AU721084B2 - A method for impregnation of wood and wood based products - Google Patents

Description

154454 A METHOD FOR IMPREGNATION OF WOOD AND WOOD BASED PRODUCTS TECHNICAL FIELD This invention comprises a method of impregnation of wood and wood based products with chromium based wood preservatives.

BACKGROUND ART It is common to impregnate wood or wood based products with preservative chemicals.

iiiiii Commonly used wood preservatives include copper chrome arsenic (CCA), other copper chrome based or copper preservatives and other water-based inorganic preservatives based on boron for example. Wood is also commonly impregnated with other wood modifying agents such as fire retardants, water repellents, dimensional stabilising agents, and wood hardening agents for example. With the latter, impregnation may be ee followed by formation of insoluble polymers to add density and hardness to the wood.

In many processes after impregnation with reactive preservatives or modifying agents it is desirable that the wood has excess impregnate chemical drained from it and the wood be subsequently heated to fix the chemicals in the wood.

Common commercially used methods of wood impregnation, with reactive wood preservative systems, for example chromium containing preservatives such as CCA, suffer from certain disadvantages.

First, following impregnation under hydraulic pressure, liquid comes out of the wood into the working chemical solution when the pressure is released. This "pressure 154454 kickback" is generally weaker and/or the ingredients are no longer in balance and it may also contain naturally occurring sugars and other molecules present in the wood which are carried back out of the wood. When the hydraulic pressure is released, the kickback solution is normally returned directly into the working solution causing imbalances in the working solution chemical concentrations and ultimately sludging in the working solution and on the wood surface in subsequent charges. The rate of sludge build up is process dependent (solution turnover, volume etc). In addition, in many treatment schedules, a vacuum is finally applied to remove excess liquid from the impregnated wood surface and chemically depleted solution will also come out of the wood during the application of the final vacuum (due to residual air in the wood moving iiiiii to the wood surface). This solution is generally termed the "vacuum kickback".

Secondly, with existing methods where kickback occurs at the end of the process it is difficult to control the exact amount of the chemical impregnated into the wood.

Fixation of chemicals such as CCA occurs naturally at ambient temperatures (usually *above 7°C) during treatment of wood. However, with such fixation the treater has no control over the amount of deposition in the wood or the degree of fixation. Further, the treater has no control over the disproportionation in the working solution. This difficulty means that where inadequate amounts, volumes or concentrates of chemicals a 20 are used, the core of the wood is not treated with an adequate level of the chemical and where the amount of chemical is adequate to treat the core of the wood, the amounts of chemical in the outer section of the timber may be excessive, significantly adding to the cost of the treatment.

154454 The existing methods generally show high variability in the amount of chemical deposited in the wood particularly for the frequently occurring situation in which the sample contains mixtures of sapwood and sometimes less permeable heartwood.

DISCLOSURE OF INVENTION The invention provides an improved and/or at least alternative process which allows effective and controlled impregnation of wood or wood based products with a chromium based wood preservative without substantial depletion and/or contamination of the balance of the unimpregnated chemical.

.ii. In broad terms the invention comprises a method of impregnating wood or wood based products with a chromium based wood preservative chemical under pressure comprising: a) heating a liquid composition comprising a chromium based wood preservative chemical and impregnating the hot composition into the wood under hydraulic pressure and controlling the hydraulic pressure to control the amount of chemical impregnated into the wood; and b) replacing the hydraulic pressure with sufficient pneumatic pressure to hold the impregnated composition in the wood while the unused composition is removed from the treatment vessel.

The hydraulic pressure phase impregnates the solution into the wood while the pneumatic pressure phase holds the impregnated chemical in the wood while the balance of the working chemical is collected. By substituting the hydraulic pressure with pneumatic pressure whilst maintaining the same pressure or increasing the 154454 pressure, pressure kickback of chemical out of the wood and contamination of the balance of the working chemical is minimised or eliminated.

In the preferred method of the invention the hydraulic pressure is controlled so as to control the volume or amount of chemical impregnated into the wood and the pressure in the pneumatic pressure phase is increased above that used in the hydraulic pressure phase to force the chemical further into the wood.

In this preferred method the level of pneumatic pressure may be increased above that required to hold the impregnated composition in the wood, to force the chemical further into the wood, by immediately introducing into the treatment vessel, gas at a pressure level which will force the chemical further into the wood, or more preferably the pressure is increased over time after initially introducing the pneumatic pressure at a lower level (eg a pressure equal to the hydraulic pressure) while the unimpregnated balance of the working chemical is removed.

After the collection of the unimpregnated balance of the chemical during the pneumatic pressure phase, the pneumatic pressure is vented to atmospheric pressure and any resulting pressure kickback liquid from the wood may be collected and separated. A S 20 vacuum can then optionally be applied to extract any excess impregnate chemical or remove any residual liquid from the wood surface and any resulting vacuum kickback liquid may also be collected and separated.

Drainage of the unimpregnated treatment composition during the pneumatic pressure phase is carried out ideally at a pressure no lower than the pressure of the hydraulic pressure phase to avoid kickback of the treating composition.

154454 The process of the invention thus separates the kickback solutions from a working solution during treatment and prevents water soluble sugars and extractives from contaminating the working solution, thereby eliminating the elemental depletion of the treating solution and risk of sludging. Preferably the unused solution is used in treatment of further batches of wood or wood products by the method of the invention.

