AU2016200266A1 - A sulphated polysaccharide compound and the preparation and use thereof - Google Patents

Abstract

A SULFATED POLYSACCHARIDE COMPOUND AND THE PREPARATION AND USE THEREOF Abstract The present invention relates to a sulfated polysaccharide compound and the preparation and use thereof, and in particular to a narrow distribution low molecular weight, highly sulfated pentosan (in this instance a xylan) referred to as glucuronoxylan sulfate (GXS). The invention has been developed primarily for use in the treatment of various clinical conditions.

Description

5 TITLE OF THE INVENTION A SULFATED POLYSACCHARIDE COMPOUND AND THE PREPARATION AND USE THEREOF 10 FIELD OF THE INVENTION The present invention relates to a sulfated polysaccharide compound and the 15 preparation and use thereof, and in particular to a narrow distribution low molecular weight, highly sulfated pentosan (in this instance a xylan) referred to as glucuronoxylan sulfate (GXS). The invention has been developed primarily for use in the treatment of various 20 clinical conditions. However, it will be appreciated that the invention is not restricted this particular field of use. COPYRIGHT NOTICE 25 This document is subject to copyright. The reproduction, communication and distribution of this document is not permitted without prior consent from the copyright owner, other than as permitted under section 226 of the Patents Act 1990. 30 PROBLEMS OF THE PRIOR ART Under-sulfation 35 Highly sulfated (sulfate esters) glycans and glycosaminoglycans form a significant therapeutic class of pharmaceuticals in human and veterinary medicine. Sulfate esters demonstrate a broad range of clinical utility in treating various conditions including osteoarthritis, myocardial ischaemia, interstitial cystitis, cancer, and the control and treatment of virus diseases, including human immunodeficiency virus 40 and other retroviruses. 1 5 Pentosan polysulfate has been used in pharmaceutical formulations to treat osteoarthritis, as an anticoagulant or for other conditions such as interstitial cystitis, transmissible spongiform encephalopathy (TSE) and immunodeficiency virus (such as HIV/AIDS or Feline Immunodeficiency Virus (FIV)) in mammals, such 10 as humans, food-producing and companion animals (such as feline, canine and equine). Pentosan polysulfate may also be used to treat haematomas, haemorrhoids, frostbite, burns, and multiparameter illnesses such as thrombosis and atherosclerosis. 15 Sulfate esters, including heparin, dextran sulfate and PPS are semisynthetic. Their derivation and synthesis have long proved to be very challenging, with production outcomes being highly variable. This has translated to inconsistent clinical outcomes. While there are currently no reported clinical trials looking at differences in clinical outcomes of osteoarthritis treatment using more 20 homogenous and more highly sulfated PPS compared with low sulfated PPS, anecdotal evidence suggests variability in clinical outcome of low sulfated PPS. There are two main chemical reasons that might be behind variability of outcome: (a) PPS with inconsistent molecular weight ranges; and (b) PPS with a high variation in the degree of sulfation (14-17%). 25 Nevertheless, US Patent No. 4,713,373 supports the claim that fractions of glycan chains such as PPS with greater degrees of sulfation will have much better efficacy than those with lower sulfation. In relation to heparin (a glycosaminoglycan), it is known that the type and position of sulfate groups as well as the level of sulfation 30 are important for efficacy. The refinement of the glycan or glycosaminoglycan molecule (to the development, for example, of low molecular weight heparins) has been well documented as resulting in the development of molecules with greater consistency and 35 predictability in clinical outcomes. However, in practice, it has proved difficult to 2 5 achieve a consistently high level of sulfation at consistent positions along the chain and in a low molecular weight range. To date no-one has looked at the importance of the type and location of the sulfate groups or distinguished the chemical structure of the PPS molecule produced by one manufacturing process from that produced by another. Also, the degree of sulfation within known PPS formulations 10 can vary widely, which can also lead to variability in clinical efficacy. Pentosan polysulfate as free acid or in the salt form (typically with inorganic cations such as sodium or calcium) is described in the prior art as a mixture of semi-synthetic polysulfated oligosaccha rides, generally obtained from beechwood 15 xylan. Pentosan polysulfate consists of sulfated linear 1-4 conjugated beta-D xylopyranose units and has 4-0-methyl-D-glucuronic acid randomly attached on every eight to ten xylose units (on average). The typical number of xylose units in a PPS mixture reported in the prior art has 20 been between six and thirty. PPS mixtures currently present on the market (when in the form of sodium salt at all S0 3 groups) typically contain 15 to 17% sulfation. While the prior art describes degrees of sulfation from 15 to 20%, it is apparent from theory and experience that 20% sulfation of PPS is not theoretically possible unless the sodium is substituted with hydrogen giving pentosan hydrogen sulfate 25 (in which case maximum sulfation is 21.9%). The highest possible degree of sulfation for physiologically active PPS is 18.9 to 19%, depending on the length of the molecule. Indeed to date, there is also no substantiation in the prior art of 19% sulfation for PPS, let alone higher degrees of sulfation. 30 Differences in the manufacturing process (especially during hydrolysis and sulfation) can result with molecular differences of the PPS molecule, such as the degree of sulfation and the position of sulfate groups on the glycan chain. It is well known that the clinical efficacy of sulfated carbohydrates can be affected by the type and position of S0 3 groups, hence the need to fully control and characterise 3 5 molecules. This is well known in relation to heparin but to date this knowledge has not been adequately applied to the PPS molecule(s). Prior art NMR analyses of sulfate esters (such as US Patent No 4,713,373) use NMR peak ratios to calculate degrees of sulfation. However, NMR peak ratios will not 10 necessarily indicate the degree of sulfation of the molecule unless the calculation is made by analysis of the entire NMR spectrum. The PPS prior art fails to characterise the position of SO3~ groups (other than to describe theoretical full sulfation) or to discuss the molecular subspecies. There 15 has been no disclosure in the prior art of where the sulfur is missing along the glycosaminoglycan or glycan chain when there is less than full sulfation. The prior art acknowledges that PPS mixtures differ but focus only on the level of sulfation and average molecular weight as being factors that may significantly affect physiological efficacy of the PPS material. 20 Studies with heparin show the efficacy of varying molecular species (of heparin) depends on the location of the -OS0 3 groups within the molecule. Specifically, the relationship of chemical structure to activity for heparin is isolated to a pentasaccharide sequence comprising three D-glucosamine and two uronic acid 25 units. The central D-glucosamine unit in this sequence contains a 3-0-sulfate moiety that is rare outside of this sequence. Sulfate groups on the D-glucosamines are found to be critical for retaining high anticoagulant activity, while undersulfation at less important locations seems not to affect the anticoagulant activity. 30 Different manufacturing techniques lead to different types (chemical structures) of heparin being produced and these different structures are shown to have different clinical efficacies. By way of analogy, the molecular species of other glycan chains (including PPS) vary according not only to the degree of sulfation but also 4 5 according to the location of the sulfur atoms. The PPS prior art does not address this in any detail. While use of PPS became widespread, and to reduce batch to batch variations that could affect pharmaceutical effectiveness, the fundamental problem to overcome 10 was production of a PPS molecular species with a constant sulfur content close to or at 18 to 19%, with narrow average molecular weight range that ensures consistent physiological benefits and sulfate groups consistently attached to positions that will guarantee physiological effect. To date, there has been no discussion in the prior art regarding the relative importance of the positions of the 15 sulfate groups on the glycosaminoglycan or glycan chain. Broad spectrum molecular weight PPS is derived from natural sources such as beechwood xylan. In its natural form, PPS consists of molecular chains of varying lengths, or molecular weights. 20 However, like heparin, the. effects of unfractionated.natural PPS can be difficult to predict. Clinical experience with heparin has found that by modifying heparin and making the mixture of molecules more homogenous (with a narrower molecular weight 25 range), greater clinical efficacy, consistency and safety can be achieved. Similar experience has emerged in the clinical use of PPS. However, in practice, it has been difficult to achieve consistency of the heterogeneous mixture of carbohydrates that make up PPS during commercial 30 production. This is because it has been difficult to achieve a consistent average molecular weight, consistently low molecular weight and steady but high level of sulfation. 5 5 OBJECT OF THE INVENTION It is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative. 10 According to one aspect of the invention there is provided a sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-3-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units. 15 According to another aspect of the invention there is provided a sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-P-D-glucuronic acid unit attached to carbon-2 of 20 every about eight to ten (on average) said xylose units, wherein said molecule has the following configuration of SO3~ groups when Fully Sulfated: (i) two SO3~ groups on each said glucuronic acid unit(s), regardless of the position of said glucuronic acid unit(s) along said molecule; 25 (ii) three S0 3 groups on a terminal xylose unit when said xylose unit is not holding a glucuronic acid group; (iii) two S0 3 groups on a terminal xylose unit when said xylose unit is holding a glucuronic acid group; (iv) two S0 3 groups on a mid-chain xylose unit when said mid-chain 30 xylose unit is not holding a glucuronic acid group; (v) one S0 3 group on a mid-chain xylose unit when said mid-chain xylose unit is holding a glucuronic acid group. 6 5 According to yet another aspect of the invention there is provided a sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-j-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, 10 wherein said molecule has the following preferential configuration of NaSO 3 ~ groups when Highly Sulfated: (i) up to two SO3 groups on each said glucuronic acid unit(s), regardless of the position of said glucuronic acid unit(s) along said molecule; 15 (ii) up to three S03 groups on a terminal xylose unit when said xylose unit is not holding a glucuronic acid group; (iii) up to two S0 3 ~ groups on a terminal xylose unit when said xylose unit is holding a glucuronic acid group; (iv) up to two S0 3 groups on a mid-chain xylose unit when said mid 20 chain xylose unit is not holding a glucuronic acid group; and (v) up to one S0 3 ~ group on a mid-chain xylose unit when said mid chain xylose unit is holding a glucuronic acid group, such that no more than a total of two S0 3 groups is absent from a Fully Sulfated State. 25 According to a further aspect of the invention there is provided a mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and 30 (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units. 7 5 According to yet a further aspect of the invention there is provided a mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of 10 every about eight to ten (on average) said xylose units, wherein said glucuronic acid unit preferentially resides on a left terminal xylose unit. According to still a further aspect of the invention there is provided a mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have 15 the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, wherein said glucuronic acid unit preferentially resides on a right terminal 20 xylose unit. According to yet another aspect of the invention there is provided a mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and 25 (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, wherein said glucuronic acid unit preferentially resides on a mid-chain xylose unit. 8 5 According to yet a further aspect of the invention there is provided a method for the production of a mixture comprising sulfated glycan molecules wherein said molecules comprise: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of 10 every about eight to ten (on average) said xylose units. According to a further aspect of the invention still there is provided a method for fractionation of sulfated glycan (sulfate ester) molecules derived from xylan using an organic solvent. 15 According to still another aspect of the invention there is provided a method for purification of a mixture comprising sulfated glycan (sulfate ester) molecules, wherein said purification involves fractionation using an organic solvent. According to yet another aspect of the invention there is provided a method for 20 decolouration of a mixture comprising sulfated glycan (sulfate ester) molecules, wherein said decolouration involves: (a) charcoal; (b) chlorine; (c) peroxide; 25 (d) fractionation using an organic solvent; or (e) any combination of the above. According to yet a further aspect of the invention there is provided a therapeutic formulation of sulfated glycan (sulfate ester) molecules suitable for parenteral 30 administration wherein said formulation includes sulfated glycan (sulfate ester) molecules in aqueous solution. 9 5 According to a further aspect of the invention yet there is provided a therapeutic formulation of sulfated glycan (sulfate ester) molecules suitable for oral administration. According to yet another aspect of the invention there is provided a delivery 10 mechanism for the administration of a therapeutic formulation of sulfated glycan (sulfate ester) molecules, wherein said delivery mechanism is a pen-like delivery device that enables: (a) dial-up dosing; (b) pre-loading with a unit-dose cartridge; 15 (c) a combination of the above. According to yet a further aspect of the invention there is provided a mixture of sulfated glycan (sulfate ester) molecules suitable for use as an antioxidant. 20 According to another further aspect of the invention there is provided an antioxidant comprising sulfated glycan (sulfate ester) molecules. BRIEF DESCRIPTION OF THE DRAWINGS 25 A preferred embodiment of the invention will now be described, by way of example only, with reference to the accompanying drawings in which: Figure 1 is a diagrammatic representation of a preferred embodiment of GXS 30 showing the points of sulfation on xylose units making up the glycan chain and the presence of a glucuronic acid unit on the left terminal xylose unit. Figure 2 is an example of a typical result from NMR spectrometry of prior art PPS compound A. 35 10 5 Figure 3 is an example of a typical result from NMR spectrometry of prior art PPS compound B. Figure 4 is an example of a typical result from NMR spectrometry of the preferred embodiment, compound C. 10 Figure 5 is an example of a typical result from NMR spectrometry of the preferred embodiment, compound C, but with the addition of trifluoroacetic acid to the D20 solution of GXS, in order to move the water peak that partially obscures the peak at 4.7ppm. 15 Figure 6 is an example of a typical capillary zone electrophoresis profile of PPS compound A. Figure 7 is an example of a typical capillary zone electrophoresis profile of PPS 20 compound B. Figure 8 is an example of a typical capillary zone electrophoresis profile of the preferred embodiment, compound C. 25 Figure 9 is a flowchart outlining a preferred embodiment of the double sulfation method. Figure 10 is a table containing exemplary data obtained from size exclusion chromatography of unfractionated GXS and fractionated GXS (obtained at the 30 ethanol concentrations listed). Figure 11 is an exemplary chromatogram relating to the unfractionated GXS sample in Figure 10. 