AU2015201318B2 - Annular Sustained Release Preparation And Production Method Thereof - Google Patents
Annular Sustained Release Preparation And Production Method Thereof Download PDFInfo
- Publication number
- AU2015201318B2 AU2015201318B2 AU2015201318A AU2015201318A AU2015201318B2 AU 2015201318 B2 AU2015201318 B2 AU 2015201318B2 AU 2015201318 A AU2015201318 A AU 2015201318A AU 2015201318 A AU2015201318 A AU 2015201318A AU 2015201318 B2 AU2015201318 B2 AU 2015201318B2
- Authority
- AU
- Australia
- Prior art keywords
- tube
- pressure
- polymer
- rod
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Provided is an annular sustained release preparation to be used by opening a center portion thereof, the preparation having a strength enough to avoid cleaving at a welded end portion. More specifically, provided is an annular sustained release preparation comprising at least two polymer tubes having both ends sealed and integrated by pressure-welding or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-welding; and a sex pheromone liquid contained by at least one of the tubes or the tube; wherein an annular space can be formed by pulling the tubes or the tube and the rod apart from each other at a center portion therebetween, the central portion not having been pressure-welded; and an angle formed between a line connecting respective centers of diameters of the tubes welded to each other or the tube and the rod welded to each other and the pressure application direction is from 0 to 45'.
Description
2015201318 08 Sep 2016 1
Title of Invention
Annular sustained release preparation and production method thereof
Technical Field
The present invention relates to an annular sustained release preparation for releasing a synthetic pheromone into the air in order to disrupt mating communication of insect pests and thereby controlling them; and a production method of the preparation.
Background Art 0 Control of insect pests through mating disruption is performed by releasing a synthetic pheromone of a target insect pest into the air, disturbing mating communication between male and female insect pests to reduce their mating ratio, and controlling the birth of the next generation. A preparation for releasing this synthetic pheromone is required to have a performance of stably releasing the sex pheromone during an emergence period (for 5 from 2 to 6 months) of the insect pest.
In a sustained release preparation already used in practice, a sex pheromone is enclosed in a polymer tube or a polymer ampoule, and released by diffusion and transmittance through the wall of the tube or ampoul e to the air. Examples of the polymer tube include a tube comprising a metal wire along the tube (PTL1 and PTL2), a tube bent 20 into a ring (PTL3), and a folded tube (PTL4). In PTL5, there is proposed an annular sustained release preparation 110 having the ends of two polymer tubes 112 and 113 w7elded into a ring as shown in FIG 12. It is hung on or winded around the branch or trunk of a plant upon use. 25 2015201318 08 Sep 2016 2
Citation List Patent Literature PTL I: Japanese Patent Application Examined Publication No. 61-016361/1986 PTL 2: Japanese Patent Application Examined Publication No. 02-063017/1990 PTL 3: Japanese Utility Model Application Unexamined Publication No. 62-122801/1987 PTL 4: Japanese Utility Model Application Unexamined Publication No. 11-000722/1988 PTL 5: Japanese Patent Application Unexamined Publication No. 11-225646/1999 The preceding discussion of the background art is intended to facilitate an understanding of the present invention only. The discussion is not an acknowledgement or 0 admission that any of the material referred to is or was part of the common general knowledge as at the priority date of the application.
Summary of Invention 5 Technical Problem
The preparation is used after opening a center portion of the preparation so that without careful handling, it splits into 115a and 115b at the end 115 as shown in FIG 13, thereby making the preparation unusable. An obj ect of the invention is therefore to provide an annular sustained release preparation strong enough to prevent cleavage at the 20 wielded end.
When a plurality of polymer tube materials are sealed under pressure, two of the tube materials adjacent to each other are usually shifted to a lateral direction, that is, a direction of 90° to the pressure application direction. Consequently, they are 25 pressure-welded while being aligned laterally. For example, as shown in FIG. 14, two polymer tube materials 122 and 123 are welded on a sealing table (not shown) while 2015201318 08 Sep 2016 3 applying a pressure P to them with a sealing pressure block 1. The present inventors have found that in the above method, however, cleavage is likely to occur at the end 115, because the contact area of these two tube materials decreases and their adhesion strength therefore decreases. More specifically, the present inventors have found that when a plurality of 5 polymer tube materials are sealed, a contact area of these tube materials differs so that their adhesion strength greatly differs, depending on an angle between a line connecting the centers Ci and C?. of the tube materials and an application directi on of a sealing pressure P. The present inventors have arrived at the invention based on these findings.
