AU2007202864A1 - Biotechnological process for the treatment of As-containing hydroxide sludge resulting from potable water treatment processes which use FeC13 as a coagulant, through the action of sulfate reducing bacteria - Google Patents
Biotechnological process for the treatment of As-containing hydroxide sludge resulting from potable water treatment processes which use FeC13 as a coagulant, through the action of sulfate reducing bacteria Download PDFInfo
- Publication number
- AU2007202864A1 AU2007202864A1 AU2007202864A AU2007202864A AU2007202864A1 AU 2007202864 A1 AU2007202864 A1 AU 2007202864A1 AU 2007202864 A AU2007202864 A AU 2007202864A AU 2007202864 A AU2007202864 A AU 2007202864A AU 2007202864 A1 AU2007202864 A1 AU 2007202864A1
- Authority
- AU
- Australia
- Prior art keywords
- sludge
- water
- treatment
- treated
- coagulant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
;Z
CAf
AUSTRALIA
PATENTS ACT 1990 COMPLETE SPECIFICATION NAME OF APPLICANT(S):: Universidad Catolica Del Norte ADDRESS FOR SERVICE: DAVIES COLLISON CAVE Patent Attorneys 1 Nicholson Street, Melbourne, 3000, Australia INVENTION TITLE: Biotechnological process for the treatment of As-containing hydroxide sludge resulting from potable water treatment processes which use FeC13 as a coagulant, through the action of sulfate reducing bacteria The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5102 Subject of the invention The present invention reveals a biotechnological process for the treatment of As- INO containing hydroxide sludge resulting from potable water treatment processes, which use 00 CK1 FeCI 3 as a coagulant, through the action of sulfate reducing bacteria.
State of the art Urban residual water treatment has undergone important progress during the last decades. Research on the effects of contaminants, more strict environmental regulations and economic factors have propelled the development of new technologies, being the main challenge waste minimization.
Hydroxide sludge resulting from physicochemical sedimentation of water in potable water treatment plants has minor content of organic matter and an important amount of water. Its characteristics will depend on physicochemical properties of raw water to be treated as well as the chemical reactants added to the water (Marin, G. R. (1998). "Gesti6n de lodos hidr6xido." Ingenieria Quimica: 173-178).
In the majority of water treatment plants, the physicochemical process of coagulation is oriented to reduce, as much as possible, suspension matter, color and turbidity of natural water.
In arsenic abatement plants, in comparison with turbidity treatment plants, the dosage of coagulant is higher in comparison to plants designed for particulate material reduction in fresh water (dosage between 40.5 56.1 ppm FeCI 3 According to Slater equation 1973. Disposal of waterworks sludge: Final Report of Research Panel, n' 14. Institution of Water and Environmental Management 27 399-408), this treatment also produces a larger amount of sludge mass in dry matter per treated raw water volume unit, compared to particulate material abatement plants. The increase in sludge volume produced makes difficult its final disposal. Also, it is worth to note that the presence of arsenicated sludge makes it a dangerous waste.
The first operation in the treatment of hydroxide sludge is thickening, which is carried out in a gravity thickener, or also in floating thickeners. From the thickening process sludge with a solid concentration between 2% and 8% and a clear effluent result. After thickening, the sludge is subjected to a dehydration process. The processes used for this aim are Smechanical dehydration processes, like centrifugation and filtration systems (press filters, (Ni Sband filters or vacuum filtration) able to increase the solid content in waste to values around In 25 to 30%. The disadvantage of these methods is that an important amount of humidity is still 0 being disposed, thus creating an excess of volume in the disposal process, an increase in (Ni lixiviates and increased costs in transport and disposal.
Use of mechanical dehydration processes for treatment of sludge coming from
ID
00 decanter tanks depends on the volume and characteristics thereof, where determinant (Ni parameters are amount and decantability, specific resistance to filtration and compressibility coefficient.
