AU3391199A

AU3391199A - Dryformed fibrous web

Info

Publication number: AU3391199A
Application number: AU33911/99A
Authority: AU
Inventors: John Hardy Mosgaard Christensen; Helmut Erwin Schilkowski
Original assignee: Dan Web Machinery As
Current assignee: DAN-WEB MACHINERY AS
Priority date: 1994-01-07
Filing date: 1999-06-07
Publication date: 1999-08-19
Anticipated expiration: 2015-01-06
Also published as: AU742702B2

Description

S F Ref: 344158D1

AUSTRALIA

PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT

ORIGINAL

o ooooo: oeoo o Name and Address of Applicant: Scan-Web I/S Bryggervej 21 DK-8420 Risskov

DENMARK

John Hardy Mosgaard Schilkowski Actual Inventor(s): Christensen, Helmut Erwin Address for Service: Invention Title: Spruson Ferguson, Patent Attorneys Level 33 St Martins Tower, 31 Market Street Sydney, New South Wales, 2000, Australia Dryformed Fibrous Web The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5845 Dryformed Fibrous Web The present invention relates to a dryformed fibrous web material based on dryformed cellulose fibres with a suitable bonding. Also disclosed is a method for manufacturing the dryformed fibrous web. The laying out of the fibres for forming a current web is usually effected by a pulp material being defibrated and admixed into an airflow, which brings the loose fibres to a distributor head above a moving, perforated forming wire, underneath which is placed a suction chamber for down suction of the fibres against the wire, where they are currently deposited as a coherent fibrous pulp web with a desired web thickness. The products are typically used as liquid absorbing sheets.

It is important that the dryformed pulp web is stabilized or bonded, and in practice this is achieved in two different ways, viz. by application of binder dispersion or by use of binding fibres: 1. Binding: On a carrier wire the pulp web is passed through a binding station, in which, by means of a number of nozzles, a suitable binder dispersion, normally of the latex-type, is sprayed on the web, whereafter the wire is lead through a tunnel oven for drying out of the binder dispersion. Thereafter the web is transferred to an overhead wire, against which it is fixed by suction from above, so that the underside of the web is exposed, and the web is then lead through or over another binding station, where binder o* dispersion is correspondingly sprayed against this underside of the web. Thereafter the o 20 web is lead through yet a tunnel oven for drying out and final setting of the binder e dispersion, whereafter the web is self-supporting and can be wound up for storage or delivery.

By this method sheet webs of rather high quality is manufacturable, but as to machinery, the method is exacting and vulnerable to irregularities in the binding stations.

It is furthermore a limitation that the method is not suitable for thick sheet webs, as it is difficult to achieve a high penetration depth of the binder dispersion, whereby a relatively thick layer tends to segregate in the centre plane, where the bonding is weak or completely lacks. The products will typically contain about 85% cellulose fibres and about 15% binding agent. Typical weights of products can be 50-120 g/m 2 as heavier products easily delaminate. Furthermore the products are badly suited for containing superabsorbers.

2. Use of binding fibres: By this method a homogeneous admixture of heat actuated binding fibres, also named thermobonding fibres, into the cellulose fibres is produced, whereby the dryformed web material may be fixed solely by being lead through a heating zone. As to system and control, this is a more simple method, by which also thick webs are manufacturable, as the binding fibres will be evenly present in the outer as well as the inner planes of the material. The weight of product may typically be of 40-800 g/m 2 and a considerable admixing of superabsorbing agents or other additives is useable. The quality achievable is fully acceptable for many different applications, however, certain disadvantages occur in that already for economical reasons the admixing percentage of IN:\LIBFF]0402:SSD 2 thermobonding fibres has to be limited typically to about 15 percent. Normally the cellulose fibres range in lengths between 0.5 and approximately 5 mm, whereas heat thermobonding fibres are often 6 mm or longer. In practice this gives a very good bonding of the longest cellulose fibres, whereas the very short cellulose fibres are bonded incompletely. This means that the material can dust with short fibres, which is generally a profound disadvantage, and the products are therefore used mainly as insert materials in outer wrappings. Thus the dust nuisances may be eliminated outwardly, but in return they occur large-scale inside the plants, where the products are handled as insert material.

Here there must be used powerful exhausting systems, which themselves create problems, lo and to this must be added that the associated aspiration of the 'dust' implies a removal of a noticeable part of the original material, whereby this part is added completely in vain and thus represents an actual waste.

