AU620061B2 - Knit or woven textile, process for its production and blood vessel repairing sheet and artificial blood vessel made therefrom - Google Patents

Description

Signature(s) of declarant(s).

To: The Commissioner of Patents, Australia 62 QPU OP1AOL DATE 05/07/89 DATE 27/07/8,9 APPLN. I D 28085 89 PCT NUMBER PCT/JP88/01217 "10 89/ 05371 D06C 29/00, A61 L 27/00 A D02G 3/04 A 1 1(43) ff~N 199V6)11 iEB (15.06.89) (21 ffitiM*j _P0T/J1PS/0 12 17 74)f4j (22) PlifH1988! z2A1B~k01. 12. 88) 03 Mj~e (WATANABE, do c hi t os hi li (31 ilYO t6 2 -3 10 6 62 T 10I1AWf 31>:Z 3 T 92 d2~ EC' e4 Z Z (32) fkB 19874:2ASH8E0S. 12. 87,' Tokyo, (JP' (71 MI W-rk -t Nt K AU, B3E%0JH47.R ),DE(Jit .r1 tn-eKt-_4±(TERUMQ KABUSHIKI KAISHA) £JP/JP) B I I#S, L 'l2, SE T151 4 2T 44I Tokyo, us.

(72) RHA f- t'NMIASUNIOTO, A t u s hi) (J P/JF) tTR.Y KATAKUR A, T ak eo :J1./J P IE TANABE, S u s umu JP/JI1K T 4 17 *~l2 6 5 6 d fy'q,,I r Shizuoka, R ;R-(I"OR1, Yu ic h iJ P/J P T 21 4 IIA"I t.Pii FT i-M1 -1 7- 5- 50 Kanagawa, kJP) (54)Title: KNIT OR WOVEN TEXTILE, PROCE'SS FOR ITS PRODUCTION AND BLOOD VESSEL REPAIRI NG SHEET AND ARTIFICIAL BLOOD VESSEL MADE THEREFROM (57) Abstract Knit or woven textile in which respective filaments are adhered to each other at predetermined positions of contact.

and substantially no adhesive exists in the space except for the contact points, and which has a suitable softness and water permeability. This textile is produced by applying an adhesive which melts when heated to filaments at predetermined intervals, knitting or weaving the resulting filaments into knit or woven textile, and heating it to melt the adhesive for adhering the filaments to each other at the contact points. The knit or woven textile is useful as a blood vessel repairing sheet, an artificial blood vessel, etc.

7) -1 A c tF 1 -C t vc9. fo AU ffi r+ Y± .7 ;f Qz Jz &t f Az- If I~ ILE f :Jz '9 I T

-C

k)ifa T-Aq AT t-7, h7 FR 75-' MR -U .z 7 AU t-7, J-51)7 GA tM.,kW 7 BB MPCH 7 CB Ij 2, NL ;t BE cm'4-- HLU NO t- BG -J)D 1) 7 IT -i~-RO A, 7 BJ 01P B z SD A BR *f 5SJ IKP 49f F"AT SE 7, CF 7 7 1) K R SN -t tbl Of b XtJU-- L'u Lt'J~ TC I-f DE I9I4-iV MC us ~t FI 7 3 ML 7 'U- -1-

SPECIFICATION

TITLE OF THE INVENTION Knitted or Woven Fabric, the Method for Producing the Fabric, Artificial Blood Vessel Restorative Sheet and Artificial Blood Vessel Formed by the Fabric TECHNICAL FIELD This invention relates to a blood vessel repair or restorative material that is not affected in porosity, flexibility or suturability and that is not liable to be raveled at cut ends, and the method for producing the material.

BACKGROUND OF ART At present, a tubular artificial blood vessel employed in a larger blood vessel having an inside diameter of not less than 5 mm or a blood vessel repair or restorative material in the form of a sheet-like patch is mainly prepared from a knitted or woven fabric of polyester or polytetrafluoroethylene fibers or from previously expanded porous polytetrafluoroethylene graft. Above all, the knitted fabric is formed by spinning with polyester type bulky filament formed by monofilaments having the diameter of L--1II J.m (monofilaments presenting meandering curves) and weaving or knitting this filament by plain weave or knitting.

