AU2008100563B4 - Method for the Recovery of Nickel from Ores

Info

Publication number: AU2008100563B4
Application number: AU2008100563A
Authority: AU
Inventors: Michael Rodriguez
Original assignee: POSEIDON NICKEL Ltd
Current assignee: POSEIDON NICKEL Ltd; Murrin Murrin Operations Pty Ltd
Priority date: 2008-06-13
Filing date: 2008-06-19
Publication date: 2008-09-04
Anticipated expiration: 2016-06-19
Also published as: AU2008100563C4; AU2008100563A4

Description

P/00/009 28/5/91 Regulation 3.2

ORIGINAL

AUSTRALIA

Patents Act 1990 COMPLETE SPECIFICATION INNOVATION PATENT Invention title: "METHOD FOR THE RECOVERY OF NICKEL FROM

ORES"

Applicant: Poseidon Nickel Limited The following statement is a full description of this invention, including the best method of performing it known to me: 00

O

CN "METHOD FOR THE RECOVERY OF NICKEL FROM ORES" SField of the Invention The present invention relates to a method for the recovery of nickel from D sulphide and/or oxide ores. More particularly, though not exclusively, the O invention relates to a hydrometallurgical method for leaching of nickel from a combination of nickel sulphide and nickel oxide ores.

00 O Background to the Invention Nickel sulphide ores have traditionally been treated via a pyrometallurgical smelting process, in order to recover nickel as a high grade nickel matte. The nickel content of the matte can range from 60 to 80% nickel as a sulphide. In Western Australia flash smelting and converting has been commercially applied to produce a high grade nickel matte 70% nickel, from nickel sulphide concentrates. The nickel sulphide concentrate is typically 12 to 18% nickel.

The high grade matte is subsequently refined utilising the Sherritt Gordon process.

Hydrometallurgical processes such as leaching have historically not been applied to nickel sulphide ores or concentrates, as smelting is commercially competitive when compared to hydrometallurgical processes. Unlike the Activox or Albion hydrometallurgical processes, smelting unlocks significant energy credits that is converted to electrical energy and produces sulphuric acid or sulphur as by-products. This co-generation approach improves the overall competitiveness of pyrometallurgical process when compared to hydrometallurgical processes.

Furthermore hydrometallurgical processes such as the Activox or the Albion Process typically require fine grinding P90 or minus 10 microns, which consumes energy. The energy released via the leaching process is lost to cooling towers or a simple flash system that does not capture any of the energy released during leaching.

-3- 00 oo It is well documented that hydrometallurgical treatments such as High SPressure Acid Leach (HPAL) plants operating in Western Australia have added sulphides as either "transition" sulphide ore or non-smeltable concentrates that cannot be treated via a conventional concentrator or smelter. However, these plants are limited in their ability to add sulphides due IDto the reducing nature of the sulphide ores or concentrates. The reducing Spotential of the sulphides lowers the oxidation reduction potential (ORP) and can result in damage to the HPAL titanium autoclave lining. Therefore these 00 plants are selective in the type of sulphide ore or concentrates added as secondary feed and they are also significantly limited in the amount of sulphide ore or concentrate that can be added to the HPAL process.

The treatment of sulphide ores via pyrometallurgical methods requires significant capital expenditure for flash furnace, convertors, slag treatment, as well as the utilities required such as power generators and sulphuric acid plants to capture sulphur dioxide emissions.

Some nickel sulphide ores also contain magnesium (Mg expressed as MgO) and when treated through a concentrator produce a sulphide concentrate that has a low iron (Fe) to MgO ratio. A low iron to MgO ratio impacts on flash furnace slag chemistry. The slag becomes viscous and can be difficult to remove from the furnace without increasing the slag operating temperature.

Some of these ores also contain arsenic (As) at levels that require careful blending to manage the occupational health and safety aspects of arsenic and its impact on human health, which makes these sulphide ores undesirable for smelting.

The present invention aims to alleviate or at least partially alleviate some of the difficulties associated with the conventional pyrometallurgical and hydrometallurgical processes for the treatment of nickel sulphide ores or concentrates. However it will be understood that it is not limited in its application to nickel sulphide ores or concentrates.

The previous discussion of the background to the invention is intended to facilitate an understanding of the present invention only. The discussion is not -4- C an acknowledgement or admission that any of the material referred to is or was part of the common general knowledge as at the priority date of this

;Z

o application. References to prior art in this specification are provided for illustrative purposes only and are not to be taken as an admission that such prior art is part of the common general knowledge in Australia or elsewhere.

