Patents Act 1990 COMPLETE SPECIFICATION FOR A DIVISIONAL PATENT

ORIGINAL

TO BE COMPLETED BY APPLICANT Name of Applicant: Actual Inventors: Address for Service: Invention Title: HUNTSMAN INTERNATIONAL LLC DAUNCH, William, Andrew; LEENSLAG, Jan-Willem; VERBEKE, Hans, Godelieve, Guido Houlihan 2 11 Gildan Street, Balwyn North, Victoria 3104, Australia FLEXIBLE POLYURETHANE FOAM The following statement is a full description of this invention, including the best method of performing it known to O -2- O FLEXIBLE POLYURETHANE FOAM The present invention is related to a flexible polyurethane foam.

5 Processes for preparing a flexible polyurethane foam by reacting a polyisocyanate, C, one or more polyether polyols and water have been described widely.

I, One of the disadvantages of the prior art processes is that the blowing efficiency is 0not optimal. This means that either part of the water used does not react with the polyisocyanate and hence no C02 is liberated or the CO2 is liberated too early and leaves the reacting mixture without effectively contributing to the foam expansion.

Therefore the density is often not as low as it could be.

Another disadvantage is that at high stoichiometric water levels the foam properties such as hysteresis and related compression set properties deteriorate.

Further, flexible polyurethane foams so prepared often do not have sufficient loadbearing properties. In order to provide such foams with enhanced load-bearing properties often polyols are used which contain particulate materials dispersed therein. Examples of such polyols are so-called SAN-based polymer polyols, PIPA-polyols and PHD-polyols. If the particulate material has particles with a rather big average particle size, often foam collaps is observed.

EP 418039 discloses a process for preparing PIPA-polyol and a process for preparing flexible polyurethane foams using such PIPA-polyol. The PIPA particles have a size falling into two discrete ranges of 100-700, preferably 100-400 and more preferably of 100-200 nm on the one hand and of 200- more than 1000, preferably up to 1000, more preferably up to 800 nm on the other hand. Example 2, sample 7 showed a particle size of 800 and of more than 1000 nm. When the experiment was repeated the average particle size was determined at 1.7 mn.

EP 555721 discloses the preparation of flexible polyurethane foams; the amount of polyol, having a high oxypropylene content, used is relatively high while the amount of polyisocyanate used is relatively low.

S-3- O WO 96/35744 discloses a process for preparing a flexible foam by crushing a rigid foam obtained by reacting a relatively high amount of polyisocyanate with a low molecular weight polyol, a high molecular weight polyol and water. The flexible Sfoams show no major glass-rubber transition between -100°C and +25°C. PIPA polyol may be used. These foams show a too high compression set for loadbearing 1 applications.

0 The formation of relatively small (up to 0.3 pm urea aggregates in flexible polyurethane foam preparation in itself is known; see Journal of Applied Polymer Science, Vol. 35, 601-629 (1988) by J. P. Armistead et al. and Journal of Cellular Plastics, Vol. 30, page 144, (March 1994) by R. D. Priester et al.

Until recently it was believed that by increasing the urea hard phase content other important properties like resiliency, hysteresis and compression set will suffer; see Polyurethanes Expo '98, 17-20 September 1998, page 227 by D. R. Gier et al.

Surprisingly it has been found that by a proper selection of ingredients which as such are known for their use in flexible polyurethane foams and by using these ingredients in special relative amounts, in particular using a relatively high amount of polyisocyanate, the foam density may be lowered and foams are obtainable with good load-bearing properties, even if no polyol is used which contains dispersed particulate material. Further such foams show good recovery properties such as compression set. It was found that during reaction of the polyisocyanate, the polyols and the water, spontaneously urea and urethane containing particulate material is formed, which, once the foam has been prepared, is predominantly located in the struts of the foam, although no particulate material was present in the ingredients used for preparing the foams; preferably at least 80% of the particulate material is located in the struts, more preferably at least 90% by weight of the particulate material is in the struts. This in-situ formed particulate material may have a relatively large average particle size and comprises urea and urethane groups.

