AU2696099A - Medium modulus film comprising substantially linear polyethylene and fabrication method - Google Patents

Description

S F Ref: 356959D1

AUSTRALIA

PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT

ORIGINAL

Name and Address of Applicant: The Dow Chemical 2030 Dow Center, Midland Michigan UNITED STATES OF Company Abbott Road 48640

AMERICA

Actual Inventor(s): Address for Service: Invention Title: Jeffrey J. Wooster, Brad A. Cobler, Larry D. Cady, David G. Bertelsman, Lisa E. Dodson and Osborne K.

McKinney Spruson Ferguson, Patent Attorneys Level 33 St Martins Tower, 31 Market Street Sydney, New South Wales, 2000, Australia Medium Modulus Film Comprising Substantially Linear Polyethylene and Fabrication Method The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5845 MEDIUM MODULUS FILM COMPRISING SUBSTANTIALLY LINEAR POLYETHYLENE AND FABRICATION METHOD This invention pertains to a medium modulus polyethylene film and a method for preparing such film. The novel film can be prepared by variable-stalk blown extrusion. The film has surprisingly high tear and impact properties. The film can be used in heavy-duty packaging and shipping applications and also in hot-fill packaging applications.

Polyethylene films with tear and impact properties are needed for packaging and shipping heavy items, such as building and construction materials, lawn and garden materials, salt, polymer pellets. Heavy-duty films and bags must also possess good rigidity and stiffness (modulus).

Good film strength properties are required to prevent bag ruptures and product losses during distribution while the rigidity and stiffness provide good dimensional stability. Dimensional stability is important during fabrication and packaging operations because it assists in maintaining the correct positioning of the film or bag as it is conveyed through the various equipment stations during bag-making and product-filling operational steps. Dimensional stability at elevated temperatures during the productfilling step is also required in some instances when the product (for example, salt) is packaged hot such as, for example, in some form-fill-seal packaging operations.

Heavy-duty packaging currently involves monolayer and multilayer polyethylene films having a calculated film density as low as about 0.920 g/cc. Typical polyethylene film compositions for heavy-duty packaging include blends of linear low density polyethylene (LLDPE) with low density polyethylene (LDPE), high density polyethylene (HDPE) modified by adding rubber and other elastomers for example, polybutylene) to impart impact resistance, LLDPE blended with a low molecular weight, high density polyethylene (LMW-HDPE), LLDPE blended with a high melt flow rate HDPE, or LLDPE blended with partially isotactic polymers.

See, for example, US Patent 5,041,401 by Shirodkar et al., US Patent 5,102,955 by Calabro et al. and US Patent 4,828,906 by Nishimura et al. Also known is the polyethylene composition disclosed by Thiersault et al. in US Patent 4,786,688 which contains 80 to 98 percent by weight HDPE and 2 to 20 percent by weight LLDPE which is alleged to be useful for thin film (20 microns) and blow molding applications. Additionally, ternary polymer blends have been used in this packaging application. For example, in US Patent 4,824,912, Su et al. disclose LLDPE blended with minor amounts of a low molecular weight HDPE (LMW-HDPE) and a high molecular weight HDPE (HMW- HDPE) for processability and film property improvements over LLDPE used alone.

The prior art shows that the linear ethylene polymers currently used in making polyethylene films provide increased tear strength as density increases to about 0.920 g/cc and then show substantially lower tear strengths as density increases above about 0.920 g/cc. Attempts to improve tear strength by increasing film thickness have been only marginally effective. When film thickness is increased to improve strength properties, the rigidity of present art polyethylene films increases disproportionately to impact and tear resistance properties, and thereby thicker films offer practitioners little or no additional benefit. Thus, although a variety of polyethylene films and film compositions are known, prior art polyethylene films are not completely satisfactory for use in heavy-duty packaging applications because they do not offer the desired balance of high tear and impact resistance at the required film rigidity or modulus and/or they do not have the desired dimensional stability.

Hence, it is an object of the present invention to provide a polyethylene film with improved tear strength and impact resistance and good dimensional stability, as well as a method for making the same, which can be used in heavy-duty packaging and shipping applications and for use in hot fill packaging applications.

Applicants have discovered a.n-,ovel medium modulus, -polyethylene blown film having good impact and tear strengths, and a method for preparing such film. The novel film comprises: from 60 to 95 weight percent, based the combined weights of components and of at least one high molecular weight linear ethylene polymer having a density in the range of 0.92 to 0.96 g/cc and an Is melt index in the range of 0.1 to 3 minutes, and from 5 to 40 weight percent, based on the combined weights of components and of at least one substantially linear ethylene/a-olefin interpolymer characterized as having: i. a melt flow ratio, I10/I2, 5.63, and ii. a molecular weight distribution, Mw/Mn, defined by the equation: Mw/Mn 5 (110/12) 4.63 wherein the substantially linear ethylene/oc-olefin interpolymer is further characterized as containing at least one a-olefin monomer and having a density in the range of 0.85 to 0.92 g/cc and an 12 melt index in the range of 0.3 to 3 minutes.

The novel method for producing such medium modulus polyethylene film is a variable-stalk extrusion process which comprises the steps of: providing an extrudable thermoplastic composition containing from to 95 weight percent, based on the combined weights of components and of at least one high weight molecular linear ethylene polymer having a density in the range of 0.92 to 0.96g/cc and an 15 melt index in the range of 0.1 to 3g/10 minutes, and from to 40 weight percent, based on the combined weights of components and of at least one substantially linear ethylene/ca-olefin interpolymer characterised as having: i. a melt flow ratio, I10/I2, >5.63, and ii. a molecular weight distribution, Mw/Mn, defined by the equation:

M,/M

n (110/12) 4.63 wherein the substantially linear ethylene/a-olefin interpolymer is further characterised as containing at least one a-olefin monomer and having a density in the range of 0.85 to 0.92g/cc and an 12 melt index in the range of 0.3 to 3g/10 minutes.

introducing said composition of step into a film extrusion apparatus equipped with an annular die, extruding said composition of step to form a tube that is subsequently blown-up and drawn-down through nip and take-off rollers to form a layflat film with a thickness greater than about 31 p.m and [N:\LUBC1356959:MEF conveying said film formed in step for subsequent use down-line of the film extrusion apparatus of step or collecting said film formed in step for subsequent use off-line.

The film of the present invention has improved tear and impact performance that is not ordinarily expected for medium modulus, polyethylene films. The novel films have at least a 30 percent, and preferably 50 percent, improvement in impact and tear properties relative to prior art polyethylene films having about the same film density, melt index and thickness. The benefit of the higher performing novel film is practitioners can now meet specified heavy-duty film requirements at substantially lower costs by down-gauging and/or by using higher diluent and recycled material loadings.

Figure 1 plots data describing the relationship between Mw/M n and 110/12 for three distinct polymer types: substantially linear polyethylene, heterogeneous linear polyethylene and homogeneous linear polyethylene.

Figures 2-4 are used to graphically summarize data presented in the Examples.

Figure 2 plots the relationship between tear strength and film thickness for Inventive Films and Comparative Films. Inventive Films are prepared from Film Compositions A, B and C and Comparative Films are prepared from Film Compositions D, E and F.

Figure 3 plots the relationship between impact resistance at 3 mils and measured film density for Inventive Films and Comparative Films. Inventive Films are prepared from Film Composition G-J and P-V. Comparative Films are prepared from Film Compositions F. L, M,and N.

Figure 4 plots the relationship between tear strength at 76 tm and measured film density for Inventive Films and both actual and predicted IN:\LIBCi356959:MEF Comparative Films. Inventive Films are prepared from Film Composition G, H and I. Comparative Films are prepared from Film Compositions E, F and K-O. The calculated or predicted tear strengths of comparative blend compositions are based on a 0.951 g/cc HMW-HDPE and a 0.870 g/cc SLEP at various ratios.

"Substantially linear ethylene polymer" (SLEP) herein designates an ethylene polymer having a polymer back-bone that is substituted with from 0.01 long chain branches/1000 carbons to 3 long chain branches/1000 carbons, more preferably from 0.01 long chain branches/1000 carb6ns to 1 long chain branches/1000 carbons, and especially from 0.05 long chain branches/1000 carbons to 1 long chain branches/1000 carbons.

"Long chain branching" is defined herein as a chain length of at least 6 carbons, above which the length cannot be distinguished using 13 C nuclear magnetic resonance spectroscopy. The long chain branch can be as long as about the same length as the length of the polymer bac-bone.

Long chain branching is determined by using 13C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method described by Randall (Rev. Macromol. Chem. Phys., C29, V. 2&3, p. 285-297).

The terms "ultra low density polyethylene" (ULDPE), "very low density polyethylene" (VLDPE) and "linear very low density polyethylene" (LVLDPE) have been used interchangeably in the polyethylene art to designate the polymer subset of linear low density polyethylenes having a density less than or equal to about 0.915 g/cc. The term "linear low density polyethylene" (LLDPE) is then applied to those linear polyethylenes having a density above about 0.915 g/cc.