ICN

Summary of the Invention According to one aspect of the present invention there is provided a oo Shydrometallurgical method for leaching a base metal in a combined pressure C 10 acid leach, the method comprising the steps of: combining a sulphide ore or concentrate with a laterite or other oxide ore and mixing them together to form a slurry; leaching the combined slurry in a pressure acid leach circuit; and, providing an oxidant to the pressure acid leach circuit wherein the oxidant allows for the conversion of substantially all of the sulphide to transition through to sulphate.

Preferably the step of combining sulphide ore or concentrate with laterite or other oxide ore and mixing them involves milling the ores together.

Preferably the method comprises the further step of leaching the combined sulphide and oxide ore together with pregnant leach solution produced from an atmospheric leach circuit, and without the requirement of additional sulphuric acid.

Typically the base metal is selected from the group consisting of nickel, cobalt, copper, lead and zinc. Preferably the sulphide ore or concentrate is a nickel sulphide or concentrate and the laterite or other oxide ore is a nickel laterite or other nickel oxide ore.

Preferably the method further comprises the steps of directing a nickel laterite or other nickel oxide ore to an atmospheric leach process to produce a pregnant leach solution, and adding the pregnant leach solution to the o00 c combined sulphide ore or concentrate and laterite or other nickel oxide ore Z during the combining step.

oO 0 Preferably the pressure acid leach circuit comprises a series of pressure Pachuca tanks.

IN According to another aspect of the present invention there is provided a Shydrometallurgical method for leaching nickel, the method comprising the 00 steps of: Scombining nickel sulphide ore or concentrate with nickel laterite or other nickel oxide ore in relative proportions selected to achieve optimum density and milling them together to form a slurry; leaching the combined slurry in a pressure acid leach circuit; and, providing air or oxygen to the pressure acid leach circuit wherein the air or oxygen allows for the conversion of substantially all of the nickel sulphide to transition through to nickel sulphate.

Preferably the method further comprises the steps of directing a nickel laterite or other nickel oxide ore to an atmospheric leach process to produce a pregnant leach solution, and adding the pregnant leach solution to the combined sulphide ore or concentrate and laterite or other nickel oxide ore during the combining and milling step.

The pregnant leach solution (PLS) from the atmospheric leach circuit preferably has a ferric iron concentration within the range of 10 to 60 g/L.

Preferably, the PLS from the atmospheric leach circuit has a free acid concentration of less than 30 g/l. Preferably the PLS from the atmospheric leach circuit has a nickel concentration of >4 g/l.

The nickel sulphide ore or concentrate preferably has a nickel concentration within the range of about 1 to 10% Ni. Preferably, the nickel laterite or oxide ore has a nickel concentration within the range of 0.8 to More preferably, -6- 00 C the nickel laterite or oxide ore for the atmospheric leach is a saprolite or Z smectite ore and the laterite or oxide ore required for the combined leach is a 00oO limonite ore.

Preferably the pressure acid leach circuit comprises a series of pressure SPachuca tanks.

INO

SPreferably, the free acid concentration achieved in the combined leach is 0 maintained within the range of 30 to 80 g/l. Preferably, the temperature within the pressure Pachuca tanks is maintained between 1600 to 260 0 C. More preferably, the temperature within the pressure Pachuca tanks is maintained at about 2200 to 250 0 C. Preferably, the oxygen over pressure within the pressure Pachuca tanks is maintained between 100 to 1000 kPag.

Typically, the ratio of nickel sulphide ore or concentrate: nickel laterite or other nickel oxide ore in the combining step is about 3:7.

Advantageously the process of leaching the combined slurry approaches autogenous leaching, releasing energy, generating sulphuric acid and producing hematite and alunite as the predominant residue minerals.

Throughout the specification, unless the context requires otherwise, the word "comprise" or variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated integer or group of integers but not the exclusion of any other integer or group of integers. Likewise the word "preferably" or variations such as "preferred", will be understood to imply that a stated integer or group of integers is desirable but not essential to the working of the invention.

Brief Description of the Drawings The nature of the invention will be better understood from the following detailed description of several specific embodiments of the hydrometallurgical method for leaching of nickel according to the invention, given by way of example only, with reference to the accompanying drawing in which: 00 C Figure l(a) and is a schematic diagram of a process circuit of a preferred method for leaching nickel in accordance with the present invention.