O-4- SA preferred process for preparing the inventive flexible polyurethane foam comprises reacting at an isocyanate index of 70 to 130, preferably 80-120, most O preferably 100-115, S1) 40-65 and preferably 45-63 parts by weight of a polyisocyanate composition (polyisocyanate 1) comprising a) 80-100% by weight of a diphenylmethane diisocyanate (MDI) component comprising, based on 100 parts by weight of the MDI component, 1) 75-100 and preferably 85-100 parts by weight of diphenylmethane diisocyanate comprising 15-75, preferably 25-75 and most preferably 30 to 70 parts by weight of 4,4'-diphenylmethane diisocyanate, and to 85, preferably 25 to 75 and most preferably 30 to 70 parts by weight of 2,4'- MDI, and 2,2'-MDI, and/or a liquid variant of such diphenylmethane diisocyanate, and 2) 0 to 25 and preferably 0-15 parts by weight of homologues of diphenylmethane diisocyanates having an isocyanate functionality of 3 or more; and b) 20-0% by weight of toluene diisocyanate; 2) 20 to 45, preferably 20-40 parts by weight of a polyether polyol (polyol 2) having an average molecular weight of 4500-10000, an average nominal functionality of 2-6 and preferably 2-4 and comprising oxypropylene and optionally oxyethylene groups, the amount of oxypropylene groups being at least by weight calculated on the weight of this polyol; 3) 3 to 20 parts by weight of a polyether polyol (polyol 3) having an average molecular weight of 700-4000 and preferably of 1000-2000, an average nominal functionality of 2-6 and an hydroxyl value of at most 225 mg KOH/g and comprising oxyethylene and optionally oxypropylene groups, the amount of oxyethylene groups being at least 70% by weight calculated on the weight of this polyol; and 4) 2-6 parts by weight of water, the amount of polyisocyanate 1), polyol polyol 3) and water being 100 parts by weight.

The in-situ formed particulate material behaves differently from the particulate material used traditionally in polyols like "polymer polyols", "SAN polymer polyols", "PHD polyols" and "PIPA polyols" upon tearing the foam according to the invention under ambient conditions the in-situ formed particulate material ci 0 fractures along the tear and the particulate material is cleaved at the fracture surface of the foam struts (as can be seen by scanning electron microscopy) while the traditional particulate material doesn't. Therefore the present invention is Sconcerned with flexible polyurethane foams comprising in situ formed particulate material comprising urea and urethane groups.

In

C

N

I The average particle size of the particles may vary widely from 0.1-20 rjm.

Preferably the average particle size is 2-20 lpm, more preferably 2.5-15 tpm and most preferably 3-10 lm. The particulate material preferably is predominantly located in the struts of the flexible foam; more preferably at least 80 volume of the particulate material is located in the struts; most preferably this figure is at least volume The volume fraction v) of the particulate material in the foam based on the volume of the solid part of the foam is at least 10% v and preferably at least 15% v and most preferably 15-40% v.

These flexible polyurethane foams preferably have a free rise core density of 5-80, more preferably of 6-50 and most preferably of 8-35 kg/m 3 measured according to ISO/DIS 845.

Further the flexible foams according to the present invention preferably have a ratio of theYoung's storage modulus E' at -100 0 C over the Young's storage modu us at of more than 15 (measured via Dynamic Mechanical Thermal Analysis according to ISO/DIS 6721-5).

In the context of the present invention the following terms have the following meaning: 1) isocyanate index or NCO index or index -6- 0 the ratio of NCO-groups over isocyanate-reactive hydrogen atoms present in a formulation, given as a percentage: 0 [NCO x 100] [Active hydrogen] In other words the NCO-index expresses the percentage of isocyanate actually used in a formulation with respect to the amount of isocyanate theoretically required for C reacting with the amount of isocyanate-reactive hydrogen used in a formulation.