The terms "heterogeneous" and "heterogeneously branched" are used herein in the conventional sense in reference to a linear ethylene/aolefin polymer having a comparatively low short chain branching distribution index. The short chain branching distribution index (SCBDI) is defined as the weight percent of the polymer molecules having a comonomer content within 50 percent of the median total molar comonomer content. The short chain branching distribution index of polyolefins can be determined by well-known temperature rising elution fractionation techniques, such as those described by Wild et al., Journal of Polymer Science, Poly. Phys. Ed., Vol. 20, p.441 (1982), L.D. Cady, "The Role of Comonomer Type and Distribution in LLDPE Product Performance," SPE Regional Technical Conference, Quaker Square Hilton, Akron, Ohio, October 1-2, pp. 107-119 (1985), or US Patent 4,798,081. Heterogeneous linear ethylene/a-olefin polymers typically have a SCBDI less than about 30 percent.

The terms "homogeneous" and "homogeneously branched" are used herein in the conventional sense in reference to an ethylene/a-olefin polymer having a comparatively high short chain branching distribution index (SCBDI) as determined by well-known temperature rising elution fractionation techniques. Homogeneous ethylene/ca-olefin polymers typically have a SCBDI greater than or equal to about 30 percent.

The term "medium modulus" is used herein in reference to the novel film to mean the calculated film density is in the range of 0.923 to 0.95g/cc. The term "calculated film density" is used herein to mean the density of film when calculated from the known weight fractions and the measured annealed densities of the component polymers or layers.

The term "thick" is used herein in reference to the novel film to mean a film thickness greater than about 31tm.

The term "variable-stalk extrusion" is a new term of art used herein to express the distance between the annular film die and stalk height or bubble expansion point which can be varied from 0 centimeters to IN:\LIBC1356959:MEF greater than 366 centimeters during blown film fabrication. The term includes both wellknown pocket blown film extrusion and stalk blown film extrusion. The term "high stalk extrusion" is used herein in the conventional sense to mean a distance between the annular film die and the air ring that is greater than or equal to 76 centimeter. The term "low stalk extrusion" is used herein in the conventional sense to mean a distance in the range of 12.7 centimeters to 76 centimeters.

The term "hot-fill" herein refers to a packaging or product-filling operation where the product temperature is greater than 45°C. The term "heavy-duty" herein refers generally to industrial items packaged in bulk or having a single-package weight greater than 4.5 kilograms.

The density of the polymers used to make the medium modulus film of the present invention is measured in accordance with ASTM D-792 and is reported as grams/cubic centimeter The measurements reported in the Examples below are determined after the polymer samples have been annealed for 24 hours at ambient conditions.

Melt index measurements are performed according to ASTM D-1238, Condition 190°C/2.16kg and Condition 190°C/5kg, and are known as 12 and I5, respectively. Melt index is inversely proportional to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt index, although the relationship is not linear.

Melt index is reported as g/10 minutes. For purposes of this invention, in calculating certain values in the Examples, 15 and 12 values roughly relate to one another by a factor of about 5.1; for example, a 1.012 index melt is equivalent to about a 5.115 melt index.

Melt index determinations can also be performed with even higher weights, such as in accordance with ASTM IN:\LIBC1356959:MEF D-1238, Condition 190'C/10kg and Condition 190°C/21.6kg, and are known as I10 and 121.6, respectively.

The term "melt flow ratio" is defined herein in the conventional sense as the ratio of a higher weight melt index determination to a lower weight determination. For measured I10 and 12 melt index values, the melt flow ratio is conveniently designated as 110/I2. For 121 6 and 110 values, the ratio is designated I21.6/I10. Other melt flow ratios are occasionally used respecting polyethylene compositions, such as, for example, 15/12 based on 15 and 12 melt index measurements. In general, 121.6/110 and 15/12 determinations provide similar melt flow values and 110/I2 values are usually greater than 121.6/110 values by a factor of about 4.4 and this factor is used for purposes of this invention in calculating certain values in the Examples.

The tear resistance of the film of the present invention is measured in accordance with ASTM D1922 and is reported in grams. Tear resistance in measured both the machine direction (MD) and in the cross direction The term "tear strength" is used herein to represent the average between MD and CD tear resistance values and, likewise, is reported in grams. The impact resistance of the film of the instant invention is measured in accordance with ASTM D1709. Where indicated and according to the relationship of higher thicknesses yield increased performance values, tear and impact results are normalized to exactly 76jtm by proportionate increases or decreases based on actual measured (micrometer) film thickness; however, such normalization calculations are only performed and reported where thickness variations are less than 10 percent, that is, where the measured thickness is in the range of 68 to 84 tm.

The medium modulus, polyethylene film of the present invention has a calculated film density in the range of 0.923g/cc to 0.95g/cc, (N:\LIBC1356959:MEF especially, 0.926g/cc to 0.948g/cc, and more especially, 0.93g/cc to 0.945g/cc.

The a film thickness is generally greater than about 3 1 m, especially, in the range of 38itm to 222gtm, and more especially, in the range of 50|Jm to 203ptm.

These novel films have tear strength or, alternately, impact resistance, at least percent greater than the tear strength or impact resistance of a comparative prior art polyethylene film having about the same film density, melt index and film thickness.

The tear strength of the novel film is also characterized by the following equation: tear strength (grams) Ax Bx 2

C

where A, B and C are numerical values and x is film thickness; when A is less than or equal to about 150, B is greater than or equal to about 12.5, preferably greater than or equal to about 13.5, and more preferably greater than or equal to about 14.5; and when A is greater than about 150, B is in the range of -80 to 40, preferably -70 to 20, and more preferably -60 to 0. For example, the expression 307.18x 26.219x 2 98.134 is thought to represent the tear strength of the film of the present invention, whereas the expression 138.22x 4.8116x 2 19.364 does not.

The strength of the novel film can be alternately characterized by the following equation: tear strength (grams) Ax 2 Bx C where A, B and C are numerical values and x is measured film density wherein A is greater than or equal to 1.5 x 106, preferably greater than or equal to 1.7 x 106 and B is greater than or equal to 2.75 x 106, preferably greater than or equal to 3.0 x 106. For example, the following expression is representative of 30 percent greater tear strength than a comparative IN:\LIBC1356959:MEF

I

polyethylene film having about the same melt index, film density and thickness: tear strength (grams) 1.565 x 10 6 (x 2 2.971 x 10 6 1.41 x 106.

The film can be even further or alternately characterized by the following equation: impact resistance (grams) Ax 2 Bx C where A, B and C are numerical values and x is measured film density where A is greater than or equal to 1.4 x 106, preferably gre r than or equal to 1.5 x 106 and B is greater than or equal to 2.5 x 106, preferably greater than or equal to 2.75 x 106. For example, the following expression is representative of 30 percent greater impact resistance than a comparative polyethylene film having about the same melt index, film density and thickness: impact resistance (grams) 1.415 x 10 6 (x 2 2.676 x 106(x) 1.265 x 106.

This novel film can be conveniently formed into bags and is useful in heavy-duty packaging and shipping applications as well as in hot-fill packaging applications where films with a good property balance, that is, high strength and medium modulus with good tear, impact and dimensional stability, are needed.

The high molecular weight linear ethylene polymers, Component for use in preparing the medium modulus, polyethylene film of the instant invention are a known class of compounds which can be produced by any well-known particle-form polymerization process, such as slurry polymerization and gas phase polymerization. Preferably, the high molecular weight linear ethylene polymers are produced using well-known Phillips or Ziegler type coordination catalysts, although metallocene catalyst systems can also be used. Although preferred, with conventional Ziegler type catalysts, slurry polymerization processes are generally limited to polymer densities greater than about 0.940 g/cc and especially limited to polymer densities greater than about 0.935 g/cc, that is, about 0.935 g/cc is the practical lower commercial limit for slurry polymerization.

The high molecular weight linear ethylene polymer can be an ethylene homopolymer or a copolymer of ethylene with at least one a-olefin of from 3 to 20 carbon atoms. However, preferably, the high molecular weight linear polymer is a copolymer with at least one C 3

-C

20 a-olefin, such as 1-propylene, 1-butene, 1-isobutylene, 4-methyl-l-pentene, 1-hexene, 1heptene and 1-octene. Most preferably, the high molecular weight linear ethylene polymer is an ethylene/1-butene copolymer prepared by a low pressure slurry polymerization process. The novel film comprises from to 95 weight percent high molecular weight linear ethylene polymer, preferably 65 to 90 weight percent, and more preferably 70 to 85 weight percent.

Component can also be a blend of linear ethylene polymers. Such blends can be prepared in-situ for example, by having a mixture of catalysts in a single polymerization reactor or by using different catalysts in separate reactors connected in parallel or in series) or by physical blending of polymers.

The high molecular weight linear ethylene polymer has an 15 melt index in the range of 0.1 g/10 minutes to 3 g/10, preferably, 0.1 minutes to 2 g/10 minutes and, more preferably, 0.15 g/10 minutes to 1 minutes. Additionally, the linear polymer preferably has a bimodal molecular weight distribution (MWD) and an 121.6/110 ratio in the range of from 1 to 12, preferably in the range of from 3.5 to 10, more preferably in the range of from 4 to 8, and most preferably in the range of from 4.5 to 6.

