AU740125B2

AU740125B2 - Rotatable cutting bit assembly with cutting inserts

Info

Publication number: AU740125B2
Application number: AU83937/98A
Authority: AU
Inventors: Ted R. Massa; David R. Siddle
Original assignee: Kennametal Inc
Current assignee: Kennametal Inc
Priority date: 1997-07-15
Filing date: 1998-07-10
Publication date: 2001-11-01
Anticipated expiration: 2018-07-10
Also published as: WO1999004128A3; CA2293276A1; PL337811A1; WO1999004128A2; AU8393798A; EP0996809A2

Description

-1- ROTATABLE CUTTING BIT ASSEMBLY WITH CUTTING INSERTS This patent application is a continuation-in-part of copending United States patent application Serial No. 08/893,059 filed of July 15, 1997 by Massa and Siddle.

BACKGROUND OF THE INVENTION The discussion of the background to the invention herein is included to explain the context of the invention. This is not to be taken as an admission that any of the material referred to was published, known or part of the common general knowledge in Australia as at the priority date of any of the claims.

The expansion of an underground mine (eg. a coal mine) requires digging a tunnel which initially has an unsupported roof. To stabilize and support the roof a roof bolt must be inserted into the roof to provide support. The operator must first drill holes in the roof through the use of a rotatable cutting bit or roof drill bit. A roof bolt is then inserted into each one of the holes.

A common roof drill bit design uses a cutting insert that has been brazed into a slot at the axially forward end of the roof drill bit body. U.S. Patent No. 5,400,861 to Sheirer discloses various roof drill bits. U.S. Patent No. 4,603,751 Erickson also discloses various roof drill bits. Applicants hereby incorporate U.S. Patent No. 4,603,751 and U.S. Patent No. 5,400,861 by reference a S 20 herein.

French Patent Application No. 2,543,212 to Muller et al. pertains to a rotatable drill bit that has a drill bit body and at least two cutting pads. Each one of the cutting pads supports a cutting insert affixed thereto. Each cutting insert has a primary outer cutting edge and a primary inner cutting edge so as to form a cutting tip at the intersection thereof. U.S. Patent No. 2,575,239 to Stephens pertains to a reversible coal bit that has an elongate body with a cutting tip attached to the forward end thereof. The cutting tip is indexable.

In addition, the following catalogs published by Kennametal Inc. of Latrobe, Pennsylvania which are hereby incorporated by reference herein, disclose roof drill bits: "Kennametal Mining Products", Catalog A96-55(15)H6 (September 1996) [36 pages in length], and p 8 39 3 7 98 Amended daims July 2000.doc:711 1100 WO 99/04128 PCTfUS98/14358 -2- "Kennametal Mining Products" Catalog B92-75R(3)M5 (1992) [36 pages in length] While brazed-on cutting inserts have provided adequate results in the drilling of holes, there have been some drawbacks associated with the utilization of the brazed-on cutting inserts. As a result of brazing, the difference in the coefficients of thermal expansion between the steel roof drill bit body and the cemented carbide tungsten carbide-cobalt alloy) cutting insert has caused residual stresses in the cemented carbide cutting insert. These residual stresses have been detrimental to the performance of the roof drill bit since they have lead to premature failure of the cutting insert. This has been especially true in those cases where the earth strata being drilled has resulted in high impact loading on the cutting insert.

The presence of these residual stresses also has required that the grades of cemented carbide used for the cutting insert have had a high transverse rupture strength. This has been a factor which has limited the number of grades which have been suitable candidates for a cutting insert in a rotatable cutting bit such as a roof drill bit.

Some materials ceramics, low binder content [3 to 6 weight percent binder] tungsten carbide, binderless tungsten carbide, diamond or refractory [CVD or PVD] coated cemented carbides or ceramics, polycrystalline diamond [PCD] composites, polycrystalline cubic boron nitride [PcBN] composites) may have been suitable materials for use as a cutting insert in a roof drill bit because of their increased wear resistance, but have not been good candidates for use as a cutting insert in a roof drill bit due to brazing difficulties. More specifically, either these materials have been difficult to satisfactorily braze, or when brazed, these materials have experienced unacceptably high residual brazing-induced stresses.

WO99/04128 PCT/US98/14358 -3- In view of the drawbacks associated with brazing the cutting insert into the seat of a roof drill bit, it would be desirable to provide a roof drill bit wherein the cutting insert would be affixed within the seat of the roof drill bit without using a brazing process. Such a roof drill bit would have less of a chance of premature failure due to the presence of residual stresses. Such a roof drill bit would be able to use a wider range of materials for the cutting insert than has been heretofore available.

There comes a point where the cutting insert in the roof drill bit has reached a condition where the cutting action by the bit is no longer sufficient. At this point one of two processes occurs. One process comprises the regrinding of the cutting insert without removing the cutting insert from the roof drill bit.

The other process comprises debrazing the cutting insert so as to be able to remove it from the roof drill bit body, and then brazing a new cutting insert to the roof drill bit body. Each process has certain costs associated therewith which add to the overall cost of the drilling operation.

To reduce these additional costs it would be desirable to provide a roof drilling bit which would not require regrinding to place the cutting insert back in condition for cutting. It would also be desirable to provide a roof drilling bit that does not require debrazing/brazing of the cutting insert to replace a worn cutting insert.

Roof drill bits which have a higher penetration rate for the drilling operation are desirable in that such a drill typically takes less time to drill the required number of holes in the mine roof earth strata). The ability of the roof drill bit to use a cutting insert made from a more wear resistant material, such as those identified above, enhances the potential to maintain a higher penetration 4 rate at a given thrust level for a longer time. Thus, it would also be desirable to provide an improved roof drill bit that has a high penetration rate.

SUMMARY

In one aspect, the invention provides a rotatable cutting bit for penetrating an earth formation, the bit comprising an elongate bit body having a forward end and a rearward end, the bit body defining a peripheral surface, the bit body having a central longitudinal axis and a center of rotation; the bit body containing a first seat wherein a first cutting insert being retained in the first seat, and a second seat at the axially forward end thereof wherein a second cutting insert being retained in the second seat; wherein the first cutting insert presenting a first clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth formation, and the first cutting insert having a first leading cutting edge that engages the earth formation, and substantially all of the first leading cufftting edge being disposed 15 at a first lead angle between 50 degrees and 90 degrees wherein the first lead angle is the included-angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the first leading cutting edge and .0 another line is parallel to the center of rotation of the bit body; and the second cutting insert presenting a second clearance cutting edge which radially o 20 extends past the peripheral surface of the bit body so as to engage the earth formation, and the second cutting insert having a second leading cutting edge that engages the earth formation substantially all of the second leading cutting edge being disposed at a second lead angle between 50 degrees and degrees wherein the second lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the second leading cufftting edge and another line is parallel to the center of rotation of the bit body.

In a second aspect, the invention provides an elongate rotatable cutting bit body for carrying at least one cutting insert, and the cutting insert presenting a clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth formation, and the cutting insert having a leading cutting edge that engages the earth formation, and substantially all of the leading cutting edge being disposed at a lead angle between f A LI\ degrees and 90 degrees wherein the lead angle is the included angle N:\IRN\601677\amendeddaims29-8-01 PA3937-98.doc between a pair of intersecting lines (E-E and F-F) wherein one line is along the leading cutting edge and another line is parallel to the centre of rotation of the bit body; and the bit body having a central longitudinal axis the bit body including a forward end, a rearward end, and a seat at the forward end, the seat receives the cutting insert; wherein the seat being defined by a bottom surface, a radial edge that extends generally radially from the central longitudinal axis of the bit body, a radial side surface which extends generally radially from the central longitudinal axis of the bit body and becomes greater as it moves radially outwardly, and a chordal side surface which extends between the radial edge and the radial side surface, and the chordal side surface becomes greater as it moves toward the radial side surface.

In a third aspect, the invention provides a cutting insert for use in a rotatable cutting bit for the penetration of an earth formation wherein the cutting 15 insert is disposed in a seat in the cutting bit with a peripheral surface; wherein o: substantially all of the leading cutting edge which engages the earth formation is disposed at a lead angle between 50 degrees and 90 degrees; the cutting insert *.***including a cutting insert body having a top surface, a bottom surface, a first side surface, and a second side surface, the first side surface intersects the S 20 second side surface to form a first edge; the first and second side surfaces joining the top surface and the bottom surface; the first edge defining at least in part a clearance cutting edge which extends radially past the peripheral surface of the cutting bit when the cutting insert is in the seat so as to engage the earth formation.

In a fourth aspect, the invention provides a replaceable cutting insert for use in a rotatable cutting bit for engaging the earth strata, the cutting bit having a cutting bit body containing a seat which receives the cutting insert; wherein the cutting insert including a cutting insert body having two surfaces which intersect to form a cutting leading edge, the leading cutting edge that engages the earth formation, and substantially all of the first leading cutting edge being disposed at a first lead angle between 50 degrees and 90 degrees wherein the first lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the first leading cutting edge and another line is parallel to the centre of rotation of the bit body; and during IRN\6O1677vamendeddaims29-8-01 PA83937-98.doc Operation of the rotatable cutting bit the cutting edge engaging the earth strata; and the cutting insert body being made from one of the following materials: ceramics, binderless tungsten carbide, polycrystalline diamond composites with ceramic binder, tungsten carbide-cobalt alloys having a hardness greater than or equal to about 90.5 Rockwell A, and hard coated cemented carbides.

In a fifth aspect, the invention provides a cutting insert for use in a rotatable cutting bit for engaging earth strata, the rotatable cutting bit having a cutting bit body with a periphery and a seat which receives the cutting insert; wherein the cutting insert having a backing having a leading surface, a trailing surface, and a pair of opposite side surfaces, one of the side surfaces being near the periphery of the bit body when the cutting insert is received in the seat, and the one side surface converging toward the opposite side surface as it moves from the leading surface to the trailing surface; and the cutting insert preventing a clearance cutting edge which radially extends past the peripheral 15 surface of the bit body so as to engage the earth formation, and the cutting insert having a leading cutting edge that engages the earth formation, and substantially all of the leading cutting edge being disposed at a lead angle (C) between 50 degrees and 90 degrees wherein the lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line (F-F) S 20 is parallel to the centre of rotation of the bit body; and a layer of polycrystalline diamond on the leading surface of the backing wherein the layer of polycrystalline diamond defines a cutting edge, and during the operation of the rotatable cutting bit the cutting edge engages the earth strata.

In a sixth aspect the invention provides a rotatable cutting bit for engaging earth strata including a cutting bit body having a periphery and a seat wherein the seat has a bottom surface; and a cutting insert being received in the seat; wherein the cutting insert including a backing having a leading surface, a trailing surface and a bottom surface adjacent to the leading surface; a layer of polycrystalline diamond on the leading surface of the backing wherein the layer of polycrystalline diamond defines a cutting edge, and during the operation of the rotatable cutting bit the cutting edge engages the earth strata; and the bottom surface of the backing providing the major brazing area to braze the cutting insert to the cutting bit body, and the bottom surface of the backing being brazed to the bottom surface of the seat so as to affix the cutting insert to the cutting bit body.

It is to be noted that, throughout the description and claims of this specification, the word 'comprise' and variations of the word such as 'comprising' and 'comprises', is not intended to exclude other additives, components, integers or steps.

