WO 98/47615 PCT/US98/07095 1 NAPHTHA REFORMING CATALYST AND PROCESS BACKGROUND OF THE INVENTION 5 Field of the Invention The invention relates to zeolite L-based reforming catalysts and their use to produce reformate having a lower content of C9 and C 1 0 aromatic compounds. 10 Description of Related Art Catalytic reforming is a major petroleum refining process used to raise the octane rating of naphthas (C 6 to C 11 hydrocarbons) for gasoline blending. 15 Catalytic reforming is also a principal source of aromatic chemicals, i.e., benzene, toluene and xylenes, via conversion of paraffins and naphthenes to aromatics. The principal reforming chemical reactions are dehydrogenation of 20 cyclohexane to aromatics, dehydrocyclization of paraffins to aromatics, dehydroisomerization of alkylcyclopentanes to aromatics, isomerization of normal paraffins to branched paraffins, dealkylation of alkylbenzenes, and hydrocracking of paraffins to light hydrocarbons. The hydrocracking of paraffins to light hydrocarbons is undesirable and should be minimized 25 because light hydrocarbons have low value. Catalysts commonly used in commercial reformers include a Group VIII metal, such as platinum, or platinum plus a second catalytic metal, such as rhenium or iridium, dispersed on an alumina substrate. Typically, 30 chlorine is incorporated on the alumina to add acid functionality. Alumina based reforming catalysts are suitable for aromatizing C3' paraffins, but WO 98/47615 PCT/US98/07095 2 are less effective for aromatizing C6 to C8 paraffins because these catalysts hydrocrack more of the lighter paraffins to low value fuel gas than they convert to aromatics. 5 Conventional reforming catalysts are bifunctional, i.e., the catalysts enhance i) dehydrogenation and cyclization reactions on the catalytic metal sites; and ii) isomerization on separate strong acid sites in the catalyst. The undesirable hydrocracking reactions also occur on the acid sites. 10 Within the past few years reforming catalysts have been developed which have been discovered to be particularly effective for aromatizing the C6 to C8 paraffin components of naphtha. These catalysts are made using zeolite, rather than alumina, as the support for the catalytic metal. They 15 are mono-functional and contain relatively few strong acid sites. Unlike conventional bifunctional catalysts, zeolite based catalysts accomplish dehydrogenation and cyclization reactions as well as isomerization on the dispersed metallic catalytic sites. Because these zeolite-based catalysts have few strong acid sites, undesirable hydrocracking reactions are 20 repressed. Zeolites which are preferred for reforming catalysts are large pore zeolites i.e., zeolites with a 6 to 15 Angstrom pore diameter. Zeolite L is the most preferred support for reforming catalysts, particularly wherein the catalytically active metal is platinum. Examples of such catalysts are disclosed in U.S. Patents 4,104,320 and 4,544,539. 25 Modified versions of these Group VIII metal-containing catalysts which also contain an ion-exchanged alkaline earth metal such as calcium, barium or strontium are disclosed in U.S. Patent 4,435,283. This catalyst is disclosed to have a higher selectivity with respect to the 30 dehydrocyclization of alkanes such as n-hexane into aromatics.

WO 98/47615 PCT/US98/07095 3 More recently, zeolite L crystallites having a cylindrical structure and shorter channel length have been developed which provide for improved run lengths, conversion and selectivity towards aromatics production 5 when used as a catalyst support in a reforming process. These crystallites may be characterized as "coin" or "hockeypuck" shaped and have a relatively large diameter and short length. The "length" of a crystal is a measurement of the outer edge of the crystal perpendicular to the basal plane containing the diameter. The length is typically 0.1 to 0.6, 10 preferably 0.1 to 0.3 microns and the diameter is generally 0.3 to 1.5 microns, preferably 0.4 to less than 1.0 micron. When the length/diameter ratio is 0.2 to 0.5, the crystal shape is termed "hockeypuck". When this ratio is less than 0.2, the shape is termed "coin". 15 These new zeolites are synthesized by hydrothermal treatment of a synthesis mixture containing water, a source of potassium, a source of Al 2 03, a source of SiO 2 and up to about 0.1 wt.%, based on the synthesis mixture, of a source of a divalent cation selected from the group consisting of magnesium, calcium, barium, manganese, chromium, cobalt, 20 nickel and zinc. The divalent cation present in the synthesis mixture serves to reduce the size and regulate the shape of the resulting zeolite L crystallites and also suppresses the formation of unwanted impurities such as zeolite W. 25 These zeolites and platinum-loaded versions thereof used as reforming catalysts are disclosed in U.S. Patents 5,486,498 and 5,491,119, the complete disclosures of which patents are incorporated herein by reference. 30 One of the primary goals in a naphtha reforming process is to achieve a reformate which contains a high content of aromatics because these WO 98/47615 PCT/US98/07095 4 chemicals are more valuable and contribute to higher octane values where the reformate is used in the gasoline product pool. Present requirements of the U.S. Clean Air Act and the physical and compositional limitations imposed by the Reformulated Gasoline (RFG) and U.S. EPA 5 Complex Model regulations will result in limitations on gasoline boiling range, typically measured by minimum Reid Vapor Pressure (RVP) and T90 specification. What this means is that reformates containing a higher content of lighter aromatics, e.g., benzene, toluene and xylene (BTX) are more valuable for use in reformulated gasoline than reformates wherein 10 the aromatics content also includes significant amounts of heavier C 9 and

