AU2013257417B2 - Thin cast steel strip with reduced microcracking - Google Patents

Abstract

A thin cast steel strip and method of making thereof with improved resistance to microcracking is 5 disclosed. The steel strip is produced by continuous casting and contains a carbon content between about 0.010% and about 0.065% by weight, less than 5.0% by weight chromium, at least 70 ppm of total oxygen and between 20 and 70 ppm of free oxygen, and manganese to sulfur ratio 10 greater than about 250:1. The carbon content in the cast strip may be below 0.035%, less than 0.005% by weight titanium, and the average manganese to silicon ratio in the strip produced may be greater than 3.5:1. The carbon content may be less than 0.035%, the casting speed less 15 than 76.68 meters per minute, and the tundish temperature of the molten metal is maintained below 16120C (2933.70F). 2179477_1 (GHMaers) 12/11/13 Fi+A Fig. 1

Description

-1 THIN CAST STEEL STRIP WITH REDUCED MICROCRACKING BACKGROUND AND SUMMARY OF THE INVENTION 5 This invention relates generally to steelmaking, and particularly carbon steels formed by continuous casting of thin strip. Thin steel strip may be formed by continuous 10 casting in a twin roll caster. In twin roll casting, molten metal is introduced between a pair of counter rotated laterally positioned casting rolls, which are cooled, so that metal shells solidify on the moving roll surfaces and are brought together at the nip between the 15 rolls to produce a solidified strip product delivered downwardly from the nip. The term "nip" is used herein to refer to the general region at which the rolls are closest together. The molten metal may be poured from a ladle into a smaller vessel from which it flows through a metal 20 delivery nozzle located above the nip to form a casting pool of molten metal supported on the casting surfaces of the rolls and extending along the length of the nip. This casting pool is usually confined between side plates or dams held in sliding engagement with end surfaces of the 25 rolls so as to dam the two ends of the casting pool against outflow. When casting thin strip with a twin roll caster, the molten metal in the casting pool will generally be at 30 a temperature of the order of 1500 0 C, and usually 1600 0 C and above. A high heat flux and extensive nucleation on initial solidification of the metal shells on the casting surfaces is needed to form the steel strip. U.S. Patent No. 5,720,336 describes how the heat flux on initial 35 solidification can be increased by adjusting the steel melt chemistry such that a substantial portion of the metal oxides formed are liquid at the initial 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -2 solidification temperature. As disclosed in U.S. Patent Nos. 5,934,359 and 6,059,014 and International Application PCT/AU99/00641 (publication No. WO 00/07753), nucleation of the steel on initial solidification can be influenced 5 by the texture of the casting surface. In particular, International Application PCT/AU99/00641 discloses that a random texture of peaks and troughs in the casting surfaces can enhance initial solidification by providing substantial nucleation sites distributed over the casting 10 surfaces. Attention has been given in the past to the steel chemistry of the melt, particularly in the ladle metallurgy furnace before the casting of the thin strip. 15 In the past, in U.S. Patent No. 7,048,033 attention has been given controlling to the oxide inclusions and the oxygen levels in the steel metal and their impact on the quality of the steel strip produced. In U.S. Patent No. 7,156,151, hydrogen levels and nitrogen levels have been 20 regulated in the molten metal to enhance the casting and quality of the steel strip. In U.S. Patent No. 6,547,849, a method is disclosed of providing silicon/manganese killed molten steel having a sulfur content of less than 0.02% by weight for casting. Finally, in U.S. Patent 25 Application SN 11/622,754, filed January 12, 2007 (publication No. U.S. 2007/0175608), a thin cast strip with reduced microcracks and a method of making the same is disclosed by controlling the sulfur content of the cast strip to between about 0.003% and about 0.008% by weight, 30 along with the carbon content to between about 0.010% and about 0.065% by weight. In these prior disclosures, the teachings are generally to have low sulfur levels, such as less than 35 0.025 or 0.02%. See, e.g, International Application PCT/AU99/00641 and U.S. Patent 6,547,849. There is no suggestion of purposely providing very low levels of 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -3 sulfur to reduce or eliminate microcracking, or for any other purpose, except for U.S. Application SN 11/622,754. There has been no suggestion to our knowledge of controlling the ratios of manganese/sulfur or 5 manganese/silicon for any reason in the casting of thin strip, or any other steelmaking. Generally, sulfur has been an undesirable impurity in steelmaking, including in continuous casting 10 of thin strip. Steelmakers generally go to great lengths and expense to minimize sulfur content in making steel. Sulfur is primarily present as sulfide inclusions, such as MnS inclusions. Sulfide inclusions may provide sites for voids and/or surface cracking. Sulfur may also decrease 15 ductility and notch impact toughness of the cast steel, especially in the transverse direction. Further, sulfur creates red shortness, or brittleness in red hot steel. Sulfur also reduces weldability. Sulfur is generally removed from molten steel by a desulphurization process. 