AU2012204139A1 - Bone growth particles and osteoinductive composition thereof - Google Patents

Abstract

This application relates to a biocompatible synthetic bone growth composition comprising a fibrillar 5 collagen component and a calcium phosphate component. The composition is formed into particles and then formed into a unitary article that may be provided at the site of a skeletal defect. An osteoinductive component may be further added, either before or after forming the unitary article. The composition may be formulated as a paste or putty and facilitates bone growth and/or repair.

Description

AUSTRALIA Patents Act COMPLETE SPECIFICATION (ORIGINAL) Class Int. Class Application Number: Lodged: Complete Specification Lodged: Accepted: Published: Priority Related Art: Name of Applicant: Zimmer Orthobiologics, Inc. Actual Inventor(s): Kevin J. Thorne Address for Service and Correspondence: PHILLIPS ORMONDE FITZPATRICK Patent and Trade Mark Attorneys 367 Collins Street Melbourne 3000 AUSTRALIA Invention Title: BONE GROWTH PARTICLES AND OSTEOINDUCTIVE COMPOSITION THEREOF Our Ref : 948417 POF Code: 221787/468597 The following statement is a full description of this invention, including the best method of performing it known to applicant(s): 6-016- BONE GROWTH PARTICLES AND OSTEOINDUCTIVE COMPOSITION THEREOF This present application is a divisional application of Australian Patent Application 2007334213, the entire contents of which are to be taken as incorporated herein by reference. FIELD OF INVENTION 5 The invention relates generally to a composition comprising bone growth particles, a method of making the composition, and a use of the composition in promoting bone growth. BACKGROUND The use of osteoinductive proteins or growth factors, such as bone morphogenetic proteins (BMPs), mitogenic growth factors, etc., improves clinical outcomes after surgical reconstructions of l0 skeletal undifferentiated perivascular connective tissue cells. Mitogenic growth factors target and accelerate the osteogenic activity of previously differentiated cells. Although advances have improved the biological activity of osteoinductive factors, their clinical application has been limited by the requirement for a superior tissue scaffold/delivery vehicle. Autologous bone grafts are the gold standard for restoring skeletal defects because they provide 15 both a natural tissue scaffold and osteoinductive growth factors. Allogenic grafts may also be used, such as demineralised bone matrices. For example, demineralised bone material can be prepared by grinding a bone, demineralising it with an acid solution, washing with a phosphate buffered solution, washing with ethanol and drying it. Demineralized bone material can also be obtained from a commercial bone or tissue bank (e.g. AlloSource, Denver CO). Because autogenic and allogenic sources of human bone are limited 20 and may be expensive or painful to obtain, the use of substitute materials is preferred. Numerous synthetic or modified natural materials have been experimentally evaluated as alternative delivery vehicles, and include but are not limited to products containing hydroxyapatites, tricalcium phosphates, aliphatic polyesters (poly(lactic) acids (PLA), poly(plycolic) acids (PGA), polycaprolactone (PCL), cancellous bone allografts, human fibrin, plaster of Paris, apatite, collastonite (calcium silicate), glass, ceramics, 25 titanium, devitalized bone matrix, non-collagenous proteins, collagen and autolyzed antigen extracted allogenic bone. However, these synthetic or modified natural materials have yet to result in delivery vehicles having osteoinductivity comparable to autograft or allograft bone sources, or having the capability to enhance the osteoinductivity of these or other osteoinductive materials. Alternate products are desirable. 30 SUMMARY OF INVENTION Biocompatible compositions that comprise bone growth particles, a method of making the compositions, and uses of the compositions in promoting bone growth are disclosed. One embodiment is a bone growth composition comprising particles of a unitary scaffold material including a fibrillar collagen component and an acidic calcium phosphate component, and an osteoinductive component. 35 The compositions may be formulated as pastes or putties. This provides ease of use and economy of product manufacture. Pastes and putties are soft masses with physical consistencies between a liquid and a solid. Pastes and putties are desirable for surgical bone repair as they can be more easily delivered to difficult surgical sites and molded in site into desired shapes. These products are desirable for the 1a reconstruction of skeletal defects, e.g., in spine, dental, and/or other orthopedic surgeries. They may be used as a substitute for autologous bone grafts or may be used in conjunction with autologous bone grafts. In one embodiment, engineered (i.e., synthetic) composite products that enhance the in vivo formation of bone tissue and preserves the availability, and thus the functional activity of osteoinductive 5 growth factors are disclosed. Local pH control enhances clinical efficacy of osteogenic proteins, and supplements local availability of essential bone components such as collagen, calcium, and phosphate. Moderately acidic microenvironments likely improve protein-stimulated osteoinduction by enhancing the rates of protein solubilization and protein release from collagen. Supplementing the local concentration of soluble (Ca 2 . and [PO4] ions enhances the quantity of bone produced, and increases rate of bone 10 formation by reducing dependence on essential ion diffusion from serum and other body fluids. The resultant increase in local concentration and cellular availability of bone morphogenetic proteins result In Improved acidic collagen delivery vehicles. One embodiment is a biocompatible synthetic bone growth composition comprising a particulate composite of a fibrillar collagen component and a calcium phosphate component. The collagen component 15 may be Insoluble collagen (e.g., crosslinked collagen or porous particles). The calcium phosphate component may be acidic calcium phosphate, such as monocalclum phosphate [Ca(H 2

