BG113343A - Reinforced packaging film - Google Patents

Reinforced packaging film Download PDF

Info

Publication number
BG113343A
BG113343A BG113343A BG11334321A BG113343A BG 113343 A BG113343 A BG 113343A BG 113343 A BG113343 A BG 113343A BG 11334321 A BG11334321 A BG 11334321A BG 113343 A BG113343 A BG 113343A
Authority
BG
Bulgaria
Prior art keywords
layer
strips
width
thickness
film
Prior art date
Application number
BG113343A
Other languages
Bulgarian (bg)
Inventor
Александър Евстатиев
Георгиев Евстатиев Александър
Георги Евстатиев
Евстатиев Евстатиев Георги
Original Assignee
"Елпласт" Еоод
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by "Елпласт" Еоод filed Critical "Елпласт" Еоод
Priority to BG113343A priority Critical patent/BG113343A/en
Priority to PCT/BG2021/000016 priority patent/WO2022192970A1/en
Publication of BG113343A publication Critical patent/BG113343A/en

Abstract

The present invention relates to a reinforced packaging film. The film finds application for manual or automated packaging of goods. The film consists of two layers, as the first layer is a standard flat stretch film and the second layer consists of two or more strips of variable thickness and width, the two long sides of each strip have a sinusoidal shape, the width and thickness of the strips varies along their entire length in a sinusoidal relationship. The strips of the second layer are placed on the first layer along its length and are adhered to each other as a result of contact between the adhering surfaces of the first layer and the second layer. The width of the strips is in the range of 21 mm to 50 mm, their thickness is in the range of 5 µm to 15 µm, and the ratio between the width and thickness of a strip is in the range of 1400:1 to 10 000:1.

Description

ПОДСИЛЕНО ОПАКОВЪЧНО ФОЛИО ОписаниеREINFORCED PACKAGING FOIL Description

Област на техникатаField of technique

Настоящото изобретение се отнася до подсилено опаковъчно фолио. Фолиото намира приложение за ръчно или автоматизирано опаковане на стоки, като транспортна опаковка. Основното приложение на фолиото е като опаковъчно фолио на палети с готова продукция, за постигане на стабилна транспортна единица (палет).The present invention relates to a reinforced packaging film. The foil is used for manual or automated packaging of goods, such as transport packaging. The main application of the film is as a packaging film on pallets with finished products, to achieve a stable transport unit (pallet).

Предшестващо състояние на техникатаPrior art

От практиката е известно, че за опаковане на различни по вид и размер стоки се използва опаковъчно фолио, което още се нарича стреч фолио. То е тънко, леко и при прилагане се разтяга и се залепва около повърхността, около която се обвива.It is known from practice that packaging film, which is also called stretch film, is used for packaging goods of different types and sizes. It is thin, light and when applied it stretches and sticks around the surface it wraps around.

В промишлеността опаковането на стоките е автоматизиран процес, при който е възможно фолиото да се разкъса както по време на опаковането на стоките, така и при тяхното съхранение и транспорт, поради което е важно фолиото да е здраво.In industry, the packaging of goods is an automated process where it is possible for the film to tear both during the packaging of the goods and during their storage and transport, therefore it is important that the film is strong.

Известни са много опити за решаване на този проблем. Един от тях е използването на фолио с по-голяма дебелина, което обаче води до по-трудна обработка, по-голямо тегло на опакованите продукти и до повече разходи.Many attempts to solve this problem are known. One of them is the use of film with a greater thickness, which, however, leads to more difficult processing, greater weight of the packaged products and more costs.

