AU2014200219A1 - In-line method of making heat-treated and annealed aluminum alloy sheet - Google Patents
In-line method of making heat-treated and annealed aluminum alloy sheet Download PDFInfo
- Publication number
- AU2014200219A1 AU2014200219A1 AU2014200219A AU2014200219A AU2014200219A1 AU 2014200219 A1 AU2014200219 A1 AU 2014200219A1 AU 2014200219 A AU2014200219 A AU 2014200219A AU 2014200219 A AU2014200219 A AU 2014200219A AU 2014200219 A1 AU2014200219 A1 AU 2014200219A1
- Authority
- AU
- Australia
- Prior art keywords
- sheet
- aluminum alloy
- feedstock
- temper
- line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Abstract A method of making aluminum alloy sheet in a continuous in-line process is provided. A continuously-cast aluminum alloy strip is optionally quenched, hot or warm rolled, annealed or heat-treated in-line, optionally quenched, and preferably coiled, with additional hot, warm or cold rolling steps as needed to reach the desired gauge. The process can be used to make aluminum alloy sheet of T or 0 temper having the desired properties, in a much shorter processing time. U-)) U-) cn0
Description
IN-LINE METHOD OF MAKING HEAT-TREATED AND ANNEALED ALUMINUM ALLOY SHEET 5 FIELD OF THE INVENTION The present invention relates to a method of making aluminum alloy sheet in a continuous in-line process. More specifically, a continuous process is used to make aluminum alloy sheet of T or 0 temper having the desired properties, with the minimum number of steps and shortest possible processing time. 10 BACKGROUND INFORMATION Conventional methods of manufacturing of aluminum alloy sheet for use in commercial applications such as auto panels, reinforcements, beverage containers and aerospace applications employ batch processes which include an 15 extensive sequence of separate steps. Typically, a large ingot is cast to a thickness of up to about 30 inches and cooled to ambient temperature, and then stored for later use. When an ingot is needed for further processing, it is first "scalped" to remove surface defects. Once the surface defects have been removed, the ingot is preheated to a temperature of about 1040*F for a period of 20 to 30 hours, to ensure that the 20 components of the alloy are properly distributed throughout the metallurgical structure. It is then cooled to a lower temperature for hot rolling. Several passes are applied to reduce the thickness of the ingot to the required range for cold rolling. An intermediate anneal or a self-anneal is typically carried out on the coil. The resulting "hot band" is then cold-rolled to the desired gauge and coiled. For non - heat-treated 25 products, the coil is further annealed in a batch step to obtain 0-temper. To produce heat-treated products, the coiled sheet is subjected to a separate heat treatment operation, typically in a continuous heat-treat line. This involves unwinding the coil, solution heat treatment at a high temperature, quenching and recoiling. The above process, from start to finish, can take several weeks for preparing the coil for sale, 30 resulting in large inventories of work in progress and final product, in addition to scrap losses at each stage of the process.
Because of the lengthy processing time in this flow path, numerous attempts have been made to shorten it by elimination of certain steps, while maintaining the desired properties in the finished product. For example, U.S. Patent No. 5,655,593 describes a method of making 5 aluminum alloy sheet where a thin strip is cast (in place of a thick ingot) which is rapidly rolled and continuously cooled for a period of less than 30 seconds to a temperature of less than 350'F. U.S. Patent No. 5,772,802 describes a method in which the aluminum alloy cast strip is quenched, rolled, annealed at temperatures between 6000 and 1200F for less than 120 seconds, followed by quenching, rolling 10 and aging. U.S. Patent No. 5,356,495 describes a process in which the cast strip is hot-rolled, hot-coiled and held at a hot-rolled temperature for 2-120 minutes, followed by uncoiling, quenching and cold rolling at less than 300'F, followed by recoiling the sheet. 15 None of the above methods disclose or suggest the sequence of steps of the present invention. There continues to be a need to provide a continuous in-line method of making heat-treated (T temper) and annealed (0 temper) sheet having the desired properties in a shorter period of time, with less or no inventory and less scrap losses. 20 SUMMARY OF THE INVENTION The present invention solves the above need by providing a method of manufacturing aluminum alloy sheet in a continuous in-line sequence comprising (i) providing a continuously-cast aluminum alloy strip as feedstock; (ii) optionally 25 quenching the feedstock to the preferred hot rolling temperature; (iii) hot or warm rolling the quenched feedstock to the required thickness, (iv) annealing or solution heat-treating the feedstock in-line, depending on alloy and temper desired; and (v) optionally, quenching the feedstock. Preferably, additional steps include tension leveling and coiling. 30 This method allows the elimination of many steps and much processing time, and yet still results in an aluminum alloy sheet having all of the desired properties. Both heat-treated and 0 temper products are made in the same production line which takes about 30 seconds to convert molten metal to finished coil. It is an object of the present invention, therefore, to provide a continuous in-line method of making aluminum alloy sheet having properties similar to or exceeding those provided with conventional methods. 