BR112014018242A2 - steel for the production of railway parts, railway crossings and diversions and method for producing said parts - Google Patents
steel for the production of railway parts, railway crossings and diversions and method for producing said partsInfo
- Publication number
- BR112014018242A2 BR112014018242A2 BR112014018242A BR112014018242A BR112014018242A2 BR 112014018242 A2 BR112014018242 A2 BR 112014018242A2 BR 112014018242 A BR112014018242 A BR 112014018242A BR 112014018242 A BR112014018242 A BR 112014018242A BR 112014018242 A2 BR112014018242 A2 BR 112014018242A2
- Authority
- BR
- Brazil
- Prior art keywords
- railway
- parts
- steel
- producing
- production
- Prior art date
Abstract
resumo patente de invenção: "aço para produção de peças para ferrovias, cruzamentos de ferrovias e desvios e método para produção das ditas peças". a presente invenção refere-se a um aço forjado para produção de peças para ferrovias, cruzamentos de ferrovias ou desvios de ferrovias caracterizado pelo fato de que compreende (em % em peso): 0,01 a 0,15% de carbono; no máximo 0,5% de silício; 10 a 15% de manganês; pelo menos 0,6 a 3,95% de molibdênio; opcionalmente um ou mais dos seguintes elementos: i. 0,05 a 0,2% de níquel e/ou ii. 0,05 a 0,2% de cobalto e/ou iii. 0,02 a 0,30% de cr e/ou iv. 0,05 a 0,2% de cobre; v. no máximo 5 ppm de h; vi. no máximo 0,20% de v; vii. no máximo 0,10% de nb; viii. no máximo 0,20% de ti e/ou zr; ix. no máximo 50 ppm de b; x. no máximo 250 ppm de n; xi. no máximo 0,2% de al; xii. no máximo 0,08% de s; xiii. no máximo 0,08% de p; xiv. no máximo 1,5% de w; e o saldo sendo ferro e as inevitáveis impurezas e a um método para produção do aço forjado e seu uso.Patent specification: "Steel for the production of railway parts, railway intersections and deviations and method for producing said parts". The present invention relates to a forged steel for the production of railway parts, railway crossings or railway diversions comprising (in weight%): 0.01 to 0.15% carbon; at most 0.5% silicon; 10 to 15% manganese; at least 0.6 to 3.95% molybdenum; optionally one or more of the following elements: i. 0.05 to 0.2% nickel and / or ii. 0.05 to 0.2% cobalt and / or iii. 0.02 to 0.30% of cr and / or iv. 0.05 to 0.2% copper; v. at most 5 ppm h; saw. at most 0.20% of v; vii. at most 0.10% nb; viii. at most 0.20% of ti and / or zr; ix. at most 50 ppm b; x. 250 ppm max n; xi at most 0.2% of al; xii. at most 0.08% of s; xiii. at most 0.08% p; xiv. maximum 1.5% of w; and the balance being iron and the inevitable impurities and a method for producing and using wrought steel.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP12152514 | 2012-01-25 | ||
US201261595014P | 2012-02-03 | 2012-02-03 | |
EP12153948 | 2012-02-03 | ||
PCT/EP2013/051517 WO2013110798A1 (en) | 2012-01-25 | 2013-01-25 | Steel for producing parts for railway, railway crossings and switches and method for producing said parts |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112014018242A2 true BR112014018242A2 (en) | 2017-07-04 |
Family
ID=48872901
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112014018242A BR112014018242A2 (en) | 2012-01-25 | 2013-01-25 | steel for the production of railway parts, railway crossings and diversions and method for producing said parts |
Country Status (11)
Country | Link |
---|---|
US (1) | US20150028165A1 (en) |
EP (1) | EP2807283A1 (en) |
JP (1) | JP2015510548A (en) |
KR (1) | KR20140119153A (en) |
CN (1) | CN104160058A (en) |
AU (1) | AU2013213544A1 (en) |
BR (1) | BR112014018242A2 (en) |
HK (1) | HK1203572A1 (en) |
MX (1) | MX2014008972A (en) |
RU (1) | RU2014134530A (en) |
WO (1) | WO2013110798A1 (en) |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101543898B1 (en) * | 2013-12-24 | 2015-08-11 | 주식회사 포스코 | Steel having excellent impact toughness of welding zone and welding property |
CA3071616A1 (en) | 2017-08-01 | 2019-02-07 | The Chamberlain Group, Inc. | System for facilitating access to a secured area |
US11055942B2 (en) | 2017-08-01 | 2021-07-06 | The Chamberlain Group, Inc. | System and method for facilitating access to a secured area |
JP6801747B2 (en) * | 2018-06-28 | 2020-12-16 | Jfeスチール株式会社 | Manufacturing method for austenitic rails |
CN113668299B (en) * | 2021-08-20 | 2023-04-25 | 宜兴市鑫煜科技有限公司 | Integral casting type frog structure for railway track train turnout and preparation process thereof |
Family Cites Families (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1178880B (en) * | 1961-10-21 | 1964-10-01 | Huettenwerk Oberhausen Ag | Process for the production of steel, wear-resistant, naturally hard single-material rails |
FR2407987A1 (en) * | 1977-11-03 | 1979-06-01 | Creusot Loire | AUSTENITIC STEEL WITH MOLDABLE AND WELDABLE MANGANESE |
JPS60128242A (en) * | 1983-12-15 | 1985-07-09 | Nippon Steel Corp | High manganese steel for nonmagnetic drill collar |
