AU4464799A - Process for preparing bitumen compositions - Google Patents
Process for preparing bitumen compositions Download PDFInfo
- Publication number
- AU4464799A AU4464799A AU44647/99A AU4464799A AU4464799A AU 4464799 A AU4464799 A AU 4464799A AU 44647/99 A AU44647/99 A AU 44647/99A AU 4464799 A AU4464799 A AU 4464799A AU 4464799 A AU4464799 A AU 4464799A
- Authority
- AU
- Australia
- Prior art keywords
- bitumen
- process according
- blocks
- poly
- bitumen composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Description
S F Ref: 438981D1
AUSTRALIA
PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT
ORIGINAL
0:0.
see* Name and Address of Applicant: 0 1 0 sees 0 0 Actual Inventor(s): Shell Internationale Research Maatschappij B.V.
Carel van Bylandtlaan NL-2596 HR The Hague THE NETHERLANDS Gerrit Van Gooswilligen, Baanders Rudolf and Koen Steernberg Spruson Ferguson, Patent Attorneys Level 33 St Martins Tower, 31 Market Street Sydney, New South Wales, 2000, Australia Process for Preparing Bitumen Compositions Address for Service: Invention Title: The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5845 M 1 Process For Preparing Bitumen Compositions The present invention relates to a process for preparing bitumen compositions, bitumen compositions obtainable by such process and the use of them in asphalt mixtures for road applications.
Bitumen is used as a binder in road asphalt mixtures, and has developed continually to meet everincreasing performance demands from road building constructors. In general bitumen performs well in road asphalt, but increasingly heavy traffic loads have led to the premature wear of many roads through rutting and cracking of the surface. Cracking is a serious defect in a road asphalt because it allows water to reach lower layers of the road surface where it causes rapid deterioration, and accelerates the need for premature repairs. Increasing the bitumen content.. of asphalt or using a softer grade of bitumen improves the crack resistance of asphalt at low temperatures but increases the risk of excessive rutting at higher temperatures because the mixture is effectively softer. Conversely, resistance of rutting can be improved by reducing the amount of bitumen in the asphalt mixture or by using a harder grade of bitumen, at the expense, of crack resistance because the mixture becomes less flexible.
•:In view of the above it will be clear that it would be advantageous to develop a hard bitumen 15 composition meeting today's crack resistance requirement, ie. a bitumen composition having both a good low temperature performance and a good high temperature rutting resistance.
*.It is known that the low temperature properties of bitumen can be improved by blending them with a polymer. However, when this modification is applied to hard bitumen, an incompatibility between the bitumen and the polymer is generally observed, resulting in hardly or not improved low temperature 20 properties and a relatively poor ageing behaviour.
It is further known to prepare industrial and roofing-grade bitumen by subjecting a bitumen/polymer mixture to a conventional blowing process. These bitumen compositions, however, appear to be not ec. suitable for road applications, due to their high softening point and relatively high penetration.
Object of the present invention is, to provide a bitumen composition suitable for road applications 25 having both a good low temperature performance and a good high temperature rutting resistance, and in addition an improved ageing behaviour.
Surprisingly, it has now been found that such bitumen composition can be prepared by. mixing a particular bitumen with a thermoplastic rubber.
Accordingly, the present invention relates to a process for preparing a bitumen composition which comprises mixing at an elevated temperature an oxidised bitumen having a penetration index of at least 0 with a thermoplastic rubber which is present in an amount of less than 5%wt,. based on total bitumen composition.
Preferably, the bitumen has a penetration index of at most 5. More preferably, the bitumen has a penetration index in the range of from 0 to 2.
Suitably, the thermoplastic rubber is present in an amount of less than 3 %wt, preferably in the range of from 0.1 to 2.5 %wt, based on total bitumen composition.
Suitably, the present process is carried out at a temperature in the range of from 160 to 220 0
C.
Preferably, the process according to the present invention is carried out at a temperature in the range of from 170 to 190 0
C.