By the invention it is desired to counter the said fibre dusting, which naturally brings about speculations in a higher percentage of admixture of binder fibres with different lengths. However, this is hardly any realistic possibility, and by the invention it is realized that a better solution will be a combined use of the two said methods, however Swith the binder dispersion method in a modified form.

According to a broad form of the invention there is provided a dryformed paper web **material comprising cellulose fibres and thermobonding fibres and prepared so as to S 2o exhibit bonding of the fibres therein, characterized in that said bonding appears as a S combination of: heat activated thermobonding fibres present with generally even distribution throughout the thickness of the web, and a surface disposition of a binding agent in an amount of 0.5-20 g per square metre at least at one side of the web.

Throughout the specification and claims, the term "binder dispersion" is to be taken as meaning a dispersion of binding agent in a carrier.

As mentioned, by the binding method a bonding result is achieved, which will be best at the web surface and poorer at the centre layer of the web, but if, by a combined application of the thermobonding binding fibres it is only a question of sealing against dusting from the web, this will be achievable by coating the web with very thin surface layers of binder dispersion. As the coherence in the web material will be secured by the activating of the thermobonding bonding fibres, a surface binder dispersion will be applicable simultaneously on both sides of the already self supporting web, and both of the applied binder dispersion layers, which, both of them, can be extremely thin, will be hardenable by passing through a single additional heating zone with relatively low capacity. When the surfaces of the web material thus appear with thin binder agent bondings, a sealing against extrusion of the short cellulose fibres from the web material is effected, and this is exactly the result desired. This implying that by the invention there will be no speculations in any increased local bonding of said fibres, though the effect [N:\LIBFF]0402:SSD may partly depend on the very occurrence of increased fibre bindings in the surface, whereas it is to a less degree a question of an actual coating of the surface.

It is thus a main feature of the invention that in the fibre bonding use is made of the admixed thermobonding fibres, whereas the web surfaces are sealed in more or less degree by adding binder dispersion in modest amounts, without ambition of any deep penetration of the binder dispersion into the material. It is then not decisive how the binder dispersion is applied, but to the invention, however, it is an important sub aspect to indicate how the binder dispersion can be applied in a new and very economical way for achieving the desired result.

Thus, according to the invention it is a preferred possibility that the binder dispersion is applied in a foamed condition, whereby it may cover the surfaces with a minimum of dry matter therein. The effect has been observed that the liquid in the settling foam preferably settles in the intercrossing areas between the fibres rather than by a general settlement on the surfaces of the fibres, and this effect is optimum for the desired result, viz. that by use of small amounts of both liquid and dry matter a bonding of the short fibres in the surface be made, so that these partly remain in place and partly assist in sealing against extrusion of the short and unbonded fibres from the inside of the web material. This remains light and porous, so that for instance it will be suited for impregnated moisture tissues.

A good effect is achievable by admixing only 1-2 g of binding agent per m 2 per side, using a waterdispersed foamed binder dispersion with only approximately 2 g dry •pulp per liter foam. The foam may be generated in a conventional foaming unit, and in the foamed volume the binding agent may then be present in an amount of only some 0.2 volume percent. Correspondingly, there will be very little water to be dried out from the product, whereby the drying and the hardening of the binder dispersion may be effected with a rather low energy consumption in the aftercoupled hardening zone.

The application of the foam may be effected in any suitable way, for instance by vertical, sloping or horizontal feed of the web through mating rollers, with controlled •.foam supply to the roller gap on both sides of the web. A rolling process of the web gives an attractive result in that the surface fibres will be bonded in couched positions, whereby the surface gets a more smooth and firm character.

By means of admixed moisturing agents it is possible to control the penetration depth of the prefoamed binder dispersion. If the penetration depth is too little, the thin bonding layer in the surface will soon be abraised, and if the depth is too large, this will partly imply an unnecessary large consumption of binder dispersion and partly give the product a plastics-like character, with sluggish water absorption.

As mentioned above, the binder dispersion can dry out and be hardened at a low energy consumption, but it can, however, take place at such a high temperature that the bonding fibres can be reactivated, and as explained further below, this can give the most [N:\LIBFF]O402:SSD extraordinary result that the tensile strength of the web can be increased to nearly the double.

The invention gives significant results as regards planning of manufacturing of products with desired qualifications, without said qualifications being altered by a successive extrusion of the short fibres from the products. As this fibre amount may be of a noticeable size, the associated result will be that it is possible to dispose in a far better way for achieving the desired qualifications of the finished product.

The invention is in a preferred embodiment shown schematically in the drawing.

