Description

1 ANTISAPSTAIN COMPOSITIONS COMPRISING A HALOALKYNYL COMPOUND, AN AZOLE AND AN UNSATURATED ACID Field of the Invention 5 The present invention relates to formulations for protecting wood and other cellulosic substrates against moulds, staining and other defacing organisms, and in particular to antisapstain applications. 10 Background of the Invention Any discussion of the prior art throughout the specification should in no way be considered as an admission that such prior art is widely known or forms part of common general knowledge in the field. 15 Antisapstain chemicals are used to protect timber, in particular freshly felled or sawn timber, from attack by moulds, sapstain and decay fungi which would otherwise discolour the timber and so reduce its value. A commonly used chemical in anti-sapstain 20 applications is 3-iodo-2-propynyl-butyl-carbamate (IPBC). However, IPBC is known to be susceptible to degradation by a number of mechanisms, all of which compromise its performance against mould and stain. Known mechanisms by which IPBC can be rendered inactive 25 are decomposition by exposure to UV, by bacteria, by hydrolysis and by reaction with metal ions. Exposure to UV can be problematic as treated timber is often stored outside in direct sunlight during common commercial practices. Furthermore, antisapstain compositions are 30 typically applied by dipping processes using metal dipping tanks. Often, either the processing equipment used to dip the timber or the dipping tank itself suffer corrosion, allowing reactive metal ions to leach into the dipping solution. These metal ions can react with 35 any IPBC present in the antisapstain solution, rendering it inactive.

2 It is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative. The present inventors have found that the 5 protection from mould and other staining organisms afforded by haloalkylnyl containing timber treatment formulations can be greatly enhanced by the inclusion of a number of unsaturated acids, salts or precursors thereof. 10 Thus, the present invention provides an antisapstain composition comprising a haloalkynyl compound, an azole and an unsaturated carboxylic or sulfonic acid, salt or precursor thereof. Unless the context clearly requires otherwise, 15 throughout the description and the claims, the words "comprise", "comprising", and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense; that is to say, in the sense of "including, but not limited to". 20 Although the invention has been described with reference to specific examples it will be appreciated by those skilled in the art that the invention may be embodied in many other forms. 25 Summary of the Invention According to a first aspect of the present invention there is provided a wood preservative composition for inhibiting discoloration due to mold, sapstain or fungi, the composition comprising: 30 a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate, 3-iodo-2-propynyl butyl carbamate, 3-iodo-2 propynyl hexyl carbamate, 3-iodo-2-propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl 2a carbamate, and mixtures thereof, a 1,2,4-triazole compound; and an unsaturated carboxylic acid, or a salt thereof, wherein the unsaturated carboxylic acid 5 has at least 4 carbon atoms, and the ratio of the unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight basis ranges from 1:1 to 25:1. 10 According to a second aspect of the present invention there is provided a method of protecting a substrate formed of wood or cellulosic material which comprises: applying to the wood or cellulosic substrate a 15 wood preservative composition in an amount to inhibit discoloration due to mold, sapstain or fungi, the wood preservative including a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate, 20 3-iodo-2-propynyl butyl carbamate, 3-iodo-2 propynyl hexyl carbamate, 3-iodo-2-propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl carbamate, and mixtures thereof, a 1,2,4-triazole compound; and 25 an unsaturated carboxylic acid, or a salt thereof, wherein the unsaturated carboxylic acid has at least 4 carbon atoms, and the ratio of the unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight 30 basis ranges from 1:1 to 25:1, or applying the individual components of the wood preservative composition to the wood or cellulosic substrate such that the wood or cellulosic substrate effectively receives the wood 35 preservative in an amount to inhibit discoloration due to mold, sapstain or fungi.

2b According to a third aspect of the present invention there is provided a substrate made of wood or cellulosic material treated with an amount of wood 5 preservative to inhibit discoloration due to mold, sapstain or fungi, the wood preservative comprising: a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate, 3-iodo-2-propynyl butyl carbamate, 3-iodo-2 10 propynyl hexyl carbamate, 3-iodo-2-propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl carbamate, and mixtures thereof, a 1,2,4-triazole compound; and an unsaturated carboxylic acid, or a salt 15 thereof, wherein the unsaturated carboxylic acid has at least 4 carbon atoms, and the ratio of the unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight basis ranges from 1:1 to 25:1. 20 The haloalkylnyl compounds used in the composition of the present invention are represented by the general formula (I): Y

CH

2 m X 25 (I) wherein Y is a halogen, preferably iodine; m is an integer between 1 and 3; and X can be (1) oxygen which is part of an organic functional group; (2) nitrogen which is part of an 30 organic functional group; (3) sulphur which is part of an organic functional group; or (4) carbon which is part of an organic functional group. The functiol Crou) oCfJ i .oXygen is a part i preferably an ether, ester, or carbamate group. The 2c fuctionla.l group of which Altrogen .is a rart is pfra a:r> aminle, amei, ere, nt rie c a roup. 1h functional grouo of which 1 i is a part s preferabIv a thiol, thiane, sulfone or sulfoxide 5 grup, The ora i functi ona group of v iCh carbnis a i: C.L 'referb V a-~ s--e )'ir -eqro1 part is prer a n ester, carbamate a or all k g rup. Examples of compounds which may be used as the haloalkynyl compound of this invention are especially the fungicidally active iodoalkynyl derivatives. 10 Suitable iodoalkynyl derivates are disclosed in U.S. Pat. Nos. 3,923,870, 4,259,350, 4,592,773, 4,616,004, 4,719,227, and 4,945,109. These iodoalkynyl derivatives include compounds derived from propargyl or iodopropargyl alcohols such as the esters, ethers, 15 acetals, carbamates and carbonates and the iodopropargyl derivatives of pyrimidines, thiazolinones, tetrazoles, 3 triazinones, sulfamides, benzothiazoles, ammonium salts, carboxamides, hydroxamates, and ureas. Thus, preferred haloalkynyl compounds include compounds of the general formula (II): 5 0 I ~~-- O 11 N R H2±H+ wherein R is selected from the group consisting of hydrogen, substituted and unsubstituted alkyl groups having from 1 to 20 carbon atoms, substituted and 15 unsubstituted aryl, alkyl aryl, and aralkyl groups having from 6 to 20 carbon atoms and from substituted and unsubstituted cycloalkyl and cycloalkenyl groups of 3 to 10 carbon atoms, and m and n are independently integers from 1 to 3, i.e., m and n are not necessarily 20 the same. Preferably, n is 1. Preferably the haloalkynyl compound is an iodopropynyl carbamate. Preferred are compounds where m is 1 and n is 1 having the following formula (III): 0 - C O N-R