It should be observed that the isocyanate index as used herein is considered from the point of view of the actual foaming process involving the isocyanate ingredient and the isocyanate-reactive ingredients. Any isocyanate groups consumed in a preliminary step to produce modified polyisocyanates (including such isocyanatederivatives referred to in the art as quasi or semi-prepolymers and prepolymers) or any active hydrogens consumed in a preliminary step reacted with isocyanate to produce modified polyols or polyamines) are not taken into account in the calculation of the isocyanate index. Only the free isocyanate groups and the free isocyanate-reactive hydrogens (including those of the water) present at the actual foaming stage are taken into account.

2) The expression "isocyanate-reactive hydrogen atoms" as used herein for the purpose of calculating the isocyanate index refers to the total of active hydrogen atoms in hydroxyl and amine groups present in the reactive compositions; this means that for the purpose of calculating the isocyanate index at the actual foaming process one hydroxyl group is considered to comprise one reactive hydrogen, one primary amine group is considered to comprise one reactive hydrogen and one water molecule is considered to comprise two active hydrogens.

3) Reaction system a combination of components wherein the polyisocyanates S-7- 0 are kept in one or more containers separate from the isocyanate-reactive components.

S4) The expression "polyurethane foam" as used herein refers to cellular products as obtained by reacting polyisocyanates with isocyanate-reactive hydrogen N containing compounds, using foaming agents, and in particular includes cellular products obtained with water as reactive foaming agent (involving a reaction of water with isocyanate groups yielding urea linkages and carbon dioxide and producing polyurea-urethane foams) and with polyols, aminoalcohols and/or polyamines as isocyanate-reactive compounds.

The term "average nominal hydroxyl functionality" is used herein to indicate the number average functionality (number of hydroxyl groups per molecule) of the polyol or polyol composition on the assumption that this is the number average functionality (number of active hydrogen atoms per molecule) of the initiator(s) used in their preparation although in practice it will often be somewhat less because of some terminal unsaturation.

6) The word "average" refers to number average unless indicated otherwise.

7) Particle size of the particulate material is defined as the number average diameter and is measured by fluorescent microscopy of microtomed sections of resin-embedded foam samples and determined by the automated image analysis protocol based on the principles of stereology described by E. Underwood in Quantitative Stereology 1970, chapter 6.4.4, figure 6.6.c, edited by Addison- Wesley Publishing Company. The volume fraction of the particulate material based on the volume of the solid part of the foam is determined likewise. The amount (on a volume basis) of particulate material in the struts based on the total amount of particulate material in the foam is determined by Brightfield Microscopy with refractive index matching.

-8o The diphenylmethane diisocyanate may be selected from isomeric mixtures of 4,4'- MDI, 2,4'-MDI and 2,2'-MDI in the indicated amounts, from liquid variants thereof, mixtures thereof and mixtures of such isomeric mixtures with one or more Sliquid variants of one or more of the constituents of these isomeric mixtures.

A liquid variant is defined as being liquid at 25 0 C and as being obtained by t introducing uretonimine and/or carbodiimide groups into said polyisocyanates, such a carbodiimide and/or uretonimine modified polyisocyanate having an NCO value of at least 20% by weight, and/or by reacting such a polyisocyanate with one or more polyols having a hydroxyl functionality of 2-6 and a molecular weight of 62-500 so as to obtain a modified polyisocyanate having an NCO value of at least by weight.

The MDI component may comprise homologues of diphenylmethane diisocyanate having an isocyanate functionality of 3 or more. This is achieved by mixing any of the aforementioned diphenylmethane diisocyanates with polymeric or crude MDI in appropriate ratios so as to obtain an MDI component with the indicated amounts of 4,4'-MDI, 2,4'-MDI and 2,2'-MDI, and homologues having a functionality of 3 or more. Polymeric or crude MDI comprise MDI and homologues having an isocyanate functionality of 3 or more and are well known in the art. They are made by the phosgenation of a mixture of polyamines obtained by the acid condensation of aniline and formaldehyde.