BRIEF DESCRIPTION OF THE DRAWINGS The following is a brief description of the drawings that form a part of this patent application: FIG. 1 is a side view of a specific embodiment of a rotatable cutting bit wherein a portion of the wall of the bit body has been cut away so as to reveal the presence of a cavity; FIG. 2 is a top view of the rotatable cutting bit of FIG. 1; FIG. 3 is an isometric view of the rotatable cutting bit of FIG. 1 without 15 the cutting inserts in their respective seats; FIG. 4 is a top view of a second embodiment of the cutting bit body; FIG. 5 is an isometric view of the forward part of another specific embodiment of a rotatable >N \IRNO167amenddclaims29.&OIPA83937.98.doc e*o o*° go* *oo o0 *eoe gi^ Cp WO 99/04128 PCTIUS98/14358 -6cutting bit using the cutting bit body of FIG. 1 and a second specific embodiment of a cutting insert; FIG. 6 is a top view of the cutting insert from the specific embodiment of FIG. FIG. 7 is a front view of the cutting insert of FIG. FIG. 8 is a left side view of the cutting insert of FIG. FIG. 9 is an isometric view of the forward part of a specific embodiment of a rotatable cutting bit using the cutting bit body of FIG. 1 and a third specific embodiment of a cutting insert; FIG. 10 is a top view of the cutting insert of FIG. 9; FIG. 11 is a front view of the cutting insert of FIG. 9; FIG. 12 is a left side view of the cutting insert of FIG. 9; FIG. 13 is an isometric view of the forward part of a specific embodiment of a rotatable cutting bit using the cutting bit body of FIG. 1 and a fourth specific embodiment of a cutting insert; FIG. 14 is a top view of the cutting insert of FIG. 13; FIG. 15 is a front view of the cutting insert of FIG. 13; FIG. 16 is a left side view of the cutting insert of FIG. 13; FIG. 17 is an isometric view of the forward part of a specific embodiment of a rotatable cutting bit using the cutting bit body of FIG. 1 and a fifth specific embodiment of a cutting insert; FIG. 18 is a top view of the cutting insert of FIG. 17; FIG. 19 is a front view of the cutting insert of FIG. 18 taken along line 19-19 of FIG. 18; WO 99/04128 PCTIUS98/1 4358 -7- FIG. 20 is a left side view of the cutting insert of FIG. 18; FIG. 21 is a graph comparing the normalized wear scar width (inches) against the distance (inches) from the outside diameter of the cutting insert; FIG. 22 is a side view of a specific embodiment of a rotatable cutting bit with a sixth specific embodiment of a cutting insert affixed thereto by brazing; FIG. 23 is a top view of the specific embodiment of FIG. 22; FIG. 24 is an isometric view of a cylindrical blank of stock material comprising a backing of cemented tungsten carbide with a layer of polycrystalline diamond (PCD) thereon wherein the geometry of the cutting insert blank is shown by dashed lines; FIG. 25 is a top view of the cutting insert blank showing the grinding lines (aa-aa and bb-bb) for grinding the cutting insert blank of FIG. 24 so as to make it a partially completed cutting insert blank; FIG. 26A is a top view of the completed cutting insert; FIG. 26B is a front view of a completed cutting insert showing the lines (ee-ee and gg-gg) along which the partially completed cutting insert blank of FIG. 25 is to be EDM machined so as to form the completed cutting insert; FIG. 26C is a side view of the completed cutting inert; FIG. 27 is a top view of a seventh specific embodiment of a cutting insert with a layer of PCD on a cemented tungsten carbide backing (or substrate); FIG. 28 is a front view of the cutting insert shown in FIG. 27; FIG. 29 is a side view of the axially forward portion of the bit body of a rotatable cutting bit WO 99/04128 PCT/US98/1 4358 -8having a pair of pockets and wherein the bit body receives a cutting insert of FIG. 27 in each one of the pockets thereof; FIG. 30 is a top view of the body of the rotatable cutting tool of FIG. 29 wherein there is shown one cutting insert brazed into one of the pockets; FIG. 31 is a side view of the axially forward portion of the bit body of the rotatable cutting bit of FIG. 29 rotated clockwise about 60 degrees from the position shown in FIG. 29; FIG. 32 is a top view of another embodiment of the cutting insert; FIG. 33 is a projected view normal to the leading surface of the cutting insert of FIG. 32; and FIG. 34 is a projected right hand view of the cutting insert of FIG. 32.

DETAILED DESCRIPTION Referring to the drawings, a rotatable cutting bit (or roof drill bit) generally designated as has an elongate bit body 32 with a forward end 34 and a rearward end 36, as well as a central longitudinal axis A-A (see FIG. Bit body 32 has a forward surface 37 which presents a generally frustoconical shape. The bit body 32 defines a cavity 38 therein. The bit body 32 further contains at the forward end 34 thereof a plurality of unobstructed debris evacuation passages 40 which communicate with the cavity 38 so as to provide communication between the cavity and the forward end of the bit body.

Although the specific embodiment illustrates a trio of equi-spaced peripheral debris evacuation passages and one central debris evacuation passage, applicants contemplate that any number of passage(s) in a suitable orientation or a single passage could be appropriate.

WO 99/04128 PCT/US98/14358 -9- Applicants also contemplate that the cutting bit body may not include any debris evacuation passages. The bit body 32 is of a generally cylindrical shape so as to present a peripheral (or generally cylindrical) surface 42.

Applicants also contemplate that the present roof bit may be used in a wet drilling operation. In a wet drilling operation, the passages 40 would function to provide a pathway for a flow of fluid water) to the forward end of the bit body, fluid would flow through the passages 40. Applicants also contemplate that for a wet drilling operation, the outside surface of the bit body may contain flats, or some other relief in the surface, so as to provide a passage for the fluid and debris to exit from near the cutting inserts.

Referring to FIG. 3, the bit body 32 further contains a trio of seats (or pockets) 46, each of which contains a cutting insert 60 of a first specific embodiment. Although the specific embodiment of FIGS. 1 and 2 shows three seats 46 and three cutting inserts 60, there is no intention to limit the invention to the use of three cutting inserts (and seats). Applicants contemplate that the invention would function with two or more cutting inserts (and seats). The dimension of the cutting bit body and the cutting inserts, as well as the particular cutting application, are factors which would influence the number of cutting inserts (and seats) presented by the rotatable cutting bit.

The following description of one seat 46 as illustrated in FIG. 3 will suffice for the description of the other two seats 46 since these three seats are essentially identical. Seat 46 presents a generally triangular shape. Seat 46 has a bottom surface 48.

Seat 46 also presents a generally radial side surface a generally chordal side surface 52, and a WO 99/04128 PCT/US98/14358 generally radial edge 54. In the specific embodiment, the radial edge 54 is generally flush with the surface of the bit body 32 at the forward end 34 thereof.

However, applicants do not intend to limit the invention to radial edge 54 being flush, but contemplate that radial edge 54 could have depth thereto. The seat 46 is defined by the bottom surface 48, the radial side surface 50, the chordal side surface 52, and the radial edge 54. The bottom surface 48 contains a threaded aperture 56 therein.

The reference to the side surface 50 and radial edge 54 as being generally radial means that the surface or the edge extends in a generally, although not precisely, radial fashion relative to (or from) the longitudinal axis of the bit body. The reference to the side surface 52 being generally chordal means that this surface extends in a generally, although not precisely, chordal fashion with respect to the generally circular periphery provided by the forward surface 37 of the bit body 32.

The radial side surface 50 does not have a juncture with the radial edge 54 because they have a relative orientation such that their intersection would exist at a Point into the central passage 40. The radial side surface 50 has a juncture with the chordal side surface 52 so as to define a first junction 57 which is near the peripheral surface of the bit body 32. As becomes apparent from the discussion below, the seat 46 is at its deepest height the seat has its greatest depth) at the first junction 57 since the seat 46 becomes deeper as it moves from the radial edge 54 to the first junction 57. In the specific embodiment shown in FIG. 3, the chordal side surface 52 does not have a juncture with the radial edge 54 because they have a relative orientation such that their intersection would exist at a point radially outside of the peripheral surface of the bit body. The WO 99/04128 PCT/US98/14358 -11seat 46 is at its shallowest height along the radial edge 54.

Referring back to the radial side surface as shown in FIG. 3, it typically increases in height as it moves (generally) radially outwardly from the longitudinal axis toward the peripheral surface 42 of the bit body 32. The extent of the change in height depends upon the difference in the orientation of the bottom surface 48 of the seat 46 with the orientation of the forward surface 37 of the bit body 32.

Referring to the chordal side surface 52, it increases in height as it moves from the peripheral surface 42 toward its juncture 57 with the radial side surface 50. This increase in height is due to the orientation of the bottom surface 48 of the seat 46.

The bottom surface 48 has an orientation so as to present a lead angle and a rake angle that orients the cutting insert 60 when in the seat 46 so that the cutting insert 60 has an insert rake angle and an insert lead angle The radial edge 54 is flush with the forward surface 37 of the bit body 32 along it entire length, but as mentioned above, applicants do not contemplate limiting the invention to where the radial edge 54 is flush with the forward surface 37.

Referring to FIGS. 1 and 2, it is preferable that rotatable cutting bit 30 mechanically retains cutting insert 60, which is indexable and presents a generally triangular shape. Even though mechanical retention is the preferred way to retain the cutting insert to the cutting bit, applicants do not intend to limit the invention to mechanical retention via a screw only, but expect to include other mechanical means for retention such as a lock pin arrangement, and other non-mechanical means such as epoxying, soldering, and even brazing when suitable. While a cutting insert of a generally triangular shape is the preferred geometry for the cutting insert, applicants contemplate that the WO 99/04128 PCT/US98/14358 -12cutting insert can take on other geometries such as any polygonal shape. Applicants also contemplate that the cutting insert may not be indexable and/or reversible, and may even take on an asymmetric shape.

FIGS. 1 and 2 show that there are three identical cutting inserts 60 so that a description of one cutting insert will suffice for all. Cutting insert 60 has a top surface 62, a bottom surface (not illustrated), a first generally radial side surface 66, a second generally chordal side surface 68, and a third generally radial side surface 70. First radial side surface 66 intersects the second chordal side surface 68 to form a first edge 72 which functions as the side clearance cutting edge when the cutting insert 60 is positioned in the bit body 32 as shown in FIGS. 1 and 2. The function of the side clearance cutting edge will be discussed in more detail hereinafter. Second chordal side surface 68 intersects with the third radial side surface 70 so as to form a second edge 74 which is radially inward of the peripheral edge of the bit body. The first radial side surface 66 intersects the third radial side surface 70 so as to form a third edge 76 which is near the central longitudinal axis of the bit body 32.

The first radial side surface 66 intersects with the top surface 62 to form a first cutting edge which in the orientation illustrated in FIG. 1 and 2 is a leading cutting edge and the function thereof will be described in more detail hereinafter.

The second chordal side surface 68 intersects with the top surface 62 to form a second cutting edge 82 when in the orientation of FIGS. 1 and 2. The third radial side surface 70 intersects the top surface 62 to form a third cutting edge 84 when in the orientation of FIGS. 1 and 2.

Cutting insert 60 contains an aperture 88 therein. Each cutting insert 60 is preferably WO 99/04128 PCTIUS98/1 4358 -13mechanically retained in its respective seat by the use of a pin or a screw 90 which passes through the aperture 88 and is received in the aperture 56 in the bottom surface 48 of the seat 46. Though less preferred, applicants contemplate that other ways press fitting, brazing) to retain the cutting insert to the cutting bit could be suitable for use herein.

There are three fundamental angles which describe the orientation of the cutting insert 60 in the seat. These angles are the lead angle the insert rake angle and the radial rake angle Referring to FIG. 1, the lead angle is defined as the included angle between a line E-E along the leading cutting edge of the cutting insert and a line F-F parallel to the center of rotation of the cutting bit and passing along the peripheral surface 42 of the bit body 32. The line E-E is the lead angle reference line. The lead angle can range between 50 degrees and 90 degrees. The preferred lead angle is 70 degrees.