SThere are drying systems whose adaptation to industrial processes entails a series of difficulties. Heat drying of sludge consists on direct or indirect contact of sludge with gases at high temperature to reduce the humidity content to 10% as a minimum. Direct drying is appropriate for easily disaggregating products, but is complicated when an amorphous, very humid mass with plastic characteristics impeding its disaggregation is to be treated (Undebarrena, M. (1999). "Tratamientos de lodos: Deshidratacion termica de lodos en el ambito industrial." Ingenieria Quimica: 99-102). On the other hand, it requires vast areas in relation to the sludge volume for drying to facilitate heat penetration and water transport to the drying surface.
The developed biotechnological treatment process seeks to modify the physicochemical properties of the produced sludge in such a way to facilitate the use of mechanical dehydration methods that allow decreasing the sludge volume and facilitating its final disposal.
Anaerobic systems for treatment of residual waters The developed process is based on the action of sulfate reducing bacteria (SRB) on the hydroxide sludge (which have minor content of organic matter and important amounts of associated water) to which an electron acceptor is added, for example sulfate, a source of carbon such as ethanol and a vitamin supplementation, for example yeast. The reactor of the invention should help to reduce the presence of oxygen in the system since sulfate-reducing bacteria are anaerobic.
Anaerobic digestion is used in treatment of residual waters with high organic charge (2,000 to 30,000 or more BOD/I), as in the case of aromatic hydrocarbon contaminated waters (Coates, Achenbach, 2004. Microbial perchlorate reduction: rocket-fueled L metabolism. Nat Rev Microbiol 2 569-80). These concentrations are present in many Sresidues, such as food and agriculture industries. In this process, colloidal and soluble Sorganic matter is transformed into volatile acids, which in turn are transformed into methane 0n and carbon dioxide. Different kinds of bacteria produce either acid or methane fermentations.
SThe produced gases contain 65% of OH 4 which allows taking advantage of it to keep a suitable temperature for digestion, around 371C, and counting on an energy surplus, depending on the characteristics of the residual water.
\O
00 ri Sulfate Reducing Bacteria C( Sulfate is used as an electron acceptor in anoxic conditions by a set of heterogeneous bacteria using fatty acids, alcohols and hydrogen as electron donors. Sulfate Cr reducing bacteria (SRB) can be considered as a unified handful of bacteria using lactate, pyruvate, ethanol and certain fatty acids as carbon and energy sources, reducing sulfate to hydrogen sulfide. Other known group of bacteria is specialized in oxidation of fatty acids, particularly acetate, reducing sulfate to sulfide. Anoxic techniques have to be used to culture reducing bacteria since they are anaerobic.
Sulfate reducing bacteria are vastly distributed in aquatic and terrestrial environments, which become anoxic due to certain microbial decomposition processes.
Bacteria responsible for sulfate dissimilatory reduction include Desulfovibrio and Desulfotomaculum. Both bacteria require anoxic conditions for its respiratory processes and use of sulfate and other sulfur oxidized compounds S032 S2032) as electron acceptors.
Description of the technical problem solved In the treatment and water recovery systems, it is required to purge the sludge from the storing tank of disposal waters. This sludge has a solid content lower than The characteristics of the produced sludge and its volume make it difficult the use of mechanical dehydration techniques such as centrifugation and filtration systems. The arsenic content in the sludge, on the other hand, prevents its treatment as non-dangerous sludge produced in water treatment plants, which are normally disposed into a municipal sewer system, public continental channels or seawater. Present regulations consider as dehydrated sludge for transport and final disposal those with a humidity percentage of 70% or lower.
Water contamination becomes very important in the need to preserve the environment, since contaminants can be accumulated and transported through streams, rivers, lakes, dams and underground waters, directly affecting human health and wildlife. The L most important sources of surface and underground water contamination are industrial and urban wastewaters.
SSludge disposal is a problem in the control of contamination in the form of air, water and ground pollution due to solid, liquid and gas emission generated from productive processes.
The process of the invention to treat arsenicated sludge allows obtaining a residue whose characteristics comply with environmental laws. namely:
IO
00 The solid residue obtained as final product has a water content lower to It is stable in lixiviation assays.
Has a slightly higher density than raw sludge, which represents an advantage to the possible wind dispersion effect.
The quality of the recovered water is within the limits allowed by Chilean law for irrigation or final disposal into sewer systems or into seawater and continental surfaces.
The application of the developed treatment process reduces: Volume of industrial waste with arsenic to be disposed securely.