The process of the invention in at least preferred forms also allows for the absorption of impregnate chemical in a mixed charge of sapwood and heartwood to be manipulated, via adjustments to the level and time of the hydraulic and pneumatic pressure phases, i to a predetermined level and thus improves the quality, and reduces the variability in eec...

chemical loading, of the treatment achieved over conventional processes. Preferably the pressure and times are chosen to allow chemical to be deposited in the core of the wood at a concentration of at least 75%, preferably at least 100%, of that in the outer one third of the cross-section of the wood.

co The process of the invention allows a predetermined amount of chemical to be taken up by the wood in the hydraulic pressure phase. The volume of the wood and the volume of the treatment vessel can be determined by methods well known in the art so as to 420 allow determination of the amount of working solution to be provided to give the required uptake of treatment composition. Pneumatic pressure holds the predetermined amount of treatment composition in the wood while the unused treatment composition is removed from the vessel. In preferred embodiments of the invention, the pneumatic pressure is higher to deliver more of the treatment chemicls to the core of the wood. The same level of deivery the rete vs c meee b eo he core of the wood may in existing processes be only achievable by using a greater uptake of working composition.

154454 Control of the hydraulic pressure phase allows a high level of control of impregnation of the required volume of impregnation chemical into the wood. The resulting reduction of coefficient of variation of the retention allows savings on chemical usage and better control over compliance with wood treatment standards.

The process of the invention in at least preferred forms reduces the net absorption of preservative and drippage from treated material post treatment when compared with conventional schedules without loss in the quality of treatment achieved. This is of environmental significance for treatment plants who may-move unfixed wet timber 4 following treatment and must invest capital in protecting soil from any drippage.

6 The process of the invention also generally takes no longer to perform than any currently available treatment schedule. Preferably the time the wood is under hydraulic pressure plus the time the wood is under pneumatic pressure is less than oo., five hours (more preferably less than two or three hours in circumstances favourable for impregnation).

The process of the invention may be used to impregnate wood or wood based products.

«e 5 20 By wood is meant solid wood of all types whether sawn, dressed or otherwise, and by wood based products is meant all forms of reconstituted wood products such as particle board, fibre board including medium density fibre board, hard board, wafer board, bonded wood products such as finger jointed wood, laminated wood, plywood and similar.

154454 The gas used in the pneumatic pressure phase may be air or nitrogen. Other gases may also be used.

Preferred pressures for the hydraulic pressure phase of the process range from 20-2000 kPa or more according to the permeability of the wood species, more preferably 400- 2000 kPa, and most preferably 600-1500 kPa. Preferred pressures, more preferred pressures and most preferred pressures for the pneumatic pressure phase range from 20-2000 kPa, 400-2000 kPa and 600-1500 kPa respectively, provided that the pressure in the pneumatic pressure phase is ideally at least as high as during the hydraulic pressure phase. In a preferred form of the process the pressure during the pneumatic pressure phase is initially the same as during the hydraulic pressure phase and is subsequently increased to further drive the impregnate chemical into the wood.

Preferably after removal of the unused treating composition, the pneumatic pressure 15 applied is at least 30% more than the pressure used during the hydraulic pressure phase. More preferably the increase is to at least 80% more than used in the hydraulic pressure phase. For example an hydraulic stage of +700 kPa may be followed after drainage at the same pressure and by a pneumatic pressure stage of 1400 kPa.

20 Typically the duration of the hydraulic pressure phase is 5-240 minutes, more preferably 7-180 minutes. The duration of the subsequent pneumatic pressure phase is preferably 5-240 minutes, more preferably 7-180 minutes. Factors affecting the pressure duration include the type of chemical being impregnated into the wood, the type of treatment required, the size of the piece or pieces of wood, the wood species (eg soft wood or hard wood), and the moisture content of the wood for example. Other 154454 important factors are the amount of penetration and retention of the impregnate chemical desired.

In a preferred form of the invention the hydraulic pressure used is in the range of 2000 kPa and after the unused composition is removed from the treatment vessel the pneumatic pressure used is 100-1000 kPa higher than used during the hydraulic pressure phase so as to force the chemical further into the wood. Preferably in this form of the invention the pneumatic pressure is at least 30% (more preferably at least higher than the pressure used in the hydraulic phase.

In another form of the invention the pneumatic pressure used to force the chemical further into the wood is 30% higher than the pressure used in the hydraulic phase, and in the range 26-2000 kPa.

More preferably the pneumatic pressured used is in the range 520-2000 kPa.

go Most preferably the pneumatic pressure is in the range 780-1500 kPa.

o 20 In another preferred form of the invention the pneumatic pressure used to force the S* chemical further into the wood is at least 80% higher than the pressure used in the hydraulic phase and in the range 36-2000 kPa.

In this form of the invention the preferred pneumatic pressure is in the range 720-2000 kPa, more preferably 1080-1500 kPa.

154454 In preferred embodiments of the invention where the chemical used can be fixed in the wood, the higher pressures in the pneumatic pressure phase used to force the chemical further into the wood is maintained for a period sufficient to allow fixation of the chemical into the wood.

The term "a hydraulic pressure phase" includes submerging of the wood in liquid impregnate chemical which is in turn under pneumatic pressure to effectively apply hydraulic pressure to the wood.

The impregnate chemical is heated prior to impregnation. Preheating of impregnate chemical means the wood takes up the hot solution to allow consistent fixation throughout the wood. It is difficult to uniformly heat wood particularly when it is saturated as the large volume of water within the wood makes heat transfer throughout 15 the wood difficult. Heat-induced fixation as in the process of the invention also avoids the need for a separate heating-fixation step and also the need to transfer of 0 impregnated timber to a separate heating vessel as is commonly done.

S...I

Heating may be up to 100°C in the case of aqueous solutions of treatment chemicals 20 with 60-95 0 C being preferred. Most preferably the temperature at the wood surface is *o 60-75 0

C.

