AU2557995A - Aluminosilicate cation exchange compounds - Google Patents
Aluminosilicate cation exchange compoundsInfo
- Publication number
- AU2557995A AU2557995A AU25579/95A AU2557995A AU2557995A AU 2557995 A AU2557995 A AU 2557995A AU 25579/95 A AU25579/95 A AU 25579/95A AU 2557995 A AU2557995 A AU 2557995A AU 2557995 A AU2557995 A AU 2557995A
- Authority
- AU
- Australia
- Prior art keywords
- xam
- cations
- material according
- oxide
- cation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
ALUMINOSILICATE CATION EXCHANGE COMPOUNDS
TECHNICAL FIELD
This invention relates to -duminosilicate compounds which have cation exchange capacity and is particularly concerned with such materials having a stuffed silica polymorph-related structure in which the aluminium is tetrahedrally coordinated.
BACKGROUND ART
Kalsilite, nepheline, camegieite and eucryptite are all crystalline minerals of ideal composition MAlSiO4, where M is an alkali metal, having a stuffed silica polymorph-related structure in which the -Quminium is tetrahedrally coordinated.
Kalsilite has ideal composition KAlSiO4, while nepheline exists as a solid-solution and has the composition Na11t K_AlSiO4, where Os_x< l. Both of these minerals have crystal structures closely related to that of the silica polymorph, tridymite (see Figure 1). Camegieite has ideal composition NaAlSiO4 and has a crystal structure closely related to that of the silica polymorph, cristobalite (see Figure 2). Eucryptite has ideal composition LiAlSi04 and has a crystal s ructure closely related to that of the silica polymorph, quartz (see Figure 3).
Tridymite, cristobalite and quartz all have the composition SiO2 and consist of a 3- dimensional framework of comer-connected SiO tetrahedra. Kalsilite, nepheline, camegieite and eucryptite have been described as stuffed derivatives of the tridymite, cristobalite or quartz structures, in that half of the silicon cations in the silicate framework i each case are replaced by aluminium cations. Alkali cations, which are required for charge balance (Si4+ <~> Al3+ + M+, M = alkali) occupy the interstices in the respective frameworks (see Figures 1-3) - hence the descriptions "stuffed tridymite", "stuffed cristobalite", and "stuffed quartz".
In kalsilite, nepheline, camegieite and eucryptite, the interstitial cations, M*, are
not exchangeable under normal conditions, that is, in aqueous salt solution at atmospheric pressure up to - 100 βC. Therefore, kalsilite, nepheline, camegieite and eucryptite have negligible cation exchange capacity (CEC). Any CEC is associated with the surface of crystals and not the bulk of the structure.
It has been proposed in, for example, Roux, J., 1971, C.R. Acad. Sci., Ser D 272, 3225-3227 to exchange the interstitial cations of kalsilite and related aluminosilicates by treating the material at high temperature and pressure under hydrothermal conditions.
It has also been proposed by Sobrados & Gregorkiewitz, 1993, Physics and Chemistry of Minerals, 20, 433-441 to achieve similar exchange of cations by treating kalsilite and related materials with molten salts such as MNO3 or MCI (M = Li, Na, K, Ag).
However, it is widely accepted that aluminosilicates with the stuffed tridymite-type structure have no cation exchange capacity associated with the bulk structure, either in aqueous solution or in organic solvents.
It has been proposed in, for example, Petranovic et al, 1991, Materials Science Monograph, 666, 2229-2236, that it is possible to exchange the interstitial Na+ cation of camegieite with Li+ by treating it with molten LiNO3. Associated with this ability to exchange cations by treatment with molten salts is the property of ionic conductivity which has been observed for camegieite and related materials.
It is also expected that, as for kalsilite and nepheline, exchange of the interstitial cations might be induced under aqueous conditions provided the material were subjected to sufficiently high temperatures and pressures, i.e. under hydrothermal conditions.
However, it is widely accepted that aluminosilicates with the stuffed cristobalite-type structure have no cation exchange capacity associated with the bulk s ructure, either
in aqueous solution or in organic solvents.
It has been proposed in, for example, Berchot et al, 1980, Journal of Solid State Chemistry, 34, 199-205, that while it is not possible to substitute Li* in β-eucryptite by treatment using molten salts with bigger cations such as Na*, K+ or Ag+, exchange by divalent cations Cu2+ and Mn2* is possible under such conditions.
However, it is widely accepted that aluminosilicates with the stuffed quartz-type structure have no cation exchange capacity associated with the bulk stmcture, either in aqueous solution or in organic solvents.
Amorphous derivatives of kaolinite and/or halloysite having large surface areas (BET surface area of at least 45 m2 g'1) and cation exchange capacity are described in International patent application WO95/00441 and related applications (including in the United States of America), the contents of which are incorporated herein by reference.
In WO95/00441 the amorphous derivatives of kaolinite and/or halloysite (referred to as "KAD") are produced by a process which comprises reacting a kaolin group mineral with an aqueous alkali halide, wherein the mole ratio of alkali metal hahde to the kaolin group mineral is from 5 to the saturation concentration of the alkali metal halide. KAD is characterised as a result of this production process by the presence of halide and substantial amounts of structural water, whether as bound water or as hydroxyl, in its composition.
SUMMARY OF THE INVENTION
According to the present invention there is provided a poorly or partly crystalline alkali metal aluminosilicate material having a stuffed silica polymorph-related stmcture in which the aluminium is predominantly tetrahedrally coordinated and a cation exchange capacity (CEC) at room temperature of at least 1 meq 100 g"1 in aqueous solution, which is produced by reacting an aluminosilicate, or a
combination of aluminium ---tide-containing and silicon oxide-containing compounds, with an alkali oxide-containing reagent. Compounds in accordance with the invention are, for convenience only, hereinafter collectively referred to as XAM.
Also according to the present invention, there is provided a process for the preparation of a poorly or partly crystalline alkali metal aluminosilicate material having a stuffed silica polymorph related-structure in which the aluminium is predominantly tetrahedrally coordinated and a cation exchange capacity at room temperature of at least 1 meq lOOg'1 in aqueous solution, in which an aluminosilicate, or a combination of aluminium oxide-containing and silicon oxide - containing compounds, are reacted together with an alkali oxide-containing reagent.
Further, the present invention extends to uses of XAM and/or of XAM which has been subjected to partial or full exchange of the alkali metal cation.