The manufacture of both the polyamine mixtures and the polyisocyanate mixtures is well known. The condensation of aniline with formaldehyde in the presence of strong acids such as hydrochloric acid gives a reaction product containing diaminodiphenylmethane together with polymethylene polyphenylene polyamines of higher functionality, the precise composition depending in known manner inter alia on the aniline/formaldehyde ratio. The polyisocyanates are made by phosgenation of the polyamine mixtures and the various proportions of diamines, triamines and higher polyamines give rise to related proportions of diisocyanates, triisocyanates and higher polyisocyanates. The relative proportions of diisocyanate, triisocyanate and higher polyisocyanates in such crude or polymeric 9- O MDI compositions determine the average functionality of the compositions, that is the average number of isocyanate groups per molecule. By varying the proportions of starting materials, the average functionality of the polyisocyanate compositions can be varied from little more than 2 to 3 or even higher. In practice, however, the 5 average isocyanate functionality preferably ranges from 2.1-2.8. The NCO value of these polymeric or crude MDIs is at least 30% by weight. The polymeric or crude MDI contain diphenylmethane diisocyanate, the remainder being polymethylene polyphenylene polyisocyanates of functionality greater than two together with by-products formed in the manufacture of such polyisocyanates by phosgenation.

The amount of 2,2'-MDI in most commercially available polyisocyanates based on MDI and/or polymeric or crude MDI is low; generally the amount is below 5% and often lower than 2% by weight.

Therefore it is to be understood that the amount of 2,2'-MDI in the above MDI component is low, generally below 5% and preferably below 2% by weight An example of an MDI component according to the present invention is a mixture of 85 by weight of MDI comprising 50% by weight of 4,4'-MDI and 50% by weight of 2,4'-MDI and 2,2'-MDI and 15 by weight of a polymeric MDI comprising about 35 pbw of 4,4'-MDI, 2 pbw of 2,4'-MDI and 63 pbw of homologues having an isocyanate of 3 or more (on 100 pbw of polymeric MDI). If desired up to 20% by weight of toluene diisocyanate (TDI), calculated on the total weight of the polyisocyanate composition, may be used. The TDI used may be 2,4-TDI, 2,6-TDI or mixtures thereof.

Polyol 2 may be selected from those known in the art. The polyol 2 may be a single polyol or a mixture of polyols meeting the restrictions as to molecular weight, nominal functionality and oxypropylene group content. The polyol 2 may be a polyoxypropylene polyol or a polyoxypropylene polyoxyethylene polyol having an oxypropylene group content of at least 70% by weight.

O o The oxyethylene groups in such polyols may be distributed over the polymer chain 0 of such polyol in random or block form or combinations thereof A particularly Spreferred polyol is a polyoxypropylene polyoxyethylene polyol wherein all oxyethylene groups are at the end of the polymer chain (so called EO-capped polyols); especially those comprising 10-25% by weight of oxyethylene groups at Sthe end of the polymer chains, the remainder of the oxyalkylene groups being N oxypropylene groups. Such polyols are widely known commercially; examples are Arcol T 1374 ex Lyondell and Daltocel F428 and F435. Daltocel is a trademark of C1 Huntsman International LLC; Daltocel F428 and F435 are obtainable from Huntsman Polyurethanes.

Polyol 3 may be selected from those known in the art. Polyol 3 may be a single polyol or a mixture of polyols meeting the restrictions as to molecular weight, nominal functionality, hydroxyl value and oxyethylene group content. Polyol 3 may be a polyoxyethylene polyol or polyoxyethylene polyoxypropylene polyol having a polyoxyethylene group content of at least 70% by weight.

The oxypropylene groups in such polyols may be distributed over the polymer chain of such polyol in random or block form or combinations thereof.

Most preferably polyoxyethylene polyols having an average molecular weight of 1000-2000, an hydroxyl value of at most 145 mg KOH/g and an average nominal functionality of 2-4 are used.

Examples of suitable polyols are polyoxyethylene glycol having a molecular weight of 1000-2000, G2005 ex Uniqema and Daltocel F526 ex Huntsman Polyurethanes.

Polyol 2 and polyol 3 include reaction products of propylene oxide and optionally ethylene oxide on the one hand and of ethylene oxide and optionally propylene oxide on the other hand, with initiators containing from 2 to 6 active hydrogen atoms per molecule. Suitable initiators include polyols, for example ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butane diol, glycerol, trimethylolpropane, triethanolamine, pentaerythritol and sorbitol; such initiators.

