AU758256B2

AU758256B2 - A molecular decomposition process for the synthesis of nanosize ceramic and metallic powders

Info

Publication number: AU758256B2
Application number: AU18076/00A
Authority: AU
Inventors: Sanjeevani Vidyadhar Bhide; Anil Vasudeo Virkar
Original assignee: University of Utah
Current assignee: University of Utah
Priority date: 1998-10-26
Filing date: 1999-10-26
Publication date: 2003-03-20
Anticipated expiration: 2019-10-26
Also published as: WO2000024676A1; AU1807600A; WO2000024676A9; JP2002528369A

Description

WO 00/24676 PCT/US99/24052

TITLE

A MOLECULAR DECOMPOSITION PROCESS FOR THE SYNTHESIS OF NANOSIZE CERAMIC AND METALLIC

POWDERS

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR

DEVELOPMENT

This invention was developed in part with funding under United States Government DOE Grant DEFG039ER45661. The United States Government may have some rights to this invention.

FIELD OF THE INVENTION This invention relates to a process for forming ceramic powders with fine nanosize particles.

BACKGROUND OF THE INVENTION Nanosize powders are generally considered to be powders having very fine particles in the nanometer range, less than a few nanometers, 100 nanometers or less, usually 10 nanometers or less.

Nanosize powders have numerous applications such as catalysts, electrocatalysts, catalyst supports, electrodes, active powders for the fabrication of dense bodies, semiconductors for energy storage, photovoltaics, ultrafine magnetic materials for information storage, environmental clean-up as destructive adsorbents, water purification, information storage, and optical computers, to name a few. Some of the numerous examples include the following: nanosize (3 to 4 nm) platinum for oxygen reduction in acid electrolytes, many metallic powders made by precipitation in aqueous and non-aqueous media for alloy fabrication and for catalysis, nanosize iron oxide catalyst for coal liquefaction, nanosize iron oxide particles for magnetic applications, tetragonal zirconia powder by a hydrothermal treatment at high pressures for structural applications, carbides and nitrides using non-aqueous media, nanosize BaTiO3 by a gas-condensation process, etc. Many oxides have potential applications rr rr r~-3n~~i Y~ Y WO 00/24676 PCT/US99/24052 as nanosize powders. These include: CeO(2-x) for catalytic reduction of S02, Yalumina as a catalyst support and for enhancing ionic conductivity of lithium iodide, V205 as a catalyst for NOx reduction, and etc. Several processes currently used for the synthesis of nanosize powders include:(l) Gas-phase condensation, (2) Mechanical milling, Thermal crystallization, Chemical precipitation, Solgel processing, Aerosol spray pyrolysis, and etc.

In gas-phase condensation, evaporation of precursors and their interaction with an inert gas leads to loss of kinetic energy, and homogeneous nucleation of nanosize powders occurs in a supersaturated vapor. Nanocrystalline powders of TiO2, doped MgO, CeO2, Y-doped ZrO2, etc. have been produced by gas-phase condensation. Aerosol spray pyrolysis has been used to synthesize BaFel2019, Fe203 among some other materials. High-energy mechanical milling is used extensively to produce nanostructured materials, especially when large quantities of materials are required. Very fine particles of nickel-aluminum alloy, Fe-Co-Ni-Si alloys, Ni-Mo alloys, for example, have been produced by mechanical milling.

Contamination by the milling process, however, is a shortcoming of this process.

Also, although very fine (un size) particles can be made, agglomeration is a problem leading to cluster sizes in the micron range.

Chemical coprecipitation has received considerable attention for the synthesis of nanosize powders. Metallic as well as ceramic powders can be made by a careful control of chemistry. Alkali metal borohydride, MBH4 where M is an alkali metal, for example, has been used as a reducing agent in aqueous media for the synthesis of metallic powders. Similarly, hydroorganoborates of the general formula MHv(BR3) or MHv[BRn(OR)3-n]v where M is an alkali or alkaline earth metal, v 1, 2, and R, R' are alkyl or aryl groups have been used as reducing and precipitating agents. It is important to control pH and ionic strength in aqueous media to prevent Ostwald ripening. In the synthesis of nanosize iron oxide, for example, it has been shown that the higher the pH and the higher the ionic strength, the smaller is the size of nanosize Fe304 particles.

-2- WO 00/24676 PCTIUS99/24052 In most methods for the synthesis of nanosize powders, two issues are particularly important; the formation of fine, uniform size particles, and the prevention of agglomeration. Nanoparticles of a uniform size can in principle be formed by carefully controlling nucleation and growth. Often, a variety of encapsulating methods are necessary to control the size of nanoparticles.

Agglomeration is often the result of Van der Waal's forces. The adverse effect of agglomeration on the sintering behavior of ceramic powders is well documented.

Even in catalysis, the need for dispersed powders is well known. Often, supercritical drying can be used to obtain nonagglomerated powders. In liquid media, agglomeration can be suppressed through steric hindrance or through the manipulation of electrostatic interactions. The latter in polar liquids can be achieved by changing the pH and the ionic strength of the solution. Many techniques involve the use of surfactants. Often the powders which are nonagglomerated and well dispersed in a liquid, tend to agglomerate during the drying stage. Fortunately, methods such as slip-casting, gel-casting, pressure slip casting can be used to achieve powder compaction in a wet state. Such has been demonstrated using submicron ceramic powders.

With the exception of milling, all the above methods are based on molecular synthesis of nanoparticles wherein the particles are built-up by atom-by-atom, or molecule-by-molecule, addition. Even in processes based on the decomposition of metal carbonyls, the growth of particles occurs by a layer-by-layer addition of atoms.

As a result, a control of nucleation and growth is necessary to ensure the formation of nanosize particles. This often requires a very precise and difficult control of the reaction system, which renders the manufacture of the nanosize powder in large quantities impractical or impossible. In addition, the molecular synthesis processes are costly because of the relatively large capital expenditures required for the equipment to control the formation of only a small quantity of nanosize product..

-3- WO 00/24676 WO 0024676PCT/US99/24052 Objects of the Invention It is, therefore, an object of the invention to provide method for the formation of nanosize powders that is easy to implement on an industrial scale and in relatively inexpensive when compared to molecular synthesis methods.