PO

4 )2, calcium hydrogen phosphate dihydrate [CaHPO 4 2H 2 0], anhydrous calcium hydrogen phosphate [CaHPO 4 ], partially dehydrated calcium hydrogen phosphate [CaHPO 4 xH 2 O, where x is between and includes 0 and 2] and/or calcium pyrophosphate [2CaO-P20 5 . In one embodiment, the composition contains an 20 osteoinductlve component, e.g., a purified bone growth factor, a recombinant bone growth factor, a bone marrow component, a blood component, demineralized bone, autologous bone, bone marrow aspirate, etc. In one embodiment, the composition pH ranges from about pH 5 to about pH 7. Another embodiment Is a process for producing a bone growth composition. A collagen component Is combined with a calcium phosphate component to produce a mineralized collagen 25 component. The mineralized collagen component may be prepared as a collagen gel, which may be frozen and lyophilized into a product referred to as a sponge. Particles of the mineralized collagen component (e.g. sponge) may be prepared by grinding, milling, chopping and/or molding the mineralized collagen component. The particulate composition may be packaged as a kit that may include a device (e.g., container) for mixing the particles with a fluid. An osteoinductive component may be added, either before 30 or after forming the particles. Another embodiment is a method of facilitating bone growth in a patient by adding an osteoinductive component to a particulate mineralized collagen component and implanting the composition In the patient. The composition. may be injected into and/or molded to fit a surgical site. These and other embodiments will be further appreciated with respect to the following drawings, 35 description, and examples. BRIEF DESCRIPTION OF THE DRAWINGS FIG, 1 shows a schematic representation of a collagen scaffold. FIG. 2 shows a flow chart representing a process for making a mineralized collagen component. 2 DETAILED DESCRIPTION The basic elements required for bone formation include a three-dimensional, open-porosity tissue scaffold, cells, and osteoinductive signaling molecules to stimulate cell differentiation, proliferation and matrix formation. Successful bone formation requires that these elements be combined in a well 5 coordinated spatial and time dependent fashion. The relative contribution of each element may vary, e.g., according to differences in patient age, gender, health, systemic conditions, habits, anatomical location, etc. Embodiments for improved bone formation and healing include the following: biocompatible, open porous bone tissues scaffold, enhanced local concentration of soluble bone mineral elements such as 10 calcium and phosphate, and preserved osteoinductive protein solubility. Each is subsequently analyzed. A biocompatible, open-porous bone tissue scaffold restores function and/or regenerates bone by providing a temporary matrix for cell proliferation and extracellular matrix deposition with consequent bone in-growth until new bony tissue Is restored and/or regenerated. The matrix may also provide a template for vascularization of this tissue. The scaffold may actively participate In the regenerative process through the 15 release of growth differentiation factors. The macro and micro-structural properties of the scaffold Influence the survival, signaling, growth, propagation, and reorganization of cells. They may also influence cellular gene expression and phenotype preservation. The following properties contribute to scaffold characteristics for bone formation: cell blocompatlability, surface chemistry, biodegradability, porosity, and pore size. 20 In one embodiment, the composition comprises fibrillar collagen. Collagen Is the main protein of connective tissue In animals and the most abundant protein in mammals. Bone Is composed of strong, fibrillar bundles of collagen encased within a hard matrix of a calcium phosphate known as hydroxylapatite. Collagen is also a constituent in cartilage, tendon and other connective tissues. The collagen protein possesses a distinctive triple-helix tertiary structure of three polypeptide 25 chains supercolled about a common axis and linked by hydrogen bonds. At least nineteen distinct molecules have been classified as collagens, and specific types are associated with particular tissues. Collagen can be converted Into gelatin by boiling or treating with an acid. The solubility of collagen is affected by its conformation and extent of associations, whereby newly synthesized collagen chains are generally soluble but after formation of fibrils, they become essentially insoluble. 30 Collagen fibrils, referred to as fibrillar collagen, result from covalent cross-linking between the supercolled chains by an enzymatic mechanism that strengthens and stabilizes the chains. Fibrillar collagen may be obtained from native sources such as human or animal dermis, tendon, cartilage or bone. It is generally recovered by proteolytically degrading natural collagen crosslinks to produce tropocollagen. Tropocollagen, the basic amino acid component, is soluble with acidic solutions (in one embodiment, 35 between pH 3 to pH 4). These solutions can be cleaned and purified prior to collagen fiber reassembly by pH neutralization. Fibrillar collagen is generally less dense, less soluble, and swells more in solution than non-fibrillar collagen. 3 Due to its high degree of blocompatibility with the humanbody, collagen has been successfully used In a variety of medical and dental applications for many years with minimal adverse responses. During its manufacture, potentially antigenic portions of the collagen molecule are removed, resulting in a product that is highly biocompatible and well-tolerated by the tissue. Collagen is also chemotactic for 5 'fibroblasts and other cells involved In bone tissue repair. Collagen blocompatibility ensures that the products are well integrated In the host tissue without eliciting an immune response. Collagen used in the particulate composition may be from any source. These include natural sources such as human and mammalian tissues, and synthetic sources manufactured using recombinant technologies. It may be of any type (e.g., collagen Types 1, 11, 111, X and/or gelatin). In one embodiment, 10 collagen used Is Type I collagen. In one embodiment, collagen