By stuffed silica polymorph-related structure is meant any alkali metal aluminosilicate material with the structure type of any of the stuffed silica polymorphs defined above. The interstitial cation may therefore be K*, Na*, or Li +, as in kalsilite, camegieite, or eucryptite, respectively. When XAM is prepared with K* as the interstitial cation a kalsilite-related structure is obtained, when prepared with Na+ a carnegieite-related stmcture is obtained, and when prepared with Li* a eucryptite-related structure is obtained. XAM may be prepared with other alkali cations, Rb* and Cs*, in which cases kalsilite-related structures are obtained. The interstitial sites in XAM may also be occupied by a mixture of two or more such cations, as in nepheline, or a mixture of alkali metal and one or more other cations, such as transition metal cations and alkaline earth cations. XAMs involving mixtures of interstitial cations typically possess the stuffed silica polymorph-related stmcture of the dominant interstitial cation. Alkali metal cations are the preferred cations, in particular K*, Na* and Li*.
Central to the present invention is the discovery that XAM can have a significant CEC in aqueous solution at room temperature. XAM preferably has a CEC of at
least 5 ------^equivalents per 100 grams (meq lOOg'1), most preferably greater than
10 meq lOOg'1, and in many embodiments will have a CEC of at least 100 meq lOOg"1. When well-prepared, XAM may have a CEC ≥ 250 meq lOOg'1, for example up to 750 meq lOOg'1, with a significant majority of the interstitial cations being exchangeable by other cations in aqueous solution at room-temperature. This discovery is in contrast to the properties of well-crystallised, ordered kalsilite-, nepheline-, camegieite-, and eucryptite-type -ϋuminosilicates which have CECs typically less than 1 meq 100 g'1 per 100 grams.
XAM can be prepared by a large number of synthetic processes preferably involving solid state reactions, and several of these processes are described below. Essential to the synthesis of XAM are reactive starting materials, that is, components or component precursors which facilitate reaction at relatively low temperatures. More rigorous conditions normally associated with the formation of aluminosilicates such as kalsilite and camegieite, for example, annealing components at -- 1000 °C overnight, produce materials which do not display the cation exchange properties of XAM, and which are normally well-crystallised and ordered.
To facilitate relatively mild reaction conditions for the formation of XAM it is advantageous to use an aluminosilicate starting material which, by definition, contains aluminium and silicon cations mixed on the unit cell, that is the nanometre, scale.
Aluminosilicate phv-losilicates are, in general, suitable reactive starting materials for the formation of XAM. Such phyllosilicates include the clay minerals, illite, vermicuhte, mon-morillonite, beidellite, bentonite, kaolinite and halloysite, as well as the minerals, pyrophyllite, muscovite and palygorskite. While there is a significant range in the silicon and aluminium contents among these starting materials, all are considered, to a greater or lesser extent, to be a suitable source of aluminosilicate in the synthesis of XAM. Other alximinosilicate minerals such as zeolites, imogolite and allophane, are also considered suitable.
One of the other advantages that mineral aluminosilicates have as reactive starting materials is their high natural abundance and low unit cost.
Various alkali salts and hydroxides are suitably reactive starting materials which provide a source of the alkali cations. Most alkali salts which decompose upon heating at a temperature up to 1000 βC to give alkali oxide are suitable. The most preferred salts are carbonates. Other preferred salts are bicarbonates, nitrates and carboxylates.
It is also possible to use reactive forms of silica, such as silica gel and colloidal silica, in combination with reactive forms of alumina, such as aluminium nitrate nonahydrate, bayerite and aluminium hydroxide gel, to provide the source of aluminosUicate for the formation of XAM. Alternatively, possible combinations of reactive starting materials are sodium nitrate or sodium carbonate with alumino- silicic gel, and gibbsite or boehmite with sodium silicate glass.
Preferred reaction conditions are 750 "C or less, for example 300 βC to 750 βC at atmospheric pressure for periods of time of, for example, 15 minutes to 24 hours. Reaction in air in an open vessel is preferred, but the reaction will proceed under different atmospheres and /or under reduced pressure provided the system is not closed.
BRIEF DESCRIPTION OF THE DRAWINGS
Various embodiments of XAMs, uses for them and processes for producing them will now be described by way of example only with reference to the accompanying drawings, in which:
Figure 1 shows polyhedral representations of Mgh-tridymite (Siθ2) and kalsilite (KAlSiO4), projected down the < 110 > direction. The stmcture of kalsilite shows the layers of interstitial and framework cations (dashed lines) which give rise to the strong X-ray diffraction (XRD) peak at - 3.1 A
Figure 2 shows polyhedral representations of high-cristobalite (Siθ2) and
high-carnegieite (NaAlSiO4), projected down the cubic <110> direction. The structure of high-carnegieite shows the layers of interstitial and framework cations (dashed lines) which give rise to the strong X-ray diffraction peaks at -4.2 and - 2.6 A; Figure 3 shows polyhedral representations of high-quartz (SiOj) and high- eucryptite (LiAlSi04), projected down the < 110 > direction. The stmcture of high- eucryptite shows the layers of interstitial and framework cations (dashed lines) which give rise to the strong X-ray diffraction peak at - 3.6 A;
Figure 4 shows ^Al MAS NMR spectra collected at 104.228 MHz of a) K- XAM prepared according to a first process described below using kaolinite and K2CO3 heated for 3 hours at 500 βC (Example 2); and b) Na-XAM prepared according to the first process using kaolinite and Ha^C03 heated for 3 hours at 500 °C (Example 4);
Figure 5 shows XRD profiles of K-XAM (d) and Na-XAM (c) prepared according to Examples 1 and 3, respectively. The XRD profiles of the same K-XAM (b) and Na-XAM (a) heated at 1000 βC for 16 hours showing well crystallised kalsilite (peaks indicated by *) and nepheline (peaks indicated by + ) are juxtaposed. Nepheline is the thermodynamically stable form of NaAlSiO4 under these conditions; Figure 6 shows XRD profiles of K-XAM (d) prepared according to Example
2. The XRD profiles of the same K-XAM heated at 850 βC (c), 900 βC (b), and 1000 βC (a) for 16 hours are juxtaposed. The series shows progressive increase in crystallinity with temperature, particularly the evolution of the broad peak at - 29 β 2θ into the strong sharp 102 reflection of well-crystallised kalsilite. Peaks belonging to well crystallised kalsilite are indicated by *;
