AU721051B2 - Method and apparatus for making an ophthalmic lens - Google Patents

Description

T*T P/00/0011 Regulation 3.2

AUSTRALIA

Patents Act 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT

ORIGINAL

oooo o Name of Applicant: Actual Inventors: Address for service in Australia: Invention Title: JOHNSON JOHNSON VISION PRODUCTS, INC Jonathan Patrick ADAMS and John B. ENNS CARTER SMITH BEADLE 2 Railway Parade Camberwell Victoria 3124 Australia Method and Apparatus for Making an Ophthalmic Lens The following statement is a full description of this invention, including the best method of performing it known to us METHOD AND APPARATUS FOR MAKING AN OPHTHALMIC LENS Background of the Invention This invention relates to an improved method and apparatus for making ophthalmic lenses. In particular, this invention is suited to molded ophthalmic lenses such as hydrogel contact lenses, although the method is also suitable for other small, high-precision ophthalmic lenses such as intraocular lenses and other methods of manufacturing such as by spin casting.

Soft ophthalmic lenses for placement on the cornea or within the eye, such as contact lenses or soft intraocular lenses, can be made by a variety of techniques.

Ophthalmic lenses can be made by spin casting a monomer material in a rotating mold then polymerizing the material "so shaped. Another method used to manufacture both contact lenses and intraocular lenses is precision lathing of a piece of material which is then polished and used as a lens.

Recently the molding of soft contact lenses and soft 25 intraocular lenses has come into favor. This technique has the advantages of repeatability and speed that compares favorably with the prior methods of manufacturing lenses. Techniques for successfully molding hydrogel lenses can be found in U.S. Patents 4,495,313 and 4,640,489 to Larsen and 4,889,664; 4,680,336 and 5,039,459 to Larsen et.al. These patents specifically described the use of acceptable monomers, a diluent which substitutes for water during the molding process and is replaced with water after the molding has been completed. The advantage VTN-66 2 of this technique is that the optical properties, size and shape of the lens thus made does not change as radically as with methods that do not utilize such diluent.

It is further known in the art to mold such ophthalmic lenses by forming a monomer or monomer mixture in a mold such as one made from polystyrene or polypropylene. An example of this art can be found in U.S. patent 4,565,348 to Larsen wherein the requirement for a polystyrene mold materials, chemistry and processes are discussed. In contrast to the above polystyrene molds, another example is the use of polypropylene or polyethylene molds such as that described in U.S. Patent 4,121,896 to Shepherd.

15 A particular problem, however, is that the monomer or monomer mixture usually contains dissolved gases from the air (02 and N 2 that may cause at a minimum bubbles from inert gas, or interfere with polymerization if the gas is reactive with free radicals available -during polymerization.

It has been recognized that in the manufacture of ophthalmic lens, particularly contact lenses, it is desirable to eliminate oxygen from the monomer mix, 25 because oxygen interferes with the polymerization reaction. This is found to still be true with the production of molded contact lenses using a diluent. One practice is to degas the monomer or monomer mixture placing the monomer mixture into a rotary evaporator unit (such as the Rotovap available from Buchi Rotavapor, Inc.

of Flawil, Switzerland; sold by Fisher Scientific of Springfield, NJ) to remove excess gas. This procedure for instance,-is applicable to the monomer mixtures described in U.S. Patents 4,889,664 and 4,495,313 where the mixture VTN-66 3 is rotated under subatmospheric pressure. The container with a monomer mixture is then flushed with nitrogen and held under a nitrogen atmosphere until it is used.

This is done in a round flask half filled with monomer.

The Rotovap unit spins the monomer to increase the surface and the reduction in gas is proportional to the ratio of the lower pressure to atmospheric pressure, that is, 760 mm Hg.

The overall gas content is reduced to the above ratio, but the N 2 to 02 ration remains the same as in air.