5 It is an additional object of the present invention to provide a continuous in-line method of making aluminum alloy sheet more quickly so as to minimize waste and processing time. It is a further object of the present invention to provide a continuous in-line method of making aluminum alloy sheet, in a more efficient and economical 10 process. These and other objects of the present invention will become more readily apparent from the following figures, detailed description and appended claims. BRIEF DESCRIPTION OF THE DRAWINGS 15 The invention is further illustrated by the following drawings in which: Figure 1 is a flow chart of the steps of the method of the present invention, in one embodiment; Figure 2 is a schematic diagram of one embodiment of the apparatus used in carrying out the method of the present invention. 20 Figure 3 is an additional embodiment of the apparatus used in carrying out the method of the present invention. This line is equipped with four rolling mills to reach a finer finished gauge. Figure 4a is a graph demonstrating the equi-biaxial stretching performance of 6022-T43 sheet (0.035 inch gauge) made in-line compared with sheet 25 made from DC ingot and heat-treated off-line. Figure 4b is a graph demonstrating the equi-biaxial stretching performance of 6022-T4 Alloy made in-line compared with sheet made from DC ingot and heat-treated off-line. Figure 5 is a picture of Sample 804908 (Alloy 6022 in T43 temper) 30 after e-coating. Figure 6a is a picture demonstrating the grain size of Alloy 6022 rolled in-line to 0.035 inch gauge without pre-quench.
Figure 6b is a picture demonstrating the grain size of Alloy 6022 rolled in-line to 0.035 inch gauge with pre-quench. Figure 7a depicts an as-cast structure in Alloy 6022 transverse section. Figures 7b and 7c consist of two micrographs demonstrating the surface and 5 shell structure of Alloy 6022, respectively, in as-cast condition in transverse section. Figures 7d and 7e are micrographs of the center zone structure of Alloy 6022 in as-cast condition in transverse section. Figures 7f and 7g are micrographs demonstrating occasional small pores and constituents (mainly AlFeSi and some Mg2,Si particles) in the center zone of Alloy 6022 cast 10 structure in transverse section. Figure 8 depicts the as-cast microstructure of A1 + 3.5% Mg alloy in transverse direction. Figure 9 graphically depicts equi-biaxial tension tests results for AX-07 alloys at 0.041 inch gauge (Mg=1.4%) and conventional alloy 5754 (3.5% Mg). 15 DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The present invention provides a method of manufacturing aluminum alloy sheet in a continuous in-line sequence comprising: (i) providing a continuously-cast thin aluminum alloy strip as feedstock; (ii) optionally, quenching the feedstock to the preferred hot or warm rolling 20 temperature; (iii) hot or warm rolling the quenched feedstock to the desired final thickness; (iv) annealing or solution heat-treating the feedstock in-line, depending on alloy and temper desired; and (v) optionally, quenching the feedstock, after which it is preferably tension-leveled and coiled. This method results in an aluminum alloy sheet having the desired dimensions and properties. In a preferred embodiment, the aluminum alloy sheet is coiled for later use. This 25 sequence of steps is reflected in the flow diagram of Figure 1, which shows a continuously-cast aluminum alloy strip feedstock 1 which is optionally passed through shear and trim stations 2, optionally quenched for temperature adjustment 4, hot-rolled 6, and optionally trimmed 8. The feedstock is then either annealed 16 followed by suitable quenching 18 and optional coiling 20 to produce 0 temper products 22, or solution heat treated 10, followed by suitable quenching 12 30 and optional coiling 14 to produce T temper products 24. As can be seen in Figure 1, the temperature of the heating step and the subsequent quenching step will vary depending on the desired temper. 4 As used herein, the term "anneal" refers to a heating process that causes recrystallization of the metal to occur, producing uniform formability and assisting in earing control. Typical temperatures used in annealing aluminum alloys range from about 6000 to 900 0 F. 5 Also as used herein, the term "solution heat treatment" refers to a metallurgical process in which the metal is held at a high temperature so as to cause the second phase particles of the alloying elements to dissolve into solid solution. Temperatures used in solution heat treatment are generally higher than those used in annealing, and range up to about 1060*F. This condition is then maintained by 10 quenching of the metal for the purpose of strengthening the final product by controlled precipitation (aging). As used herein, the term "feedstock" refers to the aluminum alloy in strip form. The feedstock employed in the practice of the present invention can be prepared by any number of continuous casting techniques well known to those skilled 15 in the art. A preferred method for making the strip is described in US 5,496,423 issued to Wyatt-Mair and Harrington. Another preferred method is as described in co-pending applications Serial Nos. 10/078,638 (now US Patent 6,672,368) and 10/377,376, both of which are assigned to the assignee of the present invention. The continuously-cast aluminum alloy strip preferably ranges from about 0.06 to 0.25 20 inches in thickness, more preferably about 0.08 to 0.14 inches in thickness. Typically, the cast strip will have a width up to about 90 inches, depending on desired continued processing and the end use of the sheet. Referring now to Figure 2, there is shown schematically a preferred apparatus used in carrying out a preferred embodiment of the method of the present 25 invention. Molten metal to be cast is held in melter holders 31, 33 and 35, is passed through troughing 36 and is further prepared by degassing 37 and filtering 39. The tundish 41 supplies the molten metal to the continuous caster 45. The metal feedstock 46 which emerges from the caster 45 is moved through optional shear 47 and trim 49 stations for edge trimming and transverse cutting, after which it is passed to a 30 quenching station 51 for adjustment of rolling temperature. The shear station is operated when the process in interrupted; vhile running, shear is open.