This process-of the invention provides a method of impregnating and fixing chromium based wood preservatives such as CCA into wood through the use of hot solutions to achieve treatment and fixation in a one-step process.

154454 This preferred form of the process of the invention can take less than four hours and as such is as fast, or faster, than many available processing options whether treatment followed by steam fixation or treatment followed by hot water fixation.

Another benefit of this form of the invention is that advantage can be taken of the greater solubility of chemicals such as disodium octaborate at higher temperatures, so as to provide a greater loading of chemical.

It is not essential to this preferred form of the process invention that the wood material be filleted and thus block-stacked wood material can in many cases be successfully processed. This preferred version of the process invention can produce touch dry material with little or no drippage or surface sludging. Less energy is required for any re-drying operations when compared to either hot water or steam fixed material. In comparison with other available treatment options, little or no time is required, post- ,.15 treatment, on a drip pad.

C

This preferred form of the process of the invention can fix chromium containing preservatives such as CCA in the wood without any or with only minimum disproportionation of the active elements when compared to a conventional process. It 20 also eliminates or at least reduces sludging in solutions, sludge deposition on surfaces o.

Sor drippage of preservative containing kickback from wood post-treatment.

Unlike both steam and hot water fixation systems the preferred form of the process of the invention fixes chromium containing preservatives such as CCA deep throughout the wood thus reducing the risk of environmental contamination from exposure to rain, 154454 or redistribution prior to fixation of the active ingredients under ambient conditions, or leaching by exposure of treated timber prior to completion of the fixation process.

In a preferred embodiment of the invention wood is impregnated with a chromium based wood preservative by a process comprising heating the preservative solution and then impregnating said solution into the wood at a solution temperature in the range 60-95°C under hydraulic pressure; replacing the hydraulic pressure with sufficient pneumatic pressure using air or nitrogen to hold the impregnated preservative in the wood while the unused solution is removed from the treatment vessel to prevent kickback contamination of the unused solution; and maintaining the pneumatic pressure at a level at least as high as the pressure in the hydraulic pressure phase wherein the temperature at which the preservative is impregnated into the wood and the level and time of the hydraulic and pneumatic 15 pressure phases is manipulated to control the amount of the preservative deposited in the wood.

S

Preferably the pneumatic pressure is increased to drive the preservative further into the wood after removal of the unused chemical.

A particularly preferred form of the invention is a method of impregnating wood with a chromium based wood preservative comprising: heating the preservative solution and impregnating said wood at a solution temperature in the range of 60-95°C under hydraulic pressure; allowing a predetermined amount of said solution to be impregnated into the wood; 154454 replacing the hydraulic pressure with sufficient pneumatic pressure, using air or nitrogen, to hold the impregnated preservative in the wood while the unused solution is removed from the treatment vessel to prevent kickback contamination of the unused solution; increasing the pneumatic pressure to force the preservative further into the wood; and maintaining the pneumatic pressure at a level higher than used in the hydraulic pressure phase for a time sufficient to allow fixation of most of the preservative within the wood.

In processes of the invention the hydraulic pressure phase and pneumatic pressure phase described may optionally be followed by a second hydraulic pressure phase and a a second pneumatic pressure phase. Four such phases particularly in combination with higher pressure in the second hydraulic pressure phase relative to the first o 15 hydraulic phase, may be used to carry out successive treatments. The first hydraulic pressure phase impregnates a first chemical into the wood and the first pneumatic pressure phase holds the chemical in the wood. A greater number of cycles may be used to impregnate three or more chemicals. The use of more than one cycle may be useful where wood is being treated with two reactants, or a reactant and a catalyst for 20 example. In other circumstances it may be useful where wood is to be treated with one chemical such as a wood preservative throughout wood, and a second chemical such as a fire retardant primarily closer to the surface of the wood.

In some preferred forms of the invention hot impregnate chemical is held in contact with the wood prior to application of the hydraulic pressure phase. This heats the wood and causes air in the wood to expand and leave the wood. When the hydraulic 154454 pressure is applied the impregnation of the chemicals into the wood is more rapid and any need to pull a vacuum initially is eliminated. Preferably the wood is left in contact with the chemical for 5-20 minutes before application of the hydraulic pressure.

The process of the invention may be used to impregnate wood preservatives such as copper chrome arsenic, copper chrome boron, copper chrome zinc fluoride, and other copper chrome containing formulations. Chrome based wood preservatives may be used both as salts and as oxides. The impregnation conditions used will vary according to the nature of the chemical.

A further form of the invention provides wood or wood products treated with a preservative by a process of the invention.

BRIEF DESCRIPTION OF FIGURES The invention will now be described by way of example only with reference to the .accompanying figures wherein: Figure 1 is a schematic diagram of one arrangement of treatment plant for carrying out 20 the process of the invention, and a Figure 2 shows pressures and temperatures during the course of a treatment of wood in treatment W of Example 154454 DESCRIPTION OF PREFERRED TREATMENT PLANT The treatment plant of Figure 1 comprises treatment cylinders 1, 2 and 3 and a working solution tank 4 containing treating solution 5. Working solution tank 4 has inlets 6 and 7 for receiving water and preservative concentrate respectively and an outlet 8 linked to a pipeline 9 which supplies treating solution 5 to treatment cylinders 1, 2 and/or 3 when appropriate according to the settings of valves in the pipeline.