Another object of the invention is to provide a method in which nanosize powders are formed by a process other than precipitation or deposition from solutions, thus eliminating the possibility of unwanted deposition and growth of the nanosize powders.

Another object of the invention is to provide a method which forms nanosize powders that have a reduced tendency to agglomerate.

Another object of the invention is to provide a method for the formation of nanosize powders that can be applied to forming a variety of powder compositions.

Further objects of the invention will become evident in the description below.

BRIEF SUMMARY OF THE INVENTION In order to overcome the problems associated with molecular synthesis and milling to form nanosize powders, the present invention presents an alternative approach for the synthesis of nanosize powders. In the present invention, a precursor inorganic compound is formed from which the unwanted component is leached away so that a fine, nanosize powder is left as a residue. Thus, the present invention is based on molecula decoM~osition. rather than molecular synthesis, or deposition.

As discussed above, one of the problems with many methods of synthesis of nanosize powders is that often it is difficult to synthesize large quantities of materials.

By contrast, the present invention is suitable for making large quantities of nanosize powders of a number of materials.

In summary, the present invention is a process for forming nanosize powders The process comprises: forming a precursor ceramic material comprising a fugitive constituent and a non-soluble constituent in a single phase; contacting the precursor material a selective solvent to form a solution of the fugitive constituent and a residue of the non-soluble constituent, -4- WO 00/24676 WO 0024676PCT/US99/24052 the precursor sufficiently reactive with the solvent to form the solution of the fugitive constituent in the solvent and the residue of the non-soluble constituent the precursor material and the non-soluble residue sufficiently insoluble in the solvent such that there is insufficient precursor material and non-soluble residue in solution to deposit and precipitate upon the residue of the non-soluble-constituent, the fugitive constituent being sufficiently soluble in the solvent such that the precursor reacts with the solvent to form a solution of the fugitive constituent without precipitation and deposition of fugitive constituent upon the residue of the non-soluble constituent in the form of nanosize particles; removing the selective solvent solution from the residue to form a nanosize powder having the same chemical composition as the non-soluble constituent.

The precursor material should be insoluble as the precursor material in the solvent. One of the objects of the present invention is to prevent deposition or precipitation of dissolved materials upon the nanosize particles that are formed from the non-soluble residue fr-eed of the fugitive constituent. Deposition or dissolved precursor material will not only contaminate the residue, but possibly result in particles that are too large. In the present invention, an object is to prevent, as much as possible, deposition of dissolved materials and the resulting growth of existing crystals. Unlike prior-art methods where small crystals are crystallized from solution, it is practical in the present invention to inhibit the crystallization and precipitation process altogether, as crystallization is not required to form initial nanosize crystals.

Accordingly, as further illustrated below, a precursor is chosen such that precipitation of any material upon the nanosize particles is essentially avoided.

Another requirement of the precursor material is that it be reactive with the solvent. Since the precursor is insoluble, the precursor composition does not dissolve, but it does react to selectively remove the fugitive constituent, leaving a fr-eed nonsoluble constituent.. The fugitive constituent is sufficiently soluble that it will not precipitate from the solution to contaminate and grow the particles of the non-soluble constitituent. The non-soluble constituent is essentially insoluble to prevent dissolved material dissolving into the solution, there thereafter precipitating upon and growing the nanosize particles of the non-soluble material formed by removal of the fugitive

K-MWEVM

WO 00/24676 WO 0024676PCT1US99/24052 constituent. Basically, the invention involves a balance between preventing precursor and non-soluble constituent from forming a solution so that it cannot redeposit and grow crystals, and removing the fugitive constituent, that is sufficiently soluble in the solution that it will not precipitate from the solution to grow crystals.

For example, BaCeO 3 does not dissolve in water, but reacts with water to form a solution of the Ba (as Ba(OH) 2 On the contrary, NaAIO 2 is soluble in water, and cannot be used as a suitable precursor for the present invention.

In order that the non-soluble constituent freed from the fugitive constituent form nanosize particles, the precursor should be a single phase material, where the differentiation between the non-soluble and the fugitive constituents is on a molecular level. Accordingly, the precursor exists as a compound existing is the form of a large molecule, or as an alloy. For ceramics, an example of a precursor material is a mixed oxide with at least two cations, the metal oxide of the first cation being soluble to function as the fugitive constituent, and the oxide of the second being nonsoluble to function as the non-soluble constituent. For forming metal nanosize powders, the precursor can exist, for example, as an alloy or an intermetallic compound.

The solvent is selected to react with the precursor and have the solubility properties as described above. For ceramics, a preferred solvent is water, but nonaqueous solvents may be required to suppress the solubilities of the non-soluble residue and/or the precursor. Usually the solvent is polar, as the fugitive constituent, which must be solubilized, is often a polar composition. Typically, suitable solvents for forming a ceramic nanosize powder are polar liquids that solubilize selected ceramic oxides, which selected oxides in the process of the invention are the fugitive constituents. As further described below, preferred solvents are water and acids. For metallic nanosize powders, the selective solvent is typically an acid that reacts with or dissolves the fugitive metal, and not the non-soluble metal.. In place of acids, an acid gas such as SO 3

N

2 0 5

CO

2 or HCl, may be used to react with and remove the fugitive constituent Any suitable process may be used for forming a precursor is contemplated.

For example, where the precursor is a mixed ceramic subjecting a powder mixture to a -6- WO 00/24676 PCTUS99/24052 suitable high-temperature treatment is suitable. Precursors for metallic powders are likewise formed by any suitable process to produce a suitable alloy or intermetallic compound, such as alloying methods or powder metallurgy.

The solvent is then removed from the remaining non-soluble constituent.

With the fugitive constituent removed, the non-soluble constituent assumes the form of nanosize particles. The solvent is removed by conventional methods, including, but not limited to settling, centrifugation, filtering, air drying, or a combination or the above. The solvent, may also be removed by replacing it with another liquid, such as replacing at aqueous solvent with an alcohol, and then separating the powder from the replacement liquid. Using a replacement liquid may be desirable to inhibit agglomeration of the powder during drying.