The invention provides an annular sustained release preparation comprising at least 0 two polymer tubes having both ends sealed and integrated by pressure-welding, or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-welding; a sex pheromone liquid contained by at least one of the tubes or the tube, wherein an annular space can be formed by pulling the tubes (or the tube and the rod) apart from each other at a center portion therebetween, the center portion not have been 5 pressure-welded; and an angle formed between a line connecting respective centers of diameters of the tubes welded to each other or the tube and the rod welded to each other and a pressure application direction is from 0 to 45°.
The invention also provides a method for producing an annular sustained release preparation comprising at least the steps of: 20 placing, between two guides which are disposed on a sealing table, are perpendicular to the sealing table and are parallel to each other with a fixed distance, respective pressure-welding planned portions of at least two polymer materials for tube (which may hereinafter be referred to as “tube-tube materials'’) aligned in a longitudinal direction or respective pressure-welding planned portions of at least one polymer material 25 for tube and at least one polymer material for rod (which may hereinafter be referred to as “tube-rod materials) aligned in a longitudinal direction, at least one of the tube-tube 2015201318 08 Sep 2016 4 materials or at least one of the tube-rod materials containing a sex pheromone liquid therein; welding the tube-tube materials or tube-rod materials between the guides while applying a pressure with a sealing pressure block from a direction parallel to the guides; and cutting the resulting product at the pressure-welded portions to obtain an annular 5 sustained release preparation comprising at least two polymer tubes having both ends sealed and integrated by pressure-welding or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-welding wherein an annular space can be formed by pulling the tubes (or the tube and the rod) apart from each other at a center portion therebetween, the center portion not have been pressure-welded; 0 wherein the fixed distance is a length calculated from diameters of the tube-tube materials or the tube-rod materials so that an angle formed between a line connecting respective centers of the diameters of the polymer materials to be welded and the pressure application direction is from 0 to 45°.
The invention further provides an annular sustained release preparation 5 comprising: at least two polymer tubes having both ends sealed and integrated by pressure-welding, or at least one polymer tube and at least one polymer rod sealed and integrated at both ends by pressure-welding; and a sex pheromone liquid contained by at least one of the tubes or the tube; 20 wherein an annular space can be formed by pulling the tubes or the tube and the rod apart from each other at a center portion therebetween, the center portion not having been pressure-welded; and an angle formed between a line connecting respective centers of diameters of the tubes welded to each other or the tube and the rod welded to each other and a pressure application direction is from 0 to 45°. 25 ο 2015201318 08 Sep fN The invention further provides a method for producing an annular sustained release preparation comprising at least the steps of. placing, between two guides which are disposed on a sealing table, are perpendicular to the sealing table and are parallel to each other with a fixed distance, 5 respective pressure-welding planned portions of at least two polymer materials for tube (which will hereinafter be referred to as “tube-tube materials”) aligned in a longitudinal direction or respective pressure-welding planned portions of at least one polymer material for tube and at least one polymer material for rod (which will hereinafter be referred to as “tube-rod materials) aligned in a longitudinal direction, at least one of the tube-tube 0 materials or at least one of the tube-rod materials containing a sex pheromone liquid therein; welding the tube-tube materials or tube-rod materials between the guides while applying a pressure with a sealing pressure block from a direction parallel to the guides; and cutting the resulting product at the pressure-welded portions to obtain an annular sustained release preparation comprising at least two polymer tubes having both ends sealed 5 and integrated by pressure-welding or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-welding wherein an annular space can be formed by pulling the tubes or the tube and the rod apart from each other at a center portion therebetween, the center portion not having been pressure-welded; wherein the fixed distance is a length calculated from diameters of the tube-tube 20 materials or the tube-rod materials so that an angle formed between a line connecting respective centers of the diameters of the materials to be welded and the pressure application direction is from 0 to 45°. 6 2015201318 08 Sep 2016
Advantageous Effects of Invention
The annular sustained release preparation according to the invention can be easily installed and stably maintained after installation because when it is opened at the center portion between the tubes or the tube and the rod upon use, cleavage due to insufficient weld strength at the wielded ends does not easily occur. It is therefore suitable for being hung on or wound around a branch or trunk of a plant, B rief Description of Drawings
Further features of the present invention are more fully described in the following 0 description of several non-limiting embodiments thereof. This description is included solely for the purposes of exemplifying the present invention. It should not be understood as a restriction on the broad summary, disclosure or description of the invention as set out above. The description will be made with reference to the accompanying drawings in which 5 [Fig. 1] FIG. 1 shows one example of an annular sustained release preparation comprising two polymer tubes.
[Fig. 2] FIG. 2 shows one example of an annular sustained release preparation comprising three polymer tubes.
