AU7170400A - Tricot nonwoven fabric - Google Patents

Description

-1-

AUSTRALIA

PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT

ORIGINAL

Name of Applicant/s: Actual Inventor/s: Address for Service: McNeil-PPC, Inc.

Susan Lynn Suehr and William F. Kelly and Charles Shimalla and Frank H. Flesch and James E. Knox BALDWIN SHELSTON WATERS MARGARET STREET SYDNEY NSW 2000 'TRICOT NONWOVEN FABRIC' Invention Title: Details of Original Application No. 69919/98 dated 04 June 1998 The following statement is a full description of this invention, including the best method of performing it known to me/us:- File: 30105AUP00 -2- TRICOT NONWOVEN FABRIC Background of the Invention Nonwoven fabrics have been known for many years. Many nonwoven fabrics are produced by forming a web or batt of textile like fibers and treating the fiber batt with binder to hold fibers together and provide some strength to the batt. In other instances a nonwoven fabric may be produced by treating a fiber batt with water streams to cause the fibers to entangle with each other and provide some strength in the batt. Many methods have been developed for treating fiber batts in such a manner in an attempt to duplicate the physical properties and appearance of woven fabrics. While the methods developed for producing non-woven fabrics have produced fabrics with some of the characteristics of woven or knitted fabrics, one property, namely drapability, has been difficult to achieve. None of the nonwoven fabrics produced to date have had the appearance, drapability or flexibility of tricot knit fabrics.

"It is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative.

Summary of the Present Invention According to a first aspect the present invention consists in a nonwoven fabric comprising a plurality of intertwined and interentangled fibers defining a predetermined pattern of openings in said fabric, said fabric having a drape index in all directions of the fabric of at least 75 degrees.

According to a second aspect the invention provides a nonwoven fabric formed on a topographically configured support member having a plurality of raised, threedimensional areas and a plurality of holes between said three-dimensional areas and 2a extending through said support member, said fabric having an upper surface facing away from said support member when said fabric is formed and a lower surface supported on the top of said three-dimensional areas when said fabric is formed, said fabric comprising a plurality of fibers disposed between said surfaces, said fibers being rearranged by the application of fluid under pressure to the fabric upper surface and said fibers being intertwined and interentangled with adjacent fibers to define a pattern of openings extending through said fabric, a portion of said openings having substantially parallel fiber segments disposed therein and arranged generally transversely of the thickness of said fabric.

Unless the context clearly requires otherwise, throughout the description and the claims, the words 'comprise', 'comprising', and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense; that is to say, in the sense f'd.m of "including, but not limited to".

V. V 9 V 9 V 2b Brief Description of the Drawings A preferred embodiment of the invention will now be described, by way of example only, with reference to the accompanying drawings in which: Figure 1 is a photomicrograph of a nonwoven fabric of the present invention enlarged about 20 times, as seen from the upper surface; Figure 2 is a photomicrograph of a nonwoven fabric of the present invention enlarged about 20 times, as seen from the bottom surface; Figure 3 is a schematic sectional view of one type of apparatus for producing the nonwoven fabrics of the present invention; Figure 4 is a diagrammatic view of another type of apparatus for producing nonwoven fabrics of the present invention; and Figure 5 is a perspective view of one type of topographical support member that may be used in the apparatus depicted in Figure 4.

Oo:: 0.0* o /p O O ,,0O ooe, 3 Detailed Description of the Invention Referring to the drawings, Figure 1 is a photomicrograph of a nonwoven fabric of the present invention at an enlargement of approximately 20 times. The fabric 10 is made from a plurality of fibers. As seen in the photomicrograph, the fibers are intertwined and interentangled and form a pattern of openings 11 in the fabric. A number of these openings include a loop 12 formed from fiber segments. Each loop is made from a plurality of substantially parallel fiber segments. The loop is in the shape of a U with the closed end of the U pointed upwardly towards the upper surface of the fabric as viewed in the photomicrograph. Figure 2 is a photomicrograph of the opposite surface of the fabric of Figure 1 at an enlargement of about 20 times. The fibers in the fabric are intertwined and entangled to form a pattern of openings 11 in the fabric. In some of these openings there are U-shaped loops 12 formed from substantially parallel fiber segments. When viewed from this bottom surface of the fabric, the open end of the Ushaped loop is pointed towards the surface of the fabric viewed in this photomicrograph.

