Description

       

   <EMI ID=1.1>  

  
Cette invention est relative au problème très particulier de la distribution et du débit de la bière sous pres&#65533; sion à domicile, c'est-à-dire en tous endroits autres que les débits publics, ceux-ci n'étant néanmoins pas systématiquement exclus. 

  
La boite métallique, comme emballage pour la bière,  <EMI ID=2.1> 

  
évidemment que ladite boite doit, de la manière traditionnelle pour l'emballage de tous produits liquides, répondre aux conditions d'étanchéité, de résistance aux différentes manutentions  et manipulations et être parfaitement neutre à l'égard du 

  
 <EMI ID=3.1> 

  
Néanmoins, si le problème d'ordre pratique semble  ainsi résolu, il faut admettre que l'économie générale de la  distribution du débit de la bière sous pression à domicile 

  
est surtout conditionnée par les récipients ou emballages, les- ; quels doivent répondre à des critères apparemment contradic-

  
 <EMI ID=4.1> 

  
tique et à rythme accéléré et, d'autre part, satisfaire aux  conditions impératives de sécurité et d'une stricte économie

  
en raison même de la quantité considérable de tels emballages susceptibles d'être mis en oeuvre pour un nombre infiniment

  
plus restreint d'appareillages débiteurs, avec cette condition supplémentaire encore que lesdits appareillages sont pratique-  ment permanents, tandis que les emballages seront généralement 

  
 <EMI ID=5.1> 

  
faut tenir compte non seulement des sollicitations accidentelles, comme dans tout emballage, mais également des limites de ares= sion intérieure qui, en 1* occurrence, sont relativement larges attendu qu'au départ la bière se trouve enclavée dans -une  enceinte entièrement fermée soumise à la pression atmosphérique ou à une pression voisine de celle-ci, tandis que, pour le dé-

  
 <EMI ID=6.1> 

  
tairement ou par inadvertance, placer un tel emballage avant ou après une ou plusieurs opérations de débit, soit dans  l'ambiance froide d'un réfrigérateur, soit dans une 'ambiance <EMI ID=7.1>  ou de cuisine. Il faut également, dans le cadre de la sécurité, considérer, chimiquement parlant, une neutralité totale entre les constituants de la bière et les constituants des produits/ de recouvrement des surfaces intérieures de l'emballage et,

  
 <EMI ID=8.1> 

  
 <EMI ID=9.1> 

  
à appliquer, sur la face de ladite tôle destinée 

  
à former la paroi intérieure de la boite métallique, une couche 

  
 <EMI ID=10.1> 

  
à appliquer, sur la face de ladite tôle destinée 

  
à former la paroi intérieure des fonds, une couche d'accrochage  <EMI ID=11.1> 

  
à sertir sur le corps le fond inférieur? à appliquer; sur toute la partie intérieure voisiné  de la couture, respectivement de la ligne de soudure du corps, une couche de rechampissage formée d'une solution de chlorure

  
 <EMI ID=12.1> 

  
à appliquer, sur toutes les surfaces'intérieures de la boîte métallique ainsi constituée, une couche de recouvrement également constituée par une solution de chlorure de poly-

  
 <EMI ID=13.1> 

  
temps relativement très court la composition de cette couche de recouvrement à la température de polymérisation 

  
Les caractéristiques technologiques prérappelêes conviennent plus particulièrement pour la réalisation d'un corps  de boîte cylindrique d'une capacité de 4 3 litres 800, la. 