[Fig. 3] FIG. 3 show's one example of an annular sustained release preparation 20 comprising a polymer tube filled with a sex pheromone liquid and a polymer tube filled with a metal wire.
[Fig. 4] FIG, 4 shows one example of an annular sustained release preparation comprising a polymer tube and a polymer rod [Fig. 5] FIGS. 5(A), (B) and (C) show examples of a pressure-welding step of two 25 polymer materials in which an angle a is 0° in (A), 30° in (B), and 45° in (C). 2015201318 08 Sep 2016 7 [Fig. 6] FIGS. 6(A), (B) and (C) show examples of a pressure-welding step of three polymer materials in which two angles a are each 0° in (A), 30° in (B), and 45° in (C).
[Fig. 7] FIG. 7 shows an example of a guide to be used in the pressure-welding 5 step.
[Fig. 8] FIG. 8 shows a side wall of a groove made in a sealing table as another exampl e of a guide to be used in the pressure-welding step.
[Fig. 9] FIGS. 9(A), (B) and (C) each shows a relationship between the length of the guide and the angle a in which the angle a is 0° in (A), 30° in (B), and 45° in 0 (C).
[Fig. 10] FIG 10 shows an embodiment in Comparative Example 1 in which a line connecting the respective centers of the polymer materials and a pressure application direction form an angle of 60°.
[Fig. 11] FIG. 11 shows a method for measuring cleavage strength of the sealed 5 ends.
[Fig. 12] FIG. 12 shows an application example of a conventional annular sustained release preparation.
[Fig. 13] FIG. 13 shows the conventional annular sustained release preparation having cleavage at the sealed end. 20 [Fig. 14] FIG. 14 shows a pressure-welding step of two polymer materials for producing the conventional annular sustained release preparation.
The drawings shown are not necessarily to scale, with emphasis instead generally being placed upon illustrating the principles of the present invention. 25 2015201318 08 Sep 2016 8
Description of Embodiments
The invention provides an annular sustained release preparation comprising at least two polymer tubes having both ends sealed and integrated by pressure-welding, and a sex pheromone liquid contained by at least one of the polymer tubes, wherein an annular space can be formed by making an opening at a center portion between the polymer tubes at which they have not been pressure welded.
The annular sustained release preparation may comprise at least two polymer tubes, each tube containing a sex pheromone liquid. It may comprise at least one tube containing a sex pheromone liquid and at least one tube not containing a sex pheromone liquid. The 0 tube not containing a sex pheromone liquid therein may contain a metal wire. The metal wire is flexible and can maintain a fixed shape so that it is suitable for installing the annular sustained release preparation. The metal for the metal wire includes, but not limited to, an aluminum wire, a copper wire and a ware made of an alloy thereof.
Polymer materials used for the at least two polymer tubes may be different from 5 each other insofar as they can be welded while applying a pressure thereto. However, when they are same, the strength of the connected part by a pressure-welding is high and they can be welded easily because they are melted under the same condition, A specific example of an annular sustained rel ease preparation comprising tw'Q polymer tubes, each containing a sex pheromone liquid, is shown in FIG. 1, while a specific 20 example of an annular sustained release preparation comprising three polymer tubes, each containing a sex pheromone liquid, is shown in FIG 2.
In a sustained release preparation 10 in FIG. I, a sex pheromone liquid 11 is enclosed in two polymer tubes 12 and 13 which can be deformed semi-elastically. The preparation has ends 15 at which the tubes have been sealed and integrated each other and 25 can form an annular space by pulling the tubes apart from one another at the center portion 16 therebetween. As the sex pheromone liquid 11, a sex pheromone substance of the same 2015201318 08 Sep 2016 9 kind or sex pheromone substances different in kind may be filled in the two tubes, respectively.
In a sustained release preparation 20 in FIG 2, a sex pheromone liquid 21 is enclosed in each of three polymer tubes 22, 23 and 24. The preparation has ends 25 at 5 which the tubes have been sealed and integrated each other and can form an annular space by pulling the tubes apart from each other at one or both of the two center portions 26 between them. As the sex pheromone liquid 21, a sex pheromone substance of the same kind or sex pheromone substances different in kind may be filled in the three tubes, respectively. 0 In an embodiment of the annular sustained release preparation, a polymer tube contains a sex pheromone substance of a certain insect pest and another polymer tube contains a sex pheromone substance of another insect pest so that a plurality of insect pests can be controlled simultaneously. In an embodiment of the annular sustained release preparation, two or more polymer tubes contain the same sex pheromone substance so that a 5 release amount at one place can be increased.
An example of an annular sustained release preparation comprising a polymer tube containing a sex pheromone liquid therein and a polymer tube containing a metal wire therein is shown in FIG. 3.
