.1 to 75%, 0.1 to 70%, 0.1 to 65%, 0.1 to 60%, 0.1 to 55%, 0.1 to 50%, 0.1 to 45%, 0.1 to 40%, 0.1 to 35%, 0.1 to 30 %, 0.1 to 25%, 0.1 to 20%, 0.1 to 15%, 0.1 to 10%, 0.1 to 9%, 0.1 to 8%, 0.1 to 7% , 0.1 to 6%, 0.1 to 5%, 0.1 to 4%, 0.1 to 3%, 0.1 to 2%, 0.1 to 1%, 1 to 90%, 5 to 90%, 10 to 90%, 15 to 90%, 20 to 90%, 25 to 90%, 30 to 90%, 35 to 90%, 40 to 90%, 45 to 90%, 50 to 90%, 55 to 90%, 60 to 90%, 65 to 90%, 70 to 90%, 75 to 90%, 80 to 90%, 85 to 90%, 1 to 85%, 5 to 80%, 10 to 80%, 15 to 75%, 20 to 70%, 25 to 65%, 30 to 60%, 35 to 55% or 40 to 50%.

036]036]

Em algumas realizações, o aditivo é um polímero tal como PVOH, presente em quantidade de 50 a 70%, 60 a 70%, 70 a 90% ou 70 a 80% de uma composição que consiste do aditivo e CNC (em outras palavras, quantidade de 70% a 90% de polímero indica 70-90% de polímero e 30-10% de CNC).In some embodiments, the additive is a polymer such as PVOH, present in an amount of 50 to 70%, 60 to 70%, 70 to 90% or 70 to 80% of a composition consisting of the additive and CNC (in other words, 70% to 90% polymer indicates 70-90% polymer and 30-10% CNC).

037]037]

Em algumas realizações a razão entre aditivo e CNC é 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9,In some embodiments the ratio between additive and CNC is 1: 1, 1: 2, 1: 3, 1: 4, 1: 5, 1: 6, 1: 7, 1: 8, 1: 9,

1:10, 10:1, 9:1, 8:1, 7:1, 6:1, 5:1, 4:1, 3:1 ou 2:1.1:10, 10: 1, 9: 1, 8: 1, 7: 1, 6: 1, 5: 1, 4: 1, 3: 1 or 2: 1.

038]038]

O pelo menos um aditivo pode ser um polímero ou qualquer outro aditivo tal como um plastificante, como glicerol ou sorbitol; tensoativo; material particulado, como partículas ou nanopartículas de Mg (excluindoThe at least one additive can be a polymer or any other additive such as a plasticizer, such as glycerol or sorbitol; surfactant; particulate matter, such as Mg particles or nanoparticles (excluding

Petição 870180060742, de 13/07/2018, pág. 12/35Petition 870180060742, of 07/13/2018, p. 12/35

10/24 nanopartículas de outros elementos); pigmento; carboidrato; sal; material condutor; extrator de oxigênio e outros.10/24 nanoparticles of other elements); pigment; carbohydrate; salt; conductive material; oxygen extractor and others.

[039] Quando o aditivo não for um polímero, ele pode estar presente em quantidades indicadas acima ou em quantidades que variam de 1% a 20%.[039] When the additive is not a polymer, it can be present in the amounts indicated above or in amounts ranging from 1% to 20%.

[040] Em algumas realizações, a camada B compreende CNC/PVOH. A camada possui espessura de 100 nm a 20[040] In some embodiments, layer B comprises CNC / PVOH. The layer is 100 nm thick at 20

pm. pm. Em In algumas some realizações, a achievements, espessura é de 100 a 900 nm, thickness is 100 to 900 nm, 900 900 nm nm a 20 pm, at 20 pm, 1000 nm a 20 1000 nm at 20 pm, 1 pm a 2 0 pm ou 1 pm a pm, 1 pm to 20 pm or 1 pm to 10 10 pm. pm. [041] [041] Em algumas In some realizações, a espessura é achievements, the thickness is de in 1 pm 1 pm a The 20 pm, 1 20 pm, 1 pm a 20 pm, 1 pm to 20 pm, 1 pm a 15 pm, 1 pm a 10 pm ou pm to 15 pm, 1 pm to 10 pm or de in 1 pm 1 pm a The 5 pm. 5 pm. [042] [042] Cada uma Each one das camadas A e C fornece layers A and C provides à The

estrutura com múltiplas camadas capacidades mecânicas e de barreira que podem ser adaptadas para atender a uma ou mais aplicações finais. O substrato e a camada de cobertura podem ser impressos, laminados ou associados de outra forma a uma ou mais camadas, folhas, filmes ou revestimentos. Uma estrutura com múltiplas camadas que possui a forma geral ABC pode ser dobrada ou disposta em um bolso, recipiente ou invólucro, de tal forma que A ou C possa ser a superfície externa do bolso, recipiente ou invólucro, ou sua superfície interna. Dependendo do produto final, pode-se selecionar o material ou a composição de cada uma das camadas A e C.structure with multiple layers mechanical and barrier capacities that can be adapted to meet one or more final applications. The substrate and the covering layer can be printed, laminated or otherwise associated with one or more layers, sheets, films or coatings. A multilayered structure that has the general shape ABC can be folded or arranged in a pocket, container or wrapper, such that A or C can be the outer surface of the pocket, container or wrapper, or its inner surface. Depending on the final product, you can select the material or composition of each of layers A and C.