Hydrostatic pressure is applied using pump 10. A second pipeline 11 allows provision of compressed air to cylinders 1, 2 and 3 via inlets 12 when the appropriate valves are open. Each treatment cylinder 1, 2 and 3 is provided with a-vacuum line 13 containing a condensor 14. Each cylinder 1, 2 and 3 also has an outlet 15 for kickback and an inlet/outlet 16 for receiving treating solution from pipeline 9 and for draining of unused treatment solution at the end of the hydraulic phase. Figure 1 shows timber 17 being impregnated with treating solution 5 in cylinder 1. In cylinder 2 treating solution is 15 being held within and forced further within timber by compressed air in the pneumatic phase. Meanwhile in cylinder 3 the pneumatic pressure has been released and the cylinder door 18 has been opened to allow removal of the timber.

The treating solution 5 is heated and filtered in a process line 19 running out of and 20 back into the working solution tank 4 and having a heat exchanger 20 which receives steam on the heating side 21. This process line also has a pump 22 and a 200 micron filter 23.

Such a treatment plant allows different phases of the process of the invention to be carried out at the same time.

154454 One plant may comprise several impregnation cylinders as shown in Figure 1. Such an integrated plant would have an increased throughput capacity, reduced chemical storage holding and reduced energy usage when compared with a conventional treatment plant. The working solution is used efficiently (which is especially important for hot solutions) as the time the solution is not in use is reduced.

The main reason why the process of the invention lends itself to this throughput improvement lies in the control of the pneumatic pressure phase to hold the required amount of liquid in wood for further depth of penetration and degree of fixation.

Conventional processes perform the same operation, but only use hydraulic pressure and as such tie up the working solution during this phase rendering it unavailable for other plants. Thus if the new process is employed it is possible to have a mother working solution tank in the middle of 3, 4 or more satellite treatment (ie impregnation) 15 plants.

The invention is further illustrated by the following examples: EXAMPLE 1 MATERIALS AND METHODS Four 5 metre long 100x50 mm Pinus radiata sapwood and four 5 metre long 100x50 mm Pinus radiata heartwood boards were selected from the green chain of Waipa sawmill. All the boards were then high temperature dried to 8% MC using a commercial 120 0 C/70°C schedule.

154454 The treatment plant utilised in the trials consisted of two, interconnected, vertically orientated, stainless steel vessels. Each vessel was 1.2 metres long and had an internal diameter of 150 mm. Each vessel was capable of being independently evacuated, or pressurised. During the trials, vacuums were drawn using a conventional vacuum pump.- However all the hydraulic pressures were obtained through the use of compressed air and nitrogen pressure on liquid surfaces rather than by conventional means.

After drying each board was dressed to 95x45 mm and then cross cut into fourteen end matched 294 mm long samples per board. These samples were then randomly allocated (one per process) to each of the nine treatment processes under evaluation.

Each sample was then end sealed with two coats of aluminium sealer to stop end penetration of preservative during treatment and weighed. A total of eight samples 15 (four sapwood and four heartwood) were used per treatment process.

.A combination of hot water and an immersion heater in the working solution tank were a used to make the CCA solution up to the required solution temperature in treatments 1 and 2. In treatment 3 hot water was used to make up the initial solution and this was 20 then further heated by bubbling high pressure dry steam through the hot solution in the working tank.

TREATMENT PROCESSES The three treatment processes evaluated using hot CCA solutions were as follows. In all cases the temperatures in the treatment plant and treating solution were monitored 154454 and recorded through the use of thermocouples and a data logger. All treatments were performed using Koppers-Hickson supplied CCA type C oxide preservative.

Treatment 1 No initial vacuum Solution temperature before flooding 89°C Flood under atmospheric pressure Solution temperature after flooding 78°C Hydraulic pressure 700 kPa for 20 minutes Drain at 700 kPa pressure (collect working solution) increase the pressure to 1400 kPa too.

*Wo and continue pressurising (using compressed nitrogen) for 120 minutes.

Release pressure 200 kPa per minute (collect pressure kickback) Final vacuum of -80 kPa for 15 minutes (collect vacuum kickback).

Treatment 2 *o0 a As for treatment 1 except that solution temperatures before flooding and after flooding were 96°C and 75°C respectively and the time for the hydraulic pressure phase was 7 20 minutes and the pressuring with compressed nitrogen continued for 133 minutes.

Treatment 3 As for treatment 1 except that no initial vacuum solution temperatures before and flooding after flooding were 92 0 C and 88°C respectively and the hydraulic pressure used was at 500 kPa. The working solution was continuously heated.

154454 Working solution, pressure kickback solution and vacuum kickback solution were collected separately. After treatment the air dried wood samples were then cross cut into a series of sections for core cross section analysis and spot testing. The central cross sectional surface of each sample was sprayed with 5% ammonia solution followed by 0.5% rubeanic acid and this resulted in any copper containing areas turning almost black after drying. In addition six samples from each treatment (3 sapwood and 3 heartwood) were selected for further analysis of preservative distribution. The sections were then analysed for copper, chromium and arsenic in accordance with AWPA Al 1- 83.

Results 6 The sapwood and heartwood uptakes and amount of solution drippage for each t 15 treatment are summarised in Table 1.

a 154454 TABLE 1: Summary of Hot Solution Treatments Uotake I/mr3 l/n3 dripped Sap/H-earc TreatLment Process Total Sapwood Heartwood Heart from Uptake drio Hearwood Ratio kPa Minutes Mean 8 Mean 4 Mean 4 Mean4 0 0 samples sampales sarnoles samples 1 700 Hydraulic 20 316.1 134.2 448.6 399 49.3 4-1.1 1400 Air 120 CV VCV V 0 153 42 1 9.7 1 3.6 kPa Minutes o 0 239.2 183.1 295.3 248-1 2 700 !-vd.-aulic 7 CV CV of CV 47.2 62 1 400 Air 133 27 12 13 -80 15 kPa Minutes *0 0 247.9 202.0 293.7 264.3 00 500 Hydraulic 20 CV CV CV 29484.3 1400 Air 120 25 21.S 1 13 1_ Treatment schedule 1 utilised preservation solution temperature of between 78 and 890C.