11 5 Figure 12 is an exemplary chromatogram showing a sliced peak of a first GXS fraction obtained using 40% ethanol as the organic solvent. Figure 13 is an exemplary chromatogram showing a sliced peak of a second GXS fraction obtained using 45% ethanol as the organic solvent. 10 Figure 14 is an exemplary chromatogram showing a sliced peak of a third GXS fraction obtained using 50% ethanol as the organic solvent. Figure 15 is an exemplary chromatogram showing a sliced peak of a fourth GXS 15 fraction obtained using 55% ethanol as the organic solvent. Figure 16 is an exemplary chromatogram showing a sliced peak of a fifth GXS fraction obtained using 60% ethanol as the organic solvent. 20 Figure 17 is an exemplary chromatogram showing a sliced peak of a sixth GXS fraction obtained using 65% ethanol as the organic solvent. Figure 18 is an exemplary chromatogram showing a sliced peak of a seventh GXS fraction obtained using 70% ethanol as the organic solvent. 25 Figure 19 is an exemplary NMR spectrum obtained from a second fractionation cycle GXS (in 45% ethanol). Figure 20 is an exemplary NMR spectrum obtained from a third fractionation cycle 30 GXS (in 50% ethanol). Figure 21 is an exemplary NMR spectrum obtained from a fourth fractionation cycle GXS (in 55% ethanol). 12 5 DETAILED DESCRIPTION A preferred embodiment of the present invention will now be described by reference to the drawings. The following detailed description in conjunction with the figures provides the skilled addressee with an understanding of the invention. 10 It will be appreciated, however, that the invention is not limited to the applications described below. Dictionary of defined terms 15 Table 1 is a dictionary of terms defined according to the invention. Terms defined in Table 1 are denoted with the use of capitalisation throughout the document. If a term is not capitalised then its plain meaning is to be construed, unless otherwise specified. 20 Table 1: Dictionary of defined terms Term Description Degree of Measurement of the relative composition of sulfur in Sulfation a glycan molecule. This is measured as relative molecular weight of the sulfur expressed as a percentage of the molecular weight of the whole chain. See below for "full", "high" and "partial" sulfation definitions. Full Sulfation, Fully Saturation of a glycan molecule in which sulfur Sulfated, Fully occupies all available positions on the xylose units Sulfated State and glucuronic acid units in the glycan chain. Full sulfation of the glycan chain is 18.9% (when sodium is not substituted with hydrogen, as discussed in problems of the prior art). GXS Glucuronoxylan sulfate anion and its salts PPS Pentosan polysulfate sodium 13 High Sulfation, High sulfation of the glycan chain is 18% or greater Highly Sulfated, sulfation. Highly Sulfated State Mp Molecular weight at the top of a size exclusion chromatography peak Partial Sulfation, Partial sulfation is less than 18% sulfation. In practice, Partially Sulfated, prior art PPS molecules (which are a glycan chain) Partially Sulfated have not exceeded 17% sulfation unless sodium is State substituted with hydrogen, resulting in pentosan hydrogen sulfate rather than PPS. Selective In this document selective fractionation means fractionation fractionation with an organic solvent such as ethanol performed in an alkaline (e.g. pH 9.0) solution 5 The elements of the invention are now described under the following headings:: A preferred embodiment of a sulfated polysaccharide compound: GXS The present invention provides a novel sulfated glycan (sulfate ester) molecule. The new molecule is the first known molecule to achieve high and full sulfation of 10 the xylan chain and shall be referred to as glucuronoxylan sulfate (GXS). GXS is distinct from known PPS molecules, as shown by chemical analysis and clinical performance studies (as discussed later in this document). No method currently disclosed in the prior art is able to achieve high or full sulfation of the PPS molecule. 15 Chemical structure According to the prior art, PPS consists of sulfated linear 1-4 conjugated beta-D xylopyranose units and has 4-0-methyl-$-D-glucuronic acid randomly attached at carbon-2 on every eight to ten xylose units (on average). 20 14 5 One arrangement of the preferred embodiment is a mixture of GXS molecules in which at least 10% of molecules in the mixture are Fully Sulfated. The term "full sulfation" is used by the applicant to refer to a configuration of the GXS molecule as illustrated in Figure 1, with the following composition of S0 3 ~ groups: (a) on the right terminal xylose unit illustrated, there are three S0 3 groups; 10 (b) on each mid-chain xylose unit, there are two S0 3 groups; and (c) on the left terminal xylose unit, there is a glucuronic acid unit (defined by a carboxyl unit and an -OCH 3 [4-methoxy] group) and two S03- units. The above configuration is based on the scientific literature (e.g. Friedrich Cavagna, Hans Deger, Jurgen Puls, Carbohydrate Research 129 (1984) 1-8), which indicates 15 that 97% of molecules in a mixture of hydrolysed glycan isomers will have the glucuronic acid unit on the left terminal pentose. It is also well known that carboxyl groups in molecular species such as enzymes often indirectly participate and guide/catalyse hydrolysis. Furthermore, 3D modelling software (specifically, proprietary software known as ACD/3D Viewer by Advanced Chemistry 20 Development, Inc.) indicate that in the non-hydrolysed sulfated xylan macromolecule, xylose units derivatised with glucuronic acid will be in twisted boat conformation, adding conformational and steric reasons to the directed hydrolysis (guided by glucuronic acid). This is in contrast to the PPS prior art that claims random allocation of glucuronic acid units on the left, right and mid-chain 25 xylose units. The preferred embodiments enable a high yield of highly and/or fully sulfated glycans. The isomers of these glycans can be separated using electrophoresis, chromatography or similar techniques, thereby producing compounds with 30 potentially greater pharmaceutical or therapeutic efficacy. In a first preferred embodiment, the GXS is fractionated using an organic solvent. No known PPS molecules extracted from xylan are fractionated in this way. In a second preferred embodiment, the GXS is unfractionated. All comments in the 15 5 detailed description apply to all embodiments and arrangements of the invention, unless specifically stated otherwise. In all arrangements, the preferred embodiment is a semi-synthetic GXS with 18% or greater sulfation, as verified by testing for degree of sulfation (expressed as a 10 weight percentage of the composition of the glycan chain). Table 1 contains examples of testing from three batches, demonstrating greater than 18% sulfation of GXS synthesised as a sodium salt using the inventive method: 15 Table 1. Degree of sulfation % sulfation Batch 1 18.2 Batch 2 18.0 Batch 3 18.4 20 GXS is an anion and may exist in a wide array of practical embodiments, by attaching to various counter ions such as inorganic metals (e.g. Na, K, Ca, Mg, Ag) or organic bases. Further examples are also included in the section "1.2 Conversion of the pyridinium salt to a sodium salt, as an exemplary arrangement of the preferred embodiment". 25 The degree of sulfation of the preferred embodiment is distinguished from known glycan chains derived from xylan (described in the prior art as PPS molecules), which have less than 17% sulfation in practice. The applicant suggests this is due to a novel difference in the method of preparation of GXS compared with known PPS, 30 as described later in this document. 16 5 The degree of sulfation of GXS compared with PPS has been ascertained through proton nuclear magnetic resonance (NMR) spectrometry, conducted by an independent laboratory using the same methodology (50 mg/mL D 2 0 with or without trifluoroacetic acid) and equipment (600 MHz) across samples of three different glycan compounds, each derived from xylan but manufactured by a 10 different source. The three different compounds analysed were as follows: (a) compound A (see Figure 2) - a PPS compound; (b) compound B (see Figure 3) - a PPS compound; and (c) the inventive compound (compound C - see Figure 4) - a GXS compound. Examples of the NMR analyses of the different compounds are demonstrated in 15 Figures 2 to 4. The inventive compound, compound C, differs from the prior art PPS compounds, as indicated by the NMR analyses (and other analyses described below). The exact NMR peak shifts will differ according to experimental conditions such as temperature, concentration of sample, solvent used, and so on. Therefore, all NMR peak shifts are approximate and indicative only. 20 Referring to Figure 2, the intensity of the peak seen at 5.1ppm indicates incomplete sulfation of compound A at position 2 of the xylose subunits. To clarify, the peak at 5.1ppm is due to the NMR shift of protons at C1 of the xylose units when a sulfate group is present at C2 (meaning that the shift of that C1 proton will 25 not be at 5.1ppm if there is no sulfation at C2). Therefore, the peak at 5.1ppm is an indirect measure of sulfation at position 2 of the xylose units. The peak at approximately 3.4ppm is due to the OCH3 group of glucuronic acid. The presence of a strong single peak at approximately 3.4ppm indicates consistent 30 sulfation at both positions 2- and 3- of the glucuronic acid unit in compound A. Referring now to Figure 3, the intensity and appearance of two peaks at 3.4ppm indicate inconsistent sulfation of compound B at positions 2- and 3- of the glucuronic acid unit. Furthermore, NMR prediction software indicated that fully 35 sulfated glucuronic acid units will be presented with peak at about 5.3ppm, while 17 5 presence of peak at 5.2ppm is typical for partially sulfated glucuronic acid (SO3 group missing at position 3). Therefore, presence of two peaks at approximately 3.4 and another two peaks at 5.2-5.3ppm region indicated inconsistent sulfation of glucuronic acid of compound B. 10 Comparing both Figures 2 and 3, the NMR spectra of both compounds A and B are showing no significant traces of peaks at 5.85ppm and 5.7ppm. According to theoretical calculations and experimental chemical structure database searches conducted by NMR modelling and prediction software (specifically, proprietary software known as ACD/C+H NMR Predictors and DB by Advanced Chemistry 15 Development, Inc.): (a) the 5.85ppm peak will be related to a fully sulfated right terminal xylose (with three sulfate groups); and (b) the 5.7ppm peak indicates that two (probably at positions 1 and 3) out of three possible sulfate groups at right terminal xylose will be present. 20 Therefore, peaks at 5.85ppm and 5.7ppm indicate a mixture of fully and partially sulfated molecules (at the right terminal xylose). Since both of these peaks are virtually negligible for compound A and compound B, this indicates that neither compound has achieved full theoretical sulfation. 25 Figure 4 contains an example of NMR spectrometry data from GXS. The NMR in Figure 4 demonstrates the significant presence of fully sulfated molecules and the existence of sulfate (SO 3 ) groups at all xylose units along the newly created glycan chain known as GXS. 30 Specifically, full sulfation of all xylose units in GXS is indicated by the appearance of peaks at 5.1ppm, 4.7ppm (see also Figure 5), 4.4ppm and 3.8ppm as shown in Figure 4. The NMR peak at 4.7ppm is more clearly seen in Figure 5, which has been collected by the addition of trifluoroacetic acid to the D 2 0 solution of GXS, in order to move the water peak (visible in Figure 4 at around 4.7ppm) and shows full 35 sulfation of that peak. The other peaks can be seen fully in Figure 4. The addition of 18 5 TFA is not the preferred mode of NMR spectra collection as the addition of such a strong acid could affect the appearance of some small yet important peaks or even induce a small change of GXS structure which is susceptible to acid degradation. The strong single NMR peak at approximately 3.4ppm indicates consistent 10 sulfation and the 5.3ppm peak indicates full sulfation of glucuronic acid. Additionally, the peaks at approximately 5.85ppm and 5.7ppm indicate a mixture of a fully sulfated right terminal xylose unit and a partially sulfated right terminal xylose unit (with SO 3 groups at positions 1 and 3). Therefore, predictive modelling of the NMR data indicated that the inventive compound GXS is a mixture of fully 15 sulfated and highly sulfated molecules, with large number of fully sulfated molecules. Figures 6 and 7 contain typical sample capillary zone electrophoresis (CZE) profiles of compounds A (Fig 6) and B (Fig 7), respectively. Compound B is the pioneer PPS 20 compound released onto the market for use in osteoarthritis. The manufacturer of compound A (Manufacturer A) subsequently released a compound (A) with the bell-shaped CZE profile shown in Figure 6 as a type of PPS. Manufacturer B previously used the difference in CZE profiles (namely, the shorter oligosaccharide peaks in the CZE profile of compound A compared with compound B) to argue that 25 the bell-shaped PPS is not a generic copy of the PPS molecule that is compound B. Manufacturer A is the applicant of patent application no. WO 2007/123800, in which it disputes the importance of well defined CZE peaks (short oligosaccharides). The bell-shaped curve component of the CZE profile represents 30 a large number of molecular species. By contrast, well-defined peaks in a CZE profile represents a smaller number of molecular species - in Figure 7, the peaks occur on the left of the bell-shaped curve, indicating a lower number of molecular species in the lower molecular weight range. The bell-shaped curve for Manufacturer A's compound has a sharper profile than that of compound B (seen 35 by comparing Figures 6 and 7). Manufacturer A has used this to support an 19 5 inference that the area under the curve represents a greater number of low molecular weight species. A typical CZE profile of the unfractionated preferred embodiment is contained in Figure 8. The profile contains a large number of well-defined peaks (short 10 oligosaccharides) to the left, continuing into the bell-shaped curve. One interpretation of the CZE profile is that it indicates that the incidence of molecular species in the lowest molecular weight range for Compound C (GXS) is greater than for compounds A and B. 15 Although the CZE profiles of GXS (Compound C) and Compound B PPS have similarities, the NMR profiles of the two compounds unequivocally show very important differences in chemical structure between the two molecules. NMR is a better technique for distinguishing molecular structure of glycans than CZE and NMR is widely recognised as a premier chemical signature technique. CZE cannot 20 be relied on with the same accuracy for determining the chemical signature of a molecule. A method of preparing GXS from xylan: a preferred embodiment A preferred embodiment provides a novel method for production of xylan sulfates 25 (specifically, the GXS described above) from beechwood xylan. The production method includes the steps of: (a) performing a novel double sulfation technique using pyridine chlorosulfonic acid complex in DMF, pyridine SO 3 complex in DMF or a combination of these in solvent; 30 (b) ultrafiltration to remove inorganic impurities (e.g. divalent cations) and some of very low MW degradation products from the GXS. Ultrafiltration can occur at one or more stages throughout the production method; and (c) in relation to the fractionated GXS embodiment, performing fractionation with an organic solvent such as ethanol, to produce narrow distribution 35 low MW GXS molecules and as a novel means for decolouration. No known 20 5 method for extracting prior art PPS molecules from xylan involves a fractionation step using an organic solvent or a mixture including an organic solvent. Further, the applicant's fractionation method includes the novel steps of: i. selective fractionation of the GXS mixture (obtained from the 10 double sulfation method) using an organic solvent, to increase the yield of highly and fully sulfated GXS molecules; ii. modification of the pH of the molecule/solvent solution to make it alkaline (thereby selectively precipitating out the higher MW molecules); and 15 iii. use of selective fractionation as a means to remove colour (a colour change from one fraction to the next indicates chemical degradation which results in colouration of the precipitate). 1. Sulfation principle 20 1.1 Production of xylan polysulfate pyridine salt Xylan reacts under certain conditions with pyridine chlorosulfonic acid, pyridine