[043] Em algumas realizações, cada uma das camadas A e C é selecionada, independentemente entre si, a partir de polietileno, polipropileno, poliéster, álcool polivinílico, álcool etileno vinílico, poliamida, poliestireno, ácido poliláctico, póli-hidroxialcanoato,[043] In some embodiments, each of the layers A and C is selected, independently of each other, from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid, polyhydroxyalkanoate,

Petição 870180060742, de 13/07/2018, pág. 13/35Petition 870180060742, of 07/13/2018, p. 13/35

11/24 policaprolactona, póli-hidroxibutirato, acetato de polivinila, poliacrilonitrila, cloreto de polivinilideno, celulose, tereftalato de polietileno, cloreto de polivinila e policarbonato.11/24 polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

[044] Em algumas realizações, uma das camadas A e C é papelão revestido com polímero, em que o polímero é selecionado a partir de polietileno, polipropileno, poliéster, álcool polivinílico, álcool etileno vinílico, poliamida, poliestireno, ácido poliláctico, pólihidroxialcanoato, policaprolactona, póli-hidroxibutirato, acetato de polivinila, poliacrilonitrila, cloreto de polivinilideno, celulose, tereftalato de polietileno, cloreto de polivinila e policarbonato.[044] In some embodiments, one of the layers A and C is cardboard coated with polymer, in which the polymer is selected from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid, polyhydroxyalkanoate, polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

[045] Em algumas realizações, pelo menos uma das camadas A e C, independentemente ente si, é ou compreende um tecido. O tecido pode ser qualquer tecido, tecido natural, tecido sintético, malha, material tecido, material não tecido ou rede de material selecionado a partir de celulose, viscose, fibras de vidro, fibras de carbono e fibras sintéticas. De forma similar, o tecido pode apresentar-se na forma de membrana, selecionada conforme indicado.[045] In some embodiments, at least one of layers A and C, independently of itself, is or comprises a fabric. The fabric can be any fabric, natural fabric, synthetic fabric, mesh, woven material, non-woven material or network of material selected from cellulose, viscose, glass fibers, carbon fibers and synthetic fibers. Similarly, the fabric may be in the form of a membrane, selected as indicated.

[046] Em algumas realizações, em que uma folha ou chapa metálica constitui pelo menos uma das camadas A e C, independentemente entre si, o metal pode ser selecionado a partir de alumínio, silício, zinco, ferro, titânio ou um de seus óxidos ou ligas.[046] In some embodiments, in which a sheet or metal plate constitutes at least one of the layers A and C, independently of each other, the metal can be selected from aluminum, silicon, zinc, iron, titanium or one of its oxides or alloys.

[047] As camadas A e B e/ou as camadas B e C podem ser associadas entre si diretamente ou separadas por um ou mais materiais de interface, conforme ilustrado para fins de exemplificação na Fig. 2. O material de interface entre A[047] Layers A and B and / or layers B and C can be associated with each other directly or separated by one or more interface materials, as illustrated for purposes of example in Fig. 2. The interface material between A

Petição 870180060742, de 13/07/2018, pág. 14/35Petition 870180060742, of 07/13/2018, p. 14/35

12/24 e B não necessita ser o mesmo material de interface que associa as camadas B e C ou um ou os dois materiais de interface podem estar ausentes. Independentemente se as camadas são ou não associadas diretamente ou por meio de material de interface, a camada de substrato e/ou a camada de cobertura podem ser previamente tratadas para permitir associação estável e de longa duração entre as camadas. Tratamento prévio pode envolver um ou mais dentre plasma, corona, chama, calor ou quaisquer métodos de tratamento prévio conhecidos.12/24 and B need not be the same interface material that associates layers B and C or one or both interface materials may be missing. Regardless of whether or not the layers are associated directly or by means of interface material, the substrate layer and / or the covering layer can be pre-treated to allow a stable and long-lasting association between the layers. Pre-treatment may involve one or more of plasma, corona, flame, heat or any known pre-treatment methods.

[048] Alternativa ou adicionalmente, as camadas podem ser associadas entre si por meio de um material de primer ou material adesivo, exibido na Fig. 2 como as camadas entre as camadas A e B ou entre as camadas B e C. Esse primer sobre adesivo pode ser inerente ao substrato ou à camada de cobertura (nomeadamente, embutida no interior do substrato/camada de cobertura ou previamente associado ao substrato/camada de cobertura ou é o material de substrato/camada de cobertura) e, portanto, não pode ser adicionado na forma de filme ou camada separada, ou como etapa de processo ou tratamento prévio separado. Em casos em que o primer ou os materiais adesivos não são parte do substrato ou da camada de cobertura, eles podem ser revestidos sobre o substrato ou a camada de cobertura para formar uma camada adicional cujo propósito pode ser a indução de adesão ou associação entre as camadas e que tipicamente, embora opcionalmente, não possuem como efeito nenhuma propriedade mecânica, funcional ou característica de outra forma da estrutura com múltiplas camadas. O filme ou camada adesiva ou de primer tipicamente não são utilizados para[048] Alternatively or additionally, the layers can be joined together using a primer material or adhesive material, shown in Fig. 2 as the layers between layers A and B or between layers B and C. This primer over adhesive can be inherent in the substrate or the covering layer (namely, embedded in the substrate / covering layer or previously associated with the substrate / covering layer or is the substrate / covering layer material) and, therefore, cannot be added in the form of a film or separate layer, or as a separate processing step or pretreatment. In cases where the primer or adhesive materials are not part of the substrate or the covering layer, they can be coated on the substrate or the covering layer to form an additional layer whose purpose may be to induce adhesion or association between the layers and which typically, although optionally, do not have any mechanical, functional or otherwise characteristic properties of the multilayer structure. The adhesive or primer film or layer is typically not used for