After optional quenching 51, the feedstock 46 is passed through a rolling mill 53, from which it emerges at the required final thickness. The feedstock 46 is passed through a thickness gauge 54, a shapemeter 55, and optionally trimmed 57, and is then annealed or solution heat-treated in a heater 59. 5 Following annealing/solution heat treatment in the heater 59, the feedstock 46 passes through a profile gauge 61, and is optionally quenched at quenching station 63. Additional steps include passing the feedstock 46 through a tension leveler to flatten the sheet at station 65, and subjecting it to surface inspection at station 67. The resulting aluminum alloy sheet is then coiled at the coiling station 10 69. The overall length of the processing line from the caster to the coiler is estimated at about 250 feet. The total time of processing from molten metal to coil is therefore about 30 seconds. Any of a variety of quenching devices may be used in the practice of the present invention. Typically, the quenching station is one in which a cooling 15 fluid, either in liquid or gaseous form is sprayed onto the hot feedstock to rapidly reduce its temperature. Suitable cooling fluids include water, air, liquefied gases such as carbon dioxide, and the like. It is preferred that the quench be carried out quickly to reduce the temperature of the hot feedstock rapidly to prevent substantial precipitation of alloying elements from solid solution. 20 In general, the quench at station 51 reduces the temperature of the feedstock as it emerges from the continuous caster from a temperature of about I 000*F to the desired hot or warm rolling temperature. In general, the feedstock will exit the quench at station 51 with a temperature ranging from about 400* to 900*F, depending on alloy and temper desired. Water sprays or an air quench may be used 25 for this purpose. Hot or warm rolling 53 is typically carried out at temperatures within the range of about 400* to 1020'F, more preferably 700* to 1000'F. The extent of the reduction in thickness affected by the hot rolling step of the present invention is intended to reach the required finish gauge. This typically involves a reduction of 30 about 55%, and the as-cast gauge of the strip is adjusted so as to achieve this reduction. The temperature of the sheet at the exit of the rolling station is between about 3000 and 850 0 F, more preferably 5500 to 800 0 F, since the sheet is cooled by the rolls during rolling. Preferably, the thickness of the feedstock as it emerges from the rolling station 53 will be about 0.02 to 0.15 inches, more preferably about 0.03 to 0.08 5 inches. The heating carried out at the heater 59 is determined by the alloy and temper desired in the finished product. In one preferred embodiment, for T tempers, the feedstock will be solution heat-treated in-line, at temperatures above about 950'F. preferably about 980'-1000'F. Heating is carried out for a period of about 0.1 to 3 10 seconds, more preferably about 0.4 to 0.6 seconds. In another preferred embodiment, when 0 temper is desired, the feedstock will require annealing only, which can be achieved at lower temperatures, typically about 7000 to 950F, more preferably about 800'-900F', depending upon the alloy. Again, heating is carried out for a period of about 0.1 to 3 seconds, more 15 preferably about 0.4 to 0.6 seconds. Similarly, the quenching at station 63 will depend upon the temper desired in the final product. For example, feedstock which has been solution heat-treated will be quenched, preferably air and water quenched, to about 1100 to 250'F, preferably to about 160*-180*F and then coiled. Preferably, the quench at 20 station 63 is a water quench or an air quench or a combined quench in which water is applied first to bring the temperature of the sheet to just above the Leidenfrost temperature (about 550*F for many aluminum alloys) and is continued by an air quench. This method will combine the rapid cooling advantage of water quench with the low stress quench of airjets that will provide a high quality surface in the product 25 and will minimize distortion. For heat treated products, an exit temperature of 200*F or below is preferred. Products that have been annealed rather than heat-treated will be quenched, preferably air- and water-quenched, to about 1 10* to 720 F, preferably to about 680* to 700*F for some products and to lower temperatures around 200'F for 30 other products that are subject to precipitation of intermetallic compounds during cooling, and then coiled.