In the drawing a forming wire 2 is shown having a conveying stretch 4 below a pair of distributor heads 6 for supplying a mixture of loose cellulose fibres and heat thermobonding fibres to the stretch 4, on which is thus formed a loose web 8. The latter is compressed between rollers 10 and then transferred to a transport wire 12 via an overhead transfer station 14. The wire 12 brings the web through a heating zone 16, in which the thermobonding fibres are activated for bonding of the cellulose fibres, normally at a temperature of 130-140'C. Thereafter, the now stabilised and self-supporting web is taken through mating rollers 18. Conventionally the web, now as a product web, is .ooo.i Shereafter taken to upwinding in rolls 34 of finished products.

o• i By the invention, however, a station 20 is after-coupled, in which the web 22, at both sides, is provided with a binder dispersion foam, preferably by the web being led 20 down around a diversion roller 24 down to a so-called foulard-unit consisting of a pair of rollers 26 placed with adjustable spacing and with non-illustrated, upper means for adding impregnating compound 28 to the upper roller gap at both sides of the lead down web 22.

It is thus possible to control the supply of impregnating compound partly by adjusting the mating gap and partly by regulating the flow of the compound to a higher or lower level above the roller gap, for instance within a regulating range of 2-20 cm.

Besides, the supply may in this case be adjusted by the contents of dry matter in the binder dispersion agent (as an example within 5-15%) and by adjusting the foam density, for instance within the interval 20-100 g/l.

hardness/softness of the product may be controlled by choice of a binder agent with a hard or soft film, respectively, whereas the hydrophile/hydrophobe qualities of the product may be controlled by means of suitable prefoaming agents or additives.

Having passed the unit 20 the web 22 is taken onto a belt 30 through a heating tunnel 32, in which the web, preferably by means of added hot air, is heated to a quick evaporation of the aqueous part of the foam 28, whereafter the web is reeled up in the usual delivery roll 34.

Surprisingly, it has proved that by use of a suitable high temperature in the tunnel oven 32, preferably 130-140'C, there is achieved not only an efficient water evaporation, but furthermore an improvement of the tensile strength of the web product of a whole 100%. This can not be explained from the very modest supply of binder dispersion at the outer sides of the web 22, but from other circumstances, however: [N:\LIBFFIO402:SSD M I M When the web 8 passes the rollers 10 it is pressed down against the carrier wire 2, which is normally a woven grid wire made of intersecting threads, which, by way of the associated intersections will form local, upwardly protruding and depressed parts, respectively. At the protruding parts the fibres in the web will be extra compressed when passing the rollers 10, so that the fibres as hereby locally depressed will be extra sensitive to the welding-effect occurring in the heating zone 16. However, this condition is weakened in that the web, while passing the transfer unit 14 is loosened somewhat, influenced by the weak tractive force and web movement, which is necessary for taking of the web from the forming wire and transferring it to the transfer wire, just as a corresponding loosening will occur at the transfer from the transfer wire to the oven wire.

Besides, the compressed web has a certain expansion power, and thus the originally well depressed fibres will not be all to well depressed when passing the hardening tunnel 16.

However, when the web 22 thereafter passes the station 20, a new compression of the web and a certain increase of the coherence in the surface layers of the web will occur, so that during the following passage through the oven unit 32 not only the said evaporation of the water from the foamed binder dispersion, but also a renewed heat activating of the thermobonding fibres will be provoked, as preferably there is operated with approximately the same temperature as in the tunnel 16, for instance approximately 140oC.

20 Thus the binder dispersion treatment of the web will be some kind of catalyzer for S the achievement of a following significantly increased tensile strength of the web material.

The immediate result of the invention, viz. the bonding or the sealing of the 'dust fibres' under maintenance of a non-sealed surface is advantageous also in another way, as a retained amount of said fibres just within the fixed surface layers has a significant fluid 25 spreading effect, which is of great importance in absorbing products. In many of these products it is almost known beforehand that the liquid supply during use will only appear at a sub area of the product, and for a desired absorbing capacity a superabsorbent has to be dosed in consideration of this. If the product can appear with a good distribution ability, the dosing of the superabsorbent can be minimized.

There is reason to stress that the aqueous foam can be added on both sides of a product having a centre layer of a superabsorbent material without said material having to become activated with water. For example, the product may have a fibre bottom layer of g/m 2 an intermediate layer of superabsorbent of 30 g/m 2 and a fibre top layer of g/m 2 The invention is advantageous also as far as filter materials are concerned, where both the significantly reduced dusting and the sustained content of short fibres is of a positive effect.