_Detailed Description of Preferred Embodiments A preferred embodiment of the hydrometallurgical method for leaching of O nickel according to the invention, as shown in schematic form in Figure 1, O relates to the leaching of nickel. The method preferably comprises the step of 0 directing a nickel laterite or other nickel oxide ore to an atmospheric leach oo O process 10, which in the embodiment of Figure 1 is a first heap leach process c 10 (not illustrated). The clarified pregnant leach solution (PLS) from the first heap leach process is then directed to a milling circuit 12. The PLS is preferably heated prior to injection into the milling circuit 12. The PLS may be derived from any suitable atmospheric leach process and is not limited to heap leaching. However in the event that a suitable source of PLS from an atmospheric leach process is not available, water may be substituted for the PLS that is directed to the milling circuit.

The method further comprises the step of combining nickel sulphide ore or concentrate 14 with nickel laterite or other nickel oxide ore 16 and milling the combination in the milling circuit 12 with the clarified PLS from the first heap leach process 10 (and/or water as the case may be). The nickel sulphide ore or concentrate 14 preferably has a nickel concentration within the range of about 1 to 10% Ni. Preferably, the nickel laterite or other nickel oxide ore 16 should have a nickel concentration within the range of 0.8 to 3% Ni. Typically, the ratio of nickel sulphide ore (or concentrate): nickel laterite ore (or other nickel oxide ore) is about 3:7. More preferably, the nickel laterite or nickel oxide ore for the atmospheric leach is a saprolite smectite ore and the laterite or oxide ore used for the combined leach is a limonite ore.

The viscosity of laterite ores is impacted by additives such as free acid or total dissolved solids. Limonites typically exhibit a reduction in viscosity when solutions from a heap leach operation are slurried with limonite ores. That is, for a given weight percent, solids milling in PLS reduces the viscosity of the pulp. However with saprolite or smectite ores slurrying in PLS will increase -8oo 00 c the viscosity for a given weight percent solids. Adding sulphides to all laterite ores, whether limonite, saprolite or smectite, acts to reduce the viscosity and

;Z

is considered innovative. By appropriate selection of the relative proportions of both kinds of minerals in the combined ores, milling at optimum density can be achieved. Therefore saprolite or smectite is the preferred ore for the IDatmospheric leach, and limonite is the preferred ore for milling in atmospheric SPLS due to the improvement in slurry density achieved.

00oo The milling is typically carried out using the PLS from the first heap leach process instead of, or in addition to, water. The clarified PLS from the first heap leach process preferably has a ferric iron concentration within the range of 10 to 60 g/l. Preferably the PLS from the first heap leach process 10 has a free acid concentration of less than 30g/l. Preferably the PLS from the first heap leach process 10 has a nickel concentration of more than 4 g/l. Hence a further significant benefit of adding the PLS to the milling circuit 12 is that the head grade of ore passing through the plant is doubled. This, together with acid credits, greatly improves the economies of scale and efficiency of the plant.

The milled combined ore from the milling circuit 12 is then subject to a screening step in screening circuit 18. Oversize ore is directed from the screening circuit 18 back to the first heap leach process 10. Undersize ore is fed from the screening circuit 18 to a slurry tank 19, and the combined slurry is then pumped by high pressure slurry pumps to a combined pressure acid leach circuit 20. Wash from the screening circuit 18 is returned to the milling circuit 12.

In the illustrated embodiment the combined pressure acid leach circuit comprises a series of pressure Pachuca tanks 22, in which pressure leaching of the combined slurry occurs preferably without the addition of sulphuric acid.

Preferably the temperature within the pressure Pachuca tanks is maintained between 1600 to 2600 C, and more preferably between 2200 to 2500 C. The use of brick-lined Pachuca tanks 22 instead of an autoclave, is much less expensive to maintain due to the high maintenance cost of the titanium used -9- Sin autoclaves. Typically, pressure leaching in the combined pressure Pachuca Sacid leach (CPPAL) circuit 20 occurs for about 90 minutes at a temperature of

;Z

about 2500 C and a pressure of about 44 bar. The nickel and cobalt in the combined slurry is converted to soluble sulphates. More particularly, the nickel and cobalt in the form of sulphides is largely converted to the metal IDsulphates via the usual chemical transition steps.