20 Steel for continuous casting may be subjected to deoxidation and then desulphurization in the ladle metallurgy, prior to casting. One such method involves stirring the molten steel by injecting inert gases, such as argon or nitrogen, while the molten metal is in contact 25 with slag having a high calcium content. See U.S. Patent No. 6,547,849. On the other hand, thin cast strip formed by twin roll casting has been known to have a tendency to form 30 microcracks in the strip surface. One cause has been the formation of an oxide layer on the surface of the casting rolls that acts as a thermal barrier causing irregular solidification of the cast strip and formation of microcracks in the strip surface. 35 The above discussion is not to be taken as an admission of the common general knowledge in Australia or 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -4 elsewhere. The applicant has found that microcracking is related to the steel chemistry and certain process 5 parameters affect solidification and that newly formed shells can be made resistant to the formation of microcracks. The applicant has also observed that sulfur is a surface active element in liquid steel. From these observations, the applicant has found that microcracking 10 in cast strip of low carbon steel can be controlled by regulating the ratio of manganese to sulphur, oxygen, and free-oxygen, and also to a lesser degree the ratio of manganese to silicon, in the molten metal. 15 The present disclosure describes a thin cast steel strip produced by continuous casting by steps comprising: a) assembling a pair of internally cooled 20 casting rolls having a nip therebetween and with confining closures adjacent the ends of the nip; b) introducing molten low carbon steel having a carbon content of between 0.010% and 0.065% by weight, 25 less than 5.0% by weight chromium, at least 70 ppm of total oxygen and between 20 and 70 ppm of free oxygen, a silicon content of 2.5% by weight or less, a sulfur content of 0.008 % by weight or less, an average manganese to silicon ratio above 3.5:1 and an average manganese to 30 sulfur ratio above 250:1 between the pair of casting rolls to form a casting pool supported on the casting surfaces of the casting rolls; c) counter rotating the casting rolls to form 35 solidified metal shells on the casting surfaces of the casting rolls; and 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -5 d) forming from said solidified shells thin steel strip downwardly through the nip between the casting rolls. 5 The average manganese to silicon ratio in the molten low carbon steel introduced to produce the cast strip is greater than 3.5:1. The thin steel strip produced by continuous 10 casting may have a carbon content between 0.025% and 0.065% by weight, or alternatively, a carbon content below 0.035% by weight. The thin cast strip may have a chromium content 15 less than 1.5% by weight or less than 0.5% by weight and/or the thin cast strip may have titanium content less than 0.005% by weight. The thin steel strip may be less than 5 mm in 20 thickness, or less than 2.5 mm in thickness. The molten metal in the casting pool may have a total oxygen content of at least 100 ppm and a free oxygen content between 30 and 50 ppm. Alternatively or in 25 addition, the thin steel strip produced by continuous casting may be from the molten metal in the casting pool having a nitrogen content less than about 52 ppm. Alternatively, or in addition, the sum of the partial pressures of the hydrogen and nitrogen is less than 1.15 30 atmospheres. Alternatively, disclosed is a method of casting thin steel strip comprising: 35 a) assembling a pair of internally cooled casting rolls having a nip therebetween and with confining closures adjacent the ends of the nip; 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -6 b) introducing molten carbon steel having a carbon content of between 0.010% and 0.065% by weight, less than 5.0% by weight chromium, at least 70 ppm of 5 total oxygen and between 20 and 70 ppm of free oxygen, a silicon content of 2.5% by weight or less, a sulfur content of 0.008 % by weight or less, an average manganese to silicon ratio above 3.5:1 and an average manganese to sulfur ratio above 250:1 between the pair of casting rolls 10 to form a casting pool supported on the casting surfaces of the casting rolls; c) counter rotating the casting rolls to form solidified metal shells on the casting surfaces of the 15 casting rolls; and d) forming from said solidified shells thin steel strip downwardly through the nip between the casting rolls. 20 The average manganese to silicon ratio in the molten low carbon steel introduced in the method to produce cast strip is greater than 3.5:1. 25 A thin steel strip produced by the method casting steel strip may have a carbon content between 0.010% and 0.065% by weight. The thin cast strip produced by the method may 30 have a chromium content less than 1.5% by weight or less than 0.5% by weight and/or the thin cast strip may have titanium content less than 0.005% by weight. The thin steel strip may be less than 5 mm in 35 thickness, or less than 2.5 mm in thickness. The applicant has also found that additional 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -7 variables that affect solidification and 'strength' of the newly formed shells are the temperature of the molten metal in the tundish and casting speed. Reduced temperature of the molten metal in a tundish and cast 5 speeds allows time for shell growth to larger thickness and more strength reducing microcracking adjacent to the surface of the cast strip. The applicant has found that the thin steel strip produced by continuous casting may be cast at a tundish temperature for the molten metal below 10 1612-C (2933.7 0 F) and a casting speed less than 76.88 meters per minute. These additional variables are relevant to both the thin cast strip produced as well as the method by which the thin cast strip is produced. 