ЕР 3 160 728 В1 описва неперфорирано подсилено стреч фолио, което се състои от основен филм е дебелина в диапазона от 3 pm до 18 pm и от 5 до 100 подсилващи ленти, фиксирани върху поне една повърхност на основния филм, като широчината на всяка подсилваща лента е в диапазона от 1 mm до 17 mm. В този вариант, лентите не се променят съществено по дължина и са постоянни по широчина, дебелина и форма, тоест тяхното напречното им сечение е относително постоянно по цялата дължина. Въпреки че участъците, върху които са разположени подсилващите ленти са подсилени, останалата част от филма не е подсилена, като е възможно лесно разкъсване в зоната, в която се намират краищата на подсилващите ленти.EP 3 160 728 B1 describes a non-perforated reinforced stretch film which consists of a base film having a thickness in the range of 3 pm to 18 pm and from 5 to 100 reinforcing strips fixed on at least one surface of the base film, the width of each reinforcing strip being is in the range of 1 mm to 17 mm. In this embodiment, the strips do not change significantly in length and are constant in width, thickness and shape, that is, their cross-section is relatively constant along the entire length. Although the areas where the reinforcing strips are located are reinforced, the rest of the film is not reinforced, and easy tearing is possible in the area where the ends of the reinforcing strips are located.

Техническа същност на изобретениетоTechnical essence of the invention

Задачата на настоящото изобретение е да се създаде тънко и разтегливо подсилено стреч фолио. Това фолио има повишена здравина и равномерно разпределение на теглото, което води до повишени работни характеристики като равномерно разпъване, равномерно разпределение на якостните показатели по дължина и широчина.The object of the present invention is to create a thin and stretchable reinforced stretch film. This film has increased strength and uniform weight distribution, which leads to increased performance characteristics such as uniform stretching, uniform distribution of strength indicators along the length and width.

Подсиленото опаковъчно фолио се състои от два слоя:The reinforced packaging film consists of two layers:

- първи слой, който представлява стандартно плоско стреч фолио;- first layer, which is a standard flat stretch film;

- втори слой, който се състои от две или повече ленти с променлива дебелина и широчина, двете дълги страни на всяка лента имат синусоидална (вълнообразна) форма;- second layer, which consists of two or more strips of variable thickness and width, the two long sides of each strip having a sinusoidal (wave-like) shape;

- широчината на лентите е променлива по цялата им дължина по синусоидална зависимост,- the width of the strips is variable along their entire length according to a sinusoidal dependence,

- дебелината на лентите е променлива по цялата им дължина по синусоидална зависимост;- the thickness of the strips is variable along their entire length according to a sinusoidal dependence;

- лентите, които образуват втория слой са разположени върху първия слой по неговата дължина, като първият слой и вторият слой са притиснати един към друг и са залепени един за друг в резултат на контакта между прилепващите повърхности на първия слой и на втория слой;- the strips that form the second layer are located on the first layer along its length, the first layer and the second layer are pressed against each other and are glued to each other as a result of the contact between the adhesive surfaces of the first layer and the second layer;

- широчината на лентите, които образуват втория слой е в диапазона от 21 mm до 50 mm;- the width of the strips that form the second layer is in the range from 21 mm to 50 mm;

- дебелината на лентите, които образуват втория слой е в диапазона от 5 pm до 15 pm;- the thickness of the strips that form the second layer is in the range from 5 pm to 15 pm;

- съотношението между широчината и дебелината на една лента е в диапазона 1400:1 до 10 000:1.- the ratio between the width and thickness of a strip is in the range of 1400:1 to 10,000:1.

Описание на приложените фигуриDescription of attached figures

На Фигура 1 е показан един пример за подсилено фолио с две ленти.Figure 1 shows an example of a reinforced film with two strips.

На Фигура 2 е показан един пример за подсилено фолио с три ленти.Figure 2 shows an example of a reinforced film with three strips.