Although the process of the invention described thus far in one embodiment having a single step hot or'warm rolling to reach the required final gauge, other embodiments are contemplated, and any combination of hot and cold rolling may be used to reach thinner gauges, for example gauges of about 0.007 5 0.075 inches. The rolling mill arrangement for thin gauges could comprise a hot rolling step, followed by hot and/ or cold rolling steps as needed. In such an arrangement, the anneal and solution heat treatment station is to be placed after the final gauge is reached, followed by the quench station. Additional in-line anneal steps and quenches may be placed between rolling steps for intermediate anneal and for 10 keeping solute in solution, as needed. The pre-quench before hot rolling needs to be included in any such arrangements for adjustment of the strip temperature for grain size control. The pre-quench step is a pre-requisite for alloys subject to hot shortness. Figure 3 shows schematically an apparatus for one of many alternative embodiments in which additional heating and rolling steps are carried out. Metal is 15 heated in a furnace 80 and the molten metal is held in melter holders 81, 82. The molten metal is passed through troughing 84 and is further prepared by degassing 86 and filtering 88. The tundish 90 supplies the molten metal to the continuous caster 92, exemplified as a belt caster, although not limited to this. The metal feedstock 94 which emerges from the caster 92 is moved through optional shear 96 and trim 98 20 stations for edge trimming and transverse cutting, after which it is passed to an optional quenching station 100 for adjustment of rolling temperature. After quenching 100, the feedstock 94 is passed through a hot rolling mill 102, from which it emerges at an intermediate thickness. The feedstock 94 is then subjected to additional hot milling 104 and cold milling 106, 108 to reach the 25 desired final gauge. The feedstock 94 is then optionally trimmed 110 and then annealed or solution heat-treated in heater 112. Following annealing/solution heat treatment in the heater 112, the feedstock 94 optionally passes through a profile gauge 113, and is optionally quenched at quenching station 114. The resulting sheet is subjected to x 30 ray 116, 118 and surface inspection 120 and then optionallycoiled. - Suitable aluminum alloys for heat-treatable alloys include, but are not limited to, those of the 2XXX, 6XXX and 7XXX Series. Suitable non - heattreatable alloys include, but are not limited to, those of the IXXX, 3XXX and 5XXX Series. The present invention is applicable also to new and non-conventional alloys as it has a wide operating window both with respect to casting, rolling and in-line processing. 5 EXAMPLES The following examples are intended to illustrate the invention and should not be construed as limiting the invention in any way. Example 1: In-line fabrication of a heat-treatable alloy. A heat-treatable 10 aluminum alloy was processed in-line by the method of the present invention. The composition of the cast was selected from the range of 6022 Alloy that is used for auto panels. The analysis of the melt was as follows: Element Percentage by weight Si 0.8 15 Fe 0.1 Cu 0.1 Mn 0.1 Mg 0.7 The alloy was cast to a thickness of 0.085 inch at 250 feet per minute speed 20 and was processed in line by hot rolling in one step to a finish gauge of 0.035 inches, followed by heating to a temperature of 980*F for I second for solution heat treatment after which it was quenched to 160*F by means of water sprays and was coiled. Samples were then removed from the outermost wraps of the coil for evaluation. One set of samples was allowed to stabilize at room temperature for 4 - 10 days to reach 25 T4 temper. A second set was subjected to a special pre-aging treatment at I 80*F for 8 hours before it was stabilized. This special temper is called T43. The performance of the samples was evaluated by several tests that included response to hemming, uniaxial tension, equi-biaxial stretching (hydraulic bulge) and aging in an auto paint bake cycle. The results obtained were compared with those obtained on sheet of the 30 same alloy made by the conventional ingot method. Deformed samples from the hydraulic bulge test were also subjected to a simulated auto painting cycle to check for surface quality and response to painting. In all respects, the sheet fabricated in-line by the present method performed as well as or better than that from the ingot method. Table 1: Tensile properties of 6022-T43 sheet fabricated in line by the present method. Measurements were made after nine days of natural aging on ASrM specimens. Cast number. 031009. pro-roll TFX in line ATC Ts UIS elongation, % r bar quench F quench, F S number ksi ksi uniform total rvalue T43 (longitudinal) off 980 114 805656 18.6 36.6 25.5 30.4 1.079 off 1000 114 805658 193 37.2 23.6 26.7 1.144 Sheet from conventional ingot -T43 typical 17.8 34.5 21.5 24.5 0.826 T43 (450) off 980 114 805656 18.5 36.4 24.2 28.0 0.760 off 1000 114 805658 19.6 37.6 25.4 29.7 0.725 Sheet from conventional ingot -T43 typical 17.0 33.4 24.5 26.9 0.602 T43 (transverse) off 980 114 805656 18.4 36.2 22.1 24.5 0.988 0.897 off 1000 114 805658 19.0 36.7 23.6 26.3 0.889 0.896 Sheet from conventional ingot-T43 typical 16.6 32.5 22.8 26.4 0.642 0.668 Custornerrequirements (min) 14.0 19.0 21.0 0.500 Notes: 1. T43 tenperwas obtained by holding samples at 180 F for 8 hours in a separate furnace after fabrication The tine between fabrication and entry ofsamples into fumace was less than 10 minutes. 