AU2012203462B2 - Crosslaminate of oriented films and methods and apparatus for manufacturing same - Google Patents

Abstract

A method of producing a biaxially oriented film including a thermoplastic polymer material, where the method includes the steps of: sequential stretching the film using at least one pair of mutually 5 intermeshing grooved rollers including alternating grooves and crests, where the rollers are either circular or helical and are adapted to stretch the film in a direction perpendicular to the machine direction or forming a small angle to the direction perpendicular to the machine direction, and where the crests on at least one of the rollers in the at least one pair of rollers have edges which are 10 sufficiently sharp to produce thinner webs on each side of the crest edges during stretching, and where a distance between each crest on one roller and adjacent crests on the other roller is sufficient to avoid the film being squeezed therebetween, and where the intermeshing between the grooved rollers is limited such that two adjacent thinner webs formed on the edges do not grow together to 15 form a single thinner web during the passage of the film between the mutually intermeshing grooved rollers, and prior to, subsequent to, or prior to and subsequent to the sequential stretching, continuously stretching the film substantially in its longitudinal direction, to form a film including a pattern of parallel, continuous or substantially 20 continuous, linearly extending thinner webs oriented substantially in a transverse film direction and between the thinner webs thicker bosses and which are oriented substantially in a longitudinal film direction.