The insert rake angle (see FIG. 1) is defined as the included angle between a line I-I normal to both the lead angle reference line E-E and line A-A and a line H-H lying along the top surface of the cutting insert 60 passing through the center of the leading cutting edge and the center of the second edge 74 wherein angle is measured in the vicinity of When the cutting insert has an orientation such that line H-H is leading line I-I upon forward penetration of the cutting bit in the direction of axial penetration, shown by arrow which occurs during drilling line H-H is above line the insert rake angle is positive. In the case where the cutting insert would have such an orientation that line H-H is trailing line I-I upon forward penetration of the cutting bit in the direction of axial WO 99/04128 PCT/US98/14358 -14penetration, shown by arrow which occurs during drilling line H-H is below line I-I as shown in FIG. the insert rake angle would be negative.

The insert rake angle varies from between a minimum of about 0 degrees (where lines I-I and H-H are coaxial) to a maximum of about negative 30 degrees (where line H-H trails line I-I by 30 degrees as shown in FIG. The preferred insert rake angle is about negative 20 degrees.

The radial rake angle is defined as the included angle between a radial line L-L from the central longitudinal axis A-A of the bit body which passes through the center "J of the leading cutting edge of the cutting insert and a line M-M formed along the leading cutting edge 80 of the cutting insert projected onto a plane perpendicular to centerline A-A (see FIG. When the cutting insert has an orientation at a point radially outwardly of the circumference of the cutting bit the point where angle is measured) where line M-M is trailing line L-L upon rotation of the cutting bit in the direction of rotation shown by arrow (which is the case as shown in FIG. the radial rake angle is negative. When the cutting insert has an orientation at a point radially outwardly of the circumference of the cutting bit the point where angle is measured) where line M-M is leading line L-L upon rotation of the cutting bit in the direction of rotation shown by arrow the radial rake angle "D" is positive. The radial rake angle can vary between a minimum of about positive 20 degrees an orientation in which line M-M leads line L-L by degrees) to a maximum of about negative 30 degrees an orientation in which line M-M trails line L-L by 30 degrees). The preferred radial rake angle is about negative 10 degrees.

WO 99/04128 PCT/US98/14358 In use, each cutting insert 60 presents two cutting edges which provide for the principal cutting (or drilling) activity. The leading cutting edge engages the earth strata and does most of the cutting of the earth strata. The edge 76 of the cutting insert also provides a starting contact point so as to reduce the amount of "walking" which may occur when starting to cut (or drill) a hole. The second cutting edge 82 and the third cutting edge 84 do not participate to a significant degree in the cutting function.

The clearance cutting edge 72, which extends radially past the peripheral surface, functions to cut the diameter of the hole and thereby provide for clearance between the peripheral surface 42 of the cutting bit 30 and the surface of the earth strata which defines the hole being cut. The second edge 74 and the third edge 76, except for providing a starting point, do not participate to a significant degree in the cutting function.

Cutting insert 60 is indexable. Thus, when cutting insert 60 is indexed counter-clockwise (see FIG. the second edge 74 then functions as the side clearance cutting edge. The second cutting edge 82 then functions as the leading cutting edge.

Where the cutting inserts are mechanically retained, the disadvantages associated with brazed-on cutting inserts are absent. Consequently, wear resistant materials, which have heretofore not been candidates for use in a roof drill bit, are now realistic candidates for cutting inserts. In this regard, exemplary materials include ceramics, low binder content (3 to 6 weight percent) tungsten carbide, binderless tungsten carbide, diamond or hard (chemical vapor deposition or physical vapor deposition) coated cemented carbides or ceramics, polycrystalline diamond [PCD composites with a metallic binder cobalt), polycrystalline WO 99/04128 PCT/US98/1 4358 -16diamond [PCD] composites with a ceramic binder silicon nitride), and polycrystalline cubic boron nitride [PcBN] composites.

Referring to FIG. 4 there is shown a second specific embodiment of the cutting bit body 32'. The principal difference between the second embodiment and the first embodiment of the bit body is that the seat of the second embodiment terminates radially inwardly of the peripheral surface. For structural features common between the first and second embodiments of the bit body, the reference numerals for the second embodiment are the same as those for the first, but are primed.

Cutting bit body 32' contains a seat 46' which presents a generally triangular shape. Seat 46' has a bottom surface 48'. Seat 46' also presents a generally radial side surface 50', a generally chordal side surface 52', and a generally radial edge 54'. The seat 46' is defined by the bottom surface 48', the radial side surface 50', the chordal side surface 52', and the radial edge 54'. The bottom surface 48' contains a threaded aperture 56' therein. The reasons for describing these edges as radial or chordal are the same as for the description of the first specific embodiment of the cutting bit body. The radial edge 54' intersects with the chordal side surface 52' to define a juncture 58' wherein juncture 58' is radially inward of the peripheral surface of the bit body. The chordal side surface 52' intersects with the radial side surface 50' to define a juncture 57'. The radial side surface 50' and the radial edge 54' do not intersect because they have a relative orientation such that their intersection would exist at a point into the central passageway Even though juncture 58' of the seat 46' terminates radially inwardly of the peripheral surface 42' of the bit body 32', the seat 46' has an WO 99/04128 PCT/US98/14358 -17orientation such that the side clearance cutting edge of a cutting insert still extends radially past the peripheral surface of the bit body. In this regard, seat 46' has a lead angle and a rake angle which orients the cutting insert therein in the desired disposition.

Referring to FIGS. 5 through 8, there is shown a second specific embodiment of a cutting insert generally designated as 100. For the sake of clarity FIG. 5 depicts the presence of only one cutting insert 100 and two empty seats 46; however, in actual use the cutting bit body 32 would contain three cutting inserts 100 with a cutting insert in each seat.

Cutting insert 100 has a top surface 102 and a bottom surface 104, as well as a first side surface 106, a second side surface 108, and a third side surface 110. The first side surface 106 and the third side surface 110 each have a generally radial orientation in that each one extends from a position near the central axis of the bit body 32 toward the peripheral surface 42 thereof. The second side surface 108 has a generally chordal orientation in that it generally extends along a line that extends between two points on the peripheral surface 42 of the bit body 32.

Each one of the side surfaces 106, 108, 110 has a generally vertical wall (or rim) 111 portion as shown in FIGS. 7 and 8. As described hereinafter, the presence of this vertical rim 111 facilitates the pressing of the cutting insert from powder components if the cutting insert is formed through powder metallurgical techniques. However, it should be appreciated that the rim 111 is not a mandatory feature, but optional, depending upon the manufacturing method used to make the cutting insert.

The cutting insert 100 also presents a first bevelled surface 112 at the juncture of the first side surface 106 and the second side surface 108, a second WO 99/04128 PCT/US98/14358 -18bevelled surface.114 at the juncture of the second side surface 108 and the third side surface 110, and a third bevelled surface 116 near the juncture of the third side surface 110 and the first side surface 106. Each bevelled surface (112, 114, 116) is disposed with respect to the top surface 102 of the cutting insert at an included angle (see FIG. 7) of about 110 degrees. Included angle may vary between about degrees and about 130 degrees depending upon the lead angle of the cutting insert for reasons expressed below.

The top surface 102 intersects with the first side surface 106 to form a first cutting edge 118. The top surface 102 intersects with the second side surface 108 to form a second cutting edge 120. The top surface 102 intersects with the third side surface 110 to form a third cutting edge 122. The cutting insert 100 contains an aperture 130 therein through which a screw 131 passes so as to mechanically retain the cutting insert to the bit body.

When in the position shown by FIG. 5, the first cutting edge 118 is the leading cutting edge.

The second cutting edge 120 and the third cutting edge 122 do not participate significantly in the cutting operation. The intersection of the first bevelled surface 112 and the first side surface 106 functions as the clearance cutting edge 113. Typically, the included angle corresponds to the lead angle in that it approximately equals 180 degrees less the amount of the lead angle. Because of this relationship, when the cutting insert 100 is in seat 46, the first bevelled surface 112 has an orientation that is generally parallel to the longitudinal axis A-A of the bit body 32. In such an orientation the bevelled surface 112 intersects with the first side surface 106 so as to define a first side clearance cutting edge 113 at such intersection. The cutting of WO 99/04128 PCT/US98/14358 -19the diameter of the hole is done over the first side clearance cutting edge 113. Typically, there is at least a small amount of relief of the first side clearance cutting edge 113.

The cutting insert 100 is indexable. When the cutting insert 100 is indexed counterclockwise (see FIG. the second cutting edge 120 becomes the leading cutting edge and the second bevelled surface 114 intersects the second side surface 108 to form a second side clearance cutting edge 115 at such intersection. The cutting of the hole diameter is done over the second side clearance cutting edge 115. When the cutting insert 100 is again indexed in a counterclockwise direction (see FIG. the third cutting edge 122 becomes the leading cutting edge.

Furthermore, the third bevelled surface-116 intersects the third side surface 110 so as to form a third side clearance cutting edge 117 at such intersection. The cutting of the diameter of the hole is done over the third side clearance cutting edge 117.

Referring to FIGS. 9 through 12 there is shown a third specific embodiment of the cutting insert generally designated as 140. Cutting insert 140 has a top surface 142 and a bottom surface 144, as well as a first side surface 146, a second side surface 148, and a third side surface 150. When in the position shown by FIG. 9, the first side surface 146 and the third side surface 150 have a generally radial orientation in that each surface (146, 150) extends from a point near the central longitudinal axis of the bit body 32 toward the peripheral edge 42 of the forward surface of the bit body 32. Each one of the side surfaces 146, 148, 150 has a generally vertical wall (or rim) 151 portion.

As described hereinafter, the presence of this vertical rim 151 facilitates the pressing of the cutting insert from powder components if the cutting insert is formed through powder metallurgical techniques. Like WO 99/04128 PCT/US98/14358 mentioned above, however, the presence of the rim 151 is an optional feature depending upon the manufacturing method of the cutting insert.

The cutting insert 140 also presents a first relieved surface 152 at the juncture of the first side surface 146 and the second side surface 148, a second relieved surface 154 at the juncture of the second side surface 148 and the third side surface 150, and a third relieved surface 156 at the juncture of the third side surface 150 and the first side surface 146. The degree of the relief may vary depending upon the specific application. The preferred degree of relief is such that when the cutting insert is in the seat, each relieved surface intersects with its corresponding side surface so as to define a side clearance cutting edge that is generally parallel to the peripheral surface of the cutting bit body. The relieved surfaces (152, 154, 156) may be entirely arcuate as shown or, in the alternative, each relieved surface may have a planar portion adjacent to the side surface of the cutting insert which blends into an arcuate portion as the relieved surface moves around the periphery of the cutting insert.

The top surface 142 intersects with the first side surface 146 to form a first cutting edge 158. The top surface 142 intersects with the second side surface 148 to form a second cutting edge 160. The top surface 142 intersects with the third side surface 150 to form a third cutting edge 162. The cutting insert 140 contains an aperture 170 therein through which a screw 171 passes so as to mechanically retain the cutting insert 140 to the bit body 32. When in the position shown by FIG. 9, the first cutting edge 158 is the leading cutting edge, and the first relieved surface 152 intersects with the first side surface 146 to form a first side clearance cutting edge 153. When in the position illustrated in FIG. 9, the second and WO 99/04128 PCT/US98/14358 -21third cutting edges (160, 162) do not participate to a significant extent in the cutting operation.

Like for the second embodiment of the cutting insert, the third embodiment of the cutting insert 140 is indexable. When indexed in a counterclockwise direction as shown in FIG. the second cutting edge 160 becomes the leading cutting edge and the second relieved surface 154 intersects the second side surface 148 so as to define a second side clearance cutting edge 155. The cutting insert 140 may be indexed again in a counterclockwise direction (see FIG. 9) so that the third cutting edge 162 is the leading cutting edge.