C

10 aromatics. Accordingly, it is an object of the invention to provide a fresh or regenerated Group VIII metal-containing zeolite L catalysts which is highly 15 selective to the production of aromatics containing lesser amounts of C 9 and C 10 aromatics. Another object of the invention is to provide a process for reforming naphtha streams using this catalyst, as well as activated and regenerated 20 versions thereof. Still another object of the invention is to provide a process for further activating or regenerating this catalyst. 25 SUMMARY OF THE INVENTION The invention provides a crystalline type L zeolite catalyst in which the crystals are cylindrical and have an average length of 0.6 microns or less and an average length: diameter ratio of less than about 0.5, said catalyst 30 containing at least one catalytically active Group VIII metal of the Periodic Table and from about 0.1 to 2 wt.% of halogen.

WO 98/47615 PCT/US98/07095 5 The invention also provides a process for reforming a C6 to C11 naphtha stream containing at least about 25 wt.% of C6 to C9 aliphatic and cycloaliphatic hydrocarbon comprising contacting said stream under 5 reforming conditions with a type L zeolite catalyst in which the crystals are cylindrical and have an average length of 0.6 micron or less and an average length: diameter ratio of less than about 0.5, said catalyst containing at least one catalytically active Group VIII metal of the Periodic Table and from about 0.1 to 2 wt.% of halogen, and recovering a 10 reformate wherein less than about 20 wt.% of the aromatics content of said reformate comprises aromatics containing nine or more carbon atoms. The invention further provides a process for enhancing the catalytic 15 activity of a crystalline type L zeolite catalyst in which the crystals are cylindrical and have an average length of 0.6 microns or less and an average length: diameter ratio of less than about 0.5, said catalyst containing at least one catalytically active Group VIII metal of the Periodic Table and from about 0.1 to 2 wt.% of halogen, said processing 20 comprising: a) contacting said catalyst with a gaseous stream comprising water, a source of chlorine, oxygen and an inert gas under oxychlorination conditions comprising a temperature of from about 4500C to 5500C and a partial pressure of chlorine derived from the source of chlorine which is greater than about 0.03 psia (206.8 Paa) for a time sufficient to form 25 oxyhalides of said metal; b) contacting the chlorinated catalyst with a gaseous stream containing water, oxygen and an inert gas under chlorine removal conditions comprising a temperature of about 4500 to 5500C and for a time effective to lower the chlorine content of the catalyst to about 2 wt.% or less; and c) contacting the catalyst of reduced chlorine content 30 with a gaseous stream containing an inert gas and hydrogen under reducing conditions including a temperature in the range of about 350°C WO 98/47615 PCT/US98/07095 6 to 5500C for a time effective to reduce metal in the catalyst to the metallic state. The catalysts of this invention are selective towards the production of 5 reformates having a high content of light C6 to C8 aromatics while at the same time producing less of the heavier C 9 and Clo0 aromatics. BRIEF DESCRIPTION OF THE DRAWINGS o10 Figure 1 is a graph plotting the % conversion of naphtha feed vs. reforming time for a catalyst of the invention and a conventional reforming catalyst. Figure 2 is a graph plotting the yield of C6 to C9 aromatics vs. reforming 15 time for a catalyst of this invention and a conventional reforming catalyst. DETAILED DESCRIPTION OF THE INVENTION Zeolite L aluminosilicates which are useful as support material for the 20 catalysts of the present invention are the small particle size cylindrically shaped crystallites such as disclosed in the above referenced U.S. patents 5,486,498 and 5,491,119. They are generally prepared by the hydrothermal treatment of a synthesis mixture containing water, a source of potassium, a source of A1 2 0 3 , a source of SiO 2 and up to about 0.1 25 wt.%, based on the weight of the synthesis mixture, of a source of divalent cation (M") selected from the group consisting of magnesium, calcium, barium, manganese, chromium, cobalt, nickel and zinc. Preferred synthesis mixtures generally have a composition falling within 30 the following molar ratios (expressed as oxides): WO 98/47615 PCT/US98/07095 7