15 BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a diagrammatic side elevation view of an illustrative strip caster; 20 FIG. 2 is an enlarged sectional view of a portion of the caster of FIG. 1; FIG. 3 is an enlarged sectional view of a portion of the caster of FIGS. 1 and 2; 25 FIG. 4 shows the reduction in microcracking with manganese to sulfur ratios above 250:1 in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; 30 FIG. 5 shows the reduction in microcracking with manganese to sulfur ratios above 250:1 in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; 35 FIG. 6 shows the reduction in microcracking with manganese to silicon ratios above 3.5:1 in a steel 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -8 composition made into cast strip by a caster similar to that shown in FIGS.1 through 3; FIG. 7 shows the reduction in microcracking with 5 manganese to silicon ratios above 3.5:1 in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; FIG. 8 shows the reduction in microcracking with 10 carbon content below 0.035% by weight in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; FIG. 9 shows the reduction in microcracking with 15 carbon content below 0.035% by weight in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; FIG. 10 shows the reduction in microcracking with 20 nitrogen levels below 52 ppm in the molten metal prior to casting in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; FIG. 11 shows the reduction in microcracking with 25 nitrogen levels below 52 ppm in the molten metal prior to casting in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3; FIG. 12 shows the reduction in microcracking in a 30 steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at casting speeds below 71.8 meters per second; FIG. 13 shows the reduction in microcracking in a 35 second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at casting speeds below 71.8 meters per second; 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -9 FIG. 14 shows the reduction in microcracking in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at a tundish 5 temperature below 1612 0 C (2933.7 0 F); FIG. 15 shows the reduction in microcracking in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at a tundish 10 temperature below 1612 0 C (2933.7 0 F); FIG. 16 shows the reduction in microcracking in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at five different 15 casting speeds; FIG. 17 shows the reduction in microcracking in a second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at the same 20 five different casting speeds; FIG. 18 shows the reduction in microcracking in a steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at five different 25 casting speeds with manganese to sulfur ratios above 250:1; FIG. 19 shows the reduction in microcracking in a second steel composition made into cast strip by a caster 30 similar to that shown in FIGS. 1 through 3 at five different casting speeds with manganese to sulfur ratios above 250:1; FIG. 20 shows the reduction in microcracking in a 35 steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at five different casting speeds with manganese to silicon ratios above 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -10 3.5:1; FIG. 21 shows the reduction in microcracking in a second steel composition made into cast strip by a caster 5 similar to that shown in FIGS. 1 through 3 at five different casting speeds with manganese to silicon ratios above 3.5:1; FIG. 22 shows the reduction in microcracking in a 10 steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at five different casting speeds with carbon content below 0.035% by weight; FIG. 23 shows the reduction in microcracking in a 15 second steel composition made into cast strip by a caster similar to that shown in FIGS. 1 through 3 at five different casting speeds with carbon content below 0.035% by weight; and 20 FIGS. 24 and 25 shows the microcracking can be turned off and on depending on the ratio of Mn/S and Mn/Si reported in Heat Nos. 175406 and 175408 in Table I. DETAILED DESCRIPTION OF THE DRAWINGS 25 Microcracking (generally referred to as "cracking") is a defect that may appear in the surface portions of thin cast strip. Cracking may result from the formation of voids, surface cavities or depressions, or 30 inclusions adjacent the surface of the strip. Cracking may occur during the formation and cooling process. Referring to FIGS. 1 through 3, the thin cast strip, and method of making the same, may be made and used 35 in the continuous strip caster shown. FIGS. 1 through 3 illustrates a twin roll caster denoted generally as 11 which produces a cast steel strip 12 that passes in a 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -11 transit path 10 across a guide table 13 to a pinch roll stand 14 comprising pinch rolls 14A. Immediately after exiting the pinch roll stand 14, the strip may pass into a hot rolling mill 16 comprising a pair of reduction rolls 5 16A and backing rolls 16B by in which it is hot rolled to reduce its thickness. The rolled strip passes onto a run out table 17 on which it may be cooled by convection by contact with water supplied via water jets 18 (or other suitable means) and by radiation. In any event, the rolled 10 strip may then pass through a pinch roll stand 20 comprising a pair of pinch rolls 20A and thence to a coiler 19. Final cooling (if necessary) of the strip takes place on the coiler. 