The sustained release preparation 30 in FIG. 3 comprises a polymer tube 32 20 containing a sex pheromone liquid 31 therein and a polymer tube 33 containing a metal wire 37 therein, has ends 35 at which the tubes have been sealed and integrated each other, and can form an annular space by pulling the tubes apart from each other at a center portion 36 therebetween.
In the invention, there is also provided an annular sustained release preparation 25 comprising at least one polymer tube and at least one polymer rod which have been sealed and integrated at both ends thereof by pressure-welding, and a sex pheromone liquid 2015201318 08 Sep 2016 10 contained by the at least one polymer tube, wherein an annular space can be formed by pulling the tube and the rod apart from each other at a center portion therebetween at which they have not been pressure-welded.
It is a modification example of the embodiment in which a tube containing a sex 5 pheromone and a tube not containing a sex pheromone are used in combination, wherein the tube not containing a sex pheromone is replaced by a rod. Hie rod is advantageous over a tube in strength because the tube is hollow. Different from the tube containing a metal wire therein, the rod does not require covering of a metal wire and can retain a fixed shape, though not so well as the metal wire. 0 Polymer materials used for the at least one polymer tube and the at least one polymer rod may be different from each other insofar as they permit wielding under pressure. However, they are preferably same from the standpoint of strength of the connected portion by the pressure-welding and ease of operation due to melting which occurs under the same state. 5 An example of the annular sustained release preparation comprising a polymer tube containing a sex pheromone therein and a polymer rod in combination is shown in FIG. 4,
An annular sustained release preparation 40 in FIG. 4 comprises a polymer tube 42 containing a sex pheromone liquid 41 therein and a polymer rod 43, has ends 45 at which 20 they have been sealed and integrated each other, and can form an annular space by pulling them apart from each other at a center portion 46 therebetween.
According to the invention, in the annular sustained release preparation, a line connecting the respective centers of diameters of the at least two polymer tubes or of at least one polymer tube and at least one polymer rod and a pressure application direction of 25 pressure-welding form an angle a of from 0 to 45°. When the angle a is more than 45°, sufficient weld strength cannot be obtained because of a decrease in the contact area 2015201318 08 Sep 2016 11 between the tube and the tube, or between the tube and the rod.
The angle a during pressure-welding can be confirmed from the shape of the annular sustained release preparation obtained. For example, since the annular sustained release preparation is obtained by being cut at positions where the tube and the tube (or the 5 tube and the rod) have been sealed and integrated by pressure-welding, it usually has remaining melt fragments at both ends thereof A plane which has been subjected to a pressure becomes flattened and the angle a during pressure-welding can be calculated based on the plane and a shape of the tube and the tube (or the tube and the rod). Even if the remaining fragment is small and the flattened direction is not clear, the direction from which 0 the pressure has been applied remains in the fragment as an internal stress so that it is possible to measure the direction of the internal stress in a known manner and determine the angle a during the pressure-welding. This means that the angle a during the pressure-welding can be a constituent element of the annular sustained release preparation thus obtained. 5 FIGS. 5(A), (B) and (C) shows a line C connecting centers €i and C2 of the diameters of two polymer materials and a line indicating a direction of pressure P to them with a pressure block 1, these lines forming an angle a. The angle a is 0° in FIG. 5(A), 30° in FIG. 5(B), and 45° in FIG. 5(C). In these drawings, M shows the direction of a pitch feed. The term “polymer material” as used herein may be a polymer material for tube or a 20 polymer material for rod.
In FIGS. 6(A), 6(B) and 6(C), three polymer materials having centers Ci, C2, and C3, respectively, are used, and an angle formed between a line connecting the centers Cj and C2 and a line indicating a pressure application direction is expressed as «π, while an angle formed between a line connecting the centers C2 and C3 and a line indicating the pressure 25 application direction is expressed as ce?3. Shown are «12=0° and 0.23=0° in FIG. 6(A), and «12=30° and a23~30° in FIGS. 6(B) and 6(C). In FIG 6(C), «13 which is an angle formed 2015201318 08 Sep 2016 12 between a line connecting the centers Ci and C3 and a line indicating the pressure application direction is 90° and equal to that of the conventional method, but it poses no problem because the polymer materials having the center Ci and the center C? are welded firmly with the angles cci2=30° and 0623=30°, respectively, to the polymer material having 5 the center C2.
The annular sustained release preparation of the invention can be produced, for example, as described below.