is derived from bovine dermis. In one embodiment, fibrillar collagen is derived from bovine dermis manufactured by Kensey Nash Corporation (Exton PA) under the name Semed F. In one embodiment, fibrillar collagen may be obtained from Kensey Nash Corporation under the name P1000. In one embodiment, the particles comprise at least about 33 percent by dry weight collagen. In another embodiment, the particles comprise from about 25 percent to 15 about 75 percent dry weight collagen. The surface chemistry of the scaffold can control and affect cellular adhesion. It can also Influence the solubility and availability of proteins essential for intracellular signaling. Intracellular signaling maximizes osteolnductivity through controlled cellular differentiation, proliferation, and stimulation. Collagen fabricates the disclosed structural scaffold and provides a physical and chemical milieu 20 favorable to bone regeneration. Collagen also provides a favorable extracellular matrix for bone forming cells, e.g., osteoblasts, osteoclasts, osteocytes, etc. The bone forming cells' natural affinity for the collagen matrix has been demonstrated to favorably influence the function and signaling required for normal cellular activity. The degradation rate of the scaffold should ideally match the bone-healing rate. Slower 25 degradation rates can hinder the rate of remodeled, load-bearing bone formation. Faster degradation can result in unhealed defects. The solubility and resorption of collagen Is affected by its conformation and the degree of collagen cross-linking. The in vivo solubility and resorption of collagen Is also Influenced by the local concentration of proteolytic agents and vascularity at the site. 30 In one embodiment, the composition is crosslinked to control the solubility and the extent and rate of collagen resorption. Collagen crosslinking may occur by various methods such as dehydrothermal (DHT), UV light exposure, chemical crosslinking with aldehydes (i.e. glyceraldehyde, formaldehyde, glutaraldehyde), carbodlimides and various amino acids. The crosslinking conditions will preserve the in vivo lifetime of the composition for up to about twelve weeks, allowing It to function as a scaffold for bone 35 healing. Collagen is eventually absorbed Into the surrounding tissue by host enzymes. In one embodiment, uncrosslinked collagen may be a component of the composition. Scaffolds desirably posses an open pore, fully interconnected geometry to allow homogeneous and rapid cell In-growth, and facilitate vascularization of the construct from the surrounding tissue. 4 To this end, the total pore volume porosity of the scaffold simulates that of cancellous bone. Cancellous bone is a highly porous structure (about 50 vol. % to about 90 vol. %) arranged in a sponge-like form, with a honeycomb of branching bars, plates, and rods of various sizes called trabeculae. The synthetic scaffold must ensure pore IntercQnnectivity to allow for the diffusion of nutrients and gases and for 5 the removal of metabolic waste resulting from the activity of the cells within the scaffold. It Is generally accepted by one skilled in the art that the pore diameters should be within the range of about 200 prm to about 900 pm range for ideal bone formation. Smaller pores can occlude and restrict cellular penetration, matrix production, and tissue vascularization. Larger pores can detrimentally influence the mechanical properties of the structural scaffold. 10 The disclosed method produces a synthetic scaffold that mimics the natural structural design of bone for bone formation. In one embodiment, the scaffold is fabricated using fibrillar collagen. Fibrillar collagen Is the cytoskeletal filament within the matrix of all tissues and organs. In addition to being a fundamental element of natural bone, fibrillar collagen allows the formation of a scaffold with high surface area and an interconnected network of high porosity, as shown In FIG 1. The total pore volume is made up 15 of both micropores 10, which is the space between collagen strands within the fibril, and macropores 12, which Is the space between collagen fibrils. In one embodiment, the composition matches the porosity of cancellous bone, with total pore volumes ranging between about 50 vol.% to about 97 vol.% and pore diameters ranging between 1 pm and 1000 pm. Enhancing local concentration of soluble bone mineral elements, such as [Ca 2 ] and/or [PO 4 ], 20 contributes to improved bone formation and healing. Calcium phosphate based products have been used for bone repair for over 80 years. Their many desirable properties include similarity In composition to bone mineral, bloactlvity (ability to form apatitic or carbonated hydroxylapatite on their surfaces), ability to promote cellular function and expression, ability to form a direct strong Interface with bone, and osteoconductivity (ability to provide a scaffold or template for 25 the formation of new bone). Commercially available calcium phosphate blomaterials differ in origin (e.g., natural or synthetic), composition (e.g.. hydroxylapatite, beta-tricalcium phosphate, and biphasic calcium phosphate), physical forms (e.g., particulates, blocks, cements, coatings on metal Implants, composites with polymers), and physicochemical properties. Subtle differences in chemical composition and crystalline structure may significantly impact their in vivo physical and biological performance. 30 The disclosed composition and method supplements the local availability of essential soluble bone components, e.g., calcium and phosphate. Biologically compatible, sparingly soluble calcium phosphates are suitable supplements to locally increase the supply of soluble calcium [Can] and phosphate (PO 4 3] Ions. As shown in Table 1, calcium phosphate salts solubilize at different equilibrium Ionic concentrations, where the local supplemented concentrations of calcium (Ca 2 ] and phosphate [P0 4 ] ons can vary by 35 more than four orders of magnitude. Calcium hydrogen phosphate (dical), an example of a calcium phosphate additive used in the disclosed composition, provides about 200 to about 300 times the concentration of soluble mineral elements in comparison to conventional calcium phosphates, such as 5 tricalcium phosphate (TCP) (Cas(PO 4