SO

3 or a combination to form sulfated xylan esters. The reaction medium contains a proton acceptor (N, N-dimethyl formamide (DMF)), which may be a higher polar 25 aprotic solvent. The equations include:

CISO

3 H+2C 5

H

5

N->SO

3

C

5

H

5

N+C

5

H

5 N.HCI Xylan-OH+SO 3

C

5

H

5 N -Xylan-O-SO 3

HC

5

H

5 N Xylan-OH+CISO 3 H-*Xylan-O-SO 3 H+HCIT 30 In the presence of DMF, quantitative reaction of pyridine with chlorosulfonic acid, for example, immediately yields SO 3

HC

5

H

5 N and a mole of pyridinium chloride. The

SO

3

HC

5

H

5 N reacts with xylan to form xylan-0-SO 3

HC

5

H

5 N, which has good solubility in DMF. The highly polar DMF associates with the hydroxyl groups of the substrate and makes them more accessible to the S0 3 -pyridine complex, which is utilised as 35 a sulfate donor. The use of excess pyridine and DMF and lower sulfation 21 5 temperature can not only avoid degradation but forms a homogenous system, which results in a more complete reaction. The hydrogen chloride formed in the reaction mixture can be absorbed in water through a CaCl 2 tube. The temperature (75 0 C) keeps the xylan dissolved in the 10 reaction system and gives a higher degree of sulfation. The pyridinium salt of sulfated xylan is recovered and purified by methanol precipitation. 1.2. Conversion of the pyridinium salt to a sodium salt, as an exemplary arrangement of the preferred embodiment 15 The pyridinium salt can be converted to the sodium salt by raising the pH to a level where the pyridine is not protonated, and is released as free pyridine. This reaction is reversible. Xylan-O-SO 3