H

2 H (III) 25 Suitable R substituents include alkyls such as methyl, ethyl, propyl, n-butyl, t-butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, dodecyl, octadecyl, cycloalkyls such as cyclohexyl, aryls such as phenyl, alkaryls and aralkyls such as benzyl, tolyl, cumyl, 30 halogenated alkyls and aryls, such as -chlorobutryl and chlorophenyl, and alkoxy aryls such as ethoxyphenyl and the like. Especially preferred haloalkynyl compounds of this formula include iodopropynyl carbamates such as 3-iodo 35 2-propynyl propyl carbamate, 3-iodo-2-propynyl butyl carbamate, 3-iodo-2-propynyl hexyl carbamate, 3-iodo-2- 4 propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl carbamate, and mixtures thereof. Most preferred is 3 iodo-2-propynyl butyl carbamate (IPBC). By "unsaturated carboxylic acid" and "unsaturated 5 sulphonic acid" is meant any carboxylic or sulphonic acid that also contains a carbon-carbon double bond. Suitable acids include linear, cyclic or aromatic carboxylic or sulphonic acids. By "precursor" is meant any group that can be 10 hydrolysed to form a carboxylic acid or sulphonic acid or its conjugate base. Suitable precursors include. esters, aides and anhydrides of carboxylic or sulphonic acids, with enters and anhydrides being preferred. Most preferred precursors are esters and anhydrides of 15 unsaturated carboxylic acids. Preferably, the precursor compound is non-polymeric. The formulations preferably comprise -unsaturated carboxylic or sulphonic acids, or salts thereof. Carboxylic acids and their salts and precursors are 20 preferred. Preferred salts of the unsaturated acid are alkali metal salts, and alkaline earth metal salts. Preferably, alkali metal salts are used. Preferred alkali metals are sodium and potassium. 25 In one preferred embodiment, the acids are unsaturated cyclic carboxylic acids. Most preferred are unsaturated cyclic monocarboxylic acids. The unsaturated cyclic acid, salt or precursor thereof may be an aromatic acid, salt or precursor -30 thereof. Suitable aromatic groups include five membered heteroaromatic groups such as furyl, pyrrolyl, and thienyl; six membered aromatic and heteroaromatic groups such as phenyl, pyridyl, pyrazinyl, pyrimidinyl, and pyridazinyl; 9 membered heteroaromatic groups such as 35 indolyl, isoindolyl, and benzimidazyl; and 10 membered aromatic and heteroaromatic groups such as naphthyl, 5 quinolyl, and isoquinolyl. Preferred aromatic or heteroaromatic groups are furyl, pyrrolyl, thienyl, pyridyl, phenyl and naphthyl. Most preferred is phenyl. Preferred aromatic acids are represented by the 5 general formula (IV) Y R)m (IV) wherein Y denotes CO 2 M or SO 3 M; each R independently denotes C 1

-C

4 alkyl, OH, OMe, OEt, NH 2 , NMe, CO 2 M or halogen, 10 wherein two R groups may optionally form naphthyl; M denotes H, K or Na; and m denotes 0 to 5. Preferably, R denotes C 1

-C

4 alkyl, CO 2 H or OH and m denotes 0 to 2. More preferably, R denotes OH and m 15 denotes 0 or 1. Preferred aromatic acids and salts are benzoic acid, sodium benzoate, salicyclic acid, sodium salicyclate, phthalic acid (or phthalic anhydride), benzene sulphonic acid, p-toluene sulphonic acid, sodium 20 tosylate, phenol sulphonic acid, naphthanoic acid, and naphthalene sulphonic acid. Particularly preferred aromatic acids are benzoic acid, sodium benzoate, salicyclic acid, and sodium salicyclate, with alkali metal salts of benzoic acid and particularly sodium 25 benzoate being the most preferred. Alternatively, or in addition to aromatic acids, the unsaturated cyclic acid, salt or precursor thereof may be an unsaturated polycyclic acid. Preferred unsaturated polycyclic acids are resin acids. Resin 30 acids are produced by parenchymatous epithelial cells that surround the resin ducts in trees from temperate coniferous forests. Typically, the compositions of the present invention will use a mixture of resin acids in the form of rosin, or other naturally derived resins. 5 Rosin (also termed rosin acid) is a solid form of resin produced by heating fresh liquid resin to vaporise the volatile liquid terpene components. Rosin consists mainly of abietic acid, and in a higher concentration than the level found in resin. 10 A further derivative containing resin acids that may be used in the composition of the present invention is tall oil. Tall oil (also called liquid rosin) is obtained as a by-product of the Kraft process of wood pulp manufacture. Crude tall oil contains rosin, resin 15 acids (mainly abietic acid and its isomers), fatty acids (mainly palmitic, oleic and linoleic acids) fatty alcohols, sterols and alkyl hydrocarbon derivatives. Preferred resin acids are' abietic-type acids such as abietic acid, neoabietic acid, dehydroabietic acid, 20 and palustric acid, as well as pimaric-type acids such as pimaric acid, levopimaric acid, isopimaric acid. Most preferred are abietic acid, sodium abietate, pimaric acid and sodium pimarate. As an alternative, or in addition to, the 25 unsaturated cyclic acid, the unsaturated acid component may comprise a linear unsaturated acid, salt or precursor thereof. By linear 1 is meant a branched or unbranched alkenyl chain. However, unbranched alkenyl chains are preferred. The linear unsaturated acid may 30 be a mono or a dicarboxylic or sulphonic acid, wherein the acid groups are at the end of the alkenyl chain. Carboxylic acids are preferred, with monocarboxylic acids, salts or precursors thereof being the most preferred. 35 The linear unsaturated acid may be of any length, although preferably the unsaturated acid has at least 4 7 carbon atoms, more preferably from 6 to 22 carbon atoms, more preferably from 6 to 18 carbon atoms, most preferably from 6 to 8 carbon atoms. Preferred linear unsaturated monocarboxylic acids 5 include sorbic acid, myristoleic acid, palmitoleic acid, oleic acid, elaidic acid, linoleic acid, a-linolenic acid, arachidonic acid, eicosapentaenoic acid, euric acid, and docosahexanoic acid. Preferred unsaturated monocarboxylic acids include sorbic acid, myristoleic 10 acid, palmitoleic acid, oleic acid, elaidic acid, linoleic acid, and a-linolenic acid. Preferably, the linear unsaturated monocarboxylic acid is an w-6 fatty acid. In a preferred embodiment, the linear unsaturated 15 carboxylic or sulphonic acids are alkali metal salts and esters. Preferred alkali metal salts are sodium and potassium. In a preferred embodiment, the unsaturated acid precursor is a glycerol ester of an unsaturated fatty 20 carboxylic acid. Especially preferred unsaturated monocarboxylic acids include sorbic acid and oleic acid and salts thereof, with sorbic acid being preferred. Alkali metal salts of sorbic acid are particularly preferred, with 25 the most preferred being sodium sorbate and potassium sorbate. Preferred linear unsaturated dicarboxylic acid include fumaric acid, maleic acid (or maleic anhydride). Most preferred is fumaric acid. 30 These linear unsaturated carboxylic acids may be present in the composition of the present invention as pure acids, or as part of a mixture of different acids. optionally, these mixtures may be in the form of a natural oil such as tall oil, linseed oil, castor oil, 35 corn oil, coconut oil, olive oil or fish oils such as 8 cod liver oil. Tall oil and linseed oil are particularly preferred. The acids are typically relatively weak, i.e. with a pKa above 4.0. 5 Thus, it is particularly preferred for the unsaturated acid to be selected from the group consisting of resin acids, alkali metal salts of salicyclic acid, for example sodium salicyclate and potassium salicyclate, alkali metal salts of benzoic 10 acid, for example sodium benzoate and potassium benzoate, and alkali metal salts or sorbic acid, for example sodium sorbate and potassium sorbate. The formulations of the present invention comprise one or more azole compounds, i.e. a compound- comprising 15 an azole group. The azole compound may be an imidazole or a 1,2,4-triazole and is preferably represented by the general formula (V) R XN R3 R2 20 V wherein X denotes CR or N; R' denotes hydrogen or a linear, branched, cyclic, aromatic or any combination thereof, saturated or 25 unsaturated, substituted or unsubstituted C, to C 4 group wherein any of the carbon atoms other than those bound to the nitrogen atom shown in formula (IV) may be replaced with an optionally substituted hetero atom; Rz denotes hydrogen, Cl-C, alkyl, C 2

-C

8 alkenyl, C 6 -C, 30 aromatic, C 5 -C,0 heteroaromatic or C.-C alkyl carbamate;