The high molecular weight linear ethylene polymer, which includes, but is not limited to, LLDPE, LMDPE and HDPE, and mixtures thereof, preferably has a density in the range of from 0.92 g/cc to 0.96 g/cc, more preferably, in the range of from 0.93 g/cc to 0.96 g/cc, and most preferably, in the range of from 0.935 g/cc to 0.958 g/c:.

The substantially linear ethylene/a -olefin polymers used in the present invention Component are a unique class of compounds that are defined in US 5,272,236 and US Patent 5,278,272 by Lai et al. Lai et al. teach that such polymers are preferably prepared by a continuous, solution phase polymerization process using the constrained geometry catalyst discovered by Stevens et al. US Patent 5,055,438. The substantially linear ethylene/aolefin interpolymers contain ethylene interpolymerized with at least one

C

3

-C

20 a-olefin, such as 1-propylene, 1-butene, 1-isobutylene, 1-hexene, 4methyl-1-pentene, 1-heptene and 1-octene, as well as other monomer types such as styrene, halo- or alkyl-substituted styrenes, tetrafluoro-ethylene, vinyl benzocyclo-butane, 1,4-hexadiene, 1,7-octadiene, and cycloalkenes, for example, cyclopentene, cyclohexene and cyclooctene. Although the substantially linear ethylene/a-olefin interpolymer can be a terpolymer where at least two a-olefin monomers are polymerized with ethylene, preferably the interpolymer is a copolymer with one a-olefin monomer copolymerized with ethylene and most preferably the substantially linear ethylene/a-olefin interpolymer is a copolymer of ethylene and 1-octene.

Substantially linear ethylene/a-olefin polymers are not the conventional homogeneously branched linear ethylene/a-olefin copolymers described in US Patent 3,645,992 (Elston) nor are they the same class as conventional Ziegler polymerized linear ethylene/a-olefin copolymers (for example, linear low density polyethylene or linear high density polyethylene made, for example, using the technique disclosed by Anderson et al. in US Patent 4,076,698), nor are they the same as traditional highly branched LDPE. The substantially linear ethylene/a-olefin polymers useful in this invention are indeed a unique class of polymers which have excellent processability, even though they have relatively narrow molecular weight distributions (typically, about 2).

Even more surprisingly, as described in US Patent 5,278,272 by Lai et al., the melt flow ratio (110/12) of the substantially linear ethylene homopolymers or interpolymers can be varied essentially independently of the polydispersity index (that is, the molecular weight distribution, Mw/Mn). As Figure 1 illustrates, the rheological behavior of substantially linear ethylene polymers constitutes a dramatic contradistinction over to the homogeneous linear ethylene/a-olefin polymer described by Elston and to conventional Ziegler polymerized heterogeneous linear polyethylene in that both heterogeneous linear and homogeneously linear ethylene polymers have rheological properties such that as the polydispersity index increases, the 110/12 value also increases.

The "rheological processing index" (PI) is the apparent viscosity (in kpoise) of a polymer measured by a gas extrusion rheometer (GER). The gas extrusion rheometer is described by M. Shida, R.N. Shroff and L.V. Cancio in Polymer Engineering Science, Vol: 17, No. 11, p. 770 (1977), and in "Rheometers for Molten Plastics" by John Dealy, published by Van Nostrand Reinhold Co. (1982) on pp. 97-99. GER experiments are performed herein at a temperature of 190°C, at nitrogen pressures between 250 to 5500psig using a 3.81cm diameter die and a 20:1 L/D rheometer with an entrance angle of 1800. The processing index is measured herein at 3,000psig.

For the substantially linear ethylene/a-olefin interpolymers used herein, the PI is the apparent viscosity (in kpoise) of a material measured by GER at an apparent shear stress of 215kPa. The substantially linear ethylene/a-olefin interpolymers used herein preferably have a PI in IN:LIBC1356959:MEF the range of 0.01 kpoise to 50 kpoise, preferably 15 kpoise or less. The substantially linear ethylene/o -olefin interpolymers used herein have a PI less than or equal to 70 percent of the PI of a comparative linear ethylene polymer (either a Ziegler polymerized polymer or a linear uniformly branched polymer as described by Elston in US Patent 3,645,992) at about the same 12 and Mw/Mn.

An apparent shear stress versus apparent shear rate plot can be used to identify the melt fracture phenomena. According to Ramamurthy in the Journal of Rheology, 30(2), 337-357,. 1986, above a certain critical flow rate, the observed extrudate irregularities may be broadly classified into two main types: surface melt fracture and gross melt fracture.

Surface melt fracture occurs under apparently steady flow conditions and ranges in detail from loss of specular film gloss to the more severe form of "sharkskin." In this disclosure, the onset of surface melt fracture (OSMF) is characterized at the beginning of losing extrudate gloss at which the surface roughness of the extrudate can only be detected by 40x magnification.

The critical shear rate at the onset of surface melt fracture for the substantially linear ethylene/a-olefin interpolymers is at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a comparative linear ethylene polymer (either a Ziegler polymerized heterogeneously branched polymer or a homogeneously branched polymer as described by Elston in US Patent 3,645,992) having about the same 12 and Mw/Mn.

Gross melt fracture occurs at unsteady extrusion flow conditions and ranges in detail from regular (alternating rough and smooth, helical, etc.) to random distortions. For commercial acceptability, (for example, in blown films and bags therefrom), surface defects should be minimal, if not absent, for good film quality and properties. The critical shear rate at the onset of surface melt fracture (OSMF) and the onset of gross melt fracture (OGMF) will be used herein based on the changes of surface roughness and configurations of the extrudate.

To more fully characterize the rheological behavior of the unique substantially linear ethylene/c-olefin interpolymers, S. Lai and G.W.

Knight introduced (ANTEC '93 Proceedings, INSITE T M Technology Polyolefins (ITP) New Rules in the Structure/Rheology Relationship of Ethylene a-Olefin Copolymers, New Orleans, La., May 1993) another rheological measurement, the Dow Rheology Index (DRI), which expresses a polymer's "normalized relaxation time as the result of long chain branching." DRI ranges from 0 for polymers which do not have any measurable long chain branching for example, "TAFMER" and "EXACT" products sold commercially by Mitsui Chemical and Exxon Chemical Company, respectively) to about 15 and is independent of melt index. In general, for low to medium density ethylene polymers (particularly at lower densities) DRI provides improved correlations to melt elasticity and high shear flowability relative to correlations of the same attempted with melt flow ratios. For the substantially linear ethylene/a-olefin polymers used in this invention, DRI is preferably at least about 0.1, and especially at least about 0.5, and most especially at least 0.8. DRI can be calculated from the equation: DRI (3652879 To 1 00649 T o -1)/10 where To is the characteristic relaxation time of the material and T1o is the zero shear viscosity of the material. Both To and T7 0 are the "best fit" values to the Cross equation, that is Tl o 1/(l To)n where n is the power law index of the material, and 11 and y are the measured viscosity and shear rate, respectively. Baseline determination of viscosity and shear rate data are obtained using a Rheometric Mechanical Spectrometer (RMS-800) under dynamic sweep mode from 0.1 to 100 radians/second at 1600C and a Gas Extrusion Rheometer (GER) at extrusion pressures from 6.89 to 34.5MPa, which corresponds to shear stress from 0.086 to 0.43MPa, using a 3.81 centimeter diameter die and 20:1 L/D rheometer at 190 0

C.

Specific material determinations can be performed from 140 to 190 0 C as required to accommodate melt index variations.

Substantially linear ethylene/a-olefin interpolymers are considered to be "homogeneous" in composition distribution since substantially all of the polymer molecules have the same ethylene-to-comonomer ratio. Moreover, the substantially linear ethylene polymers have a narrow short chain (homogeneous) branching distribution, as defined by US Patent 3,645992. The distribution of comonomer branches for the substantially linear ethylene/a-olefin interpolymers is characterized by its SCBDI (Short Chain Branch Distribution Index) or CDBI (Composition Distribution Branch Index) and is defined as the weight percent of the polymer molecules having a comonomer content within 50 percent of the median total molar comonomer content. The CDBI of a polymer is readily calculated from data obtained from techniques known in the art, such as, for example, temperature rising elution fractionation (abbreviated herein as "TREF"). The SCBDI or CDBI for the substantially linear ethylene/a-olefin interpolymers used in the present invention is preferably greater than 30 percent, especially greater than 50 percent.

The substantially linear ethylene/a-olefin polymers used in this invention essentially lack a measurable "high density" fraction, as measured by the TREF technique. Preferably, the substantially linear [N:\LIBC1356959:MEF ethylene/o(-olefin interpolymers do not contain a polymer fraction with a degree of branching less than or equal to 2 methyls/1000 carbons. The "high density polymer fraction" can also be described as a polymer fraction with a degree of branching less than 2 methyls/1000 carbons.

The molecular weight and molecular weight distribution, Mw/Mn ratio, of substantially linear ethylene/o-olefin interpolymers can be analyzed by gel permeation chromatography (GPC) on a Waters 150 high temperature chromatographic unit equipped with differential refractometer and three columns of mixed porosity. The columns are supplied by Polymer Laboratories and are commonly packed with pore sizes of 104, 105, 106 and 10 7 tm. The solvent is 1,2,4-trichlorobenzene, from which 0.3 percent by weight solutions of the samples are prepared for injection. The flow rate is milliliters/minute, unit operating temperature is 140°C and the injection size is 100 microliters.