The results indicate that the use of hot solutions reduces the volume of heartwood drippage post treatment. This reduction occurs because the hot solution cools down inside the heartwood after treatment and contracts, forcing the remaining air trapped in the wood also to contract and thus hold the solution in the wood.

154454 Analysis of the preservative penetration by spot testing the sample cross sections for copper penetration indicated that uniform and complete sapwood penetrations were achieved using all three treatment schedules evaluated. In contrast the heartwood penetrations were process dependent such that processes with the higher heartwood uptakes had the more uniform heartwood penetrations.

Sludge formation in treating, working, pressure kickback and vacuum kickback solutions were determined by storing solution samples in cylindrical sample jars in the laboratory at a temperature between 18°C to 24°C and observing the formation of sludge. The degree of sludge formation observed for all solutions and treatments can **os be summarised as follows: Working solutions did not show any sludge after one month Pressure kickback solutions for treatments 1, 2 and 3 which used hot solution did not show any sludge after one month. These solutions were clear.

20 Vacuum kickback solutions for treatments 1, 2 and 3 which used hot solution did not show any sludge after one month. These solutions were clear.

Preservative solution was collected from each stage of treatment processes 1, 2 and 3.

All these solutions were analysed for Cu, Cr and As and the results, given in Table 2, demonstrated conclusively that fixation of preservative elements occurs during treatment. By using hot solution almost all of the CCA solution fixed into the wood.

154454 TAB1LE 2: Results of Elemental Analysis of Treatment Solutions 0 0 0000 0

A

000 0 0 *4* .0.4 0 4 0000 0 0000 0 00*0 #00q

S

q~.

00 0 4.

04 0 SOLUTION ELEMENTS Treatinent Treatmnent Treatment inL) 1 2 3 Cu 0.203 0.171 08 Solution Before Treatment Cr 0. 3 4 0.1307 0.-32 As 0. 2 33 0.221 0.237 C U 0.206 0.168 0.170 Working: Solution Cr 0.343 0.3000 0.309 As 0.237 0.217 0.227 Cu 0.00816 0.00630 0.00339 Pressure Kickback Cr 0.02260 0.02030 0.00124 As 0. 00 56 0.00540 0.00135 CU 0.00388 0.00280 0.00352 Vacuum Kickback Cr 0.01510 0.01310 0.00157 As 0.00169 0.00160 0.00217 154454 EXAMPLE 2 Another 5 matched sets of radiata pine were treated as in Table 3: TABLE 3: Treatment Schedule a a a a b a a *i a 4 r Treatment A B C D E F CCA Temperature C° 12 95 90 70 90 Vacuum Before (kPa) 40 40 40 80 Soak Soak Duration (minute) 10 10 10 15 10 Pressure Dur (kPa) 215 215 215 215 215 215 Duration (minute) 60+90 60+90 60+90 60+90 60+90 60+90 Vacuum After (kPa) 90 90 86 86 86 Duration (minute) 15 15 15 15 15 Heating during treatment No No Yes Yes Yes No Wood surface After Clear Clear Sludge Sludge Sludge Clear 20 Key to table: Before before treatment Dur During treatment SAfter After treatment 60+90 60 minutes hydraulic pressure 90 minutes air pressure Flooding the very hot solution of CCA in treatments B and C caused a fast drop in temperature and vacuum. Thus in treatment D the initial solution temperature dropped to 70 0 C to facilitate the higher initial vacuum of 80 kPa. In treatments E 154454 and F the hot CCA was maintained in contact with the wood for 10 minutes in order to provide the initial vacuum (air expansion in the wood due to heating creates vacuum). During this time the wood became heated as well.

Heating the CCA before treatment (B and F) did not lead to sludging whereas heating during treatment D and E) was associated with sludging.

EXAMPLE 3 Twenty four trials using the invention were performed on a pilot-scale plant. The quality of the treatments achieved was evaluated by assessing the working solution after repetitive trials using air-dried, kiln-dried and pre-steamed wood. Preservative a absorption and retention from Hazard Classes H3 to H6 (New Zealand Timber Preservation Council standard) and resin bleeding on the surface of the wood was also investigated. The strength and balance of the Copper Chrome Arsenic Oxide (CCA oxide) working and kickback solutions produced by the processes was also see analysed.

*oo Twenty four semi-commercial trials were performed on a pilot-scale plant under the 20 following conditions:

S

Treatment plant The treatment plant used consists of a 2.4m long 1300 litre volume pressure cylinder with a 1500 litre chemical work tank.

154454 The work tank solution was heated and filtered in a process line running out of the bottom of the solution tank and into the top. Heating was achieved by a 16 kW heat exchanger which received 130°C steam on the heating side. Flow was regulated by a kW variable speed mono pump with a 200 micron 2" filter position immediately prior to the pump.

Solution temperature before all treatments was adjusted to 75 0

C.

Timber A variety of timber sizes and types were used. All timber samples were 2.4m long but varied in width and breadth. Several timber sample parameters were varied and included a mixture of sapwood/heartwood, kiln-dried, air-dried and pre-steamed radiata pine. Samples were treated to New Zealand Hazard Classes H3 to H6 (ref: NZS MP 3640).

Timber sizes and their moisture contents before and after treatment are summarised in Table 4. In all cases the charges were treated in block stack with strapping.

154454 TABLE 4: Summary of All Timber Treated in Example 3 AD air drying KD kiln drying Treatment

LD.

No.of Sample.

Measured Timber Cut Size (mm) Drying Schedule Hazard Class o*o.

