AU719067B2

AU719067B2 - Synthesis of titanocenes

Info

Publication number: AU719067B2
Application number: AU11612/97A
Authority: AU
Inventors: Craig Blankenship
Original assignee: Boulder Scientific Co
Current assignee: Boulder Scientific Co
Priority date: 1996-11-22
Filing date: 1996-11-22
Publication date: 2000-05-04
Anticipated expiration: 2016-11-22
Also published as: JP2000506545A; AU1161297A

Description

WO 98/22476 PCTI~S96/18666 -1- SYNTHESIS OF TITANOCENES FIELD OF THE INVENTION This invention relates to the synthesis of titanocenes including constrained geometry titanocene catalysts utilizing a unique titanium trichloride reagent.

BACKGROUND OF THE INVENTION The evolution of metallocene-based catalysts for the polymerization of ethylene and higher a-olefins is reviewed in H.H. Brintzinger, et al., Angew.

Chem.Int.Ed.Enql. 34:1143-1170 (1995) and in P.C.

Mohring, et al., J. Organometal.Chem. 479:1-29 (1994).

The applications of chiral metallocenes in organic synthesis are reviewed in R.L. Halterman, Chem.Rev.

92:965-994 (1992). These reviews highlight the applications of state-of-the art metallocenes. Most often, these applications center on the use of titanium containing and other Group IV metallocenes.

The early preparations of Group IV metallocenes involved reactions of the metal tetrahalides, typically the tetrachlorides, with deprotonated ligands, such as sodium cyclopentadienide, to give the metallocenes in good yields. The metallocenes of current interest possess more complicated ligand structures, and their preparations are not as straightforward. For the preparation of these metallocenes, the use of titanium tetrachloride often results in low yields of the desired metallocenes. Titanium trichloride (TiC13) is often specified for use in place of titanium tetrachloride (TiC1 4 subsequent oxidation gives the desired metallocenes in greatly improved yields.

For some recent examples which specify the use of titanium trichloride, see L.A. Paquette, et al., Organometallics 14:4865-4878 (1995); F. Zaegel, et al., Organometallics 14:4576-4584 (1995); and M. E.

Huttenloch, et al., Organometallics 11:3600-3607 (1992).

Halterman, supra, cites references which show the use of titanium trichloride in several metallocene preparations.

WO 98/22476 PCT/US96/18666 -2- The titanium trichloride so used is produced from commercial titanium tetrachloride. Titanium trichloride produced by hydrogen reduction of the tetrachloride is most often used in lab-scale preparations. For commercial-scale preparations, this is impractical due to cost and the presence of acidic impurities. These impurities require purification of the titanium trichloride, typically by preparation and isolation of an ether complex, usually the tetrahydrofuran complex.

Commercially-available titanium trichloride is produced by the reduction of the tetrachloride with alkyl aluminum compounds. The titanium trichloride so produced contains aluminum chloride, which is not removed.

Typical analyses specify 76-79 weight percent of titanium trichloride with the remaining weight percent comprised mostly of aluminum chloride. The use of aluminum-reduced titanium trichloride in metallocene preparations often gives products which contain varying amounts of aluminumcontaining impurities. Separation of these impurities from the product titanocenes is not straightforward in most cases, especially on a commercial scale. The presence of these impurities can have significant adverse effects during subsequent uses of the titanocenes, particularly in olefin polymerizations.

Accordingly, a need exists for a titanium trichloride reagent useful to produce titanocenes free of aluminum containing impurities.

DEFINITIONS

For the purposes of this invention, the following terms have the meaning stated: Titanocene Compound A compound comprised of titanium bonded to one or more cyclopentadienyl rings.

Titanocene Ligand A chemical precursor which contains cyclopentadienyl or substituted cyclopentadienyl WO 98/22476 PCT/US96/18666 -3moieties (including indenyl, fluorenyl, etc.) used to prepare a titanocene compound.

Constrained Geometry Catalyst (CGC) A catalyst in which the metal center is contained in a ring structure and covalently bonded to a cyclic group via a delocalized 7-system and covalently bonded via a sigma-bond to another atom such as carbon, nitrogen, oxygen, etc. A small ring size induces constraint about the metal atom center. For titanium-containing CGC's, the incorporated titanium atom can be in a formal or +2 oxidation state. See EP application 90309496.9, WO 95/00526 and U.S. Patent 5,470,996.

CpSA Ligand (t-butylamino)(tetramethylcyclopentadienyl)dimethylsilane.

(CpSA) 2 doubly-deprotonated CpSA ligand.