5 Results of the tensile testing are shown in Table I for T43 temper sheet in comparison with those typical for sheet made from ingot. It is noted that in all respects, the properties of the sheet made by the present method exceeded the customer requirements and compared very well with those for conventional sheet in the same temper. With respect to the isotropy of the properties as measured by the r 10 values, for example, the sheet of the present method obtained 0.897 compared to 0.668 for ingot. In these tests, a generally higher strain hardening coefficient of 0.27 (compared to 0.23 for ingot) was also found. Both of these two findings are important because they suggest that the sheet of the present method is more isotropic and better able to resist thinning during forming operations. Similar observations applied also to 15 T4 temper sheet samples. Flat hemming tests were done after 28 days of room temperature aging. In these tests, a pre-stretch of 11% was applied compared to 7% required in customer specifications. Even under these more severe conditions, all samples obtained an acceptable rating of 2 or 1, Table 2. In similar testing, sheet made from ingot shows an average of 2-3 in the longitudinal hems and 2 in transverse hems. This suggests that the sheet fabricated in-line has superior hemmability. Some samples were solution heat-treated off-line in a salt bath after fabrication. When tested, these 5 samples, too, showed excellent hemming performance as seen in Table 2. Table 2 : Flat hem rating (at 11 % pre-stretch) after 28 days' of natural aging for alloy 6022 at 0.035 inch gauge (cast number: 030820) pre-roll in-line in line gauge ATC hem rating quench anneal, F quench, F inches S number L T comments C7 10 - T43 temper off 950 160 0.035 804908 2 2 fabricated in line off 950 160 0.035 804909 2 2 fabricated in line on off 104 0.035 804912 1 2 off-line heat treat: 1040 F/I min. on 920 140 0.035 804914 2 2 off-line heat treat: 1010 F/I mm. Conventional ingot sheet - T43 temper "2-3" 2 Notes: 1. T43 temper was obtained by holding samples at 180 F for 8 hours in a separate furnace after fabrication The time between fabrication and entry ofsamples into fumace was less than 10 minutes. 2. Requirement for hemming: A rating of2 or less at 7% pre-stretch. In equi-biaxial stretching by hydraulic bulge, the performance of the sheet 10 made in line was comparable to those of sheet made from ingot as seen in stress strain curves in Figures 4a and 4b. This observation applied both in T4 and in T43 temper. The performance in this test was particularly important because it is known that continuous-cast materials typically do not perform well in this test due to the presence of center line segregation of coarse intermetallic particles. 15 Response to paint-bake cycle was evaluated by holding the samples in an oven at 338F for a duration of 20 minutes (Nissan cycle). The tensile yield strength of the samples increased by up to 13 ksi by this treatment, Table 3. In all cases, the required minimum of 27.5 ksi was met easily in the T43 temper. The overall response in this temper was comparable to the average performance of sheet made from DC ingot. As 20 expected, the T4 temper samples'were somewhat unsatisfactory in this respect.
TnbieMPain I bake response of ailoy C710 produced in Rental roled gauge of OOS inches. Cast number: 0308 Nissan/Tayoa paint bake Cycle: 2% 5i rctcb 338 F 20 msinu es, TVS required: 215 ki snin. Temper Date Natural TYS UTS Eleng SYS pre-roll TFX In line Age Sample Penek F quendhF 51T Tea Days UD kst kgP % hai T4 20-Aug 27-AMI 7 &04866-T 16) 33.9 23.2 off 9 1 70 4+PB inline 7. 904966-T 25.8 37.7 20.8 8.4 T4 20-Aug 27-Aisg 7 804867-T 168 34.0 23.0 off 950 160 T4+PB ia fie 7 804867- 269 37's 202 9.2 T43 20-Aug 27-Ausg 7 80490..T 16. 33A 22.0 off 950 160 T43+Ph iM line 7 S04908-T 27.6 39,0 19S w T43 20-Aug 27-Aug 7 804909-T 16.6 33.8 25.0 afT 950 160 T43+PB inline 7 804909-T 29.6 403 19. 13.0 T43 21-Aug 27-Aug 6 804912-T 1.4 35.2 24.2 on off 14 T43+PB 1040/1min 6 904912-7 28.9 40.5 23's I T43 22-Aug 27'Aug 9 804914-T j8.6 352 25,0 On 920 140 T434-PB 1010/m'in 5 804914-T 30.1 41.1 22.5 11.5 DC ingeo T43 7 17. 333 26.3 typical 743+PB 7 | 303 40,9 26.4 1, Now: 1. SampkCs wre held at 18O F fot hourn foe r T43 temper (senCh aaed). 