)

2 ) or tetracalclum phosphate (TTCP) (Ca 4 (PO4) 2

(OH)

2 ) or calcium hydroxyapatite (HA) (Ca 6 (P0 4

)

3 (OH)). Table 1. Equilibrium solubility of calcium and phosphate ions from several different biologically compatible calcium phosphate salts. Equilibrium Equilibrium Insoluble fraction [Caa* [PO'] . [200mg/cc] Plasma 2,200.0 pM 1,100.0 PM Ca(H 2 PO4)2 (Monocal) 14,300.0 pM 28,600.0 pM 97.0000 wt.% CaHPO 4 (Dlcal) 480.Q pM 480.0 pM 99.9700 wt.% Ca 3

(PO

4

)

2 (TCP) 1.4 pM 0.9 pM 99.9999 wt.% Ca 5 (P0 4

)

3 (OH) (HA) 2.2 pM 1.3 pM 99.9999 wt.% Cal(PO 4

)

2

(OH)

2 (TTCP) 28.2 pM 14.1 pM 99.9994 wt.% 5 Dial Is soluble and does not require osteoclastic resorption for biodegradation. It resorbs slowly enough that products can be designed to supplement the soluble mineral Ion concentration for several weeks. Local supplementation of soluble [Ca 2 *I and (PO 3 ,1 ions enhanced the quantity of bone produced 10 and Increased Its rate of formation in animals. Without being bound by a specific theory, it is believed that the use of a soluble form a calcium phosphate reduces the healing rate dependence on local osteoclastic resorption and essential ion diffusion from plasma fluids. The method and composition preserved osteoinductive protein solubility. OsteoInduction Is the process by which stem cells and osteoprogenitor cells are recruited to a bone-healing site and are 15 stimulated to undergo the osteogenic differentiation pathway. Classic synthetic, biodegradable scaffolds are only osteoconductive and require combination with an inductive bone-forming agent to stimulate and accelerate bone healing. Bone growth factor cytokines, also known as bone morphogenetic proteins (BMPs), are entrapped at high concentration within bone and are secreted by many bone-forming cell types. The primary function 20 of BMPs is cellular signaling. Intracellular signaling occurs through the binding of a soluble growth factor to a specific cell receptor site. This signal pathway stimulates several different and important bone healing events, including the proliferation, migration, and differentiation of bone forming cells. The cells are, in turn, responsible for the synthesis of other proteins and growth factors that are important for regulating and controlling bone tissue formation. Although there is a vast array of BMPs described and known to one 25 skilled in the art, BMPs 2, 4, 6 and 7 are generally considered to be the most osteoinductive. 6 The disclosed composition provides biodegradable synthetic bone graft materials to specifically preserve the solubility of osteoinductive proteins. Various forms of calcium phosphates are known to have different chemical affinities for endogenous osteoinductive proteins (e.g., BMPs). Calcium phosphates such as TCP and HA are known to strongly bind acid-soluble BMPs because of their alkaline surface 5 chemistry. In contrast, dical presents a moderately acidic surface chemistry that will not bind acidic proteins. Because of its enhanced solubility, it can also moderately buffer the local environment to an acidic range that further preserves osteoinductive BMP solubility. An In vitro study assessed the Influence of variable composition calcium phosphate salts on the soluble concentration of osteolnductive proteins. The residual concentration of soluble recombinant BMP-2 10 was measured after exposing a controlled concentration aliquot to an equi-molar quantity of calcium phosphate salt. As shown In Table 2, moderately acidic calcium phosphates salts, such as dical, preserved the highest soluble concentration of osteoinductive proteins. The enhanced local concentration and cellular availability of bone morphogenetic proteins (BMPs) better stimulate bone formation. Table 2. Equilibrium solubility of osteoinductive recombinant human BMP-2 protein in the presence 15 of equimolar concentrations of various calcium phosphates. (rhBMP-2] [rhBMP-2] mg/mil % Control 15.0 100% Ca(H 2

PO

4

)

2 (monocal) 15.0 100% CaHPO 4 (dical) 11.4 76% Caa(PO 4

)