Because the container is then back filled with N 2 nitrogen 15 gas has an opportunity to redissolve in the monomer mixture. The end result of the process is then actually o an 02 removal process. While this procedure solves the problem of 02 reaction with the monomer and polymerization process, it does not eliminate problems associated with dissolved nitrogen which may cause bubbles to form during polymerization. In addition, once the monomer is reduced in oxygen content, exposure to the oxygen in the air during subsequent handling can cause 02reabsorption.

25 In addition, at the low pressures (less than 40 mm Hg) volatile components of the monomer mixture may evaporate changing the composition of the monomer.

Finally, there are additional handling and manufacturing problems associated with maintaining a nitrogen environment around the gas-reduced monomer mixture produced in a batch process.

VTN-66 t 4 It is, therefore, an object of the present invention to greatly reduce the amount of dissolved oxygen in the monomer mixture used to produce ophthalmic lenses.

It is a further object of the invention to reduce the amount of dissolved nitrogen in the monomer mixture used for ophthalmic lens production.

SUMMARY OF THE INVENTION Accordingly, the invention provides a method of making an ophthalmic lens comprising the steps of: supplying a monomer to a receiving means, pumping said monomer from said receiving means into a gas permeable tube via one end of the tube and along the interior length of the tube, drawing and maintaining a subatmospheric pressure about the exterior of said tube, to degas the monomer within the @0 Go .gas permeable tube, 20 removing said monomer from the other end of said tube, S: to placing said monomer into a mold and causing the monomer to assume the shape of an ophthalmic lens, polymerizing said monomer into a polymer ophthalmic 0 lens, o 25 removing said polymerized ophthalmic lens from the mold.

••go o In another aspect, the invention provides an apparatus for 0000 fabricating an ophthalmic lens comprising: means for supplying a monomer, @000 S 30 a gas permeable tube connected at one end to said means for supplying the monomer so as to supply the monomer to the interior of said tube, Ja chamber about said gas permeable tube, BGC:YJ:#31125.RSI 19 April 2000 4 i1 means for drawing and maintaining a subatmospheric pressure, said subatmospheric pressure means connected to said chamber to thereby degas the monomer within the gas permeable tube, and means for removing and transferring the monomer from the other end of said tube to a lens mold to fabricate said lens.

In the preferred practice of the invention, the apparatus includes a means for introducing mixing into the flow of the monomer within the tube in order to expose the bulk of the monomer to the gas permeable walls of the tube.

Excess monomer that may be processed within the chamber and exiting the gas permeable tube, but not needed for lens molding when it is processed, may be returned to the original container from which it is drawn and is later reprocessed through the degassing system.

0o Preferably, the gas permeable tube is made of silicon rubber.

20 The method preferably includes the step of maintaining an inert gas environment around the monomer removed from the gas e permeable tube until the monomer is polymerized into an ophthalmic lens.

e g.

O0@@ O •O

O

go 0

S

OSS*

S

19 April 2000 6 BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a simplified flow chart showing the various components of the monomer degassing and lens production system.

Figure 2 is a perspective view of the physical equipment shown in the degassing flowchart of Figure 1.

Figure 3 is a detailed planar view showing in section the degas unit comprising a portion of the degassing system.

i Figure 4 shows in detail one of the individual gas permeable tubes shown in the degassing unit of Figure 2 15 and including within the tube a static flow mixer tube.

6 Figure 5 is a planar view, partially in section, of the monomer dosing portion of the subject system.

*o DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Referring now to Figures 1 and 2 showing the preferred embodiment of the present invention in flowchart and physical form, respectively, monomer is provided in a container 10, typically 15 liters in volume. The container is connected to the monomer degassing system by means of a line 12. Suction is developed by pump 14 to draw the monomer from the drum 10, through line 12, by pump 14, and out the pump discharge 16.

Unless otherwise specified herein, the lines used for monomer flow through the system can be fashioned of any gas impermeable material with which the monomer ischemically non-reactive.

VTN-66 -7- While going through discharge line 16, monomer passes through filter 18 in order to remove extraneous particulate contaminates that may be present in the monomer.