Figure 3 is a schematic cross-sectional view of apparatus which may be used to produce fabrics of the present invention. The apparatus includes a movable conveyer belt 55. Placed on top of this belt to move with the belt is a topographically configured support member 56. The support member has a plurality of raised three- 30 dimensional areas. Holes or openings extending through the support member are disposed between these three dimensional areas as will be more fully discussed in conjunction with Figure 5. The fiber web 57 to be treated is disposed or supported at the top of the three -4dimensional areas. The web may be a web of carded fibers, air laid fibers, melt blown fibers or the like. Above the fiber web is a manifold 58 for applying fluid 59, preferably water, through the fibrous web as the fibrous web is supported on the support member and moved on the conveyer belt beneath the manifold. The water may be applied at varying pressures. Disposed beneath the conveyer belt is a vacuum manifold 60 for removing water from the area as the web and support member are passed under the fluid manifold. In operation, the fiber web is placed on the support member and the fiber web and support member passed under the fluid manifold. Water is applied to the fibers to wet out the fiber web, as to be certain the web is not moved or disrupted from its position on the support member upon further treatment. Thereafter, the support member and web are passed beneath the manifold a series of times. During these passes, the pressure of the water of the manifold is increased from a starting pressure of about 100 psi to pressures of 1000 psi or more. The manifold consists of a plurality of orifices of from about 4 to 100 or more holes per inch. Preferably, the number of the holes in the manifold is 13 to 70 per inch. The holes may have a diameter of from 3/1000 of an inch to 10/1000 of an inch.

~In Figure 4, there is depicted an apparatus for continuously producing fabrics in accordance with the present invention. The schematic representation includes a conveyer belt 80 which serves as a support member in accordance with the present invention. The belt is *continuously moved in a counter-clockwise direction about spaced apart members as is well known in the art.

Disposed above this belt is a fluid feeding manifold 79 connecting a plurality of lines or groups of orifices 81.

5 Each group has one or more rows of fine diameter holes with 30 or more holes per inch. The manifold is equipped with pressure gauges 88 and control valves 87 for regulating fluid pressure in each line or group of orifices. Disposed beneath each orifice line or group is a suction member 82 for removing excess water and to keep the water from causing undue flooding. The fiber web 83 to be treated and formed into a fabric according to the present invention is fed to the support member conveyer belt. Water is sprayed through an appropriate nozzle 84 onto the fibrous web to prewet the web and aid in controlling the fibers as they pass under the pressure manifolds. A suction box 85 is placed beneath the water nozzle to remove excess water. The fibrous web passes under the fluid feeding manifold with the manifold preferably having progressively increasing pressures. For example, the first line of holes or orifices may supply fluid forces at 100 psi while the next line of orifices may supply fluid forces at a pressure of 300 psi and the last line of orifices may supply fluid forces at a pressure of 700 psi. Though 6 lines of orifices are shown, the number of lines or rows of orifices is not critical, but will depend on the width of the web, the speed, the pressure used, the number of rows and holes in 25 each line, etc. After passing between the fluid feeding and the suction manifolds, the formed fabric is passed over an additional suction box 86 to remove excess water Sfrom the web. The support member may be made from relatively rigid material and may comprise a plurality of slats. Each slat extends across the width of the conveyer and has a lip on one side and a shoulder on the opposite side so that the shoulder of one slot engages with the lip of an adjacent slot to allow for movement between adjacent slots and allow for these relatively rigid members to be 6 used in the conveyer configuration shown in Figure 4.

Each orifice strip comprises one or more rows of very fine diameter holes of approximately 7/1000 of an inch. There are approximately 50 holes per inch across the orifice strip.

Figure 5 is a perspective view of one type of support member that may be used to produce the fabrics of the present invention. The member comprises a plate 90 having a plurality of openings 91 extending through the thickness of the plate. The openings are aligned in rows extending the length and width of the plate. The top portion of each opening has a conical shape 92. The conical shape surfaces are relatively smooth with varying undulations as seen in the Figure. The surface formed from the conical shapes is the surface on which the fiber web is placed and treated in accordance with the present invention.

Following is a specific example of a method for producing the fabrics of the present invention.

EXAMPLE

SIn this Example, the starting web used to make a fabric according to the present invention comprises 100% cotton fibers. The web weighs 2.5 ounces per square yard and comprises a 1.5 ounce per sq. yd. randomized web laminated on top of a 1.0 ounces per sq. yd. carded web.