2. Samples 804912 and 804914: taboralory solution heat tret was carried out in a salt bath utder coundiont mdiated followed by waler quenehing. The deformed hydraulic bulge specimens were inspected for surface quality and were found to show no undesirable features such as orange peel, blisters, etc. Selected 5 bulge samples were subjected to a simulated auto-paint cycle. Figure 5 shows excellent painted surface quality with no paint brush lines, blisters or linear features. Sheet at finished gauge was examined for grain size and was found to have a mean grain size of 27 pm in the longitudinal and 36 urm in the thickness direction, Figure 6a. This is substantially finer than that of 50-55 pin typical for sheet made from ingot. Since a fine 10 grain size is recognized to be generally beneficial, it is likely that a part of the good/superior properties of the sheet made by the present method was due to this factor. It was found that even finer grain size could be obtained in the present method by rapidly cooling the strip to about 700DF before it is rolled. This effect is illustrated in Figures 6a and 6b where the two samples are shown side by side. The grain size of the cooled sample (Figure 6b) was 20 pm 15 in longitudinal and 27 urn in transverse direction, which are 7 and 9 pm, respectively, finer than those observed in the sheet which had no pre-quench cooling (Figure 6a). Samples of as-cast strip were quenched and examined metallographically to further understand the benefits of thin strip casting. The samples showed the three-layered structure characteristic of the Alcoa strip casting process, Figure 7a. The surfaces of the strip were 12 clean (no liquation, blisters or other surface defects) with a fine microstructure, Figures 7b and 7c. Unlike the material continuously cast by Hazelett belt casters or roll casters, the strip of the present method showed no centerline segregation of coarse intermetallic compounds. On the contrary, the last liquid to solidify had formed fine second phase particles between 5 grains in a center zone that covered about 25% of the section, Figures 7d and 7e. This absence of a marked centerline segregation in the present method provided the good mechanical properties observed, especially in the equi-biaxial stretch tests. Most of the second phase particles observed were AlFeSi phase with an average size < I pm. Figures 7f and 7g. Some Mg2Si particles were seen in the center zone of the sample, but none was 10 noted in the outer "shells", Figures 7b and 7c. This suggested that the rapid solidification in the caster was able to keep the solute in solution in the outer zones of the structure. This factor, combined with the fine overall microstructure of the strip (see Table 4), enabled the complete dissolution of all solute at substantially lower solution heat treatment temperatures of 950 - 980 0 F than 1060 0 F that would be needed for sheet prepared from DC ingot. 15 Table 4 Chfeeritis of cOAstituent particles ad4 pores found in as -cast samples ofaiiey C10 (Cast number: 030820) lcriation in strip av. diam. area av. am . area pmn % p con er, transverse 0.37 0,37 0.50 0.143 center, longitudinal 03g 034 031 0-072 averOge 0.33 0.36 0A shtI, transverse 0,35 0.21 032 023 shel, longitudinal 033 0.25 0.28 0.9 nieseg A 0.23 030 0.21 Notes: I The constiments were mainly AlFeSi phase. Small rount of M9s1i was alto seen in center zone. 2 Each result is average 20 different fames. 13 Example 2: In-line fabrication of a non-heat treatable alloy. A non heat-treatable aluminum alloy was processed by the method of the present invention. The composition of the cast was selected from the range of the 5754 Alloy that is used for auto inner panels and reinforcements. The analysis of the melt was as follows: 5 Element Percentage by weight Si 0.2 Fe 0.2 Cu 0.1 Mn 0.2 10 Mg 3.5 The alloy was cast to a strip thickness of 0.085 inch at 250 feet per minute speed. The strip was first cooled to about 700'F by water sprays placed before the rolling mill, after which it was immediately processed in-line by hot rolling in one step to a finish gauge of 0.040 inches, followed by heating to a temperature of 900'F 15 for I second for recrystallization anneal after which it was quenched to 1904F by means of water sprays and was coiled. The performance of the samples was evaluated by uniaxial tensile tests and by limiting dome height (LDH). Results of the tensile testing are shown in Table 5. The TYS and elongation of the sample in the longitudinal direction were 15.2 ksi and 25.7%, respectively, well 20 above the minimum of 12 ksi and 17% required for Alloy 5754. UTS value was 35.1 ksi, in the middle of the range specified as 29-39 ksi. In the limiting dome height test, a value of 0.952 inch was measured that met the required minimum of 0.92 inch. These values compared well with typical properties reported for sheet prepared from DC ingot. Sheet of the present invention had a higher elongation, higher UTS and 25 higher strain hardening coefficient n. A higher anisotropy value r was expected, but was not verified in the testing of this sample. The r value was 0.864 compared to 0.92 for DC sheet. Sheet at finished gauge was examined for grain size and was found to have a mean grain size of 11-14 pim (ASTM 9.5). This is substantially finer than that of 16 30 pum typical for sheet made from ingot. Since a fine grain size is recognized to be generally beneficial, it is likely that a part of the good/superior properties of the sheet made by the present method was due to this factor.