2 (TCP) 3.5 23% CaS(PO4)3(OH) (HA) 2.3 15% In one embodiment, an additive (e.g., an osteoinductive component) formulated as a putty or paste is included in the biocompatible composition that facilitates skeletal regeneration and provides a scaffold for new bone growth. Use of synthetic components reduces the potential of disease transfer and immune 20 system incompatibilities. The terms putty and paste are qualitative and generally describe a composition that is moldable/formable and flowable, respectively. When the term paste Is used to describe the composition including a liquid, it Is to be understood that a putty may also be formed, generally by decreasing the volume of liquid mixed with the composition. In one embodiment, the composition forms a paste that enhances the formation of bone tissue and 25 increases the availability, and thus the functional activity of ostaoinductive growth factors. It is provided at a surgical site during reconstruction of a skeletal defect. For example, the paste may be used In spine, dental, reconstructive, trauma, and other orthopedic surgeries. The paste may be used as a substitute for or additive to autologous bone grafts. Although the composition Is synthetic, it may Include natural 7 components, e.g., bovine collagen, and/or be combined with natural components, e.g., bone marrow aspirate. The paste controls pH to enhance clinical efficacy of osteoinductive proteins, and supplements local availability of bone components such as collagen, calcium, and phosphate. Without being. bound by a 5 specific theory and as analyzed above, moderately acidic microenvironments likely improve protein stimulated osteoinduction by enhancing the degree of protein solubilization and protein release from collagen. Supplementing the local concentration of soluble (Ca 2 *] and (P0 4 3 1 Ions increases the rate of bone formation by reducing dependence on Ion diffusion from serum and other body fluids. The resultant increase in local concentration of collagen and mineral building blocks, coupled with the enhanced cellular 10 availability of bone morphogenetic proteins, Improves acidic collagen delivery vehicles. In one embodiment, the composition formulated as a paste is both osteoinductive, i.e., it initiates or Induces bone growth, and osteoconductive, I.e., it facilitates already initiated bone growth but does not Itself initiate bone growth. Its osteoinductive effect arises, for example, from osteoinductive factors present in the liquid, e.g., bone marrow aspirate, used to make the paste. The composition is also osteoinductive in 15 that it does not Inhibit or diminish the solubility of osteoinductive factors, such as BMPs, due to the ability of the composition to induce a local pH decrease, as analyzed above. Its osteoconductive effect arises from provision of a collagen scaffold and source of bone growth materials. In one embodiment, exogenous osteoinductive factors are included as additives in the composition. A variety of calcium phosphate salts, represented by the general chemical formula xCaO,P 2 0 5 , may 20 be used to simultaneously supplement the local [Ca 2 . and [P0 4 3 1 ion concentrations and to act as short term biologic buffers. In one embodiment, the composition includes a particulate formed from crosslinked collagen and calcium phosphate. In another embodiment, a method of making the particulate composition is provided. Collagen and calcium phosphate are combined, dried, crosslinked, and particulated as subsequently described. 25 In another embodiment, a method of using the collagen and calcium phosphate particles Is disclosed. The particulate composition can be combined with a fluid, for example bone marrow aspirate, to create a paste. The paste Is then injected, manually applied, or otherwise delivered to a site of a bone. In one embodiment, the paste is an injectible bone void filler. The paste provides improved handling and delivery capabilities, allowing a surgeon to introduce the composition Into complex geometry bone defects. 30 The paste components are fully resorbable and stimulate bone regeneration in a manner similar to that achieved with natural bone. In one embodiment, the composition contains particulate, fibrillar collagen and calcium phosphate. The composition can be combined with a liquid such as biological fluids (e.g., bone marrow aspirate, whole blood, serum, plasma, etc.) to form a paste. The paste Is then used as an injectible and/or conformable 35 (i.e., moldable) bone-grafting material for primary applications in, e.g., spine fusion, dental furcation augmentation, fracture repair, etc. In one embodiment, where a fibrillar collagen component is combined with a calcium phosphate component to produce a mineralized collagen component, porous particles of the mineralized collagen 8 component may be prepared. In one embodiment, particle porosity measured as the total open pore volume is greater than about 90 percent by volume. In another embodiment, the total open pore volume within the particle ranges from about 50 percent to about 97 percent. In one embodiment, particle pore size ranges from about 1 Im to about 1000 lim. In another embodiment, particle pore sizes range from 5 about 125 Pm to about 300 pm. In one embodiment,.the particle size ranges from about 100 pm to about 840 pm. A variety of calcium phosphate salts, represented by the general chemical formula Cax(PO 4 )y(0,H,H 2 O), may be used in the product composition to simultaneously supplement the local concentration of [Ca 2 l and [P0 4 ] ion concentrations and to act as short-term biologic buffers. Calcium 10 phosphates that may be used In the composition include monocalclum phosphate (monocal) [Ca(H 2

PO

4

)

2 ], calcium hydrogen phosphate (dical) [CaHP04], calcium pyrophosphate [2CaO-P 2 0 5 , tricalcium phosphate [3CaO-P 2 0s], hydroxyapatite [3.33CaO-P 2 0 5