First, respective pressure-welding portions of at least two polymer materials for tube which have been arranged in a longitudinal direction, or respective pressure tvelding 0 portions of at least one polymer material for tube and at least one polymer material for rod which have been arranged in a longitudinal direction are placed between guides parallel to each other with a certain distance. The guides are disposed on a sealing table perpendicularly thereto. The guides may be placed on the sealing table, or may be two side walls of a groove of uniform depth made in the sealing table perpendicularly to the 5 surface of the sealing table. FIG. 7 shows guides 3a and 3b parallel to each other and perpendicular to a sealing table 2, Polymer materials 52 and 53 placed in the guides are pressurized with a sealing pressure block 1 from a direction parallel to the guides. FIG. 8 shows, as guides, side walls 4a and 4b placed on a bottom surface 2a (in a 20 sealing table 2) of the groove of uniform depth made perpendicularly to the surface of the sealing table 2. The bottom surface 2a is parallel to the surface of the sealing table 2 in which no groove has been made and an angle formed between the bottom surface 2a and each side wall is 90°. The polymer materials 52 and 53 placed in the groove are pressurized with a sealing pressure block 1 from a direction parallel to the guides 25 2015201318 08 Sep 2016 13
Next, in order to seal and integrate the polymer materials placed between the guides, the polymer materials between the guides are w elded while applying a pressure from a direction parallel to the guides with the sealing pressure block. A specific sealing method is not particularly limited. The polymer materials are 5 welded, for example, by applying a pressure of from 0.1 to 0.3 MPa to the polymer materials and oscillating them at from 200 to 1500 mmsec with an ultrasonic oscillator of from 20 to 50 (Ltm. Not only ultrasonic sealing but also heat sealing or high-frequency sealing may be employed for joining them. The ultrasonic sealing is suited for hermetic sealing because contaminants on the joining surfaces are dissipated through ultrasonic 0 vibration and the polymer materials can be joined irrespectively of the presence or absence of a pheromone.
Then, the sealed product is cut at the positions where the polymer materials have been sealed and integrated by pressure-welding, leaving respective melted fragments in order to keep the seal and integration. As a result, an annular sustained release preparation 5 can be obtained, the preparation comprising at least two polymer tubes having both ends sealed and integrated by pressure-welding, or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-w7elding, and a sex pheromone liquid contained by at least one of the polymer tubes, wherein an annular space can be formed by pulling the tubes (or the tube and the rod) apart from each other at a 20 center portion therebetween which have not been pres sure-welded.
The distance between the guides is selected so that the angle a formed between a line connecting the respective centers of the diameters of the polymer materials placed between the guides and the pressure application direction during pressure-welding is from 0 to 45°. 25 2015201318 08 Sep 2016 14
Embodiments of pressure-welding two polymer m ateri als equal in di ameter are illustrated in FIGS. 9(A), (B) and (C). FIGS. 9(A), (B) and (C) show' a line C connecting centers Ci and C2 of the diameters of tw'o polymer materials each having a radius r and a line indicating a pressure application direction with a pressure block 1, these lines forming 5 an angle a. The angle a can be adjusted to 0° by setting a distance L between the guides 4a and 4b to 2r as shown in FIG 9(A); the angle a can be adjusted to 30° by setting a distance L between the guides to 3r as shown in FIG. 9(B); and the angle a can be adjusted to 45° by adjusting a distance L between the guides to (2+ V2)r. Incidentally, V2 means a square root of 2 and is approximately 1.4, The angle a can thus be adjusted to from 0 to 0 45° by placing the polymer materials between the guides which are disposed perpendicularly to a sealing table and are parallel to each other with a distance of from 2 to 3.4 times as much as the distance of radius r.
The two polymer materials each having a radius of r as shown in FIGS. 9(A), (B) and (C) include two polymer materials for tube having the same radius r, and a combination 5 of a polymer material for tube and a polymer material for rod each having the same radius r.
Even if the two polymer materials have respectively different radii, the distance of the guides giving the angle a of from 0 to 45° can be selected according to the similar calculation.
Even if three or more polymer materials are pressure-welded, when they are placed 20 for aligning the respective centers of all the diameters in line, the distance of the guides giving the angle a of from 0 to 45° can be selected according to the similar calculation whether the radii of the three materials may be the same or different.
When three or more polymer materials are pressure-welded and the respective centers of all the diameters are not aligned in line, a desirable layout of the three or more 25 polymer materials is drawn and the distance between the guides is calculated based on the layout. When the three or more polymer materials contain an extremely thin polymer 2015201318 08 Sep 2016 15 material or an extremely thick polymer material, a desired angle a may not be obtained in theory due to movement of the tubes or rods between the guides during application of a pressure. However, in practice, there is neither utility nor necessity of polymer materials having extremely different sizes. 5 Further, setting the distance between the guides to be equal to the largest diameter of the diameters of the polymer materials is preferred because the angle a can be maintained around 0°, thereby eliminating the possibility of the angle a falling outside the range of from 0 to 45° even if a polymer material on the polymer material having the largest diameter slides during pressure-welding. 0 It is also preferred to dispose a retainer which is, for example, formed by changing a metal wire or the like into a desired shape, just upstream or downstream of the guides in order to prevent the polymer material between the guides from sliding during pressure application.