Примери за изпълнениеImplementation examples

На Фигура 1 е илюстриран пример за подсилено фолио с две ленти, а на Фигура 2 е илюстриран пример за подсилено фолио с три ленти. Първият слой А е стандартно плоско стреч фолио с дебелина 10 pm. Вторият слой В се състои от две ленти с променлива дебелина и широчина, като дебелината и широчината на двете ленти са променливи по цялата им дължина по синусоидална зависимост. Двете дълги страни на всяка лента 2 имат синусоидална (вълнообразна) форма. Лентите В, които образуват вторият слой са разположени върху първия слой А по неговата дължина, като първият слой А и вторият слой са притиснати един към друг и са залепени един за друг в резултат на контакта между прилепващите повърхности на първия слой А и на втория слой В. Широчината на двете ленти В, които образуват втория слой е в диапазона от 21 mm до 30 mm. Дебелината на лентите В е в диапазона от 5 pm до 7 pm В резултат на постоянно променящите се широчина и дебелина на лентите В, напречното сечение на лентите В също е постоянно променящо се по цялата дължина на лентите, по синусоидална зависимост.Figure 1 illustrates an example of a reinforced foil with two strips, and Figure 2 illustrates an example of a reinforced foil with three strips. The first layer A is a standard flat stretch film with a thickness of 10 pm. The second layer B consists of two strips of variable thickness and width, the thickness and width of the two strips being variable along their entire length in a sinusoidal relationship. The two long sides of each strip 2 have a sinusoidal (wavy) shape. The strips B which form the second layer are located on the first layer A along its length, the first layer A and the second layer being pressed against each other and glued to each other as a result of the contact between the adhesive surfaces of the first layer A and the second layer B. The width of the two B strips that form the second layer is in the range of 21 mm to 30 mm. The thickness of the B strips is in the range of 5 pm to 7 pm As a result of the continuously varying width and thickness of the B strips, the cross section of the B strips is also continuously varied along the entire length of the strips, following a sinusoidal dependence.

Настоящото изобретение се отнася до подсилено опаковъчно фолио, което включва различни варианти. Всяка една конкретна стойност за дадена характеристика може да се комбинира с всяка една конкретна стойност за друга характеристика, като всички възможни комбинации от отделните конкретни стойности са предвидени да попадат в обхвата на настоящото изобретение.The present invention relates to a reinforced packaging film, which includes various variants. Any particular value for a given characteristic may be combined with any particular value for another characteristic, and all possible combinations of the individual particular values are intended to fall within the scope of the present invention.

Широчината на първия слой 1 на опаковъчното фолио е в диапазона от 250 mm до 600 mm, като например 250 mm, 300 mm, 350 mm, 400 mm, 420 mm, 450 mm. 500 mm, 500 mm, 550 mm и 600 mm.The width of the first layer 1 of the packaging film is in the range of 250 mm to 600 mm, such as 250 mm, 300 mm, 350 mm, 400 mm, 420 mm, 450 mm. 500mm, 500mm, 550mm and 600mm.

Дебелината на първия слой 1 на опаковъчното фолио е в диапазона от 5 до 23 pm, като например 5 pm, 7 pm, 9 pm, 10 pm, 12 pm, 15 pm, 18 pm, 20 pm, 22 рпи 23 pm.The thickness of the first layer 1 of the packaging film is in the range of 5 to 23 pm, such as 5 pm, 7 pm, 9 pm, 10 pm, 12 pm, 15 pm, 18 pm, 20 pm, 22 pm and 23 pm.

Броят на лентите 2, които образуват втория слой е от 2 до 25, като например 2, 3, 4, 5, 6, 7, 8,9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24 и 25.The number of strips 2 that form the second layer is from 2 to 25, such as 2, 3, 4, 5, 6, 7, 8,9, 10, 11, 12, 13, 14, 15, 16, 17, 18 , 19, 20, 21, 22, 23, 24 and 25.

Широчината на лентите 2, които образуват втория слой е в диапазона от 21 mm до 50 mm. В някои примери, широчината на лентите 2 може да бъде в диапазона от 23 mm до 45 mm, като например 23, 24, 25, 30, 35, 40, 45 mm.The width of the strips 2 which form the second layer is in the range from 21 mm to 50 mm. In some examples, the width of the strips 2 may be in the range of 23 mm to 45 mm, such as 23, 24, 25, 30, 35, 40, 45 mm.

Дебелината на лентите 2, които образуват втория слой е в диапазона от 5 pm до 15 цш, като например от 7 pm до 15 pm, като например 5, 6, 7, 8, 9, 10, 11, 12, 13, 15 pm.The thickness of the strips 2 that form the second layer is in the range from 5 pm to 15 pm, such as from 7 pm to 15 pm, such as 5, 6, 7, 8, 9, 10, 11, 12, 13, 15 pm .