HC

5

H

5 N+NaOH--Xyl-O-SO 3 Na+C 5

H

5 N 20 High pH accelerates the conversion to the sodium salt, but it can cause degradation. A pH of 9.5-10 is suitable. The free residual pyridine and DMF are removed by rotary evaporation at 50 0 C. 25 In alternative arrangements, the pyridinium salt can be converted to other salts, by attaching to any other suitable counter ion such as an inorganic metal (e.g. Na, K, Ca, Mg, Ag) or an organic base. Suitable examples include: (i) Glycine ethyl ester (or other amino acid ester) 30 (ii) Glucosamine (iii) Procaine (iv) Tetracaine (v) Triethanolamine (used as triethanolamine salicylate) (vi) Benzathine 35 (vii) Choline (used as choline salicylate) 22 5 (viii) Benorylate (ix) Imipramine (x) Penicillamine (xi) Trimethoprim (xii) Mesalamine 10 (xiii) Meglumine (N-methyl glucamine) (xiv) 4-methyl 2-hexanamine (methylhexanea mine) (xv) p-amino hippuric acid. (xvi) 2-amino-2-methyl-1,3-propanediol (xvii) 2-amino-4-picoline 15 (xviii) 4- amino salicylic acid (xix) Pyrilamine (xx) Guanine. 1.3. Control of molecular size and decolouring 20 Xylan from a commercial source (e.g. Sigma or Kaden) has a larger molecular weight (10,000 to 50,000) than required. Theoretically, complete sulfation will make the molecular weight (MW) of the final sulfated xylan increase to 2.5 times that of the starting xylan. To ensure a final MW of approximately 1000 to 6000, three methods can be used: 25 1. xylan is directly sulfated following hydrolysis to suitable molecular size; 11. the reduction of molecular size and decolouring can be carried out simultaneously by carrying out the reaction in acidic medium containing hydrogen peroxide or chlorine; or Ill. xylan is directly sulfated, acid hydrolysed to a suitable molecular size, and 30 the resulting product is resulfated. Methods (11) and (1ll) have been shown to be efficient methods to obtain a sulfated low molecular weight, low viscosity GXS. The sulfated product is very water-soluble compared to native xylan so subsequent depolymerisation and dialysis are easier 35 to perform. However, both methods (1) and (11) have disadvantages. 23 5 In method (11), although sulfation followed by depolymerisation is a convenient way to obtain the desired molecular size, acid hydrolysis at high temperature (80 100 0 C) also causes some desulfation. As a result, the NMR spectrum of the final product is unsatisfactory. There is also a problem with residual oxidative power 10 imparted by the hydrogen peroxide, so it is strongly recommended that chlorine be used. In method (I), although depolymerisation followed by sulfation yields a satisfactory sulfation content, the depolymerisation step gives poor yields owing to the low 15 solubility of the native polymer in acid, leading to a heterogeneous reaction difficult to reproduce. In addition, it is not easy to desalt depolymerised, unsulfated xylan by dialysis because of low solubility leading to membrane blockage. 20 It is also known that exposure of sulfated xylan to extreme conditions such as acidic environment and heat during hydrolysis could lead to the loss of sulfur and opening of new positions for potential sulfation. The disadvantages of methods (1) and (11) may be overcome by sulfation followed 25 by depolymerisation, then resulfation method (111). Introducing sulfate groups greatly improves the solubility of xylan, and the depolymerisation step gives higher yields. Desulfation during hydrolysis can be overcome by resulfation. Though this method is more costly of reagents and is time consuming, it has been adopted by the applicant. 30 2. Double sulfation method to produce unfractionated but highly sulfated GXS: a preferred embodiment Methods of production of known sulfate esters (PPS) from xylan involve sulfation 35 then acid hydrolysis. During the hydrolysis step, there is a loss of sulfur and new 24 5 OH groups are opened up available for sulfation. In this way, acid hydrolysis results in a reduction in the degree of sulfation of the end product. Known methods do not address this disadvantage. The double sulfation method of the preferred embodiment introduces a second sulfation stage after acid hydrolysis to replenish sulfur lost during hydrolysis. This is described below. 10 2.1. Sulfation of xylan Referring to step 1 in Figure 9, a mixture of equal volumes of anhydrous pyridine and anhydrous DMF is mechanically stirred for half an hour at approximately 0 0 C in an ice bath. For example, a mixture of 650 mL anhydrous pyridine and 650 mL 15 anhydrous DMF is added into a 5L two necked round-bottom flask provided with a mechanical stirrer, a thermometer (0-100 0 C) and a 250mL dropping funnel to which is connected a silica gel drying tube. This mixture is mechanically stirred for half an hour at 0 0 C in an ice bath. 20 Referring to step 2 in Figure 9, after approximately 30 minutes, chlorosulfonic acid, pyridine S03 complex or a combination of the two (in this example, 167mL of chlorosulfonic acid) is slowly added to the solution (say 1mL/min) at 0 0 C drop by drop with constant stirring over a period of about 2 hours. The mixture is stirred at 0 0 C until all white fumes of HCI disappear. The solution is a white milky colour. 25 The ice bath is changed to a water bath, and the temperature of the water bath is gradually raised to 60"C by a temperature-controlled heater/stirrer. At this time, xylan powder (say, 100g in this example) is added to the mixture solution (see step 3 in Figure 9) in portions through the side tube of the flask via long-necked funnel 30 to give a homogenous brownish suspension. The reaction mixture is raised to 75 0 C and maintained at this temperature for approximately 4 hours (see step 4 in Figure 9), after which the water bath is removed. The reaction mixture is cooled to room temperature (see step 5 in Figure 9) with 35 continuing stirring, and then sulfated xylan is precipitated by addition to (in this 25 5 example) 6000 mL precooled (in an ice-bath) methanol with vigorous stirring (see step 6 in Figure 9). The precipitate is a white, amorphous, water-soluble pyridinium salt, and the supernatant is a brown-coloured liquid. The precipitate is collected (see step 7 in Figure 9) in this example on a Buchner funnel by water pump, the residue is washed with methanol (x3 times) to remove adhering unreacted 10 sulfating reagent. 2.2. Conversion of the pyridinium salt to the sodium salt, as an exemplary arrangement of the preferred embodiment Referring to step 8 in Figure 9, the residue is dissolved in distilled water (in this 15 example, 1.5L) with vigorous stirring, and the pH is adjusted from 3.8 to 10 (see step 9 in Figure 9) with 6N NaOH (about 230-250mL, in this example) in order to convert pyridinium xylan sulfate to sodium xylan sulfate. To ensure the pH of solution is maintained at this value, it is necessary to check the 20 pH just before rotary evaporation (step 10 in' Figure 9). After the solution is rotated and evaporated to dryness (red-brown colour) the solid residue (essentially free of pyridine and DMF) is redissolved in distilled water (see step 11 in Figure 9) and the pH of solution is adjusted to 7. 25 In alternative arrangements, the pyridinium salt can be converted to other salts, by attaching to any other suitable counter ion such as an inorganic metal (e.g. Na, K, Ca, Mg, Ag) or an organic base - as described in "1.2 Conversion of the pyridinium saft to a sodium salt, as an exemplary arrangement of the preferred embodiment", above. 30 2.3. Hydrolysis of the sulfated xylan Referring to step 12 in Figure 9, the solution in this example is made up to 1670 mL (deep brown colour) - that is, 50 X per 3mL, (X=original xylan in grams). This solution is transferred into a 3L round flask in this example and fitted with a reflux 35 condenser and heating mantle and brought to gentle boiling. Five molar H 2 SO4 26 5 (25mL in this example) is added to the sulfated xylan ester solution through the condenser tube with stirring, left for approximately 35 minutes at 100 0 C (see step 13 in Figure 9). The time is an important parameter, as it determines the molecular weight of the final product. The time will need to be determined independently for each batch size. The solution is then rapidly cooled by pouring it 10 into an ice bath. The pH of the cooled solution is 0.9-1.0. The pH is adjusted to a pH of 7 (see step 14 in Figure 9), in this example, by taking 50-55mL of 6N NaOH solution. 2.4. Dialysis and drying of hydrolysis product 15 In order to keep a reasonable flow rate of permeate at a safe, constant pressure (say 15-20 psi), the hydrolysis solution concentration should be kept less than 3-4% and preferably at 1.5-2%. This provides an increased permeate collection rate, more than offsetting the increased starting volume. 20 Referring to steps 15 and 16 in Figure 9, this solution needs to be filtered using a prefilter and a 0.45pm cellulose acetate membrane, to avoid blockage of the dialysis membrane. The solution subjected to ultrafiltration using, say, a Prep/sale TFF 6ft2 cartridge (Millipore) which has a nominal cut off MW of 1000 Daltons, with distilled water (preferably BP purified water). The working pressure (say 15 25 20psi) is maintained by an Amicon LP- 1A pump for example. After 5-6x volume of distilled water (relative to the processing solution volume) has been collected as permeate, the retained solution (including washings of the system with, in this example, 500-600mL water) is dried by rotary-evaporation typically at 50DC under reduced pressure (see step 17 in Figure 9). The final product (in this example, 160 30 180g) is ground and put in the dessicator with P 2 0 5 under vacuum. 2.5. Resulfation of sulfated xylan Referring to step 18 in Figure 9, the second sulfation method is similar to the first, with slight modification. A mixture of equal volumes of pyridine and DMF is 35 mechanically stirred. In this example, 650mL pyridine and 650mL DMF is added to 27 5 a 5000mL two-necked round bottom flask provided with a mechanical stirrer, a 250mL dropping funnel fitted with a silica gel tube, seated in an ice bath. When the temperature of mixed solvent is close to OC, 167mL (in this example) of chlorosulfonic acid is slowly dropped into the solution over about 2 hours with continuous stirring and cooling to maintain the temperature close to 0C. 10 After the addition of chlorosulfonic acid (in this example), the reaction mixture is stirred further (in this example, for a further 30 minutes). The ice bath is changed to water, and the temperature is raised to 60"C over 1.2 to 1.5 hours. Sulfated xylan (in this example, 170 to 240g) is added to the reaction solvent by side tube of 15 round flask. The temperature is further raised to 75 0 C, and is then maintained at this temperature with stirring for about 1 hour. The heater is turned off and the hot water is drained or siphoned from the water bath. The reaction mixture is allowed to cool to room temperature with stirring. The cooled solution is poured into methanol (in this example, 6000mL) with vigorous stirring. The precipitate is a 20 white coloured solid. 2.6. Conversion to the sodium salt (as an exemplary arrangement) and removal of pyridine and DMF Referring to step 19 in Figure 9, the precipitate is redissolved in distilled water (in 25 this example, 1 L), with the pH being 4.1-4.2. The pH of solution is adjusted to 10. In this example, it takes about 120-140mL of 6N NaOH solution. This solution is rotary evaporated to dryness at 50"C (grey-white colour). The residue is dissolved in distilled water (in this example, 300mL of distilled water) and poured into methanol (in this example, 2500-3000mL) with vigorous stirring (see step 20 in 30 Figure 9). At this stage, due to the presence of a large amount inorganic salt, the precipitate can easily form lumps. The precipitate is collected by filtration under water pump suction. As described in "1.2 Conversion of the pyridinium salt to a sodium salt, as an 35 exemplary arrangement of the preferred embodiment", alternative arrangements 28 5 include salt made with any other suitable counter ion such as an inorganic metal (e.g. Na, K, Ca, Mg, Ag) or an organic base. 2.7. Decolouring of resulfated xylan using a carbon cartridge The above precipitate is redissolved in distilled water (in this example, in 2L of 10 distilled water). The solution is deep brown. The colour can be removed by repeated circulation of solution through a carbon cartridge (e.g. an Aqua-Pure water filter APII) at room temperature for 2 hours (see step 21 in Figure 9). The final solution becomes light yellow in colour and is rotary evaporated to dryness. 15 Considerable losses (up to 30%) of "good" xylan sulfate can be experienced if a carbon cartridge with low selectivity is used. It is preferable to use a good grade of activated carbon powder, in a batch process. The amount of carbon relative to the xylan sulfate is approximately 20% weight/weight. 20 Alternatively, decolouration can take place during fractionation, as described below. 2.8. Dialysis and drying Referring to step 22 in Figure 9, the decoloured solution is filtered through a 25 0.45im cellulose acetate membrane with a prefilter. The filtrate is then desalted as described above (e.g. using a Millipore ultrafiltration system provided with a Prep/Scalem-TFF cartridge (cut off MW 1000) using purified water BP. The working pressure (10-20psi) is maintained by an Amicon LP-1A peristaltic pump). After collecting 10x volumes of the permeate solution, the process solution is 30 concentrated in the ultrafiltration system as high as possible (for example, 3-4%). The final solution is then dried, for example, by rotary evaporation (see step 23 in Figure 9). 3. Selective fractionation to produce a narrow spectrum low MW, highly 35 sulfated GXS 29 5 For the fractionated GXS embodiment, following completion of the double sulfation method described above, the resultant crystals are fractionated with an organic solvent such as ethanol using the procedure described below. The applicant refers to this fractionation procedure as "selective fractionation" because it uses the charge of the highly sulfated GXS molecule to "focus" the 10 fractionation process so that precipitation occurs using the charge of the molecule in addition to molecular weight. Using the method of selective fractionation (described below), it is possible to produce GXS compound with a consistently low molecular weight and within a 15 narrow spectrum of weight ranges, from 1000 to 4000. The selective fractionation method is as follows: (a) Following on from step 23 in Figure 9, the crystals are dissolved in H 2 0 to make a 10% solution. In this example 100g of solid is dissolved in 1000mL 20 of total solution. This solution has a pH of around 5.0, unadjusted. (b) The pH of the solution is adjusted to around 9.0 by the addition of NaOH. Adjusting the pH affects the charge of the GXS molecule and thereby its solubility in water/organic solvent mixtures. (c) Having adjusted the pH to around 9, organic solvent (in this example, 25 ethanol) is added in a dropwise manner (while stirring) to make up a total concentration of 40% by volume. Ethanol is added because high molecular weight fractions are the least soluble and adding an organic solvent such as ethanol will affect their solubility. (d) The high molecular weight fractions will be the first to precipitate out of the 30 solution. The first fraction is removed and the whole solution is then centrifuged. (e) Organic solvent (in this example, ethanol) is added to the supernatant (which still includes the lower MW GXS) in the same manner to make up a total concentration of 45% by volume. 