Costs of transport.
Area required for disposal.
Contamination risks.
The efficiency of the process of potable water production is increased by the technology developed, recovering more than 50% of the water, which is currently discarded.
The revealed process in the present invention allows reducing costs in the stage of dewatering and dehydration of sludge coming from potable water production processes, thus giving stability characteristics to the solid residues which will have to be finally disposed in a secure way.
Figure Description Figure 1. General diagram of installations for treatment of hydroxide sludge coming from a potable water production process using fluvial water as source with FeCI 3 as a coagulant.
Description: 1. Bioreactor hut 2.9 m x 3.4 m x 2.5 m 2. Bioreactor 3. Internal squared coil 4. Thermocouple Charge inlet and outlet, respectively (N 6. Centrifugal pump for sludge recirculation 7. Centrifugal pump for coil water 8. Heater 00 9. Water tank Decanter 11. Squared bed filter 12. Sludge distributors 13. Filtered water recollection nozzles Figure 2. Test tube sedimentation plot: allows comparison of characteristics between treated and untreated sludge. In this plot, sludge treated with the present invention process present a higher sedimentation rate than raw sludge, favoring solid residue and residual water separation.
Figure 3. Paper filtration at atmospheric pressure plot: allows comparison between treated and untreated sludge. In this plot, treated sludge shows a significantly increased filtration rate favoring the dewatering process of these residues.
Figure 4. Total arsenic and iron concentrations in supernatant during a bioreactor test. In this plot, total arsenic and iron concentration in supernatant decrease by the end of treatment due to precipitation caused by bacterial action. These results show the advantage of the process with respect to residual water production, which can be used as irrigation water, according to Chilean regulations.
Figure 5. Organic matter analysis in sludge over time. Organic matter decrease over time is expressed as BOD 5 These results show that organic matter supplemented to the bioreactor is enough and is consumed almost completely during sludge treatment in bioreactor. The presence of organic matter in the solid residue would generate a new problem for these residues.
Figure 6. Sludge humidity percentage decrease in bed filter. This plot shows that 20% water Scontent in the solid residue is reached in 9 days. Hence, drying times and water content of Sthe solid residue for final disposal are decreased.
Description of the invention The developed process is based on the action of sulfate reducing bacteria (SRB) on hydroxide sludge with an electron acceptor added such as sulfate, a carbon source such as INO ethanol and a vitamin source such as yeast.
00 C Sulfate reducing bacteria are anaerobic; hence the process is carried out in a reactor C" ensuring a reduced presence of oxygen, temperature control adequate for bacterial action and proper mixing to obtain a homogeneous product.
The process of the present invention comprises the following stages: Preparation of Sulfate reducing microorganisms (SRB) Biological material used as an initial inoculum in the process is obtained through selective enrichment of the microbial population present in the same sludge to be treated.
This sludge is composed by sulfate reducing microorganisms.
Microbial enrichment is performed by incubating raw sludge for 7 days with nutrients added (ethanol, yeast and sodium sulfate) and with no inoculum addition. Nutrient concentrations are as follows: 0.01 to 1.0 g/ ethanol, 0.01 to 1.0 g/ yeast and 0.01 to 0.5 g/ sodium sulfate. Incubation is performed at 15 to 320C.
Microbial enrichment is assessed through the capacity to perform an efficient sludge treatment by reducing sludge volume and favoring dewatering.
An initial inoculum volume of 10% the volume of the bioreactor is prepared for the initial process.
of the previous treated sludge is left in the bioreactor as an inoculum for successive batches.
Biological material isolated from treated sludge is characterized in Iverson and Newman solid mediums. Culture independent methods based on analysis of 16S rRNA for identification of microorganisms responsible for the process are also used.
For a specific sludge source, successive enrichment processes will raise a bacterial population composed by sulfate reducing bacteria, fermentative bacteria and bacteria able to precipitate arsenic such as As 2
S
3 Combination of the sludge to be treated, the inoculum obtained in stage and nutrients Sin the bioreactor SSludge to be treated with an approximate solid content between 1,500 and 3,000 mg L1, nutrients (0.01 to 1.00 g/l ethanol, 0.01 to 1.0 g/l yeast and 0.01 to 0.5 g/l sodium sulfate) and an inoculum with a volume equal to 5 to 30% of the total reactor volume are placed in an anaerobic reactor with mixing, temperature control and a manometer.
