AU702391B2 - Heating furnace system and method for producing hot rolled workpieces

Info

Publication number: AU702391B2
Application number: AU61931/98A
Authority: AU
Inventors: Francis H. Bricmont
Original assignee: Bricmont Inc
Current assignee: Andritz Metals Inc
Priority date: 1993-02-03
Filing date: 1998-04-17
Publication date: 1999-02-18
Anticipated expiration: 2014-02-03
Also published as: AU6193198A

Description

K

I'

Afy L; -s

AUSTRALIA

Patents Act 1990 COMPLETE SPECIFICATION STANDARD PATENT ao 6 *Go i Iqoo 4* 0* 04*to Kc Applicant(s): BRICMONT, INC.

r Invention Title: HEATING FURNACE SYSTEM AND METHOD FOR PRODUCING HOT ROLLED

WORKPIECES

The following statement is a full description of this invention, including the best method of performing it known to me/us:

I

F

1A HEATING FURNACE SYSTEM AND METHOD FOR PRODUCING HOT ROLLED WORKPIECES BACKGROUND OF THE INVENTION 1. Field of the Invention: The present invention relates to a heating furnace system to receive a stream of thin, continuously cast workpieces and supply such workpieces at a desired rolling temperature to a hot rolling mill, more particularly the present invention relates to such a heating furnace system having a greatly reduced floor space requirement o. while utilizing ancillary continuous casting and 0. rolling mill facilities to increased limit of 10 capacities and accommodating necessary downtimes for maintenance of such facilities.

o. 2. Description of the Prior Art: The continuous casting of thick, 8 inches, slab workpieces gave rise to possible direct rolling of the 15 workpieces by the use of an intermediate furnace to control the temperature of the workpiece entering the rolling mill. In recent years, the discovery of techniques that allow continuous casting of thin relatively wide workpieces of the order of between 2 and 4 inches thick and between 24 and 1?0 inches wide, contribute to numerous beneficial advantages that are an advancement in the art. There are disadvantages Sarising out of the reheat furnace necessary to allow Sthe direct rolling of the thin cast workpieces as well as more traditional continuously cast workpieces that can be greater than 4 inches thick and may range up to 2 inches thick. The thin cast workpieces can be processed in a hot rolling mill to produce hot strip product or steel plate. The thicker continuously cast product ranging between 4 and 10 inches can be rolled in a hot rolling mill to produce a hot rolled plate product or if desired more extensive hot rolling can be carried out to form a hot rolled strip. As the cast workpiece emerges from the casting facility, a torch or "1 0 other cutting device subdividing the casting to form workpieces of a finite length typically approximately 80 to 150 feet long with the width varying between 24 and 120 inches. An example of a facility to direct t" roll such continuous cast workpieces is illustrated diagrammatically in Figure 1. The workpiece emerging 15 at the discharge end E of a continuous caster is feed directly in a reheat furnace F. As disclosed in my United States Patent Nos. 4,991,276 and 5,082,047, flexible driven rollers may be used to convey as well as guide the thin cast workpieces along the entire length of the furnace during the reheating process.

The required length for such a furnace ranges from at least 300 feet up to 750 feet to heat a required number of continuously cast workpieces when the workpieces each measures 80 to 150 feet long. Because the reheating process is continuous and reheat time is finite for each workpiece multiple workpieces must be f heated in the furnace at any given time. Not only must 4 the ends of the workpieces be separated from one V 3 another in the furnace to allow orderly processing in the rolling mill M but also a time buffer is needed when the rolling operation is interrupted by the need to service the rolling mill equipment such as conventional roll changing. During such downtime for servicing operations, the workpiece can be oscillated forwardly and backwardly by the driven rollers in the furnace or the speed of the emerging casting from the dI, caster must be slowed; both such measures while 10 providing a time buffer have severe limitations.

S The facility illustrated in Figure 1 requires .1 cons-idering real estate as well as an inordinately long building structure to house the facility. Given that the furnace in Figure 1 must be 700 feet long there 15 must. be also provided an additional distance at each I" end of the furnace of at least 30 feet for entry and delivery tables to receive the casting at the cutting device from the caster and to deliver the workpiece at the rolling temperate to the first stand of the rolling mill. In a facility of the type illustrated in Figure 1, the capital investment represented by the rolling mill facility can be utilized to a far greater extent by the supply of workpieces from a plurality of casters. However, the castings emerging from the f. various casters can not be supplied to the same entry pass-line to a furnace.