On the other hand, an artificial blood vessel or a patch for blood vessel presenting the different degree of porosity (water permeability), shape or flexibility is frequently used in dependence upon the occasional transplant position or status of the patients. Thus the doctor usually selects a suitable restorative material and cuts it to suitable size to meet occasional requirements. At this time, yarn raveling or waste of the knitted fabric tends to be produced at the cut end or edge, whilst since the fabric is anastomosed with the living tissue at this cut end or edge, a sufficient anastomotic strength cannot be produced, such that the blood tends to leak out thereat or the perimetral portion of the repaired position tends to be contaminated.

Among the features of the knitted fabric required of the blood restorative material are a sufficient curability and the blood leakage preventive effect at the initial stage of transplantation. For improving the curability, it is necessary to increase water permeability; however, the risk of blood leakage becomes that high with increase in water permeability. For this reason, woven fabrics of lower water permeability have come into use more frequently. However, the woven fabric is also beset with a shortcoming that it is 3 more liable to yarn ravelling or waste than the knitted fabric.

It is an object of the present invention to overcome this inconvenience of the prior art and to provide a knitted or woven fabric which is not affected in porosity or flexibility and which is not liable when cut to yarn raveling or waste, the method for producing the fabric and the blood restorative sheet and the artificial blood vessel formed by such fabric.

DISCLOSURE OF THE INVENTION The present invention provides a blood vessel c restorative material comprising a woven or knitted fabric f twherein said fabric is fabricated by weaving or knitting a yarn having a heat-sensitive adhesive having a melting point lower than that of the t yarn applied thereon at a predetermined interval to form a woven or knitted fabric; and heating the woven or knitted fabric to melt the heatr sensitive adhesive such that the yarns are bonded with each other only at predetermined contact points, and spaces defined between the yarns are not filled with the adhesive so that the woven or knitted fabric will retain its flexibility, water permeability, and fraying resistance.

BRIEF DESCRIPTION OF THE INVENTION Fig. 1 is a partial diagrammatic view of a knitted fabric according to the present invention, plIAl Fig. 2 is a diagrammatic view showing the state in which the knitted fabric shown in Fig. 1 is cut partially, bc/12/5645ter.spe 91 11 6 -4 Fig. 3 is a diagrammatic view showing an example of means for applying an adhesive to the yarn.

al 0* *09 0 0 0000 0 09 d bc/12/5645ter .spe 91 11 6 BEST EMBODIMENT FOR PRACTICING THE INVENTION The present invention will be explained in more detail hereinbelow.

There are a sheet-like patch or a tubular artificial blood vessel, as the blood vessel restorative material, as mentioned above. These are generally constituted by knitted fabrics since porosity (water permeability) and flexibility are among the requirements As a result of our researches towards eliminating the above described drawbacks of the prior art system, the present inventors have succeeded in evolving a knitted or woven fabric which is not liable when cut to formation of yarn raveling or waste and which is endowed with porosity (water permeability) and flexibility, the method for producing the fabric and the blood repair or restorative material formed by the fabric.

Fig.l is a plan view showing an embodiment of using the plain weave among the woven and knitted fabrics of the present invention. The knitted or woven fabrics designate the woven fabrics and the knitted fabrics. Although the following description is made with reference to this woven fabric as a representative example, the present invention also applies to the knitted fabric as well.

As shown in Fig.l, a fabric 1 is woven from warp yarn yi, wherein i is 1 to 9 in Fig.l, and weft yarn xi, wherein i 7* i is 1 to 9 in Fig.l. The points of intersection or contact between the warp yarn and the weft yarn are bonded at predetermined positions with a heat meltable adhesive 2 applied to each yarn at predetermined intervals. In the woven fabric shown partially in Fig.l, such bonding is made at contact points A (x2, y3), B (x2, y7), C (x6, y3) and D (x6, y2).