The system is started up with temperature control between 15 and 320C. Mechanical
\,O
00 mixing is provided to allow sludge homogenization in such a way that no untreated zones remain. Mixing should be gentle to allow higher density granule formation.
Residence time of sludge in the bioreactor is from 4 to 7 days.
Treated sludge sedimentation Treated sludge is subjected to sedimentation in a decanter. The sedimentation stage has a duration of approximately 3 days.
The clarified liquid is recovered and the sediment is then subjected to a dewatering process through filtration or centrifugation.
The sedimentation process allows up to 70% recovery of clarified water with arsenic and iron concentrations of 0.3 and 3.69 mg/I respectively.
Solid residue from decanter filtration Solid residues from sedimentation stage are transferred to a bed filter to recover up to 11% of water and obtain the final residue.
Final residue characterization Solid residue water content, density, As, Fe and organic matter content are analyzed.
Lixiviation assays to analyze residue stability are also performed following, for example, the EPA method 1311 "Determination of toxicity through lixiviation procedure". The solid residue is ready to be transported to the definitive disposal site.
On the other hand, As, Fe, total solids, turbidity and fecal coliform populations in the recovered filtered water are analyzed. According to the recovered water characteristics, said water could be used for irrigation and/or released into surface water streams.
Application example S"Hydroxide sludge coming from potable water production from fluvial water using FeCI 3 ;as a coagulant was treated with the process of the present invention.
(,KI An inoculum was prepared in 6 20-liter drums with a 7 liter culture obtained through selective enrichment of microbial populations present in the sludge to be treated. Initial Ienrichment was prepared incubating the sludge to be treated (500 ml) in anaerobic 00 conditions at 280C with added nutrients (0.82 g/I ethanol, 0.5 g/ yeast extract and 0.25 g/ sodium sulfate). Successive subcultures with larger volumes, using the same conditions, allowed obtaining 7 liters of culture to inoculate the first drum.
A 20-liter drum was filled with sludge, nutrients, ethyl alcohol (0.82 sodium sulfate instant yeast (0.25 and 7 liters from the initial enrichment were added. The drum was incubated at room temperature for 7 days.
At the end of the week, half the content of the drum was transferred to a new drum, and corresponding amounts of substrates were added (ethanol, sodium sulfate and yeast) to each drum and enough sludge to fill the drums completely. The procedure was repeated until 400 liters necessary to inoculate the reactor were obtained.
The volume added to the bioreactor (400 I) was 10% of the total capacity of the bioreactor. In subsequent cycles, 10% of the treated sludge was left as an inoculum for the new batch.
A suitable reactor to perform the anaerobic process of the present invention was designed. The reactor comprises a discontinuous mixer system which is basically a pump withdrawing sludge from one zone of the reactor and pumping it into another zone. A coil with water heated in a water-heater circulating through it propelled by a pump (7) was used to keep a constant temperature inside the reactor. The tank walls and bottom were coated on their outside with 2.5 cm of glass wool as an insulator (for a 10 m 2 area). The system is completed with a bottom inlet and outlet (5 and and manometers. A 5 m 3 resincovered fiberglass tank was used for the anaerobic bioreactor construction. The bioreactor was installed in a hut prepared for this goal. Temperature was registered with a thermocouple When temperature inside the reactor fell below 300C, the heating system was turned on.
Mixing was performed through mechanical pumping of sludge through external recirculation ducts using a centrifugal pump (1,700 I/min). Fiberglass was used to construct 4 baffles with the following size: 19 cm wide and 1.7 m height.
Proper connections were made for sludge feeding from the water recovery tank and sludge drainage from bioreactor to the decanter.
SThe manometer was installed to control the possible production of H2S due to 1n bacterial sulfate reducing activity.
SThe reactor was installed 3 m above the ground to facilitate sludge discharge to the decanter placed at ground level. The reactor was installed above the discarded water recovery tank.