(CpSA)2-TiCI2 [(t-butylamido)(tetramethylcyclopentadienyl)dimethylsilane]titanium dichloride.

Substantially Stoichiometric Amount An amount not less than 90% nor more that 110% of stoichiometric.

SUMMARY OF THE INVENTION This invention includes a general method for producing titanium trichloride containing mixtures suitable for the preparation of titanium-containing metallocenes including constrained geometry Ti(IV), Ti(III) and Ti(II) complexes free of aluminum containing impurities.

The titanium trichloride containing mixtures are produced by the preferably stoichiometric reaction of an organometallic compound, such as n-butyl lithium or n-butyl magnesium chloride, with titanium tetrachloride in a non-interfering solvent medium. These mixtures are used directly without isolation of the titanium trichloride in reactions with appropriate ligands to produce the desired titanocenes, including constrained geometry titanium complexes, in good yields. The WO 98/22476 PCT/US96/18666 -4resulting titanocene products are specifically free of aluminum-containing impurities.

DETAILED DESCRIPTION OF THE INVENTION The invention is a method for producing a titaniumcontaining metallocene compound which comprises separately providing a first reaction mixture containing titanium trichloride and a second reaction mixture containing a magnesium or alkali metal or alkaline earth metal salt of a metallocene compound ligand. The first and second mixtures are combined for reaction to produce an intermediate from which an aluminum-free titanocene useful as an olefin polymerization catalyst may be synthesized.

The first reaction mixture is produced by reacting TiCl 4 with an alkali metal compound having the formula Rx-M or a Grignard reagent having the formula RMgX. In each formula, R is a straight or branched chain aliphatic hydrocarbon group, preferably an alkyl group, having 2 to 10 carbon atoms. R may also be an alkaline earth metal such as calcium, barium or strontium. X is the value of M. In the formula Rx-M, M is an alkali metal such as sodium, potassium or lithium. In the formula RMgX, X is a halogen, preferably chlorine. n-butyl lithium or n-butyl magnesium chloride are preferred. The reactants are combined in substantially stoichiometric amounts in a non-interfering, preferably hydrocarbon, medium.

Useful hydrocarbon media include aliphatic or aromatic hydrocarbons, such as hexane, heptane, cyclohexane, benzene, toluene and xylene. Toluene is preferred for the specific examples shown here. Useful ether and polyether solvents include tetrahydrofuran, diethyl ether, ethylene glycol dimethyl ether, and dioxane. Mixtures of any hydrocarbon and ether solvents are useful for the reaction.

WO 98/22476 PCT/US96/18666 The reaction is preferably accomplished under dry, oxygen-free conditions. The temperature at which the reaction is conveniently conducted is -20 0 C or 120°C, with the optimum temperature range being 30-40 0

C.

The second reaction mixture is separately provided by deprotonating the desired metallocene ligand with the appropriate base by known methods. See, generally, Paquette, et al., supra; Zaegel, et al., supra; and Halterman, supra.

The first reaction mixture, which includes the medium or solvent, titanium trichloride and a metal halide such a LiCI or MC1 2 is added directly without isolation of the titanium trichloride to the second deprotonated ligand reaction mixture to produce a first titanocene.

DESCRIPTION OF THE FIGURE Figure 1 is a generalized depiction of steps and as comprised by one embodiment of the invention for preparation of a Ti(IV) complex constrained geometry catalyst.

Step (1)-Aluminum-Free TiCl 3 Step of Figure 1 illustrates the reaction of TiC14 in substantially stoichiometric amount with n-butyl lithium or n-butyl magnesium chloride to produce TiCl 3 and lithium or magnesium chloride in a hydrocarbon or ether medium, or mixed hydrocarbon and ether medium.

Step (2)--Deprotonation Of a Metallocene Compound Ligand Step of Figure 1 illustrates the double deprotonation of the metallocene compound ligand (tbutylamino)(tetramethylcyclopentadienyl)dimethylsilane (CpSA ligand) with an organometallic deprotonating agent, preferably an organolithium or an organomagnesium WO 98/22476 PCT/US96/18666 -6compound (Grignard reagent), in a hydrocarbon medium, preferably toluene.

The solvent medium and the organometallic compound may be the same as or different from the solvent medium and the organometallic compound used in Step The concentration of the CpSA ligand in the solvent is appropriately 0.05 to 1.5 M, preferably 0.45 to 0.6 M.

Any Grignard reagent may be used to deprotonate the metallocene compound ligand, CpSA. Useful Grignard reagents have the formula RMgX as defined above.