It is assumed that the fabric shown in Fig.l is cut as shown in Fig.2. When it is also assumed that the contact points of the fabric 1 are not bonded with the adhesive 2, the weft yarn x2 tends to be dislocated from the woven fabric and is turned into yarn raveling or waste. With the weft yarn x2 detached from the woven fabric, the weft yarn x3 also tends to be raveled.

Conversely, when the warp yarn y3 and the weft yarn x2 are bonded to each other at the point of contact A with the adhesive 2 according to the present invention, raveling of the weft yarn x2 is stopped at the bonding point A between the warp yarn y3 and the weft yarn x2 without proceeding any further. Thus the weft yarn x3 is also prevented from raveling.

On the other hand, if attention is directed solely to raveling, it may be possible to resort to a method consisting in dipping the fabric in an adhesive dissolved in a solvent Sr7 to coat the fabric with the adhesive on the whole, or to a -7method consisting in partially printing the woven fabric with an adhesive. However- with these methods, the raw yarns will adhere to each other and almost all contact points between the yarns will adhere to each other, with the result that flexibility required of the blood vessel restorative material is lost and water permeability is also lowered so that it becomes difficult to turn the material into a satisfactory organ.

Conversely, in the present invention, flexibility and water permeability are not affected substantially because there are only few connecting points between the yarns by the adhesive.

On the other hand, the blood vessel restorative material is a fabric knitted or woven so closely that, in the case of the plain weave, adjacent warp or weft yarns contact each other. Therefore, when the adhesive is applied partially to the woven or knitted fabric after weaving or knitting, the major portion of the yarn is bonded together by the adhesive seeping into the yarn with the result that the fabric is affected in flexibility. On the other hand, the effect of preventing raveling is lowered because some yarns are not affixed with the adhesive.

According to the present invention, the effect of preventing raveling is significant because the resin is /A-^rNi applied to the yarns at predetermined intervals before -8weaving or knitting, so that the yarn remaining unaffixed to the adjacent yarns may be eliminated even in the case of plain weave.

As the starting material of the yarn employed in the present invention, polyester or polytetrafluoroethylene may be employed. However, from the viewpoint of biocompatibility and compatibility with the adhesive, polyester is most preferred.

As the adhesive to be applied to the yarns, any adhesive having the melting point not higher than the melting point of the yarn may be employed, such as, for example, polyurethane, polystyrene, polyolefin or gelatin.

Fig.3 shows, only by way of an illustrative example, means for applying an adhesive to the yarn at predetermined intervals.

Turning to Fig.3, an adhesive is applied at a printing drum 13 to a raw yarn 12 reeled out from a spool 11 The printing drum 13 has a rotary drum 15 revolving about a rotational shaft 14 which is provided with a groove 16 in which the raw yarn 12 is laid. A number of orifices 17 are formed at predetermined intervals in the groove 16.

The adhesive seeps out of these orifices 17 so that the adhesive 18 is applied at predetermined intervals on the raw yarn 12.

-9- The treated yarn 19 to which the adhesive 18 is applied as described above is dried in a dryer 20 before being taken up on a take-up spool 21. In this manner, the yarn to which the adhesive has been applied at predetermined intervals for preparing the knitted or woven fabric of the present invention is obtained.

The yarn obtained by the method shown for example in Fig.3 may then be woven or knitted in a conventional manner to produce the woven or knitted fabric according to the present invention.

This woven or knitted fabric is then heat-treated to melt only the adhesive to cause the points of contact or intersection between the warp and weft yarns of the fabric with the adhesive. This completes the woven or knitted fabric of the present invention.

The woven or knitted fabric thus formed is 'used mainly as the blood vessel restorative material which may be in the form of a sheet. Such a sheet-like patch may be cut to a required size to repair e.g. a hole punched in the blood vessel.