An arrangement shown in Figure 2 is also 4 S known in the art and provides separate continuous 4 casters having delivery ends E that supply workpieces cut to finite length by torches T to separate reheat furnaces F each required to have a length of about 700 feet to achieve the required workpiece reheat operations. Furnace sections S and S are mounted on a track system to allow a lateral shuttle transfer of the furnace sections into alignment with the entry table for the rolling mill M for a time sufficient to pii empty the furnace of the workpiece and then laterally S I10 reposition the furnace section so that the other such furnace is positioned for feeding a workpiece into the entry table of the rolling mill. The addition of the shuttle furnace sections increases the requirement for floor space to accommodate the length of the shuttle furnace which must be slightly greater than the length of the workpiece. For example, when the workpiece is 5150 feet long, the shuttle furnace section will be approximately 155 feet long. The shuttle furnace in this instance severs the important function of receiving and holding a workpiece at a desired rolling temperature while a workpiece is discharged from the other of the furnace sections and at the same time accommodates the requirement to bring workpieces from laterally spaced casters into an alignment with a single rolling mill installation. The present invention seeks not only to reduce the required amount I 10of real estate, but also the expense for building Structure to hc \se reheat furnace equipment for direct rolling of continuously cast think workpieces.

SUMMARY OF THE INVENTION The invention provides a method for producing a hot rolled steel product, said method including the steps of: producing two streams of continuous castings having at least solidified outer layers; subdividing the emerging casting from each of said two streams to form two streams of workpieces having finite lengths and a hot cores of latent heat of the continuous casting process; loading seriatim workpieces of said two streams 15 of workpieces from opposite sides of a first furnace into the first furnace; forming a serial stream of workpieces from said first furnace to a heated furnace; transporting such workpieces to said heating furnace; arranging a plurality of such workpieces at S. "vertically spaced apart sites in the heating furnace; 4 heating the plurality of workpieces in said heating furnace to a predetermined elevated temperature suitable for hot rolling; recovering a heated workpiece from one of said vertically spaced apart sites; transporting the recovered heated workpiece at said predetermined elevated temperature from said furnace to an entry table of a hot rolling mill; and hot rolling the heated workpiece in said rolling mill to form a hot rolled steel product.

SThe invention also provides a method for producing a hot rolled steel product, said method including the steps of: producing two streams of continuous castings having at least solidified outer layers; H\Karen\Keep\div. 61O22-94-RICxO doc 71/04/98 ar~n~ll a~sl~ BII~ a P~ b~8~y ii i.

i ,1 an11 i 1 0 15 6 subdividing the emerging casting from each of said two streams to form two streams of workpieces having finite lengths and a hot core of latent heat of the continuous casting process; loading seriatim workpieces of said two streams of workpieces from opposite sides of a first furnace into the first furnace; forming a serial stream of workpieces from said first furnace to a heating furnace; simultaneously heating a plurality of workpieces from each of said serial streams in the heating furnace; discharging a heated workpiece from said heating furnace after heating therein to a predetermined elevated temperature suitable for hot rolling of the workpiece; and hot rolling the heated workpiece in a rolling mill train to form a hot rolled steel product.

H.\-%aren\Keep\div. 61022-94-BRCtHO1r.doc 17/04/98 BRIEF DESCRIPTION OF THE DRAWINGS These features and advantages of the present invention as well as others will be more fully understood when the following description is read in light of the accompanying drawings in which: Figure 1 is a diagrammatic illustration of a prior art arrangement of a reheat furnace having a flow path aligned with a continuous caster for workpieces and the entry end of a hot rolling mill; o Figure 2 is a diagrammatic illustration of a second reheat furnace arrangement according to the prior art in which two continuous casters supply workpieces separately to a system of holding furnaces for supply through operation of a shuttle transfer of holding furnaces to the entry side of a hot rolling mill; Figure 3 is a diagrammatic illustration of a single caster to supply finite workpieces to a reheat furnace embodying the features of the present invention; t Figure 4 is a diagrammatic illustration of a preferred I embodiment of a reheat furnace for supplying I"-Cl"p sn~l -ararrsav~l81~i~u~;rraoa~-l l-r reheated workpieces to a hot rolling mill from two continuous casters; Figure 5 is an enlarged plan view of the embodiment of holding furnaces and transfer equipment shown in Figure 4; Figure 6 is sectional view taken along lines VI-VI of Figure Figure 7 is a sectional view taken along lines VII-VII of Figure 3 illustrating a preferred embodiment of a reheat furnace; Figure 8 is a sectional view taken along ,gl* lines VIII-VIII of Figure 7; Figure 9 is a sectional view taken along lines IX-IX of Figure 8; Figure 10 is a sectional view taken along lines X-X of Figure 8; and Figure 11 is an enlarged fragmentary view in elevation of the drive structure for the workpiece handling bar forming part of the reheat furnace shown in Figure 7; Figure 12 is a sectional view taken along lines XII-XII of Figure 11; and Figure 13 is an elevational view taken along lines XILI-XILlof Figure 11.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In Figure 3 there is illustrated a simplified arrangement of facilities to produce a hot rolled steel product according the present invention. In this