Description

1 CROSSLAMINATE OF ORIENTED FILMS AND METHODS AND APPARATUS FOR MANUFACTURING SAME The present invention concerns crosslaminates, i.e. laminates of films of which at least two are unisaxially or unbalanced biaxially oriented, and in which the main 5 direction of orientation in one of these films crosses the main direction in the other one. Crosslaminates of oriented films from synthetic polymer materials have been commercially produced since 1968, then mainly as described in GB-A-0792976 (Rasmussen) of May 23,1955. To the inventor's knowledge the total annual worldwide production today amounts to about 30,000 tons. The crosslaminate is used in 10 particular as industrial bags, coversheet, tarpaulins, pond-liners and similar products. Compared to generally unoriented films, crosslaminates exhibit very improved strength properties, seen in relation to the square metre weight, and since the raw material price is the most important part of the costprice, the crosslamination technology can serve to reduce the cost by reduction of weight. Compared to biaxially 15 oriented film, crosslaminates made (under adequate conditions) f rom similar polymers, exhibit dramatically improved tear propagation resistance. Nevertheless, as the figure 30,000 tons annual production indicates, the success of crosslamination technology in the marketplace has been limited. An important reason for this is difficulties in maintaining a high tear propagation resistance 20 and at the same time adequate bonding strength in relatively thin laminates, while the main advantages in particular should be the possibility to reduce the weight. The high tear propagation resistance in adequately produced crosslaminates is based on local delamination around the location where the tear propagates. Due to the unbalanced orientation in the individual films and criss-crossing of the main directions of the 25 orientation, one film will then have a tendency to propagate the tear in one direction and another film will tend to propagate the tear in another direction. Thereby there will be a tendency to eliminate the bonding at the location where the forces are concentrated, and if this tendency is sufficiently pronounced, the tear will "fork out" under a local delamination, and the "notch effect" of the tearing will almost be 30 eliminated. Hereby there will be, generally speaking, "competition" between the adhesive forces which try to withstand delamination, and the cohesive forces in each film which try to avoid a rupture or flow along any direction which is not parallel with the main direction of orientation. The said adhesive forces are (still generally speaking) independent of the thickness of the films, while the said cohesive forces are mainly 35 proportional to the film thickness, when all other parameters are unchanged. As a 2 consequence of this "competition", "thin" crosslaminates will either exhibit a relative poor tear propagation resistance or a relatively high tendency to delamination. This is much less of a problem for crosslaminates of "thick" layers. For industrial bags of gauge higher than about 60-70 grams per sq.m this "competition" will usually not cause serious 5 problems since filled bags are usually not subjected to delaminating forces, which means that a low bonding strength can be chosen, but the matter is very important e.g. for tarpaulins, cover sheets and similar products which will be subjected to repeated flexing during use, e.g. will flap in the wind. As a matter of practical experience the inventor and his licensees have found that in a tarpaulin made from a two-ply crosslaminate based on 10 combinations of LLDPE- and HMWHDPE types, each of the films must be of a gauge of at least 45-50 gm 2 , otherwise either the bonding strength or the tear propagation resistance will be unacceptable to the users. These experiences concern tarpaulins for "static" uses where there will not occur much flapping in the wind. For "dynamic" uses such as cover over trucks or goods wagons, where the tarpaulin will be subjected to 15 strong, repeated flapping, the gauge required is much higher. In low gauge film (e.g. of gauge between about 15-50 gm 2 destined for the final consumer, there is also a need for a high tear propagation resistance combined with good bonding, since such tear strength is a property which the consumer easily can evaluate. Examples of such films are films for wrapping of consumer goods and the different kinds of household films. 20 Several methods have been suggested for achieving an adequate combination of bonding strength and tear propagation resistance in crosslaminated films. They are all described in W003/074264 and all relate to a combination of a strong or relatively strong bonding in spots or lines, and weak bonding or no bonding over the rest of the film area. Of this known art, only the method and structure claimed in the said W003/074264 has 25 had industrial importance. Any discussion of documents, devices, acts or knowledge in this specification is included to explain the context of the invention. It should not be taken as an admission that any of the material formed part of the prior art base or the common general knowledge in the relevant art in Australia on or before the priority date of the claims 30 herein. It would be desirable to provide an improvement in the tear propagation resistance in crosslaminates, especially but not only in order to enable a reduction of the gauge. It would also be desirable to provide an improvement in the aesthetics of the 35 laminate, since the average consumer of plastic film and plastic bags mostly bases his judgement on very primitive strength testing and on the aesthetic impression, and 3 generally prejudges a thin film as "cheap plastics" irrespective of its objectively established strength. It would therefore be desirable to improve the aesthetics by giving the crosslaminates of oriented films a textile-like look, notably by means which also have a technical function. 5 As regards the importance of visual effects in products made of plastics, reference is made to an article in Modern Plastics December 2002 pg. 50: "Visual Effects means Business", which states: "instead of considering an exterior simply as a cover for components, manufacturers are using it as a marketing tool to differentiate products and allow personalisation". 10 It would further be desirable to enable a significant shrinkage by heat after the lamination, without thereby creating curling or irregular wrinkling (which crosslaminates normally tend to when shrinkage forces develop). Such shrinkage further enhances the tear propagation resistance and also enhances the puncture strength, since the shrunk crosslaminate has a certain memory of the state to which it was oriented before the 15 stretching, A key feature of the present invention is that the crosslaminated generally uniaxially oriented plies are supplied with a pattern of closely spaced "lines" of biaxially oriented, thinner material. These "lines" are in the following referred to as the "thinner webs", and the remaining parts of each ply are referred to as the "bosses". The pattern of 20 bosses with intervening thinner webs is produced by segmental stretching in a direction which is transverse to the main orientation of the ply, preferably a stretching between grooved rollers, as specified in the claims. This embossed pattern is preferably made as fine as practically possible, and for that purpose an improved method and improved apparatus for grooved roller stretching has been invented. It is not new to provide one or 25 both plies in a crosslaminate with a pattern of thinner webs, but it has been done under different conditions, namely in the manufacture of fluted (corrugated) crosslaminates, disclosed in W002/102592 and WO 04/054793, as it shall be discussed later. It is now found that the thinner webs, when they are unbonded or only weakly bonded to the adjacent ply, provide a surprising improvement of the tear propagation 30 resistance. This can be explained by the influence of these biaxially oriented narrow "lines" on the ability for change of orientation in the ply under the tearing forces. Such change of orientation serves to stop the tearing, and the narrow "lines" act as initiators for the re-orientation. Therefore it is also important to provide a pattern as fine as practically possible. 35 As mentioned above, it would be desirable to provide an improvement of the aesthetics, and this may be achieved by a textile-like appearance of the crosslaminated 4 embossed plies. One can say that each ply is "semi-fibrillated", and when the crosslaminate is superficially observed, it looks as if the plies really were fibrillated, especially when the visual effects are enhanced by incorporation of a pigment. Also with a view to the visual effects, it is important to make the pattern of bosses and webs as fine 5 as practically possible. One of the other desirable features mentioned above, namely a help to make a significant after-shrinkage of the laminate possible, may also be achieved by virtue of the fine pattern of thin webs, since they so to say "absorb" the compressional forces which otherwise produce the creases or the tendency to curling. This is a very pronounced 10 improvement. As background for the understanding of the invention a brief view over existing crosslamination technology may be useful. This mainly concerns the inventor's earlier publications. The polymer materials for crosslaminates have been mainly and are mainly 15 polyethylene and polypropylene of different types often modified by blending, and the old and present industrialised manufacturing processes comprise the steps of extruding a tube, which, by the draw-down, is oriented mainly in its longitudinal direction, helically cutting this tube to a web with its main direction of orientation on the bias, and continuously laminating two or more such webs with their main directions of orientation 20 criss-crossing. There can also be included in the laminate a film which is oriented mainly in its longitudinal direction. In the first commercialised technology based on these principles, the extruded tubular film, which is melt-oriented mainly in its longitudinal direction, is further cold stretched in this direction prior to the helical cutting. In a later commercialised technology, 25 disclosed e.g. in US-A-4,039,364, each tubular film is coextruded, having a layer which contributes mainly to the tensile strength in the laminate and at least one surface layer adapted to help in the bonding of the films, which at least partly takes place by pressure and heat. Also special layers are coextruded on the films, which become exterior in the 30 laminate. These special layers are adapted to modify the surface properties of the laminate, especially for improved heatsealing. In this later technology the helical cutting takes place in direct succession to the coextrusion without any cold stretching between, but in a separate production line. Further stretching is carried out when the films have been brought together in a sandwich arrangement, bonded or not yet bonded, to form a 35 laminate. The films are biaxially stretched at a relatively low 5 temperature. The transverse component of this biaxial stretching takes place between grooved rollers. In US-A-5,028,289 and US-A-5,626,944 this stretching between grooved rollers has been further developed, Practical ways of carrying out the helical cutting are disclosed in US-A 5 5,248,366. This patent also mentions an alternative cutting technique, namely that the tubular film can be provided with a helically extending melt orientation while it is drawn off from the coextrusion die, established by a relative rotation between the exit of the die and the draw-down means, and subsequently the cutting may be parallel with the axis or may be at an angle to the main direction of orientation. The process may even 10 be adjusted to produce a web in which the main direction of the melt orientation will become perpendicular to the longitudinal direction of the web. For the sake of completeness it should be mentioned that, in very early patents, there is also disclosed the possibility that longitudinally oriented polymer film material can be discontinuously crosslaminated and bonded in a press. 15 In a process which is entirely different from that described above, crosslaminates of a very stiff character are made for use in special advanced products. They consist of polymers which in molten or part-molten state are liquid crystals, and which become oriented and crosslaminated already within the extrusion die by means of counter-rotating die-parts. However, this type of process and product is not a 20 subject of the present invention. Reverting to the other types of crosslaminates, which more are commodities or technical products, the heatseal strength in a shear-type seal is adequate when a suitable lower melting polymer has been chosen for the surface layers of the laminate, while very special precautions must be taken if good shock-heat-seal strength is 25 requested in peel-type heatseals, as usually needed for industrial bags supplied with such heatseals. These precautions are disclosed in US-A-5,205,650 and WO-A 98/23434. Recent inventions concerning crosslaminates comprise the inventor's five publications W002/102592, W004/54793, W003/033241, W004/094129 and 30 W005/102669. The first two supply one or both plies in a 2-ply crosslaminate with a waved structure like the waving in corrugated paper board, but generally with a wavelength which is shorter than normal for the paper board, generally with the waves extending in the direction of molecular orientation of the respective ply. Both of these publications disclose and claim the formation of a pattern of 35 thinner, biaxial webs. In W002/102592 it concerns only one of the plies and is 6 described throughout the specification from page 8 onwards and in the claims and in W004/054793 it concerns one or both plies and is described throughout the specification from page 12 line 19 and in the claims. In both cases it concerns one set of thin linear biaxially oriented webs, which essentially for the bonded base of each flute, and further 5 one set of narrower, thin linear biaxially oriented webs, each forming the crest of a flute It is noted that the tear propagation resistance of these corrugated crosslaminates is very high, and for such laminates improvements in this respect is not needed, however there are many fields of use in which fluted laminates are not applicable, such as uses in which fine print or a special pattern of embossment is required. 10 W003/033241 and W004/094129 concern in particular special attenuation and orientation processes in connection with the extrusion, by which the strength at elevated temperature, heat-seal properties, yield tension and/or barrier properties can be improved It would be natural to believe that the best way of manufacturing a crosslaminate 15 would be to produce a transversely oriented ply by means of a tenter-frame, and laminate this with a longitudinally oriented ply, however the function of existing tenter-frames is limited to stretching at very elevated temperatures, e.g. 800C or higher, which at least in the case of HDPE or PP do not provide the ply with the properties which are adequate for crosslaminates This is explained in detail in W005/102669, which however claims a 20 modified type of tenter-frame suitable for stretching at much lower temperatures. This known art has direct importance for some embodiments of the present invention and will be described in connection with these embodiments. A product appears from claim 1 of the specification as filed, and a method of manufacturing it appears from the corresponding claim 18 of the specification as filed. 25 When the stated conditions of the bonding between ply A and ply B are fulfilled the thinner, biaxially oriented webs or "lines" have a surprising influence on the tear propagation resistance in this case a sufficient part of these "lines" have a sufficient "freedom" to act as initiators for the tear-inhibiting reorientation processes, which have been mentioned above, and the flexibility, which they provide after local delamination at 30 the location where the tear propagates, also has tear inhibiting effect. Reference is made to the comparative testing in Examples 2 and 3. As it has been mentioned above, the two publications W002/102592 and W004/054793, both dealing with crosslaminates which are fluted like corrugated paper boards, also disclose the formation of thinner, biaxially oriented webs or lines", but in 35 these disclosures the majority of the web area is stronger bonded to the adjacent ply that the bonds boss to boss. In fact the bosses are mostly unbonded. The purposes of the 7 thin webs in these products are to facilitate the formation of the flutes and enhance the stiffness of the flutes. These known corrugated crosslaminates also show a very good tear propagation resistance, however this is due to the corrugated form and not to the effects which the thin webs exert in the present invention. 5 The "slack" effect of the flutes in the above mentioned corrugated crosslaminate helps to minimize the concentration of forces in the tear propagation locations ("the notch effect"). In the present invention some "slack effect" is also preferable as long as it does not interfere with the needs especially for printability or receptability for embossed 10 patterns. As mentioned in claims 1 and 18 of the specification as filed, the plies A and B are heat-sealed together through one or more lamination layers. This can be by extrusion lamination or through coextruded lamination layers. The term "heat-sealed' includes the possibility that the plies are ultrasonically sealed together, since such sealing in effect is 15 due to a local heating caused by the ultrasonics. The test for weak bonding indicated in claim 1 of the specification as filed, namely repeated flexing and rubbing by hand, is a practical test which probably is known by all who deal with film laminates, mostly as a quick test for rejecting insufficient bonding. "No bonding" and "eliminated bonding" can be exactly detected by studying the cross-section 20 under a microscope. The pattern of bosses and intervening webs will appear generally even when different microtome cut specimens are compared, cut out perpendicularly to the bosses, following a chosen group of bosses. The pattern of bosses and thinner webs will often be overlapped by a bonding pattern determined, for instance, by corrugations on the laminating rollers, as explained in connection with fig. 3, but by examining a 25 sufficient number of microtome-cut strips of the laminate it can be detected how high a percentage of the total area of the thin webs is unbonded or weakly bonded (as defined) The peel strength of bonds that are stronger than the weakest bonding can be determined, if any doubt arises, by peeling of sufficiently narrow strips cut out, for instance, with a microtome. 30 The average thickness of each said thinner web preferably is no larger than 80%, more preferably generally between 25-50% of the maximum thickness of the adjacent bosses. Furthermore, preferably the width of the bosses is generally no more than about 1 mm, more preferably no more than generally about 0.5 mm, but most preferably generally in the region about 0.05-0.2 mm. Finally, the width of each thinner web 35 preferably is at least about 50% of the maximum thickness of the two adjacent bosses, 8 and more preferably it is no less than 25% of the average width of the two adjacent bosses. It is mentioned above that an important function of the thinner, biaxially oriented webs or "lines" is to act as initiation sites for reorientation of the plies during the tear 5 propagation. Accordingly, the degree of uniaxial orientation in the bosses and the temperatures at which this has been established are preferably limited to such an extent that during slow tear propagation each of the plies A and B reorients instead of fibrillating in the locations where the tear propagates. However, even if fibrillating instead of reorientation happens to take place due to too high a stretch ratio in the bosses or too 10 high a temperature for this stretching, the effect that the biaxially oriented webs make the location of tear propagation more flexible, still helps to increase the resistance to tear propagation. As it will be understood from the above, a weak bonding all over may be sufficient for relatively heavy crosslaminates or for bags in general, however in most cases a 15 pattern of bonding alternating with no bonding or of relatively strong bonding alternating with weak bonding is preferable. While claim 1 and claim 18 of the specification as filed indicate that "weak" refers to the possibility to eliminate the bonding by repeated flexing and rubbing, it is not possible to make indications in form of values of the peel force, since this varies with the gauge, stretching ratios, raw materials and the applications. 20 However, as already mentioned, the broad principle of such bonding patterns is state of the art, and furthermore the choice of bonding forces is a matter of routine experimentation from case to case. The bonding which is defined in the characterising part of claim 1 and claim 18 of the specification as filed can be established in principally different patterns, as specified 25 in claims 2 to 6 of the specification as filed. The structure according to claim 5 of the specification as filed is illustrated by figure 2 and explained in connection with this drawing, while the other aspects of the bonding systems according to these claims are explained in connection with figure 3. It is noted that the bonding systems which leave thinner webs unbonded, normally 30 will exhibit a higher tear propagation resistance, compared to systems which are equal to this in all respects, except that the thinner webs are weakly bonded. However, there is a draw back in the no-bonding system, namely that air can get access to the plies from the inside through the channels formed by the thin webs, and thereby the laminate becomes more susceptible to UV degradation, if the use of the laminate is such that it comes under 35 influence of strong sunlight for a long period of time.