Figure 7 shows XRD profiles of Na-XAM (e) prepared according to Example 4. The XRD profiles of the same Na-XAM heated at 665 βC (d), 800 βC (c), 900 βC (b), and 1000 "C (a) for 16 hours are juxtaposed. The series shows the increase in crystallinity with temperature, particularly the evolution of the broad composite peak between - 18 " and -34 ° 2θ into the strong sharp 111 and 220 reflections of well-crystallised high-carnegjeite, followed by transformation into well- cryst aHised nepheline. Peaks belonging to well-crystallised camegieite and nepheline
are indicated by * and + respectively;
Figure 8 shows XRD profiles of Li-XAM prepared according to Example 5 (g) and Example 6 (f), Rb-XAM prepared according to Example 10 (e) and Cs- XAM prepared according to Example 11 (d). The XRD profiles of the same Li- XAM (Example 6) (c), Rb-XAM (b) and α-XAM (a) heated at 1000 βC for 16 hours are juxtaposed. Figure 8f and 8c show the evolution of the broad composite peak between - 18 β and - 25 • 2θ into the sharp 100 and 102 reflections of well- crystallised high-eucryptite at 1000 βC (peaks indicated by *). Figures 8a and 8b show XRD profiles of well-crystallised Cs- and Rb-containing kalsilite-related materials, respectively (peaks indicated by ★ and +, respectively);
Figure 9 shows XRD profiles of mixed K/Na-XAM (d) and Na-XAM (c) prepared according to Examples 7 and 20, respectively. The XRD profiles of the same K/Na-XAM (b) and Na-XAM (a) heated at 1000 "C for 16 hours showing well crystallised kalsilite-type (peaks indicated by *) and nepheline (peaks indicated by + ) are juxtaposed; peaks indicated by * belong to partly crystalline ca egieite;
Figure 10 shows XRD profiles of the series of K-XAMs prepared according to Example 12, 033 g K2CO3 (g), 0.49 g K_,CO3 (0, 0.66 g K-,CO3 (e), and of Na-
XAMs prepared according to Example 14, 43.7 g Na2CO3 (d), and 131 g Na2CO3
(c). The XRD profiles of the same Na-XAMs heated at 1000 βC for 16 hours showing well-crystallised nepheline and camegieite (peaks indicated by * and + , respectively) are given as 10b (43.7 g) and 10a (131 g);
Figure 11 shows XRD profiles of K-XAMs prepared according to Example 8 (f), Example 15 potassium nitrate (e) and potassium acetate (d), and of Na-XAMs prepared according to Example 9 (c), Example 16 sodium nitrate (b) and sodium citrate (a);
Figure 12 shows XRD profiles of K-XAM (d) and Na-XAM (c) prepared from montmorillonite according to Example 17. The XRD profiles of the same K-
XAM (b) and Na-XAM (a) heated at 1000 βC for 16 hours showing well crystallised leucite-like (peaks indicated by +) and albite-like (peaks indicated by *) phases, respectively, are juxtaposed;
Figure 13 shows XRD profiles of K-XAM (d) and Na-XAM (c) prepared from pyrophyilite according to Example 18. The XRD profiles of the same K-XAM
(b) and Na-XAM (a) heated at 1000 βC for 16 hours showing similar broad diffraction features to the as-prepared XAMs are juxtaposed. In the as-prepared M-XAMs, diffraction peaks due to quartz impurity and unreacted pyrophyllite are indicated by ★ and o, respectively; Figure 14 shows XRD profiles of K-XAM (d) and Na-XAM (c) prepared from colloidal silica, aluminium nitrate and alkali carbonate according to Example 19. The XRD profiles of the same K-XAM (b) and Na-XAM (a) heated at 1000 βC for 16 hours showing well crystallised kalsilite-like and carnegieite-like phases, respectively, are juxtaposed. Peaks belonging to well-crystallised camegieite, nepheline and kalsilite are indicated by *, ★, and + respectively;
Figure 15 shows XRD profiles of Na-XAMs prepared from colloidal silica, aluminium nitrate and sodium carbonate according to Example 21 at Al.Si ratios of 0.2:1.0 (d) and 2.0:1.0 (c). The XRD profiles of the same Na-XAMs heated at 1000 °C for 16 hours, 0.2:1.0 (b) and 2.0:1.0 (a) showing unchanged profiles are juxtaposed.
DETAILED DESCRIPTION OF THE INVENTION
Structure and composition of XAM.
XAM is most uniquely characterised in terms of its structure and composition.
The structures of the various M-XAMs (M = alkali metal) are characterised most definitively by X-ray powder diffraction. When well prepared the various M-XAMs give X-ray powder diffraction profiles which display the broad diffraction peaks characteristic of the protocrystalline stuffed silica polymorphs. They are not amorphous, as their X-ray powder diffraction profiles display nascent diffraction peaks of the stuffed silica polymorphs. The diffraction profile in each case is primarily dependent on the alkali metal, M. The characteristic XRD profiles for the various M-XAMs can be seen in Figures 5 - 9.
Further verification that a material is XAM can be obtained by heating these poorly
or partly crystalline materials at sufficiently high temperature for sufficient time that they become well-crystallised, for example, at 1000 βC for 16 hours. Provided the stoichiometry of the XAM is reasonably close to that of one of the ideal stuffed silica polymorphs, kalsilite, nepheline, camegieite or eucryptite, namely MA1S-O4, M = alkali metal, then the dominant peaks in the XRD of the crystalline material will be characteristic of one or more of these polymorphs.
If the stoichiometry of the XAM is significantly different from one of the ideal stuffed silica polymorphs, then other crystalline phases, for example, albite, NaAlSi3O8 and leucite, KAlSijOg, can be observed (see Figures 12b and 12a, respectively). If the stoichiometry of the XAM is sufficiently exotic or the framework atoms not sufficiently homogeneous then it is possible that the poorly crystalline XAM will not transform into a more crystalline solid under these conditions (see Figures 15a and 15b).
Furthermore, as the stmcture of XAM is related to the stuffed silica polymorphs, it also comprises a framework aluminosilicate structure in which both the silicon and aluminium cations are tetrahedrally coordinated. ^Al nuclear magnetic resonance (NMR) is sensitive to the coordination environment of aluminium, that is, whether the cation is 4, 5 or 6 coordinated. The ^Al magic angle spinning (MAS) NMR spectra of K-XAM and Na-XAM prepared at 500 βC each give a single peak at - 57 ppm (FWHM = - 23 ppm) (see Figure 4) which is interpreted as tetrahedrally coordinated aluminium. For these materials there is evidence of only very minor proportions (≤ 3%) of octahedrally coordinated aluminium due possibly to unreacted starting material, kaolinite in which the aluminium is octahedrally coordinated, or to reaction byproducts or mineral impurities containing octahedrally coordinated aluminium,
The XRD profiles observed for XAMs are dependent on the choice of starting reagents and reaction conditions. They are also sometimes complicated by the presence of unreacted starting materials, reaction byproducts or impurity minerals, such as quartz and anatase, when naturally-occurring components are used.