The length of the guides, that is, the length of the guides in a longitudinal direction 5 of the polymer materials is usually from 2 to 8 mm. The pressure-welded portion becomes longer than the length of the guides because the polymer extends by pressure-welding. For example, use of a guide having a length of 5 mm results in a welded portion of about 8 mm long.
Examples of the polymer material include thermoplastics such as low density 20 polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, ethylene-acrylate copolymer, polyvinyl acetate, polyvinyl chloride, polystyrene, polyamide, polycarbonate, poivvinylidene chloride, polybutylene, methyl methacrylate-styrene copolymer, polyacetal, cellulose acetate, cellulose acetate butylate, poivvinylidene fluoride and silicon resin. They also include condensation 25 polymers made from at least one dicarboxylic acid selected from the group consisting of oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, sebacic acid, fumaric acid 2015201318 08 Sep 2016 Ιό and maleic acid, and at least one polyol selected from the group consisting of ethylene glycol, propylene glycol, butanedlol, pentanediol, hexanediol, octanediol and decanediol; condensation polymers of at least one selected from the group consisting of lactic acid, hydroxyvaleric acid, hydroxycaproic acid and hydroxycaprie acid; and aliphatic polyester 5 type thermoplastics such as polycaprolactone. A lubricant, a plasticizer, a stabilizer, a pigment and/or a filler may be added to these polymers.
The polymer material for tube which contains a sex pheromone therein can be produced by continuous processing such as extrusion. It has an inner diameter of 0 preferably from 0.4 to 2 mm, more preferably from 0.6 to 1.6 mm and has a wall thickness of preferably from 0.2 to 1.5 mm, more preferably from 0.25 to 0.8 mm. An elongated polymer material is preferred. When a polymer material for tube has an inner diameter less than 0.4 mm, it is technically difficult to be formed and it may be difficult to fill the tube with a synthetic liquid pheromone. A tube having an inner diameter greater than 2 5 mm can be filled with a large amount of a synthetic liquid pheromone, but the amount may be excessive. The wall thickness of the polymer material for tube has a large influence on the diffusion rate of a synthetic pheromone through a polymer membrane. When the polymer material for tube has a wall thickness less than 0.2 mm, it may be difficult to be formed. When the polymer material for tube has a wall thickness greater than 1.5 mm, the 20 diffusion rate of a synthetic pheromone may be reduced excessively and the productivity may be lowered due to a large amount of extrusion resin.
As the polymer material for tube which contains a metal wire therein and the polymer materia! for rod, the same materials as the above polymer materials can be employed. They may be the same or different from the polymer materials for tube which 25 contains a sex pheromone therein. The outside diameter of the polymer material for tube which contains a metal wire therein and the outside diameter of the polymer material for rod 2015201318 08 Sep 2016 17 may be preferably equal to or smaller than the outside diameter of the tube which contains a sex pheromone therein. More preferably, they may be reduced by 20% or less in comparison with the outside diameter of the tube which contains a sex pheromone therein.
The effective length of the annular sustained release pheromone preparation 5 according to the invention is preferably from 100 to 2000 mm, more preferably from 200 to 1500 mm. When the preparation has an effective length less than 100 mm, it may be diffi cult to be installed because of an excessively small diameter of the annular preparation . When the preparation has an effective length exceeding 2000 mm, it may be unsuited for transport or packaging and may be too large to be pulled apart into a ring by hands. 0 As the polymer tube containing a sex pheromone liquid therein, hollow tube or tube compri sing a porous inner layer having pores communicated to each other and an outer layer through which the sex pheromone li quid penetrates can be used. From the standpoint of uniform release of the sex pheromone liquid, the latter is preferred.
The present invention will hereinafter be described in detail. It should not be 5 construed that the present invention is limited to or by them.