Petição 870180060742, de 13/07/2018, pág. 15/35Petition 870180060742, of 07/13/2018, p. 15/35

13/24 fornecer à estrutura com múltiplas camadas uma ou mais propriedades funcionais. A seleção de primer ou material adesivo pode destinar-se, entretanto, a introduzir, fortalecer ou reduzir adicionalmente uma ou mais propriedades associadas à estrutura com múltiplas camadas como um todo ou com uma ou mais camadas destes. Essa propriedade pode ser a capacidade de dobra, elasticidade, transparência, absorção, transmissão de luz, permeabilidade de gases ou solventes, umectabilidade, resistência térmica e outras. A camada de primer ou adesiva compreende um material selecionado a partir de poliuretano, epóxi, acrilato, adesivos de fusão a quente, polietrólitos (tais como polietilenoimina) e materiais de verniz.13/24 provide the multilayer structure with one or more functional properties. The selection of primer or adhesive material may, however, be designed to introduce, strengthen or further reduce one or more properties associated with the structure with multiple layers as a whole or with one or more layers thereof. This property can be the ability to bend, elasticity, transparency, absorption, light transmission, permeability of gases or solvents, humectability, thermal resistance and others. The primer or adhesive layer comprises a material selected from polyurethane, epoxy, acrylate, hot melt adhesives, polyethylene (such as polyethyleneimine) and varnish materials.

[049] [049] Em algumas realizações, a In some achievements, the estrutura structure com with múltiplas multiple camadas compreende três camadas: layers comprises three layers: uma an camada layer de in substrato substrate (A), (THE), uma camada de CNC (B) e a CNC layer (B) and uma an camada layer de in cobertura roof (C), (Ç), cada qual conforme definido each as defined no at the presente, gift, conforme according exemplificado na Fig. 1. Em algumas exemplified in Fig. 1. In some realizações achievements , a , a

estrutura com múltiplas camadas compreende 3, 4, 5, 6, 7, 8,multilayer structure comprises 3, 4, 5, 6, 7, 8,

9 ou 9 or 10 10 camadas, de layers tal such forma que way that pelo menos uma camada at least one layer constitua constitute uma camada a layer de in substrato, substrate, conforme according definido, uma defined, a camada layer de in nanomaterial nanomaterial de in celulose, cellulose, conforme according definido, e uma defined, and a camada layer de cobertura cover , , conforme according definido. defined. Em algumas In some

realizações, o material de cada camada pode ser diferente do material de uma camada adjacente ou do material de uma ou mais camadas diferentes na estrutura com múltiplas camadas, ou pode ser diferente de um material de qualquer camada adjacente, mas idêntico ao material de camadas não adjacentes. Em uma estrutura com múltiplas camadas da forma ABCC, a camada de material A pode ser diferente de cada umaembodiments, the material of each layer may be different from the material of an adjacent layer or from the material of one or more different layers in the multilayer structure, or it may be different from the material of any adjacent layer, but identical to the non-layered material adjacent. In a multi-layer structure of the ABCC shape, material layer A may be different from each

Petição 870180060742, de 13/07/2018, pág. 16/35Petition 870180060742, of 07/13/2018, p. 16/35

14/24 das camadas de material C e cada uma das camadas de material C pode também ser diferente entre si, formando uma estrutura com múltiplas camadas da fórmula ABC1C2. Exemplos de múltiplas estruturas são fornecidos nas Figs. 3A-D.14/24 of the layers of material C and each of the layers of material C can also be different from each other, forming a multilayered structure of the formula ABC1C2. Examples of multiple structures are provided in Figs. 3A-D.

[050] Em algumas realizações, cada uma das camadas A e C é repetida duas vezes ou mais; nomeadamente, uma estrutura com múltiplas camadas pode apresentar-se na forma AABCC, ABCC, AABC, AABCBC ou ABCBCC, em que cada um dentre A, B e C é conforme definido no presente e, adicionalmente, em que cada par de camadas adjacentes pode ser associado diretamente ou por meio de primer ou camada ou filme adesivo. Em uma estrutura da forma AABCC, por exemplo, cada A pode ser diferente entre si e cada C pode ser diferente de outro C. Como as camadas de material A e C podem ser selecionadas a partir dos mesmos materiais, a estrutura com múltiplas camadas pode ser simétrica em volta da camada central B ou assimétrica.[050] In some embodiments, each of layers A and C is repeated twice or more; namely, a structure with multiple layers can be in the form of AABCC, ABCC, AABC, AABCBC or ABCBCC, where each of A, B and C is as defined herein and, in addition, each pair of adjacent layers can be associated directly or by means of primer or layer or adhesive film. In a structure of the form AABCC, for example, each A can be different from each other and each C can be different from another C. As the layers of material A and C can be selected from the same materials, the structure with multiple layers can be symmetrical around the central layer B or asymmetric.