(OH)

2 (polycrystalline and amorphous compositions)], tetracalcium phosphate [4CaO-P 2 0s] and calcium carbonate [CaCO 3 (aragonite), CaCO 3 (calcite)]. In one embodiment, the composition comprises an acidic mixture of calcium phosphates. Acidic calcium 15 phosphate refers to those compositions, with composite calcium (x) / phosphate (y) below 1.5, that either present acidic surface chemistries or solubilize in aqueous solution to a sufficient extent to cause solution buffering to an acidic value (pH<7.0). In one embodiment, the acidic calcium phosphate is calcium hydrogen phosphate dehydrate [CaHPO 4 -2H 2 01. In one embodiment, the acidic calcium phosphate is anhydrous calcium hydrogen phosphate [CaHPO 4 ]. In one embodiment, the calcium phosphate of the 20 composition is greater than about 25 percent by dry weight. In another embodiment, the calcium phosphate of the particulate composition is about 67 percent by dry weight. The composition may further comprise additives such as bloactive agents, e.g., agents that exhibit biologic activity, and liquids. For example, agents that are osteolnductive and/or osteogenic may be included. As previously stated, osteoinductive agents stimulate bone growth. Examples of osteolnductive 25 agents include bone growth factors, bone marrow components, blood components, and bone components. Bone growth factors may be purified or recombinant and include bone morphogenetic protein (BMP). Bone marrow aspirates (BMA) may be used in the composition because they contain osteoinductive agents such as bone growth factors and mesenchymal stem cells. Mesenchymal stem cells (MSCs) are multi-potent cells capable of differentiating along several lineage pathways to aid In the production of bone. MSCs are 30 considered as a readily available source of cells for many tissue engineering and regenerative medicine applications. For these reasons, osteolnductive proteins and MSCs have been used to sUpplement the performance of osteoconductive bone formation scaffolds as replacements for autologous and allogenelc bone grafts, In one embodiment, bone marrow aspirate is included in the composition. Blood components such 35 as whole blood and platelet-rich plasma, may be included In the composition. OsteoInductive bone components that may be included in the composition include demineralized bone and autologous bone. Demineralized bone refers to bone that has been treated to remove all or a majority of the calcium phosphate mineral components. Demineralization Is usually performed by exposing powdered bone, from 9 any human or mammalian source, to acidic solutions (i.e., HCI, acetic acid, ethylene diamine tetracetic acid) with a pH less than about 4. Bone that has not been demineralized may be included in the composition and also includes bone derived from an autologous or mammalian source. Adding liquid to the composition results In a paste or putty, defined as soft masses with physical 5 consistencies between a liquid and a solid. The liquid may be a biological fluid such as blood, plasma, serum, bone marrow, etc., or may be a buffer or may be capable of buffering to the physiological pH values of human serum (pH 7.1 to pH 7.4). Examples of buffers are known to one skilled In the art and Include Tris and phosphate-buffered saline. In one embodiment, the composition has a pH In the range of about pH 5 to about pH 7.4. In another embodiment, the composition has a pH in the range of about pH 5.5 to 10 about pH 6.9. More than one liquid may be Included in the composition. For example, the composition may include bone marrow aspirate and a buffering salt solution. The liquid may also include blocompatible liquids such as water, saline, glycerin, surfactants, carboxylic acids, dimethylsulfoxide, and/or tetrahydrofuran. In one embodiment, the liquid is greater than about 25 percent by volume of the composition. In another embodiment, the liquid comprises from about 75 percent to about 90 percent by 15 volume of the composition. Additionally, natural and synthetic polymers such aliphatic polyesters, polyethylene glycols, polyanhydrides, dextran polymers, and/or polymeric orthophosphates may be Included in the composition. In one embodiment, a process for producing a particulate mineralized collagen composition comprising collagen and calcium phosphate is provided. In one embodiment, a crosslinked collagen and 20 calcium phosphate composition is prepared and is then formed into particles, as shown in FIG. 2. Initially, collagen and calcium phosphate are combined with an acid, e.g. HCI, to create a slurry. The slurry may also be a gel due to the presence of collagen In an acidic environment. The types of collagen that may be used are described above and Include bovine dermal fibrillar collagen. Suitable calcium phosphate includes acidic calcium phosphate such as monocalclum phosphate [Ca(H2PO 4 )], calcium hydrogen 25 phosphate [CaHPO 4 ], and/or calcium pyrophosphate [2CaO-P 2 0 5 1. In one embodiment, about 33 percent by weight of collagen is combined with about 67 percent by weight calcium phosphate. The combination Is then subjected to freezing, lyophilization, and crosslinking. In one embodiment, the composition is frozen at about -80'C for about two hours. In. one embodiment, the composition is lyophilized for at least about sixteen hours. In another embodiment, the composition is lyophilized for at 30 least about 48 hours. The composition may be crosslinked. Crosslinking may be effected by a variety of methods known to one skilled in the art, including but not limited to dehydrothermal (DHT) crosslinking. In DHT crosslinking, the composition is placed in a vacuum oven chamber, the chamber is evacuated to create a vacuum, and the composition is heated for a period of time, In one embodiment, the composition is heated 35 to about 110<C. In one embodiment, the composition is heated in a vacuum oven for about 48 hours. Following freezing, lyophilization, and crosslinking, the solid composition is formed into particles. Methods of forming particles are known to one skilled in the art and Include, but are not limited to, grinding, milling, chopping, and/or molding, In one embodiment, particles are formed by milling the solid 10 composition. Milling may occur using a Wiley mill (Thomas Sclentific, Swedesboro NJ). The mesh size on the mill directs the size of the resultant particles. In one embodiment, a -20 mesh Is used that creates particles in the range of about 100 im to about 840 Wn. The particles may be sized by, for example, sieving. At any point in the process, additional components may be added to the composition, as 5 described above. For example, an osteoinductive component can be added prior to forming the articles. The composition may be provided as a kit. In one embodiment, the kit includes the composition described above, and may further Include other components. These include a receptacle such as a plastic container in which to place the composition and in which to add liquid to form the composition into a paste or putty, a mixing implement such as a spatula, stir rod, etc., a disposable syringe barrel without a needle in 10 which to place and deliver the mixed paste, instructions for formulating and/or using