30 5 (f) The precipitant (second fraction) is removed and the solution again centrifuged as described in step (d) above. (g) The steps (d) to (f) are repeated, increasing the concentration of ethanol by 5% in each cycle, up to a concentration of 70% in the final cycle. (h) For each fraction, the precipitate is further rinsed using additional ethanol 10 to remove as much water as possible from the crystals. Figure 10 is a table showing sample data obtained from size exclusion chromatography (SEC) of GXS produced using the double sulfation method described above. The second column from the left is exemplary data obtained 15 from one batch of unfractionated GXS; the remaining columns are for fractionated GXS, using the selective fractionation method described above. Figures 11 to 18 show chromatograms of the data from Figure 10 - namely, exemplary SECs of unfractionated and fractionated GSX. Each chromatogram 20 (Figures 11 to 18) shows refractive index (RI) against retention time (RT). The mobile phase used was pure water with 0.05% sodium azide, with a flow rate of 0.5mL per minute. Two Phenomenex Biosep S2000 connected in series at a temperature of 30 C were used in the SEC experiment. The instrument was an Agilent 1100 with an RI detector, calibrated with polystyrene sulfonate standards. 25 The sample concentration of GXS was 5mg/mL. Referring to second column of the table in Figure 10 and to Figure 11, the unfractionated GXS had an average sulfation of 18% with a peak relative MW of 3294, with the mode MW being 2759. 30 The first fraction (obtained using ethanol fractionation with ethanol in a concentration of 40%), gave a yield with an average sulfation of 18.1%. It can be seen from the %weight profile in the table in Figure 10 that the first fraction removes the highest MW molecules (22% of this fraction has a relative MW higher 31 5 than 10,000). The % weight profile of this fraction is illustrated in the chromatogram in Figure 12. The second fraction (in 45% ethanol), gave a yield with an average sulfation of 18.2%, with the mode MW being 2000-3000 (see Figure 13 and the table in Figure 10 10). The third fraction (in 50% ethanol), gave a yield with an average sulfation of 18.5%, with the mode MW also being 2000-3000 (see Figure 14 and the table in Figure 10). The fourth fraction (in 55% ethanol), gave a yield with an average sulfation of 18.4%, with the mode MW also being 2000-3000 (see Figure 15 and the table in Figure 10). The fifth fraction (in 60% ethanol), gave a yield with an 15 average sulfation of 17.8%, with the mode MW being 1500-2000 (see Figure 16 and the table in Figure 10). The sixth fraction (in 65% ethanol), gave a yield with an average sulfation of 16.9%, with the mode MW also being 1500-2000 (see Figure 17 and the table in Figure 10). The seventh fraction (in 70% ethanol), gave a yield with an average sulfation of 17.1%, with the mode MW also being less than 1500 20 (see Figure 18 and the table in Figure 10). These data indicate that second to fourth fractionation cycle gave the greatest yield of low MW, fully sulfated GXS molecules. However, yield can be affected by Mp of started unfractionated GXS. Therefore, strict control of GXS molecular 25 weight and optimisation of manufacturing parameters are crucial to obtain high yield, desirable level of sulfation and molecular weight range. The preferred embodiment is a mixture of GXS molecules that contains at least 10% of fully sulfated molecules, displaying the following NMR characteristics (and 30 as shown in the exemplary NMR spectra obtained from second to fourth fractionation cycle GXS seen in Figures 19 to 21): (a) a single OCH 3 peak of glucuronic acid around 3.3 to 3.5ppm; (b) a fully sulfated glucuronic acid peak around 5.2 to 5.4ppm; (c) at least one peak correlating to a fully sulfated right terminal xylose unit, 35 seen at around 5.5 to 6.Oppm; and 32 5 (d) the appearance of a single strong peak at around each of 5.1ppm, 4.7ppm, 4.4ppm and 3.8ppm, correlating to the fully sulfated xylose units. 4. Purification The production method includes one or more ultrafiltration steps to remove 10 impurities that can affect the quality of the end product. High performance liquid chromatography of the inventive compound, GXS, compared with prior art PPS molecules demonstrates an absence of peaks in the chromatogram tail, indicating the removal of low molecular weight impurities such as degradation products. This is achieved either by ultrafiltration or by fractionation with organic solvents, as 15 described above. 5. Colour removal by fractionation Dark colouration of the final product indicates a change of chemical structure. Colour removal therefore is important as a way for removing discoloured 20 degradation products. Colour removal can be achieved by perfusion with hydrogen peroxide or chlorine, as described in step 1.3 above, or with charcoal as described in step 2.7. These methods of colour removal have proved to be a most difficult step in production. 25 A preferred embodiment of the production method utilises selective organic solvent fractionation as a means for colour removal, because lowest molecular weight fractions are darkest in appearance. This has the advantages of not involving additives and minimising the steps and costs in production. 30 Method of use of GXS: a preferred embodiment The highly sulfated, low molecular weight GXS of the present invention is administered parenterally in a preferred embodiment (including by intramuscular, subcutaneous or intravenous injection). Delivery may be by traditional hypodermic 33 5 syringe or by a pen-like delivery device that enables dial-up dosing or pre-loading with a single-dose cartridge of GXS aqueous solution. Alternatively, the GXS may be a sustained- or controlled-release formulation administered by depot injection. This may have practical use in animals not 10 currently treated for certain conditions (such as joint inflammation and other disorders). An alternative embodiment may be administered orally, depending on the clinical condition being treated. This may have more practical application for formulations 15 containing fractionated GXS rather than unfractionated GXS, since research suggests bioavailability of the fractionated compound is better than for the unfractionated compound. Research suggests that GXS has a role in the treatment of a wide range of clinical 20 conditions in animals, including humans, food-producing animals, and companion animals (such as feline, canine and equine). The range of conditions in which GXS may have a role in treatment include: (a) non-infective inflammatory diseases such as osteoarthritis; (b) ischaemia; 25 (c) cancer; (d) the control and treatment of virus diseases, including immunodeficiency virus (such as HIV/AIDS or feline immunodeficiency virus (FIV)) and equine flu); (e) interstitial cystitis; 30 (f) Crohn's disease; (g) ulcerative colitis; (h) Reiter's syndrome; (i) prion diseases such as transmissible spongiform encephalopathy (TSE), bovine spongiform encephalopathy (BSE) and Creutzfeldt-Jakob disease 35 (CJD) and its iatrogenic variant vCJD in humans; 34 5 (j) haematomas; (k) haemorrhoids, frostbite, burns; and (1) multiparameter illnesses such as thrombosis and atherosclerosis. Dosages ranging from 1 mg/kg to 10 mg/kg have been reported in the literature for 10 the use of prior art PPS in various conditions. Experiments indicate that dosing in the range from around 1 mg/kg to 20 mg/kg for GXS would be of clinical benefit in various conditions. For example, GXS is one of a new generation of pharmaceuticals referred to as 15 Disease Modifying Osteoarthritis Drugs (DMOADs). GXS stimulates proteoglycan synthesis in the cells of arthritic cartilage, and reduces the loss of proteoglycan in the cartilage by the inhibiting enzymes which degrade cartilage, thereby modifying the disease process. In one arrangement of a preferred embodiment, GXS is a means for treating degenerative joint disease such as osteoarthritis and is clinically 20 effective in repairing joint damage. In another arrangement of the preferred embodiment, GXS is a means for prophylaxis in degenerative joint disease such as osteoarthritis and is clinically effective in preventing joint damage. 25 An exemplary method of use includes a dosing regimen of around 1 to 10 mg/kg given by intramuscular or subcutaneous injection, once a week for at least four weeks. 30 The clinical applications of the preferred embodiment are based on experiments using dosage regimens of around 3mg/kg/week for up to a 12 week course in adult and yearling thoroughbred horses. The experiments have been conducted using unfractionated GXS with 18% or greater sulfation. The studies show statistically significant improvement in treatment and prevention of degenerative joint disease 35 such as osteoarthritis. This was measured by assessing clinical lameness scores and 35 5 levels of serum biomarkers such as epitope CS846. This epitope is an indicator of proteoglycan aggrecan synthesis, which occurs during repair of cartilage. In adult horses receiving intramuscular GXS, an increase in CS846 levels (p=0.01) was seen over 12 weeks, indicating increased repair in the joint. 10 Yearlings exhibit naturally high levels of CS846 because of rapid growth and constant joint remodelling in this age group. Yearlings that received intramuscular GXS (weekly doses of 3mg/kg IM for up to 12 weeks) showed a significant decrease in CS846 levels (p=0.05) over 12 weeks, indicating a protective effect against joint damage from Stage 1 disease (onset of osteoarthritis with no visible clinical signs). 15 Prior art research in horses using known PPS at a dose of 3mg/kg and measuring clinical effectiveness in osteoarthritis (also by measuring epitope CS846 levels) failed to show a statistically significant effect. This confirms the applicant's conclusion that GXS (fractionated or unfractionated) is a different chemical entity 20 to prior art PPS extracted from xylan. A preferred embodiment of a GXS formulation In a preferred embodiment, the active ingredient GXS is formulated into aqueous 25 solution for parenteral injection (including intramuscularly, subcutaneously or intravenously). In one arrangement, the injectable formulation includes a suitable antioxidant to enable the aqueous formulation to remain substantially stable (that is to resist 30 discolouration and degradation) without refrigeration. Patent WO 2007/123800 claims a PPS formulation with "an antioxidant in the group metabisulfite, sodium bisulfate and ascorbate in a concentration of about 0.02% w/v to about 5.0% w/v" is stable without refrigeration. However, experiments by the applicant revealed that many antioxidants are not effective on GXS in an aqueous solution. For 35 example, ascorbate does not act as an anti-oxidant, since in its presence the GXS 36 5 still dissociates and becomes discoloured. This finding supports a conclusion that GXS is a distinct entity to prior art PPS extracted from xylan. Experiments by the applicant found that only sulfur-containing antioxidants are suitable for preventing degradation and discolouration of an injectable GXS 10 formulation at ambient room temperature for at least seven months. Table 2 below lists examples of sulfur-containing antioxidants found to be suitable for this use. Table 2. Examples of sulfur-based antioxidants found to be suitable 15 Name CAS no. Exemplary effective concentration * Sodium metabisulfite 7681-57-4 0.5% by weight/volume Sodium bisulfite ACS Mix of 7681- 0.5% by weight/volume Reagent 57-4 and 7631-90-5 Sodium hydroxymethane 149-44-0 1% by weight/volume sulfonate Formaldehyde-sodium 870-72-4 1% by weight/volume bisulfate * To achieve substantial stability of GXS injectable formulation The preferred embodiment may be packaged as an injectable formulation for delivery by traditional hypodermic syringe or delivery by a pen-like delivery device 20 that enables dial-up dosing or pre-loading with a single-dose cartridge of GXS aqueous solution. In a further embodiment, the GXS is a sustained- or controlled-release formulation administered by depot injection. This formulation may suit use in animals not 25 currently under regular veterinary supervision - such as dairy cattle for whom, say, 37 5 decreased mobility arising from joint pain can affect overall health, including milk production and reproduction. As cattle are not generally required to move quickly, joint pain and inflammation in such animals may go unattended. This is in contrast to animals such as thoroughbred horses or dogs that need maximal mobility and are under very regular attendance by vets. A slow-release formulation would 10 enable animals that may go untreated (e.g. for inflammatory joint conditions) to be treated with GXS without requiring regular (say, weekly) attendance by a vet, which may have both important production and animal welfare implications. A further embodiment is a solid unit dosage formulation of GXS for oral 15 administration; however, as bioavailability of unfractionated GXS is poor when taken orally, the dosage required for therapeutic effect may make oral administration of unfractionated GXS unsuitable for some clinical indications. Research suggests that bioavailability of fractionated GXS would be better than bioavailability of unfractionated GXS when taken orally. Therefore, an oral 20 formulation of fractionated GXS may have wider clinical use than oral formulations of unfractionated GXS or of prior art unfractionated sulfate esters such as PPS (which are currently indicated for interstitial cystitis in humans). Examples of arrangements of the preferred embodiment (GXS in aqueous solution 25 for parenteral administration) may comprise GXS in a concentration of about 0.1 to about 500 mg/mL. By way of example, for a 100 mg/mL solution with a 10mL pack size, the formulation may include: 30 (a) around 100 mg GXS; (b) around 10 mg benzyl alcohol as preservative (c) around 0.8 mg citric acid anhydrous as buffer; (d) around 15 mg trisodium citrate dehydrate as buffer; (e) to 1.0 mL water for injection as the vehicle. 35 38 5 A second exemplary arrangement of the preferred embodiment is a 250 mg/mL solution with a 6mL pack size. The formulation may include: (a) around 250 mg GXS; (b) around 10 mg benzyl alcohol as preservative (c) around 2 mg citric acid anhydrous as buffer; 10 (d) around 38 mg trisodium citrate dehydrate as buffer; (e) to 1.0 mL water for injection as the vehicle. For room temperature formulations of the above exemplary arrangements, a suitable antioxidant is added in an effective concentration, examples of which are 15 provided in Table 2. Optionally, the head space in the room temperature formulations may also be replaced with nitrogen. An alternative embodiment: GXS as a new or improved antioxidant 20 Experiments by the applicant show that GXS is oxidised more readily than some common antioxidants (BHA, BHT, lipoic acid, glutamic acid, gentisic acid, methyl sulfonyl methane, malic acid, nicotinic acid, ascorbates). This finding indicates that GXS has excellent antioxidant properties in its own right. Scientific literature indicates that the OS0 3 at position 1 (such as at the right terminal xylose unit in 25 GXS) is generally highly labile, hence GXS would be oxidized in preference to ascorbic acid (or the other antioxidants listed above). This conclusion is supported by the finding (discussed earlier) that only sulfur containing antioxidants are suitable for preventing degradation of GXS, because 30 the sulfur in the antioxidant is preferentially oxidised to the OS0 3 of the right terminal or other carbohydrate units in GXS. In a preferred embodiment, GXS is suitable for use as an antioxidant, including in preparations for clinical use. 35 39 Although the invention has been described with reference to specific examples, it will be appreciated by those skilled in the art that the invention may be embodied in many different other forms. Throughout this specification and the claims which follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps. The reference in this specification to any prior publication (or information derived from it), or to any matter which is known, is not, and should not be taken as an acknowledgment or admission or any form of suggestion that that prior publication (or information derived from it) or known matter forms part of the common general knowledge in the field of endeavour to which this specification relates. 40