(M'

2 0 + M" 2 /n O)/SiO 2 = 0.18 - 0.36

H

2 0/(M' 2 0 + M" 2 /n O) = 25 - 90 SiO 2

/AI

2 0 3 = 5 - 15 5 M' 2 0/(M' 2 0 + M" 2/n O) = 0.9 - 0.9999 wherein M' is an alkali metal, preferably potassium or a mixture of potassium and sodium, M" is one or a mixture of the divalent metals described above, and n is the valence of M". The Zeolite L of the 10 invention is prepared by hydrothermal heating of the synthesis mixture at a temperature of about 150 0 C to 250 0 C for a period of from about 10 to 150 hours, followed by recovery, drying and optional calcining of the resulting crystalline zeolite L product. 15 These zeolite L products are characterized by a cylindrical shape having relatively flat basal planes and relatively short channels within the zeolite crystalline structure. The length of the crystallite walls is generally in the range of from about 0.1 to 0.6 microns, more preferably from about 0.1 to 0.3 microns and the diameter is generally from about 0.3 to 1.5 microns, 20 more preferably from about 0.4 to less than 1.0 micron. The average length: diameter ratio of these crystallites may generally range from about 0.05 to about 0.5, more preferably from about 0.1 to about 0.4. The zeolite L is made catalytically active by incorporating catalytic 25 quantities of at least one Group VIII metal and halogen into the channel structure of the zeolite L. The Group VIII noble metals which are necessary for catalytic activity are those metals from Group VIII of the Periodic Table of Elements which are 30 selected from osmium, ruthenium, rhodium, indium, palladium and platinum. Preferably, the metals which are employed herein are platinum, WO 98/47615 PCT/US98/07095 8 rhodium or iridium, and most preferably platinum. The metals may be present in any combination desired. Rhenium, a Group VIIB metal, may also be present so long as at least one Group VIII noble metal is present. 5 The amount of Group VIII noble metal present in the catalyst will be an effective amount and will depend, for example, on required catalyst activity, ease of uniform dispersion, and the crystal size of the type L zeolite. Crystal size limits the effective catalyst loading since highly loaded crystals of zeolite which have a large dimension parallel to the 10 channels could be easily lead to pore plugging during operation as the noble metal agglomerates inside the channels. Generally, however, the level of metal present will range from about 0.1 to 6%, preferably 0.1 to 3.5% and more preferably 0.1 to 2.5% by weight of the catalyst. Furthermore, the amount of metal present is generally from about 0.1 to 15 2.0% by weight of the catalyst if the average zeolite crystallite size parallel to the channels is greater than about 0.2 micron, and from about 1.0 to 6% by weight if the average zeolite crystallite size parallel to the channels is no greater than about 0.2 micron. 20 The Group VIII noble metals may be introduced into the zeolite by, for example, ion exchange, impregnation, carbonyl decomposition, adsorption from the gaseous phase, introduction during zeolite synthesis, and adsorption of metal vapor. The preferably technique is ion exchange or impregnation by the so-called incipient witness method. 25 Halogen may be incorporated into the catalyst by combining it with a source of halogen such as alkali or alkaline earth chlorides, fluorides, iodides or bromides. Other halogen sources include compounds such as hydrogen halide, e.g., hydrogen chloride, and ammonium halides, e.g., 30 ammonium chloride. The preferred halogen source is a source of chlorine. The amount of halogen source combined with the catalyst WO 98/47615 PCT/US98/07095 9 should be such that the catalyst contains from about 0.1 to 2 wt.% halogen, more preferably from about 0.2 to about 1.5 wt.% halogen. The catalyst can be combined with the halogen source at the same time as the Group VIII metal source and using similar methods as described above. 5 In a preferred embodiment, the zeolite L is combined with an inorganic binder material which serves as a matrix which holds the crystals together. Suitable binder materials include silica, alumina, silica-alumina and various clays. Molded prills or extrudates may be formed by mixing the 10 zeolite L crystallites with water and the binder material to form a paste, shaping the paste to form molded prills or particulate extrudates and drying the resulting product. Preferably the binder is added at a level such that the bound catalyst 15 contains from about 10 to 50 wt.% binder. Also, the catalyst metal and halide compound may be incorporated into the zeolite either before or after the zeolite is composited with the binder. The resulting zeolite L is preferably calcined after drying under conditions 20 which tend to minimize the agglomeration of the metal component present in the catalyst. Calcination is preferably carried out in air at a temperature of 200 0 C to 550 0 C, preferably 260oC-500 0 C for a period of from about 1 to 12 hours. 25 In order to activate freshly prepared catalyst for use in the reforming process, it is preferably subjected to a hydrogen reduction step to reduce the metal cation to the metallic state. Reduction may be carried out by contacting the catalyst with a mixture of hydrogen and an inert gas at temperatures in the order of 350 0 C to 550 0 C for a period of from about 1 30 to 12 hours.