The molecular weight determination with respect to the polymer back-bone is deduced by using narrow molecular weight distribution polystyrene standards (from Polymer Laboratories) in conjunction with their elution volumes. The equivalent polyethylene molecular weights are determined by using appropriate Mark-Houwink coefficients for polyethylene and polystyrene (as described by Williams and Ward in Journal of Polymer Science, Polymer Letters, Vol. 6, p. 621, 1968) to derive the following equation: Mpolyethylene a (Mpolystyrene)b.

In this equation, a 0.4316 and b 1.0. Weight average molecular weight, is calculated in the usual manner according to the following formula: M w R wi* Mi, where wi and Mi are the weight fraction and IN:\LIBC1356959:MEF molecular weight, respectively, of the i t h fraction eluting from the GPC column.

For the substantially linear ethylene/a-olefin interpolymers used in the present invention, the Mw/Mn is preferably less than 3, especially from 1.5 to The novel film comprises from 5 to 40 weight percent, based on the combined weight of components and of the substantially linear ethylene/a-olefin interpolymer, preferably from 10 to 35 weight percent, and more preferably from 15 to 30 weight percent.

The substantially linear ethylene/a-olefin interpolymer used to prepared the film of the present invention has an 12 melt index in the range of 0.3 g/10 minutes to 3 g/10, preferably, 0.3 g/10 minutes to 2.5 minutes and, more preferably, 0.4 g/10 mi- s to 2 g/10 minutes. The substantially linear ethylene/a-olefin inter ,mer has a density less about 0.92 g/cc, more preferably, in the range of 0.85 g/cc to 0.916 g/cc, and most preferably, in the range of 0.86 g/cc to 0.91 g/cc. The I10/12 ratio of the substantially linear ethylene/a-olefin interpolymers is in the range from 5.63 to 30, preferably less than about 20, especially less than about 15, and most especially less than about Component can be a blend of substantially linear ethylene/a-olefin interpolymers or, optionally, a blend of an SLEP interpolymer with at least one heterogeneous or homogeneous linear ethylene polymers selected from the group consisting of ULDPE and LLDPE.

When the substantially linear ethylene/ac-olefin interpolymer is employed in such blends, a blend of an SLEP with a heterogeneous ULDPE, component is preferred.

Heterogeneously branched ULDPE and LLDPE are well known and commercially available materials. They are typically prepared using Ziegler- Natta catalysts in solution or gas phase polymerization processes Anderson et al., U.S. Pat. 4,076,698, is illustrative. These traditional Ziegler-type linear polyethylenes are not homogeneously branched and they do not have any long-chain branching. Heterogeneously branched ULDPE and LLDPE typical having molecular weight distributions, Mw/Mn, in the range of from 3.5 to 4.1.

Homogeneously branched ULDPE and LLDPE are also well known.

Elston disclosure in U.S. Pat. 3,645,992 is illustrative. Homogeneously branched ULDPE and LLDPE can be prepared in conventional polymerization processes using Ziegler-type catalysts such as, for example, zirconium and vanadium catalyst systems as well as using metallocene catalyst systems such as, for example, those based on hafnium. Ewen et al.

disclosure in U.S. Pat. 4,937,299 and Tsutsui et al. disclosure in U.S. Pat.

5,218,071 are illustrative. This second class of linear polyethylenes are homogeneously branched polymers, and like traditional Ziegler-type heterogeneous linear polyethylenes, they do not have any long-chain branching. Homogeneously branched ULDPE and LLDPE typical having molecular weight distributions, Mw/Mn, of about 2. Commercial examples of homogeneously branched linear polyethylenes include those sold by Mitsui Petrochemical Industries under the designation 'TAFMER" and by Exxon Chemical Company under the designation "EXACT".

The preparation of polyethylene film by blown film extrusion is wellknown. See, for example, U.S. Patent 4,632,801 by Dowd which described a typical blown film extrusion process. In the typical process, a polyethylene composition is introduced into a screw extruder wherein it is melted and forwarded through the extruder under pressure. The molten polymer composition is forced through an annular film die to form a molten tube.

Air is then provided through the annular die to inflate the tube into a 21 "bubble" with the desired diameter. Air is contained within the bubble by the annular die and nip rollers downstream of the die where thereafter the bubble is collapse into layflat film. The final thickness of the film is controlled by extrusion rate, bubble diameter and nip speed which can be a controlled by such variables as screw speed, haul-off rate and winder speed. Increasing the extrusion rate at a constant bubble diameter and nip speed, will increase final film thickness.

The typical blown extrusion process can be generally classified as either "stalk" or "pocket" extrusion. In stalk extrusion, bubble inflation and expansion are controlled or occur at a significant distance above the annular die. The air ring, usually of single-lip construction, provides air flow external to the tube and parallel to the machine direction such that the molten tube maintains the approximate diameter of the annular filni die until it is inflated at a height at least 12.7 centimeters above the annular die. Internal bubble cooling can also be used as well as an internal bubble stabilizer to insure optimum bubble stability duing fabrication.

Stalk extrusion is known to allow improved molecular relaxation and, as such, mitigates excessive orientation in one direction and thereby allows balanced film physical properties. Increasing the stalk or expansion height generally provides higher cross direction (CD) properties and, thereby, higher average film properties. Stalk extrusion, and particularly high-stalk extrusion, is very useful for preparing blown films from high molecular weight polyethylene compositions such as, for example, high molecular high density polyethylene (HMW-HDPE) and high molecular low density polyethylene (HMW- LDPE) which possess sufficient melt strength to insure adequate bubble stability.

In pocket extrusion, air is supplied by an air ring disposed immediately adjacent to the annular die to cause the bubble leaving the die IN:\LBC1356959:MEF to immediately inflate and expand. The air ring is typically a dual-lip type to insure added bubble stability. Pocket extrusion is more widely employed than stalk extrusion and is generally preferred for lower molecular weight, lower melt strength polyethylene compositions such as, for example, linear low density polyethylene (LLDPE) and ultra low density polyethylene (ULDPE).

Both monolayer and multilayer films can be prepared by stalk and pocket extrusion and the films of the present invention can be monolayer or multilayer structures.

Multilayer films can be prepared by any-known technique in the art, including, for example, coextrusion, lamination or combinations of both. However, the preferred medium modulus, thick polyethylene film of the present invention is a monolayer film structure.

Although the film of this invention can be prepared by variable stalk extrusion, pocket extrusion and low-stalk extrusion are preferred where the high molecular weight linear ethylene polymer, Component has an 15 melt index greater than about 0.5g/10 minutes, particularly greater than about 0.6g/10 minutes, and most particularly greater than about 0.7g/10 minutes. High stalk extrusion, where the distance between the die and the occurrence of bubble expansion is usually from 76 to 107 centimeters, that is, from 6 to 10 die diameters, is preferred for preparing of the film of this invention where the high molecular weight linear ethylene polymer, component has an 15 melt index less than or equal to about 0.5g/10 minutes, particularly less than about 0.4g/10 minutes, and most particularly less than about 0.3g/10 minutes.

Components and and optional Component used to prepare the film of this invention, can be individually blended (that is, where a component itself is a polymer blend of two or more subcomponent polymers) or admixed together by any suitable means known in the art.

IN:VLIBCI356959 :MEF Suitable means are thought to include tumble dry-blending the components together prior to charging the blown film extruder, weigh-feeding the components directly into the blown film extruder, melt-blending the components via compound or side-arm extrusion prior to introduction into the blown film extruder, multiple reactor polymerization of the components with reactors in series or in parallel and optionally with different catalyst and/or monomer types in each reactor, or the like as well as combinations thereof.

In addition to the above equations respecting the tear and impact performance of the film of this invention, temperature rising elution fractionation (TREF) can also be used to" fingerprint" or identify the novel film of this invention as well as the film compositions used to make the novel film.

Additives, such as antioxidants for example, hindered phenolics, such as Irganox® 1010 or Irganox® 1076 supplied by Ciba Geigy), phosphites for example, Irgafos® 168 also supplied by Ciba Geigy), cling additives (for example, PIB), Standostab PEPQTM (supplied by Sandoz), pigments, color:- Is, and fillers can also be included in the film of the present inve. mn, or the polymer compositions used to make the same, to the extent that such additives or ingredients do not interfere with the improved tear and impact resistance performance discovered by Applicants. Although generally not required, the film of the present invention can also contain additives to enhance antiblocking and coefficient of friction characteristics including, but not limited to, untreated and treated silicon dioxide, talc, calcium carbonate, and day, as well as primary, secondary and substituted fatty acid amides, release agents, silicone coatings, etc. Still other additives, such as quaternary ammonium compounds alone or in combination with ethylene-acrylic acid (EAA) copolymers or other functional polymers, can also be added to enhance the antistatic characteristics of the film of this invention and allow, for example, heavy-duty packaging of electronically sensitive goods.