R

3 and R denote hydrogen; or together R 3 and R' may provide a benzimidazole group. The imidazole compound incorporates a five-membered diunsaturated ring composed of three carbon atoms.and two nitrogen atoms at non-adjacent positions. The 5 imidazole compound may be a benzimidazole. Preferred compounds include thiabendazole, imazalil, carbendazim and prochloraz. The 1,2,4-triazole compound incorporates a five-membered 'diunsaturated ring composed of three 10 nitrogen atoms and two carbon atoms at non-adjacent positions. Preferred triazole compounds include a triazole compound selected from compounds of formula (VI): OH

H

2

H

2 R-C -C R5

CH

2 N N-J (VI) 15 wherein R 5 represents a branched or straight chain

C

1 , alkyl group (e.g. t-butyl) and R 6 represents a phenyl group optionally substituted by one or more substituents selected from halogen (e.g. chlorine, fluorine or bromine) atoms or C 13 alkyl (e.g. methyl), C 13 alkoxy 20 (e.g. methoxy), phenyl or nitro groups. Alternatively, the triazole compound is advantageously selected from compounds of formula (VII): Ra 0 R7

CH

2 N N N 10 (VII) wherein R 7 is as defined for R' above and Re represents a hydrogen atom or a branched or straight chain C,, alkyl group (e.g. n-propyl). 5 Particularly preferred triazoles include, but are not limited to, triadimefon, triadimenol, triazbutil, propiconazole, cyproconazole, difenoconazole, fluquinconazole, tebuconazole, flusilazole, uniconazole, diniconazole, bitertanol, hexaconazole, azaconazole, 10 flutriafol, epoxyconazole, tetraconazole, penconazole, and mixtures thereof. Most preferred triazoles are propiconazole, azaconazole, hexaconazole, tebuconazole, cyproconazole, triadimefon and mixtures thereof. 15 The compositions typically comprise one or more further active ingredients. Preferred examples of additional active ingredients are quaternary ammonium compounds. A further preferred active ingredient is an amine oxide. Suitable quaternary anmonium compounds and 20 amine oxides that may be used in the compositions of the present invention are described in for example W02007/135435. Preferred quaternary ammonium compounds are trimethyl alkyl quaternary ammonium compounds such as cocotrimethyl ammonium chloride; dialkyldimethyl 25 quaternary ammonium compounds such as didecyl dimethyl ammonium chloride, didecyl dimethyl ammonium carbonate, didecyl dimethyl ammonium bicarbonate, dioctyl dimethyl ammonium chloride and octyl decyl dimethyl ammonium chloride, or mixtures thereof; alkyl dimethyl or diethyl 30 benzyl ammonium salts such as benzalkonium chloride and benzalkonium hydroxide; polyethoxylated quaternary ammonium compounds such as N,N-didecyl-N-methyl poly(oxyethyl) ammonium propionate (Bardap 26) or N,N didecyl-N-methyl-poly(oxyethyl) ammonium lactate; and N 35 substituted pyridinium compounds such as cetyl pyridinium chloride. Preferred amine oxides include 11 alkyldimethylamine oxides such as C 0 alkyldimethylamile oxide, Co-C1 alkyldimethylamine oxide, C 12