WO 98/47615 PCT/US98/07095 10 Freshly prepared catalyst may also be activated and halogenated by a process which includes the following essential steps: 5 a) contacting said catalyst with a gaseous stream comprising water, a source of chlorine, oxygen and an inert gas under oxychlorination conditions comprising a temperature of from about 4500C to 550°C and a partial pressure of chlorine derived from the source of chlorine which is greater than 10 about 0.03 psia (206.8 Paa) for a time sufficient to form oxyhalides of said metal; b) contacting the chlorinated catalyst with a gaseous stream containing water, oxygen and an inert gas under chlorine 15 removal conditions comprising a temperature of about 4500C to 5500C and for a time effective to lower the chlorine content of the catalyst to about 2 wt.% or less; and c) contacting the catalyst of reduced chlorine content with a 20 gaseous stream containing an inert gas and hydrogen under reducing conditions including a temperature in the range of about 3500C to 5500C for a time effective to reduce metal in the catalyst to the metallic state. 25 The described catalyst may then be used in a reforming or aromatization process. During these reactions, the catalyst gradually loses its effectiveness. The two major reasons are considered to be the production of carbonaceous deposits ("coke") and the agglomeration of the catalytic Group-VIII metal. The process steps outlined below provide a method for 30 removing the coke and redispersing the metal in such a form that the catalyst is again effective.

WO 98/47615 PCT/US98/07095 11 The process steps described below, excepting the then-extraneous coke burn step, may also be used to distribute the Group-VIII metal throughout the zeolite before it is ever contacted with a feedstock. 5 At the beginning of the regeneration procedure, the reactor containing the catalyst may be filled with hydrocarbon feedstock, aromatic products from the dehydrocyclization reaction, and minor amounts of hydrogen and light hydrocarbons. The reactor is under the temperature and pressure 10 conditions employed in the dehydrocyclization procedure. It may be appropriate to purge the catalyst bed with hydrogen or a mixture of hydrogen and light hydrocarbons to remove the feed and product hydrocarbons. After the hydrogen or hydrogen and light hydrocarbon purge, the catalyst bed may then be purged with a dry or wet, substantially 15 inert gas, preferably nitrogen. During one or both of the hydrogen purge and inert gas purge operations, the catalyst may be cooled to an appropriate initiation temperature for the coke burn cycle to follow. This cooling obviously may be accomplished by 20 regulating the temperature of the hydrogen, recycle gas or nitrogen admitted to the catalyst bed. This initiation temperature preferably is less than about 900 0 F (4820C), more preferably less than about 850'F (454-C). 25 The coke burn step is accomplished by contacting the catalyst with a gas stream containing oxygen at a temperature in the range of about 4000C to 6000C for a period of time sufficient to burn coke of the deactivated catalyst and convert the Group VIII metal to agglomerated particles. The preferred initial coke burn temperature is at least about 830'F (443C) 30 and the temperature is gradually increased up to a preferred temperature of about 9250 (4960C) to 975 0 F (524°C). To assure substantially WO 98/47615 PCT/US98/07095 12 complete combustion of the coke on the catalyst and thereby assure that the pores of the final regenerated catalyst will be substantially free of coke - deposits, the catalyst preferably is held at the final coke burn temperature and final coke burn oxygen partial pressure for at least about two hours. 5 The decoked catalyst is then reactivated by subjecting it to activation steps (a), (b) and (c) as described above. In addition, the decoked catalyst may be reduced with hydrogen prior to step (a), in which case the de-coked catalyst is contacted with a gaseous stream containing inert gas 10 and hydrogen under reducing conditions including a temperature in the range of about 3500C to 550°C for a period of time sufficient to reduce the Group VIII metal. The regeneration steps which are used in the process of this invention are 15 generally analogous to those disclosed in U.S. Patent 4,914,068 and WO 94/05419. Naphtha streams which may be reformed in accordance with this invention include light to full range C6-C11 naphtha streams containing at 20 least 25 wt.%, more preferably at least 35 wt.% and most preferably at least 50 wt.% of C6 to C9 aliphatic and cycloaliphatic hydrocarbons and generally less than about 25 wt.%, more preferably less than 20 wt.%, of C9 - C11 aromatic compounds. Reforming is conducted by contacting the naphtha stream in a suitable reactor with activated catalyst at a preferred 25 temperature in the range of 800'F (4270C) to 1000oF (5380C), pressure of about 50 (344.7) to 3,000 psi (20684 kPa), hourly weight space velocities in the range of 0.5 to 3.0 and in the presence of hydrogen at a molar ratio to the feed in the range of 0 to 20, more preferably 1-10 moles of hydrogen per mole of feed naphtha. 30 WO 98/47615 PCT/US98/07095 13 The catalysts of the invention are highly selective towards the production of reformate having a high aromatics content, generally in excess of about 70 wt.% of C 6 to C8 aromatics (BTX). The enhanced BTX yield makes this catalyst particularly attractive for BTX production in chemical recovery 5 processes. Of the total aromatics produced, generally less than about 20 wt.%, more preferably less than 17.5 wt.% and most preferably less than 15 wt.% constitutes heavy aromatics containing nine or more carbon atoms. The 10 reformate is thus more valuable for use in reformulated gasoline where lower contents of C 9 and above aromatics are desired for environmental reasons. The following examples are illustrative of the invention. 15 Example 1 A catalyst of this invention was prepared as follows: Into a circulating solution of 12.8809 g of Pt(NH 3