9 The main product and process claims (claims 1 and 18 of the specification as filed) do not state at which step of the manufacture each of the plies A and B have been embossed by segmental stretching (normally grooved roller stretching) to form the pattern of bosses and thinner webs. However, as it is stated in claims 19 and 20 of the 5 specification as filed, this segmental stretching is preferably carried out either prior or subsequently to the all over stretching of the ply, or between two steps of the all over stretching of the ply. These two claims concern different routes of manufacturing the crosslaminate. In one route illustrated by flowsheet figure 5, the starting film is a lay-flat tubular film, the dominating direction of orientation is the longitudinal direction of the tube, 10 and the segmental stretching takes place transversely, i.e. normally by means of grooved rollers having circular grooves or helical grooves of a pitch which is very small compared to the radius of the rollers. Subsequently the two plies are cut on the bias and are continuously crosslaminated. In accordance with a first aspect of the present invention, there is provided a 15 method of manufacturing a crosslaminate including the steps of: segmentally stretching a first ply by passing the first ply through a first pair of grooved rollers with flat crests to form a first array of thicker and thinner linear bosses distributed over the first ply with a division between adjacent linear bosses of no larger than about 2 mm, where the linear bosses of the first array are integrally connected by thinner linear webs, where each web, 20 by volume, is less than 50% of an average volume of two adjacent bosses and where a delineation between a boss and an adjacent thin region includes a location where a ply thickness is an average between a thickest part of the boss and a thinnest part of the web; segmentally stretching a second ply by passing the second ply through a second pair of grooved rollers to form a second array of thicker and thinner linear bosses 25 distributed over the second ply, where the linear bosses of the second array are integrally connected by thinner linear webs; laminating the first ply to the second ply by bonding thicker linear bosses of the first ply to thicker linear bosses of the second ply without bonding the thinner linear bosses or the thinner linear webs of the first ply to the second ply and without bonding the thinner linear bosses or the thinner linear webs of the second 30 ply to the first ply, wherein when laminated a predominate direction of orientation of the first ply is at an angle to a predominate direction of orientation of the second ply and the first array of thicker and thinner linear bosses extend in a direction perpendicular to the second array of thicker and thinner linear bosses. In accordance with another aspect of the present invention, there is provided a 35 method of creating a laminate film including: passing a first ply of thermoplastic polymer material having a dominating direction of orientation in a longitudinal direction through a 9a first pair of heated grooved rollers to incrementally stretch the first ply in a transverse direction and create biaxially oriented thinner webs and first and second sets of uniaxially oriented bosses, the first set of bosses having a first thickness and the second set of bosses having a second thickness that is greater than the first thickness; wherein each 5 crest on the grooved surfaces of the grooved rollers has two edges, each of which has a radius of curvature in the range 20 to 50 pm; and bonding a second ply of thermoplastic material to the first ply by bonding the bosses having the second thickness of the first ply to the second ply without bonding the bosses having the first thickness of the first ply to the second ply and without bonding the thinner webs of the first ply to the second ply. 10 In the other route, illustrated by flowsheet 6, the dominating direction of the orientation of one ply is transverse to the machine direction, and the segmental stretching is parallel or almost parallel to the machine direction, i.e. if carried out, as normally preferred, by means of grooved rollers, the latter must have grooves extending axially or helically, in the latter case almost parallel to the axial direction. The second ply is 15 stretched similarly to the stretching which is carried out in the first mentioned route. The second route presents the advantage that all process steps can take place in-line, as shown in the flowsheet, but the machinery is much more expensive than the machinery for the first route due to the need for a tenter-frame. This tenter-frame is preferably of the type described in W005/102669 in which the ply is brought into a 20 THE REMAINDER OF THIS PAGE HAS BEEN INTENTIONALLY LEFT BLANK. THE NEXT PAGE IS PAGE 10.