The third relieved surface 156 intersects the third side surface 150 so as to define a third side clearance cutting edge 157 at the intersection thereof. The cutting of the diameter of the hole is done by one of the three side clearance cutting edges (153, 155, 157) depending upon the position of the cutting insert.

Referring to FIGS. 13 through 16, there is illustrated a fourth specific embodiment of a cutting insert, generally designated as 180, intended to be used with the bit body 32 depicted in FIG. i. Cutting insert 180 has a generally equilateral triangular top surface 182 and a generally equilateral triangular bottom surface 184. The inscribed circle 182A, i.e., the largest circle which can be imposed in the inside of the cutting insert, of the top surface 182 is less than the inscribed circle 184A of the bottom surface 184. Furthermore, the top surface is rotated about a central axis 0-0 perpendicular to the top surface 182 and relative to the bottom surface 184 about 6 degrees as shown by angle in FIG. 14. Angle is defined as the included angle between two lines wherein both lines originate from axis 0-0 of cutting insert 180.

One line passes through the point where edge 202 intersects the top surface 182 of the cutting insert and lies in a plane perpendicular to axis 0-0 and in WO 99/04128 PCT/US98/1 4358 -22which the above-mentioned point of intersection (edge 202 intersects top surface 182) lies. The other line passes through the point where edge 202 intersects the bottom surface 184 of the cutting insert and lies in a plane perpendicular to axis 0-0 and in which the abovementioned point of intersection (edge 202 intersects bottom surface 184) lies. To define angle the lines are projected so as to lie in the same plane which is perpendicular to the axis 0-0.

The cutting insert 180 has a first side surface 186, a second side surface 188, and a third side surface 190. Because of the rotation of the top surface 182 relative to the bottom surface 184, the orientation of each side surface (186, 188, 190) relative to the top surface 184 of the cutting insert 180 changes along the length of the side surface (186, 188, 190) as will be discussed hereinafter.

The top surface 182 of the cutting insert 180 intersects with the first side surface 186 to form a first cutting edge 192. The top surface 182 of the cutting insert 180 intersects with the second side surface 188 to form a second cutting edge 194. The top surface 182 of the cutting insert 180 intersects with the third side surface 190 to form a third cutting edge 196.

The first side surface 186 and second side surface 188 intersect to form a first cutting edge 198.

The second side surface 188 and third side surface 190 intersect to form a second cutting edge 200. The third side surface 190 and first side surface 186 intersect to form a third cutting edge 202.

Referring to the orientation of the first side surface 186, when the side surface 186 is at the edge 198 it has an orientation so as to be generally perpendicular to the top surface 182 of the cutting insert 180. At the edge 202, first side surface 186 has an orientation so as to have an included angle "Q" WO 99/04128 PCT/US98/14358 -23between itself and the top surface 182 of about 110 degrees. Over the length of the side surface 186, the orientation thereof consistently changes from being generally perpendicular to the top surface 182 to being disposed at about 110 degrees from the top surface 182.

The same orientation, and change of orientation over the length, exists for the other two side surfaces. In this regard, second side surface 188 has a generally perpendicular orientation with respect to the top surface at edge 200. The orientation of second side surface 188 changes along its length from edge 200 toward edge 198 so that at edge 198 side surface 188 is disposed at an included angle of about 110 degrees with respect to the top surface 182. Third side surface 190 has a generally perpendicular orientation with respect to the top surface at edge 202. The orientation of third side surface 190 changes along its length from edge 202 toward edge 200 so that at edge 200 side surface 190 is disposed at an included angle of about 110 degrees with respect to the top surface 182. The maximum included angle of disposition included angle may range between about degrees and about 130 degrees depending upon the lead angle of the cutting insert. The preferred angle of disposition 'IQ" is about 11i0degrees. Typically, this angle of disposition corresponds to the lead angle in that included angle equals 180 degrees less the amount of the lead angle. Because of this relationship, when the cutting insert 180 is in seat 46, the first edge 198 has an orientation that is generally parallel to the longitudinal axis A-A of the bit body 32. Such an orientation permits the first edge 198 to present a side clearance cutting edge wherein the cutting of the diameter of the hole is done over the clearance cutting edge.

The cutting insert 180 has a generally vertical wall (or rim 204) portion near the bottom of WO 99/04128 PCT/US98/14358 -24each one of the side surfaces (186, 188, 190). As will be mentioned hereinafter, the presence of the vertical rim facilitates the pressing of the powder components of the cutting insert if it is made via powder metallurgical techniques. As mentioned above, the presence of the rim 204 is an optional feature depending upon the manufacturing method. The cutting insert 180 contains an aperture 208 through which passes a screw 209 that mechanically retains the cutting insert 180 to the bit body. In the orientation shown in FIG. 13, the first cutting edge 192 functions as the leading cutting edge and the first edge 198 functions as the side clearance cutting edge. Like for earlier cutting inserts, this embodiment of the cutting insert 180 is indexable. When cutting insert 180 is indexed counterclockwise (see FIG. 13), the second cutting edge 194 functions as the leading cutting edge and the second edge 200 functions as the side clearance cutting edge.

Referring to FIGS. 17 through 20 there is illustrated a fifth specific embodiment of the cutting insert, generally designated as 216, which is suitable for use with the bit body 32 of FIG. 1. Cutting insert 216 is a reversible cutting insert.

In the orientation shown in FIGS. 17 and cutting insert 216 has a top surface 218 and a bottom surface 220. Cutting insert 216 also has a first side surface 222, a second side surface 224, and a third side surface 226. There is a first bevelled surface 228 at the juncture of the first side surface 222 and the second side surface 224 wherein the bevelled surface 228 is near the top surface 218 of the cutting insert 216. There is a second bevelled surface 230 at the juncture of the third side surface 226 and the first side surface 222 wherein the bevelled surface 230 is near the bottom surface 220 of the cutting insert 216. The top surface 218 intersects the first side WO 99/04128 PCT/US98/1 4358 surface 222 to from a first cutting edge 232. The bottom surface 220 intersects the first side surface 226 to form a second cutting edge 234.

The first bevelled surface 228 is disposed with respect to the top surface 218 at an included angle equal to about 110 degrees. The second bevelled surface 230 is disposed with respect to the bottom surface 220 at an included angle equal to about 110 degrees. Included angles and may range between about 90 degrees and about 130 degrees depending upon the lead angle of the cutting insert.

The cutting insert has a top rim 236 of material about a portion of the top surface 218. The cutting insert has a bottom rim 238 of material about a portion of the bottom surface 220. As will be mentioned hereinafter, the presence of the top rim 236 and the bottom rim 238 facilitates the pressing of the powder components of the cutting insert if the cutting insert is made via powder metallurgical techniques. The rims 236, 238 are optional features depending upon the method for manufacturing the cutting insert.

When the cutting insert 216 is oriented so that the top surface 218 is in an exposed position, the first bevelled surface 228 defines the side clearance cutting edge and the first cutting edge 232 is the leading cutting edge. When the cutting insert 216 is oriented so that the bottom surface 220 is in an exposed position, the second bevelled surface 230 defines the side clearance cutting edge and the second cutting edge 234 is the leading cutting edge.

In order to demonstrate the performance of the roof drill bit of the instant invention using cutting inserts with different grades of cemented tungsten carbide (see Compositions Nos. 1, 2, 3 and 4 in Table I) as compared with a conventional style of roof drill bit using a cutting insert in one grade of WO 99/04128 PCT/US98/14358 -26cemented tungsten carbide Composition No. 1 in Table I).

Table I Compositions and Physical Properties of Compositions Nos. 1-4 Grade Cobalt Ti Ta Nb Other HC RA Comp. No. 1 6.2 .3 115 89.7 Comp. No. 2 6.0 V=0.2 350 93.3 Comp. No. 3 7.9 .3 110 89.4 Comp. No. 4 5.7 1.9 265 92.7 The compositions are set forth in weight percent wherein the balance of each one of the above compositions is tungsten carbide. The coercive force (HC) is set forth in oersteds and the hardness is set forth in Rockwell A.

The test results are set forth in Table II below. In this regard, in Table II Comparative Bit No. 1 was a roof drill bit made by Kennametal Inc. of Latrobe, PA (USA) under the designated KCV4-1 (see Kennametal Mining Products Catalog A96-55(15)H6 at page 20) using a cemented tungsten carbide cutting insert of Composition No. 1, as set forth above. In Table II, Comparative Bit No. 2 was a roof drill bit made by Kennametal Inc. of Latrobe, PA (USA) under the designated KCV4-1RR (Roof Rocket) [see Kennametal Mining Products Catalog A96-55(15)H6 at page 20] using a cemented tungsten carbide cutting insert of Composition No. 1, as set forth above.

Invention Nos. 1, 2, 3, and 4 in Table II below were each a roof drill bit with a structure along the lines of the specific embodiment of FIG. 1 using a tungsten carbide cutting insert of Composition Nos. 1, 2, 3 and 4 (Table respectively.

WO 99/04128 PCT/US98/14358 -27- Table II Test Results for Drilling in Sandstone Samle Rotational Speed Hole Depth Average Feed Average Thrust Average Torque ,t (RPM) (inches) Rate (in/second) (Ibs.) (in-lbs) Invention No. 1 406 164.6 2.1 2479 1145 Invention No. 2 418 165.1 1.99 2137 1125 Invention No. 3 404 162.6 2.16 2403 1209 Invention No. 4 401 166.7 1.96 2342 1323 Comparative No. 1 418 165 1.34 2619 919 Comparative No. 2 409 157.2 1.68 2433 1104 The test results and parameters comprise the rotational speed in revolutions per minute (RPM), the depth of the hole in inches at the completion of the test, the average feed rate of the drill bit in inches per second (in./second), the average thrust of the drill bit into the substrate in pounds and the average torque of the drill bit in inch-pounds (in-lbs). The test results show that the penetration rates for the roof drill bits of the invention are meaningfully higher than for the conventional roof drill bits. A comparison of the roof drill bit of the invention (Invention No. 1) against the conventional KCV4-1 roof drill bit in the same carbide grade shows that the present invention had a penetration rate of 2.1 inches/second at an average thrust of 2479 Ibs. as compared to a penetration rate of 1.34 inches/second at a slightly higher average thrust of 2619 lbs. The present invention experienced an increase in penetration rate of about 56.7 percent at a somewhat lower average thrust. A comparison of the same roof drill bit (Invention No. 1) against the other conventional roof drill bit, KCV4-1RR (Roof Rocket) in the same carbide grade, reveals that the present invention experienced an increase in the penetration rate of about 25 percent at almost the same average thrust (2479 lbs. vs. 2433 lbs.).

-e WO 99/04128 PCTIUS98/14358 -28- A comparison of the roof drill bit of the specific embodiment of the invention tested against the KCV4-1 roof drill bit in different carbide grades shows that for all of the carbide grades tested the present invention had an increase in the penetration rate at a lesser average thrust. For the roof drill bit of the invention (Invention No. 2) having a lower cobalt content and higher hardness than the carbide grade of the conventional roof drill bit, there was an increase in the penetration rate of about 48.5 percent at an average thrust which was meaningfully lower (2137 lbs.

vs. 2619 lbs.). For the roof drill bit of the invention (Invention No. 3) having a higher cobalt content and a similar hardness, the roof drill bit of the invention had an increase in the penetration rate of about 61.2 percent at a lower average thrust (2403 Ibs. vs. 2619 lbs.). For the roof drill bit (Invention No. 4) having a lower cobalt content and a higher hardness there was an increase in the average penetration rate of about 46.3 percent at a lower average thrust (2342 lbs. vs. 2619 lbs.).

A comparison of the roof drill bit of the invention against the KCV4-1RR (Roof Rocket) roof drill bit in different carbide grades shows that for all of the carbide grades tested the present invention had an increase in the penetration rate at a lesser average thrust. For the roof drill bit of the invention (Invention No. 2) having a lower cobalt content and higher hardness than the carbide grade of the conventional roof drill bit, there was an increase in the penetration rate of about 18.4 percent at an average thrust which was lower (2137 Ibs. vs.