  
 <EMI ID=14.1> 

  
 <EMI ID=15.1> 

  
Pour l'exécution des fonds adaptables audit corps de boîte. cylindrique, il est préconisé de faire usage de fer  blanc électrolytique dont le coefficient de dureté est .de l'ordre de 57 à 65 unités Rockwell, 1* épaisseur de métal étant

  
 <EMI ID=16.1> 

  
du type à fond et ciel sertis, avec interposition d'un joint d'étanchéité, lesdits ciel et fond étant, en l'occurrence,  caractérisés par un bord annulaire rentrant de l'ordre de   <EMI ID=17.1> 

  
Les emballages selon l'invention sont encore carac-

  
 <EMI ID=18.1> 

  
bordés par une moulure périphérique profonde coopérant à une.., plus grands résistance de la partis adjacente au sertissage  et réduisant sensiblement le diamètre du disque disposé dans

  
un même plan; la profondeur de ladite moulure périphérique,  respectivement la profondeur de sa partie cylindrique marginale, sont variables au prorata de la conformation de la- partie 

  
 <EMI ID=19.1> 

  
défini par le disque délimité par ladite moulure périphérique--  le niveau du bord limitrophe de l'ouverture centrale du fond  supérieur de l'emballage est inférieur à celui du plan du  disque délimité par la moulure périphérique; le niveau du bord' 

  
 <EMI ID=20.1> 

  
d*une part, par le bord limitrophe périphérique de l'orifice  central du fond supérieur et d'autre part par le bord marginal  supérieur du sertissage dudit fond sur le corps du récipient  <EMI ID=21.1>  oeuvre, dans l'un et 1[deg.]autre cas, d'un appareil de soutirage donné ou unique; le profil convexe de la partie centrale du 

  
 <EMI ID=22.1> 

  
lors du remplissage de l'emballage, et plus particulièrement lors du choc.', auquel est soumis l'emballage rempli avant la fermeture par un bouchon étanche; l'emballage,en vue de pouvoir résister  à des pressions intérieures résultant de températures de 1* ordre de 50[deg.] C, est réalisé à l'aide d'une épaisseur de tôle

  
 <EMI ID=23.1> 

  
 <EMI ID=24.1> 

  
consiste en l'application spécifique, pour l'exécution des 

  
 <EMI ID=25.1> 

  
 <EMI ID=26.1> 

  
plus particulièrement de telles boîtes ou récipients métalliques 

  
 <EMI ID=27.1> 

  
 <EMI ID=28.1> 

  
 <EMI ID=29.1> 

  
 <EMI ID=30.1> 

  
 <EMI ID=31.1> 

  
 <EMI ID=32.1> 

  
 <EMI ID=33.1> 

  
suffisante pour atteindre, dans le produit laminé à froid et  recuit, ledit niveau de limite élastique, l'usage de ladite tôle  étant combiné avec l'utilisation d'un vernis protecteur.,

  
On voit donc que, pour résoudre le problème spécifique 

  
 <EMI ID=34.1> 

  
 <EMI ID=35.1> 

  
 <EMI ID=36.1>  gardant des possibilités suffisantes de sertissage;  <EMI ID=37.1>  sation de couches de vernis protecteur.- 

  
 <EMI ID=38.1> 

  
 <EMI ID=39.1>   <EMI ID=40.1> 

  
aucune déformation préjudiciable, lesdites boites métalliques

  
 <EMI ID=41.1> 

  
récipients expérimentés contenaient de la bière mise sous

  
 <EMI ID=42.1> 

  
à la température ambiante, la bière a pu être débitée sous 

  
 <EMI ID=43.1> 

  
Une réalisation est décrite ci-après et schématisée

  
 <EMI ID=44.1>  la figure 1 représente en vue de face un emballage  selon l'invention équipé d'un dispositif distributeur de bière <EMI ID=45.1>  la figure 2 représente l'emballage métallique selon l'invention en demi-vue de face et en demi-coupe radiale; la figure 3 représente à échelle agrandie la partie  <EMI ID=46.1> 

  
Dans cette exécution est représenté l'emballage 

  
 <EMI ID=47.1> 

  
sous pression. L'emballage proprement dit est constitué par

  
 <EMI ID=48.1> 

  
 <EMI ID=49.1> 

  
périphérique, respectivement [pound]-7.* 

  
Le fond supérieur présente un trou central 8 dont 

  
 <EMI ID=50.1> 



   <EMI ID = 1.1>

  
This invention relates to the very particular problem of the distribution and flow of beer under pres &#65533; at home, that is to say in all places other than public debits, these are not however systematically excluded.