10 pleated state with the pleats extending transversely, to allow a longitudinal contraction during the transverse stretching. This tenterframe process is characterised in that the orientation process at each position of the passage essentially is limited to one or two narrow neck-zones each controlled by long, narrow heating means which, seen in the 5 transverse dimension of the apparatus, each act over a narrow space and over which the film is passed in frictionless or low-friction engagement, and has its longitudinal direction angularly disposed to the film travel in such way that in each film cross section the narrow neck-zone or zones gradually proceeds over the width of the film until essentially the entire width to become oriented has passed such zone or zones. 10 In the two flowsheets, the segmental stretchings (grooved roller stretchings) are indicated as taking place subsequently to the other stretching step or steps. However, it could also be at an earlier stage of the manufacturing process. The carrying out of the segmental stretching after finalisation of the other stretching or at a late stage of the latter can give the orientation of the webs the most biaxial character and provide 15 the most effectful tear-inhibiting effect, while segmental stretching at an earlier stage, especially prior to any other stretching in solid state, can lead to a finer pitch of the embossed pattern and thereby improved aesthetics. This is under the condition that the ply is allowed an almost free contraction perpendicularly to the direction of stretching. For tenter-frame stretching this can be 20 achieved by the pleating mentioned above, and for longitudinal stretching this can also be achieved by pleating prior to the stretching, the latter taking place between closely spaced rollers, as disclosed in the inventor's old patent US 3,233,029. Furthermore segmental stretching as an early step of the orientation process followed by the stretching in pleated state, promotes the tendency to give the thinner webs a slack 25 form. This shall be explained later. In the carrying out of the segmental stretching, normally under use of grooved rollers, the pitch of the produced segments of stretching should preferably be almost as fine as possible, and for this purpose an improved stretching method and apparatus for this has been invented. This method concerns in general longitudinally stretching 30 of a film consisting of thermoplastic polymer material in generally uniaxial manner below its melting range in one or more steps, and prior or subsequently to this stretching or between two of such steps transversely and segmentally stretching the film between intermeshing grooved rollers having circular grooves or helical grooves of a low pitch compared to the radius of the rollers. The method is characterised in that 35 each crest on the grooved surfaces of the rollers has two edges which each is 11 sufficiently sharp for producing the said thinner linear web in the ply. To achieve this best possible, the said two edges preferably protrude to limit the contact between the ply and the grooved rollers to the edge portions of the crests. In other words, the crests on the grooved rollers should preferably have concave shape, see figure 8. 5 In this connection it is furthermore preferable that the grooved rollers are heated, e.g. to about 60-80 0 C, while the web is introduced to the rollers at a lower temperature, e.g. about 20-45 0C to selectively heat the ply on the edge portions of the grooved roller crests. The heating helps to provide control over the thickness of the webs. This embodiment is further explained in connection with figure 9. 10 In any case, the pitch of the grooved rollers should preferably be between about 0.8-1.2 mm, and the distance from one to the other of said two edges on the crest should preferably be between about 0.3-0.5 mm. In order to achieve the maximum of fineness in the pitch of the embossed pattern on the film, several segmental stretching processes can be carried out in 15 register with each other, in particular (as illustrated in figure 10) when the segmental stretching is a transverse stretching between circular grooved rollers (in this connection referred to as the first grooved rollers). This embodiment of the stretching method is characterised in that, prior or subsequently to the segmental stretching between the first grooved rollers, the ply is subjected to a second segmental stretching between 20 second circular grooved rollers, said second grooved rollers a) producing only one stretching zone on each crest, b) having under the operational conditions exactly the same pitch as the first grooved rollers, and c) being in exact registration with the first grooved rollers such that each 25 stretching zone formed by the second grooved rollers falls between or joins with the two stretching zones formed on the edges of one crest of the first grooved rollers. For industrial production the roller lengths must normally be at least about or more than 1 m, and 2-3 m length may also be required. Therefore the machining of 30 the roller surfaces requires an extreme accuracy, and each roller must be composed of segments mounted on a core. The description of the roller drawings deals in further detail with the achievement of the accuracy and with a correct degree of sharpness on the edges of the crests on the grooved roller surfaces. It is emphasised that the above mentioned segmental stretching methods in 35 which at least a part of the segments are produced on the edges of flat or concave 12 crests of grooved rollers, are not limited to the manufacture of the product according to claim 1. These methods can e.g. also with advantage be used in the manufacture of the fluted crosslaminates dealt with in the above mentioned W002/102592 and W004/054793, since the pitch of the fluting can be finer by application of the described 5 measures. Furthermore, the biaxially oriented film produced by these methods can in many cases be used as a single ply without any lamination process, e.g. as a packaging film for wrapping or for sanitary purposes, especially when the average gauge of such film is about 0.05 mm or lower. Going back to the main aspect of the invention, the two plies A and B may have a 10 straight extension, as it appears from the foregoing or one or both may comprise slacks, but preferably the over-length of the slacks should be limited as stated in claim 7 of the specification as filed. Two different types of slacks are illustrated by the microphoto figure 1 and by the drawing figure 2. Such slacks are quite different from the flutes disclosed in the above mentioned W002/102592 and W004/054793. They have a positive influence 15 on the resistance to tear propagation since they distribute the tearing forces around the location where the tear propagates, thereby reducing the notch effect. Furthermore they help to give the crosslaminate a textile-like look and/or feel and may remove gloss, if desired. Alternatively, there may be a need, e.g. for printing purposes or for subsequent decorative or functional embossment - to make the crosslaminate without any such 20 slacks. The slacks are formed by shrinkage of the laminate during the lamination process or during an after-shrinkage process at elevated temperature. When ply A shrinks, the bosses in ply B will be brought closer together, leading to slack formation in the webs of B unless these webs can shrink similarly in the same direction. Similar effects happen to 25 the webs in ply A when ply B shrinks. As mentioned above the formation of slacks is promoted by carrying out the segmental stretching as an early step of the orientation processes, followed by the stretching in pleated state. The explanation is that, since this stretching gives the ply on its whole a possibility for contraction transverse to the direction in which the stretching takes place, it reduces the biaxial character of the 30 orientation in the thinner webs, which means that they are stabilized against further contraction in the same direction. Another measure for stabilizing the thinner webs, and thereby promote slack formation during lamination or in an after-shrinkage process, is to selectively heat treat the thin webs with hot air while the bosses are kept at a lower temperature by contact 35 with a cooled surface, normally a roller surface. The selective heating is possible since 13 there will be some air-space between the web and the cooled surface. This heat treatment may even be carried out to such an extent that the thinner webs partly melt. As mentioned there are cases in which slacks are not wanted. If they are formed accidentally during the lamination or during an after-shrinkage process, they 5 may be removed, first on one side, then on the other side of the laminate, by heating the slacks with hot air while contacting the bosses with a cooled surface, normally a cooled roller surface. The conditions of the heating must be carefully adjusted since in this case some parts of the bosses will be heat insulated from the cooled surface. Very suitable materials as main component in the crosslaminate due to strength 10 properties, stiffness and relatively low price - are HDPE or crystalline PP of high or medium high molecular weight. With a view to the possibilities for reorientation during tearing it is advantageous to carry out stretching in the dominating direction of orientation at a temperature around or below 504C, at least when the polymer material is based on PP or HDPE. 15 A subsequent heat treatment, e.g. at about 80-90"C may then be needed in order to avoid shrinkage at a wrong stage of the manufacturing process. The orientation of the plies is preferably carried out to such an extent that the ultimate tensile strength of the crosslaminate, at least in one direction but normally in all directions, becomes no less than about 25 MPa, more preferably no less than about 20 40 MPa. In the determination of this strength, which is expressed as a force per area cross section, the thickness must be understood as average thickness in compacted state. In practice this is calculated from the square metre weight, when the density of the constituents in the film are known. The bonding layer is preferably selected as a blend of two or more compatible 25 polymers of significantly different melting ranges, such that the lower melting of said blended polymers starts to melt at a temperature at which there will be minimal disturbance or the orientation produced in the main portions of each ply. The blending ratio and the lamination temperature should be selected to produce the desired balance between resistance to delamination and tear propagation resistance. For 30 instance, in the case of HDPE based crosslaminates the lamination layer or layers can with advantage consist of a blend of LLDPE and metalocene LLDPE or LLDPE and EVA. With a view e.g. to the aesthetic effect, the plies A and/or B are preferably microvoided. As it is well known this can be achieved by admixture of a suitable 35 powder (e.g. talc) and/or by the choice of conditions for the stretching steps. As it also 14 is known, HDPE and PP form microvoids without any admixture of powder if the orientation is carried out at a temperature around or below 500C. As mentioned above it is also found advantageous for the strength properties of the crosslaminate based on HDPE or PP that the majority of the orientation is carried out at such relatively low 5 temperatures. However, more important than the aesthetic effect is the possibility to make a breathable crosslaminate by adjusting the conditions of the stretching steps and/or the choice of admixed powder such that the voids in the thinner webs become continuous through the webs. Microporous thin breathable films are normally laminated with fabrics to give them sufficient strength, but in this aspect of the invention 10 the reinforcement, namely the uniaxially oriented bosses, are integral with the microporous thin film material. Such breathable crosslaminates according to the invention can in heavier gauges, e.g. in average gauge about 0.05-0.15 mm, be used for "house-wrap-film", roof underlay, breathable bags and rain coats, and in lower gauges, e.g. about 0.01-0.03 mm, for miscellaneous medical and sanitary purposes. 15 Alternatively the laminate according to the invention may be microperforated. Further details of the invention appear from the accompanying drawings and the following description of the drawings. Figure 1 is a retouched but true microphoto showing a section parallel with one of the main directions of the "semi-fibrillated" crosslaminate produced as explained in 20 example 1. Figure 2 is a drawing, showing in similar section as figure 1 a "semi-fibrillated" (i.e. segmentally stretched) crosslaminate comprising two categories of bosses, namely the thicker bosses X which are bonded and the unbonded thinner bosses Y. Figure 3 is a schematic representation of advantageous bonding/no bonding 25 or strong bonding/weak bonding or strong bonding/weak bonding/no bonding patterns. Figure 4 shows a set of rollers suited for laminating very thin plies while bonding boss to boss but keeping the thinner webs unbonded. Figures 5 and 6 are flowsheets representing two different routes of manufacturing the "semi-fibrillated" crosslaminate. 30 Figures 7 and 8 each show a detail of two intermeshing grooved rollers in the process of segmental stretching of a film material, making two thin webs on each crown of the grooved surfaces. The grooves may be circular or helical but almost circular. The indicated ranges of measures are generally indicated below. Figure 9 shows a preferred set-up and operation of the grooved rollers 35 represented by figure 8 when the rollers are heated.