A

-9embodiment there is a continuous caster 1ithat receives a supply of molten steel and produces a continuous casting comprising a thin cast a thin cast slab or a conventional cast slab. The casting emerging from the caster passes a cut-off device 3 which operates to sever the casting to predetermined finite lengths. A dwell time exists while the leading end of the casting passes the cut-off device and to protect against an unwanted loss of heat of the casting a holding furnace 4 protectively houses the casting throughout its movement until the cut-off device operates to define its finite length. The casting is then advanced along a roller hearth of the holding furnace to emerge therefrom and enter through a openi;ng exposed by a moveable door and an end wall of a heating furnace The workpiece is received in the heated furnace on a roller hearth which advances the workpiece in the direction of its length to a point where it is wholly located within the L~ngth of the furnace, thus the furnace length substantially corresponds to the length thetheatringfuce The~ showningrs 7-14h aosrcin wil ofe theatn wfrkpice dtaoni togthes constuctin ofll be described in greater detail hereinafter. A plurality of such workpleces is simultaneously heated in the heating furnace and when a desired temperature is attained for a hot rolling process, 'that workpiece A is removed from the furnace and delivered to the entry f- iIi 10 end of a hot rolling mill 6. The hot rolling mill is per se well known in the art.

Referring now to Figure 4, there is illustrated delivery tables 10 and 11 of side-by-side continuous casters 12 and 13, each continuous caster being of a type per se well known in the art and produces from a supply of molten steel a continuously cast product that is thin as to its thickness in Srelation to its width and is sometimes referred to in the art as a thin cast slab. The continuously cast workpiece may be a continuously cast slab having a thickness within a range of 4 to 10 inches. The cast product typically will have a thickness of between 2 and 4 inches and a width of between 24 and 70 inches.

too 15 The cast products passing from the delivery tables have a solidified outer shell surrounding a hot core that is also solidified but at a significant higher temperature than the shell. The continuous casting passing from each deliver table moves at a speed of about, for example, 190 inches per minute, which is significantly greater by a factor of 5 or more than the casting speed of a conventional 10 inch thick slab. The streams of continuous castings are severed to finite lengths while Spassing cutoff devices 14 and 15 during their respective movement from tables 10 and 11 to holding furnaces 16 and 17.

i A significant feature of the present invention provides that the holding furnaces each have

L

0: 0 g,00 00 0 0 70 a a 1.

11 a length generally corresponding to the length of the finite casting when cut from the upstream part of the casting by the respective cutoff device. Specifically, for example, each of the holding furnaces 16 and 17 will nave a length of about 155 feet when the finite length of the continuously cast workpiece is established at 150 feet. The holding furnaces function to retard the loss of heat from the continuous casting process. The favorably influence to the unwanted loss of heat by the holding furnaces may include burners within the holding furnaces. Since the casting process requires a period of time to complete a formation of the required workpiece length, the holding furnace avoids undue cooling to the leading end portion of the workpiece. Extractors 18 and 19 which can take the form of chain transfers, peel bars or other well known forms of furnace extractor equipment transfer the workpiece laterally from the holding furnaces 16 and 17 to a central holding furnace 20. The transfer proces.

is seriatim such that a workpiece received in furnace f 4 from furnace 16 will be followed by receipt of a workpiece from furnace 17 in furnace 20. Furnace like furnaces 16 and 17 is a holding furnace and houses the workpieces to prevent heat loss during conveyance of a workpiece by driven rollers forming a rotary hearth therein to a reheat furnace 21. The details of the construction of the holding furnace 20 are shown in i Figures 5 and 6 and will be discussed hereinafter. The l.

C-_II-Y

i; i r :i -6 ~CCr~-R~s~l r~3e~Lm~ w rD. *r *0 S 5 e S. S 5 9..