15 As shown in FIGS. 2 and 3, twin roll caster 11 comprises a main machine frame 21 which supports a pair of cooled casting rolls 22 having casting roll surfaces 22A, assembled side-by-side with a nip between them. Molten metal of plain carbon steel may be supplied during a 20 casting operation from a ladle 28 to a tundish 23, through a refractory shroud 24 to a distributor 25 and thence through a metal delivery nozzle 26 generally able the nip 27 between the casting rolls 22. The molten metal thus delivered to the nip 27 forms a pool 30 supported on the 25 casting roll surfaces 22A above the nip and this pool is confined at the ends of the rolls by a pair of side closures, dams or plates (not shown), which may be positioned adjacent the ends of the rolls by a pair of thrusters (not shown) comprising hydraulic cylinder units 30 (or other suitable means) connected to the side plate holders. The upper surface of pool 30 (generally referred to as the "meniscus" level) may rise above the lower end of the delivery nozzle so that the lower end of the delivery nozzle is immersed within this pool. 35 Casting rolls 22 are internally water cooled so that shells solidify the moving casting surfaces of the 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -12 rolls. The shells are then brought together at the nip 27 between the casting rolls sometime with molten metal between the shells, to produce the solidified strip 12 which is delivered downwardly from the nip. 5 Frame 21 supports a casting roll carriage which is horizontally movable between as assembly station and a casting station. 10 Casting rolls 22 may be counter-rotated through drive shafts (not shown) driven by an electric, hydraulic or pneumatic motor and transmission. Rolls 22 have copper peripheral walls formed with a series of longitudinally extending and circumferentially spaced water cooling 15 passages supplied with cooling water. The rolls may typically be about 500 mm in diameter and up to about 2000 mm long in order to produce strip product of about 2000 mm wide. 20 Tundish 23 is of conventional construction. It is formed as a wide dish made of a refractory material such as for example magnesium oxide (MgO). One side of the tundish receives molten metal from the ladle. 25 Delivery nozzle 26 is formed as an elongate body made of a refractory material such as for example alumina graphite. Its lower part is tapered so as to converge inwardly and downwardly above the nip between casting rolls 22. 30 Nozzle 26 may have a series of horizontally spaced generally vertically extending flow passages to produce a suitably low velocity discharge of molten metal throughout the width of the rolls and to deliver the 35 molten metal between the rolls onto the roll surfaces where initial solidification occurs. Alternatively, the nozzle may have a single continuous slot outlet to deliver 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 - 13 a low velocity curtain of molten metal directly into the nip between the rolls and/or the nozzle may be immersed in the molten metal pool. 5 The pool is confined at the ends of the rolls by a pair of side closure plates that are adjacent to and held against stepped ends of the rolls when the roll carriage is at the casting station. Side closure plates are illustratively made of a strong refractory material, 10 for example boron nitride, and have scalloped side edges to match the curvature of the stepped ends of the rolls. The side plates can be mounted in plate holders which are moveable at the casting station by actuation of a pair hydraulic cylinder units (or other suitable means) to 15 bring the side plates into engagement with the stepped ends of the casting rolls during a casting operation. The twin roll caster may be the kind illustrated and described in some detail in, for example, U.S. Patent 20 Nos. 5,184,668; 5,277,243; 5,488,988; and/or 5,934,359; U.S. Patent Application No. 10/436,336 (Publication No. U.S. 2004/0144519); and International Patent Application PCT/AU93/00593 (Publication No. WO 94/12300), the disclosures of which are incorporated herein by reference. 25 Reference may be made to those patents for appropriate constructional details but forms no part of the present invention. Referring to FIGS. 4 and 5, the result of the 30 mean rate of microcracking ("mean sum CR") in the surfaces of cast thin strip of two grades of steel show the response of the manganese to sulfur ratio. The steel compositions are of grade designation 1005-S4 having 0.035% carbon, 0.68% manganese, 0.20% silicon and 0.015% 35 chromium, and grade designation 1005-S2 having 0.035% carbon, 0.85% manganese, 0.25% silicon and 0.015% chromium. The total oxygen content of the steel 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -14 composition was >100ppm and free oxygen content was 43 ppm, and the nitrogen content was 43 ppm as measured in the tundish 23 for convenience. And the partial pressures of hydrogen and nitrogen was <1.15 atmospheres. The steel 5 strip produced was made by a twin roll caster similar to that illustrated in FIGS. 1 through 3. During crack assessment the top and bottom surfaces of the strip are each divided into 7 areas (14 10 areas for 2 sides) and a crack rating is given for each area. The crack rating for each area may range from "0" (for essentially defect free strip) to "5", where "1" is less than 5 microcracks, "2" is between 5 and 24 microcracks, "3" is between 24 and 42 microcracks, "4" is 15 between 42 and 60 microcracks, and "5" is greater than 60 microcracks in the strip. The overall crack rating "CR" is the sum of the