15 Figure 10 shows another preferred set-up and operation of the grooved rollers represented by figures 7 and 8, namely in "registration" with a set of grooved rollers, which makes one thin web on each crown of the grooved surfaces. Figures 11 and 12 show two lines of rollers for lamination and shrinkage on 5 laboratory scale. These are described in connection with the examples. In figure 1, boss (1) is formed in a first one of the two "semi-fibrillated" plies. Bosses 2 are formed in a second "semi-fibrillated" ply, and the interrupted line (3) indicates the interphase between the two plies. It should be understood that the first ply, when viewed in a section perpendicular to the boss (1), looks generally as the 10 second ply does in this microphoto. All bosses are relatively strongly oriented in their longitudinal direction. As it appears from the example, each ply is a coextruded, 3 layered film consisting of HDPE in its middle, LLDPE on the surface which also forms a surface of the laminate, a blend of metalocene LLDPE and normal LLDPE forming a bonding layer. However the microphoto does not show that the two films are 3 15 layered, nor does it show the bonding phase indicated by the interrupted line (3). Three of the four regions (4) shown in the microphoto form slacks or loops, and as it has been described above and claimed this feature has an important positive influence on the tear propagation resistance of the crosslaminate. However, if desired the slack effect can be eliminated by selective heating of the thinner webs, 20 In the drawing figure 2, the unbonded spaces are made wider. This conveniently can be done by overstretching of the thinner webs. This widening has been established by means of the bosses Y, which are thicker than the webs (4), but thinner than the bosses X. Each web (4) is adjacent to one boss X and one boss Y. The linear pattern of different thicknesses can be established as explained in 25 connection with figure 10, and the bonding of generally all bosses X in ply A to bosses X in ply B while maintaining the rest of the area of the laminate essentially unbonded, can be achieved by a suitable choice of hardness on the surface of the laminating rollers and a suitable roller pressure. The webs (4) and bosses Y are shown in a slack state, but can be straightened out by heat treatment. 30 In the schematic representation of advantageous bonding systems, figure 3, the vertical lines show delineations between bosses/thinner webs in ply A, and the horizontal lines show similar delineations in ply B. The lines need not follow the machine/transverse directions of the crosslaminate, but could e.g. be under an angle of 450 to these directions. Furthermore, the webs and bosses in ply A need not extend 35 perpendicularly to the webs and bosses in ply B as here shown. On the contrary, the 16 best tear propagation resistance in all directions is usually found when the two directions of the embossed pattern, and thereby the main directions of orientation in A and B, form an angle of about 55-65* with each other. The perpendicular arrangement of the two arrays in the pattern is here chosen for the sake of 5 simplification. The boss to boss intersections comprise the solid squares (101) and the squares (102) marked with a dot. The rest of the squares represent either web to web or web to boss arrangements as described below. Bonding system 1: Bonding in the squares (101) and (102), no bonding over the rest of the 10 squares, achieved by adjustment of the surface hardness of the laminating rollers and the roller pressure. Established in examples 1 (see figure 1) and 2. Bonding system 2: Bonding in the squares (101) and (102), also bonding but a weaker bonding over the rest of the squares, achieved by adjustment of the surface hardness of the 15 laminating rollers and the roller pressure. Established in example 4. Bonding system 3: Bonding in the squares (101) and no bonding over the rest of the squares, as in example 3, achieved either by a suitable embossed pattern on one or both lamination rollers, so as to bring plies A and B under heat and pressure in bosses 20 which each comprise several cross-points between the bosses, or by coextruding the lamination layer on ply A and ply B in form of an array of closely spaced narrow strips as disclosed in W003/074264. Bonding system 4: Relatively strong bonding in the squares (101), weaker bonding in the squares 25 (102) and similar bonding or no bonding overthe rest of the squares. This is preferably also achieved by the above mentioned coextrusion method disclosed in W003/074264, but in this case the coextruded film must comprise (as also disclosed in the said publication) two lamination layers, one strongly bonded which is in the form of narrow strips, and one weaker bonding, continuous lamination layer between the strips and the 30 main layer of the coextruded film. Bonding system 5: Bonding only the squares (101) and in squares directly adjacent to these squares as in example 5. This is achieved in a similar way as bonding system 3, but the hardness of the lamination roller surfaces and/or the roller pressure is adapted also 35 to bond the thin webs adjacent to squares (101).