[051] A estrutura com múltiplas camadas de acordo com o presente modelo pode apresentar-se na forma de folha ou folha moldada ou dobrada de material, conforme definido no presente. Quando apresentada na forma de folha de material, ela pode possuir qualquer tamanho e formato, pode ser impressa ou colorida, pode ser totalmente transparente ou opaca e pode ser tratada na superfície. A folha pode ser cortada, dobrada ou processada em qualquer formato, tamanho ou objeto, tal como bolso, invólucro, envelope ou recipiente que é formado com a folha, ou que compreende pelo menos um elemento ou característica que é elaborado com uma estrutura com múltiplas camadas de acordo com o presente modelo. Em algumas realizações, o objeto destina-se à embalagem de[051] The multilayer structure according to the present model can be in the form of a sheet or a molded or folded sheet of material, as defined herein. When presented as a sheet of material, it can have any size and shape, can be printed or colored, can be completely transparent or opaque and can be treated on the surface. The sheet can be cut, folded or processed into any shape, size or object, such as a pocket, wrapper, envelope or container that is formed with the sheet, or that comprises at least one element or feature that is made with a structure with multiple layers according to the present model. In some embodiments, the object is intended for the packaging of

Petição 870180060742, de 13/07/2018, pág. 17/35Petition 870180060742, of 07/13/2018, p. 17/35

15/24 produtos, alimentos, líquidos, produtos farmacêuticos ou qualquer material que necessite de isolamento ou proteção contra o meio ambiente, tal como gases, vapor d'água, certos comprimentos de onda de luz e outros efeitos ou agentes prejudiciais dos quais a estrutura com múltiplas camadas pode proteger (formando uma barreira impermeável).15/24 products, foods, liquids, pharmaceuticals or any material that needs insulation or protection from the environment, such as gases, water vapor, certain wavelengths of light and other harmful effects or agents of which the structure with multiple layers it can protect (forming an impermeable barrier).

[052] Devido às suas propriedades exclusivas, a folha pode ser utilizada como substituição para folhas de alumínio em materiais de embalagem. Como é conhecido na técnica, folhas de alumínio são amplamente utilizadas na embalagem de produtos, devido à sua capacidade de bloquear completamente a permeação de gases, água e luz, bem como devido à sua contribuição para a estabilidade mecânica da embalagem. Existem, entretanto, certas desvantagens para o uso de folhas de alumínio, principalmente com referência ao seu impacto ao meio ambiente, causado pela sua incapacidade de sofrer degradação e dificuldades associadas à reciclagem de embalagens que contêm alumínio. As propriedades de bloqueio da luz de alumínio também são consideradas uma desvantagem quando são necessárias embalagens transparentes. Outra desvantagem do alumínio é a sua capacidade de transmissão de calor, que não é desejada em aplicações como painéis isolados a vácuo, em que é necessária boa barreira contra gases, mas sem alta transferência de calor.[052] Due to its unique properties, the foil can be used as a replacement for aluminum foils in packaging materials. As is known in the art, aluminum foils are widely used in product packaging, due to their ability to completely block the permeation of gases, water and light, as well as due to their contribution to the mechanical stability of the packaging. There are, however, certain disadvantages to the use of aluminum foils, mainly with reference to their impact on the environment, caused by their inability to suffer degradation and difficulties associated with recycling aluminum-containing packaging. The light blocking properties of aluminum are also considered a disadvantage when transparent packaging is required. Another disadvantage of aluminum is its ability to transmit heat, which is not desired in applications such as vacuum insulated panels, in which a good gas barrier is required, but without high heat transfer.

[053] A estrutura em camadas de acordo com o presente modelo é substituição apropriada de alumínio, fornecendo um material que possui propriedades mecânicas e de barreira, com o benefício de ser reciclável e degradável, transparente para a luz, isolante térmico e poder ser fornecido na forma de camadas de barreira muito mais finas,[053] The layered structure according to the present model is an appropriate replacement for aluminum, providing a material that has mechanical and barrier properties, with the benefit of being recyclable and degradable, transparent to light, thermal insulating and can be supplied in the form of much thinner barrier layers,

Petição 870180060742, de 13/07/2018, pág. 18/35Petition 870180060742, of 07/13/2018, p. 18/35

16/2416/24

atingindo reaching as propriedades de the properties of barreira desejadas desired barriers (uma barreira (a barrier de 2 pm, from 2 pm, por exemplo, gera for example, it generates o nível The level de OTR desejado em of desired OTR in uma an estrutura structure na qual normalmente é which is usually utilizada used uma folha a leaf de in alumínio aluminum de 5 pm). [054] Segundo 5 pm). [054] Second alguns some aspectos, aspects, portanto, therefore, o O presente gift modelo fornece um model provides a artigo na forma de article in the form of estrutura structure com with múltiplas multiple camadas que consiste de layers consisting of três a sete camadas three to seven layers de in

material, em que a estrutura com múltiplas camadas possui a forma ABC e cada um dentre A, B e C é uma camada de material, em que:material, where the structure with multiple layers has the form ABC and each of A, B and C is a layer of material, in which:

[055] - a camada A é um substrato que compreende um material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso, material de membrana, material mineral, verniz e material metálico;[055] - layer A is a substrate comprising a material selected from polymeric material, paper or paper-based material, material based on polymer-coated paper, nanocellulose film, nanocellulose and polymer film, woven material , porous material, membrane material, mineral material, varnish and metallic material;

[056] - a camada B é um nanomaterial de celulose selecionado a partir de nanocristasis (CNC), celulose nanofibrilar (NFC), celulose microfibrilada (MFC), uma combinação de CNC e NFC, uma combinação de CNC e MFC e uma mistura de CNC com pelo menos um aditivo hidrossolúvel ou dispersível em água; e [057] - a camada C é uma camada de cobertura que compreende um material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso, material de membrana, material mineral, verniz e material metálico.[056] - layer B is a cellulose nanomaterial selected from nanocristasis (CNC), nanofibrillar cellulose (NFC), microfibrillated cellulose (MFC), a combination of CNC and NFC, a combination of CNC and MFC and a mixture of CNC with at least one water-soluble or water-dispersible additive; and [057] - layer C is a covering layer that comprises a material selected from polymeric material, paper or paper based material, material based on polymer coated paper, nanocellulose film, nanocellulose film and polymer , woven material, porous material, membrane material, mineral material, varnish and metallic material.