Claims (54)

1. A sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of 10 every about eight to ten (on average) said xylose units.

2. A sulfated glycan (sulfate ester) molecule according to claim 1, wherein one said glucuronic acid unit resides on a left terminal xylose unit. 15

3. A sulfated glycan (sulfate ester) molecule according to claim 1 or claim 2, wherein said molecule includes one said glucuronic acid unit on a left terminal xylose unit and at least one said glucuronic acid unit: (a) on a mid-chain xylose unit; (b) on a right terminal xylose unit; or 20 (c) any combination of the above.

4. A sulfated glycan (sulfate ester) molecule according to claim 1, wherein one said glucuronic acid unit resides on a right terminal xylose unit. 25

5. A sulfated glycan (sulfate ester) molecule according to claim 1 or claim 4, wherein said molecule includes one said glucuronic acid unit on a right terminal xylose unit and at least one said glucuronic acid unit: (a) on a mid-chain xylose unit; 41 5 (b) on a left terminal xylose unit; or (c) any combination of the above.

6. A sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and 10 (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, wherein said molecule has the following configuration of S0 3 ~ groups when Fully Sulfated: (i) two SO3 groups on each said glucuronic acid unit(s), regardless of the 15 position of said glucuronic acid unit(s) along said molecule; (ii) three S0 3 groups on a terminal xylose unit when said xylose unit is not holding a glucuronic acid group; (iii) two S03~ groups on a terminal xylose unit when said xylose unit is holding a glucuronic acid group; 20 (iv) two SO3~ groups on a mid-chain xylose unit when said mid-chain xylose unit is not holding a glucuronic acid group; (v) one S0 3 group on a mid-chain xylose unit when said mid-chain xylose unit is holding a glucuronic acid group. 25

7. A sulfated glycan (sulfate ester) molecule according to claim 6 wherein said molecule has the following configuration of S03 groups when Fully Sulfated: (a) three S0 3 ~ groups on a right terminal xylose unit; (b) two SO3 groups on each mid-chain xylose unit; 42 5 (c) two S0 3 groups on a left terminal xylose unit; and (d) two SO 3 - groups on said glucuronic acid unit.