Advantageously, because of the improved strength properties-of the novel film, recycled and scrap materials as well as diluent polymers can be incorporated or admixed into the film compositions used to make the novel film at higher loadings than is typically possible with prior art polyethylene film compositions and still provide or maintain the desired performance properties for successful use in heavy-duty packaging and shipping applications. Suitable diluent materials include, for example, elastomers, rubbers and anhydride modified polyethylenes for example, polybutylene and maleic anhydride grafted LLDPE and HDPE) as well as with high pressure polyethylenes such as, for example, low density polyethylene (LDPE), ethylene/acrylic acid (EAA) interpolymers, ethylene/vinyl acetate (EVA) interpolymers and ethylene/methacrylate (EMA) interpolymers, and combinations thereof.

i Examples The following examples illustrate some of the particular embodiments of the present invention, but the following should not be construed to mean the invention is limited only to the particular embodiments shown.

Table 1 lists various resin types for use in investigating the requirements for improved medium modulus films.

Table 1 Resin Types and Properties Resin Type* MIg/10 Density Melt Flow Mw/Mn Critical Critical Comonomer Process min g/cc Ratio Shear Rate Shear Type Type 1/sec Stress kPa HMW-HDPE 0.2615 0.942 5.5121.6/I1o NA NA NA Butene Slurry HMW-HDPE 0.7515 0.951 NA NA NA NA Butene Slurry HMW-HDPE 0.2615 0.935 5.3126.6/I 1 NA NA NA Butene Slurry 0 MDPE 1.012 0.935 7.7110/12 NA NA 240 Octene Solution ULDPE 0.812 0.905 8.7110/12 3.8-4.0 NA 360 Octene Solution LLDPE 1.012 0.920 7.6110/12 3.5-3.8 NA 390 Octene Solution SLEP 0.812 0.911 10.9110/12 NA 1,044 430 Octene Solution SLEP 1.012 0.870 7.4110/12 1.98 503 300 Octene Solution SLEP 0.912 0.898 10.8110/12 2.17 258 240 Octene Solution SLEP 1.012 0.902 7.5110/12 2.12 NA 430 Octene Solution SLEP 1.012 0.909 9.6110/12 2.06 1,766 450 Octene Solution RM-HDPE 0.112 0.935 NA NA NA NA NA NA HMW-HDPE, HMW-HDPE, LLDPE, SLEP and MDPE resins are supplied by the Dow Chbmical Company. RM-HDPE denotes a Polybutylene Rubber-Modified HDPE is supplied by Allied-Signal under the designation "PAXON 3208'.

Tables 2 7 summarize the various component resins and film compositions for use in determining the requirements for medium modulus, polyethylene films with improved strength properhes. The tables also summarize the fabrication conditions for use in investigating improved medium modulus, polyethylene film. Except for Inventive Example 43 which involves side-arm extrusion preparation, all blend compositions used in the investigahion were performed by tumble-blending IN:\LIBC356959:MEF the individual polymer components together according to the weight percentage amounts shown in the various Tables.

Inventive Films 2-4, 6-8 and 10-12 as well -as Comparative Films 1, 7, 9 and 13-24 were fabricated by using a seven-zone Kiefel high stalk blown film line equipped with a grooved-barrel extruder, a decompression screw and no internal bubble cooling. Inventive Films 25-28, 34-40, 42 and 43 as well as Comparative Films 29-33 and 41 were fabricated utilizing a conventional pocket blown film line equipped a LLDPE barrier screw. With the exception of Comparative Films prepared from Compositions F and L, which were fabricated using an incline extruder temperature profile, all film fabrications employed a reverse temperature profile. The physical properties of the resultant Inventive Films and Comparative Films from Compositions A W as a function of thickness are also summarized in Table 2 7.

The Tables report both measured and calculated film density. Like calculated film density determinations, the composition I5 values reported in the tables were also derived from weight-fraction calculations. For purposes of this invention and for component polymers, all reported 12 values less than 0.5 g/10 minutes and 15 values greater than 1.0 minutes are calculated values based on the following relationship: 12 5.1 Is.

Additionally, for component polymers, reported 121.6/110 values less than 4.0 and 110/I2 values greater than 15 are also calculated values based on the following relationship: 4.4 I10/I2 1.0 I21.6/I10 For purposes of this invention, and as an example, the following computation is the weight-fraction calculation for determining the calculated film density of Inventive Example 1 which comprises 80 weight percent of a HDPE having a density of 0.942g/cc and 20 weight percent of a SLEP having a density of 0.902g/cc: calculated film density (g/cc) (0.8)(0.942g/cc) (0.2)(0.902g/cc) 0.934g/cc The following computation example is the weight-fraction calculation for determining the calculated composition 15 of Inventive Example 25 which comprises weight percent of a HDPE having an 15 of 0.75g/10 minutes and 20 weight percent of a SLEP having an 12 of 1.0g/10 minutes: calculated composition 15 (g/10 min.) (0.8)(0.7515) (0.2)(1.012)(5.115/1.012) 1.62 The following computation example is the factor-based calculation for determining the 15 melt index of the SLEP having a 0.77g/10 minutes 12 that used to prepared Composition B: calculated component polymer 15 (g/10 min.) (0.77 12)(5.15/1.0 12) 3.93 The following computation example is the factor-based calculation for determining the 121.6/110 ratio of the SLEP having a 10.9 110/12 ratio that used to prepared Composition B: calculated component polymer 121.6/110 (10.9110/12)(1.0121.6/110 4.4110/12) 2.47121.6/10 The following computation example is the normalization calculation for determining the tear strength of Inventive Example 10 at 76.tm where the tear strength is 762 grams at 74[tm: tear strength at 7 6tim (grams) (762g)(76jm/74tm) 777 grams [N:LIBC1356959:MEF Table 2 Film Compositions, Fabrication Conditions and Film Properties COMPOSITION A B Inventive Example 1* 2 3 4 5* 6 7 8 COMPONENT

(A)

Type HDPE HDPE HDPE HDPE HDPE HDPE HDPE HDPE Polymerization Process Slurry Slurry Slurry Slurry Slurry Slurry Slurry Slurry Comonomer Butene Butene Butene Butene Butene Butene Butene Butene grams/10 minutes 0.26 0.26 0.26 0.26 0.26 0.26 0.26 0.26 12, grams/10 minutes 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 Density, g/cc 0.942 0.942 0.942 0.942 0.942 0.942 0.942 0.942 121.61110 5.5 5.5 5.5 5.5 5.5 5.5 5.5 110/12 24.2 24.2 24.2 24.2 24.2 24.2 24.2 24.2 COMPONENT (B) Type SLEP SLEP SLEP SLEP SLEP SLEP SLEP SLEP Polymerization Process Solution Solution Solutio Solution Solution Solution Solution Solution n Comonomer Octene Octene Octene Octene Octene Octene Octene Octene grams/10 minutes 5.1 5.1 5.1 5.1 3.9 3.9 3.9 3.9 12, grams/10 minutes 1.00 1.00 1.00 1.00 0.77 0.77 0.77 0.77 Density, g/cc 0.902 0.902 0.902 0.902 0.911 0.911 0.911 0.911 1216/110 1.7 1.7 1.7 1.7 2.5 2.5 2.5 110/12 7.5 7.5 7.5 7.5 10.9 10.9 10.9 10.9 BLEND WT. percent 80/20 80/20 80/20 80/20 80/20 80/20 80/20 80/20 FABRICATION CONDITIONS Annular Die Diameter, mm 113 113 113 113 113 113 113 113 Extruder Diameter, mm 70 70 70 70 70 70 70 Extruder Length/Diameter 24/1 24/1 24/1 24/1 24/1 24/1 24/1 24/1 Die Gap, mm 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 Output, kg/hr 77 100 100 100 100 100 100 100 Blow-up Ratio 3.3/1 3.3/1 3.3/1 3.3/1 3.3/1 3.3/1 3.3/1 3.3/1 Stalk Height, cm 104 104 104 104 104 104 104 104 Target Melt Temperature, °C 213 213 213 213 213 213 213 213 PHYSICAL PROPERTIES Film Thickness, tm 12 72 130 207 15 56 94 129 Cal. Film Density, g/cc 0.934 0.934 0.934 0.934 0.935 0.935 0.935 0.935 Composition 15, g/10min. 1.20 1.20 1.20 1.20 0.71 0.71 0.71 0.71 CD Tear, grams 105 801 1205 >1600 127 763 799 816 MD Tear, grams 11 642 1253 >1600 8 199 499 777 Tear Strength, grams 58 722 1229 >1600 68 481 649 797 Denotes Comparative Examples only, that is, the examples are not examples of the present invention.

Cal. Film Density denotes calculated film density.

IN:\LIBC1356959:MEF Table 3 Film Compositions, Fabrication Conditions and Film Properties COMPOSITION C D Example 9* 10 11 12 13* 14* 15* 16* COMPONENT (A) Type Polymerization Process Comonomer grams/10 minutes 12, grams/10 minutes Density, g/cc 121.6/110 110/12 COMPONENT (B) Type Polymerization Process Comonomer grams/10 minutes 12, grams/10 minutes Density, g/cc 121.6/110 110/12 COMPONENT (C) Type Polymerization Process Comonomer grams/10 minutes 12, grams/10 minutes Density, g/cc 1216/110 110/12 BLEND WT. percent FABRICATION CONDITIONS Annular Die Diameter, mm Extruder Diameter, mm Extruder Length/Diameter Die Gap, mm Output, kg/hr Blow-up Ratio Stalk Height, cm Melt Temperature, °C PHYSICAL PROPERTIES Film Thickness, -Lm Cal. Film Density, g/cc Composition 15, g/10min.