the composition, etc. In another embodiment, a method of facilitating bone growth is provided. In one embodiment, the method includes adding at least one osteoinductive component such as a purified bone growth factor, a recombinant bone growth factor, a bone marrow component, a blood component, demineralized bone, autologous bone, etc., to the particulate composition previously described. In embodiments where the 15 osteoinductive component is bone marrow aspirate, blood, or a blood component, It may be acutely obtained and added to the composition (e.g., blood and/or bone marrow may be obtained from the same surgical site for repairing the defect). Adding the osteoinductive component(s) and/or another liquid to the composition, with stirring, results in a paste or putty, which is provided to the desired anatomical site of the patient. In one embodiment, the paste is loaded Into the barrel of a disposable 5 cc syringe, without a 20 needle attached, and is extruded through the barrel aperture to the desired anatomical site. In another embodiment, the putty is manipulated or formed into a configuration of desired size, shape, length, etc., either manually or by instrumentation, and gently pressed on and/or In the desired anatomical site. The site Is desirably prepared to expose healthy bleeding bone, facilitating subsequent bone growth. The method may be performed using minimally Invasive procedures known to one skilled in the art. The 25 method may be used in at least partially filling bone voids and/or gaps of the skeletal system (i.e., extremitles, pelvis, spine, oral cavity) that are not intrinsic to the stability of the bone structure. These voids and/or gaps may be a result of trauma, either natural or by surgical creation. The paste Is gently provided on and/or in the void and/or gap. The paste Is resorbed by the body during the healing process (over days, weeks, and months). The paste may be molded into the bone void or defect by manipulating either 30 manually or using an instrument (e.g., spatula, syringe, probe, cannula, etc.). The following examples further illustrate embodiments of the invention. EXAMPLE 1 A composite collagen and calcium phosphate gel dispersion was prepared (5 vol.% collagen gel) by weighing 6 g collagen. A 10 mM HCI solution was volumetrically measured (246 ml) to prepare a 35 5 vo.% gel. Twelve g sterilized dicalcium phosphate {CaHPO 4 ] powder (66.7 wt.% calcium phosphate) was added and stirred to a uniform consistency. The combination was mixed, for example, by repeated shear material transport, until a uniform collagen gel dispersion of moderate viscosity (about 1,000 P to about 1,500 P) was obtained. 11 About 16.5 ml of the collagen and calcium phosphate gel dispersion was then cast Into an autoclaved TEFLON® mold of 4.5 cm (L) x 1.7 cm (W) x 2.t cm (H), with removable upper and lower autoclaved glass plates. The collagen gel dispersion was Injected Into the mold with the lower glass plate attached and the composition was evenly spread using a spatula. The upper autoclaved glass plate was 5 then-fixed in contact with the dispersion and the plates were secured using countersunk flat head screws. The mold was then maintained at -80 0 C for at least one hour. After freezing, the glass plates were removed from both sides of the mold backing and the mold containing the frozen product was placed in a sterile paper autoclave pouch and frozen within a glass lyophilization vessel for two hours. 10 The frozen composition was then lyophilized (i.e. freeze-dried) at room temperature in a Laboratory Freeze Dryer (Freezemobile 25EL, VIrTis Inc., Gardiner NY) for at least 24 hours. The lyophilization vessel containing the product was attached to the vacuum port of the Freezemobile in operation with a condenser temperature of -50*C or below, and a manifold pressure of 104 mm Hg or less. The vacuum port to the vessel was opened exposing the frozen product to pressure sufficient to freeze dry the product within 24 15 hours at room temperature. The composition was then crosslinked via a dehydrothermal (OHT) process. The composition was removed from the mold and placed onto an autoclaved aluminum pan. The samples were then placed into a vacuum oven. The gas vents were closed and the chamber was evacuated to 103 mm Hg. The vacuum chamber was heated to 110*C. After 48 hours of constant temperature heating, the samples were cooled 20 to room temperature (about 20 0 C to about 220C) under vacuum. After the composition bar cooled, the chamber was repressurized with 0.2 micron filtered air. The composition bar was removed using sterile forceps and stored in a sterile paper autoclave pouch. The samples were then processed Into particles. Samples were placed Into the hopper of a clean Wiley Mini-Mill (Thomas Scientific, Swedesboro NJ), and milled at about 1,700 rpm. The samples were 25 swept around by rotor until cut to sufficient fineness to pass through the sieve top of a delivery tube that formed the bottom of the chamber. The final product was collected using a 20 mesh delivery unit located under the mill blades. In one embodiment, the particles were also subjected to compression molding to form storage disks. The particles were weighed and Introduced Into a cylindrical mold to produce solid disks through 30 uni-axial compression. The compression pressure was optimized to simultaneously produce a solid product. This product resisted breakage during normal shipping and facilitated rapid product mixing (less than two min). EXAMPLE 2 Prior to opening a container containing particles of the above composition, the volume of a bone 35 void to be repaired was determined. Based on the bone void, an appropriate volume of non-human animal blood was obtained, using a ratio of 0.75 : 1 blood or bone marrow aspirate : bone void volume. Appropriate volumes of liquid were added, as subsequently described, to obtain products of desired cohesive consistency (e.g. paste). As one example, per 1 cc dry particle volume, 0.75 ml whole blood was 12 added to obtain a cohesive putty, or 0.85 ml whole blood was added to obtain a paste. As another example, per 1 cc dry particle volume, 0.75 ml bone marrow aspirate was added to obtain a cohesive putt, or 0.85 ml bone marrow aspirate was added to obtain a paste. Immediately prior to implantation on an isolated bone, the liquid was mixed with the composition to obtain a paste of desired consistency. The bone void site was irrigated as needed and the paste was packed into the bone void. The site was sealed with surrounding soft tissue as needed, e.g. to close the.wound and restore soft tissue configuration. Rigid fixation of the defect site stabilized the bone void. It should be understood that the embodiments and examples described are only illustrative and are not limiting in any way. Therefore, various changes, modifications or alterations to these embodiments may be made or resorted to without departing from the spirit of the invention and the scope of the following claims. Throughout the description and claims of this specification the word "comprise" and variations of that word, such as "comprises" and "comprising", are not intended to exclude other additives, components, integers or steps. 13