*o o *..2f2.

*o .2: oo o* A 10 200.* 50 AD H3 B 10 100 50 AD H3 150 50 AD Ha D 10 200"50 AD H4 E 10 100 50 AD H4 F 10 150 50 AD H4 S 1Q_ 200 KD Ha H 1Q100 50 KD Ha i10 1 50 50 KD H3 10 200 50 KD H4 K 10 T 100 50 KD H4 L 10 150 50 KD H4 M 10 -90 90 Steamed H4 /VN 9 4 *0 5 8 Steamed H4 0 1Q 71780 Steamedi H P 10 2 *0 8 4 1810 Steamed S0 2210 Steamed R- 3 241 0_ Steame H6 S 14 125 125. Steamed H T 14 125 125 Steamed l 15 _10 Steamed V 15 100 10 Steamed w 19 10Q 10 Steamed m 100 100 Steamed 154454 CCA and Solution Heating All treatments were performed using Tanalith CCA Type C Oxide preservative. For each charge approximately 1300 litres of pre-mixed CCA solution was heated to the required temperature of 75 0 C. All trials were preformed as soon as the working solution reached 75 0

C.

Treatments After flooding, the hydraulic impregnation phase was achieved by regulating air pressure onto the surface of the working solution. This pressure was transmitted through to the treatment cylinder as hydraulic pressure. The hydraulic pressures used ranged for the 24 samples ranged from 619.6 kPa to 758.7 kPa.

At the end of the hydraulic pressure phase the treatment solution was drained from the treatment cylinder (at the same or higher air pressure) by slowing releasing the air pressure in the work tank whilst admitting air pressure directly into the treatment cylinder. Once the working solution had drained from the treatment cylinder the air pressure in the treatment cylinder was further increased and .20 maintained for a set time period. This constituted the pneumatic phase of the S. process. The increased pressures maintained were in ranges from 947-1117 kPa.

At the end of pneumatic phase and before the total pressure was released the residual working solution in the treatment cylinder (ie that which resulted from: drippage from the wood, or bogey, or pipework contamination) was collected. The 154454 pneumatic pressure was then released in a controlled manner and the resultant volume of pressure kickback was measured.

A final vacuum was drawn on the treatment cylinder range -81 kPag to -91 kPag for a pre-determined period. Tlis vacuum was further improved by using a condenser to condense vapours generated from hot wood under vacuum. Upon release of the vacuum to air the vacuum kickback was collected prior to removal of the charge. At the end of treatment vacuum condensate was also collected.

Treatment processes Treatment time for all phases of 24 treatments A to X are summarised in Table o p

C

1 54.54 TABLE 5: Process Time for Each Treatment

S~

ao~ a Treatment Flooding Hydraulic Drainage Pneumatic Vacuum Total Process LD. Period Period Period Period Period Time Minutes Minutes Minutes AIinutes Minutes Minutes A 7.0 22.0 125.0 12.0 175 B 5.0 30.0 11.0 119.0 17.0 182 C 6.0 26.0 90 123.5 20.3 185 D 5.0 40.0 9.0 130.0 20.0 204 E 4.0 40.3 6.0 132.0 18.0 200 F 3.0 40.0 8.0 124.7 19.2 195 G 4.0 26.3 9.0 128.3 22.2 190 H 3G0 26.0 10.0 133.0 18.3 190 I 5.5 20.0 8.0 127.2 16.2 177 J 278 40.7 4.0 129.0 i9.0 195 K 3.0 43.0 6.0 124.0 16.0 192 L 3.7 40.0 9.0 127.5 192 199 M 2.8 40.3 7.0 128.5 19.5 198 N 3.0 61.5 6 13. 20.0 221 0 5.0 42.0 7.0 126.5 30.0 211 P 3.0 42.0 6.0 131.3 30.5 213 Q 3.6 61.8 7.0 131.7 31.0 234 R 4.1 61.4 7.4 130.5 41.0 246 S 3.9 40.8 5.0 129.0 40.8 219 T 3.8 61.0 5.0 130.0 4 239 U 3.0 1.6 4.9 183.5 41.3 234 V 0.5 8.7 3.2 4170 185 W 4.3 11.8 5.5 131.0 41.2 194 X 4.3 4.9 6.1 131.5 T 39. 187 In treatment W (refer to Table 5) after the ramping up of pneumatic air pressure the treatment plant was sealed and the compressor disconnected. Figure 2 shows that during this period which lasted for 2 hours, the air pressure did not drop in the 1300 litre treatment plant. Steam and hydraulic pressure systems in a large plant can 154454 experience relatively high reductions in pressure if the pressure source is disconnected.

The timber produced from treatments W was touch dry, drip free with no extra kickback contamination.

Preservative solution analyses Solution analyses was carried out for solutions before treatment, working and kickback solutions. Solution analyses covered analysis of Cu, Cr, As and Cr(Vl. The kickback solution consisted of pressure kickback, vacuum kickback and vacuum condensate. The results of the above analyses are shown in Table 6.

9 99* o 9 9.