The product is chemically the same as the non-soluble constituent. The process of the invention is particularly suitable for synthesizing nanosize powders of A1 2 0 3 CeO 2 ZrO 2 TiO 2

V

2 0 5 rare earth (RE) oxide-doped CeO 2 and RE- or

Y

2 0 3 doped ZrO2.

BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic showing a reaction illustrative of the process of the invention Figure 2(a) is an XRD (X-ray diffraction) trace of a single-phase perovskite precursor material (Gd-doped BaCeO 3 Figure 2(b) is an XRD trace of the material of Figure 2(a) after boiling in water for two days, showing conversion to nanosize CeO 2 Figure 2(c) is an XRD trace of a comparative coarse (not nanosize) CeO2 powder.

Figure 3(a) is an XRD trace of an as-received, precursor (non-nanosize) Na 2 ZrO 3 powder.

Figure 3(b) is an XRD trace of the residue after boiling the Na 2 ZrO 3 of Figure 3(a) in water for 10 minutes.

Figure 3(c) is an XRD trace of the residue from the boiling of Na 2 ZrO 3 from Figure 3(c) after heating in air to 100°C for 1.5 hours.

WO 00/24676 PCT/US99/24052 Figure 3(d) is an XRD trace of the residue after 1.5 hours in air at 200°C.

Figure 3(e) is an XRD trace of the residue after 1.5 hours in air at 300°C.

Figure 3(f) is an XRD trace of the residue after 1.5 hours in air at 350°C.

Figure 3(g) is an XRD trace of the residue after 1.5 hours in air at 400°C.

Figure 3(h) is an XRD trace of the residue after 1.5 hours in air at 500°C.

Figure 3(i) is an XRD trace of the residue after 1.5 hours in air at 600°C.

DETAILED DESCRIPTION OF THE INVENTION Synthesis of Precursor Powders: The present invention is suitable for the synthesis of many types of powders.

Although the following discussion is confined to specific materials, the applicability of the present invention to other powders will be evident to one of ordinary skill in the art. For the purposes of discussion, rare earth (RE)-doped CeO2 and Y203-doped ZrO2 are used as examples. Y 2 0 3 -doped ZrO2 has many applications such as in oxygen sensors, solid oxide fuel cells, as a constituent in electrodes and in structural ceramics. RE-doped CeO2 has applications in oxygen separation membranes, in fuel cells as well as in catalysis.

Respective precursor powders can be synthesized using conventional processing methods. For example, for the synthesis of nanosize RE20 3 -doped CeO2 by the present invention, a precursor can be BaCe(1.x)REO(3-8). The precursor is synthesized using BaCO3, RE 2 0 3 and CeO2 in a powder form, mixing reagent powders, and calcining at 1250°C. A similar procedure can be used for other materials such as Y 2 0 3 -doped ZrO 2 Other examples included BaCe(i.xREXOR or SrCel.xRExO, precursors for a composition of the final nanosize powder is Ce,.

xRExO 2 or BaZr 1 .xRExO3 or BaZr,.xREXO precursors for a composition of the nanosize powder of Zr,.RExO 2 8 RE is a rare earth metal or Y, x is between 0 and about 0.25, and 8 is between 0 and about 0.13.

WO 00/24676 WO 0024676PCTIUS99/24052 Synthesis of Nanosize Powders from the Precursor: Synthesis of the nanosize powders from the precursor involves exposing the precursor to a selective solvent that leaves the desired component The following approaches can be used be used: A reaction with water.

A reaction with a dilute acid such as HNO 3 HCl, H 2 C0 3 and H 2 S0 4 A reaction with C0 2 and S03 in polar, non-aqueous solvents.

A Reaction with Water: Water is the ideal solvent Also, in many cases, thermodynamics of the formation of alkali hydroxides or alkaline earth hydroxides are favorable. There are, however, a few potential complications, in particular many elements form hydroxides, and there is the danger of agglomeration during the drying stage. For example, in the synthesis of ZrO2 the undesired formation of Zr(OH)4 is possible. However, it has been shown that with Na 2 ZrO 3 as a precursor, a direct reaction with water can be readily effected without the formation of Zr(OH) 4 The potential for agglomeration can be suppressed by replacing the water with alcohol after solvation.

(1b) A Reaction with Acids: In many cases, reaction with water is not favorable. For example, reaction of BaZrO3 with water to form ZrO 2 and Ba(OH)2 is not favored. However, as shown in Table B, reaction of BaZrO3 with HN0 3 or N 2 0, to form Ba(N03)2 and ZrO2 is favored. Also, Ba(N03)2 has a reasonable solubility in water. With HN0 3 as a reactant, the formation of Zr(OH)4 is suppressed. The tendency for agglomeration can be minized, by either replacing water with an alcohol or other organic liquids of high vapor pressures, or drying under supercritical conditions. It is also within contemplation of the invention to use surfactants, to minimize agglomeration, either based on electrostatic interactions or steric effects.

-9- WO 00/24676 WO 004676PT/US9924052 Reactions with non-aqueous electrolytes Reactive gases in Polar, Non-aqueous Solvents: This approach is particularly suitable when there is a tendency to form hydroxides of the product oxides which precludes the use of water when the objective is to synthesize nanosize powders with minimal agglomeration. In such cases, the use of non-aqueous, polar liquids may be necessary. Table C lists a few non-aqueous solvents, which are used for non-aqueous electrolytes. The polar liquid used as a solvent should also have a reasonable solubility for the reacting gas, which may be, for example, CO 2

SO

3

SO

2 or N 2 0,.

i0 Suitable solvents are selected based on the following criteria: the solubility of the reacting gas in the solvent, and (ii) the solubility of the fugitive compound formed; e.g. BaCO 3 or BaSO4 in the case of CO 2 or SO 3 In order to increase contact between the precursor powder BaGdxCe(1..x)O(3-&) &0-O.13) and the gas (CO 2 or SO 3 the suspension of the powder is preferably agitated, e.g. by constant stirring, while the gas is bubbled through it. The solvent vapors are also preferably recovered and returned back to the reactor, by using, for example, a watercooled condenser.