)

4

CI

2

H

2 0, 19.74 g of 25.27 wt.% KOH 20 solution, 9.09 g of KCI and 1399.0 g of water, there was added 800.0 g of a 1/16" extrudate consisting of a 70 wt.% of small particle KMgL zeolite and a 30 wt.% alumina binder. After 1.5 hr, the loading solution was drained and the wet extrudate was dried at 300oF (149 0 C) for 5 hr and calcined at 662oF (350 0 C) for 2 hr. Elemental analysis of the resultant 25 extrudate gave a 0.846% of Pt and 0.20% of Cl loading on the zeolite L support. Example 2 30 The catalyst of Example 1 was tested and coked in a pilot plant reactor using a 06-07 light naphtha. After about 150 hours on oil, the coked WO 98/47615 PCT/US98/07095 14 catalyst was regenerated by a regeneration procedure involving the following steps: (1) cool down to 833oF (445 0 C) in H 2 , (2) coke burn between 833 (4450C) 5 and 950'F (510 0 C), (3) H 2 reduction at 950 0 F (5100C), (4) wet oxychlorination with HCI and 02 at 950 0 F (5100C), (5) wet air soak at 950oF (5100C), (6) wet N 2 purge at 950OF (5100C), (7) wet H 2 reduction at 950OF (5100C) and (8) dry H 2 cool down and N 2 purge. 10 Example 3 A full range 06-011 naphtha was hydrofined and subsequently treated with massive Ni and 4D sieve for removing sulfur to about 4 ppb sulfur in the feed. G. C. analysis of this treated feed gave the following composition: 15 05 (0.26%), 06 (5.85%), 07 (18.99%), C8 (22.35%), C9 (21.60%), C10 (10.37%), C1i (2.93%), A 6 (0.32%), A 7 (3.13%), A 7 (3.13%), A 8 (5.33%),

A

9 (8.07%) and A 10 (0.80%). Using this liquid feed, two experiments were conducted in the lab units: one with an alumina-bound regenerated 0.85% Pt/KMgL catalyst of Example 2, and the other with a sulfided Pt-Re/Al 2 0 3 20 Cl catalyst (i.e., KX-120 catalyst). Reaction conditions were 860°F (4600C), 1 WHSV (relative to catalyst charge), 100 psig (689.4 kPa), 6

H

2 /feed (mole/mole) and over a period of 165 hr. Table 1 summarizes the experimental results of the time average values. 25 Table 1 Feed A6-A8 Time Avg. Yield of Aromatics Ex Catalyst Cony. Select A 6