,-11- Water is used as the sole blowing agent.

As stated before, in the preferred process of manufacture particulate material is formed in-situ and therefore there is no need to have particulate material in the ingredients used for making the foam. However, if desired e.g. for processing reasons or for additional reinforcement such particulate material may be used and therefore polyol 2 and/or polyol 3 may contain particulate material; preferably polyol 2 contains the particulate material. Such modified polyols often referred to as "polymer" polyols have been fully described in the prior art and include products obtained by the polymerisation of one or more vinyl monomers, for example styrene and acrylonitrile, in polyether polyols, or by the reaction between a polyisocyanate and an amino- or hydroxy-functional compound, such as triethanolamine, in a polyether polyol.

The polymer modified polyols which are particularly interesting are products obtained by polymerisation of styrene and/or acrylonitrile in polyoxyethylene polyoxypropylene polyols and products obtained by reaction between a polyisocyanate and an amino or hydroxy-functional compound (such as triethanolamine) in a polyoxyethylene polyoxypropylene polyol. Polyoxyalkylene polyols containing from 5 to 50% of dispersed polymer are particularly useful.

In addition to the polyisocyanate, the polyols 2) and 3) and the water, one or more auxiliaries or additives kown m g the for the production of polyurethane foams may be used. Such optional auxiliaries or additives include chain extenders and/or cross-linkers; catalysts like tin compounds, such as stannous octoate and/or dibutyltin dilaurate, and/or tertiary amines, such as dinethylcyclohexylamine dibutyltin dilaurate, and/or tertiary amines, such as dimethylcyclohexylamine S-12o and/or triethylene diamine, and/or phosphates like NaH2P04 and/or Na2HP0 4 and 0 polycarboxylic acids, like citric acid, ethylene diamine tetra acetic acid and salts O thereof; foam-stabilizing agents or surfactants, for example siloxane-oxyalkylene copolymers and polyoxyethylene polyoxypropylene block copolymers; fire retardants, for example halogenated alkyl phosphates such as tris chloropropyl phospate, melamine, expanded graphite, bromine-containing compounds and guanidine carbonate, anti-oxidants, UV stabilizers, anti-microbial and anti-fungal compounds and fillers like latex, TPU, silicates, barium and calcium sulphates, cN chalk, glass fibres or beads and polyurethane waste material.

Chain extenders and cross-linkers may be selected from those isocyanate-reactive compounds known in the art for that purpose like polyamines, aminoalcohols and polyols. Of particular importance for the preparation of the foams are polyols and polyol mixtures having hydroxyl numbers of more than 225 mg KOH/g and an average nominal hydroxyl functionality of from 2 to 8. Suitable polyols have been fully described in the prior art and include reaction products of alkylene oxides, for example ethylene oxide and/or propylene oxide, with initiators containing from 2 to 8 active hydrogen atoms per molecule. Suitable initiators include polyols, for example ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butane diol, glycerol, trimethylolpropane, triethanolamine, pentaerythritol, sorbitol and sucrose; polyamines, for example ethylene diamine, tolylene diamine, diaminodiphenylmethane and polymethylene polyphenylene polyamines; and aminoalcohols, for example ethanolamine and diethanolamine; and mixture of such initiators. Other suitable polyols include polyesters obtained by the condensation of appropriate proportions of glycols and higher functionality polyols with polycarboxylic acids. Still further suitable polyols include hydroxyl terminated polythioethers, polyamines, polyesteramides, polycarbonates, polyacetals, polyolefins and polysiloxanes. Still further suitable isocyanate-reactive compounds include ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butane diol, glycerol, trimethylolpropane, ethylene diamine, ethanolamine, cN -13- 0 diethanolamine, triethanolamine and the otler initiators mentioned before.

O Mixtures of such isocyanate-reactive compounds may be used as well.

The amount of chain extender and/or cross linker in general will be less than Sby weight calculated on the amount of polyol 2) and polyol preferably this is at most 8% by weight.