17 in this principal sketch there are only shown 9 of the cross-points (101) within each group of bonding or strong-bonding. However, since the width of each boss on the plies A and B most preferably is about 0.05-0.2 mm, and the linear dimensions of each of these groups preferably is, as a rough indication about 1 to 5 mm, it is clear 5 that the number of cross-points (10) within each group is much higher than shown. There may e.g. be about 500 or more of such cross-points within each group. As it appears from the foregoing the selection of surface hardness on the lamination rollers and pressure between the rollers will in many cases be critical, especially if the thickness of the plies is very low, e.g. about 0.01 mm, and if at the 10 same time all of the thinner webs should be kept free of bonding. In such cases it may even be necessary to laminate with steel surfaces on both rollers. In this and other cases, the application of an even roller pressure over the full width of the plies, which normally will be more than 1 m, is also a problem which must be solved. Figure 4 shows a practical solution to this. One central roller (104) is used, and on opposite 15 sides of this are located two rollers (105), which consist of segments connected through shafts (107), On each shaft there is a bearing (108), which is biased towards the central roller (104), e.g. by pneumatic or hydraulic means, here indicated by the arrows (109). Means for circulating hot water or oil (not shown) may also be provided. The processes according to the flowsheets figures 5 and 6 have already been 20 explained in the general description. With reference to figure 7, the mutually intermeshing grooved rollers (112) and (113) which effect the segmental transverse stretching have flat crests (114) on their circular teeth (flat seen in cross-section) with relatively sharp edges (115). The segmental stretching starts on these edges and develops into thin continuous webs (116). The intermeshing is limited such that there 25 are maintained thicker material, bosses, on the flat crests (114) of the circular teeth. The requirements for precision in the manufacture of the roller surfaces is high, and it is highly advisable to make the outer part of rollers from short segments. The radius of curvature on the "sharp edges" is of importance. It depends on the properties of the coextruded film, but should normally be within a range of about 20-50 30 micrometre. A suitable industrial method of making a relatively exact adjustment of this curvature is first to make the edges really sharp, then round them by electrolytic polishing, and finally carry out electrolytic Cr-plating. These electrolytic processes must of course take place under precisely established conditions. In figure 7 the width of the thinner webs is shown to be about equal to the width 35 of the bosses. Normally, but not always, it is preferred that the thinner webs in the final 18 product should be narrower than the bosses to give the product good stability. However, in figure 7 shows the cross-section of the laid-flat tubular film while it is tentered, and the width of the thin regions will be reduced when it leaves the grooved rollers. 5 The purpose of making relatively sharp edges on the circular teeth of the grooved rollers is to make the pattern of embossment particularly fine. The precision of this embossment is enhanced by the profile of the teeth which is shown in figure 8. Here the crests are not flat, seen in cross-section, but have a concave shape, so that the edges protrude radially beyond the part of the crest between the edges. 10 In figure 9, it should be understood that the two grooved rollers (112) and (113), which are similar to the two rollers in figure 9, are heated such that the formation of the thinner webs on the protruding edges (115) is facilitated and their thickness can be better controlled. There is added a third grooved roller (110) with smooth, rounded crests (111). The three grooved rollers are shown in a compact form, that is only two 15 diametrically opposite segments of each roller, and their centerlines (112a), (113a) and (11 0a) are shown. While rollers (112) and (113) are heated, e.g. to 70-90*C, roller (110) is kept at a much lower temperature, e.g. at around 20*C. Under operational conditions the three grooved rollers must have exactly the same pitch, i.e. at room temperature rollers 20 (112) and (113) will have a pitch which is smaller than the pitch on roller (110). This roller set-up operates as follows: The ply follows roller (112) over a distance sufficient to heat the ply-part in contact with the warm protruding edges (115) to the temperature, which has been chosen for the segmental stretching. This takes place when the grooved surface on 25 roller (112) intermeshes with the grooved surface on roller (113). At this point the ply portions which come in contact with the protruding crown edges on roller (113) will not be stretched since they have not yet been heated, or will be stretched only to a low degree. These ply portions heat up while they follow roller (113), and become stretched when the crests on roller (113) intermesh with the cold, smooth crests on 30 roller (110). The intermeshing between rollers (112) and (113) and between rollers (113) and (110) should be adjusted to make the widths of all webs as equal as possible. In figure 10, the two "registered" sets of grooved rollers are shown in a similar compact drawing as the three rollers in figure 9. Rollers (112) and (113) are similar to 35 the two rollers in figure 8, while roller (119) has only one relatively sharp edge on the 19 crest of each circular tooth, namely (120) in the middle of the tooth. The teeth on rollers (118) and (119) are mutually intermeshing, each making one stretching zone (thin web) and the two pairs of grooved rollers are in "registration" such that the middle of each tooth on roller (119) almost touches the middle of a tooth on roller (112). In 5 figure 8b the registration is indicated by the broken lines (121). Means for securing exact registration between grooved rollers in the manufacture of the latter are known from WO-A-02-102592. As a result of this registered transverse stretching the film will have formed two bosses (122) corresponding to each crest of rollers (112) and (113), and thereby a still finer pattern of embossment is achieved. 10 Rollers (112) and (113) can be installed downstream of rollers (118) and (119), or vice versa, namely that the former are installed upstream of the latter. It depends on the properties of the extruded, meltoriented film which one of the two options is chosen. However, if the tips (120) of the crests on rollers (118) and (119) are made 15 smoothly rounded, this set-up of grooved rollers can be used to manufacture the structure shown in figure 2. The relatively thin bosses Y are formed on the rounded tips (120). Example 1 A 60 micrometre thick 3-layer tubular film is extruded, composed as follows: 20 Middle layer, 80% of total: HDPE of m.f.i. = 0.2 and density - 0.944 g mi". Outer surface layer - lamination layer, 10% of total: 50% Affinity 8770 (a metalocene of m.f.i. = 1.0. Inner surface layer, 10% of total: LLDPE of m.f.i. = 1 Blow ratio: 1:1:1. 25 Longitudinal drawn down ratio: 30:1. The tubular, uniaxially meltoriented film is semi-fibrillated at 40 0 C (ambient temperature) between grooved rollers as shown in figure 7 with pitch 1.2 mm and with 0.3 mm distance from sharp edge to sharp edge on the crests. The downstream grooved roller moves 5% faster than the upstream one. It has quite generally been 30 found that such small velocity difference helps to make the embossment (the segmental stretching) even. In immediate succession to these grooved rollers the tubular film is taken through a pair of intermeshing, driven grooved rollers of pitch 15 mm having rounded crests, adjusted to transform the fine pleating to a coarser pleating without performing any further segmental stretching. This has also generally been 35 found to help making the product even, when the segmental stretching takes place 20 before the longitudinal stretching. As mentioned in the general description, a longitudinal stretching is preferably started in pleated state, however it was found that very fine pleats tend to change during the route to the stretching rollers and form a more irregular and coarse pleating. 5 The coarsely but evenly pleated tubular film proceeds to a series of driven smooth rollers, kept at the mentioned temperature 400C, and adjusted to stretch the film in the ratio 2:4:1. From this unit the film proceeds to a series of stabilization rollers in which it is stabilized at 900C without any further stretching, is cooled to about 20 0 C on a water-cooled roller and finally spooled up. 10 In a separate process line the tubular, oriented film with bosses and thin webs is helically cut at an angle of 450, and in a third separate process line two such helically cut films are crosslaminated under pressure at a temperature about 100*C. Shrinkage is avoided upstream of the roller nip and allowed as the laminate leaves this nip. The lamination pressure is adjusted to a low value to obtain maximum tear propagation 15 resistsance without disrupting the structure. The laminate hereby became relatively strongly bonded boss to boss all over. A part of the mainly longitudinally oriented film was also used to make a crosslaminate of the type in which ply A is oriented in the machine direction, and ply B is oriented in the transverse direction. To make such ply B in simple way for 20 laboratory purposes, the mainly longitudinally oriented film was cut into relatively short lengths, and several such lengths were heat-sealed together to make the orientation transverse. Ply A and ply B were laminated together and then allowed to shrink with the same apparatus and under the same process condition as the above mentioned 45 0 cut film samples. The produced structure appears from the microphoto figure 1. 25 The lamination and shrinkage was carried out with the laboratory apparatus shown in figure 11, and shall now be described in further detail. The plies A and B are brought together on the idle roller (10), pass over the idling transfer roller (11), the function of which is to avoid wrinkling on the passage to the laminating rollers (12) and (13). Roller (12) is a steel roller, while roller (13) is 30 coated with rubber of a hardness about 70 ShoreA. Both rollers are heated to give the "sandwich" of A and B the desired lamination temperature, which as mentioned is about 100 *C in this example. The distance over which A and B follow roller (12) before they get under lamination pressure in the nip between rollers (12) and (13) is adjusted to obtain weak bonding with minimum shrinkage before the nip. After the 35 lamination, A and B still follow the hot roller (12) over a relatively long distance to 21 become further heated and shrink in both directions. The laminate passes the idling transfer roller (14) and is wound up on reel (15). The winding tension is kept as low as possible to allow a shrinkage as high as possible under the given conditions of heating. The bonding system is that which in the description of figure 3 is called bonding 5 system 1. Example 2 An about 0.15 mm thick 2-layers tubular film is extruded, composed as follows: Main layer, about 80% of total: HDPE of m.f.i. = about 0.2 and density = about 0.95 g ml-. 10 Outer surface layer = lamination layer, about 20% of total: an ethylene copolymer which starts melting at about 95 *C. Blow ratio about 1:2:1. The lay-flat tubular film is longitudinally stretched at about 30*C in a ratio about 3:1, as measured after relaxation and stabilization by heat. This stretching is carried 15 out in several steps between very closely spaced stretching rollers, as known in the art. After the stretching the gauge of the film is measure to be 0.040 mm. This cold stretched tubular film is used for all crosslaminated samples produced in this example and in example 3. Comparative experiments are carried out as follows: 20 a) the layflat longitudinally oriented tubular film is "semi-fibrillated", helically cut at an angle of 450, and then crosslaminated, b) similar procedure as under a) except that the film is not "semi fibrillated", C) like procedure a) but the cutting angle is 630 which the inventor normally 25 prefers, d) similar procedure as under c) except that the film is not "semi fibrillated". The "semi-fibrillation" (segmental stretching between grooved rollers) is carried out as described in example 1, but it is noted that in example 1 the semi-fibrillation is 30 carried out prior to the longitudinal cold-stretching, and in this (and the next) example after the longitudinal cold-stretching. The lamination plus shrinkage is carried out as explained in example 1, except that the film temperature during lamination is slightly higher, namely 105*C. The bonding system is that which in the description is called bonding system 1.