Mechanism of the Kinetics of Synthesis of Nanosize Powders: The kinetics of the formation of nanosize powders is a factor that should be considered in choosing the precursor and solvent for the desired. The data in Table B give the thermodynamic basis for the occurrence of certain given reactions. Assuming a given reaction is favored over undesired competing reactions, an important consideration is the kinetics of the reaction. With reference to the schematic of the reaction given in Figure 1, it is readily seen that the kinetics of the reaction should depend upon the transport of soluble reactants and products. The overall reaction mechanism is expected to involve the following steps; The tranport of the dissolved reacting gas, N205, CO 2 or S03, (or the respective acids) through the porous layer formed to the interface separating the precursor and the product, (b) Reaction at the interface, and The transport of the dissolved byproduct, e.g., Ba(N03)2, BaCO3 or BaSO4, from the interface through the porous layer, into the WO 00/24676 WO 0024676PCr/US99/24052 bath. The overall kinetics may be influenced by all three of the factors, and may be dictated by whichever is the slowest step. The solubility of the reacting gas is a function of pressure; the higher the pressure, the higher is the solubility. Both the kinetics of the actual reaction occurring at the interface as well as the transport through the porous layer are functions of the concentration of the dissolved reactant species; the higher the concentration, the faster should be the kinetics. The temperature dependence of the reaction at the interface, however, will in general be different from that of the transport of dissolved species. The known theoretical models of transport through porous bodies can be used in this analysis.

Propensity for Particle Growth: The advantage of the present invention over the other methods for the synthesis of nanosize powders is that there is negligible tendency for the occurrence of particle growth by either Ostwald ripening or by precipitation. This is because neither the precursor nor the desired product, are soluble in the solvent. For example, neither BaCeQ 3 nor CeO 2 is soluble in water; only the leachable Ba(OH) 2 is soluble in water.

Since the product is nanosize, it could be argued that its solubility may be higher than bulk materials. It is known, for example, that the solubility of a sparingly soluble species is related to its size by the following equation; C(r) _-C(oo)expI

I

L rk,TJ where, C(co) is the bulk solubility (particle of a large radius), C(r) is the solubility of a particle of radius r, y is the particle-solvent interfacial energy, Q~ is the molecular volume of the particle, is the Boltzmann constant, and T is the absolute temperature. Assuming the following values for the various parameters; particle radius, r -2 n, interfacial energy, r -0.5 J/m 2 molecular volume, f) -0.125 nm 3 (125 A3), and the temperature, T 350* 0 K, then the ratio C(r) /C(co) is about 3.6.

This shows that as long as C(oo) is rather low, even for nanosize particles the solubility enhancement is not large enough to cause any Ostwald ripening. Thus, there should be negligible particle growth.

11 WO 00/24676 PCT/US99/24052 Sintering Behavior ofPowders: The sintering (densification) behavior of nanosize powders synthesized by the present invention is expected to result in densification at lower temperatures, resulting in a finer microstructure.

Characterization of Sintered Bodies: The grain size of sintered bodies made from the nanosize powders should be smaller than those made from conventional ceramic powders. It is well known that very fine-grained ceramics often exhibit interesting properties, such as, for example, superplasticity at elevated temperatures, and high strength at low temperatures.

Metallic Powders: The present invention is also applicable to the synthesis of metallic powders, by the appropriate choice of the metallic precursor and the selective solvent. For example, synthesis of Pd powder can be achieved with precursor of an equimolar alloy of Ba and Pd, which is actually a line compound BaPd. The alloy can be made by arc melting or by powder metallurgy. The powdered alloy is then treated in dilute HCI to remove the Ba to form nanosize Pd.

Suitability for the Synthesis of Large Quantities of Nanosize Powders: The process of the invention for the synthesis of nanosize powders is simple, and can be adapted by using chemical leaching technology. Especially with water as the solvent, the process does not require exotic equipment nor exotic precursors. The precursors can be made by simple calcination or alloy fabrication methods. The starting particle size of the precursors need not be very small. Finally, the process has a general applicability for a wide range of materials. The process thus is easily amenable to scale up for production of large quantities of materials.

In summary, nanosize powders of a variety of materials are usually made by one or more processes which may be categorized as belonging to molecular synthesis wherein particles are built up by an atom-by-atom or a molecule-by-molecule addition on a particle nucleus. The present invention is based on molecular decomposition wherein unwanted species are chemically leached away thus producing a nanosize -12- -414 4- WO 00/24676 PCT/US99/24052 powder as a residue, starting with a precursor of a macroscopic size. The method of the present invention should result in nanosize particles of a uniform composition and size. In the present invention, neither the precursor nor the product is soluble in the reaction medium. As a result, particle coarsening is not expected to occur.

EXAMPLES

The following describes a general approach of the practice of the invention with two illustrative examples; namely the synthesis of nanosize CeO 2 and ZrO 2 Example I Synthesis of Nanosize Ce02: The starting precursor may be one of the alkaline earth cerates, such as BaCeO3. At room temperature, the standard free energy for the reaction BaCeO3 1120 Ba(OH) 2 CeO 2 is 189.79 kJ/mol indicating that this reaction is favored. The volume of CeO2 per molecule is -77 A 3 and the linear dimension is (cube root of the volume) 4.25 A. The volume per molecule of BaCeO3 is -85 A 3 and the linear dimension is 4.4 A. Thus, if BaO is leached out as Ba(OH)2, the change in volume for the original BaCeO 3 is 77)/85) x 100 or or the change in linear dimension is 4.25)/4.4) x 100 or Figure 1 shows a schematic of a particle 11 reacting with H20 to form Ba(OH) 2 The Ba(OH) 2 formed dissolves into water thus leaving a porous layer 13 of CeO 2 The volume percent porosity in the layer is expected to be about The fact that BaCeO3 readily reacts with water suggests that the porosity is open. This facilitates the transport of the reacting species, H20 here, to the CeO2 (porous)/BaCeO3 (dense) interface 15. The reaction continues until all of the BaCeO3 17 reacts to form porous CeO2. The formed CeO2 should be fragile and break into a fine, nanosize powder.