Claims (20)

1. A bone growth composition comprising 5 particles of a unitary scaffold material including a fibrillar collagen component and an acidic calcium phosphate component, and an osteoinductive component.

2. The composition of any preceding claim wherein the collagen component comprises 10 insoluble collagen.

3. The composition of any preceding claim wherein the collagen component comprises crosslinked collagen. 15

4. The composition of any preceding claim wherein the composition comprises 25 - 75 dry weight percent collagen component.

5. The composition of any preceding claim wherein the composition is porous. ?0

6. The composition of any preceding claim wherein the calcium phosphate component comprises an acidic mixture of calcium phosphates.

7. The composition of any preceding claim wherein the acidic calcium phosphate component comprises monocalcium phosphate [Ca(H 2 PO 4 ) 2 1,], calcium hydrogen phosphate [CaHPO4], 25 calcium pyrophosphate [2CaO-P 2 0s], and combinations thereof.

8. The composition of any preceding claim wherein the acidic calcium phosphate component comprises calcium hydrogen phosphate [CaHPO 4 ]. 30

9. The composition of any preceding claim wherein the calcium phosphate component exceeds 25 dry weight percent.

10. The composition of any preceding claim wherein the composition is in the form of a paste or putty. 35 14

11. The composition of any preceding claim wherein the osteoinductive component comprises a bone growth factor, a bone marrow component, a blood component, a bone component and combinations thereof. 5

12. The composition of any preceding claim wherein the osteoinductive component comprises a bone marrow component including bone marrow aspirate, mesenchymal stem cells and combinations thereof.

13. The composition of any preceding claim wherein the osteoinductive component comprises a 10 bone component including demineralized bone, autologous bone and combinations thereof.

14. The composition any preceding claim wherein the osteoinductive component includes a liquid comprising bone marrow aspirate, whole blood, serum, plasma or platelet-rich plasma. 15

15. The composition of any preceding claim further comprising a liquid.

16. The composition of claim 15 wherein the liquid comprises a biocompatible liquid including water, saline, glycerin, surfactants, carboxylic acids, dimethylsulfoxide, tetrahydrofuran and ?0 combinations thereof.

17. The composition of claim 16 wherein the biocompatible liquid comprises saline.

18. The composition of any one of claim 14, 15, 16 or 17 wherein the liquid exceeds 25 volume 25 percent of the composition.

19. The composition of any preceding claim wherein the composition has a pH between pH 5 to pH 7. 30

20. A composition according to claim 1 substantially as hereinbefore described with reference to any one of the Examples. 15