22 Details of process conditions and test results appear from the tables after example 5. The comparison between "semi-fibrillated" and "no-semi-fibrillated" samples are here based on the tear propagation resistance, as measured by a modified tongue tearing test. The modifications, compared to the ASTM method, 5 consist in a higher tearing velocity (see the tables) and different dimensions of the specimens, namely: sample size 100mm x 100 mm and depth of incision 30 mm. The results of the tear testing appearing from the tables show a significant positive effect of the thinner webs produced by the "semi-fibrillation". In addition to this, the samples which are not "semi-fibrillated" show a very strong tendency to curling, while the "semi 10 fibrillated" samples do practically not show such tendency. Finally the "semi-fibrillated" samples show an elegant textile-like pattern due to the different appearance of the microvoiding in the bosses and in the thinner webs. This effect of textile-like appearance is relatively weak, which may be preferable, but if a dominating textile-look is wanted it can be achieved by adding pigment in the extrusion process. 15 Examinations in cross-sections in microscope show that the thickness of the thin webs on the average is 30% of the thickness of the adjacent bosses, and the width of the thin webs on the average is 30% of the width of adjacent bosses, thus the volume of the thin webs is about 9% of the volume of the bosses. Example 3 20 This is carried out like example 2, except for the lamination process which now takes place by the spot-bonding which in the description of figure 3 is referred to as "bonding system 3". Only film cut at an angle of 630 is laminated. As in example 2 crosslaminates with "semi-fibrillated" plies and crosslaminates with "non-semi fibrillated" plies are compared. 25 The lamination/shrinking process and apparatus deviates from what is described in example 1 with reference to figure 11, in that the rollers (12) and (13) are adapted to produce spot-bonding, The lamination roller (12) is a grooved roller with circular grooves of pitch 1.5 mm, having 0.5 mm thick, flat crests. The rubber-coated lamination roller (13) is also a grooved roller, but with axially extending grooves, pitch 30 about 1,5 mm and having about 0.7 mm thick, flat crests. The hardness of these teeth is about 70 shoreA. The temperature of the plies during lamination is adjusted to 1050oC. The lamination pressure and the tension at which the laminated film is drawn from roller (13) are kept low. 35 The comparative experiments are chosen as follows: 23 e) the layflat longitudinally oriented tubularfilm is "semi-fibrillated", helically cut under 630, and then crosslaminated, f) similar procedure as under e) except that the film is not "semi fibrillated". 5 Further details of the process and the comparative test results in form of tear propagation resistance under fast tearing, appear from the tables after example 5. Also in this example the "semi-fibrillated" samples are very clearly stronger in this respect than the "non-semi-fibrillated". The dimensions of the thin webs and the bosses when studied in microscope, appear equal to the dimensions found in example 10 2. Example 4 This example illustrates the manufacture of a very thin crosslaminate according to the invention, with the bonding system which in the description of figure 3 is called "bonding system 2". 15 The extruded tubular film has a thickness of only 0.015 mm. Composition: Main layer 60% of total: HDPE of d = 0.95 and m.f.i. = 0.2. Inner surface layer (heat-seal layer) 20% of total: LLDPE of m.f.i. = 1.0. 20 Outer surface layer (lamination layer) 85% LLDPE (m.f.i. = 1.0) + 15% metalocene LLDPE (m.f.i. = 1.0). This metalocene LLDPE has melting range about 50-60 0 C. The blow ratio during extrusion was about 2:1 and the drawdown ratio about 40:1. The layflat tube was longitudinally stretched in a line, in which it first was supplied with fine pleats. 25 Such "pleat-stretching" has been mentioned in the general description. The stretching took place between rubber-coated rollers of diameter only about 30 mm, which were supported by heavier rollers. After this stretching this tubular film was "semifibrillated" exactly as in examples 2 and 3, and then helically cut at an angle 630. 30 The lamination without shrinkage was carried out as a separate, first lamination process by means of the apparatus shown in figure 12, and an after-lamination plus shrinkage process was carried out by means of the apparatus shown in figure 11. The apparatus of figure 12 deviates from that of figure 11 by a first lamination counter roller (16), rubber-coated and not heated, which serves to eliminate air 24 entrapment and bring the plies in good contact with the hot roller (12). Roller (16) is mildly pressed towards roller (12) by pneumatic mean (17). Final gauge of laminate: 19 pm. In this example the film temperature during lamination has been only 70*C to 5 avoid irregular shrinkage. After lamination (i.e. stronger bonding) with the apparatus of figure 11, was carried out with the laminate heated to about 900C. Further details of the process appear from the tables. The manufactured crosslaminate had average gauge 19 pm. Examination of cross-sections in microscope show that the thickness of the thin 10 webs on average is 25% of the thickness of the adjacent bosses, and the width of the thin webs on average is 20% of the width of the adjacent bosses, thus the volume of the thin webs is about 5% of the volume of the bosses. Example 5 This example illustrates the manufacture of a similarly thin crosslaminate 15 according to the invention, but with the bonding system which in the description of figure 3 is called "bonding system 5". Regarding film composition, extrusion conditions and "semi-fibriliation", the example is similar to example 4, but the lamination was carried out at 700C, practically without shrinkage with the apparatus of figure 11. 20 After lamination and after shrinkage was not applied. In order to obtain a suitable, not too high and not too low bonding strength, the contents of the metalocene LLDPE in the coextruded lamination layer, which in example 4 was 15%, was in this example increased to 30%. Final gauge of laminate: 19 pm. 25 The dimensions of the thin webs and the bosses, when studied in microscope appear equal to the dimensions found in example 4.

25 Table of tearing results m.d. = machine direction t.d. = transverse direction d.d. = diagonal direction 5 a) Cutting Angle 45", not "semi-fibrillated", smooth lamination rollers, final gauge 0.08mm b) Cutting Angle 45', "semi-fibrillated", smooth lamination rollers, final gauge 0.06mm c) Cutting Angle 63', not "semi-fibrillated", smooth lamination rollers, 10 final gauge 0.08mm d) Cutting Angle 63, "semi-fibrillated", smooth lamination rollers, final gauge 0.06mm e) Cutting Angle 63', not "semi-fibrillated", corrugated lamination rollers, final gauge 0.08mm 15 f) Cutting Angle 63", "semi-fibrillated", corrugated lamination rollers, final gauge 0.06mm Tearing velocity: 15cm per sec. In the calculations of % improvements the 25% reduction of gauge by the "semifibrillation" has been considered. 20 1st test (N) 2nd test (N) 3rd test (N) 4th test (N) average (N) % Improvement a) m.d. 3.0 4.0 3.0 3.3 b) m.d. 10.0 6.0 9.0 8.3 235 25 a) t.d. 3.6 4.9 3.0 3.8 b) t.d. 6.8 6.3 5.2 6.1 115 a) d.d. 3.8 3.2 3.9 3.6 30 b) d.d. 7.6 5.6 6.0 6.4 140 c) m.d. 9.2 5.6 6.5 7.1 d) m.d. 10.5 8.0 20.0 12.8 140 35 c) td. 5.0 2.8 6.5 4.8 d) t.d. 22 35 11.5 22.8 535 c) d.d. 6.5 4.0 8.0 6.2 d) d.d. 14.2 11.0 10.5 11.9 155 40 e) m.d. 26.0 24.3 25.2 f) m.d. 27.0 52.0 45.0 41.3 120 e) t.d. 20.0 21.2 27.0 13.0 20.3 45 f) t.d. >40 15.0 27.0 >47 >32.3 115 e) d.d. 39 37 8.0 28 f) d.d. 15.5 79 46 74 53.6 150 50 26 Table of measurements of stretching and shrinkage The percentages relate to the dimensions of the extruded films before the 5 mentioned process step.