\,O
00 The bioreactor was fed with sludge, designated as "raw sludge", which was extracted using a submersible pump from the discarded water tank. The solid content of raw sludge was 2,500 mg/I. The following nutrients were added: 0.5 gll yeast, 0.25 g/l sodium sulfate and 0.16 g/I ethanol.
The sludge residence time was 7 days with a daily mixing period of 1 hour. The temperature inside the bioreactor was kept at 300C.
The treated sludge was transferred to the decanter by means of the level difference.
Fiberglass was used to build the 5 m 3 tank for sludge sedimentation.
All connections needed for extracting sludge from the bioreactor and sludge transferring to bed filter and recovery of clarified water were made.
The sedimentation rate was evaluated at the end of the test in the bioreactor. Measurements were made in test tubes obtaining a curve of interface height vs. time. Using Talmage and Fitch method, 1955 (Talmage, and Fitch, 1955, Determining thickener unit areas, Ind. Eng. Chem., Vol. 47, No. 1, pp. 38-41), and using the system of tangents to the obtained curve, sedimentation rate was determined to be 0.0560 m/h The sedimentation stage has a duration of 2 days after the transfer of treated sludge from the bioreactor to the decanter. Once sedimentation has finished, clarified water is withdrawn through the upper part of the tank using a submersible pump and the treated sludge is transferred to the bed filter.
Solid content of sediment and recovered water characteristics were analyzed.
The solid content obtained in the decanter is shown in Table 1.
Table 1. Sludge solid content in the bioreactor and decanter.
Sample ST (mg/L) Raw sludge in bioreactor inlet 2.645 Treated sludge in bioreactor outlet 2.925 Clarified water from decanter 1.759 Treated sludge decanter outlet 9734 70% of clarified water was recovered with arsenic and iron concentrations of 0.30 and S3.69 mg/I respectively.
=Solid sediment residues are transferred to the bed filter using level difference. A 7.84 Sm 2 wood polyethylene coated bed filter (11) was constructed with three filtering layers. The first layer is composed of quartz (2 m3), the following layer is composed of a mix of quartz and sand (2 m 3 and the final layer is composed of fine sand (1 m 3 The height difference 0 between the decanter (10) and the bed filter allows the transfer of sludge using sludge Sdistributors (12) with no need of pumps. Filtered water percolate is drained through nozzles (13).
Around 11% of water from the bed filter was recovered, with arsenic and iron (N concentrations of 0.068 and 0.04 mg/l respectively, a turbidity of 195 NTU and 40 mg/l average total solids. The content of fecal coliforms in filtered water was around 200 to 1,000 CFU/100 ml.
After nine days of filtration and evaporation, the solid residue had a humidity of and was stable in lixiviation assays performed according to method 1311 "Determination of toxicity through lixiviation procedure, EPA" (Table Dry treated sludge has a slightly higher density than dry raw sludge (Table suggesting an advantage when taking into account the possible dispersion due to wind Average composition in dry base was 14.5 g/kg As, 240 g/kg Fe and 30 g/kg organic matter.
Table 2. As and metal concentration in lixiviation solutions of final product Sample Time As Fe Mn Mg (days) (ppm) (ppm) (ppm) (ppm) Raw sludge 0 0.545 <0.03 1.185 5.505 Raw sludge 14 0.038 0.093 13.300 15.250 Treated sludge 0 1.365 0.042 0.960 2.025 Treated sludge 14 0.068 0.078 9.550 8.050 Chilean regulation establishes a maximum of 5 mg/l As in lixiviates.
Table 3. Density determination of sludge results in mg/ml determined by picnometry.
I Treated sludge density 2.4062 2.6506 2.4117 average 2.4895 Raw sludge density 2.0429 2.0969 2.0211 average 2.0536 00 Results in Table 3 show the increase in density of treated sludge compared to raw sludge. This increase is an additional advantage of the final product compared to the raw sludge since wind dispersion is more difficult.
Throughout this specification and the claims which follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps.
The reference in this specification to any prior publication (or information derived from it), or to any matter which is known, is not, and should not be taken as an acknowledgment or admission or any form of suggestion that that prior publication (or information derived from it) or known matter forms part of the common general knowledge in the field of endeavour to which this specification relates.