Ser 12 workpiece passing from holding furnace 20 is received in a roller hearth section of the reheat furnace 21 for heating a plurality of such workpieces during suitable residence times in the high temperature environment of the furnace to a predetermined temperature which is suitable for carrying out hot rolling operations.

After a workpiece obtains the desired temperature for rolling, it is discharged from the furnace to an entry table 22 of a hot rolling mill 23. A feature of the 10 present invention resides in the use of the reheat furnace 21 with a length required to accommodate the predetermined length of the workpiece and a furnace width to allow side by side transfer of a workpiece by a roller hearth along one side of the heat zone wherein 15 individual workpieces are stacked in a vertically spaced relation. With respect to the required furnace length, when the workpiece is 150 feet long then the reheat furnace will have a length slightly greater such as 155 feet. The furnace arrangement shown in Figure 4 requires a length of ;loor space within a building of about, for example, 360 feet which compares very favorably and reduces by a factor of 2, to a corresponding amount of floor space required by furnace arrangement known in the art and shown, for example, in Figures 1 and 2 In Figures 5 and 6 the arrangement of holding furnaces and heating furnace of Figure 4 are illustrated in greater detail. Furnaces 16, 17 and At i a 1j 1 ar

N

13 o 0 I *s 6 0* 0 005*00 s.

*o each embody the usual refractory lining supported by an outer metal shell that is in turn supported by buckstays extending along the outer parts of the sidewalls when they project upwardly beyond furnace roof portions where the buckstays are joined with an overhead super structure 26 including horizontally extending beams 27 that span across the tops of the furnaces and join by posts 28 extending downward to anchor sites comprising foundation supporting bases.

10 As can be seen in Figure 5, the beams 27 are spaced apart at regular intervals along the lengths of the furnaces 16, 17 and 20. The use of the super structure 26 to support the furnaces enhLnces the furnace construction and allows roller hearth 29 and furnace 16; roller heart 30 and furnace 20; and roller hearth 31 and furnace 17 to be supported by individual foundations. Furnaces 16 and 17 may have doors 32 and 33, respectively, when desired, at the ends of the furnaces facing the continuous caster which are selectively opened to allow entrance of a casting emerging from the associated caster. Once the casting is housed in the furnace, the door may be closed to maintain the high temperature furnace environment within the furnace. As discussed previously, burners may be arranged at spaced apart locations in the furnace walls to form heat sources. Furnaces 16 and 17 each have a longitudinal sidewall wherein there is located along the entire length of the sidewall furnace ;I'i *t '1 f 14-1 14 1 doors 34 and 35, respectively, that allow a lateral transfer of the workpiece from the furnace hearth by an associated extractor 18. The doors 32, 33, 34 and preferably embody a construction well known, per se in the art. A preferred source for such doors is from Aucmet, Inc. of McMurray, Pennsylvania, and sold under the tradename "perma close doors". Furnace 20 has doors 36 and 37 along each of its longitudinal sides to 'allow seriatim passages of a workpiece removed from furnaces 16 and 17 into furnace 20. Workpieces are discharged from furnace 20 in a serial fashion through a opening end thereof, normally closed by doors 38 to HC allow passage of the workpiece to a rotary hearth of heating furnace 21. Door 38 as vell as doors 36 and 37 may also comprise the aforesaid permaclose doors.

The details of the construction of a preferred embodiment of a heating furnace 50 suitable to form reheat furnace 21 of the embodiment of Figure 4 as well as heating furnace 5 in the embodiment of Figure 3 are shown in Figures 7-14. The furnace Sincludes spaced apart refractory side walls 51 and 52 having a length corresponding to but slightly greater than the length of workpieces to undergo heating in the furnace. The furnace also includes end walls 53, only one of which is shown in Figure 7, having doors that can be selectively opened to allow passage of a workpiece into the furnace where into a furnace for support by a hearth which includes spaced apart roller rr 15 assemblies 54. The roller assemblies each include a journal member extending in opposite directions through suitable openings in the refractory side walls 51 and 52 where bearing supports are rotatably support the rolls while connected to drive motors 55. The rollers 54 may be constructed in a manner disclosed in my United States Patent No. 4,991,276 or according to the j "construction shown in my co-pending patent application Serial No. 07/740,147 which is incorporated herein by reference hereto. The sidewalls 51 and 52 and walls 53 as well as roof 56 embody a usual heat resistant furnace construction that includes an inner lining of refractory 57 supported by an outer metal shell 58 that in turn receives structural support from buckstays 59 15 at horizontally spaced locations along the side walls.