2433 lbs.). For the roof drill bit of the invention (Invention No. 3) having a higher cobalt content and a similar hardness, the roof drill bit of the invention had an increase in the penetration rate of about 28.6 percent at about the same average thrust (2403 lbs.

WO 99/04128 PCT[US/1 4358 -29vs. 2433 lbs.). For the roof drill bit (Invention No. 4) having a lower cobalt content and a higher hardness there was an increase in the average penetration rate of about 16.7 percent at a lower average thrust (2342 lbs. vs. 2433 lbs.). These test results show that the roof drill bit of the present invention provides for an improvement in the average penetration rate while decreasing the magnitude of the average thrust.

Table III below sets forth the results of wear testing in sandstone of the cutting insert of roof drill bits according to the present invention, a roof drill bit with the structure depicted in FIG. 1 hereof, and conventional roof drill bits. The identification of the roof drill bits in Table III corresponds in structure and in the composition of the cutting insert to that of the roof drill bits of Table II. A wear scar was inscribed in each cutting insert and measured beginning at the plane of the original leading edge of the cutting insert to the point towards the trailing edge where wear was noted.

The measurement was done at the outside diameter (OD) of the cutting edge and at the positions along the cutting edge the indicated distance (inches) away from the outside diameter until reaching the inside diameter The wear scar length was then normalized to the actual cut depth for each cutting edge. The results are set forth in Table III. The results are also plotted in FIG. 21.

WO 99/04128 PCT/US98/14358 Table III Normalized Wear Scar (Inches) Test Results Roof Bit/Distance O.D. 0.016 0.03 0.045 0.08 from 0.D. (in.) Invention No. 1 -0.13 -0.10 -0.10 -0.10 -0.10 Invention No. 3 -0.17 -0.11 -0.11 -0.11 -0.10 Invention No. 2 -0.07 -0.03 -0.01 -0.01 0.00 Invention No. 4 -0.17 -0.08 -0.05 -0.03 -0.02 Comparative No. 1 -0.21 -0.18 -0.18 -0.12 -0.12 Comparative No. 2 -0.12 -0.09 -0.08 -0.08 -0.08 Roof Bit/ Distance 0.09 0.12 0.18 0.3 I.D.

from O.D. (in.) Invention No. 1 -0.10 -0.10 -0.09 -0.08 -0.07 Invention No. 3 -0.10 -0.10 -0.09 -0.09 -0.09 Invention No. 2 -0.00 -0.00 -0.00 -0.00 0.00 Invention No. 4 -0.02 -0.01 -0.01 -0.01 -0.01 Comparative No. 1 -0.10 -0.09 -0.07 -0.05 -0.04 Comparative No. 2 -0.08 -0.07 -0.06 -0.04 -0.04 These test results and plotted in FIG. 21, show set forth in Table III, that the amount of wear at the critical O.D. location is better for the roof drill bit of the invention than the KCV4-1 roof drill bit when using the same grade of carbide. In this regard, the wear for the invention is -0.13 as compared to -0.21 for the KCV4-1 roof drill bit. The wear between the roof drill bit of the invention and the KCV4-1RR is about the same with the conventional roof drill bit having a slightly better wear (-0.12 vs. The harder carbide grade used in Invention No. 2 showed better wear against both styles of conventional roof drill bits. The grades used in Invention Nos. 3 and 4 showed better wear than the KCV4-1 roof drill bit (-0.17 vs. but not as good as wear against the KCV4-1RR roof drill bit (-0.17 vs. -0.12).

WO 99/04128 PCT/US98/14358 -31- Applicants contemplate using other compositions of cobalt cemented carbide for the cutting insert wherein these compositions include one composition comprising 6.0 weight percent cobalt with the balance being tungsten carbide, and having a coercive force (H

C

equal to 350 oersteds and a hardness equal to 93.3 Rockwell A. These compositions also include another composition comprising 5.7 weight percent cobalt with the balance being tungsten carbide, and a coercive force (HC) equal to 265 oersteds and a hardness equal to 92.7 Rockwell A.

Furthermore, applicants contemplate using cobalt cemented tungsten carbide compositions wherein the hardness is greater than or equal to 90.5 (RA) Rockwell A or using cobalt cemented tungsten carbide compositions wherein the hardness is greater than or equal to 91 (RA) Rockwell A. In addition, other compositions which applicants contemplate using a cobalt cemented tungsten carbide composition having a coercive force (H

C

greater than or equal to 160 oersteds, and a cobalt cemented tungsten carbide composition having a coercive force (Hc) greater than or equal to 180 oersteds.

Referring to FIGS. 32 through 34 there is shown another specific embodiment of a cutting insert generally designated as 500. Cutting insert 500 comprises a cemented tungsten carbide material of the Composition No. 1 of Table I hereof. The geometry of cutting insert 500 is generally along the lines of the geometry of the cutting insert 100 (the embodiment of FIGS. but cutting insert 500 has only one clearance cutting edge since it is not indexable contrary to cutting insert 100 which is indexable.

Cutting insert 500 also does not have a center hole since it is brazed to the seat as opposed to being screwed to the seat like cutting insert 100. The preferred braze alloy for brazing cutting insert 500 to WO 99/04128 PCT/US98/14358 -32the seat of the bit body is HANDY HI-TEMP 548 braze alloy available from Handy Harman, Inc., 859 Third Avenue, New York, New York 10022. HANDY HI-TEMP 548 braze alloy is composed of 55+1.0 weight percent Cu, 6+0.5 weight percent Ni, 4±0.5 weight percent Mn, 0.15+0.05 weight percent Si, with the balance zinc and 0.50 weight percent maximum total impurities. Further information on HANDY HI-TEMP 548 braze alloy can be found in Handy Harman Technical Data Sheet No. D-74 available from Handy Harman, Inc.

Cutting insert 500 has a top surface 502, a bottom surface 504, a leading surface 506, and a trailing surface 508. Cutting insert 500 further has a radially inward side surface 510, a radially inward relief surface 512, a radially outward side surface 514, a radially outward relief surface 516, and a radially outward bevelled surface 520.

The intersection of the top surface 502 and the leading surface 506 defines a leading cutting edge 524. The intersection of the bevelled surface 520 and the leading surface 506 defines a clearance cutting edge 528.

Tests were conducted using the embodiment of the cutting insert FIGS. 32 through 34 (made from Composition No. 1) affixed to a cutting bit body along the lines of the cutting bit body shown in FIGS. through 8. The orientation of the cutting insert was such so that the clearance cutting edge was generally parallel to the longitudinal axis of the cutting bit body. The drilling was done into a type of sandstone with a compressive strength of 19,000 pounds per square inch (psi). This is compared to the weaker sandstone used for the tests of Table II wherein the weaker sandstone had a compressive strength of 8000 psi. The test results for testing these cutting inserts (which look like cutting insert 500) are set forth in Table IV below.

WO 99/04128 PCT/US98/1 4358 -33- Table IV Test Results for Drilling in Sandstone Using the Cutting Insert 500 Sample Number of Rotational Hole Depth Average Feed Average Average Holes Drilled Speed (RPM) (inches) Rate (inches Torque Thrust per second) (inch- (pounds) pounds) 1 first hole 424 16.3 [total 0.38 1370 2200 depth for the first hole only] 1 second hole 414 21.6 [total 0.48 2280 3000 depth for the second hole only] 2 three holes 411 59.5 [total 0.90 2330 3500 depth for all three holes] 3 two holes 398 40.1 [total 1.55 2550 4050 depth for all two holes] Referring to Table IV, the columns identified as "Sample" and "Number of Holes Drilled" indicate the sample which was used and the actual number of holes drilled by that sample, respectively. More specifically, Sample 1 was used to drill two holes, the first hole (at an average thrust of 2200 pounds) and the second hole (at an average thrust of 3000 pounds), wherein the respective depths of the holes were 16.3 inches and 21.6 inches. Thus, Sample 1 drilled holes totalling a depth of 37.9 inches at two different average thrust levels. Sample 2 was used to drill three holes at an average thrust of 3500 pounds for a total depth of 59.5 inches. Sample 3 was used to drill two holes at an average thrust of 4050 pounds for a total depth of 40.1 inches. The column identified as the "Rotational Speed" was the speed of rotation of the cutting bit in revolution per minute (RPM). The column identified as the "Hole Depth" sets forth the depth in inches of each drilled hole. The column identified as the "Average Feed Rate" sets forth the average rate of axial feed of the cutting bit in inches per second.

The column identified as "Average Torque" sets forth WO 99/04128 PCT/US98/14358 -34the average torque in inch-pounds. The column identified as "Average Thrust" sets forth the average thrust in pounds.

The test results of Table IV show that drilling in the higher strength sandstone, earth strata, leads to a reduction in the average feed rate for a given thrust level as compared to the test results set forth in Table II hereof. In addition, it can be seen that when drilling in the higher strength sandstone, an increase in the thrust levels resulted in an increase in the average feed rate. Wear scar inspections after completion of each drilled hole showed that the cutting inserts performed better at higher thrust levels because they had smaller wear scars for the same distance drilled as compared to drilling at lower thrust levels.

It becomes apparent that applicants have provided an improved rotatable cutting bit, as well as an improved cutting insert and an improved bit body for a rotatable cutting bit. There are a number of advantages associated with the instant invention.

The mechanical retention of the cutting inserts to the bit body increases the number of materials which may now be viable candidates for use as the cutting insert. Some of these materials are identified above and their use provides an opportunity to improve the overall efficiency of the cutting or drilling operation.

The mechanical retention through the use of a screw passing through an aperture in the cutting insert so as to be received in a threaded aperture in the seat in the bit body makes it easy to attach or detach the cutting insert to or from the bit body. Thus, the operator in the mine environment may easily switch out used (or worn) cutting inserts for new (or reground) cutting inserts. The operator may also easily index the cutting insert to present a new leading cutting WO 99/04128 PCTIUS98/14358 edge. The ability to easily make this switch (or index the cutting insert) in the mine environment without the need for special (or expensive) equipment will reduce the costs associated with the cutting operation.

In some of the embodiments the cutting insert presents a side clearance cutting edge which is generally parallel to the peripheral surface of the bit body, as well to the central longitudinal axis of the bit body. Due to this orientation, the side clearance cutting edge cuts the diameter of the hole along an edge surface and thus provides for adequate clearance between the bit body and the earth strata which defines the hole.

It is advantageous that the specific embodiments of the cutting inserts provide protection, at least to some extent, for the cutting edges which are not involved in the principal cutting activities.

By providing this protection, the cutting ability of the cutting insert is not diminished when the cutting insert is indexed or reversed.

Specific embodiments of the cutting insert also provide for there to be a 90 degree corner a vertical wall or rim) at the bottom surface of the indexable cutting inserts and at both the top and bottom surfaces of the reversible cutting insert. The existence of this 90 degree corner reduces the chance that the press operator will damage the tooling when forming the part via pressing a powder mixture because the rim allows clearance between the tooling punch and die set. The existence of the 90 degree corner also helps seat the cutting insert so that it is securely positioned within the seat.

Referring to FIGS. 22 through 26C, there is illustrated a specific embodiment of a roof drill bit, a rotatable cutting tool, generally designated as 290 in FIG. 22. Roof drill bit 290 has an elongate bit body 292, typically made of steel, with an axially WO 99/04128 PCT/US98/1 4358 -36forward end 294 and an axially rearward end 296. The forward end 294 of the bit body 292 contains a plurality of vacuum or fluid ports 298 wherein the preferred mode of operation for the bit is vacuum, but the bit can be used wet. A trio of cutting inserts, generally designated as 300, are affixed by brazing to corresponding seats (not illustrated) in the forward end 294 of the bit body 292. Because this rotatable cutting bit cuts at a lower temperature, cooler, than earlier bits, a lower temperature braze alloy is acceptable to braze the cutting insert to the bit body.