When K-XAM is poorly crystalline and free from unreacted starting material and reaction byproducts, its XRD profile comprises a single very broad diffraction peak (see Figures 5d and 6d) which corresponds to the 102 reflection in kalsilite. This broad peak indicates that, while other long-range ordering is absent in these poorly crystalline K-XAMs, there is still periodic stmcture (protoc-yst--llini.y) associated with the layers of interstitial and framework cations (refer to - 3.1 A layers indicated by dashed lines in Figure 1). When heated at higher temperatures the K- XAM transforms into well-crystallised kalsilite and the resultant diffraction peaks can be indexed accordingly.
When Rb-XAM and Cs-XAM are poorly crystalline and free from unreacted starting material and reaction byproducts their XRD profiles (Figures 8e and 8d respectively) are dominated by a single very broad diffraction peak corresponding to the 202 reflections of their kalsilite-related structures (see Table 1). As for K- XAM these broad peaks are associated with slightly increased layer spacing due to the larger cation size. When heated at higher temperatures the Rb-XAM and Cs- XAM transform into well-crystallised kalsilite-related materials (Figures 8b and 8a respectively) and the resultant diffractions patterns can be indexed accordingly.
When Na-XAM is poorly crystalline and free from unreacted starting material and reaction byproducts its XRD profile comprises a composite of two overlapping broad diffraction peaks (see Figures 5c and 7e) which correspond to the 111 and 220 peaks of high-carnegieite. These broad peaks indicate that, while other long- range ordering is absent in these poorly crystalline Na-XAMs, there is still periodic stmcture (protocrystallinity) associated with the layers of interstitial and framework cations (refer to - 4.2 and 2.6 A layers indicated by dashed lines in Figure 2). When heated at higher temperatures the peaks initially sharpen and other high- carnegieite peaks appear (see Figure 7), then upon further heating the material begins to transform to well-crystallised nepheline and the resultant diffraction peaks can be indexed accordingly.
When Li-XAM is poorly crystalline and free from unreacted starting material and
reaction byproducts its XRD profile comprises a composite of two broad overlapping diffraction peaks (see Figure 8f) which corresponds to the 100 and 102 peaks of high-eucryptite. This broad composite peak indicates that, while other long-range ordering is absent in these poorly crystalline Li-XAMs, there is still periodic stmcture (protocrystallinity) associated with the layers of interstitial and framework cations (refer to - 3.6 A layers indicated by dashed lines in Figure 3). When heated at higher temperatures the Li-XAM transforms into weU-crystallised eucryptite and the resultant diffraction peaks can be indexed accordingly.
The d-spacings, relative intensities and derived unit cell dimensions for selected examples of these well-crystallised materials derived from Cs-XAM, Rb-XAM, K- XAM, Na-XAM and Li-XAM are listed in Table 1.
Table 1 - CrystaUographic data of well-crystallised materials derived from various XAMs in Figures 5-8.
XAMs can also generally be characterised by a specific surface of less than 45 m2g-1- Preferably the specific surface is at least 0.1 π^g"1, more preferably at least 1 m2 g'1, most preferably at least 5 m2 g"1. Specific surfaces of 45m2g'1 or more are very unlikely to be achieved using solid state reaction processes unless very high specific surface reagents are used. Kaolin group minerals are the most preferred aluminosilicate reagents and do not have sufficiently high specific surfaces to produce XAMs by a solid state reaction process with specific surfaces of 45m2g'1 or more.
M-XAM can be further characterised by its composition when it is dehydrated, that is, when it is free of adsorbed water. Its composition range is given by
MpAl-Si^O^H .1
where M = alkali, 0.0 < p ≤ 2.0, 0.0 ≤ q < 1.0, 1.5 ≤ r ≤ 3.0, and 0.0 ≤ s ≤ 0.1. It should be noted that this general formula does not account for minor amoimts of
other elements being present in the XAM structure, e.g. Fe, Mg, or Ca, nor does it account for impurity minerals or compounds which are not integrated into the XAM structure, e.g. TiO2-anatase, SiO2-quartz.
The water identified in the empirical composition may be present as hydroxyl or bound water. Free water and adsorbed water, that is, water which can be removed by heating the M-XAM at 400°C for 16 hours, is not included in the composition. Thermogravimetric analysis of M-XAM to 1000 βC is able to determine the amount of water present as hydroxyl or bound water, and selected data are presented in Table 2.
Composition analyses and derived formulae (corresponding to formula 1) of several M-XAMs are also given below in Table 2 with cross-references to the synthesis examples described hereinafter. It is believed that unreacted reagent anions which may be used in the synthesis of XAM, for example, carbonate, bicarbonate, nitrate, are also not integrated into the XAM structures, and it is for this reason that they are not included in the empirical compositions.
Table 2 - Composition of XAMs*
Weight % as oxide implied formula XAM Na O M O AI2O3 SiO K O CaO T1O2 Fe2O r s
Determined using quantitative X-ray spectroscopy ( DS). Values not given indicate amount below detection limit.
Table 2 cont. - Composition of XAMs
XAM Na2O
K-XAM Example 19 1.2
Na-XAM Example 19 25.5
Na-XAM Ex.21 2.0: 1 10.8
Na-XAM Ex.21 0.2: 1 1 1.1
K-XAM Example 17 1.15
Na-XAM Example 17 12.6
K-XAM Example 18 1.2
Na-XAM Example 18 1 1.4 0.2 8.8 77.6 1.0 0.1 0.2 0.8 0.27 0.12 2.08
0.02
* Determined using quantitative X-ray spectroscopy (EDS). Values not given indicate amount below detection limit. t Lithium contents assumed as charge balancing with aluminium in the eucryptite-related structure
Synthesis of XAM
XAMs are prepared by a process in which an aluminosilicate, or a combination of aluminium oxide-containing and silicon oxide - rant-lining compounds, are reacted together with an alkali oxide-containing reagent. Preferably the reaction is a solid state reaction, and three such reaction processes for the synthesis of XAM are described generally below. However, aqueous reactions may also produce acceptable XAMs.
Process 1
The first process involves solid state reaction of oxide-containing alkali salt and aluminium-containing phyllosilicates. The range of conditions for the successful formation of XAM by this process is dependent on the aluminium-containing phyllosilicate used.
While many oxide-containing alkali salts and all aluminiiim-containing phyllosilicates are suitable as starting materials for this process, we exemplify the process using alkali carbonate and kaolin group minerals, which are among the preferred starting materials.
In this first process the mole ratio of alkali carbonate (M2CO3) to the kaolin group mineral (Al^O^OH^) is preferably from 0.05 to 2, and most preferably is in the range of 0.5 to 1.