The blood vessel restorative material may also be knitted or woven into a tube. The resulting tubular fabric is used as an artificial blood vessel in substitution for a portion of an injured blood vessel.

In the woven or knitted fabric of the present invention, the adhesive is applied only in the vicinity of the contact points of the yarns for affixture, while virtually no adhesive is applied to the voids between the yarns, Thus the fabric is not affected in flexibility, as compared with the woven or knitted fabric produced from the yarns not treated with the adhesive, while exhibiting moderate flexibility and sufficient porosity or water permeability, so that it may be employed satisfactorily as the blood vessel restorative material.

The present invention will be explained in more detail with reference to an illustrative example thereof.

Using a rotary press shown in Fig.3, polyurethane dissolved in a solvent was applied to a 5 denier polyester fiber, at intervals of 2 mm each to a width of 100 Lm.

The thus produced yarn was woven by plain weave and processed into a patch for blood vessel which was then heated to 185 0 C. The patch for blood vessel produced is not affected substantially in flexibility, as compared with the patch produced from the yarn not treated with the adhesive, while remaining substantially free from yarn raveling or waste when cut with scissors. Although water permeability is lowered by about 5 such a minor decrease in water permeability does not raise practically any problem.

-11- APPLICABILITY TO INDUSTRY In the woven or knitted fabric of the present invention, the adhesive is applied only in the vicinity of the contact points of the yarns for affixture, while virtually no adhesive is applied to the voids between the yarns, Thus the fabric is not affected in flexibility, as compared with the woven or knitted fabric produced from the yarns not treated with the adhesive, while exhibiting moderate flexibility and sufficient porosity or water permeability, so that it may be employed satisfactorily as the blood vessel restorative material.

Such woven or knitted fabric may be produced easily anid inexpensively by a method consisting in applying an adhesive to the raw yarns at predetermined intervals, weaving or knitting the yarns to form a fabric and heating the fabric to melt the adhesive to cause the yarns of the fabric to adhere to each other at the contact points between the yarns.

~ALI,~

iul

Claims (4)

1. A blood vessel restorative material comprising a woven or knitted fabric wherein said fabric is fabricated by weaving or knitting a yarn having a heat-sensitive adhesive having a melting point lower than that of the yarn applied thereon at a predetermined interval to form a cha woven or knitted fabric; and wov heating the woven or knitted fabric to melt the heat- bet sensitive adhesive such that the yarns are bonded with sub each other only at predetermined contact points, and poi "0 spaces defined between the yarns are not filled with the fle adhesive so that the woven or knitted fabric will retain its flexibility, water permeability, and fraying pro resistance. tha 0 0

2. The blood vessel restorative material of claim 1 to *0 wherein the fabric is a sheet. are

3. The blood vessel restorative material of claim 1 hea wherein the fabric is a tube. eac "2Q,

4. A blood vessel restorative material substantially as hereinbefore described with reference to ves the accompanying drawings. DATED this 6 November, 1991 CARTER SMITH BEADLE Fellows Institute of Patent Attorneys of Australia Patent Attorneys for the Applicant: U lj1 TERUMO KABUSHIKI KAISHA Sjbc/12/5645ter.spe 91 11 6 91116 1 44 ABSTRACT The present invention provides a woven or knitted fabric characterized in that it comprises a knitted fabric or a woven fabric wherein predetermined ones of contact points between yarns are affixed with an adhesive, there being substantially no adhesive in voids exclusive of contact points of the yarns, the fabric exhibiting moderate flexibility and water permeability. Such woven or knitted fabric is produced by a method for producing a woven fabric or a knitted fabric characterized in that an adhesive that may be melted upon heating is applied to yarns at predetermined intervals, the yarns thus produced are knitted or woven to form a fabric and the adhesive is heat melted to cause the yarns of the fabric to adhere to each other at. contact points between the yarns. Such woven or knitted fabric is useful as the blood vessel restorative sheet or as the artificial blood vessel.