crack rating of all 14 areas of the strip. As shown in the left hand columns in FIGS. 4 and 5, the mean sum of microcracks in the surfaces of the thin strip 20 having a manganese to sulfur ratio lower than 250:1 was 19.53 on grade 1005-S4 and was 20.78 for the grade 1005 S2, respectively. By contrast, as shown in the right hand columns in FIGS. 4 and 5, the mean sum of microcracks in the cast strip with manganese to sulfur ratio above 250:1 25 was 10.15 and 11.39, respectively, in the two grades of steel in FIGS. 4 and 5. This analysis verified that the microcracking in the cast thin strip, and the method of making the same, 30 was much reduced in different steel compositions with a manganese/silicon ratio above 250:1. Referring to FIGS. 6 and 7, a similar analysis was done with regard to the same steel compositions of 35 grade designations 1005-S4 and 1005-S2 on effect of microcracking ("mean sum CR") with manganese to silicon ratios above and below 3.5. As shown in FIGS. 6 and 7, 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 - 15 the mean sum of microcracking in the surfaces of the thin cast strip for a manganese to silicon ratio below 3.5 were mean sums of 20.37 and 18.51 in the two steel grades, compared to the mean sums of microcracking of 13.57 and 5 14.31 in the two different steel grades with manganese to silicon ratios above 3.5:1. Here again, the benefit of the cast thin strip, and method of making the same, was verified with a manganese to silicon ratio above 3.5:1 in different steel compositions. 10 The benefits of the present cast strip, and method of making the same, are also illustrated in the heats 175404, 175406 and 175408 reported in Table I below in percent by weight. Heats 175404 and 175406 produced 15 steel with surface microcracks and heat 175408 produced steel without surface microcracks. TABLE I Heat Carbon Cu Cr Ti Mn Si S N Mn/S Mn/ Si 175404 0.0307 0.0771 0.0425 0.0012 0.892 0.2164 0.005 0.0056 178 4.12 175406 0.0312 0.0534 0.0296 0.0015 0.7786 0.2634 0.0041 0.0054 189 2.95 175408 0.0303 0.0555 0.0231 0.0016 0.9198 0.2265 0.0029 0.0043 316 4.06 20 The values given in Table I are percent by weight, as are other values of element content given this application unless otherwise stated. 25 As shown by Table I, considerably improved results in microcracking of the surfaces of the thin strip in heat 175408 were obtained when the manganese to sulfur ratio was 316 and the manganese to silicon ratio was 4.06. The manganese, sulfur and silicon, like oxygen levels 30 described above, were measured in the tundish 23 by known techniques. 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -16 From Heats 175404, 1754406, and 175408 the applicant found it was possible to turn microcracks on and off between campaigns by varying the ratios of Mn/S and Mn/Si. When the ratio of Mn/S was below 250:1 and the 5 ratio of Mn/Si was below 3.5:1, both the bottom and top surfaces of the cast strip showed microcracks across of the entire width of the strip as shown in FIG. 24. The sample was elongated by 6% in this analysis to assist in identifying the microcracks. TD and BD are the middle of 10 top and bottom of the strip, DS are top and bottom of drive side edge of the strip, and OS are the top and bottom operator side edge of the strip. Three sections were also independently analysed on both the top and bottom surfaces of the strip between the middle and edges 15 of the strip as shown in FIG. 24. When the ratio of Mn/S was above 250:1 and the ratio of Mn/Si was above 3.5:1, both the bottom and top surfaces of the cast strip were clear of microcracks as shown in FIG. 25. The sample was elongated by 4% in this analysis to assist in identifying 20 the microcracks. Referring to FIGS. 8 and 9, the same two steel grades of steel composition were studied for different carbon content in the relationship to microcracking ("mean 25 sum CR") of the surfaces of the thin strip. As shown by FIGS. 8 and 9, the mean sum of microcracks was markedly improved in both steel grades with mean sums of microcracking rates of 13.9 and 13.29, respectively, with the carbon content below 0.035% by weight, compared to 30 mean sums of microcracking rates of 21.7 and 19.00 when the carbon exceeded 0.035% in the respective steel grades. Referring to FIGS. 10 and 11, the same two grades of steel compositions were studied for different the 35 levels of nitrogen in the thin cast strip on the microcracking in the surfaces ("mean sum CR"). As shown by FIGS. 10 and 11, the microcracking was markedly 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -17 improved when the nitrogen was below 0.0052% (52 ppm) by weight with the mean sum of microcracking rates 13.89 and 14.45, respectively, in the two steel grades, compared to microcracking rates of 19.11 and 16.59 when the nitrogen 5 levels were above 0.0052% (52 ppm) by weight in the two steel grades. Referring to FIGS. 12 and 13, the effect of variation in casting speed on the microcracking of the 10 surfaces of the thin cast strip was studied in the same two grades of steel. As shown by FIGS. 12 and 13, the microcracking was markedly improved, showing mean sums of microcracking rates of 13.99 and 13.32, respectively, when the casting speed was below 71.7 meters per minute, 15 compared mean sums of microcracking rates of 18.29 and 18.93 when the casting speed was above 71.7 meters per minute. Referring to FIGS. 14 and 15, the effect of 20 variation in temperature of the molten metal in the tundish 23 on the microcracking of the surfaces of the thin cast strip was studied in the same two grades of steel. Temperature of the molten metal was measured in