99 99 9 9 9 .9999 99 9 .9 9999 9 99 9 a 9 9 9 9 9 9 9 9 9 9 9 9 9 9 9 9 099 99 ,c 154454 Table 6: Solution Analyses For All treatments Solution Beforertnt wordiig 0Solioll I(ickbtck Soluions Treaitte C Cr As TAE C11 C As 'LIE C Cr s No. r/1Ogl g10011 2/01' Ifg9 001g61iI gIOOgR 1 gIOOI g1110011Q/l100111 g1 1001111 nId 0011 A 0.132 0.094 0.304 .077 0.13 .00.295 0. 0. 0063 B 0.116 0.206 0.142 464 0.202 0.136 0.452 0.00258 0.01770 0.00272 Q0230 0118 .2 0 5 .7 0.6 .1 0.206 D.131 0.459 0.00344 0.01140 0.232 0.0171F D -720- 0.75 7Y 0823 0720Y -O 0.232 0. 003 17 07-TM70 WMOT9 T U =1 E 0.209 -633 D724 0.8 5 70T 0.359 -F236-W 07W2- -07 0.01640 W-0Tf3- Wmi F 0214 O072- .T0.83 0.21 0.37 6W 0.839 0.00374 -0.02420 017307- M ST G 0109 0 .13 7 O-T0T 070W.109 07132 0.44255 0.00278 07OF3T 0.0073 H 0105 -"4F 0.117 0.406 7106 -0.185 0.117 0.408 070o7T Oo 0.00111 00-56 1 010 0.1174 01237 -TIM-F 0.171 0.123 07D5 0.00226 0.00601 0.00211 WU.OIT .1 0.219 O-7T 7 UY43 0.11 0.363 .235- -M09 07T0- 0.00103 0.0021 O7T K 02 0 W2W 0. 3068 W 10.8171 0. 22- 816 0.00265 0.00585 00134 0.0098 L 0.217 W7 .255 .851 0.217 0.373 O723W O7.84 O7 T07 OUM W O7UUi1W 070 1' 0.273 063 WTIT FU4W 72 0.457 0.304 173Y 0.00505 W0080 00374 0.01759 N -6-F 0420.655 0.407 F47Y 0.00891 0M0355 07.0060 O7-UMT 0 6.515 0.97 037-T61 0.14 0.964 0.568 2.0O6 0.2T 0308 0.08Yg48 -17057OT 1) 3S4T- 0615 2.3 WZ554 0.6 -7.598 21 12 .117 0.03375 0.007 3 5 DT 0.21 0.6W 172 0.52 0.952 F66F 2.137 09 0.04600 0TU0TMW 0.07160 R 0.90 1. TT W T11 0.920 -T.620 1.150 3 0.04560 nTF 00 -60.18460 S 0.745 .300 0 01 1 0.7 1.8 0.90 2F937 0.0219T W500 0.01160 0.0985 T 0.416 0735 W4qfl TM 0.412T 0.730 0.473 1.615 7 T 07-WY f051TY 00020 U U7 .378 1 8 1.445 W T74W5 3.248 -0.0 2f T U03 Ta W.1306 V 0.712 1.T0 W5T 2775 0.95-1T-0 0.825 2.710 0.0417 0.11600 070RW 1660 P *0.440 0.754 0.521 1.715 07 -0.752 0.519 1.708 017003O5W 0.056 0.0732 x 0.48T-1 1 0.603 1T9 0T8DT 1YR 075WT i7W 0 0 03 00 W 9 9 9 9 i.

9 99 9 154454 Cu, Cr and As ratios did not change during the 24 treatments. This shows that although hot CCA solution was used for all trials, solution disproportionation did not occur. Comparison of treating solution elemental ratios with initial CCA oxide concentration elemental ratios shows that the elemental ratios remained substantially constant (see Table 7).

TABLE 7 Treatment Solution Before Solution Before Solution Before Treatment Treatment Treatment No Cu Cr As Ratio% Ratio% Ratio% CCA Oxide 25.1 44.0 30.9 Concentrate A 25.7 43.4 30.9 B 25.0 44.4 30.6 C 25.7 44.6 29.8 D 25.2 45.6 29.3 E 25.6 44.8 29.6 F 25.7 44.6 29.7 G 24.2 45.2 30.6 H 25.9 45.3 28.8 I 25.2 43.8 31.0 J 26.0 44.7 29.3 K 25.7 45.4 28.9 L 25.5 44.5 30.0 M 26.0 44.2 29.8 N 24.9 46.0 29.1 0 25.0 47.3 27.8 P 25.4 45.8 28.8 Q 24.8 44.9 30.4 R 25.0 44.0 31.0 S 25.2 44.1 30.7 T 25.4 44.8 29.9 U 25.2 44.2 30.6 V 25.7 43.6 30.7 W 25.7 44.0 30.4 X 24.9 44.0 31.1 154454 The invention can successfully treat air- and kiln-dried, gauged and ungauged, steamed, square sawn, round and half round radiata pine timber when performed as a combined impregnation and fixation process. Treatments achieved comply to standard MP 3640 and Hazard Classes H3, H4, H5 and H6.

The same working solution (with 'top-ups') was used for all 24 treatments and remained in very good condition with no apparent sludging. The only sludge which has appeared on the timber has been a function of resin bleed from the timber not from the working solution.

The above examples are intended to illustrate use of the invention. The invention may be practised with numerous modifications and variations as will be apparent to iii those skilled in the art. For example numerous types of wood samples, treatment times, chemicals, concentrations of chemicals and treatment times may be used.

9 9 9 oooo *oo *r

Claims (36)

1. A method of impregnating wood or wood based products with a chromium based wood preservative chemical under pressure comprising: a) heating a liquid composition comprising a chromium based wood preservative chemical and impregnating the hot composition into the wood under hydraulic pressure and controlling the hydraulic pressure to control the amount of chemical impregnated into the wood; and b) replacing the hydraulic pressure with sufficient pneumatic pressure to hold the impregnated composition in the wood while the unused composition is removed from the treatment vessel.

2. A method according to claim 1 including finally subjecting the wood to a vacuum sufficient to remove any residual liquid from the surface of the wood to clean said surface.

3. A method according to either one of claims 1 and 2, wherein the composition is heated to a temperature in the range 60 0 C to 95 0 C prior to impregnation into the wood. 9*59 r.