An oxidant is preferably injected into the Pachuca tanks 22. The preferred o00 oxidant is oxygen or air; ferric iron generated in a separate atmospheric leach process, and/or manganese present in the ores as manganese dioxide (MnO 2 may also be used. Preferably, the oxygen over pressure within the pressure Pachuca tanks is maintained between 100 to 1000 kPag. Without oxygen or air in the CPPAL a significant amount of iron as ferrous remains in solution "locking up" sulphuric acid. However with sufficient oxygen (or other oxidant) most of the iron is converted to hematite.

The combined ore is preferably leached in the pressure Pachuca tanks 22 without adding acid and most of the energy required is generated by the oxidation of the sulphide minerals. Advantageously the process within the CPPAL 20 approaches autogenous leaching, releasing energy, generating sulphuric acid and producing hematite and alunite as the predominant residue minerals. As is well known in the art, sulphides produce acid, whereas laterites and other oxide ores consume acid. Therefore with the correct balance of the two kinds of ores in the combined slurry fed to the CPPAL the acid released in the hydrolysis circuit as free acid can be matched with the acid consumed. However if additional acid is required an acid plant 24 is provided to direct high pressure acid to the Pachuca tanks 22. Steam generated by the acid plant 24 is also injected into the Pachuca tanks 22 at bar. The balance of the steam may be used for generating power.

The resulting leach slurry exiting from the pressure Pachuca tanks 22 is at high temperatures (typically between 1600 to 2600 Some of this heat is used to preheat the combined slurry as it is fed into the CPPAL 20 to further improve the efficiency of the CPPAL 20. For this purpose a heater coil 26 00 oO C uses some of the waste heat to generate steam, which is then fed back to a preheat circuit 28 on the CPPAL feed to heat the combined slurry to about o 1760 C. The PLS solutions have been found to scale in a similar way that an autoclave will scale in a typical HPAL operation. Increasing the temperature beyond 180' C will initiate the precipitation of iron and aluminium t' IDpredominantly. In the proposed system the first stage preheater 28 is kept Sbelow 180' C to prevent iron and aluminium in the PLS solution (added to the milling circuit) from precipitating in the preheat circuit.

oO The leach slurry exiting from the CPPAL 20 undergoes further cooling to atmospheric temperature and pressure in a flash cooling circuit 30. Waste heat from the flash cooling circuit 30 is used for preheating the PLS from the first heap leach process 10. The leach slurry then undergoes solid/liquid separation (thickening) in a counter current decantation (CCD) circuit 32 (see Figure The CCD circuit 32 typically consists of five thickeners which separate the slurry into two streams. The first stream consisting of the pressure leach residue solids is eventually sent as underflow from the last thickener to tailings. The second stream consisting of the clarified solution (containing dissolved nickel and cobalt sulphates) is then preferably directed to a second heap leach process 34 (not shown).

The clarified solution from the CCD circuit 32 still has a substantial volume of free acid (typically about 20 litres/tonne) available for further downstream processing. The purpose of the second heap leach process 34 is to utilise this free acid for further leaching of nickel (and cobalt) from a nickel laterite or other nickel oxide ore, rather than wasting it by removal in a neutralisation circuit. However, if preferred, the free acid can be removed in a conventional neutralisation circuit, without passing the solution through a second heap leach.

The PLS from the second heap leach process 34 is then subject to iron removal using calcrete in a conventional precipitation circuit 36 consisting of a series of agitated tanks. Calcrete is not as efficient as limestone or quicklime for iron removal, however it is readily available locally. The calcrete 37 is 11- 00 N milled and mixed with water to produce calcrete slurry. The calcrete slurry is used to neutralise the free acid in the PLS from the second heap leach process, and to precipitate the ferric ions in solution as jarosite/geothite.

An iron free clarified solution is obtained by treating the solution from the C precipitation circuit 36 in a second CCD circuit 38 for solid/liquid separation *V (thickening). The thickener underflow solids are discharged with the pressure O leach residue solids from the first CCD circuit 32 to tailings. The iron free 0 clarified solution is then subjected to a direct solvent extraction process and electrowinning process 42 in a conventional manner for the extraction and refining of nickel, cobalt, zinc and copper. Solvent extraction raffinate and a barren liquor bleed from the electrowinning process 42 is returned to the first CCD circuit 32 as wash liquor.

The present invention is further illustrated by way of the following non-limiting examples: Example 1 One combined pressure acid leach was conducted at 2550C at 30% (w/w) sulphide ore. The approximate ratio of sulphide ore: laterite ore used was of the order of 7:3, and the ores were milled together in accordance with the invention. The compositions of the laterite and sulphide ores are provided in Table 1.