-C

6 alkyldimethylamine oxide, C, 6

-C,

8 alky-ldimethylamine oxide, and mixtures thereof. Particularly preferred are 5 C 1 -C alkyldimethylamine oxides, with C 2 alkyidimethylamine oxide being the most preferred. In an alternative, but also preferred class of formulations, amine oxide is not included in the formulation.. Alternatively, if an amine oxide is 10 present, it is not included in combination with either a betaine, a quaternary ammonium compound or a dimethyl alkyl amine. The compositions according to the invention may additionally comprise other active ingredients such as 15 termiticides, insecticides, bacteriocides and other fungicides. Suitable additional fungicides would be apparent to one skilled in the art and will vary according to the application. In particular, additional fungicides which extend the spectrum of activity of the 20 formulation may be chosen, such as fungicides active against bluestain fungi, white rots, brown rots, dry rots and moulds. Suitable additional fungicides include for example, dichlofluanid, acypetacs, including copper and zinc salts, isothiazolones, tolyfluanid, 25 chlorothanonil, -fenpropimorph, borates, guazatine and salts thereof, oxathiazines such as bethoxazin, TCMTB, MBT, PCP and its salts, N-(3-aminopropyl)-N dodecylpropane-1,3-diamine, Dazomet, (E)-1-(2-chloro 1,3-thiazol-5-ylmethyl-2-nitroguanadine, 30 polyhexamethylenebiguanide hydrochloride (PHMB), as well as metal compounds such as copper, Cu-oxide, copper naphthenate, copper carbonate, copper oxine, copper hydroxide, copper dihydroxide, Cu-HDO, potassium-HDO, also iron and zinc and salts, compounds and soaps 35 thereof. However, preferred compositions of the 12 invention are free of biocidal metal ions, particularly free of copper. Suitable insecticides would also be apparent to the skilled man depending upon the intended application, and 5 include, for example, chlorpyrifos, cypermethrin, fenvalerate, fenoxycarb, fipronil, farox, tetramethrin, isofenphos, permethrin, silafluofen, deltamethrin, bifenthrin, cyfluthrin, chlorfenapyr, thiachloprid; etofenprox, chlothianidin, thiamethoxam and 10 imidacloprid, and benzoylureas such as lufenuron, hexaflumuron and flufenoxuron and in particular, flurox. The compositions adcording to the invention may additionally comprise other components which may act to improve the characteristics of the wood treated with 15 these biocides. Such compounds could include water repellents based on waxes, silicones and polysiloxanes, latex, fluorocarbon, organic carboxylate/metals, paper sizing agents or amine oxides, or combinations 'thereof; resins or 'crosslinking agents based on alkyds, acrylics, 20 polyurethanes, formaldehydes, dimethylol,' and epichlorohydrin or combinations thereof. oils may also be used as may UV absorbers, corrosion inhibitors, penetrating aids including glycols, bactericides for example PHMB, colouring agents, antioxidants, metal 25 chelators especially iron chelators, optical brightening agents, defoamers, pH buffers or other stabilisers. Preferred coadditives include PHMB and ethoxylated amines, such as those described in W02007/026008. Ethoduomeen T/130 is a particularly preferred 30 ethoxylated amine. The inventors have shown that the efficacy of the formulations described is surprisingly greater than would be expected based on an additive effect. Therefore synergy is taking place. Thus, preferred 35 compositions comprise an azole and, in proportions which are synergistic as between the two components, a 13 haloalkylnyl compound and an unsaturated carboxylic or sulphonic acid, salt or precursor thereof. It has been found that in some embodiments using complex mixtures of naturally occurring fatty acids, the 5 presence of large amounts of saturated fatty acids can reduce the synergistic effect of the unsaturated acids. Therefore, in a preferred embodiment, the fatty acid component contains less than 40 weight percent saturated carboxylic acids, preferably, less than 25 weight 10 percent saturated carboxylic acids, more preferably less than 10 weight percent saturated carboxylic acids, most preferred is less than 5 weight percent weight saturated carboxylic acids. In relation to the total formulation, the 15 formulation of the present invention preferably contains less that 2 weight percent saturated fatty acid, more preferably less than I weight percent saturated fatty acid, more preferably less than 0.5 weight percent saturated fatty acid, more preferably less than 0.2 20 weight percent saturated fatty acid, most preferred is less than 0.1 weight percent saturated fatty acid. In this context, a saturated fatty acid is a carboxylic acid having an alkyl group with from 6 to 24 carbon atoms. 25 Particularly effective ratios of unsaturated acid, salt or precursor thereof to haloalkylnyl compound are 1:5 to 50:1, preferably 1:2 to 30:1, more preferably 1:1 to 25:1, more preferably 2:1 to 15:1, most preferably 2:1 to 10:1. 30 The ratio of unsaturated acid to haloalkylnyl will vary depending.upon the type of acid present in the composition. In general, it has been found that the amount of acid present should be greater than the amount of haloalkylnyl (in weight percent). However, some of 35 the naturally occurring cyclic acids such as rosin have relatively poor solubility. The compositions of the 14 invention typically comprise about 1-2 weight percent haloalkylnyl compound. If it is not possible to dissolve. an excess of unsaturated acid in the composition, then the unsaturated acid is typically 5 added to form a saturated or near saturated solution of the acid. All of the above ratios refer to weight percent as a percentage of the total weight of the composition. Thus, a ratio of 1:1 will refer to two components being 10 present in equal weight percents in a composition. Thus, especially preferred formulations according to the present invention comprise benzoic acid (or sodium benzoate), sorbic acid (or potassium sorbate), or rosin; a triazole compound; and IPBC; all as defined 15 above and preferably at the ratios specified above. The concentration of the -formulation required for preservative treatment depends on the ratio of particular active agents selected, the method of treatment employed, the timber species, the level of 20 protection required and the nature and quantity of any other biocides present. The amounts necessary can be determined readily by one skilled in the art. In concentrate form the wood treatment composition will typically comprise as active ingredients 0.1-10%, 25 preferably 0.2-5%, e.g. 0.2-2% w/w of azole, and 0.1-10%, preferably 0.2-5%, e.g. 0.5-3% w/w haloalkylnyl compound. Typically these concentrates will be diluted prior to application to the wood. Dilution will preferably be with water, e.g. at a ratio, 30 water:concentrate v/v of 15:1 to 250:1 e.g. 75:1 to 150:1. The appropriate dilution level can be determined by one skilled in the art dependent upon cost, the type of wood to be treated, environmental conditions and the length of time protection is required. 35 In a further aspect, the invention provides a method of preserving wood or other cellulosic substrates 15 which comprises applying to the wood or other cellulosic substrate a composition of the invention as described above or applying the individual components to the wood/substrate such that the wood/substrate effectively 5 receives a composition as described. Preferably, the invention provides a method of preventing sapstain formation on wood or other cellulosic material which comprises applying to the wood or other cellulosic substrate a composition of the invention as described 10 above or applying the individual components to the wood/substrate such that the wood/substrate effectively receives a composition as described. Thus, the invention also provides a method of maintaining the visual appearance of wood or other 15 substrates which comprises applying to the wood or other cellulosic substrate a composition of the invention as described above or applying the individual components to the wood/substrate such that the wood/substrate effectively receives a composition as described. The 20 Examples disclose methods of assessing visual appearance. Types of wood which can benefit from treatment with the formulations of the invention include -sawn timber, logs, glulam, plywood, laminated veneer lumber, wood 25 based composite products such as oriented strandboard, medium density fibreboard, fibreboard, hardboard and particle board. It will be understood that "wood" in the context of this invention does not encompass living trees or other 30 plants. Other materials which can benefit from treatment with the formulations of the invention are lignocellulosic substrates, wood plastic composites, cardboard and cardboard faced building products such as. 35 plasterboard, and cellulosic material such as cotton. Also, leather, textile materials and even synthetic 16 fibres, hessian, rope and cordage as well as composite wood materials. For convenience, the invention is described with reference to the treatment of wood but it will be appreciated that other materials may be treated 5 analogously. Preferably, though not exclusively, the formulations are applied to sawn timber, logs or laminated veneer lumber. Most preferably, the formulations are applied to unseasoned timber. Conveniently, the compositions of the present 10 invention are applied as a liquid composition. They may also be applied as a solid implant or paste. Preferably, the compositions are applied as a liquid composition, e.g. in the form of an emulsion made up of solubilised liquid droplets. These emulsions do not 15 contain any biocides in a solid, particulate form. Preferably, the emulsions are in the form of a micro emulsion- The person skilled in the art of making emulsions knows how to make an emulsion according to the invention by the use of suitable solvents and 20 emulsifying agents. Preferably, when applied in liquid form, this is in an aqueous solution, but one or more organic solvents or a mixture of water and an organic solvent could also be used. Suitable organic solvents include both aromatic 25 and aliphatic hydrocarbon solvents such as white spirit, petroleum distillate, kerosene, diesel oils and naphthas. Also, benzyl alcohol, 2-phenoxy ethanol, methyl carbitol, propylene carbonate, benzyl benzoate, ethyl lactate and 2-ethyl hexyl lactate. 30 The application of these compositions may be by one or more of dipping, deluging, spraying, brushing or other surface coating means or by impregnation methods, e.g. high pressure or double vacuum impregnation into the body of the wood or other material, all being 35 techniques well known to the man skilled in the art. Impregnation under pressure is particularly advantageous 17 when the substrate is wood or a wood composite material which is made to become wet during its life, fort example, wood for window frames, timber used above ground in exposed environments such as decking and 5 timber used in ground contact or fresh water br salt water environments. Substrates made of wood or cellulosic material which have been treated with a composition or by a method according to the invention as described herein, 10 comprise further aspects of the present invention. Additionally, substrates made of wood or other cellulosic material comprising a composition according to the invention comprise a further aspect of the present invention. 15 A further aspect of the present invention is the use of compositions of the present invention in the treatment or preservation of wood or other cellulosic substrates. Preferably, the invention provides the use of compositions of the present invention in the 20 prevention of sapstain, particularly in the prevention of sapstain on freshly felled timber. Preferably, the compositions are applied to timber. components before they are used but they can also be used remedially as a curative action in preventing 25 continued wood defacement. In yet a further aspect, the invention provides a method of making an antisapstain composition which comprises admixing a haloalkynyl compound, an azole, and an unsaturated carboxylic or sulphonic acid, salt or 30 precursor thereof. Preferred-embodiments discussed above in relation to other aspects of the invention apply mutatis mutandis and thus the above three components may be further combined with one or more of a quaternary ammonium compound, and amine oxide etc.

18 The invention will be further described with reference to the following non-limiting Examples and Figures in which: 5 Figure 1 is a drawing of the decking/cladding assembly used in Example 1. Figure 2 is a photograph of wood treated with formulation 11-2 after exposure for 25 weeks. 10 Figure 3 is a photograph of wood treated with formulation 11-14 after exposure for 25 weeks. Figure 4 is a photograph of wood treated with 15 formulation 11-19 -after exposure for 25 weeks. Figure 5 is a photograph of wood treated with formulation 11-24 after-exposure for 25 weeks. 20 Figure 6 is a photograph of wood treated with formulation 11-1 after exposure for 25 weeks. Figure 7 is a photograph of wood treated with formulation 11-16 after exposure- for 25 weeks. 25 Figure 8 is a photograph of wood treated with formulation 11-27 after exposure for 25 weeks. Figure 9 is a photograph of wood treated with 30 formulation 11-32 after exposure for 25 weeks. Figure 10 is a photograph of wood treated with formulation 11-33 after exposure for 25 weeks. 35 Figure 11 is a photograph of wood treated with formulation 11-34 after exposure for 25 weeks.

19 Figure 12 is a photograph of wood treated with formulation 11-35 after exposure for 25 weeks. 5 Figure 13 is a photograph of wood treated with formulation II-36 after exposure for 25 weeks.