In order to verify the concept, the following preliminary experiments were done. Gd203-doped BaCeO3 powder of composition BaGdO.2Ceo.80(3-8) was synthesized using BaCO3, CeO2, and Gd203 powders. The powders were mixed in -13- WO 00/24676 PCT/US99/24052 requisite proportions and wet ball-milled for 24 hrs. The well-mixed powder was then dried and calcined at 1450C for 6 hrs. The calcined powder was then ball-milled and examined by X-ray diffrction (XRD) with CuKa radiation to ensure the existence of a single-phase perovskite (Figure The calcined powder was then boiled in water for 2 days, filtered using a fine filter paper, washed with water to dissolve away Ba(OH)2, dried and then examined by XRD. Figure 2(b) shows the corresponding XRD trace. Also shown in Figure 2(c) is an XRD trace of as-received CeO2. A comparison of Figures 2(a) and 2(b) shows that upon boiling, BaCeO3 completely decomposes. The sharp peak at -24* is due to remnant Ba(OH) 2 not removed completely during washing.

A comparison of Figures 2(b) and 2(c) shows that the powder formed upon boiling is indeed CeO2 (presumably Gd-doped). The important difference between the two is that the XRD peaks of the powder formed by boiling BaCeO3 are considerably broader than for the as-received CeO2 powder. Using the Scherrer formula, the particle size of the ceria formed is estimated to be -4 urn. This shows that the method of the present invention involving molecular decomposition of starting a starting material with a larger molecule can lead to a fine, nanosize powder even when the initial powder is quite coarse.

Example II Synthesis of Nanosize ZrO2: The starting precursor may be a suitable alkali or alkaline earth zirconate. In the preliminary work, Na2ZrO 3 was used as the precursor. This was simply boiled in water for a few minutes. The reaction is Na 2 ZrO 3

H

2 0 Zr02 2NaOH No thermodynamic data are available. However, preliminary experimental work, results of which are described below, shows that the above reaction is indeed favored..

Powder of Na 2 ZrO 3 was purchased from a commercial vendor. Approximately gms. of the powder was boiled in water for ten minutes. The residue was filtered, washed, and dried. The residue was subsequently examined by X-ray diffraction -14- 4~iZ~ r~ WO 00/24676 WO 0024676PCTIUS99/24052 (XRD) with CuKa radiation. The residue was then subjected to a number of thermal treatments. The following are the results of this experiment.

Figure 3(a) is an XRD trace of the as-received Na 2 ZrO 3 powder. Sharp peaks indicate a relatively coarse (at least a few tenths of a micron or more) particle size.

Very tiny peaks at approximately 28 and 31.5 degrees are due to a small amount of monoclinic ZrO 2 that was present in the as-received Na2ZrO 3 powder.

Figure 3(b) is an XRD trace of the residue after boiling Na 2 ZrO 3 in water for minutes, washing and drying. The trace shows the absence of the original Na 2 ZrO 3 powder. The trace mainly consists of two very broad peaks. These peaks belong to the cubic phase of ZrO 2 The peaks are very broad and contain more than one peak in each of the peaks. These very broad peaks are indicative of a very fine (nano) particle size. The reaction that occurred is the following: Na 2 Zr 3

+H

2 0 -4ZrO 2 +NaOH The two sharp peaks at -28 and -3 1.5 degrees are again due to the small amount of monoclinic ZrO 2 present in the original Na 2 ZrO 3 powder.

Note that the intensity scales in 3(a) and 3(b) are quite different, and that the same monoclinic peaks with about the same intensities are present in Na 2 ZrO 3 Note also that the integrated peak intensity of the monoclinic peak is very small compared to that of the nanosize ZrO 2 formed (broad peaks). Some growth of the original monoclinic, ZrO 2 particles is expected by the deposition of new ZrO 2 (by the above reaction) on them. These monoclinic ZrO 2 particles are not expected to be nanosize, consistent with observations.

Figure 3(c) is an XRD trace of the residue after heating in air to 100 0 C for hours. Note that the trace is similar to that in Figure 3(b).

Figure 3(d) is an XRD trace of the residue after 1.5 hours in air at 200*C in air.

The peaks have become somewhat sharper (peak widths are less in this figure as compared to that in Figures 3(b) and This is indicative of a slight coarsening of particles.

Figure 3(e) is an XRD trace of the residue after 1.5 hours in air at 300*C. The peaks not only have become sharper but that the initial very broad peaks of the residue have now split into more peaks. A total of 4 broad peaks are apparent,. in addition to 15 WO 00/24676 PCT/US99/24052 the two sharp peaks corresponding to the original monoclinic ZrO 2 The four broad peaks are identified with cubic ZrO 2 The peaks correspond to (111), (200), (220), and (311) reflections, in increasing diffraction angle.

Figure 3(f) is an XRD trace of the residue after 1.5 hours in air at 350 0 C. The four peaks have become slightly sharper.

Figure 3(g) is an XRD trace of the residue after 1.5 hours in air at 400 0 C. The four peaks have become even sharper.

Figure 3(h) is an XRD trace of the residue after 1.5 hours in air at 500°C.

Figure 3(i) is an XRD trace of the residue after 1.5 hours in air at 6000C.

The corresponding XRD traces in Figures 3(c) to 3(i) show the formation of cubic zirconia as the residue is heated to higher temperatures.. The stable phase of ZrO 2 at low temperatures is monoclinic. The formation of a very fine (nanosize) ZrO 2 by the described process leads to the stabilization of cubic ZrO 2 due to surface energy considerations (yck yud where r denotes surface energy of the respective polymorph). The present experiment showed that: Na 2 ZrO 3 can be used to synthesize nanosize ZrO 2 The nanosize ZrO 2 formed is of cubic crystal structure.

Using the Scherrer formula, which relates the particle size, d, to peak broadening, B, diffraction angle, 0, and X-ray wavelength, 2, by d 0.92 BcosO the particle size of the ZrO 2 formed as a function of subsequent heat treatment temperature was calculated. The calculated particle size as a function of thermal treatment is given in Table A.

Table A Nanosize ZrO 2 powders produced by reaction of Na2ZrO 3 with water.