Struccural members 60 provide support for the roof 56.

As can be seen in Figure 7, the rollers 54 on the rotary hearth have a face length slightly greater than the width of the workpiece W supported thereon.

The hearth terminates at an upstanding wall portion which extends to an elevated floor 62 that underlies and forms the base of a heating zone 63. The heating zone has a width slightly greater than the width of workpieces and extends from the inside surface wall 52 j 25 to a vertical plane 64. Horizontally beyond plane 64 B of the heating zone 63 there is a loading zone 65. The loading zone 65 is bounded at its base by the rotary hearth and extends upwardly therefrom along the entire -16height of the heating zone. In the heating zone 63 there extends in a cantilever fashion from wall 52 a plurality of rows 66 of aligned workpiece supports 67.

The details of which are best shown in Figures 8, 9 and 10. Heat support 67 is comprised of a bent pipe 68 which forms an acute angle at its most inwardly projecting part from which there extends leg portions 69 that pass through spaced apart openings in the refractory lining and metal shell of side wall 52. At the points where the leg portions 69 emerge from the side wall the leg portions traverse a horizontal support 70 (Figure 9) which provides load bearing support to the carriers. Outwardly beyond support the legs 69 have bent portions that extend vertically along other supports 71 which also extend beyond the e buckstays and supply support that resists a bending moment imparted to the carriers by the weight of the workpiece thereon. The upturn portions of the legs externally of the furnace have jumper pipe headers or the like to supply liquid coolant for passage along the tubular part of the carriers. Inside the furnace, the legs 69 are encased with insuiation 72 except for spaced apart sites where vertically extending heat 'Aresistant pads 73 protrude from the insulation and define the actual contact areas with the downwardly directed face surface of a workpiece.

-t As shown in Figure 7, between the rows 66 of supports there is arranged in the side walls 52 rows of 17 burners 74 which operate to establish and maintain a highly heated environment within the heating zone.

As can be seen from Figure 8, the bent configuration of the supports avoids contacting the workpiece along areas transverse to the workpiece so as to minimize affects of cold spots during the hot rolling operation.

As shown in !igure 8, legs 69 of each carrier intersect with vertical planes containing the 10 rotational axis of roller assemblies 54 forming p.rrt of the hearth and residing in the loading zone 65. The vertical planes which contain the rotational axis of the rollers as well as legs 69 are spaced apart by a distance sufficient to accommodate vertical as well as *0tt horizontal movement in a vertical plane 75 by transport arms 76. The transport arms operate exclusively within oa.

vertical planes 75 to receive a workpiece from the rollers of the hearth lifted vertically in the loading zone 65 and then move it horizontally from zone 65 to heating zone 63 where it is deposited into supporting engagement with one of the rows 66 of supports 67.

Similarly, after the workpiece attains a desired temperature suitable to carryout the hot rolling process, the transport arms are removed to retrieve the workpiece from its supporting engagement with a row of carriers and deposit it in the transport zone on the rollers of the hearth. For this purpose, transport arms 76 are provided with an extended length arranged 18 so that the workpiece engaging part of the arms extends through a vertically extending slot in the side wall 51 of the furnace. The portion of the arms externally of the transport zone are supported oy spaced apart rollers 77 above the arms and a drive roller 78 below the arms. The drive rollers 78 have gear teeth on their outer periphery that engage with rack gear segments on the underside of the arms such that operation of drive motors propel the arms to and fro between the loading zone 65 and the heating zone 63.

Drive roller 78 and its associated motor are supported by a platform 79 that also carries a frame used to support a nut member while threaded engaged with threads on a vertically arranged drive spindle 80. The lower end of the drive spindle is supported by a thrust bearing on a pedestal 81 while the upper end of the spindle is rotatably supported in a bearing housing 82 and provided with a gear wheel meshing with a worm driven by a motor 83. Rotation of spindles 83 imparts vertical movement to the frame 79 hence also transport arms 76 supported thereby causing the workpiece engaging end of the transport arm to move vertically within the transfer zone 63. This movement is such that the workpiece engaging end of the arts passes in planes 75 below the upper surface of the hearth rollers to allow a workpiece to be advanced by the rollers into the furnace by a loading operation and a heated ti L t*

{I

L o *0aS**

C

1" i i 19 workpiece can be discharged by the rolls at the completion of a heating operation.