Monomer is then provided to the inlet 20 of the degas unit 22. Within the degas unit, monomer is divided among a plurality of tubes 24, and then recombined into a degas unit discharge 26. The degas unit is operated under a low ambient pressure typically around four torr which is provided by vacuum pump 28. This vacuum pump is attached to the degas unit 22 by line 30 and discharges the excess air from the degas unit by way of line 32.

15 After the monomer exits degas unit 22 by discharge line 26, it passes through an oxygen monitor 34. This monitor measures the residual oxygen within the monomer to insure that the degas unit is functioning properly. If the oxygen content of the monomer is indicated as being too high, operation of the ophthalmic lens production line can be halted until the problem is corrected in order to avoid production of defective lenses.

Once oxygen monitor 34 has determined that the oxygen oooo 25 content of the monomer is sufficiently low, monomer passes through line 36 into manifold 38. The manifold is used as a common source to supply a plurality of precision dose pumps 40 regulated by pump controllers 41 and used to fill individual contact lens molds at, the monomer dosing station 43. The pumps 40 used to pump processed monomer delivered to manifold 38 are IVEK pumps made by the Motor and Control Division of Pacific Science, Rockford,

IL.

These pumps provide precision doses of degassed monomer to mold cavities 74 via nozzles 72.

VTN-66 -8 The excess degas monomer which is processed by the system travels along return line 42 to the monomer drum 10. In addition to assuring that sufficient monomer is processed to supply the filling machines used to produce the lenses, this return line 42 allows the monomer degassing system to continue to operate if the filling machines are temporarily shut down for any reason. In this way, there is no need to shut down the monomer degassing system if the remainder of the lens production system is inoperative.

Turning now to Figure 3, there is shown in greater detail the monomer degassing unit 22. The degassing unit is i"1' shown to be comprised of a pressure boundary consisting of *15 an outer cylindrical wall 44, a top plate 46 and a bottom plate 48. Contained within the cylindrical side wall 44 is a port 30, which is connected to vacuum pump 28 (not "shown).

Top plate 46 and bottom plate 48 are attached to the cylindrical side walls 44 by use of flanges 50 compressed upon 0-rings 52 and 54 found on the bottom and top plates, respectively. Compression of the o-rings and attachments of plates 46 and 48 to flanges 50 is accomplished by bolts 56 that attach the plates to the flanges.

Passing through top plate 46 is the monomer inlet line This inlet line passes through the top plate 46, divides within the chamber 22 by means of a connector into two lines 57 of equal length. Lines 57 are preferably of equal length in order to provide equal back pressure resulting in equal of monomer flow through both lines to two separate headers 58. -Each of these headers is connected to ten silicon tubes 60-which are permeable to VTN-66 -9 oxygen. The tubes 60 are arranged in a 3 4 3 offset array, 0.300 spacing center-to-center. The flow through the tubes is from the bottom up in order to fill the tubes and not entrain voids in the liquid.

The internal structure of the degas unit stands off the bottom of chamber 22 by stainless steel pipe 66.

Stainless steel pipe 67 supports Delrin blocks 68 at the desired separation and these blocks, in turn, support manifolds 58 and 62 containing therebetween extended gas permeable tubes During its time of residence in the silicon tube 60 in the low pressure degas chamber 44, oxygen and nitrogen migrate 15 out of the monomer through tube wall 60, drawn out by the vacuum pump through chamber outlet 30. As the monomer approaches the top of the chamber it is essentially free of dissolved gasses.

The silicon tubes near the top of the chamber are connected to second headers 62 which combine silicon tubes back into common tubes 64. These tubes are made of an impervious material and are of the same length in order to avoid pressure differences which could result in flow imbalances. Tubes 64 are then connected in a fashion to provide a single degas unit outlet 26. The monomer then continues as described by reference to Figures 1 and 2.