Isopropyl magnesium chloride is preferred. A practical range of Grignard concentration in the solvent is to 3.0 M, preferably 1.9 to 2.3 M. For CpSA, the temperature is controlled to be 45-50 0 C. at the end of the Grignard feed, and then heated to 85-90*C for the prescribed time.

The Step reaction mixture is preferably used directly in Step as the toluene solution present in the reaction vessel in which it is produced.

Step (3)-Reaction of TiCl 3 With Deprotonated Ligands-Production of (CpSA)2-TiCl 2 Step of Figure 1 illustrates one method for reacting the titanium trichloride containing reaction mixture of Step with the (CpSA) 2 containing second reaction mixture of Step to produce [(t-butylamido) (tetramethylcyclopentadienyl) dimethylsilane]titanium dichloride, (CpSA)2- TiC1 2 In this embodiment of the invention, the agitated Step reaction mixture is transferred directly into the reactor containing agitated Step reaction mixture. Preferably, the vessel which contained the Step mixture is rinsed with toluene which is then charged to the Step reactor. The exothermic reaction mixture becomes reddish brown in color. A temperature rise of about 15*C. is usually observed.

WO 98/22476 PCT/US96/18666 -7- A chloride-containing oxidizing agent, such as dichloromethane or silver chloride, is then charged to the reaction vessel utilized in Step The resulting reaction mixture is agitated for a time appropriate, usually about two hours, for the Step reaction to occur.

Solvents are removed under reduced pressure, 60-80 mm Hg, to about one-half of the starting volume. Hydrocarbon solvent, toluene, is added back, Celite® filter aid is added, and the mixture is filtered. Solvents are distilled to concentrate the product.

The solid titanocene can be isolated from this mixture by methods dependent upon the actual compound being produced. For the (CpSA) 2 -TiC 2 example shown in Figure 1, the solid product was collected in 75-80% yield as described in Example 6. Additional material of lower purity can be isolated upon further manipulation of the mother liquors. Alternatively, the product solution obtained after removal of the magnesium salts can be used directly to produce other metallocenes described in Example 6.

EXEMPLIFICATION OF THE INVENTION Preparative Procedures For Titanium Trichloride Reactant Mixtures and Resulting Metallocenes The general procedure for the preparation of titanium trichloride-containing mixtures by the reaction of titanium tetrachloride and an organometallic compound under an inert atmosphere is first described, followed by three specific examples. The reaction apparatus consisted of a 500-mL 3-neck flask equipped with a mechanical stirrer. On one side-neck was placed a Claisen adapter with a reflux condenser and a thermometer inserted into the reaction mixture. This apparatus was previously dried and then purged with nitrogen after WO 98/22476 PCT/US96/18666 -8assembly. The solvent was added via the other side-neck of the reaction flask, which was then capped with a rubber septum. TiCl 4 (ca. 25 mL, 42-44 g. 0.22-0.23 mol) was transferred from a weighed bottle to the reaction flask using a syringe. The rubber septum was replaced with a dried, nitrogen-purged addition funnel. The THF and/or the organometallic compound was transferred to the addition funnel and then added to the TiCl 4 /solvent reaction mixture at the desired temperature.

EXAMPLE 1 A solution of n-butyllithium (BuLi) in hexanes (156 mL of a 1.60 M solution, 0.250 mol of BuLi) was added to TiC1 4 (43.0 g, 0.227 mol) in 300 mL of toluene over min. The initial temperature of the reaction mixture was 10°C, the temperature increased to 40*C during the addition, and was then maintained at 35-40 0 C using external cooling. After the addition of the BuLi, the reaction mixture was stirred at 35-40*C for 1 hour.

After cooling to room temperature, the addition funnel, condenser, and Claisen adapter were removed while maintaining an inert atmosphere of nitrogen over the TiC1 3 product mixture. The resulting TiCl 3 containing mixture was used directly in reactions with deprotonated metallocene ligands.

EXAMPLE 2 THF (100 mL) was added to a solution of TiC14 (43.4 g, 0.229 mol) in 200 mL of toluene over 30 minutes at 0-15°C. Then BuLi in hexanes (156 mL of a 1.60 M solution, 0.250.mol) was added over 40 min at 5-10*C.

The resulting mixture was heated to 35-40*C and stirred for 1 hour. After cooling, the resulting TiC1 3 slurry was used directly in reactions with deprotonated ligands.

EXAMPLE 3 THF (75 mL) was added to a solution of TiC1 4 (42.0 g, 0.221 mol) in 150 mL of toluene over 20 min at 0-15"C.