Example 1
Two polymer materials for tube having an inner diameter of 1.10 mm and a wall thickness of 0.50 mm were prepared by extruding an ethylene-vinyl acetate copolymer. A 20 synthetic pheromone liquid of a leaf roller was then fdled in these polymer materials under pressure. The resulting two polymer materials were then placed between guides provided with a distance of 2.2 mm and were subjected to ultrasonic sealing with an aluminum block having a width of 5 mm at a pitch distance of 204 mm. A sustained release preparation was obtained by cutting the sealed product at the sealed parts. 25 2015201318 08 Sep 2016 18
Incidentally, ultrasonic sealing was performed such that an angle between a pressure application direction with the aluminum block and a line connecting the respective centers of the two polymer materi als was 0C (meaning that they had the same direction). 5 Comparative Example 1
Two polymer material s for tube having an inner diameter of 1.10 mm and a wall thickness of 0.50 mm were prepared by extruding an ethylene-vinyl acetate copolymer. A synthetic pheromone liquid of a leaf roller was then filled in these polymer materials under pressure. The resulting two polymer materials were placed between guides provided with 0 a distance of 4.6 mm and were subjected to ultrasonic sealing with an aluminum block having a width of 5 mm at a pitch distance of 204 mm. A sustained release preparation was obtained by cutting the sealed product at the sealed parts.
Incidentally, ultrasonic sealing was performed such that an angle a between a pressure application direction with the aluminum block and a line connecting the respective 5 centers of the two polymer materials was 90°.
Example 2
Two polymer materials for tube having an inner diameter of 0.80 mm and a wall thickness of 0.35 mm were prepared by extruding a copolymer which is a condensation 20 polymer of adipic acid (a dicarboxylic acid) and butanediol. A synthetic pheromone liquid of an oriental fruit moth was then fi Sled in the polymer materials under pressure. The resulting two polymer materials were placed between guides provided with a distance of 1,6 mm and were subjected to ultrasonic sealing with an aluminum block having a width of 5 mm at a pitch distance of 2204 mm. A sustained release preparation was obtained by 25 cutting the sealed product at the sealed parts.
Incidentally; ultrasonic sealing was performed by placing the two tubes in a groove having a width of 3.76 mm and a depth of 5.0 mm made in a sealing table and then applying a pressure with a sealing aluminum block provided with a clearance to the groove. In this case, an angle between a line connecting the respective centers of the two tubes and a 5 pressure application direction was 45°. 2015201318 08 Sep 20
Example 3
Two polymer materials for tube having an inner diameter of 0.80 mm and a wall thickness of 0.35 mm were prepared by extruding a copolymer which is a condensation 0 polymer of adipic acid (a dicarboxylic acid) and butanediol. A synthetic pheromone liquid of an oriental fruit moth was then filled in the polymer materials under pressure. The resulting two polymer materials were placed between guides provided with a distance of 2.25 mm and were subjected to ultrasonic sealing with an aluminum block having a width of 5 mm at a pitch distance of 2204 mm. A sustained release preparation was obtained by 5 cutting the sealed product at the sealed parts.
Incidentally, ultrasonic sealing was performed by placing the two tubes in a groove having a width of 2.3 mm and a depth of 5.0 mm made in a sealing table and then applying a pressure with a sealing aluminum block provided with a clearance to the groove. In this case, an angle between a line connecting the respective centers of the two tubes and a 20 pressure application direction was 30°.
Comparative Example 2
Two polymer materials for tube having an inner diameter of 0.80 mm and a wall thickness of 0.35 mm were prepared by extruding a copolymer which is a condensation 25 polymer of adipic acid (a dicarboxylic acid) and butanediol. A synthetic pheromone liquid of an oriental fruit moth was then filled in these polymer materials under pressure. The 2015201318 08 Sep 2016 20 resulting two polymer materials were aligned and were subjected to ultrasonic sealing with an aluminum block having a width of 5 mm at a pitch distance of 204 mm. A sustained release preparation was obtained by cutting the sealed product at the sealed parts.
Incidentally, ultrasonic sealing was performed by placing the two tubes in a groove 5 having a width of 4.10 mm and a depth of 5.0 mm made in a sealing table and then applying a pressure with a sealing aluminum block provided with a clearance to the groove. In this case, an angle formed between a line connecting the respective centers of the two tubes and a pressure application direction was 60° (FIG. 10).
Strength against the cleavage of the sustained release preparations obtained in 0 Examples 1 to 3 and Comparative Examples 1 and 2 was measured using a method shown in FIG. 11, More specifically, a digital balance 5 was connected to the center portion of a sustained release preparati on (Sample S), applying a tensile force F so as to pull Sample S apart at the center portion thereof, and measure a load at the time when cleavage occurred at the welded end of the sample. Measurement was conducted 20 times and average, 5 maximum, and minimum values are shown in Table 1.