It is by the invention possible to use the bonding foam as carrier for colouring pigments, these being added before the foaming, whereby a certain dyeing of the products can be produced in a most simple way. However, as the binder agent is normally used in [N:\LIBFF]0402:SSD very modest amounts, only dyeing in pastel colours is achievable, unless the process is specifically adapted with respect to a more powerful dyeing.

By the invention it has proved possible to foam-coat a thermally bonded air laid product which only contains some few percents of binding fibres, for instance by application of an increased amount of binder dispersion, for instance 10%, whereby it is possible to manufacture a predominantly 'latex-bonded' product without the binder dispersion having to be added by the traditional spraying technique. Hereby the same abrasive resistant surface is achieved as by traditional binder dispersion spraying, but without the associated limitation of the maximum thickness of the web, which usually lies at 100/120 g/m 2 At such thicknesses it has been necessary to impregnate the web in order to avoid delamination of the product, but this is not necessary in the present situation, and this means, inter alia, that products with rather low density can be manufactured. According to the invention, in working with a significantly reduced amount of binder dispersion, thick products will hold a noticeably increased amount of cellulose fibres not covered by a film of binder dispersion and thus having optimum absorption abilities.

From a process point of view it is advantageous that the application of the binder Sodispersion is effected at only one place in the system and not at two places as in the prior art. Moreover, it is most advantageous to avoid the traditional spraying stations, which give rise to many problems with respect to both operation and maintenance, while e.g. a S foulard provides for a good and even treating result and is easy to maintain. However, other foam application techniques could be used, e.g. the so-called screen coating.

In principle, nothing prevents the binder dispersion foam from being applied to the web already before the same is thermally fixed, and in that case it may be sufficient to use 25 a single succeeding heating zone for the actuation of both the binding fibres and the **binding agent.

Examples Finally a couple of examples of manufacture of specific products according to the invention should be given: A. Production of a foam coated, hydrophile product.

An air laid product, 60 g/m 2 consisting of 85% wooden cellulose fibres with largest possible content of long fibres and 15% thermobonding fibres, is foam coated in a foulard, the roller gap of which is adjusted to 0.6 mm. The prefoamed binder is produced in the following way: Binder mix specification: 11.1% Sarpifan WRG (Stockhausen, DE) 0.2% Rohagal 10 n (Rhm GmbH, DE) 88.7% Water The binder is foamed to a density of 20 g/l.

IN:\LIBFFIO402:SSD If the foam level in the foulard is about 4 cm, approximately 1.5 g binder (100% drystuff) each m 2 at each side of the product is added.

After the foam coating, the product is dryed in a normal way, for instance at 140 0

C.

B. Manufacturing of a foam coated, hydrophobe product.

The product is manufactured in the same way as mentioned above, but with a different binder mix specification: Binder mix specification: 11.1% Sarpifan WRG (Stockhausen, DE) Stokal STA (Stockhausen, DE) 86.9 Water 0* [N:\LIBFF]0402:SSD