Petição 870180060742, de 13/07/2018, pág. 19/35Petition 870180060742, of 07/13/2018, p. 19/35

17/24 [058] Em algumas realizações, a camada do nanomaterial de celulose compreende 0,1% em peso a 3% em peso de impurezas do peso total da camada, em que as impurezas são selecionadas a partir de carboidratos e sais.17/24 [058] In some embodiments, the cellulose nanomaterial layer comprises 0.1% by weight to 3% by weight of impurities of the total weight of the layer, where the impurities are selected from carbohydrates and salts.

[059] Em algumas realizações, o artigo consiste de uma camada de CNC ou uma camada de uma mistura de CNC e pelo menos um aditivo, um substrato e uma camada de cobertura.[059] In some embodiments, the article consists of a layer of CNC or a layer of a mixture of CNC and at least one additive, a substrate and a covering layer.

[060] Em algumas realizações, o artigo consiste de uma camada de mistura de CNC e PVOH, um substrato e uma camada de cobertura.[060] In some embodiments, the article consists of a mixture layer of CNC and PVOH, a substrate and a covering layer.

[061] Em algumas realizações, cada uma dentre a camada A e a camada C é papel ou um material com base em papel.[061] In some embodiments, each of layer A and layer C is paper or a paper-based material.

[062] Em algumas realizações, cada uma dentre a camada A e a camada C é de material polimérico, material com base em papel revestido com polímero ou filme de nanocelulose e polímero.[062] In some embodiments, each of layer A and layer C is polymeric material, material based on paper coated with polymer or nanocellulose and polymer film.

[063] Em algumas realizações, a camada B compreende CNC e/ou NFC combinados com pelo menos um polímero selecionado a partir de PVOH, PVAc, EVOH, PVP, amido, chitosan, ácido poliacrílico, polietilenoimina, carboidratos, EVA e poliuretanos.[063] In some embodiments, layer B comprises CNC and / or NFC combined with at least one polymer selected from PVOH, PVAc, EVOH, PVP, starch, chitosan, polyacrylic acid, polyethyleneimine, carbohydrates, EVA and polyurethanes.

[064] Em algumas realizações, a quantidade do pelo menos um polímero varia de 0,1 a 99% em peso do material de nanocelulose.[064] In some embodiments, the amount of at least one polymer ranges from 0.1 to 99% by weight of the nanocellulose material.

[065] Em algumas realizações, o pelo menos um aditivo é um polímero ou aditivo selecionado a partir de plastificante, tensoativo, material particulado, pigmento, carboidrato, sal, material condutor e extrator de oxigênio.[065] In some embodiments, the at least one additive is a polymer or additive selected from plasticizer, surfactant, particulate material, pigment, carbohydrate, salt, conductive material and oxygen extractor.

Petição 870180060742, de 13/07/2018, pág. 20/35Petition 870180060742, of 07/13/2018, p. 20/35

18/24 [066] Em algumas realizações, o pelo menos um aditivo está presente em quantidade que varia de 1% a 20%.18/24 [066] In some embodiments, at least one additive is present in an amount ranging from 1% to 20%.

[067] Em algumas realizações, a camada B possui espessura de 100 nm a 20 pm.[067] In some embodiments, layer B is 100 nm thick at 20 pm.

[068] Em algumas realizações, cada uma das camadas A e C é de um material selecionado, independentemente entre si, a partir de polietileno, polipropileno, poliéster, álcool polivinílico, álcool etileno vinílico, poliamida, poliestireno, ácido poliláctico, póli-hidroxialcanoato, policaprolactona, póli-hidroxibutirato, acetato de polivinila, poliacrilonitrila, cloreto de polivinilideno, celulose, tereftalato de polietileno, cloreto de polivinila e policarbonato.[068] In some embodiments, each of layers A and C is of a material selected, independently from each other, from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid, polyhydroxyalkanoate , polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

[069] Em algumas realizações, uma ou as duas camadas A e C são de papelão revestido com polímero, em que o polímero é selecionado a partir de polietileno, polipropileno, poliéster, álcool polivinílico, álcool etileno vinílico, poliamida, poliestireno, ácido poliláctico, pólihidroxialcanoato, policaprolactona, póli-hidroxibutirato, acetato de polivinila, poliacrilonitrila, cloreto de polivinilideno, celulose, tereftalato de polietileno, cloreto de polivinila e policarbonato.[069] In some embodiments, one or both layers A and C are made of polymer-coated cardboard, in which the polymer is selected from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid , polyhydroxyalkanoate, polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

[070] Em algumas realizações, pelo menos uma das camadas A e C, independentemente ente si, é ou compreende um tecido.[070] In some embodiments, at least one of layers A and C, independently of itself, is or comprises a fabric.

[071] Em algumas realizações, as camadas A e B e/ou as camadas B e C são diretamente associadas entre si ou separadas por um material de interface selecionado a partir de material de primer e um material adesivo.[071] In some embodiments, layers A and B and / or layers B and C are directly associated with each other or separated by an interface material selected from a primer material and an adhesive material.

[072] Em algumas realizações, o artigo consiste[072] In some embodiments, the article consists of

Petição 870180060742, de 13/07/2018, pág. 21/35Petition 870180060742, of 07/13/2018, p. 21/35

19/24 de três camadas: uma camada de substrato, uma camada de CNC e uma camada de cobertura.19/24 three layers: a substrate layer, a CNC layer and a covering layer.