A

7

A

8

A

9 Ao 10

C

1

-C

4 2 Pt/MgKL 74.6 76.4 7.0 26.0 24.0 4.2 4.8 10.9 Cont. KX-120 65.7 51.3 3.0 12.9 17.7 6.4 3.0 19.7 WO 98/47615 PCT/US98/07095 15 As can be seen in Figures 1 and 2, the regenerated Pt/KMgL catalyst was more stable than that observed with the KX-120 catalyst in terms of converting the feed and producing A 6

-A

9 aromatics. Also, of the total 5 aromatics produced, only about 13.6 wt.% constituted A 9 and A 10 aromatics using the catalyst of Example 2 whereas about 21.7 wt.% of the aromatics produced using the control catalyst constituted A 9 and A 10 aromatics.

Claims (15)

1. A crystalline type L zeolite catalyst in which the crystals are cylindrical and have an average length of 0.6 microns or less and an average length: diameter ratio of less than about 0.5, said catalyst containing at least one catalytically active Group VIII metal 10 of the Periodic Table and from about 0.1 to 2 wt.% of halogen.

2. The catalyst recited in claim 1 wherein said Group VIII metal comprises platinum. 15

3. The catalyst recited in claim 1 or 2 wherein said Group VIII metal is present in said catalyst at a level of from about 0.1 to 6 wt.%.

4. The catalyst recited in any preceding claim wherein said halogen is chlorine, bromine or fluorine. 20

5. The catalyst recited in claim 4 wherein said halogen is chlorine.

6. The catalyst recited in any preceding claim containing from about 0.2 to 1.5 wt.% halogen. 25

7. The catalyst recited in any preceding claim wherein said crystals are held together with an inorganic binder material selected from the group consisting of silica, alumina, silica-alumina and clay. 30

8. The process recited in claim 7 wherein said binder is alumina. WO 98/47615 PCT/US98/07095 17

9. A process for reforming a C6 to C 11 naphtha stream containing at least about 25 wt.% of C6 to 09 aliphatic and cycloaliphatic hydrocarbons comprising contacting said stream under reforming 5 conditions with a crystalline type L zeolite catalyst according to any of the preceding claims and recovering a reformate wherein less than about 20 wt.% of the aromatics content of said reformate comprises aromatics containing nine or more carbon atoms.

10 10. The process recited in claim 9 wherein less than about 17.5 wt.% of the aromatics content of said reformate comprises aromatics containing nine or more carbon atoms.

11. A process for enhancing the catalytic activity of a crystalline type L 15 zeolite catalyst recited in any of claims 1 to 8, said process comprising: a) contacting said catalyst with a gaseous stream comprising water, a source of chlorine, oxygen and an inert gas under 20 oxychlorination conditions comprising a temperature of from about 4500C to 550'C and a partial pressure of chlorine derived from the source of chlorine which is greater than about 0.03 psia (206.8 Paa) for a time sufficient to form oxychlorides of said metal; 25 b) contacting the chlorinated catalyst with a gaseous stream containing water, oxygen and an inert gas under chlorine removal conditions comprising a temperature of about 4500C to 5500C and for a time effective to lower the chlorine 30 content of the catalyst to about 2 wt.% or less; and WO 98/47615 PCT/US98/07095 18 c) contacting the catalyst of reduced chlorine content with a gaseous stream containing an inert gas and hydrogen under reducing conditions including a temperature in the range of 5 about 350°C to 550 0 C for a time effective to reduce metal in the catalyst to the metallic state.

12. The process recited in claim 11 wherein said catalyst is a coke containing, partially deactivated catalyst and wherein, prior to step 10 (a), a substantial portion of said coke is removed by contacting said catalyst with a gas stream containing oxygen at a temperature in the range of about 400 0 C to 600 0 C for a time sufficient to burn coke off the catalyst. 15

13. The process recited in claim 12 wherein prior to step (a), said de coked catalyst is contacted with a gaseous stream containing inert gas and hydrogen under reducing conditions including a temperature in the range of about 350 0 C to 550 0 C for a time sufficient to reduce said metal. 20

14. An activated catalyst produced by the process recited in any of claims 11 to 13.

15. A process for reforming a C 6 to C11 naphtha stream containing at 25 least about 25 wt.% of C 6 to C9 aliphatic and cycloaliphatic hydrocarbons comprising contacting said stream under reforming conditions with a catalyst recited in any of claims 11 to 14 and recovering a reformate wherein less than about 20 wt.% of the aromatics content of said reformate comprises aromatics containing 30 nine or more carbon atoms.