Reaction is suitably carried out at an elevated temperature at atmospheric pressure for a sufficient period of time to enable conversion to XAM. Initially, the kaolin group mineral and alkali carbonate are intimately mixed then heated to between 300 and 750 βC until all the kaolin group mineral has reacted The preferred conditions for this process are 450 to 550 βC for a period of between 3 and 24 hours. The resultant solid contains XAM which is usually free of reaction byproducts, but may contain some unreacted M2CO3 which can be removed by rinsing with cold water.
Process 2
The second process involves solid state reaction of alkali hydroxide and aluminium- containing phyllosilicates. The range of conditions for the successful formation of XAM by this process is dependent on the aluminium-containing phyilosilicate used. We exemplify the second process using kaolin group minerals, which are among the preferred starting materials.
In this second process the mole ratio of alkali hydroxide (MOH) to the kaolin group mineral (Al^O^OH^) is preferably from 0.1 to 4, and most preferably is in the range of 1.0 to 2.0.
Reaction is suitably carried out at an elevated temperature at atmospheric pressure for a sufficient period of time to enable conversion to XAM. Initially, the kaolin group mineral and alkali hydroxide are intimately mixed then heated to between 400 βC and 750 βC until all the kaolin group mineral has reacted. The preferred conditions for this process are 500 βC to 550 βC for a period of between 3 and 24 hours. The resultant solid contains XAM which is usually free of reaction byproducts, but may contain some unreacted MOH which can be removed by rinsing with cold water.
Process 3
The third process involves solid state reaction of reactive forms of silica and alumina with alkali oxide-containing reagent. We exemplify the third process using colloidal silica, aluminium nitrate nonahydrate and alkali carbonate (M2CO3: M = alkali).
In this third process, the mole ratios of colloidal silica ( - SiO^ to aluminium nitrate nonahydrate (Al(NO3)3).9H2O) to alkali carbonate (M2CO3) are typically 2:2:1, but can vary substantially from this within the composition range described earlier for XAM. It is possible to replace the colloidal silica by other forms of silica, such as soluble alkali silicate.
Reaction takes place by dissolving the aluminium nitrate nonahydrate and alkali carbonate in a small amount of water then adding the colloidal silica to the dissolved salts. The reaction mixture is homogenised then the water evaporated slowly, giving a gel. This gel is then further reacted at elevated temperature and atmospheric pressure for a sufficient period of time to enable conversion to XAM. The gel is heated to between 300 βC and 750 βC until XAM is observable by XRD. The preferred conditions for this process are 550 βC to 650 βC for a period of between 2 days and 6 hours. The resultant solid contains XAM which is free of starting materials and is usually free of reaction byproducts.
Examples of specific conditions of synthesis.
Examples of the specific conditions of synthesis under which the components react together to give XAM are given below.
1. A mixture containing 2.6 g of kaolinite from Weipa, Australia, and 1.6 g of K2CO3 was dispersed in a small amount of distilled water to give a thick slurry. The slurry was dried at - 50 βC, then heated at 500 βC in a platinum vessel for 16 hours. The reaction products were then thoroughly rinsed with distilled water to remove excess K2CO3, then dried at 100 *C. The dried reaction products weighed 2.7 g and comprised single phase K-XAM. The XRD profile for this material as prepared is shown in Figure 5.
2. 2 kg of kaolinite from Skardon River, Australia, was dispersed in 4.7 litres of water. A solution containing 0.92 kg of commercial grade K2C03 in 3.5 Utres of water was slowly added, and the resultant slurry was stirred vigorously for 20 minutes. This slurry was dehydrated using a spray drier with an inlet temperature of 250 βC. The spray dried reaction mixture was heated at 500 βC for 3.5 hours. Excess K2CO3 was removed by repeated rinsing with water until the pH of the elute dropped to - 9. The BET surface area of this material was 7.86 m2g l. The XRD profile of this material as prepared is shown in Figure 6.
3. A mixture containing 10.24 g of kaolinite from Weipa, Australia, and 4.24 g of Na2CO3 was dispersed with 10 ml of distilled water to give a slurry. The slurry was partially dried at - 50 "C, then heated at 600 βC in an alumina vessel for 16 hours. The resultant dry reaction product was remixed witii water, again partly dried, then heated at 600 βC for 7 hours. The reaction product was thoroughly rinsed with distilled water to remove excess N-^CO^ then dried at 100 βC. The dried reaction products weighed 9.0 g and comprised single phase Na-XAM. The XRD profile for this material is shown in Figure 5.
4. 1 kg of kaohnite from Skardon River, Australia, was dispersed in 2.33 litres of water. A solution containing 0365 kg of commercial grade Na_.CO3 in 1 litre of water was slowly added and the resultant slurry was stirred vigorously for 20 minutes. This slurry was dehydrated using a spray drier with an inlet temperature of 250 °C. The spray dried reaction mixture was heated at 500 "C for 3.5 hours. Excess Na2CO3 was removed by repeated rinsing with water until the pH of the elute dropped to - 9. The BET surface area of this material was 24.50 m 1. The XRD profile of this material as prepared is shown in Figure 7.
5. A mixture containing 2.5 g of kaohnite from Skardon River, Australia, and 0.7 g of AR grade Li2CO3 was dispersed in a small amount of distilled water to give a thick slurry. The slurry was dried at 100 *C, then heated at 460 °C in an alumina vessel for 16 hours. The reaction product was remixed with water to give a thick slurry, dehydrated at 100 "C then heated again at 460 βC for 3.5 hours. These reaction products were throroughly rinsed with distilled water to remove excess Li2CO3, then dried at 100 βC The dried reaction products weighed 2.0 g and comprised single phase Li-XAM. The XRD profile for this material as prepared is shown in Figure 8.
6. 200g of kaolinite from Skardon River, Australia, was dispersed in 470 ml of water. A solution containing 134 g of AR grade lithium acetate dihydrate in 350 ml of water was slowly added and the resultant slurry was stirred vigorously for 30 minutes. This slurry was dehydrated using a spray drier with an inlet temperature
of 250 βC. The spray dried reaction mixture was heated at 500 βC for 16 hours. Excess lithium acetate was removed by repeated rinsing with water until the pH of the elute dropped to - 9. The XRD profile of this material as prepared is shown in Figure 8.