[073] Em algumas realizações, a camada de CNC consiste de uma combinação de CNC e PVOH.[073] In some embodiments, the CNC layer consists of a combination of CNC and PVOH.

[074] Em algumas realizações, a estrutura com múltiplas camadas possui forma selecionada a partir de AABCC, ABCC, AABC, AABCBC e ABCBCC, em que cada um dentre A, B e C é conforme definido no presente.[074] In some embodiments, the structure with multiple layers has a shape selected from AABCC, ABCC, AABC, AABCBC and ABCBCC, where each of A, B and C is as defined in the present.

[075] Em algumas realizações, o artigo é fornecido quando utilizado na embalagem de produtos, alimentos, líquidos e produtos farmacêuticos.[075] In some embodiments, the article is provided when used in the packaging of products, food, liquids and pharmaceutical products.

[076] O presente modelo fornece adicionalmente um artigo na forma de estrutura com múltiplas camadas que consiste de três a sete camadas de material, em que a estrutura com múltiplas camadas possui a forma ABC e cada um dentre A, B e C é uma camada de material, em que:[076] The present model additionally provides an article in the form of a multilayered structure consisting of three to seven layers of material, in which the multilayered structure has the shape ABC and each of A, B and C is a layer material, where:

[077] - a camada A é um substrato que compreende um material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso, material de membrana, material mineral, verniz e material metálico;[077] - layer A is a substrate that comprises a material selected from polymeric material, paper or paper based material, material based on polymer coated paper, nanocellulose film, nanocellulose and polymer film, woven material , porous material, membrane material, mineral material, varnish and metallic material;

[078] - a camada B é um nanomaterial de celulose selecionado a partir de nanocristais (CNC) e uma combinação de CNC com pelo menos um material ou aditivo hidrossolúvel ou dispersível em água, em que a camada é livre de material nanoparticulado metálico e celulose nanofibrilada (NFC); e [079] - a camada C é uma camada de cobertura[078] - layer B is a cellulose nanomaterial selected from nanocrystals (CNC) and a combination of CNC with at least one water-soluble or water-dispersible material or additive, in which the layer is free of metallic nanoparticulate material and cellulose nanofibrilated (NFC); and [079] - layer C is a cover layer

Petição 870180060742, de 13/07/2018, pág. 22/35Petition 870180060742, of 07/13/2018, p. 22/35

20/24 que compreende um material selecionado a partir de material polimérico, papel ou material com base em papel, material com base em papel revestido com polímero, filme de nanocelulose, filme de nanocelulose e polímero, material tecido, material poroso, material de membrana, material mineral, verniz e material metálico.20/24 comprising a material selected from polymeric material, paper or paper-based material, polymer-based paper-based material, nanocellulose film, nanocellulose and polymer film, woven material, porous material, membrane material , mineral material, varnish and metallic material.

DESCRIÇÃO DETALHADA DO MODELODETAILED DESCRIPTION OF THE MODEL

Exemplo 1Example 1

[080] [080] Estrutura Structure com with três camadas: three layers: [081] [081] - Camada - Layer A: THE: polietileno com polyethylene with baixa low densidade (LDPE) density (LDPE) - 20 μπ, tratado - 20 μπ, treated com Corona; with Corona; [082] [082] - Camada B - Layer B : camada de PVOH/CNC - 5 : PVOH / CNC layer - 5 μm; e μm; and [083] [083] - Camada - Layer C Ç polietileno com polyethylene with baixa low

densidade (LDPE) - 20 μη, tratado com Corona e revestido sobre o lado tratado com adesivo.density (LDPE) - 20 μη, treated with Corona and coated on the side treated with adhesive.

[084] A camada múltipla inclui Camada A/Camada B/Camada C.[084] The multiple layer includes Layer A / Layer B / Layer C.

[085] Método de preparação:[085] Preparation method:

[086] 1. O filme de LDPE (Camada A) foi tratado na superfície com corona;[086] 1. The LDPE film (Layer A) was treated on the surface with a corona;

[087] 2. a suspensão em água de PVOH/CNC foi revestida sobre a superfície tratada do LDPE, seguida por secagem completa (Camada B); e [088] 3. o filme de LDPE tratado com corona foi revestido com uma camada adesiva e laminado à Camada B, com o lado revestido com adesivo frontal à camada de PVOH/CNC (Camada C).[087] 2. the PVOH / CNC suspension in water was coated on the treated LDPE surface, followed by complete drying (Layer B); and [088] 3. the corona-treated LDPE film was coated with an adhesive layer and laminated to Layer B, with the side coated with adhesive front to the PVOH / CNC layer (Layer C).

[089] A estrutura com múltiplas camadas foi transparente, flexível e pôde ser adicionalmente laminada para incluir camadas adicionais para a produção de embalagens[089] The multilayer structure was transparent, flexible and could be further laminated to include additional layers for packaging production

Petição 870180060742, de 13/07/2018, pág. 23/35Petition 870180060742, of 07/13/2018, p. 23/35

21/24 rígidas ou flexíveis com boas capacidades de barreira. As camadas de LDPE forneceram capacidades de barreira contra água, vapor d'água e óleo. A camada interna de PVOH/CNC forneceu capacidades de barreira contra gases.21/24 rigid or flexible with good barrier capabilities. The LDPE layers provided barrier capabilities against water, water vapor and oil. The inner layer of PVOH / CNC provided gas barrier capabilities.