20 Examples Example 1 5 A field trial was initiated in which a number of formulations were investigated for their ability to prolong the period which treated timber could be maintained in a stain and mould free condition. 10 The formulations were prepared by adding all of the water insoluble ingredients (e.g. azoles, IPBC, any insoluble acids etc.) to the solvent (Dowanol DPM®) and stirring until fully dissolved. The surfactant was then stirred in and water added. Any water soluble additives 15 (e.g. sodium benzoate) were added last. The formulations used in the test were as follows (including their dilution levels when applied to wood): 20 Formulation I-1 (Comparative) Dowanol DPM@ 5.01 Tebuoconazole (97%) 0.50 IPBC (98%) 0.50 Propiconazole (50%) 0.50 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) 4.99 Water 88.50 Diluted to 3.33% Formulation 1-2 (Comparative) 25 Dowanol DPM@ (Glycol Ether Solvent) 8.99 Tebuoconazole (97%) 1 Propiconazole (50%) 1.03 Dehscofix c0130F® (40M ethoxylate castor oil surfactant) 11-.34 Tetra-Sodium EDTA (45%) 1.5 21 Sodium Benzoate 22.5 Water 53.64 Diluted to 1.17% Formulation 1-3 (Comparative) Tebuoconazole (97%) 0.33 Propiconazole (50%) 0.33 Uradil AZ543@ (Water Soluble Alkyd Resin) 15 Carboquat@ (didecyldimethylammonium carbonate) 10 Sodium Benzoate 22.5 Water 51.84 5 Diluted to 1.33% Formulation 1-4 Dowanol DPM) (Glycol Ether Solvent) 8.99 Tebuoconazole (97%) 1 IPBC (98%) 1.2 Propiconazole (50%) 1.04 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) 11.24 Tetra-Sodium EDTA (45%) 1.5 Sodium Benzoate 22.5 Water 52.53 Diluted to- 1.02% 10 Formulation 1-5 Dowanol DPM@ (Glycol Ether Solvent) 8.99 Tebuoconazole (97%) 0.75 IPBC (98%) 1.2 Triadamedon (97%) 0.75 Dehscofix C0130F® (40M ethoxylate castor oil surfactant) 11.24 Tetra-Sodium EDTA (45%) 1.5 Sodium Benzoate 22.5 Water 53.07 Diluted to 1.17% 22 Formulation 1-6 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 4.99 Tebuoconazole (97%) . 0.51 Propiconazole (50%) 0.51 Dehscofix C0130F® (40M ethoxylate castor oil surfactant) 5.00 Rosin Acid Emulsion (50% Rosin Acid) 2.52 Water 86.48 Diluted to 3.33% 5 Formulation 1-7 Dowanol DPM@ (GlycolrEther Solvent) 5.00 Tebuoconazole (97%) 0.51 IPBC (98%) 0.51 Propiconazole (50%) 0.51 Dehscofix CO130F (40M ethoxylate castor oil surfactant) 4.99 Rosin Acid Emulsion (50% Rosin Acid) 2.52 Water 85.96 Diluted to 3.33% 10 Formulation 1-8 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 8.99 Tebuconazole (97%) 1 IPBC (98%) 1.2 Propiconazole (50%) 1.04 Dehscofix C0130F@ (4CM ethoxylate castor oil surfactant) 11.24 Tetra-Sodium EDTA (45%) 1.5 Sodium Nitrite 18.5 Water 56.53 Diluted to 1.17% 15 23 Formulation 1-9 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 5.00 Tebuoconazole (97%) 0.35 IPBC (98%) 0.39 Propiconazole (50%) 0.66 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) 5.05 Styrene-Acrylic Resin 9.99 Water 78.56 Diltued to 3.33% 5 Formulation 1-10 (Comparative) Dowanol DPM@. (Glycol Ether Solvent) 4.98 Tebuoconazole (97%) 0.35 IPBC (98%) 0.39 Propiconazole (50%) 0.66 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) 4.98 Iron Oxide Pigment 0.50 Water 88.15 Diluted to 3.33% Formulation I-i (Comparative) 10 Dowanol DPM@ (Glycol Ether Solvent) 4.98 Tebuoconazole (97%) 0.35 IPBC (98%) 0.39 Propiconazole 150%) 0.6 Uradil AZ543@ .(Water Soluble Alkyd Resin) 4.98 Anilazine 0.35 Water 88.15 Diluted to 3.33% 15 24 Formulation 1-12 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 4.97 Tebuoconazole (97%) 0.50 IPBC (98%) 0.51 Propiconazole (50%) 0.51 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) . 4.96 HAL* (4-Hydroxy-2,2,6,6-tetramethylpiperidinoxyl) 0.29 Water 88.27 Diluted to 3.33% * HAL =. Hindered amine light scavenger 5 Formulation 1-13 (Comparative) Dowanol DPM® (Glycol Ether Solvent) 4.98 Tebuoconazole (97%) 0.35 IPBC (98%) 0.39 Propiconazole (50%) 0.66 Uradil AZ543® (Water Soluble Alkyd Resin) 4.98 Titanium Dioxide Pigment 0.50 Water 88.15 Diluted to 3.33% 10 Formulation 1-14 (Comparative) Dowanol DPM® (Glycol Ether Solvent) 4.61 Tebuoconazole (97%) 0.47 IPBC (98%) 0-47 Propiconazole (50%) 0.48 Dehscofix C0130OF (40M ethoxylate castor oil surfactant) 4.61 Vantocil IB® (20% PHMB) 11.08 Water 78.27 Diluted to 3.33% 15 25 Formulation 1-15 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 4.95 Tebuoconazole (97%) 0.50 IPBC (98%) 0.50 Barlene 12C (amine) 2.39 Propionic Acid 1.48 Propiconazole (50%) 0.50 Dehscofix C0130F@ (40M ethoxylate castor oil surfactant) 4.95 Water 84.72 Diluted to 3.33% 5 Formulation 1-16 (Comparative) Dowanol DPM@ (Glycol Ether Solvent) 5.00 Tebuoconazole (97%) 0.35 Propiconazole (50%) 0.66 Uradil AZ543@ (Water Soluble Alkyd Resin) 5.00 Ethoduomeen T13® 1.34 Water 87.65 Diluted to 3.33% The test formulations were evaluated using small pine 10 blocks and pine decking/cladding structures. The small block test substrates consisted of planed timber blocks of dimension 135 x 70 x 25mm which were machined from Scots Pine (pinus sylvestris). The upper 15 face of each block consisted entirely of sapwood. Five duplicate blocks were treated with each of the formulations. The blocks were treated using vacuum-pressure 20 impregnation with initial wet vacuum of 650mm Hg vacuum applied for a period of 30 minutes followed by a pressure cycle of 12kg/cm also for 30 minutes. After 26 treatment the blocks were allowed to dry slowly on the bench for one week prior to exposure. For exposure the blocks were mounted horizontally on 5 untreated pine racks at ground level on a gravel surface for natural weathering exposure. The decking/cladding structure for natural weathering exposure were also machined from Scots Pine. The 10 dimensions of each of the section types used in construction of each structure are shown in Table 1 below. For each treatment solution, 6 deck sections, 4 cladding sections, 3 joists, and 2 batons were treated. The end of each section was then sealed with a 15 nitrocellulose lacquer to reduce the risk of solution penetration occurring only through the end grain rather than laterally. This ensured that large pieces of timber received the same level of formulation across their entire length. The structures were assembled as 20 per Figure 1. Width Depth Length Pine mm mm mm Decking 120 30 730 Cladding 125 15 730 Joists 100 50 530 Batons 50 35 700 Table 1: Timber section dimensions for pine decking/cladding structure 25 The treated timber were then exposed above ground in an in-service situation defined as Hazard Class 3 (uncoated) by EN355. The samples were periodically inspected to determine if stain and/or mould had begun 30 to grow. The stain and mould free period of each of the 2.7 formulations (i.e. the number of months that the sample was graded 0 according to the EN152:1988 standard) is summarised in Table 2. Form. Fungicides do-additive Stain and mould free period I-I* IPBC/Teb/Prop 2 months I-2* Teb/Prop Na Benzoate 2 months I-3* DDAC/Teb/Prop Na Benzoate 1 month 1-4 IPBC/Teb/Prop Na Benzoate 9 months 1-5 IPBC/Teb/Tria Na Benzoate 9 months I-6* Teb/Prop Rosin 2 months 1-7 IPBC/Teb/Prop Rosin 7 months I-8* IPBC/Teb/Prop Na Nitrite 1 month I-9* IPBC/Teb/Prop Styrene .1 month I-10* IPBC/Teb/Prop Iron Oxide 3 months 1-11* IPBC/Teb/Prop UV Absorber 3 months I12* IPBC/Teb/Prop UV Absorber 3 months I-13* IPBC/Teb/Prop TiO, 3 months I-14* IPEC/Teb/Prop Anti Microb. 3 months I-15* IPBC/Teb/Prop Anti Microb. 3 months I-16* IPBC/Teb/Prop Diamine 2 months 5 Table 2: Stain and mould free period of timber treated with formulations I-1 to 1-16 (* denotes comparative example). 10 The data for formulations I-1 to 1-5 show that timber treated with a combination of IPBC/azole/benzoate has a stain and mould free period 7 months longer than timber treated with the combination of IPBC/azole or azole/benzoate alone. Furthermore, the improved 15 resistance is not present in formulation 1-3, which contains DDACarbonate (a known fungicide and adjuvant) in place of IPBC. The levels of each of the active fungicides present in each of the compositions is the same. Therefore, synergy is present in the combination 20 of IPBC/azole/benzoate. The data for formulations 1-6 and 1-7 show that timber treated with a combination of IPBC/azole/rosin has a stain and mould free period 5 months longer than timber 28 treated with azole/rosin alone.. Therefore, synergy is present in the IPBC/azole/rosin combination. Sodium benzoate is a known corrosion inhibitor. 5 However, formulation 1-8 contains sodium nitrite which is also known to have corrosion inhibiting properties. The timber treated with formulation I-8 showed poor resistance to stain and mould. 10 Including co-additives in the formulation to help prevent IPBC degradation does not significantly increase the stain and mould free period. For example, the presence of water repellent additives (formulation 1-9), UV absorbers or metal oxide particles which either 15 absorb or scatter light to prevent photodegredation (formulations I-10 to 1-13), or antimicrobials (formulations 1-14 and 1-15) in the compositions used to treat the timber did not prolong the stain and mould free period. The inclusion of adjuvants such as amine 20 proprionate or Ethoduomeen T13@ (an ethoxylated diamine) (formulations 1-15 and 1-16), which could be expected to facilitate azole/IPBC penetration, also does not prolong the stain and mould free period. 25 Example 2 L A trial was conducted in which a number of formulations were investigated for their ability to prevent blue stain growth. 30 The formulations were prepared by adding all of the water insoluble ingredients.(e.g. azoles, IPBC, any insoluble acids etc.) to the solvent (Dowanol DPM®) and stirring until fully dissolved. The surfactant was then 35 stirred in and water added. Any water soluble additives (e.g. sodium benzoate) were added last.