7. 200g of kaolinite from Skardon River, Australia, was dispersed in 472 ml of water. A solution containing 36.5 g of commercial grade Na2CO3 and 46 g of commercial grade K-.CO3 in 350 ml of water was slowly added and the resultant slurry was stirred vigorously for 20 minutes. This slurry was dehydrated using a spray drier with an inlet temperature of 250 βC. The spray dried reaction mixture was heated at 500 βC for 3 hours. Excess Na_.C03 and K2CO3 were removed by repeated rinsing with water until the pH of the elute dropped to ~ 9. The XRD profile of this material as prepared is shown in Figure 9.
8. 1.28 g of kaolinite from Weipa, Australia, was thoroughly dry mixed with 0.5 g of finely powdered KOH. The mixture was heated in a platinum vessel at 500 βC for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess KOH, then dried at 100 βC. The dried reaction products weighed 1.20 g and comprised single phase K-XAM. The XRD profile for this material as prepared is shown in Figure 11.
9. 1.28 g of kaolinite from Weipa, Australia, was thoroughly dry mixed with 0.4 g of finely powdered NaOH. The mixture was heated in a platinum vessel at 500 βC for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess NaOH, then dried at 100 βC. The dried reaction products weighed 1.1 g and comprised single phase Na-XAM. The XRD profile for this material as prepared is shown in Figure 11.
10. A mixture containing 2.5 g of kaolinite from Skardon River, Australia, and 2.3 g of AR grade Rb2CO3 was dispersed in a small amount of distilled water to give a thick slurry. The slurry was dried at 100 βC then heated at 460 βC in an alumina vessel for 16 hours. The reaction products were thoroughly rinsed with distilled
water to remove excess Rb^CO^ then dried at 100 βC. The dried reaction products weighed 3.15 g and comprised single phase Rb-XAM. The XRD profile for this material as prepared is shown in Figure 8.
11. A mixture containing 2.5 g of kaolinite from Skardon River, Australia, and 3.5 g of AR grade Cs_.CO3 was dispersed in a small amount of distilled water to give a thick slurry. The slurry was dried at 100 βC, then heated at 460 βC in an alumina vessel for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess C-^CO^ then dried at 100 βC. The dried reaction products weighed 4.18 g and comprised single phase Cs-XAM. The XRD profile for this material as prepared is shown in Figure 8.
12. Four separate mixtures containing 1.28 g of kaolinite from Skardon River, Australia, and 0.85, 0.66, 0.49 and 0.33 g, respectively, of K2CO3 were each dispersed in a small amount of distilled water to give a thick slurry. The slurries were dried at - 50 "C, then heated at 500 βC in alumina vessels for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess K2CO3 then dried at 100 βC. The dried reaction products weighed 1.59, 1.32, 1.31 and 1.2 g, respectively, and comprised single phase K-XAM. The XRD profiles for three of these as-prepared materials are shown in Figure 10.
13. Two separate mixtures containing 5.12 g of kaohnite from Skardon River, Austraha, and 2.12 g of commercial grade N-^COj, and 1.28 g of the same kaolinite and 0.42 g of N-ijCOj, were each dispersed in a small amount of distilled water to give a thick slurry. The slurries were dried at 100 *C, then heated at 600 βC in alumina vessels for 16 hours. The reaction products were then thoroughly rinsed with distilled water to remove excess Na2CO3 then dried at 100 βC.
14. Two separate spray dried reaction mixtures were prepared at different mole ratios. Two aliquots of 200 g of kaolinite from Skardon River, Australia, were each dispersed in 492 ml of water. Solutions containing 43.7 g of commercial grade Na2CO3 in 125 ml of water and 131 g of commercial grade Na-jCOj in 500 ml of hot
water were slowly added and the resultant slurries were stirred vigorously for 20 minutes. These slurries were dehydrated using a spray drier with an inlet temperature of 250 "C. The spray dried reaction mixture was heated at 500 *C for 3.5 hours. Excess Na2CO3 was removed in each case by repeated rinsing with water until the pH of the elute dropped to - 9. The XRD profiles of the respective materials as prepared are shown in Figure 10.
15. Two separate mixtures containing 1.28 g of kaolinite from Skardon River, Australia, and 1.0 g of KNO3, and 1.0 g of potassium acetate were dispersed in a small amounts of distilled water to give thick slurries. The slurries were dried at 100 βC, then heated at 450 βC in alumina vessesl for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess potassium salt then dried at 100 βC. The dried reaction products each weighed 1.3 g. The nitrate and acetate products comprise single phase K-XAM. The XRD profiles for these materials are shown in Figure 11.
16. Two separate mixtures containing 2.56 g of kaolinite from Skardon River, Australia, and 1.7 g of NaNO3 and 2.0 g of sodium citrate were dispersed in a small amount of distilled water to give thick slurries. The slurries were dried at 100 "C, then heated at 450 °C in alumina vessesl for 16 hours. The reaction products were thoroughly rinsed with distilled water to remove excess sodium salt, then dried at 100 βC. The dried reaction products weighed 2.02 and 2.2 g respectively. The nitrate and citrate products comprise single phase Na-XAM. The XRD profiles for these materials are shown in Figure 11.
17. Two separate mixtures containing 1.00 g of montmorillonite from Texas, USA, and 0.41 g of K2CO3, and 0.27 g of NajCOj were dispersed in a small amount of distilled water to give slurries. The slurries were partially dried at - 50 βC, then heated at 600 ° C in an alumina vessel for 16 hours. The resultant potassium dry reaction products were remixed with water, again partly dried, then heated at 600 βC for 16 hours. Both reaction products were thoroughly rinsed with distilled water to remove excess K-,C03 and NajCO then dried at 100 βC. The dried
reaction products weighed 0.88 and 0.75 g respectively. The XRD profiles for these materials are shown in Figure 12.
18. Two separate mixtures containing 1.00 g of pyrophyilite and 0.46 g of K2CO3, and 0.30 g of N-^COj were dispersed in a small amount of distilled water to give slurries. The slurries were partially dried at - 50 β then heated at 600 βC in an alumina vessel for 16 hours. The resultant sodium dry reaction products were remixed with water, again partly dried, then heated at 600 βC for 16 hours. Both reaction products were thoroughly rinsed with distilled water to remove excess K2CO3 and Na2CO3, then dried at 100 βC. The dried reaction products weighed 0.85, 0.67 g respectively. The XRD profiles for these materials are shown in Figure 13.
19. To 5 ml of distilled water were added 3.75 g of aluminium nitrate nonahydrate and 0.53 g of anhydrous sodium carbonate or 0.825 g of potassium carbonate hydrate. 1.58 g of Ludox AM (du Pont) colloidal silica was added to this solution and stirred for 30 minutes. The resultant solution was evaporated to dryness at 100 "C in a platinum crucible, then heated at 500 βC for 16 hours. The dried reaction product was poorly crystalline single phase Na-XAM or K-XAM, depending on the carbonate used. The XRD profiles for these reaction products are shown in Figure 14.