JP2533935B2 (en) * | 1989-06-10 | 1996-09-11 | 株式会社神戸製鋼所 | Method for producing high Mn non-magnetic steel having excellent SR embrittlement resistance, high strength and high toughness |
DE19735285C2 (en) * | 1997-08-14 | 2001-08-23 | Butzbacher Weichenbau Gmbh | Process for the production of a track part |
CN1061385C (en) * | 1998-06-19 | 2001-01-31 | 四川工业学院 | High-performance abrasion-resistant steel for switch tongue of high-speed or quasi high-speed railway |
GB0204558D0 (en) * | 2002-02-27 | 2002-04-10 | Allen Edgar Eng | Railway crossings, etc |
CN100484701C (en) * | 2005-10-17 | 2009-05-06 | 大连交通大学 | Forging (rolling) manufacture method of high-manganese steel frog centering rail |
CN100463992C (en) * | 2007-06-12 | 2009-02-25 | 燕山大学 | Forged (rolled) abrasive austenic permanganic steel and its manufacture |
-
2013
- 2013-01-25 BR BR112014018242A patent/BR112014018242A2/en not_active IP Right Cessation
- 2013-01-25 EP EP13702617.5A patent/EP2807283A1/en not_active Withdrawn
- 2013-01-25 US US14/373,741 patent/US20150028165A1/en not_active Abandoned
- 2013-01-25 AU AU2013213544A patent/AU2013213544A1/en not_active Abandoned
- 2013-01-25 JP JP2014553744A patent/JP2015510548A/en active Pending
- 2013-01-25 MX MX2014008972A patent/MX2014008972A/en unknown
- 2013-01-25 WO PCT/EP2013/051517 patent/WO2013110798A1/en active Application Filing
- 2013-01-25 CN CN201380012280.1A patent/CN104160058A/en active Pending
- 2013-01-25 KR KR1020147023571A patent/KR20140119153A/en not_active Application Discontinuation
- 2013-01-25 RU RU2014134530A patent/RU2014134530A/en not_active Application Discontinuation
-
2015
- 2015-04-22 HK HK15103913.1A patent/HK1203572A1/en unknown
Also Published As
Publication number | Publication date |
---|---|
JP2015510548A (en) | 2015-04-09 |
CN104160058A (en) | 2014-11-19 |
EP2807283A1 (en) | 2014-12-03 |
MX2014008972A (en) | 2015-03-19 |
WO2013110798A1 (en) | 2013-08-01 |
AU2013213544A1 (en) | 2014-08-28 |
RU2014134530A (en) | 2016-03-20 |
HK1203572A1 (en) | 2015-10-30 |
KR20140119153A (en) | 2014-10-08 |
US20150028165A1 (en) | 2015-01-29 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112014018242A2 (en) | steel for the production of railway parts, railway crossings and diversions and method for producing said parts | |
BR112014015715A8 (en) | high strength steel tube and high strength steel sheet excellent in low temperature deformation and toughness capability, and steel sheet production method | |
BR112015005216A2 (en) | ALLOY STEEL FOR HIGH STRENGTH AND LOW ALLOY STEEL | |
BR112013000436A8 (en) | steel plate with ni added and production method thereof | |
MX363648B (en) | Steel for oil well pipe, and method for producing same. | |
MX366958B (en) | Steel sheet for hot stamping, method for producing same, and hot-stamped steel material. | |
MX353669B (en) | Non-grain-oriented magnetic steel sheet. | |
MX2015014099A (en) | Hot-rolled steel sheet and production method therefor. | |
BR112013028960A2 (en) | hot stamped article, hot stamped article production method, energy absorbing member, and energy absorbing member production method | |
BR112014002875A2 (en) | high performance hot rolled steel plate which has excellent low temperature impact energy absorption and haz softening resistance, and production method thereof | |
UA117494C2 (en) | HIGH-QUALITY MANGANESE STEEL FOR PETROLEUM AND PIPES FOR PETROLEUM | |
UA109963C2 (en) | CATHANE STEEL, APPROVING CONSEQUENCES OF SEPARATION OF PARTS AFTER HOT FORMING AND / OR CUTTING IN TOOL, THAT HAS A HIGHER MACHINE | |
BR112014014191A2 (en) | corrosion resistant high strength austenitic alloys | |
BR112019025042A2 (en) | LAMINATED STEEL FOR SPRING STEEL | |
BR112014003519A2 (en) | steel plate with ni added and production method thereof | |
MX363411B (en) | Steel for bolts, bolt, and method for producing bolt. | |
MY176531A (en) | Austenitic stainless clad steel plate and method for producing thereof | |
ES2422456T3 (en) | High strength corrosion resistant alloy for oil extraction applications | |
MX2014001644A (en) | Steel oil well pipe having excellent sulfide stress cracking resistance. | |
MX2018005059A (en) | Non-quenched and tempered wire rod having excellent cold workability and manufacturing method therefor. | |
IN2015DN00283A (en) | ||
MX2015016224A (en) | Heat-treated steel material and method for producing same. | |
MX2017016905A (en) | Corrosion resistant steel, method for producing said steel and its use thereof. | |
MX2014001872A (en) | Spring steel and spring. | |
MX2015006992A (en) | Steel material and shock-absorbent member. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B08F | Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette] | ||
B08K | Patent lapsed as no evidence of payment of the annual fee has been furnished to inpi [chapter 8.11 patent gazette] |