Exemplo [090] Example [090] 2 2 Estrutura com Structure with múltiplas camadas multiple layers (três (three camadas): layers): [091] [091] - Camada A: - Layer A: polipropileno - 30 polypropylene - 30 pm, pm, revestido coated com uma with one camada adesiva adhesive layer de fusão a quente hot melt (por (per exemplo, example, etileno ethylene vinil acetato); vinyl acetate); [092] [092] - Camada B: camada de PVOH/CNC - 5 pm; e - Layer B: PVOH / CNC layer - 5 pm; and [093] [093] - Camada C: - Layer C: polipropileno - 30 polypropylene - 30 pm, pm, revestido coated com uma with one camada adesiva adhesive layer de fusão a quente hot melt (por (per exemplo, example, etileno ethylene vinil acetato). vinyl acetate). [094] [094] A camada múltipla inclui Camada A/Camada The multiple layer includes Layer A / Layer B/Camada B / Layer C. Ç. [095] [095] Método de preparação: Preparation method: [096] [096] 1. Filme de polipropileno (Camada 1. Polypropylene film (Layer A) é A) is

revestido com adesivo de fusão a quente (por exemplo, etileno vinil acetato);coated with hot melt adhesive (eg ethylene vinyl acetate);

[097] 2. suspensão em água de PVOH/CNC é revestida sobre a camada de fusão a quente, seguida por secagem completa (Camada B); e [098] 3. filme de polipropileno, revestido com uma camada de fusão a quente, é laminado à Camada B, com o lado revestido com adesivo frontal à camada de PVOH/CNC (Camada C).[097] 2. PVOH / CNC suspension in water is coated over the hot melt layer, followed by complete drying (Layer B); and [098] 3. polypropylene film, coated with a hot melt layer, is laminated to Layer B, with the side coated with adhesive front to the PVOH / CNC layer (Layer C).

[099] A estrutura com múltiplas camadas é transparente, flexível e pode ser adicionalmente laminada a mais camadas para a produção de embalagens rígidas ou[099] The multilayer structure is transparent, flexible and can be additionally laminated to more layers for the production of rigid or

Petição 870180060742, de 13/07/2018, pág. 24/35Petition 870180060742, of 07/13/2018, p. 24/35

22/24 flexíveis com boas capacidades de barreira. As camadas de polipropileno fornecem capacidades de barreira contra água, vapor d'água e óleo. A camada interna de PVOH/CNC fornece capacidades de barreira contra gases e aprimora as propriedades mecânicas.22/24 flexible with good barrier capabilities. Polypropylene layers provide barrier capabilities against water, water vapor and oil. The PVOH / CNC inner layer provides gas barrier capabilities and improves mechanical properties.

[0100] As propriedades mecânicas das estruturas em camadas descritas no Exemplo 2 foram testadas por meio de testes de tensão, utilizando uma máquina Instron:[0100] The mechanical properties of the layered structures described in Example 2 were tested by means of stress tests, using an Instron machine:

[0101] - o módulo elástico aumenta em 40%-125% em comparação com a referência das camadas A e C laminadas entre si; e [0102] - o alongamento na quebra aumenta em 720% em comparação com a referência das camadas A e C laminadas entre si.[0101] - the elastic modulus increases by 40% -125% compared to the reference of layers A and C laminated to each other; and [0102] - the elongation at break increases 720% in comparison with the reference of layers A and C laminated to each other.

Exemplo 3 [0103] Estrutura com cinco camadas:Example 3 [0103] Structure with five layers:

[0104] - Camada A1: polietileno com baixa densidade (LDPE) - 20 pm;[0104] - Layer A1: low density polyethylene (LDPE) - 20 pm;

[0105] - Camada A2: papelão, revestido com LDPE;[0105] - Layer A2: cardboard, coated with LDPE;

[0106] - Camada A3: polietileno com baixa densidade (LDPE) - 15 pm, tratado com corona;[0106] - Layer A3: low density polyethylene (LDPE) - 15 pm, treated with corona;

[0107] - Camada B: camada de PVOH/CNC - 4 pm;[0107] - Layer B: PVOH / CNC layer - 4 pm;

[0108] - Camada C1: polietileno com baixa densidade (LDPE) - 15 pm, tratado com corona; e [0109] - Camada C2: polietileno com baixa densidade (LDPE).[0108] - Layer C1: low density polyethylene (LDPE) - 15 pm, treated with corona; and [0109] - Layer C2: low density polyethylene (LDPE).

[0110] A camada múltipla inclui Camada A1/Camada[0110] The multiple layer includes Layer A1 / Layer

A2/Camada B/Camada C1/Camada C2.A2 / Layer B / Layer C1 / Layer C2.

[0111] Método de preparação:[0111] Preparation method:

[0112] 1. O filme de LDPE (Camada A3) foi[0112] 1. The LDPE film (Layer A3) was

Petição 870180060742, de 13/07/2018, pág. 25/35Petition 870180060742, of 07/13/2018, p. 25/35

23/24 tratado na superfície com corona;23/24 treated on the surface with corona;

[0113] 2. a suspensão em água de PVOH/CNC foi revestida sobre a superfície tratada do LDPE, seguida por secagem completa (Camada B);[0113] 2. the PVOH / CNC suspension in water was coated on the treated LDPE surface, followed by complete drying (Layer B);

[0114] 3. o filme de LDPE tratado com corona foi[0114] 3. the corona-treated LDPE film was

laminado à laminated to Camada Layer B, com o B, with the lado side tratado com corona corona treated frontal à front to camada de layer of PVOH/CNC PVOH / CNC (Camada (Layer C1); C1); [0115] [0115] 4. LDPE 4. LDPE foi was extrudado sobre a superfície extruded on the surface de papelão cardboard (camada (layer A2); A2); [0116] [0116] 5. LDPE 5. LDPE foi was extrudado a partir extruded from do outro from the other

lado do papelão (camada A1);cardboard side (layer A1);

[0117] 6. a camada múltipla das camadas A3/B/C1 foi laminada à Camada A2; e [0118] 7. LDPE foi extrudado sobre a Camada C1 (camada C2).[0117] 6. the multiple layer of layers A3 / B / C1 was laminated to Layer A2; and [0118] 7. LDPE was extruded over Layer C1 (layer C2).