CD Tear, grams MD Tear, grams Tear Strenoth. arams HDPE HDPE HDPE HDPE Slurry Slurry Slurry Slurry Butene Butene Butene Butene 0.26 0.26 0.26 0.26 0.05 0.05 0.05 0.05 0.942 0.942 0.942 0.942 5.5 5.5 5.5 5.5 24.2 24.2 24.2 24.2 ULDPE ULDPE ULDPE ULDPE Solution Solution Solutio Solution n Octene Octene Octene Octene 4.1 4.1 4.1 4.1 0.8 0.8 0.8 0.8 0.905 0.905 0.905 0.905 2.0 2.0 2.0 8.7 8.7 8.7 8.7 SLEP SLEP SLEP SLEP Solution Solution Solutio Solution n Octene Octene Octene Octene 3.9 3.9 3.9 3.9 0.77 0.77 0.77 0.77 0.911 0.911 0.911 0.911 2.5 2.5 2.5 10.9 10.9 10.9 10.9 80/10/10 80/10/10 80/10/10 80/10/10 HDPE HDPE HDPE HDPE Slurry Slurry Slurry Slurry Butene Butene Butene Butene 0.26 0.26 0.26 0.26 0.05 0.05 0.05 0.05 0.935 0.935 0.935 0.935 5.25 5.25 5.25 5.25 23.1 23.1 23.1 23.1 None None None None None None None None 113 70 24/1 1.2 77 3.3/1 104 213 13 0.935 0.71 141 10 76 113 113 113 70 70 70 24/1 24/1 24/1 1.2 1.2 1.2 100 100 100 3.3/1 3.3/1 3.3/1 104 104 104 213 213 213 75 121 197 0.935 0.935 0.935 0.71 0.71 0.71 1120 1471 >1600 404 923 >1600 762 1197 >1600 100/0/0 113 70 24/1 1.2 77 3.3/1 104 213 14 0.935 0.26 95 9 52 100/0/0 100/0/0 100/0/0 113 70 24/1 1.2 100 3.3/1 104 213 73 0.935 0.26 573 306 440 113 70 24/1 1.2 100 3.3/1 104 213 130 0.935 0.26 828 726 777 113 24/1 1.2 100 3.3/1 104 213 157 0.935 0.26 1100 969 1035 V Denotes Comparative Examples only, that is, the examples are not examples of the present invention.

Cal. Film Density denotes calculated film density.

[N:\LIBC1356959:MEF Table 4 Film Compositions, Fabrication Conditions and Film Properties COMPOSITION E F Example 17* 18* 19* 20* 21* 22* 23* 24* COMPONENT (A) Type HDPE HDPE HDPE HDPE MDPE MDPE MDPE MDPE Polymerization Process Slurry Slurry Slurry Slurry Solution Solution Solution Solution Comonomer Butene Butene Butene Butene Octene Octene Octene Octene grams/10 minutes 0.26 0.26 0.26 0.26 5.1 5.1 5.1 5.1 12, grams/10 minutes 0.05 0.05 0.05 0.05 1.0 1.0 1.0 Density, g/cc 0.942 0.942 0.942 0.942 0.935 0.935 0.935 0.935 121.6/110 5.5 5.5 5.5 5.5 1.8 1.8 1.8 1.8 110/12 24.2 24.2 "24.2 24.2 7.7 7.7 7.7 7.7 COMPONENT (B) Type None None None None None None None None Polymerization Process Comonomer grams/10 minutes 12, grams/10 minutes Density, g/cc 121.6/110 110/12 (A(IIB)I(CI BLEND WT. percent 100/0 100/0 100/0 100/0 100/0 100/0 100/0 100/0 FABRICATION CONDITIONS Annular Die Diameter, mm 113 113 113 113 152 152 152 152 Extruder Diameter, mm 70 70 70 70 64 64 64 64 Extruder Length/Diameter 24/1 24/1 24/1 24/1 24/1 24/1 24/1 24/1 Die Gap, mm 1.2 1.2 1.2 1.2 1.6 1.6 1.6 1.6 Output, kg/hr 77 100 100 100 64 64 64 64 Blow-up Ratio 3.3/1 3.3/1 3.3/1 3.3/1 2.5/1 2.5/1 2.5/1 2.5/1 Stalk Height, cm 104 104 104 104 <12.7 <12.7 <12.7 <12.7 Target Melt Temperature, °C 213 213 213 213 213 213 213 213 PHYSICAL PROPERTIES Film Thickness, p.m 22 71 120 186 16 73 88 209 Cal. Film Density, g/cc 0.942 0.942 0.942 0.942 0.935 0.935 0.935 0.935 Composition 15, g/10min. 0.26 0.26 0.26 0.26 5.1 5.1 5.1 5.1 CD Tear, grams 89 263 454 931 323 441 556 1359 MD Tear, grams 28 224 514 1054 31 305 333 1027 Tear Strength, grams 59 244 484 993 177 373 445 1193 Impact Resistance, gram NA NA NA NA 50 165 185 505 Denotes Comparative Examples only. that is, the examples are not examples of the present invention.

Cal. Film Density denotes calculated film density.

IN:\LIBCI356959:MEF Table Film Compositions, Fabrication Conditions and Film Properties COMPOSITION G H I J K L M N O Example 25 26 27 28 29* 30* 31* 32* 33* COMPONENT (A) Type HOPE HDPE HDPE HDPE None MDPE HDPE None HOPE Polymerization Process Slurry Slurry Slurry Slurry Solution Slurry Slurry Comonomer Butene Butene Butene Butene Octene Butene Butene grams/10 minutes 0.75 0.75 0.75 0.75 5.1 0.75 0.3 12, grams/10 minutes 0.15 0.15 0.15 0.15 1.0 0.15 Density, g/cc 0.951 0.951 0.951 0.951 0.935 0.951 0.950 110/12 NA NA NA NA 7.7 NA 2.4 COMPONENT (B) Type SLEP SLEP SLEP SLEP SLEP None None LLDPE None Polymerization Process Solution Solution Solutio Solution Solution Solution n Comonomer Octene Octene Octene Octene Octene Octene grams/10 minutes 5.1 5.1 5.1 5.1 5.1 5.1 12, grams/10 minutes 1.0 1.0 1.0 1.0 1.0 Density, g/cc 0.870 0.870 0.870 0.870 0.870 0.920 110/12 7.4 7.4 7.4 7.4 7.4 7.6 BLEND WT. 80/20 75/25 85/15 90/10 0/100 100/0 100/0 0/100 100/0 percent

FABRICATION

CONDITIONS

Annular Die Diameter, mm 152 203 203 152 152 152 152 152 113 Extruder Diameter, mm 64 89 89 64 64 64 64 64 Extruder Length/Diameter 24/1 30/1 30/1 24/1 24/1 24/1 24/1 24/1 24/1 Die Gap, mm 1.6 2.8 2.8 1.6 1.6 1.6 1.6 1.6 1.2 Output, kg/hr 64 68 68 42 31 64 64 64 100 Blow-up Ratio 2.5/1 2.5/1 2.5/1 2.0/1 2.0/1 2.5/1 2.5/1 2.5/1 3.3/1 Stalk Height, cm <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 104 Viton Processing Aid None None None None None Yes None None None Extruder Amps 58 NA NA 58 NA 71 58 65 na Target Melt Temperature, 213 213 213 213 213 213 213 213

C

Die Pressure, psi 3170 3450 3450 4650 4170 3170 3420 3130 NA PHYSICAL PROPERTIES Film Thickness, pm 76 76 76 76 76 76 76 76 76 Meas. Film Density, g/cc 0.934 0.936 0.943 0.941 0.870 0.935 0.951 0.92 0.950 Composition 15, g/10min. 1.6 1.8 1.4 1.2 5.1 5.1 0.75 5.1 0.30 CD Tear, grams 324 1391 1826 464 91 328 80 1558 228 MD Tear, grams 1419 362 126 110 62 593 284 >1600 125 Tear Strength, grams 872 876 976 287 77 461 182 1580 177 Impact Resistance, grams 425 432 198 185 >850 250 125 800 NA *Denotes Comparative Examples only. that is. the examples are not examples of the present invention.

Meas. Film Dcnsiq denotes measured film density. NA denotes data not available.

Viton is a fluoropolymer processing aid supplied by Dupont Chemical Company.