Cl) wu 00l to0 .,u E C C 'Jo CD E caE0 0 -0)

-

0 V to E 0D -a P E C Eu E CY) X Co LOO 04 CV 04 L) 00 .0 ID C:) U) c ClLn 0 0

Claims (20)

1. A method of manufacturing a crosslaminate including the steps of: segmentally stretching a first ply by passing the first ply through a first pair of grooved rollers with flat crests to form a first array of thicker and thinner linear bosses distributed over the first ply with a division between adjacent linear bosses of no larger than about 2 mm, where the linear bosses of the first array are integrally connected by thinner linear webs, where each web, by volume, is less than 50% of an average volume of two adjacent bosses and where a delineation between a boss and an adjacent thin region includes a location where a ply thickness is an average between a thickest part of the boss and a thinnest part of the web; segmentally stretching a second ply by passing the second ply through a second pair of grooved rollers to form a second array of thicker and thinner linear bosses distributed over the second ply, where the linear bosses of the second array are integrally connected by thinner linear webs; laminating the first ply to the second ply by bonding thicker linear bosses of the first ply to thicker linear bosses of the second ply without bonding the thinner linear bosses or the thinner linear webs of the first ply to the second ply and without bonding the thinner linear bosses or the thinner linear webs of the second ply to the first ply, wherein when laminated a predominate direction of orientation of the first ply is at an angle to a predominate direction of orientation of the second ply and the first array of thicker and thinner linear bosses extend in a direction perpendicular to the second array of thicker and thinner linear bosses.

2. The method according to claim 1, further including the step of: prior to the laminating step, either longitudinally stretching the first ply in a substantially uniaxial manner, or longitudinally stretching each of the first and second plies in a substantially uniaxial manner.

3. The method according to claim 1, wherein the flat crests each have two edges, each edge having a radius of curvature in the range 20 to 50 pm.

4. The method according to claim 3, wherein the two edges of each crest protrude further than the rest of the crest, and wherein the first pair of grooved rollers are heated to a temperature between about 600 C. and 800 C., while the first ply is fed onto the rollers at a lower temperature between about 350 C. and 400 C. to selectively heat the 29 first ply at portions that contact the two edges of the crests of the first pair of grooved rollers.

5. The method according to claim 3, wherein a pitch of the first pair of grooved rollers is less than 5 mm, and a distance from one to the other of the two edges on the crest is between about 0.3-0.5 mm, and a radius of curvature of the edges is in the range 20 to 50 pm.

6. The method according to claim 3, wherein segmental stretching the first ply includes transversely stretching the first ply between the first pair of grooved rollers, where prior or subsequently to this segmental stretching, the method includes segmental stretching the first ply between a third pair of grooved rollers, where the third pair of grooved rollers: a) produce only one stretching zone on each crest, b) have a pitch the same as the first pair of grooved rollers, and c) are in registration with the first pair of grooved rollers such that each stretching zone formed by the third pair of grooved rollers falls between or joins with the stretching zones formed on the edges of the first pair of grooved rollers.

7. The method according to claim 1, wherein laminating the first ply to the second ply includes passing the first ply and the second ply together through a fourth pair of grooved rollers.

8. The method according to claim 7, wherein a first roller of the fourth pair of grooved rollers has axially extending crests and a second roller of the fourth pair of grooved rollers has radially extending crests.

9. The method according to claim 1, further including extruding a bonding layer in one or more of the first ply and the second ply, wherein a pattern of bonding in spots or linear regions is achieved by coextruding the bonding layer in the first ply and the second ply in form of an array of closely spaced narrow strips, whereby the strips in the first ply form an angle to the strips in the second ply, wherein laminating the first ply to the second ply includes using a temperature and pressure adapted such that within each spot or linear region, the first ply and the second ply either become evenly bonded to each other all over, or become bonded to each other in a pattern of bonding/no bonding or stronger bonding/weaker bonding, corresponding to the pattern of bosses/thinner 30 webs, while the remainder of the laminate is maintained unbonded or more weakly bonded than the average bonding within the spots or linear regions, referring to peel testing at 200 C.

10. The method according to claim 1, wherein a degree of uniaxial orientation in the bosses of the first and second arrays of thicker and thinner linear bosses is such that during slow tear propagation in the crosslaminate each of the first and second plies reorients instead of fibrillating in the location where the tear propagates.

11. The method according to claim 1, wherein laminating the first ply to the second ply includes laminating using heat and wherein during or following the lamination of the first ply to the second ply, the crosslaminate shrinks along at least one of the main directions of orientation.

12. The method according to claim 11, further including selectively stabilizing the thinner webs in one or more of the first ply and the second ply by heating the thinner webs with hot air while the bosses are maintained at a lower temperature by contact with a cooled surface.

13. The method according to claim 12, further including removing slacks formed in the crosslaminate by heating with hot air while cooling the remainder of the crosslaminate by contacting the crosslaminate with a cooled roller.

14. The method according to claim 1, further including supplying the first ply and/or the second ply with an admixture of a suitable powder such that microvoids are formed during incremental stretching that pierce the thinner webs to make the crosslaminate breathable.

15. The method according to claim 1, wherein laminating the first ply to the second ply includes passing the first and second plies together through a fourth pair of grooved rollers having a first roller with a first diameter and a second roller with a second smaller diameter.

16. A method of creating a laminate film including: passing a first ply of thermoplastic polymer material having a dominating direction of orientation in a longitudinal direction through a first pair of heated grooved rollers to 31 incrementally stretch the first ply in a transverse direction and create biaxially oriented thinner webs and first and second sets of uniaxially oriented bosses, the first set of bosses having a first thickness and the second set of bosses having a second thickness that is greater than the first thickness; wherein each crest on the grooved surfaces of the grooved rollers has two edges, each of which has a radius of curvature in the range 20 to 50 pm; and bonding a second ply of thermoplastic material to the first ply by bonding the bosses having the second thickness of the first ply to the second ply without bonding the bosses having the first thickness of the first ply to the second ply and without bonding the thinner webs of the first ply to the second ply.

17. The method according to claim 16, wherein the two edges protrude further than the rest of the crest to limit the contact between the first ply and the grooved rollers to the edge portions of the crests.

18. The method according to claim 16, wherein a pitch of the grooved rollers is less than 5 mm, and the distance from one to the other of the two edges on the crest is between 0.3-0.5 mm.

19. The method according to claim 16, wherein bonding the second ply of thermoplastic material to the first ply includes passing the first ply and the second ply together through a second pair of rollers.

20. A method of manufacturing a crosslaminate, substantially as herein before described with reference to the accompanying drawings; or a method of creating a laminate film, substantially as herein before described with reference to the accompanying drawings. THE GLAD PRODUCTS COMPANY WATERMARK PATENT AND TRADE MARKS ATTORNEYS P29493AU01