Temperature Corrected (111) Peak Particle CC) Width (rad) Size (rm) 300 0.0476 3.4 350 0.0371 4.3 400 0.0164 9.8 500 0.0124 13.0 600 0.0113 14.2 -16- WO 00/24676 PCT/US99/24052 The preceding two examples demonstrate the approach and the potential of the present invention for the synthesis of nanosize oxide powders.

The preceding shows that nanosize CeO2 and ZrO 2 can be produced respectively by leaching out BaO from BaCeO3, as Ba(OH)2 and Na 2 O from Na 2 ZrO 3 as NaOH. Various other reacting species can also in principle be used. As an example, let us examine the formation of A1203 starting with BaA1204 by reacting it with HNO3 by the following reaction.

BaA1204 2HN03 Ba(N0 3 2

H

2 0 A1203 The free energy for the above reaction at room temperature is 255.35 kJ/mol..

The change in volume upon removing BaO is -59% and the change in linear dimension is Note that volume percent porosity in this case is much higher than for BaCeO3 CeO 2 conversion and the reaction is expected to progress with ease. In general, the greater the amount of material that has to be leached away per unit amount of the desired final product, the finer should be the particle size. In this context, with Ba3A1206 as a precursor is superior since three molecules of BaO have to be removed to form one molecule of A1203. The standard free energy for the reaction.

Ba3A1206 6HN03 3Ba(N03) 2 A1203 3H20 at room temperature is -884.15 kJ/mol. indicating that the reaction is favored. The percent change in volume per one molecule of A1203 formed is greater than with BaAl204, implying a greater porosity, potentially faster kinetics, and a potentially finer particle size. A similar reaction can be envisioned with H 2

CO

3 as the reactant.

However, BaCO 3 has negligible solubility in water. With HNO 3 as the reactant, several reactions are possible. One such successfully conducted in our laboratory is the reaction of MgTiO 3 with HNO 3 to form Mg(N03)2 and TiO 2 given by MgTiO3 2HN0 3 Mg(N03) 2 TiO2 H 2 0 The above reaction is thermodynamically favored at room temperature. Also, Mg(NO 3 2 is water soluble. Preliminary experiments were done wherein MgTiO3 was boiled in dilute HNO3 for 11 hours. The reaction went to completion and the -17- S9 ^38iiW SWeWPS^ WO 00/24676 PCT/US99/24052 resulting TiO2 was indeed nanosize, as judged by XRD peak broadening. The XRD traces are not given here for the sake of brevity.

The preceding discussion was on reactions of precursor powders with HNo 3 It is also possible and advantageous to use H2S04 since the magnitudes of standard free energies (IAG°I with AG* 0) of the corresponding reactions are often larger with

H

2 S0 4 than with HNO3. As an example of the use of S03, consider the synthesis of V205, which is used as a catalyst in NOx reduction, starting with Na4V207.

Reaction with S03 is given by Na4V207 2H 2 SO4 2Na2SO4 V205 2H20 with the standard free energy at room temperature given by -326.4 kJ/mol.

Also, Na2SO4 is highly soluble in many polar liquids including of course water. Also, as long as Na4V207 is present, VOSO4 will not form.

In the preceding paragraphs, several reactions in water as a solvent are described. In some cases, the use of water as a solvent may lead to the formation of hydroxides, e.g. A(OH) 3 In such cases, instead of acids, the suitable reactants may be the respective gases; e.g. N 2 0 instead of HNO 3 and SO 3 instead of H 2

SO

4 and non-aqueous, polar solvents. The advantage of using non-aqueous solvents is that there is no possibility of the formation of AI(OH) 3 which must be heated to remove water thus risking agglomeration and coarsening. The possible use of other solvents is discussed below. Table B gives a few of the possible reactions to form a number of oxide powders. All of the reactions are given with reactive gaseous species. Similar data can readily be given with aqueous acids as well.

-18- WO 00/24676 PCTIUS99/24052 Table B: Some examples of the synthesis of fine ceramic powders by the present invention.

Ceramic Precursor Chemical Reaction with Selective Solvent Standard Of Free En- Interest ergy,

AG°

(kJ/mol.) A1203 BaAl204 BaAl204 CO2 BaCO3 A1203 113.19 A1203 Ba 3 Al206 Ba3Al 2 06 3C02 3BaCO3 A1203 459.51 A1203 NaAO0 2 2NaA102 SO3 Na2SO4 A1203 342.6 Cr203 MgCr204 MgCr204 CO2 MgCO3 Cr203 6.93 Cr203 MgCr204 MgCr204 SO3 MgSO4 Cr203 188.13 ZrO2 BaZrO3 BaZrO3 C02 BaCO3 ZrO2 88.33 ZrO2 BaZrO3 BaZr03 S03 BaSO4 ZrO2 336.14 ZrO2 BaZrO3 BaZr03 N205 Ba(N03)2 ZrO2 260.3 TiO2 MgTiO3 MgTiO3 2HN03 Mg(N03)2 TiO2 H20 81.07 TiO2 Mg2TiO4 Mg2Ti04 2CO2 2MgCO3 TiO2 77.34 TiO2 Mg2TiO4 Mg2TiO4 2S03 2MgS04 TiO2 440.82 TiO2 Na2TiO3 Na2TiO3 CO2 Na2CO3 Ti02 80.62 TiO2 Na2TiO3 Na2Ti03 SO3 Na2S04 Ti02 325.81 V205 Na4V207 Na4V207 S03 2Na2SO4 V205 458.01 *Standard free energy for 3Na 2 S0 4 Al 2 0 3 3Na 2 0 Al2(SO 4 3 at 298 K is +1,155 kJ/mol. showing that the formation of Na2SO4 is favored over that of Al 2

(SO

4 3 Thus, reaction of NaAlO 2 with S03 should proceed as shown. Also, while this reaction can be effected in water, a preferred is to identify a solvent with a high solubility for Na 2 SO4 but negligible for NaAIO 2 This is because of the possible formation of alumina precipitate which would tend to grow the particles. The formation of alumina using an aqueous solution of NaAlO 2 would be the conventional chemical precipitation process, and it is anticipated that in such a case a careful control of parameters would be necessary to prevent particle growth.