One type of an acceptable braze alloy is a low temperature silver-based braze alloy which is suitable for the joinder of steel and cobalt cemented tungsten carbide. One preferred braze alloy is the silver-based braze alloy sold under the designation EASY-FLO 45 by Handy Harman of New York, New York (USA). This braze alloy has a composition of 15 weight percent copper, 16 weight percent zinc, 45 weight percent silver, and 24 weight percent cadmium, and a melting point of 1125 0

F.

Each cutting insert 300 has a generally triangular shape, but it should be appreciated that other geometric shapes such as trapezoids or parallelograms may be appropriate geometries for the cutting insert. Each cutting insert 300 may have an orientation to the bit body 292 when brazed thereto like the orientation of cutting insert 60 to the bit body 32 as illustrated in FIGS. 1 and 2. Furthermore, the range of possible orientations of cutting insert to bit body 32 is also available for the orientation of the cutting insert 300 to the bit body 292.

FIG. 24 illustrates a cylindrical blank, generally designated as 302, which comprises a thicker backing 304 and a thinner layer 306 of polycrystalline diamond material. Generally, the backing 304 is at least about five times, and preferably about seven WO 99/04128 PCT/S98/1 4358 -37times, and even more preferably about ten times, thicker than the layer of polycrystalline diamond 306.

Backing 304 is typically made from a cobalt cemented tungsten carbide material wherein the cobalt content may range between about 8 weight percent and about weight percent with the balance being tungsten carbide.

The first step in the process to make the cutting insert 300 is to cut out electric discharge machining [EDM]) a blank from the cylindrical blank 302. Referring to FIG. 24, a blank 308 is shown by dashed lines in the volume of the cylindrical blank 302. The blank 308 has a backing 310 of cemented tungsten carbide and a layer of polycrystalline diamond 312.

As shown by FIG. 25, the overall thickness of the rectangular blank 308 is The backing 310 has a thickness and the polycrystalline diamond layer 312 has a thickness In an actual sample, the backing 310 may have a thickness "jj" which ranges between about 3.5 to about 9.5 millimeters The polycrystalline diamond layer 312 may have a thickness "kk" which ranges between about 0.5 to about 1.5 mm.

The preferred thickness "jj" of the backing 310 is about 7.3 mm. The preferred thickness "kk" of the polycrystalline diamond layer 312 is about 0.7 mm. The overall thickness "ii" thus ranges between about 4.0 mm to about 11.0 mm with the preferred overall thickness "ii" equalling about 8.0 mm.

Referring to FIG. 26B, in the process of making the blank 308 via EDM machining material is removed, EDM machined, from the side surfaces of the backing 310 and the polycrystalline diamond layer 312. These side surfaces are EDM machined along the lines ee-ee and gg-gg illustrated in FIG. 26B.

Line ee-ee is disposed at an included angle "ff" with respect to the adjacent side surface of the polycrystalline layer 312 of the partially completed WO 99/04128 PCT/US98/14358 -38cutting insert blank. Line gg-gg is disposed at an included angle "hh" with respect to the adjacent side surface of the polycrystalline layer 312 of the partially completed cutting insert blank. Angle "ff, may range between about ten degrees and about fortyfive degrees with a preferred angle "ff" being about twenty degrees. Angle "hh" may range between about twenty degrees and about eighty degrees with a preferred angle "hh" being about seventy degrees.

Line ee-ee defines the radially outward side of the cutting insert that is near the periphery of the cutting bit body when the cutting insert is affixed thereto. It should be appreciated that line ee-ee has an orientation so as to define a side clearance wherein the bevelled portion defines a cutting edge (as described hereinafter) of a sufficient dimension so as to avoid "rifling", and thus, create a bore hole defined by a generally smooth bore wall. Line gg-gg has an orientation so that the cutting edge (as described hereinafter) defined by the radially inward bevelled portion is of such a dimension so as to reduce the tendency of the cutting insert to break upon initial impingement of the earth strata.

Referring to FIG. 25, after completion of the EDM machining of the blank, the next step is to grind the backing 310 of the blank 308 along the grind lines aa-aa and bb-bb. These grind lines (aa-aa and bb-bb) are disposed at an included angle of "cc" degrees and an included angle of "dd" degrees, respectively, with respect to the adjacent side surface of the blank 308.

Angle "cc" may range between about fifteen degrees and about forty-five degrees with a preferred angle "cc" being about thirty degrees. Angle "dd" may range between zero degrees and about forty-five degrees with the preferred angle "dd" being about thirty degrees.

FIG. 25 illustrates angles "cc" and "dd" as being equal; however, it is contemplated that these WO 99/04128 PCTIUS98/1 4358 -39angles and may not necessarily be equal.

At this stage of the process the cutting insert blank may be characterized as a partially completed cutting insert blank.

It should be appreciated that the backing 310 now presents a geometry that has sufficient relief so as to not interfere with the cutting by the cutting edges of the polycrystalline diamond layer. In other words, the backing 310 does not directly impinge upon the earth strata during the cutting drilling) operation. In this regard, the radially outward side surface as defined by angle "cc" must have a sufficient relief while the radially inward side surface defined by angle "dd" may not have to have any relief so as to maximize the mass of the backing, if necessaryso as to be suitable for a particular application.

After completion of the grinding of the partially completed cutting insert blank, except for treating the cutting edges, the process to make the cutting insert 300 is complete. As is discussed hereinafter, the cutting edges are typically treated, honed and/or chamfered and/or impinged with an abrasive media in a fluid medium, so as to remove the sharpness therefrom.

Referring to structure of the cutting insert 300, cutting insert 300 comprises a backing (or substrate) 310 and a polycrystalline diamond layer 312 which is on the backing 310. The backing 310 has a top surface 316, a bottom surface 318, a leading surface 320, and a trailing surface 322. The surface area of the bottom surface 318 of the backing 310 is greater than the surface area of the leading surface 320. The bottom surface 318 provides the major area for brazing the cutting insert to the cutting bit body. The backing 310 further has one side surface 324 which has a bevelled portion 326 wherein the bevelled portion 326 is a result of EDM machining along line ee-ee. The WO 99/04128 PCTIUS98/14358 backing 310 also has another side surface 328 which has a bevelled portion 330 wherein the bevelled portion 330 is the result of EDM machining along line gg-gg.

The polycrystalline diamond layer 312 has a top surface 332, a bottom surface 334, a leading surface 336, and a trailing surface 338. The polycrystalline layer 312 further has one side surface 340 which has a bevelled portion 342 wherein bevelled portion 342 is a result of EDM machining along line ee-ee. The polycrystalline diamond layer 312 also has another side surface 344 which has a bevelled portion 346 wherein bevelled portion 346 is a result of EDM machining along line gg-gg. As illustrated in FIG. 26B, the trailing surface 338 of the polycrystalline layer 312 is adjacent to the leading surface 320 of the backing 310.

Referring now to the edges of the cutting insert 300, the intersection of the leading surface 336 and the bevelled portion 346 defines a cutting edge 351. The intersection of the top surface 332 and the leading surface 336 defines another cutting edge 348.

The intersection of the bevelled portion 342 of the side surface 340 with the leading surface 336 defines still another cutting edge 350. The intersection of the non-bevelled portion of the side surface 340 with the leading surface 336 defines a side edge 352 that generally does not perform a cutting function in that it does not directly impinge the earth strata during the cutting operation.

Referring to FIGS. 22 and 23, it can be appreciated that the cutting edges 348, 350 and 351 comprise the cutting edges that engage the earth strata during the operation of the rotatable cutting bit wherein the cutting edge 351 first engages the earth strata while cutting edge 350 cuts the side clearance for the hole. It should be appreciated that these cutting edges (348, 350 and 351) are preferably honed WO 99/04128 PCTIUS98/14358 -41or chamfered at the intersection of the surfaces. The presence of such a hone or chamfer will reduce the potgntial for chipping or cracking of the polycrystalline diamond layer at these intersections.

Referring to the specific embodiment set forth in FIGS. 27-31, there is illustrated a seventh specific embodiment of a cutting insert generally designated as 400. Cutting insert 400 may be made from a cylindrical blank like blank 302 wherein the blank comprises a backing of cemented tungsten carbide and a layer of polycrystalline diamond (PCD) material affixed to the backing.

Cutting insert 400 has a backing (or substrate) 402 of cemented tungsten carbide which has a leading surface 404, a trailing surface 406, a top surface 408, a bottom surface, one side surface 412 and another side surface 414. The surface area of the bottom surface area is greater than the surface area of the leading surface 404. The bottom surface also provides the major area for brazing the cutting insert to the cutting bit body. Cutting insert 400 further includes a layer of polycrystalline diamond (PCD) 418 affixed to the leading surface 404 of the backing 402.

The PCD layer 418 includes a leading surface 420, a trailing surface 422, a top surface 424, a bottom surface 426, one side surface 428 and another side surface 430. It should be appreciated that the trailing surface 422 of the PCD layer 418 is adjacent to the leading surface 404 of the backing 402.

Both side surfaces (412 and 414) of the backing 402 converge toward each other as they move away from the leading surface 404 (or toward the trailing surface 406) of the backing 402. The included angle of convergence "oo" of the one side 412 with respect to a plane perpendicular to the leading surface 420 of the PCD layer 418. The included angle of convergence "oo" may range between about WO 99/04128 PCTIUS98/14358 -42fifteen degrees and about forty-five degrees with the preferred angle "oo" equalling about thirty degrees.

The included angle of convergence "pp" of the other side 414 with respect to a plane perpendicular to the leading surface 420 of the PCD layer 418. The included angle of convergence "pp" may range between about zero degrees and about forty-five degrees with the preferred angle "pp" equalling about thirty degrees.

The configuration of the one side surface 412 of the backing 402 and the one side surface 428 of the PCD layer 418 are the same so that the following description of the one side surface 428 of the PCD layer 418 will suffice for the description of the one side surface 412 of the backing 402. Referring to FIG. 28, one side surface 428 has a lower arcuate portion 432, a mediate straight portion 434, and an upper arcuate portion 436. Lower arcuate portion 432 is of a radius R1 and joins the mediate straight portion 434 and the bottom surface 426. The included angle "qq" between the bottom surface 426 and the mediate straight portion 434 is seventy-four degrees.

Included angle "qq" may range between about forty-five degrees and about eighty degrees. The geometry of the seat in the bit body and the magnitude of angle "q" must correspond so as to properly orient the mediate straight portion 434 when the cutting insert is affixed in the seat. Upper arcuate portion 436 is of a radius R2 and joins the top surface 424 and the mediate straight portion 434.

The configuration of the other side surface 414 of the backing 402 and the other side surface 430 of the PCD layer 418 are the same so that the following description of the other side surface 430 of the PCD layer 418 will suffice for the description of the other side surface 414 of the backing 402. Other side surface 430 has a lower arcuate portion 440, a mediate straight portion 442, and an upper arcuate portion 444.

WO 99/04128 PCT/US98/14358 -43- Lower arcuate portion 440 is of a radius R3 and joins the mediate straight portion 442 and the bottom surface 426. The bottom surface 426 and the mediate straight portion 442 are disposed at ninety degrees with respect to each other. Upper arcuate portion 444 is of a radius R4 and joins the top surface 424 and the mediate straight portion 442. The top surface 424 an the mediate straight portion 442 are disposed at ninety degrees with respect to each other.