C06992 The process may be carried out at ambient pressure or elevated pressure. Normally, however, it will be carried out at ambient pressure.
Suitably, the present process is carried out over a period of time of less than 6 hours, preferably less than 2 hours.
The oxidised bitumen is suitably obtained by subjecting a bitumen to a blowing process. More preferably, the oxidised bitumen is obtained by subjecting a bitumen to a catalytic blowing process.
Suitable catalysts to be used in such blowing process include those taught in the art such as ferric chloride, phosphorus pentoxide, aluminium chloride, boric acid and phosphoric acid, the latter being preferred. The catalyst is normally added to the bitumen to be blown in an amount of less than based on bitumen. The blowing process is carried out with an oxygen-containing gas, such as air or pure oxygen. Preferably, use is made of air., The blowing process may be carried out at ambient pressure or elevated pressure. Normally, however, it will be carried out at ambient pressure.
S.°•Suitably, the catalytic blowing process is carried out over a period of time of less than 8 hours, preferably less than 4 hours.
15 Suitably, such blowing process is carried out at a temperature in the range of from 200 to 350'C, preferably in the range of from 250 to 300 0
C.
The bitumen to be oxidised may be a residue from distillation of crude oil, a cracked residue, an extract of a crude oil, a bitumen derived from propane bitumen, butane bitumen, pentane bitumen or mixtures thereof. Other suitable bitumens include mixtures of the above bitumen with extenders (fluxes) 20 such as petroleum extracts, eg. aromatic extracts, distillates or residues. Suitably, the bitumen to be oxidised has a penetration in the range of from 50 to 400dmm, preferably 100 to 300dmm, and more preferably 200 to 300dmm (as measured by ASTM D 5 at 25°C), and a softening point in the range of from 30 to 650C, preferably in the range of from 35 to 600C (as measured by ASTM D 36).
The penetration index (PI) of the oxidised bitumen is determined by means of its penetration and o 25 softening point as is well appreciated by the skilled person (see for instance The Shell Bitumen Handbook, 1991, pages 74 and The oxidised bitumen is mixed with a thermoplastic rubber. Suitably, the oxidised bitumen can be mixed with one or more different types of thermoplastic rubbers.
Although a wide range of thermoplastic rubbers can suitably be used in accordance with the present invention, the preferred thermoplastic rubbers comprise optionally hydrogenated block copolymers which comprise at least two terminal poly(monovinylaromatic hydrocarbon) blocks and at least one central poly(conjugated diene) block, forming a continuous network.
Preferably block copolymer constituents are selected from the group consisting of those of the formulae A(BA)m or (AB)nX, wherein A represents a block copolymer of predominantly poly(monovinylaromatic hydrocarbon), wherein B represents a block of predominantly poly(conjugated diene), wherein X represents the residue of a multivalent coupling agent and wherein n represents an integer 1, preferably and in represents an integer 1, preferably m is 1.
More preferably, the blocks A represent predominantly poly(styrene) blocks and the B blocks represent predominantly poly(butadiene) blocks or predominantly poly(isoprene) blocks. Multivalent coupling agents to be used include those commonly known in the art.
C06992 With the term "predominantly" is meant that the respective blocks A and P are mainly derived from monovinyl aromatic hydrocarbon monomers and conjugated diene monomers, which monomers may be mixed with other structurally related or non-related co-monomers, eg. monovinyl aromatic hydrocarbon monomers as main component and small amounts (up to 10%) of other monomers or butadiene mixed with isoprene or small amounts of styrene.
More preferably, the block copolymers contain pure poly(styrene)r pure poly(isoprene) or pure poly(butadiene) blocks, of which the poly(isoprene) or poly(butadiene) blocks may be selectively hydrogenated to at most a residual ethylenic unsaturation of 20%, more preferably less than 5% of its original unsaturation content prior to hydrogenation. Preferably, however, the block copolymers are not selectively hydrogenated. Most preferably, the applied block copolymer has the structure ABA, wherein A has an apparent molecular weight of from 3000 to 100 000, preferably from 5000 to 25 000 and the diblocks AB have an apparent molecular weight in the range of from 50 000 to 170 000. Preferably, the diblocks AB have-an apparent molecular weight in the range of from 70 000 to 120 000.