The web is prebonded by placing it on a 100 X 92 mesh bronze belt and passing the web and belt under columnar water jet streams. The jet streams are produced from 0.007 inch diameter orifices arranged in a row running in the transverse direction or the width of the web. There are 30 orifices per inch. The web is passed under the columnar jet streams at a speed of 92 ft/min. Three 7 passes are made at 100 psig and 9 passes at 900 psig. The web to orifice spacing is 0.75 inch. The pretreated web is removed from the belt surface, turned over and placed on a forming plate as depicted in Figure 5. The forming plate and web are passed under columnar water jet streams as described above. The plate and web are passed under the jet streams at 90 ft/min. One pass is made at 600 psig and 7 passes at 1400 psig. The resulting fabric is dried on drying cans to remove the water. As previously mentioned, the fabrics of the present invention have excellent drapability in all directions of the fabric. While drapability may be measured by various techniques, the drapability of the fabrics of the present invention are measured by taking a 12 inch X 12 inch square of the fabric and conditioning it for at least 6 hours in a room at a temperature of 70°F. and a relative humidity of 65 percent. The conditioned fabric is placed S" on a flat, horizontal surface and one edge of the fabric o 20 moved over the edge of the surface so that 6 inches of the fabric extends beyond the surface edge and is unsupported by the surface. The angle the fabric deflects from the 0" horizontal surface is measured. This angle is called the drape index of the fabric. The fabrics are tested in the i 25 machine direction, the cross direction and at 45 degrees and 135 degrees from the machine direction.

A comparison of the drapability of the fabrics of the present invention with prior art nonvoven fabrics is made.

The fabric of the present invention made as described in the previous Examples is processed through a binder pad operation and impregnated with 20% acrylic binder pickup and dried on drying cans.

8 One of the comparative prior art samples is made using the same base web of 2 1/2 ounces per square yard, the web is treated and formed into a nonwoven fabric as described in U.S. Patent 3,485,706. Another comparative sample is made using the 2 1/2 ounces per square yard base web. The web is treated and formed into a- fabric as described in U.S. Patent 5,098,764. The fabric of the invention described above and the fabrics made' as described in U.S. Patent 3,486,168 and U.S. Patent 5,098,764 are passed through a jet dyeing process to enhance properties. The process used is a standard dyeing process used on many apparel and home finishing fabrics to soften the fabric and provide uniform color distribution.

Such finishing processes are standard in the textile industry and are used with many woven, knit and nonwoven fabrics. The other fabric compared is a commercial entangled nonwoven fabric sold by DuPont under the trademark Sontara. This fabric is made from polyester and pulp fibers which are not as stiff as cotton fibers. The fabric is commercially finished to enhance softness and drapability. Cotton is used in the comparison since it has poor drapability as a result of the stiffness properties of cotton. The drape index of each of the three fabrics is determined by the drapability test previously described. Each of the samples is tested in the machine direction, the cross-direction, and at 45 and 135 degrees to the machine direction. The samples had the •BO following drape indices: *.i *oo *o 9 Oe Drape Fabric of U.S. U.S. Sontara Index Present Patent Patent Invention 3,485,706 5,098,764 Machine 800 65* 750 72° Direction Cross 87* 850 85" 840 Direction 450 81° 630 77° 66° 1350 800 63° 710 66° As may be seen from the above table, the fabrics of the present invention have a drapability index of at least 15 75 degrees and preferably 80 degrees or more in all directions of the fabric. Preferably, the drapability of the fabrics of the present invention, in the machine direction, is at least 80 degrees and in the crossdirection is at least 85 degrees.

Having now described the invention in specific detail and exemplified the manner in which it may be carried into practice, it will be readily apparent to those skilled in the art that many variations, applications, modifications, and extensions of the basic principles involved may be made without departing from its spirit or scope.

Claims (4)

1. A nonwoven fabric comprising a plurality of intertwined and interentangled fibers defining a predetermined patter of openings in said fabric, said fabric having a drape index in all directions of the fabric of at least 75 degrees.

2. A nonwoven fabric according to claim 1, having a drape index in all directions of the fabric of at least 80 degrees.

3. A nonwoven fabric according to claim 1, having a drape index in the machine direction of the fabric of at least 80 degrees and a drape index in the cross-section of the fabric of at least 85 degrees.

4. A nonwoven fabric formed on a topographically configured support member having a plurality of raised, three-dimensional areas and a plurality of holes between said three-dimensional areas and extending through said support member, said fabric having an upper surface facing away from said support member when said fabric is formed and a lower surface supported on the top of said three-dimensional areas when said fabric is oo 3 S15 formed, said fabric comprising a plurality of fibers disposed between said surfaces, said .o.o fibers being rearranged by the application of fluid under pressure to the fabric upper surface and said fibers being intertwined and interentangled with adjacent fibers to define a pattern of openings through said fabric, a portion of said openings having substantially parallel fiber segments disposed therein and arranged generally transversely 20 of the thickness of said fabric. o :S :DATED this 20th Day of November, 2000 MCNEIL-PPC, INC. Attorney: CHARLES W. TANSEY Registered Patent Attorney of The Institute of Patent and Trade Mark Attorneys of Australia of BALDWIN SHELSTON WATERS