8. A sulfated glycan (sulfate ester) molecule according to claim 6 or claim 7 wherein said molecule has the following configuration of SO3 groups when 10 Fully Sulfated: (a) three SO3 groups on a left terminal xylose unit; (b) two S03~ groups on each mid-chain xylose unit; (c) two SO 3 groups on a right terminal xylose unit; and (d) two SO 3 - groups on said glucuronic acid unit. 15

9. A sulfated glycan (sulfate ester) molecule according to any of claims 6 to claim 8 wherein said molecule has the following configuration of S0 3 ~ groups when Fully Sulfated: (a) three SO3 groups on a right terminal xylose unit; 20 (b) a S03 group on a mid-chain xylose unit holding a glucuronic acid unit; (c) two S03~ groups on each of one or more mid-chain xylose units lacking glucuronic acid; (d) three S0 3 ~ groups on a left terminal xylose unit; and (e) two SO 3 - groups on a glucuronic acid unit. 25

10. A sulfated glycan (sulfate ester) molecule according to claims 6 to claim 9 wherein said molecule includes: (a) a glucuronic acid unit on a left terminal xylose unit; 43 5 (b) a glucuronic acid unit on a right terminal xylose unit; (c) one or more glucuronic acid units on one or more mid-chain xylose units; (d) any combination of the above. 10

11. A sulfated glycan (sulfate ester) molecule having: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, wherein said molecule has the following preferential configuration of NaSO 3 15 groups when Highly Sulfated: (i) up to two S0 3 groups on each said glucuronic acid unit(s), regardless of the position of said glucuronic acid unit(s) along said molecule; (ii) up to three S0 3 groups on a terminal xylose unit when said xylose unit is not holding a glucuronic acid group; 20 (iii) up to two S0 3 groups on a terminal xylose unit when said xylose unit is holding a glucuronic acid group; (iv) up to two S03~ groups on a mid-chain xylose unit when said mid-chain xylose unit is not holding a glucuronic acid group; and (v) up to one S0 3 ~ group on a mid-chain xylose unit when said mid-chain 25 xylose unit is holding a glucuronic acid group, such that no more than a total of two SO 3 groups is absent from a Fully Sulfated State. 44 5

12. A sulfated glycan (sulfate ester) molecule according to claim 11 wherein said molecule has the following preferential configuration of S03- groups when Highly Sulfated: (a) up to three SO3~ groups on a right terminal xylose unit; (b) up to two SO3 groups on each mid-chain xylose unit; 10 (c) up to two S03 groups on a left terminal xylose unit; and (d) up to two SO 3 -groups on said glucuronic acid unit such that no more than a total of two S0 3 ~ groups are absent from a Fully Sulfated State. 15

13. A sulfated glycan (sulfate ester) molecule according to claim 11 or claim 12 wherein said molecule has the following preferential configuration of S0 3 groups when Highly Sulfated: (a) up to three S0 3 groups on a left terminal xylose unit; (b) up to two S03 groups on each mid-chain xylose unit; 20 (c) up to two S03- groups on a right terminal xylose unit; and (d) up to two SO 3 - groups on said glucuronic acid unit such that no more than a total of two SO3 groups are absent from a Fully Sulfated State. 25

14. A sulfated glycan (sulfate ester) molecule according to any of claims 11 to claim 13 wherein said molecule has the following configuration of S03~ groups when Highly Sulfated: (a) up to three S0 3 ~ groups on a right terminal xylose unit; 45 5 (b) up to one S03~ group on a mid-chain xylose unit holding a glucuronic acid unit; (c) up to two S0 3 groups on each of one or more mid-chain xylose units lacking glucuronic acid; (d) up to three S03 groups on a left terminal xylose unit; and 10 (e) up to two S03- groups on a glucuronic acid unit, such that no more than a total of two S0 3 groups is absent from a Fully Sulfated State.

15. A sulfated glycan (sulfate ester) molecule according to claims 11 to claim 14 15 wherein said molecule includes: (a) a glucuronic acid unit on a left terminal xylose unit; (b) a glucuronic acid unit on a right terminal xylose unit; (c) one or more glucuronic acid units on one or more mid-chain xylose units; (d) any combination of the above. 20

16. A sulfated glycan (sulfate ester) molecule according to any of the preceding claims wherein said sulfated glycan molecule includes glucuronoxylan sulfate (GXS) anion and salts thereof. 25

17. A sulfated glycan (sulfate ester) molecule according any of the preceding claims having a degree of sulfation no less than 18% when the molecule is bound to Na*. 46 5

18. A sulfated glycan (sulfate ester) molecule according to any of the preceding claims having a relative molecular weight in the range of about 1000 to about

6000.

19. A sulfated glycan (sulfate ester) molecule according to any of the preceding 10 claims having a relative molecular weight in the range of about 1000 to about 5000.

20. A sulfated glycan (sulfate ester) molecule according to any of the preceding claims having a relative molecular weight in the range of about 1000 to about 15 4000.

21. A mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and 20 (b) at least one 4-0-methyl-S-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units.

22. A mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: 25 (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, 47 5 wherein said glucuronic acid unit preferentially resides on a left terminal xylose unit.

23. A mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: 10 (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units, wherein said glucuronic acid unit preferentially resides on a right terminal xylose unit. 15

24. A mixture comprising sulfated glycan (sulfate ester) molecules wherein said molecules have the following typical chemical structure: (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of 20 every about eight to ten (on average) said xylose units, wherein said glucuronic acid unit preferentially resides on a mid-chain xylose unit.

25. A mixture according to any one of claims 21 to 24 wherein about 100% of said 25 sulfated glycan molecules are Fully Sulfated.

26. A mixture according to any one of claims 21 to 25 wherein at least about 90% of said sulfated glycan molecules are Fully Sulfated. 48 5

27. A mixture according to any one of claims 21 to 26 wherein at least about 80% of said sulfated glycan molecules are Fully Sulfated.

28. A mixture according to any one of claims 21 to 27 wherein at least about 70% 10 of said sulfated glycan molecules are Fully Sulfated.

29. A mixture according to any one of claims 21 to 28 wherein at least about 60% of said sulfated glycan molecules are Fully Sulfated. 15

30. A mixture according to any one of claims 21 to 29 wherein at least about 50% of said sulfated glycan molecules are Fully Sulfated.

31. A mixture according to any one of claims 21 to 30 wherein at least about 40% of said sulfated glycan molecules are Fully Sulfated. 20

32. A mixture according to any one of claims 21 to 31 wherein at least about 30% of said sulfated glycan molecules are Fully Sulfated.

33. A mixture according to any one of claims 21 to 322 wherein at least about 20% 25 of said sulfated glycan molecules are Fully Sulfated.

34. A mixture according to any one of claims 21 to 33 wherein at least about 15% of said sulfated glycan molecules are Fully Sulfated. 49 5

35. A mixture according to any one of claims 21 to 34 wherein at least about 10% of said sulfated glycan molecules are Fully Sulfated.

36. A mixture according to any one of claims 21 to 35 wherein at least about 5% of 10 said sulfated glycan molecules are Fully Sulfated.

37. A mixture according to any one of claims 21 to 36 wherein about 100% of said sulfated glycan molecules are Highly Sulfated. 15

38. A mixture according to any one of claims 21 to 37 wherein at least about 90% of said sulfated glycan molecules are Highly Sulfated.

39. A mixture according to any one of claims 21 to 38 wherein at least about 80% of said sulfated glycan molecules are Highly Sulfated. 20

40. A mixture according to any one of claims 21 to 39 wherein at least about 70% of said sulfated glycan molecules are Highly Sulfated.

41. A mixture according to any one of claims 21 to 40 wherein at least about 60% 25 of said sulfated glycan molecules are Highly Sulfated.

42. A mixture according to any one of claims 21 to 41 wherein at least about 50% of said sulfated glycan molecules are Highly Sulfated. 50 5

43. A mixture according to any one of claims 21 to 42 wherein at least about 40% of said sulfated glycan molecules are Highly Sulfated.

44. A mixture according to any one of claims 21 to 43 wherein at least about 30% 10 of said sulfated glycan molecules are Highly Sulfated.

45. A mixture according to any one of claims 21 to 44 wherein at least about 20% of said sulfated glycan molecules are Highly Sulfated. 15

46. A mixture according to any one of claims 21 to 45 wherein at least about 15% of said sulfated glycan molecules are Highly Sulfated.

47. A mixture according to any one of claims 21 to 46 wherein at least about 10% of said sulfated glycan molecules are Highly Sulfated. 20

48. A mixture according to any one of claims 21 to 47 wherein at least about 5% of said sulfated glycan molecules are Highly Sulfated.

49. A mixture according to any one of claims 21 to 48 wherein said sulfated glycan 25 molecule in a Fully Sulfated State typically has the following configuration of SO 3 groups: (a) three S03~ groups on a right terminal xylose unit; (b) two S03 groups on each mid-chain xylose unit; 51 5 (c) two S0 3 units and a glucuronic acid unit on a left terminal xylose unit; (d) two SO 3 - groups on glucuronic acid unit

50. A mixture according to any one of claims 21 to 49 wherein said mixture displays the following indicative characteristics on proton nuclear magnetic 10 resonance (NMR) spectrometry: (a) a single OCH 3 peak of glucuronic acid around the range of about 3.3 to about 3.5ppm; (b) a fully sulfated glucuronic acid peak around the range of about 5.2 to about 5.4ppm; 15 (c) at least one peak correlating to a sulfated right terminal xylose unit, seen at around the range of about 5.5 to about 6.Oppm; and (d) a single strong peak at around each of about 5.1ppm, about 4.7ppm, about 4.4ppm and about 3.8ppm, correlating to fully sulfated xylose units. 20

51. A mixture according to any of any one of claims 21 to 50 having said sulfated glycan molecules with molecular weight in the range of about 1000 to about 6000.

52. A mixture according to any one of claims 21 to 51 having said sulfated glycan 25 molecules with molecular weight in the range of about 1000 to about 5000. 52 5 53. A mixture according to any one of claims 21 to 52 having said sulfated glycan molecules with molecular weight in the range of about 1000 to about 4000. 54. A method for the production of a mixture comprising sulfated glycan molecules wherein said molecules comprise: 10 (a) one or more linear 1-4 conjugated beta-D-xylose units; and (b) at least one 4-0-methyl-p-D-glucuronic acid unit attached to carbon-2 of every about eight to ten (on average) said xylose units. 55. A method for the production of a mixture according to claim 54 wherein said 15 sulfated glycan molecules are Fully Sulfated. 56. A method for the production of a mixture according to either claim 54 or claim 55 wherein said sulfated glycan molecules are Highly Sulfated. 20 57. A method for the production of a mixture according to any one of claims 54 to 56 wherein said mixture is a combination of Fully Sulfated and Highly Sulfated glycan molecules. 25 58. A method for the production of a mixture according to any one of claims 54 to 57 wherein said sulfated glycan molecule includes a GXS anion and the salts thereof.

53 5 59. A method for the production of a mixture according to any one of claims 54 to 58, wherein said mixture displays the following typical characteristics on nuclear magnetic resonance (NMR) spectrometry: (a) a single OCH 3 peak of glucuronic acid around the range of about 3.3 to about 3.5ppm; 10 (b) a fully sulfated glucuronic acid peak around the range of about 5.2 to about 5.4ppm; (c) at least one peak correlating to a fully sulfated right terminal xylose unit, seen at around the range of about 5.5 to about 6.Oppm; and (d) a single strong peak at around each of about 5.1ppm, about 4.7ppm, about 15 4.4ppm and about 3.8ppm, correlating to fully sulfated xylose units. 60. A method for the production of a mixture according to any of claims 54 to 59 wherein said sulfated glycan molecules have molecular weight in the range of about 1000 to about 6000. 20 61. A method for the production of a mixture according to any of claims 54 to 60 wherein said sulfated glycan molecules have molecular weight in the range of about 1000 to about 5000. 25 62. A method for the production of a mixture according to any of claims 54 to 61 wherein said sulfated glycan molecules have molecular weight in the range of about 1000 to about 4000.