Referring to FIG. 27 and the dimensions of an actual sample of the cutting insert 400, cutting insert 400 has an overall thickness "ss" of about 8 mm. The PCD layer has a thickness "tt" of about 0.7 mm. The backing has a thickness "uu" of about 7.3 mm. The maximum length dimension "rr" of the PCD layer 418 is about 12.85 mm. The height "vv" of the PCD layer is about 4.7 mm. It is preferred that the height "vv" of the polycrystalline diamond layer is less than the thickness "uu" of the backing. Radius R1 and radius R3 each equal about 0.25 mm. Radius 2 equals about 2.86 mm. Radius R4 equals about 0.5 mm.

Referring to FIGS. 29 through 31 there is illustrated a rotatable cutting bit body generally designated as 450. Bit body 450 has opposite axially forward and rearward ends wherein only the axially forward end 452 is depicted by FIGS. 29 through 31.

Bit body 450 contains a pair of seats 454, as well as a trio of vacuum or fluid ports 456, in the axially forward end 452 thereof. Each seat 454 has a bottom surface 458. Rotatable cutting bit body 450 receives a cutting insert 400 in each one of the seats 454.

Each cutting insert 400 may have an orientation with respect to the cutting bit body 450 when brazed thereto like the orientations of each cutting insert 60 to bit body 32 as illustrated in FIGS. 1 and 2. The range of possible orientations of each cutting insert 60 to the bit body 32 is also WO 99/04128 PCT/US98/14358 -44available for the orientation of the cutting insert 400 to the bit body 450.

Even though a wide range of orientations is available, FIGS. 29 through 31 show the orientation of the seats 454. In this regard for each seat 454, line "ww" lies on the surface of the seat 454 and passes through the mid-point of the front edge 455 and the trailing apex 457 of the seat 454. Line "ww" is disposed with respect to a horizontal plane (line xx-xx being coplanar with such horizontal plane) passing through the leading edge of the seat at an included angle "yy" wherein angle "yy" equals ten degrees (see FIG. 29). The bottom surface of each seat 454 also has an orientation such that it is disposed at an included angle of with respect to the horizontal wherein angle "zz" equals 26 degrees. In this regard, angle "zz" is defined as the included angle between a line "aaa-aaa" which lies along the front edge of seat 455 and a horizontal line that is in the same vertical plane as line "aaa-aaa". The axially forward generally frusto-conical surface 452 is disposed at an included angle "bbb" with respect to the horizontal wherein angle "bbb" equals twenty degrees.

Referring to FIG. 30, there is shown one cutting insert 400 brazed into its corresponding seat 454. Cutting insert 400 has an orientation with respect to seat 454 such that at least a part of the lower arcuate portion 432 of the PCD layer 418, as well as the mediate straight portion 434 of the PCD layer 418, extend radially past the periphery of the bit body 450.

The intersection of the lower arcuate portion 432 with the leading surface 420 of the PCD layer 418 defines a lower arcuate edge 460. The intersection of the mediate straight portion 434 with the leading surface 420 of the PCD layer 418 defines a cutting edge 462. The intersection of the upper arcuate portion 436 WO 99/04128 PCTIUS98/14358 with the leading surface 420 of the PCD layer 418 defines another cutting edge 464. The intersection of the top surface 424 with the leading surface 420 defines a cutting edge 466. The intersection of the upper arcuate portion 444 with the leading surface 420 defines still another cutting edge 467. Cutting edges 462, 464, 466 and 467 engage the earth strata during the operation of the rotatable cutting bit. More specifically, the cutting edge 467 first engages the earth strata. The cutting edge 462 cuts the side clearance for the hole. The other cutting edges 464 and 466 assist in the cutting operation.

It is apparent that cutting insert 300 and cutting insert 400 provide certain advantages.

The use of polycrystalline diamond layer of the cutting insert will be able to take advantage of the high penetration rates provided by this design of cutting insert. Higher penetration rates lead to an improvement in the overall performance and efficiency of the cutting bit.

The higher ratio of the thickness of the cemented carbide backing to the thickness of the polycrystalline diamond layer results in an increase in the strength of the overall cutting insert. A stronger cutting insert will typically result in a longer operating life and a reduction in the instances of premature failures.

The design of the cutting insert of this invention permits an increase in air flow at the axially forward end of the drill bit which results in lower operating temperatures for dry drilling. Lower operating temperatures permit the use of a low temperature braze alloy, a silver-based braze, to braze the cutting insert to the bit body for dry drilling operations. This is in contrast to the use of a clamp to mechanically connect the cutting insert to the bit body.

WO 99/04128 PCTIUS98/1 4358 -46- As described hereinabove, the polycrystalline diamond layer is on the leading surface of the backing, which is adjacent to, as well as perpendicular to, the bottom surface of the backing. The leading surface has a smaller surface area than the bottom surface, and the braze joint is between the bottom surface of the backing and the seat.

By using the larger bottom surface to form the braze joint in conjunction with the polycrystalline diamond layer being on the smaller leading surface, the cutting insert can be brazed to the cutting bit body using a relatively shallow seat that does not require a large shoulder. The use of such a shallow seat reduces the expense associated with the manufacture of the cutting bit body.

The cutting edges of the polycrystalline layer are removed such a distance from the surface which forms the braze joint. These cutting edges thus are not negatively impacted by the higher temperatures which occur during manufacture.

During the post-brazing cooling of the cutting insert and cutting bit body, stresses are formed due to the difference in the coefficient of thermal expansion between the cemented tungsten carbide backing and the steel cutting bit body. The steel body contracts to a greater extent than the cemented carbide so as to set up tension in the surface of the backing that is opposite to the surface which forms the braze joint. Because the polycrystalline diamond layer is on a surface which is perpendicular to the bottom surface which forms the braze joint, the polycrystalline diamond layer does not experience post-brazing stresses to the same extent as in earlier cutting bits in which the polycrystalline layer is on the surface of the backing opposite to that surface which forms the braze joint. The reduction of the stress on the surface WO 99/04128 PCT/US98/14358 -47which has the polycrystalline layer promotes a'longer operating life of the tool.

Even though the specific embodiment shown by FIGS. 26A through 26C has abrupt corners at the intersections of the surfaces and the specific embodiment shown by FIGS. 27 and 28 has rounded corners at the intersections of the surfaces, it should be appreciated that applicants contemplate the invention to include a combination of abrupt corners and rounded corners at selected intersections of the surfaces. In other words, some of the intersections of the surfaces may have an abrupt corner and others of the intersections may have rounded corners.

Although the specific embodiment is a roof drill bit, it should be appreciated that applicants contemplate that the invention encompasses other styles of rotatable cutting bits. One such example is a rotary percussive drill bit. In addition, although the cutting inserts are either indexable or reversible, applicants contemplate that the invention may encompass cutting inserts that are asymmetric and which are not indexable or reversible. It should also be understood that although the specific embodiments set forth herein comprise roof drill bits for use in the penetration of earth strata, the principles set forth with respect to these cutting inserts also have application to metalcutting inserts, as well.

The patents and other documents identified herein are hereby incorporated by reference herein.

Other embodiments of-the invention will be apparent to those skilled in the art from a consideration of the specification or practice of the invention disclosed herein. It is intended that the specification and examples be considered as illustrative only, with the true scope and spirit of the invention being indicated by the following claims.

Claims

1. A rotatable cutting bit for penetrating an earth formation, the bit comprising an elongate bit body having a forward end and a rearward end, the bit body defining a peripheral surface, the bit body having a central longitudinal axis and a center of rotation; the bit body containing a first seat wherein a first cutting insert being retained in the first seat, and a second seat at the axially forward end thereof wherein a second cutting insert being retained in the second seat; wherein the first cutting insert presenting a first clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth formation, and the first cutting insert having a first leading cutting edge that engages the earth formation, and substantially all of the first leading cutting edge being disposed at a first lead angle between 50 degrees and degrees wherein the first lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the first leading 4 cutting edge and another line is parallel to the center of rotation of the bit S.body; and the second cutting insert presenting a second clearance cutting edge which radially extends past the peripheral surface of the bit body so as to 4oo engage the earth formation, and the second cutting insert having a second leading cutting edge that engages the earth formation substantially all of the second leading cutting edge being disposed at a second lead angle (C) between 50 degrees and 90 degrees wherein the second lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one 4 line is along the second leading cutting edge and another line is parallel to the center of rotation of the bit body.

2. A rotatable cutting bit according to claim 1 wherein the first cutting insert is disposed so as to have a first radial rake angle between positive degrees and negative 30 degrees wherein the first radial rake angle is the included angle between a pair of intersecting lines (L-L and M-M) wherein one line is a radial line from the central longitudinal axis of the bit body through the center point of the first leading cutting edge and the other line S is along the first leading cutting edge of the first cutting insert so that the first radial rake angle is negative when the line along the first leading N:\IRi601677%amendedcaims29-8-01 PA83937.98.doc 49 cutting edge trails the radial line at a location outside the periphery of the cutting insert with respect to the direction of rotation of the cutting bit, and the first radial rake angle is positive when the line along the first leading cutting edge leads the radial line at a location outside the periphery of the cutting insert with respect to the direction of rotation of the cutting bit.

3. A rotatable cutting bit according to claim 2 wherein the first cutting insert includes an edge opposite to the first leading cutting edge; and the first cutting insert being disposed so as to have a first insert rake angle between 0 degrees and -30 degrees wherein the first insert rake angle is defined as the included angle between a line normal to both the lead angle reference line and the central longitudinal axis of the bit body and a line (H-H) lying along the top surface of the cutting insert and passing through the center of the leading cutting edge and the center of the edge wherein the first insert rake angle is measured in the vicinity of the center of the edge; when the cutting insert has an orientation such that line is leading S0 line upon forward penetration of the cutting bit in the direction of axial penetration during drilling the insert rake angle is positive; and when the cutting insert has an orientation such that line is trailing line upon forward penetration of the cutting bit in the direction of axial penetration (Y) during drilling the insert rake angle would be negative.

4. A rotatable cutting bit according to claim 3 wherein the first lead angle is about 70 degrees, the first insert rake angle is about negative 20 degrees, and the first radial rake angle is about negative 10 degrees.

5. A rotatable cutting bit according to any preceding claim wherein at least a portion of the first clearance cutting edge being disposed at an included angle (N or Q or R or S) with respect to the first leading cutting edge of between degrees and 130 degrees.

6. A rotatable cutting bit according to claim 5 wherein at least a portion of the first clearance cutting edge of the first cutting insert being disposed at an included angle (N or Q or R or S) of about 100 degrees with respect to the first leading cutting edge. Hr t N:URNfiO1677'amendedciaims29-8-01PA83937-98.doc I-

7. A rotatable cutting bit according to any preceding claim wherein at least a portion of the first clearance cutting edge of the first cutting insert being generally parallel to the axis of rotation of the bit body.

8. A rotatable cutting bit according to any preceding claim wherein the bit body containing a cavity, the bit body containing an unobstructed passage at the forward end thereof, and wherein the passage providing communication between the cavity and the forward end of the bit body.

9. A rotatable cutting bit according to any preceding claim wherein the first cutting insert is of a generally triangular shape, and the second cutting insert is of a generally triangular shape. A rotatable cutting bit according to any preceding claim wherein the first cutting insert includes a top surface, one side surface, and another side surface, the one side surface intersecting the top surface to form the first leading cutting edge, the one side surface intersecting the other side surface to form an 15 edge, and a relieved surface at the edge wherein the intersection of the relieved surface and the one side surface define a first clearance cutting edge. l•

11. A rotatable cutting bit according to claim 10 wherein the relieved surface is generally arcuate.

12. A rotatable cutting bit according to claim 10 wherein the relieved surface is generally planar. °13. A rotatable cutting bit according to claim 10 wherein one portion of the relieved surface is generally arcuate and another portion of the relieved surface is generally planar.