Samples of as-cast strip were quenched and examined metallographically. Despite differences in chemical composition, the as-cast samples showed the same three-layered structure as that described above for Alloy 6022, Figure 8. This confirms that the three-layered fine microstructure that enables in-line processing of 5 the strip described in this invention, is a characteristic of the Alcoa strip casting process. Variations of the fabrication path were also investigated. In one test, 0.049 inch gauge sheet was fabricated in-line without the in-line anneal, Table 5. The sample was then flash-annealed off-line in a salt bath at 975'F for 15 s followed by 10 water quenching. That sample showed similar properties and a high r value comparable to those described above for sheet fabricated with in-line anneal. This equivalence conformed that in-line fabrication is able to develop the full properties of the alloy in 0-temper. In another test, the strip was hot rolled in-line to 0.049 inch gauge and was quenched to 160'F with no in-line anneal. It was then cold-rolled to 15 0.035 inch gauge and was flash-annealed at 950*F for 15 seconds, Table 5. That sheet, too, developed good mechanical properties. These observations suggested that hot and cold rolling could be combined with an-in line final anneal to make sheet of a wide range of thickness of 0-temper products by the present invention. Table 5: Uniaxial tensile test results forAl-3.5 %Y MgAX alloy processed in line by the present invention. 1Reno0 c1s hot roll flow path L TYS UITS elongation, % rvlue r ba n vau Number inch inch quench Tel,F quenchF T ki s ufr _a M.5%L 6. 22.3 0.781 0309 805314 M30902B MA 0.033 0.049 . a1f on 45 1 68 35.3 24.1 29.8 1.120 0.947 0311 M T 16.1 35.6 21.3 22.2 0.766 0.306 SL 15.6 35.9 19.2 20.8 0.035 0.314 005035 030902B Al-3.5% 0049 009 on olf n 45 15.4 35.5 21.7 32.5 1.200 1.15 0303 MgT 15.0 35.0 22.4 26.9 0.963 0.317 LlM 15. 35.1 23.2 257 0.778 0-323 005747 31021 A - 0.04 0041 on 960 190 45 146 34.8 231 25.3 0938 U.864 0.326 Mg T 146 347 23.2 24.5 1 . 2 0.322 Alloy 5754 for comprison L 14.6 29.7 20 4 22.2 0.078 0301 DCingot 5754 0036 45 14.4 289 21.2 20 0809 U.92 0.3D3 T 14.6 20,9 19.7 22.4 1.082 0305 Noies . AA regisewd requirmeis ior3754. 'YS-12 kst min. (L). UT5-29-39 ksi (L), Elongton- 17 %min (L). LDH 0.92 inches min 20 2. San 1314 e nd 805035 wCn annelaed of.line m a sah bath in 95V F.nd 975 F. secgtively, for 15 seconds folloing wlhch they were quenched in wter.
Example 3: In-line fabrication of a non - heat-treatable ultra high Mg alloy. An Al -10% Mg alloy was processed by the method of the present invention. The composition of the melt was as follows: Element Percentage by weight 5 Si 0.2 Fe 0.2 Cu 0.2 Mn 0.3 Mg 9.5 10 The alloy was cast to a strip thickness of 0.083 inch at 230 feet per minute speed. The strip was first cooled to about 650'F by water sprays placed before the rolling mill. It was then immediately hot-rolled in-line in one step to a finish gauge of 0.035 inch followed by an anneal at 860*F for I second for recrystallization and spray quenching to 190'F. The sheet was then coiled. Performance of the sheet in 0 15 temper was evaluated by uniaxial tensile tests on ASTM - 4 d samples removed from the last wraps of the coil. In the longitudinal direction, the samples showed TYS and UTS values of 32.4 and 58.7 ksi, respectively. These very high strength levels, higher by about 30% than those reported for similar alloys, were accompanied by high elongation: 32.5% total elongation and 26.6% uniform elongation. The samples 20 showed very fine grain structure of- 10 pm size. Example 4: In-line fabrication of a recyclable auto sheet alloy. An Al -1.4% Mg alloy was processed by the method of the present invention. The composition of the melt was as follows: 25 Element Percentage by weight Si 0.2 Fe 0.2 Cu 0.2 Mn 0.2 30 Mg 1.4 The alloy was cast to a strip thickness of 0.086 inch at 240 feet per minute speed. It was rolled to 0.04 inch gauge in one step, flash annealed at 950 F, following which it was water quenched and coiled. The quenching of the rolled sheet was done in two different ways to obtain 0 temper and T temper by different settings of the post quench 63. For the T temper, the strip was pre 5 quenched by quench 53 to about 700 F before warm-rolling to gauge and was post-quenched to 170 F (sample #:804995 in Table 6). In a second case, the sheet was post quenched to around 700 F and was warm coiled to create 0 temper. The 0-temper coil was done both by warm rolling (sample: 804997) and by hot rolling (sample: 804999). Performance of the sheet was evaluated by uniaxial tensile