Table B shows that the standard free energies of the reactions are all negative suggesting that all of these reactions are thermodynamically favored. Carbonates, sulfates or nitrates ofAl, Ti, and Zr are less stable than the corresponding alkaline earth compounds. No thermodynamic data appear to be available for the former.

Non-aqueous Solvents: Reactions of the various oxides with C0 2

N

2 0 5 and SO 3 to respectively form carbonates, nitrates, and sulfates can in principle be carried out in water or other polar -19- SUBSTITUTE SHEET (RULE 26) IMB I-IB---il WO 00/24676 PCT/US99/24052 liquids. Ba(N03)2 is soluble in water, but BaCO3 and BaS04 are essentially insoluble. There are a number of nonaqueous, polar liquids as possible candidates.

The prospective solvent to be used must have the following characteristics: It must have a reasonable solubility for the reacting gases, namely, C02, S03 or N20 5 It must have a significant solubility for BaCO3, BaSO 4 or Ba(N03)2. Table C gives a list of possible candidates and their physical properties. It is important to note that the boiling points of these liquids are quite high. Thus, as long as the solvent does not chemically react with either the precursor or the product, the process can be carried out over a wide temperature range. Also, the solubilities ofBaCO3, BaS04 and Ba(N03)2 should be greater at higher temperatures. At the same time, however, the solubilities of the reacting gases in liquids decreases with an increasing temperature.

Thus, a suitable optimum temperature must be identified at which the reaction rate is maximum.

Table C Physical properties of some nonaqueous, polar liquids.

Material Formula b.p. m.p. Viscosity Dielectric Density (millipois) Constant (g/ml) Formamide HCONH2 210.7 2.55 39.7 111.5 1.135 at 20°C at 20 0 C at 18°C N-Methyl CH3CONHCH3 24.13 151.8 0.9336 -acetamide at 50 0 C at 50°C at N-Methyl HCONHCH3 180 -5.4 19.9 200.1 1.007 -formamide at 15°C at 15°C at N-Methyl C2H5CONHCH3 60.6 185 0.9347 -propionamide at 20°C at Propylene 241 -49 25.3 64.4 1.19 Carbonate______ Ethylene (CH20)2CO 248 39 18.5 89.6 1.3218 Carbonate at 40°C at 39°C The method of the present invention can also be used to synthesize doped powders. For example, if the desired powder is Y203-doped Zr02 of composition Zr(l-x)YxO(2-6), then the starting precursor could be BaZr(1-x)YxO(3-?). After reaction with HNO3, as an example, the resulting powder should be Zr(I-x)YxO(2.-8).

Another example is RE-doped CeO2, where RE is a rare earth, namely Ce(1- SUBSTITUTE SHEET (RULE 26) WO 00/24676 PCTIUS99/24052 which can be made using doped BaCeO3, that is, BaCe(l-x)RExO(3- In the preliminary work, nanosize Gd-doped CeO2 was synthesized.

As already discussed, the method of the present invention can be used with water as the solvent in many cases. With water as the solvent, the corresponding aqueous acids, namely H2CO3 or H2S04 or HN03, can be used, the choice of the acid being dependent upon the solubility of the leachable compound to be formed, assuming of course that the thermodynamics are favorable. For example, the synthesis of nanosize TiO 2 starting with MgTiO 3 using HNO 3 has been demonstrated.

Further, if the leachable compound is Na 2

SO

4 as in the formation ofV 2 0 5 starting with Na 4

V

2 07, H 2 S0 4 should be the acid. However, with barium-containing compounds, HNO 3 is the acid of choice. There are two potential problems with water, however. There is the potential for hydroxide formation. (ii) Agglomeration has been shown to occur readily when water is present. This may be avoided by replacing water with another solvent, and/or by supercritical drying. For the synthesis of REdoped CeO 2 starting with BaCe(1-x)RExO(3-x) as a precursor, water is the ideal solvent since cerium hydroxide does not readily form. Preliminary work, discussed earlier, has indeed shown that nanosize ceria can be formed in an aqueous medium.

Example III Synthesis of Nanosize Metallic Powders: The present invention should also be useful for the synthesis of nanosize metallic powders, provided suitable intermetallic compounds can be used as precursors. There are numerous binary and ternary intermetallic compounds which may be used as precursors. As an example, for the synthesis of nanosize Pd, a possible precursor is BaPd which is an intermetallic line compound. The possible approach would consist of first fabricating BaPd by a conventional metallurgical process and then reacting it with an acid, HC1 acid. It is readily shown that the AG* for the reaction, BaCl2 Pd Ba PdCl2 is positive suggesting that the first compound to form will be BaCl2. The BaCl2 -21- -rascsaa.i-aaiaaaass_^ WO 00/24676 WO 0024676PCTIUS99/24052 formed will dissolve into water thus forming nanosize Pd powder. The so-formed Pd powder should be nanosize and continue to remain nanosize since Pd has a negligible solubility in water. Thus, as long as the concentration of HCl is low, and there is BaPd to react with, that is, there is Ba to react with HCl; PdCl2 will not form. Note that this process differs from the synthesis of Pd by the reduction of PdCl2. In the latter case, particle growth of Pd readily occurs since the deposition of Pd on the already formed Pd powder continues to occur as PdCl2 in solution reacts with a reducing agent, an alkali metal borohydride. In such a case, the experimental conditions must be carefully controlled to prevent particle growth. By contrast, the process of the present invention should readily lead to the formation of nanosize Pd with negligible particle growth.

Advantages of the Method of the Present Invention over the other Synthesis Methods for Nanosize Powders: 1) Uniform mixing at a molecular or an atomic level Since the powders are produced by leaching unwanted constituents from an initial homogeneous solid solution or a compound, the remaining constituents should be intimately mixed. For example, in the synthesis of Gd 2

O

3 -doped CeO 2 starting with BaCe(1..x)Gd,,O(3_8), Gd and Ce are expected to be intimately mixed since the original solid solution is uniform.