the tundish by a temperature probe. As shown by FIGS. 14 and 25 15, the microcracking was improved, showing mean sums of microcracking rates of 15.887 and 14.12, respectively, when cast at a tundish temperature of molten metal below 1612-C (2933.7-F) in both steel composition, compared mean sums of microcracking rates of 16.88 and 16.97 when the 30 tundish temperature of the molten metal was above 1612'C (2933.7-F). Referring to FIGS. 16 and 17, the applicant further analysed the data more detail on the effect of 35 casting speed on the degree of microcracking in the surfaces of thin cast strip of the same composition. In this analysis, the mean sum of microcracking rates on 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -18 strip were categorized at speeds below 67.8 meters per minute, between 67.8 and 70.92 meters per minute, between 70.92 and 73.44 meters per minute, between 73.44 and 76.68 meters per minute and 76.68 and higher meters per minute. 5 As shown in FIGS. 16 and 17, the mean sum of microcracking rates was improved when the casting speed was maintained below 76.68 meters per minute in both grades of steel compositions, while microcracking markedly increased to 24.9 and 26.9 in the mean sum of microcracking rates when 10 the casting speed was above 76.68 meters per minute. Referring to FIGS. 18 and 19, the effects on microcracking in the cast strip surfaces were studied for the interrelationship of the same range speeds of casting 15 with the ratios of manganese/sulfur above and below 250:1. As shown in FIGS. 18 and 19, there was a marked improvement in the mean sum of microcracking rate with manganese to sulfur ratios above 250:1 at all casting speeds, and particularly, when the casting speed was below 20 76.68 meters per minute, in both grades of steel compositions. Referring to FIGS. 20 and 21, the interrelationship of the manganese/silicon ratios above 25 and below 3.5:1 on microcracking rates in the cast strip surfaces with the same different casting speeds was analyzed. As shown in FIGS. 20 and 21, there was a marked improvement in the mean sums of microcracking rates at all casting speeds, when the manganese/silicon ratios were 30 above 3.5, and particularly when it was above 3.5:1 with a casting speed below 76.68 meters per minute. Referring to FIGS. 22 and 23, the interrelationship of carbon levels and casting speed for 35 the two different designations of steel composition was studied for effect on the microcracking rates of the thin cast strip. As shown in FIGS. 22 and 23, there was a 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -19 marked improvement in microcracking rates when the carbon level was below 0.035% at all casting speeds in both grades of steel compositions, and particularly when the casting speed was below 76.68 meters per minute. 5 The applicant also did statistical tests on the interrelationships between the variable studied, particularly on manganese/sulfur ratio, manganese/silicon ratio, casting speed, carbon content, nitrogen content, 10 and tundish temperature. These are reported in Table II below, with the 5 columns in the Table being outputs of the statistical analysis. Specifically, column 1 is the variable being looked at, column 2 (type 3 sum of squares) is a number that explains the amount of error in 15 variations in the variable in column 1, column 3 (df) is the degrees of freedom, column 4 (mean square) is the sum of squares (column 2) divided by the degrees of freedom (column 3), and column 5 (sig.) is the probability that the result is not significant. 20 TABLE II TESTS OF BETWEEN-SUBJECTS EFFECTS Dependent Variable: SumC 25 Type III Sum Source df Mean Square F Sig. of Squares ____ Corrected Model 195668.130 62 3155.938 22.115 .000 Intercept 698373.579 1 698373.579 4893.905 .000 Nom 2 TundishTemp 3211.298 1 3211.298 22.503 .000 Nom 2 Nitrogen 2886.082 1 2886.082 20.224 .000 Nom 2 CastSpeed 9880.504 1 9880.504 69.238 .000 Nom 2 Mn Si ratio 17924.057 1 17924.057 125.604 .000 Nom 2 Carbon 19607.330 1 19607.330 137.400 .000 Nom 2 Mn S Ratio 51643.646 1 51643.646 361.897 .000 Rom_2_TundishTemp 695.302 1 695.302 4.872 .027 * Nom 2 Nitrogen 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -20 Type III Sum Source df Mean Square F Sig. of Squares ____ Nom_2_TundishTemp 1205.539 1 1205.539 8.448 .004 * Nom 2 CastSpeed Nom 2 Nitrogen * -- e 739.559 1 739.559 5.183 .023 Nom 2 CastSpeed Nam_2_T undishTemp * Nom_2_Nitrogen * 326.054 1 326.054 2185 .131 Nom 2 CastSpeed Nom_2_TundishTemp 3.529 1 3.529 .025 .875 * Nom 2 Mn Si ratio Nom 2 Nitrogen * - *9,989 1 9.989 .070 .791 Nom 2 Mn Si ratio Nom_2_TundishTemp * Nom_2_Nitrogen * 50.546 1 50.546 .354 .552 Nom 2 Mn Si ratio Nom_2_CastSpeed 1307.667 1 1307.667 9.164 .002 Nom 2 Mn Si ratio Nom_2_TundishTemp * Nom_2_CastSpeed * 1442.565 1 1442.565 10.109 .001 Nom 2 Mn Si ratio Nom_2_Nitrogen * Nom_2_CastSpeed * 2236.165 1 2236.165 15.670 .000 Nom 2 Mn Si ratio om_2_TundishTemp * Nom_2_Nitrogen * 1,389 1 1.389 .010 .921 Nom_2_CastSpeed Nom 2 Mn Si ratio Nom_2_TundishTemp 609.876 1 609.876 4.274 .039 * Nom 2 Carbon iom 2 Nitrogen * 3714.569 1 3714.569 26.030 .000 Nom 2 Carbon Nom_2_TundishTemp * Nom_2_Nitrogen * 152.133 1 152.133 1,066 .302 Nom 2 Carbon Rom_2_CastSpeed 1692.383 1 1692.383 11.660 001 Nom 2 Carbon 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -21 Type III Sum Source df Mean Square F Sig. of Squares ____ Kom_2_TundishTemp * Nom_2_CastSpeed * 1095.570 1 1095.570 7.677 .006 Nom 2 Carbon Nom_2_Nitrogen * Nom_2_CastSpeed * .982 1 .982 .007 .934 Nom 2 Carbon m_2_TundishTemp * Nom_2_Nitrogen * 1.259 1 1.259 .009 .925 Nom_2_CastSpeed Nom 2 Carbon Rom_2_MnSi ratio * 19.373 1 19.373 .136 .713 Nom 2 Carbon Nom_2_TundishTemp * Nom_2_MnSi ratio 368.798 1 368.798 2.584 .108 * Nom 2 Carbon Nom_2_Nitrogen Nom_2_MnSi ratio * 1364.117 1 1364.117 9;559 .002 Nom 2 Carbon Nom_2_TundishTemp * Nom_2_Nitrogen * 743.037 1 743.037 5.207 .023 Nom_2_MnSi ratio * Nom 2 Carbon Nom_2_CastSpeed Nom_2_MnSi ratio * 573.013 1 573.013 4.015 .045 Nom 2 Carbon Nom_2_TundishTemp * Nom_2_CastSpeed * 815.529 1 815.529 5.715 .017 Nom_2_MnSi ratio Nom 2 Carbon Nom_2_Nitrogen Rom 2 CastSpeed * 264.656 1 264.656 1.855 .173 Nom_2_MnSi ratio Nom 2 Carbon Rom_2_TundishTemp 200.957 1 200.957 1.408 .235 * Nom_2_Nitrogen * 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -22 Type III Sum Source df Mean Square F Sig. of Squares ____ Rom_2_CastSpeed * Nom_2_MnSi ratio Nom 2 Carbon Rom 2TundishTemp 146.236 1 146.236 1.025 .311 * Nom 2 Mn S Ratio Nom 2 Nitrogen * -- *387.696 1 387.696 2.717 .099 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_Nitrogen * 831.865 1 831.865 5.829 .016 Nom 2 Mn S Ratio Nom_2_CastSpeed * 27.716 1 27.716 .194 .659 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_CastSpeed * 423.801 1 423.801 2.970 .085 Nom 2 Mn S Ratio Nom_2 _Nitrogen * Nom_2_CastSpeed * 417.891 1 417.891 2.928 .087 Nom 2 Mn S Ratio om_2_TundishTemp * Nom_2_Nitrogen * 6.805 1 6.805 .048 .827 Nom_2_CastSpeed * Nom 2 Mn S Ratio Nom_2_MnSi ratio * 4838.907 1 4838.907 33 909 .000 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_MnSi ratio 1269.925 1 1269.925 8.899 .003 * Nom 2 Mn S Ratio Nom_2_Nitrogen * Nom_2_MnSi ratio * 484.197 1 484.197 3.393 .066 Nom 2 Mn S Ratio om_2_TundishTemp * Nom_2_Nitrogen * 486.009 1 486.009 3,406 .065 Nom_2_MnSi ratio Nom 2 Mn S Ratio Nom_2_CastSpeed 536.336 1 536.336 3.758 .053 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -23 Type III Sum Source df Mean Square F Sig. of Squares ____ Rom_2_MnSi ratio * Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom 2 CastSpeed * -- 14.180 1 14.180 .099 .753 Nom_2_MnSi ratio Nom 2 Mn S Ratio Nom_2_Nitrogen * Nom 2 CastSpeed * 1602.869 1 1602.869 11.232 .001 Nom_2_MnSi ratio Nom 2 Mn S Ratio om_2_TundishTemp * Nom_2_Nitrogen * Nom_2_CastSpeed * 20.909 1 20.909 .147 .702 Nom _2_MnSi ratio_ Nom 2 Mn S Ratio Nom 2 Carbon 572.876 1 572.876 4.014 .045 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_Carbon * 686.005 1 686.005 4,807 .028 Nom 2 Mn S Ratio Nom_2_Nitrogen * Nom_2_Carbon * 242.113 1 242.113 1.697 .193 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom 2 Nitrogen 194178 1 194.178 1.361 .243 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_CastSpeed * Nom_2_Carbon * 198.290 1 198.290 1.390 .239 Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_CastSpeed * 2.489 1 2.489 .017 .895 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_Nitrogen * 252.648 1 252.648 1.770 .183 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -24 Type III Sum Source df Mean Square F Sig. of Squares ____ Kom_2_CastSpeed * Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_Nitrogen * Nom_2_CastSpeed * 640.454 1 640.454 4,488 .034 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_MnSi ratio Nom_2_Carbon * 174.833 1 174.833 1.225 .268 Nom 2 Mn S Ratio om_2_TundishTemp * Nom_2_Mn Si ratio "_ N -M -S 1.303 1 1.303 .009 .924 * Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_Nitrogen * Nom_2_MnSi ratio * 167.640 1 167.640 1.175 .279 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_TundishTemp * Nom_2_Nitrogen * Nom_2_MnSi ratio * 138.327 1 138.327 .969 .325 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_CastSpeed * Nom 2 Mn Si ratio * 296.352 1 296.352 2.077 .150 Nom_2_Carbon * Nom 2 Mn S Ratio Nom_2_TundishTemp *Nom_2_CastSpeed* Nom_2_MnSi ratio * i 422.782 1 422.782 2.963 .085 Nom_2_Carbon * Nom 2 Mn S Ratio Nom 2 Nitrogen * 33.001 1 33.001 .231 .631 om_2_CastSpeed * 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -25 Type III Sum Source df Mean Square F Sig. of Squares ____ Rom_2_MnSi ratio * Nom_2_Carbon * Nom_2 Mn S Ratio Error 501171.975 3512 142.703 Total 626271.000 3575 Corrected Total 696840.105 3574 As shown in Table II, statistical correlations were found the particular levels of each of the parameters reposted above, namely manganese/sulfur ratio, 5 manganese/silicon ratio, casting speed, carbon content, nitrogen content, and tundish temperature. The continuously thin cast strip may be of low carbon steel, which may include 2.5% or less silicon, 0.5% 10 or less chromium, less than 0.005% by weight titanium, 2.0% or less manganese, 0.5% or less nickel, 0.25% or less molybdenum, and 1.0% or less aluminum, together with sulfur between 0.003 and 0.008% and phosphorus and other impurities at levels that normally occur in making carbon 15 steel by electric arc furnace. Low carbon steel, for example, may vary to have manganese content in the range 0.01% to 2.0% by weight, and silicon content in the range 0.01% to 2.5% by weight. In any event, the steel may have aluminum content of the order of 0.1% or less by weight, 20 and may be 0.06% or less by weight. In addition to or in the alternative, the steel may have a vanadium content of the order of 0.02% or less and a niobium content on the order of 0.01% or less. 25 <<<insert comprises para>>> While this invention has been described and illustrated with reference to various embodiments, it shall be understood that such description is by way of 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -26 illustration and not by way of limitation. Accordingly, the scope and content of the present invention are to be defined only by the terms of the appended claims. 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16