Table 1 Sample Unit Analysis Ni Co Fe Fe(lll) Mg S 2 S° FA Sulphide 1.25 0.009 15.0 4.1 10.5 0.8 Laterite 1.2 0.09 17.0 5.7 Leach Sol g/L 5.5 0.40 47 45.0 25 12-

OO

O

=N

ca The results from the leach test are provided in Table 2.

The main observations from this test were: No acid addition to the CPPAL was required 700 kPag oxygen overpressure was maintained using oxygen Almost all of the iron precipitated as hematite Almost all the aluminium precipitated as alunite Over 94% nickel and cobalt extraction was achieved for the combined leach The nickel concentration in the PLS after 90 minutes was much higher than for a typical HPAL circuit (10 g/L compared with 6 g/L).

Table 2 The test conditions are provided in Table 3.

Table 3 Test No. Vol. of Acid Addition, kglt Sulphide Ore Column PLS 1 30 100 Nil -13oO 00 C Conclusions: SThe CPPAL of a combined laterite or oxide ore with a sulphide ore or _concentrate when leached in pregnant solution from a separate atmospheric leach process, with an overpressure of oxygen of 700 kPag, can successfully C' extract nickel and cobalt without the addition of acid.

\O

It is therefore envisaged that with appropriate blending of sulphide ore or concentrate in combination with a laterite or oxide ore milled in pregnant oO Ssolution from an atmospheric leach circuit, the combined blend can be C 10 successfully leached without the addition of acid in a pressure Pachuca with oxygen over pressure.

It is further envisaged that saprolite or smectite is used for the atmospheric leach and limonite is the preferred ore for milling in atmospheric leach pregnant solution due to the improvement in slurry density achieved.

It is further envisaged that clarified solution from either a heap leach or atmospheric leach can be applied to replace water for milling in the CPPAL circuit.

It is further envisaged that a direct synergistic solvent extraction and electrowinning process is applied for the extraction and refining of nickel, cobalt, zinc and copper.

It is also envisaged that the CPPAL process can be applied to a wide variety of nickel, cobalt, copper and zinc bearing laterite and sulphide ores or concentrates.

Furthermore it is also envisaged that some mines can be unconstrained by the successful application of the above process as it is tolerant to arsenic and iron to magnesium chemistry.

Now that preferred embodiments of a hydrometallurgical method for leaching nickel in a combined pressure acid leach have been described in detail, it will be apparent that the embodiments provide a number of advantages over the prior art, including the following: -14- 00 oO C The combined Pachuca pressure acid leach (CPPAL) significantly reduces the acid production requirement per tonne

;Z

of ore treated.

(ii) The CPPAL process approaches autogenous heating therefore Sreducing external energy generation requirements.

(iii) The CPPAL process is undertaken in brick-lined Pachuca tanks instead of an autoclave, which is less expensive to maintain oO than titanium-lined autoclaves.

(iv) The CPPAL process can be applied to a wide variety of nickel, cobalt, copper, lead and zinc bearing laterite and sulphide ores or concentrates.

It will be readily apparent to persons skilled in the relevant art that various modifications and improvements may be made to the foregoing embodiments, in addition to those already described, without departing from the basic inventive concepts of the present invention. Therefore, it will be appreciated that the scope of the invention is not limited to the specific embodiments described.

Claims

2. A hydrometallurgical method for leaching nickel as defined in claim 1, further comprising the steps of directing a nickel laterite or other nickel oxide ore to an atmospheric leach process to produce a pregnant leach solution, and adding the pregnant leach solution to the combined sulphide ore or concentrate and laterite or other nickel oxide ore during the combining and milling step.
3. A hydrometallurgical method for leaching nickel as defined in claim 2, wherein the ratio of nickel sulphide ore or concentrate: nickel laterite or other nickel oxide ore in the combining step is about 3:7.
4. A hydrometallurgical method for leaching nickel as defined in any one of claims 1 to 3, wherein the nickel laterite or oxide ore for the atmospheric leach is a saprolite or smectite ore and the laterite or oxide ore required for the combined leach is a limonite ore. A hydrometallurgical method for leaching nickel as defined in any one of the preceding claims, wherein the pressure acid leach circuit comprises a series of pressure Pachuca tanks. Dated this 28 th day of July 2008 Poseidon Nickel Limited by its Patent Attorneys Janet Stead Associates