tests on ASTM--4 d samples and 10 by hydraulic bulge test. In the T temper, the sheet showed tensile yield strength, ultimate tensile strength and elongation values well above the requirements for alloy 5754 in 0-temper and as good as those available in sheet made by the conventional ingot method, Table 6. In the hydraulic bulge test, too, the performance of the T temper AX-07 was very close to that of alloy 5754, Figure 9. This suggests that AX-07 in T temper made by the method of the present invention can be used to replace 15 the 5754 sheet in inner body parts and reinforcements in auto applications. Such a replacement would have the advantage of making those parts recyclable into the 6xxx series alloys, by virtue of the lower Mg content, used in outer skin parts of autos without the need for separation. Samples were also tested in 0-temper made by the present method. In that temper, the strength levels were lower, around 8.8 ksi yield strength and 23 ksi tensile strength. The performance 20 in the hydraulic bulge test improved equaling that of conventional 5754 as may be seen in Figure 9. This temper thus offers a material that would be formed more easily at lower press loads. Whereas particular embodiments of this invention have been described above for purposes of illustration, it will be evident to those skilled in the art that numerous variations of the details of the present invention may be made without departing from the invention as defined in the appending 25 claims. Table 6: Uniaxial tensile test results for alloy AX-07 sheet samples in T and 0 temper. test hot roll flow path & TYS UTS elongation, % Hollomon constant cat ube lly gauge, gauge, pre-rolil X r value r bar identification cast number alloy g e I inch -uench , quench, F ksi ksi uniform total n K, ksi L 15.3 31.8 21.9 23.1 0.862 0.276 61.08 804995 30818 AX-07 (T) 0.041 0.041 on 950 170 45 14.2 30.4 24.3 29.0 1.261 1.123 0.275 57.71 T 14.7 30.8 18.4 22.7 1.107 0.275 59.62 AX-07 L 8.9 23.3 19.1 20.5 0.947 0.289 47.23 804997 30818 0.042 0.042 on 950 650 45 8.6 22.9 22.1 22.9 1.210 1.102 0.293 45.86 (0) T 8.7 23.0 19.8 25.2 1.039 0.293 46.33 L 8.2 23.3 20.0 25.2 1.053 0.299 48.07 804999 30818 AX-07 0.040 0.040 off 950 700 45 8.9 23.5 19.6 24.5 1.167 1.128 0.288 47.82 T 8.7 23.2 17.9 23.4 1.124 0.298 4834 L 14.6 29.7 20.4 22.2 0.978 0.301 61.27 793669 DC ingot 5754-0 0.036 45 14.4 28.9 21.2 22.0 0.809 0.92 0.303 58.64 T 14.6 28.9 19.7 22.4 1.082 0.305 59.79 17 Throughout this specification and the claims which follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" and "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps. 5 The reference to any prior art in this specification is not, and should not be taken as, an acknowledgement or any form of suggestion that the prior art forms part of the common general knowledge in Australia. 18
Claims (10)
1. A method of manufacturing an aluminum alloy sheet in a continuous in-line sequence comprising: (i) providing an aluminum alloy strip as feedstock by casting a molten alloy as a strip material thereby rapidly solidifying the molten alloy in a caster to keep solute in solid solution in outer zones of the strip; and (ii) quenching the feedstock with a quenching device before any further processing of the feedstock to a sheet takes place.
2. The method of claim 1, further comprising: (iii) hot or warm rolling the quenched feedstock to a sheet; (iv) annealing; and (v) quenching the sheet to a temperature of 43'C to 382'C (1 10 F to 720'F), in particular to form an 0 temper.
3. The method of claim 1, further comprising: (iii) hot or warm rolling the feedstock to a sheet; (iv) solution heat treating and (v) quenching the sheet to a temperature of 43'C to 121 C (1 10 F to 250'F), in particular to form a T temper.
4. The method of claim 2 or claim 3, further comprising tension leveling and coiling the aluminum alloy sheet.
5. The method of claim 2 or claim 3, wherein the hot or warm rolling step is carried out at a temperature of 204'C to 549'C (400'F to 1020'F).
6. The method of claim 3, wherein at step (iv) the feedstock is solution heat treated at a temperature of 427'C to 571 0 C (800 0 F to 1060 0 F).
7. The method of claim 6, wherein at step (iv) the solution heat treatment is carried out for a period of 0.1 to 3 seconds. 20
8. The method of any one of claims 1 to 3, wherein the aluminum alloy is selected from the group consisting of 2XXX, 6XXX, and 7XXX series alloys.
9. The method of claim 2 or 3, wherein the alloy sheet is manufactured without cold rolling.
10. Aluminum alloy sheet having been produced with a method according to any one of claims 1 to 9.