Turning now to Figure 4, there is shown in detail a section of gas permeable tube 60. Contained within this gas permeable tube is static flow mixer VTN-66 10 Without such a flow mixer 70, the amount of monomer exposed to the inner tube surface of the gas permeable tube 60 would be greatly lessened. Although the flow of the monomer through the tube without the static mixer would not be plug flow, that is, with no mixing at all, a realistic expectation would be that laminar flow would occur. There would be some mixing, but a boundary layer would form along the inner surface of the tube wall. The introduction of the static flow mixer 70 breaks up the boundary layer and causes turbulent flow over the entire cross section of the flow along the entire length of the tube.

The type of gas permeable tubing used must be selected with care. The use of a blood oxygenator tubing made of porous polypropylene in reverse (to remove gas rather than supply it) was attempted and found to be adequate in reducing the oxygen content of the monomer, but had the draw back of allowing- monomer to leach -through the polypropylene tubing. A solid membrane is needed to prevent leaching of the monomer.

Another blood oxygenation material, a silicon membrane, was employed and found to be both permeable to oxygen and nitrogen while not allowing monomer to leach through the tubing wall. It was found, however, that a color additive to the silicon membrane leached into the monomer during processing.

For this reason, the preferred material for the gas permeable tubing is STHT tubing produced by Sanitech Inc.

of Andover, NJ from Q74780 medical grade silicone rubber manufactured by Dow Corning of Midland, MI. This silicon VTN-66 11 tubing does not contain an additive that can be taken into the monomer.

The apparatus is arranged so that each set of tubes 24 contains ten tubes, each 1\4 inch inner diameter with a wall thickness of 1\32 inch. Tubing originally employed having a 60 durometer hardness was found to have inadequate resistance to back pressure of the monomer being pumped. The walls of the tubing would expand and circumvent the function of the static mixers. In addition, under operating vacuum conditions, the monomer pressure would expand and subsequently rupture the tube.

The use of 80 durometer silicon tubing was found to 15 eliminate the above problems.

e The apparatus then ultimately consists of two sets of ten tubes three feet long, each of the tubes containing static mixers. These static mixers are made of Delrin, inch in diameter and 6 -inches long, produced by KOFLO, Inc. of Carrie, IL.

In operation, monomer flows into the degas unit with an :oxygen concentration of 17 parts per million and exits the chamber at .6 parts per million. The preferred vacuum level in the chamber (outside the tubing) is between 2 and torr.

Referring now to Figure 5, there is shown in greater detail monomer dosing station 43. Leading into the station from precision dose pumps 40 (not shown) is 1/8 inch outer diameter tube 76 meeting the above established criteria of gas impermeability and chemical inertness with respect to the monomer. This inlet tube 76 is connected VTN-66 12 by means of fitting 78 having 1/8 inch knurled nylon thumb screws 80 to 1/16 inch outer diameter tube 82.

These tubes in turn are attached to 1/16 inch plastic ferrule 81 by means of 1/16 inch nylon knurled thumb screws 84. Ferrules 81 are connected to nozzles 72 which provide the dose of monomer to cavities 74 (not shown, see Figure 1).

The dosing nozzle 72 has its exit surface 86 cut at an angle of 450 150. The nozzle is placed .50mm .2mm above the cavity being dosed.

The performance of the system is shown in the tables S: 15 below.

TABLE 1 MONOMER RATE 18.6 ml/ min S: OXYGEN VACUUM (TORR) CONCENTRATION (PPM) TEMPERATURE

(OC)

760 17.6 22.9 4 2.5 22.2 25 25 TABLE 2 MONOMER RATE 8.5 ml/ min

OXYGEN

VACUUM (TORR) CONCENTRATION (PPM) TEMPERATURE (oC) 760 17.4 22.5 4 0.58 22.4 The length of silicon tubing to process the above flow of monomer is a total of 60 meters. Without the static mixtures, it has been calculated that approximately 2 to 3 kilometers of tubing would be required.