With the term "apparent molecular weight" as used throughout the specification is meant the 15 molecular weight of a polymer, as measured with gel permeation chromatography (GPC) using poly(styrene) calibration standards.
The originally prepared poly(conjugated diene) blocks usually contain from 5 to 65% by weight vinyl groups, originating from 1,2 polymerisation relative to the conjugated diene molecules, and preferably a vinyl content from 10 to 55% by weight.
20 The complete block copolymer to be used according to the present invention, is normally containing polymerised vinyl aromatic hydrocarbon monomers in an amount of from 10 to 60% by weight and preferably from 15 to 45% by weight.
The apparent molecular weight of the total block copolymer will normally be in the range of from 100 000 to 500 000 and preferably in the range! of from 250 000 to 450 000, and most preferably in the! 25 range of from 350 000 to 400 000.
As examples of suitable pure block copolymers can be mentioned KRATON G-1651, KRATON G- 1654, KRATON G-1657, KRATON G-1650, KRATON G-1701, KRATON D-1101, KRATON D-1102, KRATON D-1107, KRATON D-1111, KRATON D-1116, KRATON D-1117, KRATON D-1118, KRATON D- 1122, KRATON D-1135X, KRATON D-1184, KRATON D-1144X, KRATON D-1300X, KRATON D-4141 and KRATON D-4158 (KRATON is a trademark).
The present invention further provides a bitumen composition obtainable by any of the processes described hereinbefore. Such bitumen composition is very attractive since it displays both a good low temperature performance and a good high temperature rutting resistance.
Suitably, the bitumen composition has a penetration in the range of from 30 to 300dmm, preferably of from 100 to 200dmm (as measured by ASTM D 5 at 25"C), and a softening point in the range of 50 to 120 0 C, preferably of from 60 to 100 0 C (as measured by ASTM D 36).
Suitably, such bitumen composition has a G*/sin8-value of at least 1kPa (at 64 0 C) preferably in the range of from 1 to 2kPa (at 64°C), and a m-value of at least 0.30 (at preferably at least 0.33 (at (both the G*/sin 6-value and the m-value have been defined in Superpave Series No. 1 (SP-1), Asphalt Institute, which document is hereby incorporated by reference).
C06992 Fillers such as carbon black, silica and calcium carbonate, stabilisers, antioxidants, pigments, and solvents are known to be useful in bitumen compositions and can be incorporated in the bitumen compositions of this invention in concentrations taught in the art.
The present invention still further provides the use of a bitumen composition as described hereinbefore in an asphalt mixture for road applications.
The present invention will now be illustrated by means of the following Examples.
Example 1 An oxidised bitumen having a PI of 0.8 was obtained by subjecting a bitumen having a PI of -0.7 to a catalytic blowing process using phosphoric acid as catalyst, whereafter the blown bitumen obtained was mixed with a naphthenic flux. Said oxidised bitumen was then mixed at a temperature of 180 0 C and for 1 hour with 2% by weight of a non-hydrogenated radial polystyrene-polybutadiene-polystyrene block copolymer, based on total bitumen composition. The block copolymer had a 30%w styrene content, an apparent molecular weight of 380 000 and contained polystyrene-polybutadiene diblocks having an apparent molecular weight of 112 000. The main properties of the bitumen composition so obtained are 15 given in the upper part of Table 1.
The bitumen composition obtained was then subjected to the Rolling Thin film Oven Test (RTFOT, ASTM test method D 2572) whereafter it was further aged in a Pressure Ageing Vessel (PAV, AASHTO PP1). The main properties of the bitumen composition after these ageing tests are shown in the bottom part of Table 1.