  
The metal box, as packaging for beer, <EMI ID = 2.1>

  
obviously that said box must, in the traditional way for the packaging of all liquid products, meet the conditions of sealing, resistance to different handling and handling and be perfectly neutral with regard to the

  
 <EMI ID = 3.1>

  
Nevertheless, if the practical problem seems thus solved, it must be admitted that the general economy of the distribution of the flow of beer under pressure at home

  
is mainly conditioned by the containers or packaging, the-; which must meet seemingly contradictory criteria

  
 <EMI ID = 4.1>

  
tick and at an accelerated rate and, on the other hand, meet the imperative conditions of safety and strict economy

  
because of the considerable quantity of such packaging capable of being used for an infinitely many

  
more restricted of debtor apparatus, with the further condition that said apparatus is practically permanent, while the packaging will generally be

  
 <EMI ID = 5.1>

  
It is necessary to take into account not only the accidental stresses, as in any packaging, but also the limits of internal ares = sion which, in 1 * case, are relatively wide since at the beginning the beer is enclosed in a completely closed enclosure subjected at atmospheric pressure or at a pressure close to it, while, for de-

  
 <EMI ID = 6.1>

  
inadvertently or inadvertently, placing such packaging before or after one or more debit operations, either in the cold environment of a refrigerator, or in an <EMI ID = 7.1> or kitchen environment. In the context of safety, it is also necessary to consider, chemically speaking, a total neutrality between the constituents of the beer and the constituents of the products / covering of the interior surfaces of the packaging and,

  
 <EMI ID = 8.1>

  
 <EMI ID = 9.1>

  
to be applied on the face of said sheet intended

  
to form the inner wall of the metal box, a layer

  
 <EMI ID = 10.1>

  
to be applied on the face of said sheet intended

  
to form the inner wall of the funds, a bonding layer <EMI ID = 11.1>

  
to crimp the lower bottom on the body? to apply; on the entire inner part near the seam, respectively the weld line of the body, a recoat layer formed of a chloride solution

  
 <EMI ID = 12.1>

  
to apply, to all the interior surfaces of the metal box thus formed, a covering layer also constituted by a solution of poly- chloride.

  
 <EMI ID = 13.1>

  
relatively very short time the composition of this covering layer at the polymerization temperature

  
The prérappelêes technological characteristics are more particularly suitable for producing a cylindrical box body with a capacity of 43 liters 800, the.

  
 <EMI ID = 14.1>

  
 <EMI ID = 15.1>

  
For the execution of backdrops adaptable to said box body. cylindrical, it is recommended to use electrolytic tinplate with a hardness coefficient of the order of 57 to 65 Rockwell units, the thickness of the metal being

  
 <EMI ID = 16.1>

  
of the type with crimped bottom and top, with interposition of a seal, said top and bottom being, in this case, characterized by an annular edge re-entering of the order of <EMI ID = 17.1>

  
The packaging according to the invention is still characterized

  
 <EMI ID = 18.1>

  
bordered by a deep peripheral molding cooperating with a .., greater resistance of the parties adjacent to the crimping and significantly reducing the diameter of the disc disposed in

  
the same plan; the depth of said peripheral molding, respectively the depth of its marginal cylindrical part, are variable in proportion to the conformation of the part

  
 <EMI ID = 19.1>

  
defined by the disc delimited by said peripheral molding - the level of the bordering edge of the central opening of the upper bottom of the packaging is lower than that of the plane of the disc delimited by the peripheral molding; edge level '

  
 <EMI ID = 20.1>

  
on the one hand, by the peripheral bordering edge of the central opening of the upper base and on the other hand by the upper marginal edge of the crimping of said base on the body of the container <EMI ID = 21.1> work, in one and 1 [deg.] Other case, of a given or single withdrawal device; the convex profile of the central part of the

  
 <EMI ID = 22.1>

  
during filling of the packaging, and more particularly during impact. ', to which the filled packaging is subjected before being closed by a sealed cap; the packaging, in order to be able to withstand internal pressures resulting from temperatures of the order of 50 [deg.] C, is carried out using a sheet thickness