Съотношението между широчината на една лента В и нейната дебелина е в диапазона 1400:1 до 10 000:1, като например от 1400:1 до 9000:1, 1500:1 до 1800:1, 1600:1 до 2100:1 и други.The ratio between the width of a band B and its thickness is in the range of 1400:1 to 10,000:1, such as 1400:1 to 9000:1, 1500:1 to 1800:1, 1600:1 to 2100:1, and others .

В един вариант, на изображението от Фигура 1, дългите страни на лентите В от втория слой имат вълнообразна форма така, че пиковете на вълните от едната страна да са разположени срещу пиковете на вълните от другата страна, а падовете на вълните от едната страна са разположени срещу падовете на вълните от другата страна.In one embodiment, in the image of Figure 1, the long sides of the B strips of the second layer have a wavy shape so that the peaks of the waves on one side are located opposite the peaks of the waves on the other side, and the troughs of the waves on one side are located against the falls of the waves on the other side.

Конкретно посоченият вариант на фолио, изработено с посочените параметри и характеристики представлява класически пример за тънко и здраво стреч фолио, което има високи якостни показатели както в надлъжно, така и напречно направление.Specifically, the specified version of a film made with the specified parameters and characteristics represents a classic example of a thin and strong stretch film that has high strength indicators in both longitudinal and transverse directions.

Използване на изобретениетоUse of the invention

Настоящото изобретение се отнася до подсилено опаковъчно фолио. Фолиото намира приложение за ръчно или автоматизирано опаковане на стоки, като транспортна опаковка. Основното приложение на фолиото е като опаковъчно фолио на палети с готова продукция, за постигане на стабилна транспортна единица (палет). Настоящото изобретение превъзхожда другите подобни фолия чрез високата си технологичност, висока степен на безопасност по време на употреба, както и чрез равномерното разпределение на относителното тегло на подсилващите елементи, което се постига, чрез специфичното им постоянно изменящо се сечение. Това води до високи якостни показатели.The present invention relates to a reinforced packaging film. The foil is used for manual or automated packaging of goods, such as transport packaging. The main application of the film is as a packaging film on pallets with finished products, to achieve a stable transport unit (pallet). The present invention surpasses other similar foils by its high manufacturability, high degree of safety during use, as well as by the uniform distribution of the relative weight of the reinforcing elements, which is achieved by their specific constantly changing section. This leads to high strength indicators.

Claims (1)

1. Подсиленото опаковъчно фолио, което се състои от два слоя, като първият слой А е стандартно плоско стреч фолио, а вторият слой се състои от две или повече ленти В, характеризиращо се с това, че вторият слой се състои от две или повече отделни ленти В е променлива дебелина и широчина; двете дълги страни на всяка лента В имат синусоидална (вълнообразна) форма;1. The reinforced packaging film which consists of two layers, the first layer A being a standard flat stretch film and the second layer consisting of two or more strips B, characterized in that the second layer consists of two or more separate bands B is variable thickness and width; the two long sides of each band B have a sinusoidal (wavy) shape; широчината на лентите В е променлива по цялата им дължина по синусоидална зависимост;the width of the bands B is variable along their entire length according to a sinusoidal dependence; дебелината на лентите В е променлива по цялата им дължина по синусоидална зависимост;the thickness of strips B is variable along their entire length according to a sinusoidal dependence; лентите В, които образуват втория слой са разположени върху първия слой А по неговата дължина, като първият слой А и вторият слой са притиснати един към друг и са залепени един за друг в резултат на контакта между прилепващите повърхности на първия слой А и на втория слой;the strips B forming the second layer are located on the first layer A along its length, the first layer A and the second layer are pressed against each other and are glued to each other as a result of the contact between the adhesive surfaces of the first layer A and the second layer ; широчината на лентите В, които образуват втория слой е в диапазона от 21 mm до 50 mm;the width of the strips B that form the second layer is in the range of 21 mm to 50 mm; дебелината на лентите В, които образуват втория слой е в диапазона от 5 μηι до 15 pm;the thickness of the strips B that form the second layer is in the range of 5 μηι to 15 pm; съотношението между широчината на дебелината на една лента В е в диапазона 1400:1 до 10 000:1the width to thickness ratio of one B band is in the range of 1400:1 to 10,000:1
BG113343A 2021-03-15 2021-03-15 Reinforced packaging film BG113343A (en)