VTN-66 13 In operation, the unit is supplied with the monomer in liter containers and operated as described above and depicted in Figures 1 and 2. The method preferably includes the step of maintaining an inert gas environment around the monomer removed from the gas permeable tube until the monomer is polymerized into an ophthalmic lens.

This is done by having the monomer travel through gas impermeable lines and reservoirs containing no gas, or by maintaining an inert gas environment about the degassed monomer. Further to Figures 1 and 2, the monomer processed and delivered to manifold 38 is pumped by precision dose pumps 40. These pumps and controllers 41 are IVEK pumps made by the Motor and Control Division of Pacific Science, Rockford, IL. These pumps supply nozzles 15 72 which then deposit precision doses of degassed monomer in mold cavities 74.

These mold cavities are then mated with the opposing mold portion to form a cavity containing the degassed monomer and forming the shape of the lens. Polymerization is then initiated by exposure to UV light and the mold halves are then separated and the ophthalmic lens is removed. Ways by which the lens may be removed from the mold are known in the art and depend upon the molding process and materials used. One example in which lens removal is accomplished is found in US Patents 5,094,609 and 5,080,839, both to Kindt-Larsen.

The above described preferred process utilizes a mold casting method but may alternately employ a spin cast process where only one portion of a mold is dosed with the appropriate amount of degassed monomer. Rotated at an angular velocity to cause the unclosed surface of the VTN-66 14 monomer to take on the desired shape, polymerization is then initiated by ultraviolet light or heat.

The above description sets forth by example only, the invention which is defined in its broadest sense by the claims that follow.

•o° VTN-66

Claims (12)

1. A method of making an ophthalmic lens comprising the steps of: supplying a monomer to a receiving means, pumping said monomer from said receiving means into a gas permeable tube via one end of the tube and along the interior length of the tube, drawing and maintaining a subatmospheric pressure about the exterior of said tube, to degas the monomer within the gas permeable tube, removing said monomer from the other end of said tube, placing said monomer into a mold and causing the monomer to assume the shape of an ophthalmic lens, polymerizing said monomer into a polymer ophthalmic lens, o removing said polymerized ophthalmic lens from the mold.

2. The method of claim 1 further comprising the step of -inducing mixing of the monomer within said tube.

S"3. The method of claim 1 further comprising the step of 20 returning an amount of monomer removed from said tube which is in excess of that required for said mold cavity to said receiving means.

4. The method of claim 1 further comprising the step of maintaining an inert environment for said monomer removed 25 from said gas permeable tube until said monomer is 0000 polymerized into a lens.

5. The method of claim 1 wherein said pumping of monomer is 6600 into a silicone rubber tube.

6. An apparatus for fabricating an ophthalmic lens 0000 30 comprising: means for supplying a monomer, a gas permeable tube connected at one end to said means A for supplying the monomer so as to supply the monomer to the 19 April 2000 interior of said tube, a chamber about said gas permeable tube, means for drawing and maintaining a subatmospheric pressure, said subatmospheric pressure means connected to said chamber to thereby degas the monomer within the gas permeable tube, and means for removing and transferring the monomer from the other end of said tube to a lens mold to fabricate said lens.

7. The apparatus of claim 6 further comprising means for inducing monomer mixing within said tube.

8. The apparatus of claim 7 wherein said means for inducing mixing is a static mixer.

9. The apparatus of claim 6 further comprising means for returning the amount of monomer removed from the other end of said tube that is in excess of that required for said mold cavity to said receiving means.

The apparatus of claim 6 wherein said gas permeable tube is comprised of silicone rubber.

11. A method of making an ophthalmic lens including the 20 steps substantially as hereinbefore described. 5

12. An apparatus for fabricating an ophthalmic lens substantially as hereinbefore described with reference to the accompanying drawings. DATED: 19 April 2000 *oSo 25 2500 CARTER SMITH BEADLE :"Patent Attorneys for the Applicant: 0 "JOHNSON JOHNSON VISION PRODUCTS INC 0055 O 00 o 0• 19 April 2000