20 Example 2 A process was carried out in a similar way as described in Example 1 except that a bitumen having a PI of -0.9 and which had not been subjected to an oxidation treatment was mixed with 4% by weight of the radial polystyrene-polybutadiene-polystyrene block copolymer, based on total bitumen composition.
The main properties of the non-oxidised bitumen composition so obtained are given in the upper part of 25 Table 1 The bitumen composition was then subjected to the Rolling Thin film Oven Test (ASTM test method D 2572) whereafter it was further aged in a Pressure Ageing Vessel (AASHTO PP1). The main properties of the bitumen composition after these ageing tests are shown in the bottom part of Table 1.
Table 1 Bitumen composition Example 1 Example 2 Before RTFOT/PAV Penetration at 25"C, dmm 151 113 Softening point °C 49.5 62.9 Viscosity at 135°C, Pa.s 0.764 0.818 G*/sin 6 at 640C, kPa 1.13 1.23 After RTFOT G*/sin 6 at 64*C, kPa 3.87 2.47 After RTFOT/PAV G* sin 6 at 19*C, kPa 2082 4094 Stiffness at -24*C, MPa 124 278 m-value at -24 0 C 0.333 0.317 C06992 From Table 1 it will be clear that the bitumen composition prepared in accordance with the present invention (Example 1) displays i) an improved high temperature rutting resistance (after RTFOT) and ii) an improved low temperature performance (after RTFOT/PAV) when compared with a bitumen composition falling outside the scope of the present invention (Example 2).
A finding which is especially surprising if one takes into account the fact that in Example 1 much less block copolymer is applied.
C06992
Claims (14)
1. Process for preparing a bitumen composition which comprises mixing at an elevated temperature an oxidised bitumen having a penetration index of at least 0 with a thermoplastic rubber which is present in an amount of less than 5%wt, based on total bitumen composition.
2. Process according to claim 1, wherein the bitumen has a penetration index of at most
3. Process according to claim 3, wherein the bitumen has a penetration index in the range of from 0 to 2.
4. Process according to any one of claims 1 to 3, wherein the thermoplastic rubber is present in an amount of less than 3%wt.
5. Process according to claim 4, wherein the thermoplastic rubber is present in an amount of 0.1 to
6. Process according to any one of claims 1 to 5, wherein the bitumen comprises a catalytically blown bitumen.
7. Process according to any one of claims 1 to 6, wherein the thermoplastic rubber comprises 15 an optionally hydrogenated block copolymer which comprises at least two terminal poly(monovinylaromatic hydrocarbon) blocks and at least one central poly(conjugated diene) block.
8. Process according to claim 7, wherein the block copolymer has the formulae A(BA)n or (AB)nX wherein A represents a block of predominantly poly(monovinyl aromatic hydrocarbon) and wherein B represents a block of predominantly poly(conjugated diene), wherein X represents the residue of a 20 multivalent coupling agent and wherein n is an integer of at least 1 and m is an integer of at least 1.
9. Process according to claim 8, wherein the A blocks are predominantly poly(styrene) block and the B blocks are predominantly poly(butadiene) blocks or predominantly poly(isoprene) blocks.
10. Process according to claim 8 or 9, wherein diblocks prepared from A and B have an apparent molecular weight in the range of from 50 000 to 170 000. 25
11. Process according to any one of claims 1 to 10, wherein the temperature is in the range of from 160 to 220°C.
12. Process for preparing a bitumen composition, substantially as hereinbefore described with reference to examplel but excluding the comparative example 2.
13. Bitumen composition obtainable by a process as defined in any one of claims 1 to 12.
14. Use of a bitumen composition as defined in claim 13 in an asphalt mixture for road applications. An asphalt mixture for road applications including or consisting of a bitumen composition as defined in claim 13. Dated 20 August 1999 SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B. V. Patent Attorneys for the ApplicantlNominated Person SPRUSON FERGUSON C06992