SThe reaction of the polyisocyanate with polyol 2, polyol 3, the water and optionally CN the chain-extender and/or cross-linker is conducted at an isocyanate index of 70 to 130 and preferably of 80-120 and most preferably this index is 100 to 115.

In operating the process for making the foams of the invention, the known one-shot, prepolymer or semi-prepolymer techniques may be used together with conventional mixing methods and the foam may be produced in the form of free-rise foam, slabstock, mouldings including foam in fabric and pour-in-place applications, sprayed foam, frothed foam or laminates with other materials such as hardboard, plasterboard, plastics, paper or metal or with other foam layers. Since the flow of the ingredients is relatively good, these are in particular suitable for making moulded flexible polyurethane foams, minimizing the amount of overpack required.

It is convenient in many applications to provide the components for polyurethane production in pre-blended formulations based on each of the primary polyisocyanate and isocyanate-reactive components. In particular, an isocyanatereactive composition may be used which contains the auxiliaries, additives and the blowing agent in addition to the isocyanate-reactive compounds and in the form of a solution, an emulsion or dispersion. This composition is thn mixed with the polyisocyanate in order to prepare a foam according to the present invention.

The foam is prepared by allowing the aforementioned ingredients to react and foam until the foam does not rise any more. Subsequently the foam may be crushed.

The foams according to the present invention show good load-bearing properties like compression hardness values without the use of external fillers together with a -14- 0 good resilience, tear strength and durability (fatigue resistance) even at very low 0 densities. In conventional flexible foams often high amounts of filler need to be 0 used to obtain satisfactory loadbearing properties. Such high amounts of fillers hamper the processing due to a viscosity increase of the polyol.

The foams of the present invention may be used as cushioning material in furniture Sand automotive seating and in mattresses, as carpet backing, as hydrophilic foam in diapers, as packaging foam, as foams for sound insulation in automotive applications and for vibration isolation in general.

Another aspect of the invention is that since the amount of aromatic polyisocyanate and more in particular of MDI and polymethylene polyphenylene polyisocyanate used to prepare the foam is rather high, the content of cyclic and more in particular of aromatic residues in the flexible foam is relatively high as compared to conventional flexible polyurethane foams. The foams according to the invention preferably have a content of benzene rings, derived from aromatic polyisocyanates, which is 20 to 40 and most preferably 25 to less than 35% by weight based on the weight of the foam. Since polyols, polymer polyols, fire retardants, chain extenders and/or fillers, which contain benzene rings, may be used, the overall benzene ring content of the flexible foam may be higher and preferably ranges from 20 to 55 and most preferably from 25 to 50% weight as measured by calibrated Fourier Transform Infrared Analysis.

The invention is illustrated by the following example.

Example 1 A polyisocyanate composition was prepared by mixing 84.3 parts by weight of MDI comprising 50% by weight of 4.4'-MDI and 50% by weight of 2,2'- MDI and 15.7 parts by weight (pbw) of a polymeric MDI having an NCO value of o 30.7% by weight and comprising 35.4 pbw of 4,4'-MDI, 2.3 pbw of 2,4'+2,2'-MDI and 62.3 pbw of homologues having an isocyanate functionality of 3 or more.

A polyol composition was prepared by mixing 36.2 pbw of Arcol 1374, 9.4 pbw of SDaltocel F526, 2.9 pbw of water, 0.24 pbw of EPK-38-1, a surfactant ex 5 Goldschmidt, 0.34 pbw of a mixture of Irganox 1135 and Irgafos TNPP (50/50, Sw/w), both anti-oxydants ex Ciba.

The polyisocyanate composition (49.8 pbw) and the polyol composition (50.3 pbw) were mixed and allowed to react under free-rise conditions, the isocyanate index was 105. The foam obtained was a flexible polyurethane foam containing particulate material comprising urethane and urea groups as determined by inspection of the amide-I region via Infrared Microscopy Analysis using a high powered source and the foam had the following physical properties: method of measurement free rise core density, kg/m 3 20 ISO/DIS 845 compression set at 70 0 C dry, 15 ISO 1856 compression load deflection at 40% 1.4 ISO 3386/1 compression, kPa average particle diameter of 3.9 see before particulate material, tmu volume fraction of particulate 20 see before material based on volume of the solid part of the foam, %v amount of particulate material in the >90 see before struts based on the amount of particulate material in the foam, v -16- Example 2 Scanning Electron Microscopy images were made of foams made from PIPA polyol, PHD polyol and from ingredients according to the present invention.