Referring now particularly to Figures 11-13 and as described previc,sly, the transport arms operate within a vertical slot in the side wall 51 of the furnace. A moveable seal 125 closes the slot above and below the site of the transport arm, The seal includes a vertically stacked mosque of refractory brick 126 having a width corresponding to the width of the slot and a thickness to extend it into the slot. The bricks are adhered to a face part of vertically ending strips of refractory insulation 127 that have a width greater than the wich of the slot to slide along the outer faces of the metal shell of the side wall. A strip of wire mesh, such as that used for conveyor belting 128, supports the insulation 127 along a central portion of the strip and along opposite marginal edges 129 and 130 of the belting 128 there is formed transverse bars at regular intervals forming tooth members that can engage with teeth on upper and lower pulleys 131 and 132. As shown in Figure 12, the belting is affixed to brackets 133 supported by platform 79 whereby movement of the platform vertically displaces the seal vertically in the slot. The belting extends beyond pulleys 131 and 132 away from the furnace to a second set of upper and lower pulleys 134 and 135 where the belting formed in an endless fashion. When the transport arm moves vertically, brick 126 on insulation 127 is stored at an

'A

20 elevated site and when the transport arm moves downwardly, broken insulation is stored at a site near the pedestal 81.

While the present invention has been described in connection with the preferred embodiments of the various figures, it is to be understood that other similar embodiments may be used or modifications and additions may be made to the described embodiment for performing the same function of the present 10 invention without deviating therefrom. Therefore, the present invention should not be limited to any single embodiment, but rather construed in breadth and scope in accordance with the recitation of the appended claims.

o r sr

D

e oo s s e r

~D

r o rr

I

i

I

o

Claims

1. A method for producing a hot rolled steel product, said method including the steps of: producing two streams of continuous castings having at least solidified outer layers; subdividing the emerging casting from each of said two streams to form two streams of workpieces having finite lengths and a hot cores of latent heat of the 10 continuous casting process; loading seriatim workpieces of said two streams of workpieces from opposite sides of a first furnace into the first furnace; .forming a serial stream of workpieces from said first furnace to a heated furnace; transporting such workpieces to said heating furnace; arranging a plurality of such workpieces at j-.0 vertically spaced apart sites in the heating furnace; A 20 heating the plurality of workpieces in said heating furnace to a predetermined elevated temperature suitable for hot rolling; recovering a heated workpiece from one of said vertically spaced apart sites; transporting the recovered heated workpiece at said predetermined elevated temperature from said furnace to an entry table of a hot rolling mill; and hot rolling the heated workpiece in said rolling mill to form a hot rolled steel product.

2. A method for producing a hot rolled steel product, said method including the steps of: producing two streams of continuous castings having at least solidified outer layers; subdividing the emerging casting from each of I said two streams to form two streams of workpieces having finite lengths and a hot core of latent heat of the H:iKare\Keep\div. 61(2-94-aRICHOZ1T.doc 17/04/98 forming a serial stream of workpieces from said 22 continuous casting process; loading seriatim wstreams rkpieces of said two streamsce; of workpieces from opposite sides of a first furnace into the first furnace; forming a serial stream of workpieces from said first furnace to a heating furnace; simultaneously heating a plurality of workpieces from each of said serial streams in the heating furnace; discharging a heated workpiece from said heating 10 furnace after heating therein to a predetermined elevated temperature suitable for hot rolling of the workpiece; and hot rolling the heated workpiece in a rolling I 20 o.t mill train to form a hot rolled steel product. Dated this 17th day of April 1998 •BRICMONT, INC. GRIFFITH HACK Fellows Institute of Patent Attorneys of Australia. C faea HTIKar\Kcep~di.61022-94-3iRICMaFdoc 11/c)4/gs _IIIC r'<V -i ABSTRACT A heating furnace system is provided for receiving finite lengths of workpieces from one or more continuous casters and from a supply of heated workpieces at a temperature suitable for rolling in a hot rolling mill The system includes, in one aspect, a holding furnace receiving a workpiece during continuous casting until it is severed by a cutoff device to prevent unwanted cooling. The workpiece is fed from a holding furnace to a heating furnace wherein it is deposited onto one ot a series of vertically spaced supports in a heated section where it remains static throughout the heating process. After heating the workpiece is removed from the stationary 15 supports and returned to rollers of the hearth for discharge from the furnace to a rolling mill 0000.0 So a o o 0o 0 o eo o 0 0 o~eu 0 o A Hlt\Karen\Keep\div.61022-94-BRICMOCT.doc 17/04/98