WO 98/22476 PCT/US96/18666 -9- Then a solution of butylmagnesium chloride (BuMgCl) in THF (115 mL of a 2.10M solution, 0.242 mol of BuMgCl) was added over 30 min. The initial temperature of the reaction mixture was 0°C; the temperature increased to 40°C during the addition and was then maintained at 35-40°C using external cooling. After the BuMgCl addition, the reaction mixture was stirred for 1 hour at 35-40*C. The resulting TiC13 product slurry was used directly in reactions with deprotonated ligands.

EXAMPLE 4 The Deprotonation of CpSA Ligand With i-Propylmagnesium Chloride The reaction apparatus consisted of a 2000-mL 3-neck flask equipped with a mechanical stirrer; on one sideneck was placed a Claisen adapter with a Vigereaux column and distillation head for solvent distillation. A thermometer was inserted into the reaction flask through the Claisen adapter. The glass apparatus was previously dried and purged with nitrogen after assembly. Toluene (425 mL) and CpSA ligand (55.0 g, 0.219 mol) were added to the reaction flask. The temperature of the reaction mixture was adjusted to 45-50"C. A solution of ipropylmagnesium chloride (i-PrMgC1) in ether (205 mL of a 2.30 M solution, 0.472 mol of i-PrMgCl) was added over 1 hour using an addition funnel. After the i-PrMgCl addition, the reaction mixture was gradually heated to 85-90°C over 2 hours and stirred at this temperature for an additional 2 hours. The (CpSA)2-(MgCl) 2 formed a gummy solid at this stage. The heating is removed and the temperature of the reaction mixture cooled to 60-65"C. At this temperature, THF (150 mL) was added dropwise over 15 min, which dissolved the solid (CpSA) 2 (MgCl) 2 The reaction mixture is then cooled to room temperature. The distillation head, Vigereaux column, and addition funnel are then removed from the reaction WO 98/22476 PCT/US96/18666 apparatus while maintaining an inert atmosphere of nitrogen over the product mixture. This (CpSA) 2 (MgCl) 2 solution was then used directly in a reaction with a TiCl 3 slurry prepared previously.

EXAMPLE The Deprotonation of CpSA Ligand with n-Butyllithium The reaction apparatus consisted of a 2000-mL 3-neck flask equipped with a mechanical stirrer; on one sideneck was placed a Claisen adapter with a reflux condenser and a thermometer inserted into the reaction flask. The glass apparatus was previously dried and purged with nitrogen after assembly. Ether (300 mL) and CpSA ligand (62.9 g, 0.250 mol) were added to the reaction flask.

The reaction mixture was cooled to -200C. A solution of BuLi in hexanes (305 mL of a 0.170 M solution, 0.518 mol of BuLi) was added over 1.5 hours; the temperature was maintained at -20 to -15*C during this addition. The reaction mixture was then warmed to 0-5°C over 1.5 hours and stirred at this temperature for 3 hours. The resulting (CpSA) 2 'Li 2 slurry, which consisted of a white solid with a pale yellow supernatant, was used directly in a reaction with a TiCl 3 slurry prepared as described in Examples 1 to 3.

EXAMPLE 6 The Preparation of (CpSA) 2 -TiC1 2 The TiC13 containing mixture from Example 1 above was transferred under nitrogen pressure via a wide-bore cannula to the (CpSA) 2 '(MgCl) 2 solution from Example 4 above over 2-3 min. Toluene (100 mL) was added to the TiCl 3 flask which contained some residual TiCl 3 and this wash was quickly transferred to the reaction flask. The initial temperature of the reaction mixture was 22*C; the temperature increased to 35*C during the TiCl 3 addition.

The reaction mixture was stirred for 15 min at 35°C, at WO 98/22476 PCT/US96/18666 -11which time dichloromethane (13.5 g) was added over 1 min; the temperature increased to 38*C. The resulting redbrown mixture was stirred for 2 hours with gradual cooling to 25°C. Solvents were removed by simple distillation under reduced pressure (60-80 mm Hg) to a final volume of ca. 600 mL; the temperature ranged from 30 to 60°C during this distillation. After cooling to 20'C and pressurizing with nitrogen, toluene (400 mL) was added to the product mixture. Magnesium salts were removed from this mixture by pressure filtration under nitrogen using Celite® filter-aid. The reaction flask and filter cake were washed with two 200-mL portions of fresh toluene. The red-brown filtrate was concentrated by simple distillation under reduced pressure as before to a volume of 400 mL. This toluene solution is again filtered under nitrogen pressure to remove residual magnesium salts. The filtrate is concentrated again to a volume of 200 mL by simple distillation under reduced pressure. Heptanes (400 mL) were added over 30 min with stirring at 20-25 0 C. A first crop of orange, crystalline (CpSA) 2 TiCl2 is collected by filtration under nitrogen, washing with heptanes, to give 61.1 g of product in 76% yield. A second crop was obtained by concentration of the mother liquors to ca. 100 mL and dilution with heptanes.