IN:LIBC1356959:MEF Table 6 Film Compositions, Fabrication Conditions and Film Properties COMPOSITION P Q R S T U V W Example 34 35 36 37 38 39 40 41* COMPONENT (A) Type HDPE HDPE HDPE HDPE HDPE HDPE HDPE RM-HDPE Polymerization Process Slurry Slurry Slurry Slurry Slurry Slurry Slurry Rubber Comonomer (or Rubber Type) Butene Butene Butene Butene Butene Butene Butene Polybutylene grams/10 minutes 0.75 0.75 0.75 0.75 0.75 0.75 0.75 0.51 12, grams/10 minutes 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.10 Density, g/cc 0.951 0.951 0.951 0.951 0.951 0.951 0.951 0.935 110/12 NA NA NA NA NA NA NA NA COMPONENT (B) Type ULDPE ULDPE SLEP SLEP SLEP SLEP SLEP None Polymerization Process Solution Solution Solution Solution Solution Solution Solution Comonomer Octene Octene Octene Octene Octene Octene Octene grams/10 min 4.1 4.1 4.6 4.6 5.1 5.1 4.6 12, grams/10 min 0.8 0.8 0.9 0.9 1.0 1.0 0.9 Density, g/cc 0.905 0.905 0.898 0.898 0.909 0.909 0.898 110/12 8.7 8.7 10.8 10.8 9.6 9.6 10.8 COMPONENT (C) Type None None None None None None ULDPE None Polymerization Process Solution Comonomer Octene g/10 min. 4.1 12, g/10 min. 0.8 Density, g/cc 0.905 110/12 8.7 BLEND WT. 90/10/0 80/20/0 90/10/0 80/20/0 90/10/0 80/20/0 80/10/10 100/0 percent FABRICATION CONDITIONS Annular Die Diameter, mm 152 152 152 152 152 152 152 152 Extruder Diameter, mm 64 64 64 64 64 64 64 64 Extruder Length/Diameter 24/1 24/1 24/1 24/1 24/1 24/1 24/1 24/1 Die Gap, mm 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 Output, kg/hr 31 31 31 31 31 31 31 31 Blow-up Ratio 2.0/1 2.0/1 2.0/1 2.0/1 2.0/1 2.0/1 2.0/1 2.0/1 Stalk Height, cm <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 <12.7 Target Melt Temperature, °C 229 229 229 229 229 229 229 229 Die Pressure, psi 4170 4170 4170 4170 4170 4170 4170 4170 PHYSICAL PROPERTIES Film Thickness, ipm 76 76 76 76 76 76 76 76 Meas. Film Density, g/cc 0.944 0.941 0.950 0.940 0.945 0.942 0.941 0.934 Composition 15, g/10min. 1.1 1.4 1.1 1.5 1.2 1.6 1.5 0.51 CD Tear, grams 322 411 318 506 266 328 312 544 MD Tear, grams 115 138 114 131 94 112 110 110 Tear Strength, grams 219 275 216 319 180 220 211 327 Impact Resistance, grams 175 173 164 175 163 164 164 403 *Denotes Comparative Examples only, that is, the examples are not examples of the present invention.

Meas Film Density denotes measured film density. NA denotes data not available. RM-HDPE denotes PAXON 3208 polybutlene rubber modified HDPE IN:\LIBC1356959:MEF Table 7 Effect of Stalk Height on Impact Properties COMPOSITION G G EXAMPLE 42 43 COMPONENT (A) Type HDPE HDPE Polymerization Process Slurry Slurry Comonomer Butene Butene g/10min. 0.75 0.75 12, g/10min. 0.15 0.15 Density, g/cc 0.951 0.951 110/12 NA NA COMPONENT

(B)

Type SLEP SLEP Polymerization Process Solution Solution Comonomer Octene Octene Is, g/10min. 5.1 5.1 12, g/10min. 1.0 Density, g/cc 0.870 0.870 110/12 7.4 7.4 BLEND WT. percent 80/20 80/20 FABRICATION CONDITIONS Annular Die Diameter, mm 152 152 Extruder Diameter, mm 64 64 Extruder Length/Diameter 24/1 24/1 Die Gap, mm 2.8 2.8 Output, kg/hr 64 64 Blow-Up Ratio 2.5/1 2.5/1 Stalk Height, cm 12.7 102 Frost Line Height, cm 76 127 Target Melt Temperature, °C 232 232 PHYSICAL PROPERTIES Film Thickness, pm 76 76 Meas. Film Density, g/cc 0.934 0.934 Impact Resistance, grams 400 425 Denotes Comparative Examples only, that is, the examples are not examples of the present invention. Meas. Film Densiq denotes measured film densiq. NA denotes data not available.

tDenotes Composition G is prepared in a commercial-scale slurry polymerization manufacturing plant by side-arm extrusion incorporation of the substantially linear ethylene/ a-olefin interpolymer.

The physical property data in Tables 2 7 and Figures 2 4 demonstrate that films prepared in accordance with the present invention exhibit substantially improved tear strength and impact resistance in comparisons with other films prepared from individual component polymers that have the same film density, film thickness and similar melt IN:\LIBC356959:MEF index. The tables also show Inventive Films exhibit superior tear strength and impact resistance over PAXON 3208 (Comparative Example 41), a polybutylene rubber modified HDPE used commercially for a variety of heavy-duty packaging applications. The superior performance of the Inventive Films of the present invention allow practitioners down-gauging savings while still providing polyethylene films that meet the demanding requirements of heavy-duty packaging.

Figure 2 specifically illustrates that Inventive Films prepared from Composition A, B and C exhibit superior tear strength at film thicknesses greater than 31jim, particularly in the range of 38 to 222 tm, and especially in the range of 50ptm to 203ptm in io comparison to Comparative Films prepared from Compositions D, E and F.

Figure 2 also shows Inventive Films comprising Components and as well as those comprising Components and as three-component blends, exhibit exceptional comparative tear performance. A comparison between the Inventive Pilms prepared using Compositions B and C indicates a substantially linear ethylene/a-olefin interpolymer, Component having an 110/12 ratio less than about 10 is most preferred for film thicknesses greater than about 3 mils. In direct comparisons, Inventive Films show from 30 percent greater tear strength at 3 mils (comparison between films based on Compositions B and D) to as high as about 180 percent greater tear strength at 5 mils (comparison between films based on Compositions C and E).

Figure 3 shows at equivalent densities, Inventive Films (tentive Examples 25-28 and 34-38) exhibit superior impact resistance at 76ptm over Comparative Films (Comparative Examples 22 and 30-32 where Comparative Examples 22 and 30 are averaged and plotted as a single data point). Figure 3 also indicates Inventive Examples and 26 show more (N:\LIBC1356959:MEF I II than 100 percent greater impact resistance than is ordinarily expected for their respective measured densities. These Inventive Films also indicate that substantially linear ethylene/ao-olefin interpolymers, Component having densities less than 0.89 g/cc are most preferred for preparing the novel film of the present invention.

Figure 4 illustrates Inventive Examples 25, 26 and 27 exhibit synergistically superior tear strength relative to predicated or calculated performance based on their respective componc: polymers, a 0.951 g/cc HMW-HDPE and a 0.87 g/cc SLEP at 100 percent/0 percent, 90 percent, 80 percent/20, 70 percent/30 percent and 0 percent/100 percent, respectively. Figure 4 also shows that Inventive Films can exhibit more than about 90 percent greater tear strength than comparative films having about the same melt index, film thickness and measured film density.

Table 7 specifically indicates, although low-stalk and pocket extrusion are preferred for fabricating Inventive Film comprising a Component (A) polymer having a Is greater than 0.5 g/10 minutes, Inventive Films can also be successfully fabricated using variable-stalk extrusion, that is pocket and stalk extrusion. Even more surprisingly, is these Inventive Examples indicate the novel film can be fabricated with a high-stalk on conventional pocket extrusion lines. This feature of the invention allows Practitioners the significant commercial benefits of equipment selection flexibility and equipment utilization efficiency.

Claims (38)

1. A medium modulus, polyethylene film characterised as having a thickness greater than about 31 tm which comprises: from about 60 to about 95 weight percent, based on the combined weight of components and of at least one high molecular weight linear ethylene polymer having a density in the range of about 0.92 to about 0.96g/cc and an 15 melt index in the range of about 0.1 to about 3g/10 minutes, and from about 5 to about 40 weight percent, based on the combined weight of components and of at least one substantially linear ethylene/a-olefin interpolymer characterised as having: i. a melt flow ratio, I10/I2, 5.63, and ii. a molecular weight distribution, Mw/Mn, defined by the equation M,/Mn (I11o/2)-4.63 wherein the substantially linear ethylene/a-olefin polymer is further characterised as containing at least one a-olefin monomer and having a density in the range of about 0.85 to about 0.92g/cc and an 12 melt index in the range of 0.3 to about 3g/10 minutes, wherein the medium modulus polyethylene film is further characterised as having a tear strength at least 30 percent greater than the tear strength of a second polyethylene film, wherein the second polyethylene film is comprised of a single polymer component and is characterised as having essentially the same density, thickness and melt index as the medium modulus polyethylene film, and wherein the at least 30 percent greater tear strength is represented by the equation: tear strength (grams) Ax Bx 2 C where A, B and C are numerical values and x is film thickness, and when A is less than or equal to 150, B is greater than or equal to 12.5, and when A is greater than 150, B is in the range of -80 to

2. The film of Claim 1 wherein said film is a blown film.

3. The film of Claim 1 or Claim 2 wherein the film thickness is in the range of about 38pm to about 222p-m.

4. The film of Claim 3 wherein the film thickness is in the range of about 50 to about 203p.m.

The film of any one of Claims 1 to 4 wherein the calculated film density is in the range of about 0.923g/cc to about 0.95g/cc.