29 The formulations tested were as follows (with the ingredients listed as weight percent): 5 Formulation 11-1 (Comparative) IPBC (-98%) 1.11 Surfactant - 11.25 Dowanol DPM@ 8.8 Water 78.84 Formulation 11-2 (Comparative) 10 IPBC (98%) 1.11 -Surfadtant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 56.34 Formulation 11-3 (Comparative) IPBC (98%) 1.11 Surfactant 30.05 Dowanol DPM@ 16.6 Abietic Acid 3.76 Water 48.48 15 Formulation 11-4 (Comparative) Tebuconazole (95%) 1.5 Surfactant 11.25 Dowanol DPM® 8.8 Water 78.45 30 Formulation 11-5 (Comparative) Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Water 76.95 Formulation 11-6 (Comparative) 5 Triadimefon (95%) 1.5 Surfactant 11.25 Dowanol DPM® 8.8 Water 78. 45 Formulation II-7 (Comparative) Imazalil (97.5%) 1.5 Surfactant 11.25 Dowanol DPM@ 8.8 Water 78.45 10 Formulation 11-8 (Comparative) Tebuconazole (95%) 1 Propiconazole (50%) 1 Surfactant 11.25 Dowanol DPM® 8.8 Water 77.95 Formulation 11-9 (Comparative) Tebuconazole (95%) 0.75 Triadimefon (95%) 0.75 Surfactant 11.25 Dowanol DPM® 8.8 Water 78.45 31 Formulation 11-10 (Comparative) Tebuconazole (95%) 1.5 Surfactant 11.25 Dowanol DPM@ 8.8 Sodium Benzoate 22.5 Water 55.95 5 Formulation 11-11 (Comparative) Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 54.45 Formulation 11-12 (Comparative) Triadimefon (95%) 1.5 Surfactant 11.25 Dowanol DPM@® 8.8 Sodium Benzoate 22.5 Water 55.95 10 Formulation II-13 (Comparative) Imazalil (97.5%) 1.5 Surfactant 11.25 Dowanol DPM@ 8.8 Sodium Benzoate 22.5 Water 55.95 15 32 Formulation 11-14 (Comparative) Tebuconazole (95%) 1 Propiconazole (50%) 1 Surfactant 11.25 Dowanol DPM® 8.8 Sodium ~ Benzoate 22.5 Water 55.45 Formulation I1-15 (Comparative) 5 Tebuconazole (95%) 0.75 Triadimefon (95%) 0.75 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 55-.95 Formulation 11-16 (Comparative) IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Water 75.84 10 Formulation 11-17 (Comparative) IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Water 75.84 33 Formulation 11-18 (Comparative) IPBC (98%) 1.11 Imazalil (97.5%) 1.5 Surfactant 11.25 Dowanol DPM® 8.8 Water 77.34 Formulation 11-19 (Comparative) 5 IPBC (98%) 1.11 Tebuconazole (95%) 1 Propiconazole (50%) 1 Surfactant 11.25 Dowanol DPM@ 8.8 Water 76.84 Formulation 11-20 (Comparative) IPBC (98%) 1.11 Tebuconazole (95%) 0.75 Triadimefon (95%) 0.75 Surfactant 11.25 Dowanol DPM@ 8.8 Water 77.34 10 Formulation 11-21 IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 53.34 34 Formulation 11-22 IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 53.34 Formulation 11-23 5 IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 53.34 Formulation 11-24 IPBC (98%) 1.11 Propiconazole (50%) 3 Surfactant 11.25 Dowanol DPM® 8.8 Sodium Benzoate 22.5 Water 53.34 10 Formulation 11-25 IPBC (98%) 1.11 Tebuconzole (95%) 0.75 Triadimefon (95%) 0.75 Surfactant .11.25 Dowanol DPM@ 8.8 Sodium Benzoate 22.5 Water 54.84 35 Formulation 11-26 IPBC (98%) 1.11 Tebuconzole (95%) 1.5 Surfactant 30.05 Dowanol DPM@ 16.6 Abietic Acid 3.76 Water 46.98 5 Formulation 1-27 IPBC (98%) 1.11 Propiconazole- (50%) 3 Surfactant 30.05 Dowanol DPM@ 16.6 Abietic Acid 3.76 Water 45.48 Formulation 11-28 IPBC (98%) 1.11. Triadimefon (95%) 1.5 Surfactant 30.05 Dowanol DPM® 16.6 Abietic Acid 3.76 Water - 46.98 10 Formulation 11-29 (Comparative) Tebuconzole (95%) 1.5 Surfactant 30.05 Dowanol DPM® 16.6 Abietic Acid 3.76 Water 48.09 36 Formulation 11-30 (Comparative) Propiconazole (50%) 3 Surfactant 30.05 Dowanol DPM@ 16.6 Abietic Acid 3.76 -Water 46.59 Formulation 11-31 (Comparative) 5 Triadimefon (95%) 1.5 Surfactant 30.05 Dowanol DPM@ 16.6 Abietic Acid 3.76 Water 48.09 Formulation 11-32 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 30.05 Dowanol DPM® 16.6 Sodium Salicylate 3.76 Water 46.48 10 Formulation I1-33 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 11.25 Dowanol DPM® - 8.8 Potassium Sorbate 22.5 Water 54.34 37 Formulation 11-34 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 11.25 Dowanol DPM@ 8.8 Rosin Acid Emulsion (50%) 7.57 Water 69.27 5 Formulation 11-35 IPBC (98%) 1.11. Tebuconzole (95%) 1 Propiconazole (50%) Surfactant 28.02 Dowanol DPM@ 46.1 Sorbic Acid 3.76 Water 19.01 Formulation 11-36 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 28.02 Dowanol DPM@ 46.1 Oleic Acid 3.76 Water 19.01 10 The test formulations (diluted to 0.83% with water) were evaluated using small pine blocks, using identical substrate types and conditions to those described in Example 1. 15 38 The treated samples were assigned a grade according to the level of blue stain determined (Table 3). The grading system is in accordance with EN152:1988 parts 1 and 2, which is the standard concerning a laboratory 5 method for determination of the protective effectiveness of a wood preservative treatment against blue stain in wood in service.