  
 <EMI ID = 23.1>

  
 <EMI ID = 24.1>

  
consists of the specific application, for the execution of

  
 <EMI ID = 25.1>

  
 <EMI ID = 26.1>

  
more particularly such metal boxes or containers

  
 <EMI ID = 27.1>

  
 <EMI ID = 28.1>

  
 <EMI ID = 29.1>

  
 <EMI ID = 30.1>

  
 <EMI ID = 31.1>

  
 <EMI ID = 32.1>

  
 <EMI ID = 33.1>

  
sufficient to reach, in the cold-rolled and annealed product, said elastic limit level, the use of said sheet being combined with the use of a protective varnish.,

  
We therefore see that, to solve the specific problem

  
 <EMI ID = 34.1>

  
 <EMI ID = 35.1>

  
 <EMI ID = 36.1> keeping sufficient crimping possibilities; <EMI ID = 37.1> use of protective varnish layers.

  
 <EMI ID = 38.1>

  
 <EMI ID = 39.1> <EMI ID = 40.1>

  
no detrimental deformation, said metal boxes

  
 <EMI ID = 41.1>

  
containers tested contained beer put under

  
 <EMI ID = 42.1>

  
at room temperature the beer could be dispensed under

  
 <EMI ID = 43.1>

  
One embodiment is described below and schematized

  
 <EMI ID = 44.1> FIG. 1 represents a front view of a packaging according to the invention equipped with a beer dispenser device <EMI ID = 45.1> FIG. 2 represents the metallic packaging according to the invention in half-view from the front and in radial half-section; FIG. 3 represents on an enlarged scale the part <EMI ID = 46.1>

  
In this execution is shown the packaging

  
 <EMI ID = 47.1>

  
under pressure. The actual packaging consists of

  
 <EMI ID = 48.1>

  
 <EMI ID = 49.1>

  
device, respectively [pound] -7. *

  
The upper bottom has a central hole 8 of which

  
 <EMI ID = 50.1>

Claims

The diameter of the groove bottom is equal to or approximate

pclyvinyl-ketone. Finally, on all the interior faces of the

killed by a solution of polyvinyl hydrocarbon ketone chloride. These different layers were brought to temperature

polymerization.

The relative dimensions correlatively to the raw materials used are obviously variable in the -

equipped with a device allowing the beer to be dispensed

pressure, characterized in that it consists substantially on the one hand, from, for the execution of the cylindrical body. :

ment perforated and profiled along the marginal edge of said central hole to form the upper bottom of the package; to crimp, on one

hard, a layer formed from a solution of polyvinylketone chloride; crimp the centrally perforated upper bottom on said cylindrical body and, finally, to apply, over the entire interior surface of the metal packaging thus formed, a covering layer also consisting of a chloride solution

for a relatively short time the composition of said

.cover layer at polymerization temperature, <EMI ID = 62.1>

after the welding operation in order to take advantage of the

4.- Method according to claim 1, characterized in that the protective layer based on polyvinyl chloride is applied by spraying after complete formation of the

cooperating with greater resistance from the adjacent part

crimping and significantly reducing the diameter of the discs. arranged in the main plane; the depth of said peripheral molding, respectively the depth of its marginal cylindrical part, are variable prorata_de.la conformation of the central part of the upper bottom of the packaging; said

upper bottom has a central circular hole whose bordering part is at a level slightly higher than that which is defined by the disc delimited by said peri-molding.

upper is such that it promotes the evacuation of air during

filling the packaging, and more particularly when

impacts to which the filled packaging is subjected before closing

6.- Packaging according to claim 1, characterized in that its body is produced using a tinned sheet of 5. ' gold- .

balling carried out using these sheets and capable of withstanding / very high internal pressures has a height

in that the two bottoms are made from a sheet - cold rolled with high elastic limit in non-extra soft steel and recrystallized by annealing in the. composition of which

in that the quantity of Nb contained in the sheets used '

beer under pressure, substantially as described;