2) Narrow particle size distribution Since the constituent to be removed, Ba is distributed on a regular, periodic basis, it is anticipated that molecular level cracks or fissures are formed when Ba is removed as, Ba(OH) 2 or Ba(N0 3 2 This should lead to a uniform particle size.

3) Negligible growth of nanosize particles unlike in conventional chemical synthesis: The resulting nanosize particles in the present invention are essentially insoluble in the liquid media used, and so are the precursors. As a result, growth is not expected unlike conventional chemical synthesis approaches which rely on -22precursors reacting in solution to form an insoluble product; the formation of insoluble Fe 3 0 4 from Fe(II) and Fe(III) chlorides in solution. In such cases, growth of particles can readily occur.

While this invention has been described with reference to certain specific embodiments and examples, it will be recognized by those skilled in the art that many variations are possible without departing from the scope and spirit of this invention, and that the invention, as described by the claims, is intended to cover all changes and modifications of the invention which do not depart from the spirit of the invention, When used in this specification and claims, the terms "comprises" and "comprising" and variations thereof mean that the specified features, steps or integers are included. The terms are not to be interpreted to exclude the presence of other features, steps or components.

23

Claims

1. A process for forming a nanosize ceramic powder comprising: fonning a precursor ceramic material comprising a fugitive constituent and a. non-soluble constituent in a single phase; contacting the precursor material with a selective solvent to form a solution of the fugitive constituent in the solvent and a non-dissolved residue of the non-soluble constituent, the precursor material sufficiently reactive with the solvent to form the solution of the fugitive constituent in the solvent and form the non-dissolved residue of the non-soluble constituent; the precursor material and the non-soluble residue sufficiently insoluble in the solvent such that there is essentially no precursor material and non-soluble residue in the solution that will deposit and precipitate upon the residue of the non-soluble-constituent; the fugitive constituent being sufficiently soluble in the solvent such that from the solution of the fugitive constituent essentially no fugitive constituent will deposit and precipitate upon the residue of the non-soluble constituent; removing the solution of the fugitive constituent from the residue to form a nanosize powder of the residue of the non-soluble constituent.

2. The process as in Claim 1 wherein the precursor is BaCe(.--,xO3. or SrCe,_xRExO, 3 and the composition of the nanosize powder is CxRE.,fiO 2 where RE. is a rare earth metal or Y, x is between 0 ahd about 0.25, and 5 is between 0 and.abdut 0.13.

3. The process as in Claim 1 whetein the precursor is BaZr.xRExO,x3 or BaZr,.xREXO, 4 and the composition of the nanosize powder is ZrlRExOuwhere RE is a rare earth metal or Y, x is between 0 and about 0.25, and 8 is between 0 and about 0.13. 24 WO 00/24676 PCT/US99/24052

4. The process as in Claim 1 wherein the composition of the resultant nanosize powder is A1 2 0 3 The process as in Claim 3 wherein the precursor is selected from the group consisting of BaAl2O 4 Ba 3 A120O, and NaALO,.

6. The process as in Claim 1 wherein the composition of the resultant nanosize powder is Cr20 3

7. The process as in Claim 6 wherein the precursor is MgCr20 4

8. The process as in Claim 1 wherein the composition of the resultant nanosize powder is ZrO 2

9. The process as in Claim 8 wherein the precursor is BaZrO 3 The process as in Claim 1 wherein the composition of the resultant nanosize powder is TiO

11. The process as in Claim 10 wherein the precursor is MgTiO 3 or MgTiO

12. The process as in Claim 1 wherein the composition of the non-soluble constituent and the nanosize powder is V 2 0 5

13. The process as in Claim 12 wherein the precursor is Na 4 V 2 0 7

14. The process as in Claim 1 wherein the selective solvent is water. The process as in Claim 1 wherein the selective solvent is an acid.

16. The process as in Claim 15 wherein the acid is selected from the group consisting of HNO 3 HC1, H 2 CO 3 and H 2 SO 4

17. The process as in Claim 15 wherein the acid is contacted with the precursor with an acid gas. .18. The process as in Claim 17 wherein the acid gas is SO 3 N 2 05, CO2 or HC1.

19. The process as in Claim 1 wherein the selective solvent is a reacting gas dissolved in a non-aqueous polar solvent.

20. The process as in Claim 19 wherein the polar solvent is selected from Sthe group consisting of formanide, N-Methyl-acetamide, N-Methyl-fornamide, N- Methyl-propioriamide, propylene carbonate, and ethylene carbonate, and the reacting gas is selected from the group consisting of CO,, SO,, SO,, and N,0,.

21. A process for forming a naposize metallic powder comprising: forming a precursor ceramic material comprising a fugitive metal constituent and a non-soluble constituent in a siligle phase; contacting the precursor material with a selective solvent to form a solution of the fugitive constituent and a non-dissolved residue of the non-soluble constituent, the precursor material sufficiently reactive with the solvent to form the solution of the fugitive constituent in the solvent and form the non-dissolved residue of the non-soluble constituent, the precursor material sufficiently reactive with the solvent to form the solution of the fugitive constituent in the solvent and form the non-dissolved residue of the non-soluble constituent, the precursor material and the non-soluble residue sufficiently insoluble in the solvent such that there is essentially no precursor material and non-soluble residue in the solution that will deposit and precipitate upon the residue of the non-soluble-constituent, the fugitive constituent being sufficiently soluble in the solvent such that from the solution of the fugitive constituent essentially no fugitive constituent will deposit and precipitate upon the residue of the non-soluble constituent; removing the solution of the fugitive constituent from the residue to form a nanosize powder of the residue of the non-soluble constituent.

22. The process as in Claim 21 wherein the precursor is an alloy or an intermetallic compound.

23. The process as in Claim 21 wherein the precursor is PaPd. -26- U~c~ mt~ ii-ji.

24. The process.as in Claim 21 wherein the selective solvent is an acid. The process as in Claim 21 wherein the selective solvent is HC1.

26. A process for forming a nanosize ceramic powder substantially as hereinbefore described with reference to the accompanying drawings. Dated this 15th day of January 2003 PATENT ATTORNEY SERVICES Attorneys for UNIVERSITY OF UTAH -27