20. A mixture containing 2.56 g of halloysite from Mataura Bay, New Zealand, and 1.04 g of commercial grade N_-2CO3 was dispersed in a small amount of distilled water to give a thick slurry. The slurry was dried at 100 βC, then heated at 460 βC in an alumina vessel for 16 hours. The reaction product was remixed with water to give a thick slurry, dehydrated at 100 'C, then heated again at 460 βC for 3.5 hours. The reaction products were thoroughly rinsed with distilled water to remove excess then dried at 100 βC. The dried reaction products weighed 1.8 g and comprised single phase Na-XAM. The XRD profile for this material is shown in Figure 9.
21. Two extreme compositions of Na-XAM were prepared as follows.
To give an Al:Si ratio of 0.2:1.0, 5 ml of distilled water were added to 1.875 g of aluminium nitrate nonahydrate and 0.265 g of anhydrous sodium carbonate. 3.9 g of Ludox AM (du Pont) colloidal silica was added to this solution and stirred for 30 minutes. The resultant solution was evaporated to dryness at 100 βC in a platinum crucible, then heated at 500 βC for 16 hours. The dried reaction product weighed 1.32 g and was single phase Na-XAM.
To give a Al:Si ratio of 2.0:1.0, 5 ml of distilled water were added to 3.7 g of aluminium nitrate nonahydrate and 0.53 g of anhydrous sodium carbonate. 0.8 g of Lύdox AM (du Pont) colloidal silica was added to this solution and stirred for 30 minutes. The resultant solution was evaporated to dryness at 100 βC in a platinum crucible, then heated at 500 βC for 16 hours. The dried reaction product weighed 0.7 g and was single phase Na-XAM. The XRD profiles for these reaction products are shown in Figure 15.
Properties of XAM
In XAM it is possible to exchange, at least partly, the alkali metal cation with any cation which is stable in aqueous solution. Such exchange cations include other alkali metal cations, alkaline earth cations, transition metal cations, lanthanide and actinide cations, other metal cations and ammonium. There are many transition metal cations (e.g. Co2*, Ni2*, Cu2+, Fe2*), lanthanide cations (e.g. La3*) other metal cations (e.g. Pb2*, Cd2*, Zn2*) and actinide cations (e.g. UO2 2*) which show high levels of cation exchange for XAM prepared under certain conditions. However, the extent of exchangeability of cations depends on the method of preparation of XAM and the conditions of the exchange reaction, such as temperature, time and concentration of exchange solution.
Table 3 lists the percent cation exchange for a selection of cations for a range of XAMs. Cation exchange was performed using concentrated solutions (typically
>5M) of the relevant soluble salt, except for UO2 2* which used a 0.33 M uranyl nitrate solution and La3* which used a 0.65 M solution.
Table 3 - Cation exchange capacity* (CEC) derived from replacement of alkali metal§ in selected XAMs
200
381
Weight percent as oxide of exchange cation* for a range of cations
Cu + Cd2+ Pb2+ Mg2+ Zn2+ Ca + La3+ UO2 2+ Fe3+ Ni2+ Co2+
K-XAM Example 2 48.3 8.7 28.5 8.0 39.1 3.5 10.0 21.9 4.3 31.0 33.5
Na-XAM Example 4 39.3 7.6 34.8 8.3 31.6 3.9 9.8 22.8 5.2 40.0 33.1
* milliequivalents per 100 g determined as percent removal of alkali cation § reduction of alkali metal determined by X-ray spectroscopy (EDS) t exchange cation content determined by X-ray spectroscopy (EDS)
In aqueous suspension, XAM has a particular affinity to certain cations. The cations include the alkaline earths Mg2*, Sr2* and Ca2*, the transition metals Cu2*, Ni2*, Co2*, Ag\ Fe2*, Cr3* and Mn2*, the other metal cations Al3*, Zn2*, Cd2*, Pb2* and Hg2*, the lanthanide Nd3*, and the actinide-containing cation UO2 2*. It is expected that XAM will also have affinity to other aqueous cations with similar size, shape and charge to those listed above. Also, due to the similar chemical behaviour of divalent lanthanides it is assumed that the properties demonstrated for Nd3+ will apply to all trivalent lanthanides, including Y3*.
The affinity of XAM for these cations has been demonstrated by measuring the percent uptake of each of these cations from a solution containing a low concentration (10-100 ppm) of the subject cation and a relatively high concentration of Na* (0.1 M). The details of selectivity experiments together with their results are given in Table 4. The level of selectivity of XAM towards these cations is relatively independent of temperature but the rate of exchange is significantly enhanced by increase in temperature.
For the purposes of this invention, to identify those cations for which M-XAM (M = alkali metal) is highly selective in aqueous solution, we arbitrarily define high selectivity as removing ≥90% of that cation from a solution containing 0.1 M Na* as background. We define M-XAM as being selective when ≥ 10% of that cation is removed under the same conditions.
Table 4 • Selectivity results (% removed) for a selection of XAMs for various cations
K-XAM Example 1 99.9 _ _ _ _ _
Na-XAM Example 3 99.8 64.4 95.1 86.3 93.6 97.0
Unless otherwise indicated 25 ml of solution is treated with 0.09 g of XAM overnight at room temperature. All solutions contain a background of 0.1 M Na+.
All cation concentrations measured by atomic absorption spectroscopy (AAS)
Unless otherwise indicated 100 ml of solution is treated with 1 g of XAM for 15 minutes at room temperature. All solutions contain a background of 0.1 M Na+ except for Ca +
Cu2+ and Ca2+ concentrations measured by ion selective electrodes, all other cation concentrations measured by atomic absorption spectroscopy (AAS)
Table 4 continued.
Cu2+ and Pb2+ selectivity for other XAMs (percent removed)
Example XAM Reagent /weight
Cu+ 97.2 99.99 99.99 99.99 99.7 Pb2+ 99.8 98.7 99.8 99.7 99.8
Example
XAM
Reagent/weight
Cu2+ g. Pb2+
E o. to Example
XAM
Reagent/weight
Cu + 10.7 0.0 Pb2+
0.0
For all analyses 100 ml of solution is treated with 1 g of XAM for 15 minutes at room temperature. All solutions contain a background of O.lMNaL 5
Cu2+ concentrations measured by ion selective electrode. Pb2+ concentrations measured by atomic absoφtion spectroscopy (AAS).
Table 4 continued.