Alternatively, the product solution in toluene obtained after removal of the magnesium salts was used directly to prepare other metallocenes. For example, the toluene solution of (CpSA) 2 TiCl 2 was treated with 2 equivalents of methylmagnesium chloride (THF solution) to give (CpSA) 2 Ti(CH 3 2 in 70-75% overall yield.

Claims

1. In a process for producing a titanocene wherein a titanium trichloride reagent is reacted with a titanocene ligand, the improvement which comprises: utilizing as said titanium trichloride reagent a mixture produced by reacting titanium tetrachloride with a compound having the formula R-M, in which R is a straight or branched chain alkyl group having 2 to 8 carbon atoms and M is an alkali metal, or the formula RMgX, in which X is a halogen in substantially stoichiometric amount in a non-interfering solvent wherein a reaction mixture containing titanium trichloride, said solvent and a MC1 or MgCl 2 is produced; and (ii) reacting said step reaction mixture directly with said titanocene ligand to produce a titanocene.

2. The process of claim 1 in which said titanium trichloride and said ligand are reacted at a temperature in the range of -20 to 120*C.

3. The process of claim 1 in which said compound RM is added to titanium tetrachloride at an initial temperature range of 10-20 0 C, after which the reaction mixture is heated to 34-40°C for about one hour.

4. The process of claim 1 in which said non- interfering solvent is a hydrocarbon.

The process of claim 1 in which said non- interfering solve is a hexane, a heptane, benzene, toluene, a xylene, or a mixture thereof.

6. The process of claim 1 in which the ether solvent is a cyclic or cyclic ethers or a polyether.

7. The process of claim 1 in which an non- interfering solvent is an ether. WO 98/22476 PCT/US96/18666 -13-

8. The process of claim 1 in which the non- interfering solvent is dimethyl ether, diethyl ether or dibutyl ether.

9. In a process for producing a titanocene wherein a titanium trichloride reagent is reacted with a titanocene ligand, the improvement which comprises: utilizing as said titanium trichloride reactant a mixture produced by reacting titanium tetrachloride with a compound having the formula R-M, in which R is a straight or branched chain alkyl group having 2 to 8 carbon atoms and M is an alkali metal, or the formula RMgX, in which X is a halogen in substantially stoichiometric amount in a non-interfering liquid medium wherein a reaction mixture containing titanium trichloride, said solvent and MC1 or MgC12 is produced; (ii) reacting said step reaction mixture with a deprotonated titanocene ligand to produce a second reaction mixture including said liquid medium, and a titanocene corresponding to said titanocene ligand; and (iii) optionally isolating said titanocene of step (ii) from said step (ii) second reaction mixture.

In a process for producing a titanocene wherein a titanium trichloride reactant is reacted with titanocene ligand, the improvement which comprises: utilizing as said titanium trichloride reactant a mixture produced by reacting titanium tetrachloride with a compound having the formula R-M, in which R is a straight or branched chain alkyl group having 2 to carbon atoms and M is an alkali metal, or the formula RMgX, in which X is a halogen in substantially stoichiometric amount in a non-interfering solvent wherein a reaction mixture containing titanium trichloride, said solvent and MC1 or MgCl 2 is produced; (ii) reacting said step mixture with a deprotonated titanocene ligand to produce a reaction WO 98/22476 PCT/US96/18666 -14- mixture including said solvent, and a titanocene corresponding to said titanocene ligand and MC1 or MgClz; (iii) separating said MCI or MgCl 2 from said step (ii) reaction mixture; and thereafter (iv) utilizing said step (ii) reaction mixture to prepare another titanocene.

11. A method for producing a constrained geometry titanocene catalyst which comprises: reacting n-butyl lithium or isobutyl lithium with titanium tetrachloride in substantially stoichiometric amount in a non-interfering hydrocarbon medium to produce a first reaction mixture containing titanium trichloride and lithium chloride; and (ii) combining said first reaction mixture with a titanocene ligand in a non-interfering medium for reaction to produce a titanocene corresponding to said ligand.

12. The claim 11 method in which said titanocene corresponding to said ligand produced in step (ii) is (CpSA)2-TiCl 2 ([(t-butylamido) (tetramethylcyclo- pentadienyl)dimethylsilane]titanium dichloride).