4. A method according to any preceding claim wherein a pressure in the range 20 to 2000 kPa is used in the hydraulic pressure phase.

A method according to claim 4 wherein a pressure in the range 400 to 2000 kPa is used in the hydraulic pressure phase. 154454

6. A method according to claim 5 wherein a pressure in the range 600 to 1500 kPa is used in the hydraulic pressure phase.

7. A method according to any one of claims 4 to 6 wherein the pneumatic pressure used while the unused composition is removed from the treatment vessel is at least as high as the hydraulic pressure which it replaces.

8. A method according to claim 7 wherein the pressure of the pneumatic phase while the unused composition is removed from the treatment vessel in the range 20 to 2000 kPa.

9. A method according to claim 8 wherein said pneumatic pressure while the unused composition is removed from the treatment vessel in the range 400 to 2000 kPa.

10. A method according to claim 9 wherein the pneumatic pressure of the unused composition is removed is in the range 600 to 1500 kPa. S

11. A method according to any one of claims 7 to 10 wherein after removal of the unused composition, the pneumatic pressure used is at least 30% more than the pressure used during the hydraulic pressure phase.

12. A method according to claim 11 wherein after removal of the unused composition, the pneumatic pressure used is at least 8 0% more than the pressure used during the hydraulic pressure phase. 154454

13. A method according to any preceding claim wherein the duration of the hydraulic phase is in the range 5 to 240 minutes.

14. A method according to claim 13 wherein the duration of the hydraulic phase is in the range 7 to 180 minutes.

A method according to any preceding claim wherein the duration of the pneumatic phase is in the range 5 to 240 minutes.

16. A method according to claim 14 wherein the duration of the pneumatic phase is in the range 7 to 180 minutes.

17. A method according to any preceding claim wherein the hydraulic pressure used is in the range of 20 to 2000 kPa and after the unused composition is 15 removed from the treatment vessel the pneumatic pressure is increased to a pressure I 100-1000 kPa higher than the pressure used during the hydraulic pressure phase so as to force the preservative further into the wood. S and in the range 26 to 2000 kPa.

18. A method according to claim 17 wherein the pneumatic pressure used to force the chemical further into the wood is at least 3 0 o higher than the pressure used in the hydraulic phase; and in the range 26 to 2000 kPa.

19. A method according to claim 17 wherein the pneumatic pressure used to force the chemical further into the wood is 154454 at least 8 0 higher than the pressure used in the hydraulic phase; and in the range 36 to 2000 kPa.

20. A method according to claim 18 wherein said pneumatic pressure is used to force the chemical further into the wood is in the range 520 to 2000 kPa.

21. A method according to claim 20 wherein said pneumatic pressure used to force the chemical further into the wood is in the range 780 to 1500 kPa.

22. A method according to any preceding claim wherein the chemical is deposited in the core of the wood at a concentration of at least 75% of that in the outer one third of the cross-section of the wood. 9 15

23. A method according to claim 22 wherein the chemical deposited in the core of the wood is at a concentration of at least 100/% of that of the outer one third of the cross-section of the wood.

24. A method according to any preceding claim wherein the time the wood 20 is under hydraulic pressure plus the time the wood is under pneumatic pressure is less than five hours.

A method of claim 24 wherein said time is less than two hours.

26. A method according to any preceding claim wherein the material to be impregnated is a mixed charge of sapwood and heartwood. impregnated is a mixed charge of sapwood and heartwood. 154454

27. A method according to any one of claims 1 to 26 wherein the chromium based wood preservative chemical is a copper chrome arsenic, copper chrome boron, copper chrome zinc fluoride or copper chrome based wood preservative chemical.

28. A method according to claim 27 wherein the preservative is a copper chrome arsenic preservative.

29. A method according to any preceding claim wherein the gas used to apply the pneumatic pressure is air or nitrogen.

A method according to any preceding claim wherein the pneumatic pressure is maintained for a period sufficient to allow fixation of the chemical in the 9 wood. i

31. A method of impregnating wood with a chromium based wood preservative comprising: 9 9 heating the preservative solution and impregnating said solution the wood at a solution temperature in the range of 60 to 95oC under hydraulic pressure; allowing a predetermined amount of said solution to be impregnated S* into the wood; replacing the hydraulic pressure with sufficient pneumatic pressure, using air or nitrogen, to hold the impregnated preservative in the wood while the unused solution is removed from the treatment vessel to prevent kickback contamination of the unused solution; 38 increasing the pneumatic pressure to force the preservative further into the wood, and maintaining the pneumatic pressure at a level higher than used in the hydraulic pressure phase for a time sufficient to allow fixation of most of the preservative within the Swood.

32. A method according to any preceding claim wherein prior to application of hydraulic pressure the composition comprising the preservative or other wood modifying chemical is heated and held in contact with the wood for about 5-20 minutes.

33. A method according to any preceding claim wherein following commencement I0 of the pneumatic pressure phase, the pressure vessel is sealed to maintain the elevated pressure without using a compressor.

34. A method of impregnating wood or wood based products with a chromium based wood preservative, substantially as hereinbefore described with reference to any one of the examples, but excluding reference to any comparative examples. i

35. A wood or wood based product treated by a method of any proceeding claim.

36. A wood or wood based product impregnated with a chromium based wood preservative, substantially as hereinbefore described with reference to anyone of the I examples, but excluding reference to any comparative examples. 0* 0 Dated 20 April, 2000 New Zealand Forest Research Institute Limited Patent Attorneys for the Applicant/Nominated Person SPRUSON FERGUSON [I :\l)ay I ih\l3 U103521 .doc:KWW