39 Grade Blue Stain Level 0 Not blue stained: no blue stain can be detected visually on the surface. I Insignificantly blue stained. The surface exhibits only individual small blue stained spots with a largest diameter of 2mm. 2 Blue stained: the surface is continuously blue stained up to a maximum of one third of the surface area, or blue stained partially or in streaks up to half the total area. 3 Strongly blue stained. More than half the surface area is continuously stained or more than half the surface area is partially blue stained. Table 3: Blue Stain Assessment Grades. 5 The blue stain grading for each of the formulations is shown in Table 4.

40 Ingredient Ingredient Grade at Form 1 2 Ingredient 3 25 Weeks Untreated* 3 II-1* IPBC 3 II-2* IPBC Na Benzoate 2 II-3* IPBC . -Abietic Acid 2 II-4* Tebuconazole 3 II-5* Propiconazole 3 II-6* Triadimefon 3 II-7* Imazalil 3 II-8* Teb/Prop 3 II-9* Teb/Tria 3 II-lo* Tebuconazole Na Benzoate 3 II-11* Propiconazole Na Benzoate 3 II-12* Triadimefon Na Benzoate 3 II-13* Imazalil Na Benzoate 3 II-14* Teb/Prop Na Benzoate 2 II-15*. Teb/Tria Na Benzoate 3 II-16* IPBC Propiconazole 3 1I-17* IPBC Triadimefon 3 II-18* IPBC Imazalil 3 II 19* IPBC Teb/Prop 3 1I-20* IPBC Teb/Tria 3 11-21 IPBC Propiconazole Na Benzoate 1 11-22 IPBC Triadimefon Na Benzoate 1 11-23 IPBC Imazalil Na Benzoate 1 11-24 IPBC Teb/Prop Na Benzoate 1 11-25 IPBC Teb/Tria Na Benzoate 1 11-26 IPBC Tebuconazole. Abietic Acid 2 11-27 IPBC Propiconazole Abietic Acid 2 11-28 IPBC Triadimefon Abietic Acid 2 II-29* Tebuconazole Abietic Acid 3 II-30* Propiconazole Abietic Acid 3 II-31* Triadimefon Abietic Acid 3 11-32 IPBC Teb/Prop Na salicylate 2 11-33 IPBC Teb/Prop K Sorbate 0 11-34 IPBC Teb/Prop Rosin Acid 0 11-35 IPBC Teb/Prop Sorbic acid 2 11-36 IPBC Teb/Prop Oleic acid 2 Table 4: Blue stain gradings (EN152:1998) of timber treated with formulations II-1 to 11-36 (* denotes 5 comparative example).

41 Commercially acceptable blue stain levels are considered to.be grades 0 and 1 only. The data in Table 4 demonstrate that the majority of, the formulations according to the invention meet the commercially 5 acceptable standards. Of the formulations according to the invention that did not achieve grade 0 or 1, the addition of the unsaturated acid was nevertheless found to be an improvement over the composition absent the acid (see formulations 11-26 to 11-28 as compared to 10 formulations 11-29 to 11-31; and formulations 11-32, II 35 and 11-36 as compared to formulation 11-19). It is notable that the grading scheme is not entirely satisfactory, given the lack of an intermediate level 15 between grade 1 (insignificant stain) and grade 2 (stain partially or in streaks up to half the total area); This may explain why a number of the formulations according to the invention fail to meet current commercial standards, despite the fact that the timber 20 boards treated with these compositions show a marked improvement over the relevant control boards. To aid comparison of the different formulations, photographs of the test samples were taken after 25 25 weeks' exposure under diffuse daylight (i.e. overcast conditions) using a Fuji FinePix S5700 digital camera. White balance was set to overcast. Automatic exposure was used giving a typical.aperture of f/4.0 and 1/160 second exposure. The samples were photographed from a 30 distance of around 60cm with the camera held perpendicular to the plane of the block surface. The photographs obtained were then visually compared to reference samples treated with the equivalent IPBC/Azole 35 formulation absent the additive. These visual comparisons were done by systematically comparing side- 42 by-side colour photographs (displayed on a computer screen) of the exposed wood substrates, and rating the aesthetic quality of the substrates treated with the formulation according to the invention compared its 5 respective control substrate absent the unsaturated acid. A rating of very high indicates that no noticeable discolouration of the substrate is observable, while high indicates that only minor staining is present. A rating of moderate indicates 10 that although staining is present, the composition represents a noticeable improvement over the control sample. Table 5 summarises the results from these visual comparisons. Formulation Unsaturated acid Anti-Stain Performance Effectiveness 11-24 Na Benzoate Very high II-27* Abietic acid Moderate 11-32 Na Salicyclate High 11-33 K Sorbate Very high 11-34 Rosin Very high 11-35 Sorbic acid High 11-36 Oleic acid High 15 Table 5: Results from visual comparison of unsaturated acid containing formulations versus formulation 11-19 containing only IPBC/tebuconazole/propiconazole (* denotes the comparison is made with respect to 20 formulation I-16) Figures 2 to 5 show pictures taken after exposure for 25 weeks of the substrates treated with formulations 11-2, 11-14, 11-19 and 11-24 respectively. A comparison of 25 these photographs clearly shows that the combination of IPBC, tebuconazole/propiconazole and sodium benzoate shows a marked improvement over formulations that are absent one of these three ingredients. Figure 6 shows the substrates treated with formulation II-I (IPBC) 43 after 25 weeks' exposure. Notably, a comparison of Figures 2 and 6 shows that sodium benzoate appears to improve the efficacy of IPBC even when an azole is not present, demonstrating that the unsaturated acid serves 5 to stabilise IPBC improving its long term efficacy. The data in Table 5 indicate that all of the formulations according to the invention except that containing abietic acid can be rated as high or very 10 high anti-stain performance, indicating that the addition of the unsaturated acid greatly increases the resistance to blue stain growth. However, Figures 7 and 8 clearly show that even though it was only rated as moderate, abietic acid clearly improves the efficacy of 15 a mixture containing IPBC/tebuconazole. The pictures of the substrates from the remaining formulations given in Table 5 are shown in Figures 9 to 13. As can be seen, the wood treated with formulations 20 11-32, 11-33, 11-34, 11-35, and 11-36 all show lower blue stain levels than the control formulation 11-19, shown in Figure 4. In particular, the substrates treated with Formulations 11-33 and 11-34 show virtually no blue stain, indicating that potassium sorbate and 25 rosin are particularly effective unsaturated acids in the formulations of the present invention. Example 3 30 The following formulations within the scope of the invention are also described: Formulation 1II-1 IPBC (98%) 1.11 Tebuconazole (95%) 1.5 44 Surfactant 11.25 Solvent 8.8 Sodium Benzoate 22.5 Water 54.84 Formulation 111-2 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 30.05 Solvent 16.6 Linoleic Acid 3.76 Water 46.48 5 Formulation 111-3 IPBC (98%) 1.11 Tebuconzole (95%) 1 Propiconazole (50%) 1 Surfactant 28.02 Solvent 46.1 Fumaric Acid 3.76 Water 19.01 Formulation 111-4 10