14. A rotatable cutting bit according to any preceding claim wherein the 25 first cutting insert comprising a top surface, a bottom surface, a first side surface, a second side surface, and a third side surface; the first, second and third side surfaces joining the top and bottom surfaces; the first side surface intersecting the second side surface to form a first edge, the second side surface intersecting the third side surface to form a second edge, and the third side surface intersecting the first side surface to form a third edge; and the first side surface adjacent the first edge being disposed at an included angle with respect to the top surface of Amended claims July 2000.doc:7111/00 S7r 51 about 90 degrees, and the first side surface adjacent the third edge being disposed at an included angle with respect to the top surface of about 110 degrees. A rotatable cutting bit according to claim 14 wherein the second side surface adjacent the first edge being disposed at an included angle with respect to the top surface of about 90 degrees, and the second side surface adjacent the second edge being disposed at an included angle with respect to the top surface of about 110 degrees, and the third side surface adjacent the third edge being disposed at an included angle with respect to the top surface of about 90 degrees.

16. A rotatable cutting bit according to any preceding claim wherein the cutting insert is indexable.

17. A rotatable cutting bit according to any preceding claim wherein the cutting insert is reversible. 9* o* 15 18. A rotatable cutting bit according to any preceding claim wherein the first cutting insert comprising a top surface, a bottom surface, a first side surface, a second side surface, and a third side surface; the first, second and third side S: surfaces joining the top and bottom surfaces; the first side surface intersecting the second side surface to form a first edge, the second side surface intersecting the third side surface to form a second edge; a first relieved surface being at the first adjacent to the top surface of the cutting insert; and a second relieved surface being at the second edge adjacent to the bottom surface of the ooo° cutting insert.

19. A rotatable cutting bit according to claim 18 wherein the first relieved logo• 25 surface presenting a generally planar surface disposed at an included angle with respect to the top surface of between 90 degrees and 130 degrees; and the second relieved surface presenting a generally planar surface disposed at an included angle with respect to the bottom surface of between 90 degrees and 130 degrees.

20. An elongate rotatable cutting bit body for carrying at least one cutting insert and the cutting insert presenting a clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth formation, and the cutting insert having a leading cutting edge that engages the earth formation, and substantially all of the leading cutting edge being disposed N:\IRNO601677 amendedclaims29-8-01 PA83937-98.doc I 52 at a lead angle between 50 degrees and 90 degrees wherein the lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the leading cutting edge and another line (F-F) is parallel to the center of rotation of the bit body and the bit body having a central longitudinal axis the bit body including a forward end, a rearward end, and a seat at the forward end, the seat receives the cutting insert; wherein

21. A cutting bit body according to claim 20 wherein the deepest portion of the seat is adjacent to the juncture of the chordal side surface and the radial side surface.

22. A cutting bit body according to either of claims 20 or 21 wherein the chordal side surface and the radial edge intersect radially inwardly of the peripheral surface of the cutting bit body.

23. A cutting bit body according to either of claims 20 or 21 wherein the chordal side surface and the radial edge do not intersect so that the seat is 15 open where the radial edge intersects the peripheral surface of the cutting bit body.

24. A cutting insert for use in a rotatable cutting bit for the penetration of an *earth formation wherein the cutting insert is disposed in a seat in the cutting bit with a peripheral surface; 20 wherein substantially all of the leading cutting edge which engages the ae earth formation is disposed at a lead angle between 50 degrees and a a degrees; the cutting insert including a cutting insert body having a top surface, a bottom surface, a first side surface, and a second side surface, the first side surface intersects the second side surface to form a first edge; the first and second side surfaces joining the top surface and the bottom surface; the first edge defining at least in part a clearance cutting edge which extends radially past the peripheral surface of the cutting bit when the cutting insert is in the seat so as to engage the earth formation. A cutting insert according to claim 24 wherein the first edge has a portion thereof being generally arcuate.

26. A cutting insert according to either of claims 24 or 25 wherein the first edge has a portion thereof being generally planar.

27. A cutting insert according to any of claims 24 to 26 wherein the cutting insert body further includes a third side surface which joins the top and bottom surfaces; the second side surface intersecting the third side surface to form a second edge, and the third side surface intersecting the first side surface to form a third edge; and the first side surface adjacent the first edge being disposed at an included angle with respect to the top surface of about 90 degrees, and the first side surface adjacent the third edge being disposed at an included angle with respect to the top surface of about 110 degrees. 15 28. A cutting insert according to claim 27 wherein the second side surface adjacent the first edge being disposed at an included angle with respect to the top surface of about 90 degrees, and the second side surface adjacent the second edge being disposed at an included angle with respect to the top surface of °about 110 degrees; and the third side surface adjacent the second edge being 20 disposed at an included angle with respect to the top surface of about 110 i. .degrees, and the third side surface adjacent the third edge being disposed at an included angle with respect to the top surface of about 90 degrees.

29. A cutting insert according to any of claims 24 to 28 wherein the cutting insert is indexable. 25 30. A cutting insert according to any of claims 24 to 29 wherein the cutting insert is reversible.

31. A cutting insert according to any of claims 24 to 30, the cutting insert body further including a third side surface joining the top and bottom surfaces; the second side surface intersecting the third side surface to form a second edge; a first relieved surface being at the first edge adjacent to the top surface of the I claims July 2000.doc:7/11/00 54 cutting insert; and a second relieved surface being at the second edge adjacent to the bottom surface of the cutting insert.

32. A cutting insert according to claim 31 wherein the first relieved surface presenting a generally planar surface disposed at an included angle with respect to the top surface of between 90 degrees and 130 degrees; and the second relieved surface presenting a generally planar surface disposed at an included angle with respect to the bottom surface of between 90 degrees and 130 degrees.

33. A replaceable cutting insert for use in a rotatable cutting bit for engaging the earth strata, the cutting bit having a cutting bit body containing a seat which receives the cutting insert; wherein the cutting insert including a cutting insert body having two surfaces which intersect to form a leading cutting edge, the leading cutting edge that *engages the earth formation, and substantially all of the first leading cutting 15 edge being disposed at a first lead angle between 50 degrees and degrees wherein the first lead angle is the included angle between a pair of *intersecting lines (E-E and F-F) wherein one line is along the first leading cutting edge and another line is parallel to the center of rotation of the bit body; and during operation of the rotatable cutting bit the cutting edge engaging 20 the earth strata; and the cutting insert body being made from one of the following materials: ceramics, binderless tungsten carbide, polycrystalline diamond composites with metallic binder, polycrystalline diamond composites with ceramic binder, *eo tungsten carbide-cobalt alloys having a hardness greater than or equal to about So 25 90.5 Rockwell A, and hard coated cemented carbides.

34. A cutting insert according to claim 33 wherein the ceramics include silicon nitride-based ceramics, and alumina-based ceramics. A cutting insert according to claim 33 wherein the tungsten carbide- cobalt alloys comprise between 5.7 and 6.0 weight percent cobalt with the balance being tungsten carbide, and the alloys having a coercive force (He) between 265 and 350 oersteds and a hardness between 92.7 and 93.3 Rockwell A.

36. A cutting insert according to claim 33 wherein the tungsten carbide- 7 obalt alloys have a hardness greater than or equal to 91.0 Rockwell A. 9

37. A cutting insert according to claim 33 wherein the tungsten carbide- cobalt alloys have a coercive force greater than or equal to 160 oersteds.

38. A cutting insert according to claim 33 wherein the tungsten carbide-cobalt alloys have a coercive force (Hc) greater than or equal to 180 oersteds.

39. A cutting insert for use in a rotatable cutting bit for engaging earth strata, the rotatable cutting bit having a cutting bit body with a periphery and a seat which receives the cutting insert; wherein the cutting insert having a backing having a leading surface, a trailing surface, and a pair of opposite side surfaces, one of the side surfaces being near the periphery of the bit body when the cutting insert is received in the seat, and the one side surface converging toward the opposite side surface as it moves from the leading surface to the trailing surface; the cutting insert presenting a clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth formation, and the cutting insert having a leading cutting edge that engages the earth formation, and substantially all of the leading cutting edge being disposed at a lead angle between 50 degrees and 90 degrees wherein the lead angle is the included angle between a pair of intersecting lines (E-E and 20 F-F) wherein one line is along the leading cutting edge and another line is parallel to the centre of rotation of the bit body; and A layer of polycrystalline diamond on the leading surface of the backing wherein the layer of polycrystalline diamond defines a cutting edge, and during the operation of the rotatable cutting bit the cutting edge engages the earth strata. A cutting insert according to claim 39 wherein the backing having a first thickness (jj) and the layer of polycrystalline diamond having a second thickness and wherein the first thickness (jj) is at least about five times the second thickness (kk).

41. A cutting insert according to claim 40 wherein the first thickness (jj) is at least about seven times the second thickness (kk).

42. A cutting insert according to either of claims 40 or 41 wherein the leading surface of the backing having a height, and the height being less than the sum of the first thickness (jj) and the second thickness (kk). N:\IRN60167'amendeddalms29-8-01 PA83937-9g.doc OFF\C 56

43. A cutting insert according to any of claims 39 to 42 including a bottom surface adjacent to the leading surface, the bottom surface having a first surface area and the leading surface having a second surface area, the first surface area being greater than the second surface area, and the bottom surface resting in the seat when the cutting insert is received within the seat.

44. A cutting insert according to any of claims 39 to 43 wherein the one side surface converges so as to provide sufficient clearance whereby the one side surface does not impinge the earth strata during operation of the rotatable cutting bit.

45. A cutting insert according to any one of claims 39 to 44 wherein the one side surface and the opposite side surface each converge toward the other as they move from the leading surface to the trailing surface of the backing.

46. A rotatable cutting bit for engaging earth strata including a cutting bit body having a periphery and a seat wherein the seat has a bottom surface; and 15 a cutting insert being received in the seat; wherein the cutting insert including a backing having a leading surface, a trailing *.•:surface and a bottom surface adjacent to the leading surface; the cutting insert presenting a clearance cutting edge which radially extends past the peripheral surface of the bit body so as to engage the earth 20 formation, and the cutting insert having a leading cutting edge that engages the earth formation, and substantially of the leading cutting edge being disposed at a lead angle between 50 degrees and 90degrees wherein the lead angle is the included angle between a pair of intersecting lines (E-E and F-F) wherein one line is along the leading cutting edge and another S 25 line is parallel to the centre of rotation of the bit body; a layer of polycrystalline diamond on the leading surface of the backing wherein the layer of polycrystalline diamond defines a cutting edge, and during the operation of the rotatable cutting bit the cutting edge engages the earth strata; and the bottom surface of the backing providing the major brazing area to braze the cutting insert to the cutting bit body, and the bottom surface of the backing being brazed to the bottom surface of the seat so as to affix the cutting /r,"PS ,"sert to the cutting bit body. 57

47. A rotatable cutting bit according to claim 46 wherein the backing of the cutting insert further includes a pair of opposite side surfaces, one of the side surfaces being near the periphery of the bit body when the cutting insert is received in the seat, and the one side surface converging toward the opposite side surface as it moves from the leading surface to the trailing surface.

48. A rotatable cutting bit according to either of claims 46 or 47 wherein the bottom surface of the backing has a first surface area and the leading surface has a second surface area, and the first surface area is larger than the second surface area.

49. A rotatable cutting bit substantially as herein described herein with reference to the accompanying drawings. An elongate rotatable cutting bit body substantially as described herein with reference to the accompanying drawings.

51. A cutting insert for use in a rotatable cutting bit substantially as described 15 herein with reference to the accompanying drawings. 10 September 2001 PHILLIPS ORIVONDE FITZPATRICK Attorneys for KENNAMETAL, INC. •O

60. 00OS *o•Oo O DATED: 10 September 2001 20 PHILLIPS ORMONDE FITZPATRICK OO5. Attorneys for KENNAMETAL, INC. 0 0