Pictures show the following Figure 1 2 3 4 6 Scale bar (pnm) 20 5 20 5 20 10 Foam invention invention

PIPA

PIPA

PHD

PHD

First of all the difference in particle size is noticeable (compare figures 1, 3 and In figure 1 big particles with clear boundaries are visible; in figure 3 the particles are much smaller and in figure 5 the boundaries are not so clear and the PHD material seems to form conglomerates with not sharply defined boundaries.

Secondly, figures 1 and 2 nicely show the particles cleaved at the fracture surface of the foam struts. Figures 3-6 show particulate material, which did not cleave.

-17- Example 3 58 pbw of Daltocel F428, 30 pbw of polyol X, 12 pbw of Daltocel F526, 7 bw of water, 1.2 pbw of B4113 (a surfactant from Goldsclunidt), 0.6 pbw of D8154 (a amine catalyst from AirProducts), 0.1 pbw of Niax Al (a catalyst from Union Carbide) and 0.3 pbw of D33 LV (a catalyst from AirProducts) where mixed in all open bucket of 101. To this was added 110 pbw of a mixture of the MDI and polymeric MDI used in example I in a weight ratio of 4:1. The index was 100.

This mixture was allowed to react. A flexible polyurethane was obtained having open cells and a free rise density of 19 kg/m 3 Polyol X is an polyoxyethylene polyoxypropylene polyol having a nominal functionality of 3, an average equivalent weight of about 2000, having an EO content of 28% by weight, an EO-capped content of 15% by weight and the remainder of the EO being randomly distributed with the PO; the primary hydroxyl content is about 85% and the monool content is about 12% mole.

Where the terms "comprise", "comprises", "comprised" or "comprising" are used in this specification, they are to be interpreted as specifying the presence of the stated features, integers, steps or components referred to, but not to preclude the presence or addition of one or more other feature, integer, step, component or group thereof.

Further, any prior art reference or statement provided in the specification is not to be taken as an admission that such art constitutes, or is to be understood as constituting, part of the common general knowledge in Australia.

This application is a divisional of Australian Patent Application No. 2001287584 the disclosure of which is incorporated herein by way of reference.

Claims (9)

1. Flexible polyurethane foam comprising in-situ formed particulate material comprising urea and urethane groups.

2. Flexible polyurethane foam according to Claim 1 comprising particulate material, which particulate material has an average particle size of 2-20 jm, comprises urea and urethane groups and which particulate material has been formed in-situ.

3. Flexible polyurethane foam according to Claim 1 or Claim 2 wherein the average particle size is 3-10 pm.

4. Flexible polyurethane foam according to any one of Claims the foam comprises 20-45% by weight of benzene groups.

Flexible polyurethane foam according to any one of Claims the foam comprises 25-40% by weight of benzene groups.

6. Flexible polyurethane foam according to any one of Claims the foam has a free rise core density of 5-80 kg/m 3

7. Flexible polyurethane foam according to any one of Claims the foam has a free rise core density of 6-50 kg/m 3

8. Flexible polyurethane foam according to any one of Claims the foam has a free rise core density of 8-35 kg/m 3 1 to 3 wherein 1 to 4 wherein 1 to 5 wherein 1 to 6 wherein 1 to 7 wherein

9. Flexible polyurethane foam according to any one of Claims 1 to 8 comprising at least 10% v of particulate material based on the volume of the solid part of the foam. Flexible foam according to any one of Claims 1 to 9 substantially as hereinbefore described with reference to the accompanying Examples. DATED this 29 t day of September, 2005 HUNTSMAN INTERNATIONAL LLC By their Patent Attorneys: Houlihan 2 v1t