[Table 1] angle a load of cleavage at the welded end (degree) maximum (kg) minimum (kg) average (n=20) (kg) Example 1 0 2.7 0.95 1.83 Example 2 45 2.3 0.70 1.50 Example 3 30 1.6 0.70 1.20 Comp.Ex. 1 90 1.5 0.25 0.69 Comp.Ex.2 60 1.0 0.10 0.40 2015201318 08 Sep 2016 21
The results in Table 1 have revealed that the annular sustained release preparations obtained by adjusting the angle a formed between a pressure application direction with an aluminum block and a line connecting the respective centers of two tubes to 0°, 30° and 45°, respectively, have higher strength against cleavage than those obtained by adjusting the angle a to 60° and 90°. Particularly when the angle a is adjusted to 0°, that is, when the pressure application direction with an aluminum block and the direction of aligning the two tubes are same, the strength against cleavage becomes the maximum.
The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting. As used herein, the singular forms “a”, “an” and “the” may be intended to include the plural forms as well, unless the context clearly indicates otherwise. The terms “comprise”, “comprises,” “comprising,” “including,” and “having,” or variations thereof are inclusive and therefore specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
Modifications and variations such as would be apparent to the skilled addressee are considered to fall within the scope of the present invention. Use present invention is not to be limi ted in scope by any of the specific embodiments described herein. These embodiments are intended for the purpose of exemplification only. Functionally equivalent products, formulations and methods are clearly within the scope of the invention as described herein. 2015201318 08 Sep 20
Reference Signs List 1 Pressure block 2 Sealing table 2a Bottom surface 3a, 3b Guide 4a, 4b Side wall 5 Digital balance 1(3, 20, 30, 40, 110 Sustained release preparation 11, 21, 31, 41 Sex pheromone liquid 0 12, 13, 22, 23, 24, 32, 33, 42, 112, 113 Polymer tube 15, 25, 35, 45, 115, 115a, 115b End 16, 26, 36, 46 Center portion 37 Metal wire 43 Polymer rod 5 52, 53, 122, 123 Polymer material α, (x j.\. a!3, a-n Angle C Line
Cl, C2, C3 Center F Tensile force 20 L Distance M Direction of pitch feed P Pressure R Radius S Sample
Claims (6)
- CLAIMS [Claim 1] An annular sustained release preparation comprising: at least two polymer tubes having both ends sealed and integrated by pressure-welding, or at least one polymer tube and at least one polymer rod sealed and integrated at both ends by pressure-welding; and a sex pheromone liquid contained by at least one of the tubes or the tube; wherein an annular space can be formed by pulling the tubes or the tube and the rod apart from each other at a center portion therebetween, the center portion not having been pressure-welded; and an angle formed between a line connecting respective centers of diameters of the tubes welded to each other or the tube and the rod welded to each other and a pressure application direction is from 0 to 45°. [Claim
- 2] The annular sustained release preparation according to Claim 1, wherein the angle is 0°. [Claim
- 3] The annular sustained release preparation according to Claim 1 or 2, wherein at least one of said at least two polymer tubes comprises a metal wire therein, [Claim
- 4] A method for producing an annular sustained release preparation comprising at least the steps of: placing, between two guides which are disposed on a sealing table, are perpendicular to the sealing table and are parallel to each other with a fixed distance, respective pressure-welding planned portions of at least two polymer materi als for tube (which wall hereinafter be referred to as “tube-tube materials”) aligned in a longitudinal direction or respective pressure-weiding planned portions of at least one polymer material for tube and at least one polymer material for rod (which will hereinafter he referred to as “tube-rod materials) aligned in a longitudinal direction, at least one of the tube-tube materials or at least one of the tube-rod materials containing a sex pheromone liquid therein; welding the tube-tube materials or tube-rod materials between the guides while applying a pressure with a sealing pressure block from a direction parallel to the guides; and cutting the resulting product at the pressure-welded portions to obtain an annular sustained release preparation comprising at least two polymer tubes having both ends sealed and integrated by pressure-wielding or at least one polymer tube and at least one polymer rod having both ends sealed and integrated by pressure-welding wherein an annular space can be formed by pulling the tubes or the tube and the rod apart from each other at a center portion therebetween, the center portion not having been pressure-welded; wherein the fixed distance is a length calculated from diameters of the tube-tube materials or the tube-rod materials so that an angle formed between a line connecting respective centers of the diameters of the materials to be welded and the pressure application direction is from 0 to 45°. [Claim
- 5] The method for producing an annular sustained release preparation according to Claim 4, wherein said guides are sidewalls of a groove of uniform depth made in the sealing table perpendicularly to the surface of the sealing table. [Claim
- 6] The method for producing an annular sustained release preparation according to Claim 4 or 5, wherein the fixed distance is equal to the largest diameter among the diameters of the tube-tube materials or the tube-rod materials.