6. The film of any one of Claims 1 to 5 wherein said high molecular weight linear ethylene polymer is an interpolymer of ethylene and at least one a-olefin selected from the group consisting of 1-propylene, 1-butene, 4-methyl-l-pentene, 1-hexene and 1- octene.

7. The film of Claim 6 wherein said high molecular weight linear ethylene interpolymer is a copolymer of ethylene and 1-butene. [R:\LLBH]00796.doc:KWW 1

8. The film of any one of Claims 1 to 7 wherein the substantially linear ethylene/ a-olefin polymer is further characterised as having: iii an improved gas extrusion rheology such that the critical shear rate at onset of surface melt fracture for the substantially linear ethylene/a-olefin polymer is at least 50 percent greater than the critical shear rate at onset of surface melt fracture for a linear ethylene polymer, wherein the substantially linear ethylene/a-olefin polymer and the linear ethylene polymer comprise the same monomer or monomers, have essentially the same 12 and Mw/Mn and are measured at the same melt temperature using a gas extrusion rheometer.

9. The film of any one of Claims 1 to 8 wherein said substantially linear ethylene/a-olefin polymer is further characterised as having from about 0.01 long chain branches/1000 carbons to about 3 long chain branches/1000 carbons along the polymer backbone.

The film of any one of Claims 1 to 9 wherein said substantially linear ethylene/a-olefin polymer is an interpolymer of ethylene and at least one a-olefin selected from the group consisting of 1-propylene, 1-butene, 4 -methyl-l-pentene, 1-hexene and 1- octene.

11. The film of Claim 10 wherein said substantially linear ethylene/a-olefin interpolymer is a copolymer of ethylene and 1-octene.

12. The film of any one of Claims 1 to 11 wherein said high molecular weight linear ethylene polymer has an 15 melt index in the range of about 0.lg/10 minutes to about 2g/10 minutes.

13. The film of any one of Claims 1 to 11 wherein said substantially linear ethylene polymer has an 12 melt index in the range of about 0.3g/10 minutes to about 2.5g/10 minutes.

14. The film of any one of Claims 1 to 13 wherein said high molecular weight linear ethylene polymer has a density in the range of about 0.93g/cc to about 0.96g/cc.

The film of any one of Claims 1 to 14 wherein said substantially linear ethylene polymer has a density in the range of about 0.86g/cc to about 0.91g/cc.

16. A medium modulus, polyethylene film, substantially as hereinbefore described with reference to any one of the examples but excluding the comparative examples.

17. A method for preparing a medium modulus, polyethylene film comprising the steps of: providing an extrudable thermoplastic composition containing from about 60 to about 95 weight percent, based on the combined weight of components (A) and of at least one high weight molecular linear ethylene polymer having a density in the range of about 0.92 to about 0.96g/cc and an 15 melt index in the range of about 0.1 to about 3g/10 minutes, and from about 5 to about 40 weight percent, based on the combined weight of components and of at least one substantially linear ethylene/ a-olefin polymer containing at least one a-olefin and having a density in the range of (n:\libc]00796:MEF about 0.85 to about 0.92g/cc and an 12 melt index in the range of 0.3 to about 3g/10 minutes. introducing said composition of step into a heated film extrusion apparatus equipped with an annular die, extruding said composition through said annular die to form a molten or semi-molten thermoplastic tube of said composition that is subsequently blown-up beyond the die diameter and drawn-down through nip and take-off rollers to form a layflat film with a thickness greater than about 31p.m, and conveying said film formed in step for subsequent use down-line of lo the blown film extrusion apparatus of step or collecting said film formed in step (3) for subsequent use off-line, wherein the medium modulus polyethylene film is further characterised as having a tear strength at least 30 percent greater than the tear strength of a second polyethylene film, wherein the second polyethylene film is comprised of a single polymer component and is characterised as having essentially the same density, thickness and melt index as the medium modulus polyethylene film, and wherein the at least 30 percent greater tear strength is represented by the equation: tear strength (grams) Ax Bx 2 C where A, B and C are numerical values and x is film thickness, and when A is less than or equal to 150, B is greater than or equal to 12.5, and when A is greater than 150, B is in the range of -80 to

18. The method of Claim 17 wherein said extrusion apparatus is a variable stalk extrusion film line.

19. A method for preparing a medium modulus, polyethylene film substantially as hereinbefore described with reference to any one of the examples but excluding the comparative examples.

The film produced by the method of any one of Claims 17 to 19.

21. A medium modulus, polyethylene film characterized as having a thickness greater than about 1.25 mils which comprises: from 60 to 95 weight percent, based on the combined weight of components and of at least one high molecular weight linear ethylene polymer having a density in the range of 0.92 to 0.96 g/cc and an I melt index in the range of 0.1 to 3 minutes, and from 5 to 40 weight percent, based on the combined weight of components (A) and of at least one substantially linear ethylene/c-olefin interpolymer characterised as having: i. a melt flow ratio, 110/12, >5.63, and ii. a molecular weight distribution, Mw/Mn, defined by the equation Mw/Mn (110o/12)-4.63 [R:\LIBH]00796.doc: KWW wherein the substantially linear ethylene/a-olefin polymer is further characterised as containing at least one a-olefin monomer and having a density in the range of 0.85 to 0.92g/cc and an 12 melt index in the range of 0.3 to 3g/10 minutes, wherein said film is further characterized as having a tear strength at least 30 percent greater than the tear strength of a comparative polyethylene film having essentially the same density, thickness and melt index.

22. The film of Claim 21 wherein said film is a blown film.

23. The film of Claim 21 wherein the film thickness is in the range of 1.5 mils to 8.75 mils.

24. The film of Claim 23 wherein the film thickness is in the range of 2 to 8 mils.

The film of Claim 21 wherein the calculated film density is in the range of 0.923g/cc to 0.95g/cc.

26. The film of Claim 21 wherein said high molecular weight linear ethylene polymer is an interpolymer of ethylene and at least one a-olefin selected from the group consisting of 1-propylene, 1-butene, 4-methyl-l-pentene, 1-hexene and 1-octene.

27. The film of Claim 26 wherein said high molecular weight linear ethylene interpolymer is a copolymer of ethylene and 1-butene.

28. The film of Claim 21 wherein said substantially linear ethylene/a-olefin polymer is further characterized as having: iii. a critical shear rate at onset of surface melt fracture at least 50 percent greater than the critical shear rate at onset of surface melt fracture of a comparative linear ethylene polymer having about the same 12 and Mw/M.n

29. The film of Claim 21 wherein said substantially linear ethylene/a-olefin polymer is further characterized as having from 0.01 long chain branches/1000 carbons to 3 long chain branches/1000 carbons along the polymer backbone.

The film of Claim 21 wherein said substantially linear ethylene/a-olefin polymer is an interpolymer of ethylene and at least one a-olefin selected from the group consisting of 1-propylene, 1-butene, 4-methyl-l-pentene, 1-hexene and 1-octene.

31. The film of Claim 30 wherein said substantially linear ethylene/a-olefin interpolymer is a copolymer of ethylene and 1-octene.

32. The film of Claim 21 wherein said high molecular weight linear ethylene polymer has an I, melt index in the range of 0.lg/10 minutes to 2g/10 minutes.

33. The film of Claim 21 wherein said substantially linear ethylene polymer has an 12 melt index in the range of 0.3g/10 minutes to 2.5g/10 minutes.

34. The film of Claim 21 wherein said high molecular weight linear ethylene polymer has a density in the range of 0.93g/cc to 0.96g/cc.

The film of Claim 21 wherein said substantially linear ethylene polymer has a density in the range of 0.855g/cc to 0.918g/cc.

36. A method for preparing a medium modulus, polyethylene film comprising the steps of: [R:\LIBH]00796.doc: KWW providing an extrudable thermoplastic composition containing from 60 to weight percent, based on the combined weight of components and of at least one high weight molecular linear ethylene polymer having a density in the range of 0.92 to 0.96g/cc and an I1 melt index in the range of 0.1 to 3g/10 minutes, and from 5 to 40 weight percent, based on the combined weight of components and.(B), of at least one substantially linear ethylene/a-olefin polymer containing at least one a-olefin and having a density in the range of 0.85 to 0.92g/cc and an I2 melt index in the range of 0.3 to 3g/10 minutes, introducing said composition of step into a heated film extrusion apparatus o equipped with an annular die, extruding said composition through said annular die to form a molten or semi- molten thermoplastic tube of said composition that is subsequently blown-up beyond the die diameter and drawn-down through nip and take-off rollers to form a layflat film with a thickness greater than about 1.25 mils (31 microns), and conveying said film formed in step for subsequent use down-line of the blown film extrusion apparatus of step or collecting said film formed in step for subsequent use off-line, wherein said film is characterized as having a tear strength at least 30 percent greater than the tear strength of a comparative polyethylene film having essentially the same density, thickness and melt index.

37. The method of Claim 36 wherein said extrusion apparatus is a variable stalk extrusion film line.

38. The film produced by the method of Claim 37. Dated 5 May 1999 The Dow Chemical Company Patent Attorneys for the Applicant/Nominated Person SPRUSON FERGUSON [R:\LIBH]00796.doc:KWW