[0119] A presente estrutura com múltiplas camadas pode ser utilizada para embalagens rígidas. A camada de papelão forneceu estabilidade mecânica e as camadas de LDPE forneceram capacidades de barreira contra água, vapor d'água e óleo. A camada interna de PVOH/CNC forneceu capacidades de barreira contra gases:[0119] The present multilayer structure can be used for rigid packaging. The cardboard layer provided mechanical stability and the LDPE layers provided barrier capabilities against water, water vapor and oil. The inner layer of PVOH / CNC provided gas barrier capabilities:

[0120] - essa estrutura com a Camada B que possui espessura de cerca de 1,2 pm apresentou OTR de cerca de 4 sob umidade relativa de 80%;[0120] - this structure with Layer B, which has a thickness of about 1.2 pm, had an OTR of about 4 under 80% relative humidity;

[0121] - essa estrutura com a Camada B que possui espessura de cerca de 2,4 pm apresentou OTR de cerca de 2 sob umidade relativa de 80%;[0121] - this structure with Layer B, which has a thickness of about 2.4 pm, had an OTR of about 2 under 80% relative humidity;

[0122] - essa estrutura com a Camada B que possui espessura de cerca de 4 pm apresentou OTR de cerca de 1 sob umidade relativa de 80%; e[0122] - this structure with Layer B, which has a thickness of about 4 pm, presented OTR of about 1 under 80% relative humidity; and

Petição 870180060742, de 13/07/2018, pág. 26/35Petition 870180060742, of 07/13/2018, p. 26/35

24/24 [0123] - essa estrutura com a Camada B que possui espessura de cerca de 5 μm apresentou OTR de cerca de 1 sob umidade relativa de 80%.24/24 [0123] - this structure with Layer B, which is about 5 μm thick, had an OTR of about 1 under 80% relative humidity.

Claims

1. ARTICLE IN STRUCTURE FORM WITH MULTIPLE LAYERS consisting of three to seven layers of material, characterized by the multilayer structure having the form ABC, in which each of A, B and C is a layer of material and:

- layer A is a substrate comprising a material selected from polymeric material, paper or paper based material, material based on polymer coated paper, nanocellulose film, nanocellulose and polymer film, woven material, porous material , membrane material, mineral material, varnish and metallic material;

- layer B is a cellulose nanomaterial selected from nanocrystals (CNC) and a combination of CNC with at least one water-soluble or water-dispersible material or additive, in which the layer is free of metallic nanoparticulate material and nanofibrilated cellulose (NFC ); and

- layer C is a covering layer comprising a material selected from polymeric material, paper or paper based material, material based on polymer coated paper, nanocellulose film, nanocellulose and polymer film, woven material, porous material, membrane material, mineral material, varnish and metallic material.

2. ARTICLE, in wake up with the claim 1, featured by article consist in a CNC layer or a layer of combination CNC and fur less an additive or material, a substrate and a layer coverage. 3. ARTICLE, in wake up with the claim 1,

Petition 870180060742, of 07/13/2018, p. 28/35

2/3 characterized by the article consisting of a combination layer of CNC and PVOH, a substrate and a covering layer.

4. ARTICLE, according to claim 1, characterized in that each of layer A and layer C is paper or paper-based material.

5. ARTICLE, according to claim 1, characterized in that each of layer A and layer C is made of polymeric material, material based on paper coated with polymer or nanocellulose and polymer film.

6. ARTICLE, according to claim 1, characterized by layer B consisting of CNC combined with PVOH.

7. ARTICLE according to claim 6, characterized in that the amount of PVOH varies from 0.1 to 99% by weight of the CNC material.

8. ARTICLE, according to claim 1, characterized in that at least one additive or material is a polymer or additive selected from plasticizer, surfactant, particulate material, pigment, carbohydrate, salt, conductive material and oxygen extractor.

9. ARTICLE according to claim 1, characterized in that each of the layers A and C is of a material selected, independently from each other, from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid, polyhydroxyalkanoate, polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

Petition 870180060742, of 07/13/2018, p. 29/35

3/3

10. ARTICLE according to claim 1, characterized in that one or both layers A and C are made of polymer-coated cardboard, in which the polymer is selected from polyethylene, polypropylene, polyester, polyvinyl alcohol, ethylene vinyl alcohol, polyamide, polystyrene, polylactic acid, polyhydroxyalkanoate, polycaprolactone, polyhydroxybutyrate, polyvinyl acetate, polyacrylonitrile, polyvinylidene chloride, cellulose, polyethylene terephthalate, polyvinyl chloride and polycarbonate.

11. ARTICLE according to claim 1, characterized by layers A and B and / or layers B and C being directly associated with each other or separated by an interface material selected from a primer material and an adhesive material.

12. ARTICLE, according to claim 1, characterized by consisting of three layers: a substrate layer, a CNC layer and a covering layer.

13. ARTICLE, according to claim 1, characterized by the multilayer structure having a shape selected from AABCC, ABCC, AABC, AABCBC and ABCBCC, in which each of A, B and C is as defined in claim 1.

14. ARTICLE, according to claim 1, characterized in that it is used in the packaging of products, food, liquids and pharmaceutical products.