C

12 dimethylamine (100% a.i.) 10.0% w/w

C

2 amine dipropionate (35% a.i) 20 IPBC (98% a.i.) 2.1 Propiconazole (50% a.i.) 0.8 15 Dowanol DPM® 12 Propionic acid 3.4 40 mole ethoxylated castor oil 10 Sodium benzoate 5 45 Defoamer 0.2 Water to 100 Formulation 111-5 5

C

1 amine dipropionate (35% a. i.) 20% w/w

C

1 dimethylamine (100% a.i.) 10 IPBC (98% a-i.) 2.1 Propiconazole (50% a.i.) 0.8 10 Dowanol DPM 12 Propionic acid 3.4 40 mole ethoxylated castor oil 10

C

1 amine oxide (30% a.i) 3.0 Sodium benzoate 5 15 Defoamer 0.2 Water to 100

Claims (18)

1. A wood preservative composition for inhibiting discoloration due to mold, sapstain or fungi, the 5 composition comprising: a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate,

3-iodo-2-propynyl butyl carbamate, 3-iodo-2 propynyl hexyl carbamate, 3-iodo-2-propynyl 10 cyclohexyl carbamate, 3-iodo-2-propynyl phenyl carbamate, and mixtures thereof, a 1,2,4-triazole compound; and an unsaturated carboxylic acid, or a salt thereof, wherein the unsaturated carboxylic acid 15 has at least 4 carbon atoms, and the ratio of the unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight basis ranges from 1:1 to 25:1. 20 2. A composition according to claim 1, wherein the halopropynyl compound is 3-iodo-2-propynyl butyl carbamate (IPBC). 3. A composition according to claim 1, wherein the 25 unsaturated carboxylic acid, or salt thereof, is an unsaturated cyclic carboxylic acid, or salt thereof.

4. A composition according to claim 3, wherein the 30 unsaturated carboxylic acid, or salt thereof, is an aromatic acid, or salt thereof. 47

5. A composition according to claim 4, wherein the aromatic acid is of formula (IV): Y (IV) 5 wherein Y denotes CO 2 M; each R independently denotes Ci-C 4 alkyl, OH, OMe, OEt, NH 2 , NMe 2 , CO 2 M or halogen, wherein two R groups may optionally form 10 naphthyl; M denotes H, K or Na; and m denotes 0 to 5.

6. A composition according to claim 5, wherein the 15 aromatic acid, or salt thereof, is selected from the group consisting of benzoic acid and sodium benzoate.

7. A composition according to claim 3, wherein the 20 cyclic carboxylic acid is a resin acid, or salt thereof.

8. A composition according to claim 7, wherein the resin acid, or salt thereof, is selected from the 25 group consisting of abietic acid, sodium abietate, pimaric acid and sodium pimarate.

9. A composition according to claim 1, wherein the 48 unsaturated carboxylic acid, or salt thereof, is a linear unsaturated acid, or salt thereof.

10.A composition according to claim 1, wherein the 5 unsaturated acid, or salt thereof, is selected from the group consisting of sorbic acid, sodium sorbate, potassium sorbate, myristoleic acid, palmitoleic acid, oleic acid, elaidic acid, linoleic acid, ulinolenic acid, arachidonic acid, 10 eicosapentaenoic acid, euric acid, docosahexanoic acid, fumaric acid, maleic acid, maleic anhydride, and mixtures thereof.

11.A composition according to claim 10, wherein the 15 unsaturated acid, or salt thereof, is selected from the group consisting of sorbic acid, sodium sorbate and potassium sorbate.

12.A composition according to claim 1, wherein the 20 1,2,4-triazole compound is a compound selected from the group consisting of formula (VI): OH R"-C -C RS CH, N (VI) 25 wherein R 5 represents a branched or straight chain C 1 - 5 alkyl group and R represents a phenyl 49 group optionally substituted by one or more substituents selected from halogen, C 1 - 3 alkyl, C 1 - 3 alkoxy, phenyl or nitro; formula (VII): 5 CH2 N N (VII) wherein R7 is as defined for R above and R represents a hydrogen atom or a branched or 10 straight chain C 1 - 5 alkyl group; and mixtures thereof.

13.A composition according to claim 12, wherein the 1,2,4-triazole is selected from the group 15 consisting of triadimefon, triadimenol, triazbutil, propiconazole, cyproconazole, difenoconazole, fluquinconazole, tebuconazole, flusilazole, uniconazole, diniconazole, bitertanol, hexaconazole, azaconazole, flutriafol, 20 epoxyconazole, tetraconazole, penconazole and mixtures thereof.

14.A composition according to claim 12, wherein the 1,2,4-triazole is selected from the group 25 consisting of propiconazole, azaconazole, hexaconazole, tebuconazole, cyproconazole, 50 triadimefon and mixtures thereof.

15.A composition according to claim 1, wherein the formulation is in a liquid form. 5

16.A composition according to claim 15, wherein the formulation is an emulsion.

17.A method of protecting a substrate formed of wood 10 or cellulosic material which comprises: applying to the wood or cellulosic substrate a wood preservative composition in an amount to inhibit discoloration due to mold, sapstain or fungi, the wood preservative including 15 a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate, 3-iodo-2-propynyl butyl carbamate, 3-iodo-2 propynyl hexyl carbamate, 3-iodo-2-propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl 20 carbamate, and mixtures thereof, a 1,2,4-triazole compound; and an unsaturated carboxylic acid, or a salt thereof, wherein the unsaturated carboxylic acid has at least 4 carbon atoms, and the ratio of the 25 unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight basis ranges from 1:1 to 25:1, or applying the individual components of the wood preservative composition to the wood or cellulosic 30 substrate such that the wood or cellulosic substrate effectively receives the wood preservative in an amount to inhibit discoloration 51 due to mold, sapstain or fungi.

18.A substrate made of wood or cellulosic material treated with an amount of wood preservative to 5 inhibit discoloration due to mold, sapstain or fungi, the wood preservative comprising: a haloalkynyl compound selected from the group consisting of 3-iodo-2-propynyl propyl carbamate, 3-iodo-2-propynyl butyl carbamate, 3-iodo-2 10 propynyl hexyl carbamate, 3-iodo-2-propynyl cyclohexyl carbamate, 3-iodo-2-propynyl phenyl carbamate, and mixtures thereof, a 1,2,4-triazole compound; and an unsaturated carboxylic acid, or a salt 15 thereof, wherein the unsaturated carboxylic acid has at least 4 carbon atoms, and the ratio of the unsaturated carboxylic acid, or salt thereof, to the haloalkynyl compound on a weight to weight basis ranges from 1:1 to 25:1. 20

19.A wood preservative composition according to claim 1, wherein the haloalkynyl compound is present in an amount from 0.1 to 10 percent by weight. 25 20.A wood preservative composition according to claim 1, wherein the 1,2,4-triazole compound is present in an amount from 0.1 to 10 percent by weight. 30 Dated this 1 3 th day of February 2015 Shelston IP Attorneys for: Arch Timber Protection Limited