Claims (20)

1. A thin cast steel strip produced by continuous casting by steps comprising: 5 a) assembling a pair of internally cooled casting rolls having a nip therebetween and with confining closures adjacent the ends of the nip; b) introducing molten carbon steel having a carbon content of between 0.010% and 0.065% by weight, less 10 than 5.0% by weight chromium, at least 70 ppm of total oxygen and between 20 and 70 ppm of free oxygen, a silicon content of 2.5% by weight or less, a sulfur content of 0.008 % by weight or less, an average manganese to silicon ratio above 3.5:1 and an 15 average manganese to sulfur ratio above 250:1 between the pair of casting rolls to form a casting pool supported on the casting surfaces of the casting rolls; c) counter rotating the casting rolls to form 20 solidified metal shells on the casting surfaces of the casting rolls; and d) forming from said solidified shells thin steel strip downwardly through the nip between the casting rolls. 25

2. The thin cast steel strip as claimed in claim 1 having a carbon content between 0.025% and 0.065% by weight and produced by a molten steel having this carbon content. 30

3. The thin cast steel strip as claimed in claim 1 or claim 2 having a carbon content below 0.035% by weight and produced by a molten steel having this carbon content. 35

4. The thin cast steel strip as claimed in any one of the preceding claims having a titanium content less than 0.005% by weight and produced by a molten steel 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -28 having this titanium content.

5. The thin cast steel strip as claimed in any one of the preceding claims produced by a molten steel having 5 a total oxygen content of at least 100 ppm and a free oxygen content between 30 and 50 ppm in the casting pool.

6. The thin cast steel strip as claimed in any one of the preceding claims produced by a molten steel having 10 a nitrogen content less than 52 ppm in the casting pool.

7. The thin cast steel strip as claimed in any one of the preceding claims produced by casting the steel strip at a casting speed less than 76.68 meters per 15 minute.

8. The thin cast steel strip as claimed in any one of the preceding claims produced by maintaining a tundish temperature of the molten steel below 1612'C (2933.7'F). 20

9. The thin cast steel strip as claimed in any one of the preceding claims having a chromium content below 1.5% by weight and produced by a molten steel having this chromium content. 25

10. The thin cast steel strip as claimed in any one of the preceding claims having a chromium content below 0.5% by weight and produced by a molten steel having this chromium content. 30

11. The thin cast steel strip as claimed in any one of the preceding claims having, by weight, less than 0.1% aluminium, less than 0.005% titanium, less than 0.01% niobium, and less than 0.02% vanadium. 35

12. The thin cast steel strip as claimed in any one of the preceding claims produced by maintaining the sum of 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -29 the partial pressures of hydrogen and nitrogen in the casting pool to be less than 1.15 atmospheres.

13. The thin cast steel strip as claimed in any one 5 of the preceding claims having an average manganese to silicon ratio greater than 3.5:1 and produced by a molten steel having this manganese to silicon ratio.

14. A method of casting thin steel strip comprising: 10 a) assembling a pair of internally cooled casting rolls having a nip therebetween and with confining closures adjacent the ends of the nip; b) introducing molten carbon steel having a carbon content of between 0.010% and 0.065% by weight, less 15 than 5.0% by weight chromium, at least 70 ppm of total oxygen and between 20 and 70 ppm of free oxygen, a silicon content of 2.5% by weight or less, a sulfur content of 0.008 % by weight or less, an average manganese to silicon ratio above 3.5:1 and an 20 average manganese to sulfur ratio above 250:1 between the pair of casting rolls to form a casting pool supported on the casting surfaces of the casting rolls; c) counter rotating the casting rolls to form 25 solidified metal shells on the casting surfaces of the casting rolls; and d) forming from said solidified shells thin steel strip downwardly through the nip between the casting rolls. 30

15. The method of casting thin steel strip defined in claim 14 wherein step (b) comprises introducing molten carbon steel having an average manganese to silicon ratio in the strip greater than 3.5:1. 35

16. A thin steel strip produced by the steps comprising casting steel strip from molten steel having a 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16 -30 carbon content between 0.010% and 0.065% by weight, less than 5.0% by weight chromium, at least 70 ppm of total oxygen and between 20 and 70 ppm of free oxygen, a silicon content of 2.5% by weight or less, a sulfur content of 5 0.008 % by weight or less, an average manganese to silicon ratio above 3.5:1 and an average manganese to sulfur ratio above 250:1.

17. The thin steel strip as claimed in claim 16 10 wherein the steel strip is less than 5 mm in thickness.

18. The thin steel strip as claimed in claim 16 or claim 17 wherein the steel strip is less than 2.5 mm in thickness. 15

19. The thin steel strip as claimed in claim 19 wherein the steel strip is less than 5 mm in thickness.

20. The thin steel strip as claimed in claim 19 or 20 claim 20 wherein the steel strip is less than 2.5 mm in thickness. 75019181 (GHMatters) P72677.AU.1 PETAK 8/03/16