Ni + Co2+ Ag+ Fe2+ Cr3+ Mn2+ Sr2+ Al3+ Nd3+ UO2 2+ pH 5.5 5.5 4.0 5.0 4.5 5.5 6.0 4.5 4.5 2.5
Concentration (ppm) 100 100 100 100 100 100 100 100 5230 2390
K-XAM Example 2 100.0 99.55 99.66 99.92 100.0 79.63 67.49 98.68 25 31
Na-XAM Example 4 89.75 90.70 99.79 99.95 100.0 60.75 58.76 99.68 25 29
Li-XAM Example 6 66.90 80.70 99.79 94.66 99.35 54.02 45.92 80.38 15 16
Unless otherwise indicated 100 ml of solution is treated with 1 g of XAM for 15 minutes at room temperature. All solutions contain a O background of 0.1 M Na+.
All cation concentrations measured by atomic absoφtion spectroscopy (AAS) except for Nd3+ and UO22+ which are determined by w UV/visible spectroscopy.
Λ a
El
1
.σ_
Applications of XAM
The high CEC which XAM displays and its high selectivity to a number of aqueous cations makes XAM potentially useful in the treatment of industrial and mine waste water, as well as in the remediation of contaminated environmental waters. In particular, its high selectivity to aqueous Cu2*, Zn2*, Cd2*, and Pb2* ail of which are toxic and environmentally problematic, make XAM particularly useful for such applications. It is probable the XAM will also sequester these cations from non- aqueous solvents or from liquid mixtures containing such non-aqueous solvents, such as wine.
XAM is also potentially suitable for application as a detergent builder or water softener as it shows a capability to sequester Ca2* and Mg2* from solution.
The potentially high CEC of XAM enables high loading levels of various cations. These highly exchanged XAMs may have application in the delivery of these cations in pharmaceuticals, stock feed, horticulture and agriculture.
XAMs which have been highly exchanged by transition metals or lanthanides are likely to have potential usage as heterogeneous catalysts.
Whilst the above has been given by way of illustrative example of the invention, many modifications and variations may be made thereto by persons skilled in the art without departing from the broad scope and ambit of the invention as herein set forth.
Claims (23)
1. A poorly or partly crystalline alkali metal aluminosilicate material having a stuffed silica polymorph related-structure in which the aluminium is at least predominantly tetrahedrally coordinated and a cation exchange capacity at room temperature of at least 1 meq lOOg'1 in aqueous solution, which is produced by reacting an aluminos icate, or a combination of aluminium oxide-containing and silicon oxide-containing compounds, with an alkali oxide-containing reagent.
2. A material according to claim 1 having a BET surface area of at least 0.1, preferably at least 1, more preferably at least 5 m2 g"1, and less than 45 m2 g'1.
3. A material according to claim 1 wherein said cation exchange capacity is at least 10 meq 100 g"1.
4. A material according to claim 3 wherein said cation exchange capacity is in the range 50-750 meq 100 g'1.
5. A material according to claim 1 wherein interstitial sites of the structure are occupied by two or more cations of which at least one is alkali metal.
6. A material according to claim 1 which in a pure, dehydrated form has the composition MpAlqSi1^Or.sH2O where M = alkali metal, 0.0 < p ≤ 2.0, 0.0 ≤ q < 1.0, 1.5 ≤ r ≤ 3.0 and 0.0 ≤ s ≤ 0.1.
7. A material according to claim 1 wherein the alkali cation can be exchanged partly or fully by one or more cations selected from the group comprising: the alkalis Li*, Na*, K*, Rb*, Cs*; ammonium NH4 *; the alkaline earths Ca2*, Mg2*, Sr2*; the transition metals Cr3*, Mn2*, Fe2*, Fe3*, Ag2*. Cu2*, Ni2*, Co2*; the other metals Al3*, Zn2*, Cd2*, Pb2* and, Hg2*; the lanthanides Nd3* and Ln3*, and the uranyl UO2 2+
8. A material according to claim 7 which is highly selective in its cation exchange towards one or more of the aqueous cations selected from the group comprising Ca2*, Al3*, Cu2*, Ni2*, Co2*, Ag\ Fe2*, Cr3*, Zn2*, Cd2* and Pb2*.
9. A material according to claim 7 which is selective in its cation exchange towards the aqueous cations Ca2*, Mg2*, St2*. Al3*, Cu2*, Ni2*, Co2*, Ag*, Fe2*, Cr3*, Mn2*, Zn2*, Cd2*, Pb2*, Hg2*, Nd3*, Ln3* and UO2 2*.
10. Use of a material according to claim 9 which is selective in its cation exchange towards the aqueous cations Ca2* and Mg2*, as a water softener or detergent builder.
11. A material according to claim 1 which has been subjected to partial or full exchange of the alkali metal cation by at least one cation selected from the group comprising: the alkalis Li*, Na*, K*, Rb*, Cs*; ammonium NH/; the alkaline earths Ca2*, Mg2*, Sr2*; the transition metals Cr3*, Mn2*, Fe2*, Fe3*, Ag*, Cu2*, Ni2*, Co2*; the other metals Al3*, Zn2*, Cd2*, Pb2* and Hg2*; the lanthanides Nd3* and Ln3*, and the uranyl UO2 2*.
12. Use of a marterial according to claim 11 for the delivery of a cation in a pharmaceutical, stock feed, horticulture and agriculture.
13. Use of a material according to claim 11 as a heterogeneous catalyst.
14. A process for the preparation of a poorly or partly crystalline alkali metal aluminosilicate material having a stuffed silica polymorph related-structure in which the aluminium is at least predominantly tetrahedrally coordinated and a cation exchange capacity at room temperature of at least 1 meq lOOg'1 in aqueous solution, in which an aluminosihcate, or a combination of aluminium oxide-containing and silicon oxide - containing compounds, are rearted together with an alkali oxide-containing reagent.
15. A process according to claim 14 which is performed at a temperature of 750 °C or less.
16. A process according to claim 15 wherein the reaction is performed at a temperature in the range of 300 to 750 βC.
17. A process according to claim 14 wherein the alkali oxide containing reagent decomposes in air at a temperature below 1000 "C to give alkali oxide.
18. A process according to claim 17 wherein the alkah oxide-containing reagent is a carbonate or hydroxide.
19. A process according to claim 17 wherein the alkah oxide-containing reagent is a bicarbonate, nitrate, or carboxyiate.
20. A process according to claim 14 wherein the aluminosilicate is a phy-losilicate.
21. A process according to claim 20 wherein the phyilosilicate is a kaolin group mineral.
22. A process according to claim 20 wherein the phyilosilicate is montmorillonite or pyrophyUite.
23. A process according to claim 14 which involves a solid state reaction.