Claims

2. A web material according to claim 1, consisting of a mixture of 75-90% by o weight cellulose fibres and 10-25 thermobonding fibres, the binding agent being present in an amount of 0.5-10 g per square metre.
3. A web material according to claim 1, consisting of a mixture of 93-97% by weight cellulose fibres and 3-7% thermobonding fibres, the binding agent being present in an amount of 5-20 g per square metre.
4. A web material according to claim 1, in which the binding agent is present in an amount of 1-2 g per square metre.
5. A web material according to any one of claims 1-4, appearing as an outer ooooo layer in a laminated product. **o A web material according to claim 5, in which the binding agent is the dry 0 20 product of an aqueous binder dispersion, said laminate containing a super absorbent material.
7. A web material according to any one of claims 1-6, in which the binding agent o is pigmented.
8. A dryformed paper web material, substantially as herein described with reference to any one of the Examples.
9. A dryformed paper web material, substantially as herein described with reference to the drawing.
10. Method for manufacturing a dryformed paper material by successive laying of a web of cellulose fibres on a forming wire and treating the web to provide bonding of the fibres therein, characterised in that the binding of the fibres is effected by a combination of an activating of thermobonding fibres supplied by previous admixing into the cellulose fibres and an application of binder dispersion to the surfaces of the web, this application being conducted with a dry matter part of the binder dispersion significantly below by weight, for bonding of short cellulose fibres at the surface.
11. Method for manufacturing a dryformed paper material by successive laying of a web of cellulose fibres on a forming wire and treating the web to provide bonding of the fibres therein, characterized in that the binding of the fibres is effected by a combination of a heat activating of thermobonding fibres supplied by previous admixing into the cellulose fibres and an application of a binder dispersion to the surfaces of the web, this application being conducted with a dry matter part of the binder dispersion significantly IN:\LIBFFIO402:SSD below 15 by weight for bonding of short cellulose fibres at the surfaces, the binder dispersion being applied in an amount of 0.5-20 g dry matter per square metre web surface.
12. A method according to claim 10 or 11, wherein the dry matter part is 0.5-5% by weight of the binder dispersion.
13. A method according to any one of claims 10 to 12, characterized in that the binder dispersion is applied in an amount of 0.5-10 g dry matter per square metre web surface.
14. A method according to claim 10, characterized in that the binder dispersion is applied to the surface of the web after the web is stabilized by thermal activating of the thermobonding fibres, and the binder dispersion is hardened by running-through heating of the web at such a high temperature that the thermobonding fibres are reactivated. A method according to any one of claims 10 to 14, characterized in that the binder dispersion is applied in foamed condition, i.e. with water/air as carrier.
16. A method according to claim 15, characterized in that the web material, despite the application of the binder dispersion in foamed condition, is manufactured with one or more centre layers containing or consisting of superabsorbent material.
17. A method according to any one of claims 10 to 16, characterized in that the •binder dispersion is used in admixture with pigments. 20 18. A method according to claim 10, characterized in that for manufacturing of a o predominantly termally bonded material use is made of a web with 10-25% by weight to* thermobonding fibres and a binder dispersion dosage of 0.5-10 g dry matter per square metre web surface.
19. A method according to claim 10, characterized in that for manufacturing of a 25 predominantly binding agent bonded material use is made of a web with 3-7% by weight thermobonding fibres and a binder dispersion dosage of 5-20 g dry matter per square meter web surface.
20. A method for manufacturing a dryformed paper material by successive inlaying of a web of cellulose fibres on a forming wire and treating the web to provide bonding of the fibres therein, which method is substantially as herein described with reference to Example A or B.
21. An apparatus for carrying out the method according to claim 10, comprising a device for dry-laying of the fibres on a forming wire for forming of a fibrous web and a device for actuation of means for bonding of the fibres, characterized by the combination of the device for dry-laying of the fibres being of the type which operates based on fibres with admixed thermobonding fibres, whereby the actuation device is a heating zone, and by the presence of a station for application of small amounts of binder dispersion to the surfaces of the web, viz. so as to make the finished web material mainly non-dusting.
22. An apparatus according to claim 21, including means for drying the web. [N:\LIBFF]O402:SSD
23. An apparatus according to claim 21 or 22, characterized in the binder dispersion station comprising means such as a foulard for application of the binder dispersion in foamed condition.
24. An apparatus for manufacturing a dryformed paper material by successive inlaying of a web of cellulose fibres on a forming wire and treating the web to provide bonding of the fibres therein, which apparatus is substantially as herein described with reference to the drawing. A dryformed paper web material obtained by the method according to claim 11, comprising cellulose fibres and thermobonding fibres and prepared so as to exhibit o bonding of the fibres therein, characterized in that said bonding appears as a combination of: heat activated thermobonding fibres present with generally even distribution throughout the thickness of the web, and a surface disposition of a binding agent in an amount of 0.5-20 g per square metre at least at one side of the web.
26. A web material according to claim 25, consisting of a mixture of 75-90% by Sweight cellulose fibres and 10-25 thermobonding fibres, the binding agent being present in an amount of 0.5-10 g per square metre.
27. A web material according to claim 25, consisting of a mixture of 93-97% by 6 e 20 weight cellulose fibres and 3-7% thermobonding fibres, the binding agent being present in an amount of 5-20 g per square metre.
28. A web material according to claim 25, in which the binding agent is present in an amount of 1-2 g per square metre.
29. A web material according to any one of claims 25 to 28, appearing as an outer Og. 25 layer in a laminated product. OSO ~30. A web material according to claim 20, in which the binding agent is the dry product of an aqueous binder dispersion, said laminate containing a super absorbent material.
31. A web material according to any one of claims 25 to 30, in which the binding agent is pigmented.
32. A dryformed paper web material produced by the method of any one of claims to Dated 15 March 1999 Scan-Web I/S Patent Attorneys for the Applicant/Nominated Person SPRUSON FERGUSON [N:\LIBFFO402:SSD