54 5 63. A method for the production of a mixture according to any of claims 54 to 62 including the following steps: (a) hydrolysis, wherein said hydrolysis is performed at least once during said method and wherein said hydrolysis is performed on: 10 (i) xylan; (ii) xylan sulfate; or (iii) either of the above in a separate hydrolysis step; and (b) sulfation, wherein said sulfation is performed at least twice during said method and wherein said sulfation is performed on: 15 (i) xylan; (ii) xylan sulfate; or (iii) either of the above in one or more separate sulfation steps. 64. A method for the production of a mixture according to any of claims 54 to 63 20 including the steps of: (a) performing sulfation of xylan, said sulfation including use of: (i) pyridine chlorosulfonic acid complex in DMF; (ii) pyridine SO 3 complex in DMF; or (iii) a mixture of (i) and (ii) above, 25 to produce pyridinium xylan sulfate; (b) replacing pyridinium with a suitable counter ion (examples as listed below), to form a non-pyridine xylan sulfate salt, followed by removal of said pyridine and DMF: 55 5 (i) an inorganic metal (e.g. Na, K, Ca, Mg, Ag); (ii) an organic base (e.g. an amine); or (iii) any other suitable counter ion; (c) performing acid hydrolysis said non-pyridine xylan sulfate salt to adjust its final relative molecular weight; 10 (d) performing ultrafiltration of said sulfated xylan to remove inorganic impurities (e.g. divalent cations) and degradation products, wherein said ultrafiltration may occur at one or more steps of the production method including this and later steps; and (e) performing at least one resulfation/hydrolysis cycle of said sulfated xylan, 15 followed by conversion to a sodium salt and removal of said pyridine and DM F to form an unfractionated precipitate. 65. A method for fractionation of sulfated glycan (sulfate ester) molecules derived from xylan using an organic solvent. 20 66. A method for fractionation of sulfated glycan (sulfate ester) molecules according to claim 65 wherein said method of fractionation is performed in an alkaline solution. 25 67. A method for fractionation of sulfated glycan (sulfate ester) molecules according to either claim 65 or claim 66 wherein said method includes the steps of: 56 5 (a) dissolving unfractionated sulfated glycan (sulfate ester) molecules in solution; (b) adjusting the pH of said solution to make an alkaline solution; (c) performing at least one fractionation cycle by adding organic solvent to said alkaline solution. 10 68. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any one of claims 65 to 67 wherein said method includes the steps of: (a) dissolving unfractionated sulfated glycan (sulfate ester) molecules in 15 solution; (b) adjusting the pH of said solution to make an alkaline solution; (c) performing a first fractionation cycle to precipitate molecules from said solution by adding organic solvent to said alkaline solution; (d) removing said first fraction; 20 (e) performing a second fractionation cycle to precipitate a second fraction from said solution by adding organic solvent to said supernatant; and (f) repeating steps (d) and (e) above, incrementally increasing the concentration of organic solvent in said supernatant in each cycle (for example by 5%) for one or more further fractionation cycle. 25 69. A method for fractionation of sulfated glycan (sulfate ester) molecules according to claim 65 to 68 wherein said organic solvent is ethanol. 57 5 70. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 69, wherein: (a) said concentration of said organic solvent is around 30% in a first cycle of fractionation; and 10 (b) said pH of said solution is around 8 to around 11. 71. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 70, wherein said concentration of said organic solvent is around 35%. 15 72. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 71, wherein said concentration of said organic solvent is around 40%. 20 73. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 72, wherein said concentration of said organic solvent is around 45%. 74. A method for fractionation of sulfated glycan (sulfate ester) molecules 25 according to any of claims 65 to 73, wherein said concentration of said organic solvent is around 50%. 58 5 75. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 74, wherein said concentration of said organic solvent is around 55%. 76. A method for fractionation of sulfated glycan (sulfate ester) molecules 10 according to any of claims 65 to 75, wherein said concentration of said organic solvent is around 60%. 77. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 76, wherein said concentration of said organic 15 solvent is around 65%. 78. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 77, wherein said concentration of said organic solvent is around 70%. 20 79. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 78, wherein said concentration of said organic solvent is around 75%. 25 80. A method for fractionation of sulfated glycan (sulfate ester) molecules according to any of claims 65 to 79, wherein said concentration of said organic solvent is around 80%. 81. A method for the production of a mixture according to any of claims 54 to 80 30 including the steps of: 59 5 (a) one or more hydrolysis steps; (b) two or more sulfation steps; and (c) one or more cycles of fractionation. 82. A method for purification of a mixture comprising sulfated glycan (sulfate 10 ester) molecules, wherein said purification involves fractionation using an organic solvent. 83. A method for decolouration of a mixture comprising sulfated glycan (sulfate ester) molecules, wherein said decolouration involves: 15 (a) charcoal; (b) chlorine; (c) peroxide; (d) fractionation using an organic solvent; or (e) any combination of the above. 20 84. A therapeutic formulation of sulfated glycan (sulfate ester) molecules suitable for parenteral administration wherein said formulation includes sulfated glycan (sulfate ester) molecules in aqueous solution. 25 85. A therapeutic formulation according to claim 84, wherein said formulation is a controlled-release formulation. 60 5 86. A therapeutic formulation of sulfated glycan (sulfate ester) molecules suitable for oral administration. 87. A therapeutic formulation according to claim 84 or claim 85 wherein said formulation includes an antioxidant such that said formulation is enabled to 10 remain substantially stable at ambient room temperature. 88. A therapeutic formulation according to claim 87 wherein said antioxidant includes a sulfur-containing antioxidant. 15 89. A therapeutic formulation according to any one of claims 84 to 88, wherein said sulfated glycan is glucuronoxylan sulfate (GXS), including GXS anion and the salts thereof. 20 90. A therapeutic formulation according to any one of claims 84 to 89, wherein said GXS is present in a concentration ranging from about 0.1 to about 1000 mg/mL. 25 91. A therapeutic formulation according to any one of claims 84 to 90, wherein said GXS is present in a concentration ranging from about 1.0 to about 500 mg/mL. 61 5 92. A therapeutic formulation according to any one of claims 84 to 91, wherein said GXS is present in a concentration ranging from about 10 to about 350 mg/mL. 93. A therapeutic formulation according any one of claims 84 to 92, wherein said 10 formulation has therapeutic application in clinical conditions including: (a) non-infective inflammatory diseases such as osteoarthritis; (b) ischaemia; (c) cancer; (d) the control and treatment of virus diseases, including 15 immunodeficiency virus (such as HIV/AIDS or feline immunodeficiency virus (FIV)) and equine flu); (e) interstitial cystitis; (f) Crohn's disease; (g) ulcerative colitis; 20 (h) Reiter's syndrome; (i) prion diseases such as transmissible spongiform encephalopathy (TSE), bovine spongiform encephalopathy (BSE) and Creutzfeldt-Jakob disease (CJD) and its iatrogenic variant vCJD in humans; (j) haematomas; 25 (k) haemorrhoids, frostbite, burns; (1) multiparameter illnesses such as thrombosis and atherosclerosis. 62 5 94. A delivery mechanism for the administration of a therapeutic formulation of sulfated glycan (sulfate ester) molecules, wherein said delivery mechanism is a pen-like delivery device that enables: (a) dial-up dosing; (b) pre-loading with a unit-dose cartridge; 10 (c) a combination of the above. 95. A delivery mechanism according to claim 94 wherein said formulation of sulfated glycan (sulfate ester) molecules is a formulation comprising GXS molecules. 15 96. A method of use of a therapeutic formulation of sulfated glycan (sulfate. ester) molecules according to any one of claims 84 to 95, wherein said formulation is administered in a dose ranging from about 0.1 mg/kg to about 100 mg/kg. 20 97. A method of use of a therapeutic formulation according to claim 96, wherein said formulation is administered in a dose ranging from about 1 mg/kg to about 50 mg/kg. 25 98. A method of use of a therapeutic formulation according to claim 96 or 97, wherein said formulation is administered in a dose ranging from about 2 mg/kg to about 25 mg/kg. 63 5 99. A method of use of a therapeutic formulation according to any one of claims 96 to 98 wherein said dose is administered as a single dose. 100. A method of use of a therapeutic formulation according to any one of 10 claims 96 to 99 wherein said dose is administered on about a weekly basis. 101. A method of use of a therapeutic formulation according to any one of claims 96 to 100 wherein said dose is administered on about a weekly basis for a course of one or more weeks. 15 102. A method of use of a therapeutic formulation according to any one of claims 96 to 101 wherein said dose is administered on about a weekly basis for a course of at least four weeks. 20 103. A method of use of a therapeutic formulation according to any one of claims 96 to 102 wherein said dose is administered as a controlled-release depot. 25 104. A mixture comprising sulfated glycan (sulfate ester) molecules suitable for use as an antioxidant. 105. A mixture according to claim 104 wherein said sulfated glycan molecules are GXS, including GXS anion and the salts thereof. 64 5 106. An antioxidant comprising sulfated glycan (sulfate ester) molecules. 107. An antioxidant according to claim 106 wherein said sulfated glycan (sulfate ester) molecules are GXS, including GXS anion and the salts thereof. 10 108. A sulfated glycan (sulfate ester) molecule substantially as herein described with reference to the accompanying drawings. 15 109. A mixture comprising sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 110. A method for the production of a mixture comprising sulfated glycan (sulfate ester) molecules substantially as herein described with reference to 20 the accompanying drawings. 111. A method for fractionation of sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 25 112. A method for the purification of a mixture comprising sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 65 5 113. A method for the decolouration of a mixture comprising sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 114. A therapeutic formulation of sulfated glycan (sulfate ester) molecules 10 substantially as herein described with reference to the accompanying drawings. 115. A delivery mechanism for the administration of a therapeutic formulation of sulfated glycan (sulfate ester) molecules substantially as herein 15 described with reference to the accompanying drawings. 116. A method of use of a therapeutic formulation of sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 20 117. A mixture of sulfated glycan (sulfate ester) molecules suitable for use as an antioxidant substantially as herein described with reference to the accompanying drawings. 25 118. An antioxidant comprising sulfated glycan (sulfate ester) molecules substantially as herein described with reference to the accompanying drawings. 66